US20170151514A1 - Air filter material - Google Patents

Air filter material Download PDF

Info

Publication number
US20170151514A1
US20170151514A1 US15/300,164 US201415300164A US2017151514A1 US 20170151514 A1 US20170151514 A1 US 20170151514A1 US 201415300164 A US201415300164 A US 201415300164A US 2017151514 A1 US2017151514 A1 US 2017151514A1
Authority
US
United States
Prior art keywords
polyester
nonwoven fabric
melting point
nearly
shape
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/300,164
Other languages
English (en)
Inventor
Yukihiro Kihara
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Unitika Ltd
Original Assignee
Unitika Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Unitika Ltd filed Critical Unitika Ltd
Assigned to UNITIKA LTD. reassignment UNITIKA LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KIHARA, YUKIHIRO
Publication of US20170151514A1 publication Critical patent/US20170151514A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D39/00—Filtering material for liquid or gaseous fluids
    • B01D39/14—Other self-supporting filtering material ; Other filtering material
    • B01D39/16—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres
    • B01D39/1607—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres the material being fibrous
    • B01D39/1623—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres the material being fibrous of synthetic origin
    • B01D39/163—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres the material being fibrous of synthetic origin sintered or bonded
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D39/00—Filtering material for liquid or gaseous fluids
    • B01D39/14—Other self-supporting filtering material ; Other filtering material
    • B01D39/16—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres
    • B01D39/1607—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres the material being fibrous
    • B01D39/1623—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres the material being fibrous of synthetic origin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D46/00—Filters or filtering processes specially modified for separating dispersed particles from gases or vapours
    • B01D46/54—Particle separators, e.g. dust precipitators, using ultra-fine filter sheets or diaphragms
    • B01D46/546—Particle separators, e.g. dust precipitators, using ultra-fine filter sheets or diaphragms using nano- or microfibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/02—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer
    • B32B5/022—Non-woven fabric
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/22—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed
    • B32B5/24—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer
    • B32B5/26—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer another layer next to it also being fibrous or filamentary
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B7/00—Layered products characterised by the relation between layers; Layered products characterised by the relative orientation of features between layers, or by the relative values of a measurable parameter between layers, i.e. products comprising layers having different physical, chemical or physicochemical properties; Layered products characterised by the interconnection of layers
    • B32B7/04—Interconnection of layers
    • B32B7/12—Interconnection of layers using interposed adhesives or interposed materials with bonding properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/02—Types of fibres, filaments or particles, self-supporting or supported materials
    • B01D2239/025—Types of fibres, filaments or particles, self-supporting or supported materials comprising nanofibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/06—Filter cloth, e.g. knitted, woven non-woven; self-supported material
    • B01D2239/0604—Arrangement of the fibres in the filtering material
    • B01D2239/0618—Non-woven
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/06—Filter cloth, e.g. knitted, woven non-woven; self-supported material
    • B01D2239/065—More than one layer present in the filtering material
    • B01D2239/0668—The layers being joined by heat or melt-bonding
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/06—Filter cloth, e.g. knitted, woven non-woven; self-supported material
    • B01D2239/065—More than one layer present in the filtering material
    • B01D2239/0681—The layers being joined by gluing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/12—Special parameters characterising the filtering material
    • B01D2239/1233—Fibre diameter
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/12—Special parameters characterising the filtering material
    • B01D2239/1291—Other parameters
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2275/00—Filter media structures for filters specially adapted for separating dispersed particles from gases or vapours
    • B01D2275/10—Multiple layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0253—Polyolefin fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0276—Polyester fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/724—Permeability to gases, adsorption

Definitions

  • the present invention is related to an air filter material for filtering gas, such as air and the like, particularly to a middle efficiency or high efficiency air filter material.
  • Nonwoven fabric formed from ultrafine fibers has been employed for middle efficiency or high efficiency air filter material.
  • the nonwoven fabric can be so-called melt blown nonwoven fabric. Since the melt blown nonwoven fabric is consisted from ultrafine fibers, tensile strength or tear strength is poor and the fabric is difficult to treat. Accordingly, the melt blown fabric is laminated with another nonwoven fabric composed of filaments or fibers having high fineness, such as spun bonded nonwoven fabric or nonwoven fabric of staple fibers obtained by card method (Patent Literature 1).
  • adhesive component is changed from the portion of the constituent filaments of the spun bond nonwoven fabric to the other adhesive agent to bond and to integrate the melt blown nonwoven fabric with the spun bond nonwoven fabric.
  • the other adhesive agent may include emulsion type adhesive agent or hot melt adhesive agent.
  • the adhesive agent might be flown out and filled in the openings of the spun bond nonwoven fabric, thus reducing air permeability.
  • An object of the present invention is to provide an air filter material in which spun bond nonwoven fabric and melt blown nonwoven fabric are laminated and integrated without reducing the air permeability.
  • the present invention solves the above mentioned problem by employing a combination of a specific spun bond nonwoven fabric with a specific hot melt adhesive agent. That is, the present invention is to provide an air filter material comprising ultrafine fiber nonwoven fabric formed from ultrafine fibers and polyester nonwoven fabric formed from polyester continuous filaments, the ultrafine fiber nonwoven fabric being laminated and integrated with the polyester nonwoven fabric,
  • a shape of the polyester continuous filament in the cross section is the following nearly ‘Y4’ shape in which the bottom ends of the nearly ‘Y’ parts are connected to up, down, left and right:
  • the ultrafine fiber nonwoven fabric is bonded with the polyester nonwoven fabric by powder type or spider web type hot melt adhesive agent having a melting point lower than the melting points of the ultrafine fiber and the polyester continuous filament.
  • the polyester nonwoven fabric for forming the air filter material of the present invention contains polyester continuous filaments having a specific cross sectional shape as constituent filaments.
  • the cross sectional shape has four nearly Y shapes as shown in FIG. 1 .
  • the nearly Y shape has a bottom end 1 which is connected with the other nearly Y shapes in the directions of up, down, left and right to form the nearly Y4 shape as shown in FIG. 2 .
  • the nearly Y4 shape has four concave portions 2 , eight convex portions 3 and four small concave portions 4 .
  • the four concave portions 2 form relatively large opening portions in or with the polyester continuous filaments.
  • the polyester continuous filament is composed of a low melting point polyester component and a high melting point polyester component. That is, the polyester continuous filament is preferably a conjugate polyester continuous filament in which nearly V shape portions 6 of the cross sectional shape is formed from the low melting point polyester component and a nearly+shape portion 5 is formed from the high melting point polyester component.
  • the polyester nonwoven fabric used in the present invention can be produced by collecting conjugate type continuous filaments which are melt-spun through conjugate type spinning nozzles, and softening or melting the low melting point polyester, followed by solidifying, whereby the polyester continuous filaments are heat-bonded with each other by the low melting point polyester components.
  • the resulting polyester nonwoven fabric are excellent in mechanical properties, such as tensile strength or tear strength and excellent in treatment ability, because the polyester continuous filaments are bonded each other by the heat bonding of the low melting point polyester components.
  • the heat bonding of the low melting point polyester components can be conducted by a heat treatment such as heat embossing process or heat air treatment.
  • a heat treatment such as heat embossing process or heat air treatment.
  • heat pressing portions are partially present and in the heat pressing portions, the polyester continuous filaments are heat bonded at crossing points of polyester continuous filaments.
  • the polyester continuous filaments are heat bonded with each other as a whole.
  • the heat embossing process can be combined with the heat air treatment and may be used together.
  • preferred is the heat embossing process wherein heat pressing is partially conducted by applying heat and pressure, in order to enhance the mechanical properties of the polyester nonwoven fabric.
  • a pressure bonding area ratio of the embossing roll employed may preferably be within the range of 10 to 20%.
  • the pressure bonding area ratio is too small, the mechanical properties, such as tensile strength and the like, would be deteriorated.
  • the pressure bonding area ratio is too high, the resulting nonwoven fabric has a very small opening area between polyester continuous filaments, thus reducing the air permeability.
  • a conjugate ratio of the low melting point polyester component and the high melting point polyester component both constituting the polyester continuous filament may preferably be within the range of 1/4 to 1/1 (mass ratio) in low melting point polyester component/high melting point polyester component.
  • the amounts of the low melting point polyester component are low, the physical properties, such as tensile strength, of the polyester nonwoven fabric would be deteriorated.
  • the low melting point polyester components are flown out in the openings among the polyester continuous filaments by heat treatment and the air permeability would be reduced.
  • the polyester nonwoven fabric can be manufactured by any methods known to the art, such as spun bond method, with the exception that a nozzle orifice using at a time of melt spinning is changed. That is, in a method wherein conjugate type continuous filaments obtained by a conjugate melt spinning of the low melting point polyester and the high melting point polyester are accumulated to form a spun bond nonwoven fabric, a nozzle orifice shape using at a time of melt spinning has the following figure:
  • the figure of the nozzle orifice is said ‘Y4’ figure in which the bottom ends of ‘Y’ parts are connected to up, down, left and right, besides the ‘/’ parts of the adjacent ‘Y’ parts are paralleled and the ‘ ⁇ ’ parts of the adjacent ‘Y’ parts are paralleled.
  • the nozzle orifice has four ‘Y’ parts as shown in FIG. 3 .
  • the bottom ends of ‘Y’ parts are connected to up, down, left and right to become ‘Y4’ figure.
  • the ‘/’ parts 8 , 8 of the adjacent ‘Y’ parts are paralleled with each other, and the ‘ ⁇ ’ parts 9 , 9 of the adjacent ‘Y’ parts are paralleled with each other.
  • the polyester resin is provided and melt spun in the nozzle orifice which has ‘Y4’ figure to become the polyester filament having the nearly ‘Y4’ shape in the cross section.
  • the polyester filament has the four big concave sections 2 because the ‘/’ parts 8 , 8 of the nozzle orifice are paralleled and the ‘ ⁇ ’ parts 9 , 9 are parallel.
  • the polyester filament has the nearly ‘+’ part 5 and the nearly ‘V’ parts 6 joined to the each tip of ‘+’ part 5 .
  • the low melting point polyester resin is provided in ‘V’ parts 10 of the nozzle orifice and the high melting point polyester resin is provided in a ‘+’ part 11 of the nozzle orifice. After melt spinning, the conjugate continuous polyester filament in which the nearly ‘V’ parts 6 are formed from the low melting point polyester and the nearly ‘+’ part 5 is formed from the high melting point polyester is obtained.
  • the filaments are accumulated to form a filamentous web.
  • the filamentous web is then subjected to a heat treatment in which the low melting point polyester components of the conjugate polyester filament are molten or softened, and cooled to solidify.
  • the conjugate polyester filaments are bonded with each other by the low melting point polyester components to manufacture the polyester nonwoven fabric of the continuous polyester filaments. If necessary, a small amount of a binder agent may be applied to the nonwoven fabric.
  • the continuous polyester filament preferably has a fineness of not less than 10 dtex, more preferably not less than 15 dtex.
  • a fineness of less than 10 dtex air permeability and mechanical properties would be deteriorated.
  • An upper limit of the fineness is not limited, but it may preferably be about 30 dtex. If the fineness is more than 30 dtex, it is not easy to cool the continuous polyester filament in the melt spinning process, thus resulting in poor productivity.
  • the polyester nonwoven fabric preferably has a weight of 30 g/m 2 to 130 g/m 2 . Weights of less than 30 g/m 2 would reduce mechanical properties and those of more than 130 g/m 2 would be too heavy and would make the treatment of the fabric difficult.
  • the ultrafine fiber nonwoven fabric can be any types known to the art, especially melt blown nonwoven fabric.
  • the ultrafine fiber can be formed from polyolefin (such as polypropylene), polyester or the like.
  • the ultrafine fiber may have a fiber diameter (converting it into a circular fiber diameter) of 1 to 5 micrometers. The fiber diameters of more than 5 micrometers would not obtain the middle efficiency or high efficiency air filter materials. Those of less than 1 micrometer would reduce productivity.
  • the ultrafine fiber fabric preferably has a weight of 10 g/m 2 to 30 g/m 2 . Weights of less than 10 g/m 2 would not obtain the middle efficiency or high efficiency air filter materials. Those of more than 30 g/m 2 would reduce productivity.
  • the ultrafine fiber nonwoven fabric and the polyester nonwoven fabric are bonded by the powder type or spider web type hot melt adhesive agent.
  • the adhesive agent has to have a melting point lower than the melting points of the ultrafine fiber and the polyester continuous filament.
  • the hot melt adhesive agent has to have a melting point of lower than the polypropylene ultrafine fibers.
  • the melting point of the hot melt adhesive agent is preferably within the range of 50 to 120° C.
  • the hot melt adhesive agent In the case where the melting point of the hot melt adhesive agent is higher than those of the ultrafine fiber and the polyester continuous filament, it is not preferred that, when the hot melt adhesive agent is molten or soften to bond the ultrafine fiber nonwoven fabric with the polyester nonwoven fabric, the ultrafine fiber nonwoven fabric or the polyester nonwoven fabric would be heat deformed before the melting or softening of the adhesive agent, to reduce filterability of the obtained filter.
  • the hot melt adhesive agent has to be powder type or spider web type. This is because the reduction of the air permeability of the air filter material is prevented by keeping area portions where no adhesive agent is present. For example, if a film type hot melt adhesive agent is employed to bond the ultrafine fiber nonwoven fabric with the polyester nonwoven fabric, the hot melt adhesive agent would be present all over the surface and would severely deteriorate the air permeability of the air filter material.
  • An application amount of the hot melt adhesive agent may preferably be within the range of 1 to 30 g/m 2 .
  • Application amounts of less than 1 g/m 2 would easily peel off the bonding of the ultrafine fiber nonwoven fabric and the polyester nonwoven fabric.
  • Those of more than 30 g/m 2 would reduce the air permeability because the areas where no adhesive agent is present are reduced.
  • the air filter material of the present invention is employed as air filter by methods known to the art.
  • the air filter material may be cut into a suitable size and is equipped in a filter frame to use as an air filter in a clean room.
  • the air filter material of the present invention is subjected to pleating process and fixed in a filter frame to use an air filter for a dust collection machine, an automobile or the like.
  • the air filter material of the present invention is composed of the polyester nonwoven fabric formed from the polyester filaments having a specific cross section, the ultrafine fiber nonwoven fabric being laminated and integrated with the polyester nonwoven fabric by using a specific hot melt adhesive agent.
  • the air filter material has technical effects that the air permeability is not easily reduced.
  • a melting point was determined to be a temperature indicating a maximum value of a melting endothermic peak measured at a rising temperature speed of 20° C./min using a differential scanning calorimeter DSC-7 manufactured by Perkin Elmer Co., Ltd.
  • a sample of 0.5 g was dissolved in 100 ml of a mixture solution of phenol and ethane tetrachloride in an equal amount ratio and a relative viscosity was determined by a conventional method at a temperature of 20° C.
  • a low melting point polyester was prepared by copolymerizing 92 mol % of terephthalic acid and 8 mol % of isophthalic acid, as a dicarboxylic acid, with 100 mol % of ethylene glycol, as a diol.
  • the low melting point polyester had a melting point of 230° C. and a relative viscosity [ ⁇ rel] of 1.44.
  • Four % by mass of titanium oxide as a nucleating agent was added into the low melting point polyester, which was employed as the low melting point polyester component.
  • a high melting point polyester was prepared by copolymerizing 100 mol % of terephthalic acid as a dicarboxylic acid with 100 mol % of ethylene glycol as a diol.
  • the high melting point polyester had a melting point of 260° C. and a relative viscosity [ ⁇ rel] of 1.38, which was employed as the high melting point polyester component.
  • the low melting point polyester component was provided and melt spun in ‘V’ parts shown FIG. 4 of the nozzle orifice and the high melting point polyester component was provided in a ‘+’ part shown FIG. 4 .
  • the melt spinning was performed by providing the two types of polyester at the rate of 8.33 g/min. per nozzle orifice and at 285° C.
  • a mass ratio of the low melting point polyester component/the high melting point polyester component was 1/2.
  • the continuous filaments spun from the nozzle orifices were passed in an air sucker device located 2 m below the nozzle orifices and drawn into 17 dtex in fineness to form conjugate continuous filaments which had a cross section as shown in FIG. 2 .
  • the conjugate continuous filaments were opened by an opening device, and accumulated on a moving net conveyor to obtain a continuous filamentous web.
  • the filamentous web was passed between an embossing roll and a flat roll as a heat embossing device to obtain a polyester nonwoven fabric A.
  • the embossing roll had convex tips which had the area of 0.7 mm 2 , and a total area of the convex parts was occupied 15 percent of the entire surface of the embossing role.
  • the embossing conditions were a surface temperature of 213° C. and a linear pressure of 300 N/cm.
  • the polyester nonwoven fabric A had a weight of 40 g/m 2 .
  • a polyester nonwoven fabric was obtained as generally described in Production Example A, with the exception that the weight of the final polyester nonwoven fabric A was changed to 70 g/m 2 .
  • Polypropylene having a melting point of 162° C. was introduced into a melt blown die from which heated air was blown, to form ultrafine fibers having a diameter of about 3 micrometers.
  • the ultrafine fibers were accumulated on a moving conveyor to obtain an ultrafine fiber nonwoven fabric having a weight of 20 g/m 2 .
  • the ultrafine fiber nonwoven fabric was spray-coated with powder type hot melt adhesive agent (powder formed from low density polyethylene having a melting point of about 100° C.) in a spray-coating amount of 5 g/m 2 , and then laminated thereon with the polyester nonwoven fabric A to obtain a layered laminate.
  • the laminate was put on a lower conveyor combined with an upper conveyor in a heat treatment device, both conveyors being covered with Teflon coating on the surfaces, and heated with moving.
  • a temperature of the space between the upper conveyor and the lower conveyor was controlled to 100° C. and the space was gradually narrowed from an entrance to an exit to set a width of the space of 1 mm at the exit.
  • the layered laminate was cooled to obtain an integrated air filter material composed of the ultrafine fiber nonwoven fabric and the polyester nonwoven fabric.
  • the air filter material had an air permeability of 26.5 cc/m 2 /sec. Since the ultrafine fiber nonwoven fabric was firmly integrated with the polyester nonwoven fabric A, the ultrafine fiber nonwoven fabric was damaged when it was peeled off from the polyester nonwoven fabric.
  • An air filter material was obtained as generally described in Example 1, with the exception that the polyester nonwoven fabric A was changed to the polyester nonwoven fabric B.
  • the resulting air filter material had an air permeability of 25.7 cc/m 2 /sec.
  • the ultrafine fiber nonwoven fabric was firmly integrated with the polyester nonwoven fabric B.
  • An air filter material was obtained as generally described in Example 1, with the exception that a spray-coating amount of the powder type hot melt adhesive agent (powder formed from low density polyethylene having a melting point of about 100° C.) was changed to 10 g/m 2 .
  • the resulting air filter material had an air permeability of 25.3 cc/m 2 /sec.
  • the ultrafine fiber nonwoven fabric was firmly integrated with the polyester nonwoven fabric A.
  • An air filter material was obtained as generally described in Example 2, with the exception that a spray-coating amount of the powder type hot melt adhesive agent (powder formed from low density polyethylene having a melting point of about 100° C.) was changed to 10 g/m 2 .
  • the resulting air filter material had an air permeability of 25.0 cc/m 2 /sec.
  • the ultrafine fiber nonwoven fabric was firmly integrated with the polyester nonwoven fabric B.
  • An air filter material was obtained as generally described in Example 1, with the exception that the powder type hot melt adhesive agent (powder formed from low density polyethylene having a melting point of about 100° C.) was changed to a spider web type hot melt adhesive agent (available from Kurehatech Ltd. as Item Stock Number LNS0020, based on copolymerized polyamide, melting point 115° C., coating amount 20 g/m 2 ).
  • the resulting air filter material had an air permeability of 23.7 cc/m 2 /sec.
  • the ultrafine fiber nonwoven fabric was firmly integrated with the polyester nonwoven fabric A.
  • An air filter material was obtained as generally described in Example 2, with the exception that the powder type hot melt adhesive agent (powder formed from low density polyethylene having a melting point of about 100° C.) was changed to a spider web type hot melt adhesive agent (available from Kurehatech Ltd. as Item Stock Number LNS0020, based on copolymerized polyamide, melting point 115° C., coating amount 20 g/m 2 ).
  • the resulting air filter material had an air permeability of 23.9 cc/m 2 /sec.
  • the ultrafine fiber nonwoven fabric was firmly integrated with the polyester nonwoven fabric B.
  • the ultrafine fiber nonwoven fabric and the polyester nonwoven fabric A or B are laminated and integrated using powder type or spider web type hot melt adhesive agent to obtain an air filter material having excellent air permeability.
  • FIG. 1 is one nearly ‘Y’ part in the nearly ‘Y4’ shape which is the cross sectional view of the continuous filament used in the invention.
  • FIG. 2 is the cross sectional view of the continuous filament used in the invention.
  • FIG. 3 is one ‘Y’ part in the ‘Y4’ figure of the nozzle orifice.
  • FIG. 4 is the ‘Y4’ figure of the nozzle orifice.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Nanotechnology (AREA)
  • Nonwoven Fabrics (AREA)
  • Filtering Materials (AREA)
  • Laminated Bodies (AREA)
US15/300,164 2014-03-31 2014-03-31 Air filter material Abandoned US20170151514A1 (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2014/059486 WO2015151168A1 (ja) 2014-03-31 2014-03-31 エアフィルター材

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/059486 A-371-Of-International WO2015151168A1 (ja) 2014-03-31 2014-03-31 エアフィルター材

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US16/223,999 Division US10610814B2 (en) 2014-03-31 2018-12-18 Air filter material

Publications (1)

Publication Number Publication Date
US20170151514A1 true US20170151514A1 (en) 2017-06-01

Family

ID=54239538

Family Applications (2)

Application Number Title Priority Date Filing Date
US15/300,164 Abandoned US20170151514A1 (en) 2014-03-31 2014-03-31 Air filter material
US16/223,999 Active US10610814B2 (en) 2014-03-31 2018-12-18 Air filter material

Family Applications After (1)

Application Number Title Priority Date Filing Date
US16/223,999 Active US10610814B2 (en) 2014-03-31 2018-12-18 Air filter material

Country Status (4)

Country Link
US (2) US20170151514A1 (de)
EP (1) EP3127594B1 (de)
JP (1) JP6249537B2 (de)
WO (1) WO2015151168A1 (de)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017222120A (ja) * 2016-06-17 2017-12-21 ユニチカ株式会社 高空隙積層ボードの製造方法
US20190276686A1 (en) * 2016-09-23 2019-09-12 Devan Chemicals Textile coating composition
US10610814B2 (en) * 2014-03-31 2020-04-07 Unitika Ltd. Air filter material
US11470505B2 (en) * 2019-08-30 2022-10-11 Parallel Wireless, Inc. Support for linking of packet detection rules (PDR) for optimizing throughput of combined serving gateway (SGW)/packet gateway (PGW) architecture

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6795167B2 (ja) * 2016-04-22 2020-12-02 ユニチカ株式会社 清拭布
JP6910055B2 (ja) * 2017-05-26 2021-07-28 ユニチカ株式会社 熱成型不織布の製造方法
KR102354177B1 (ko) * 2019-10-16 2022-01-24 주식회사 휴비스 저융점 폴리에스테르 섬유를 포함하는 캐빈에어필터용 부직포

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002001020A (ja) * 2000-04-10 2002-01-08 Toray Ind Inc 濾 材
JP2013076182A (ja) * 2011-09-30 2013-04-25 Unitika Ltd ポリエステル長繊維不織布及びその製造方法

Family Cites Families (34)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3169089A (en) 1960-04-22 1965-02-09 Celanese Corp Filaments
US3940302A (en) 1972-03-02 1976-02-24 Imperial Chemical Industries Limited Non-woven materials and a method of making them
JPS54151617A (en) * 1978-05-15 1979-11-29 Teijin Ltd Synthetic fibers
US4791026A (en) 1986-11-27 1988-12-13 Teijin Limited Synthetic polymer multifilament yarn useful for bulky yarn and process for producing the same
JPH0723562B2 (ja) * 1986-11-27 1995-03-15 帝人株式会社 潜在嵩高性マルチフィラメント及びその製造法
JPS63295712A (ja) 1987-02-16 1988-12-02 Mitsubishi Rayon Co Ltd 異形断面熱融着繊維
US5057368A (en) 1989-12-21 1991-10-15 Allied-Signal Filaments having trilobal or quadrilobal cross-sections
US5176926A (en) 1991-08-27 1993-01-05 E. I. Du Pont De Nemours And Company Spinnerets for producing trilobal and tetralobal filaments exhibiting low glitter and high bulk
JP2947646B2 (ja) 1991-09-27 1999-09-13 東レ株式会社 タフテッドカーペット用基布
US5277976A (en) 1991-10-07 1994-01-11 Minnesota Mining And Manufacturing Company Oriented profile fibers
ZA933072B (en) 1992-05-01 1994-10-30 Hoechst Celanese Corp A tufted fabric.
US6093491A (en) 1992-11-30 2000-07-25 Basf Corporation Moisture transport fiber
US5380592A (en) 1993-12-28 1995-01-10 E. I. Du Pont De Nemours And Company Trilobal and tetralobal cross-section filaments containing voids
US5707735A (en) * 1996-03-18 1998-01-13 Midkiff; David Grant Multilobal conjugate fibers and fabrics
JPH09256255A (ja) 1996-03-21 1997-09-30 Toray Ind Inc 不織布およびカーペット用一次基布およびカーペットおよび壁材
JP3168564B2 (ja) * 1996-08-27 2001-05-21 チッソ株式会社 不織布およびそれを用いた吸収性物品
JP3741180B2 (ja) * 1997-01-20 2006-02-01 チッソ株式会社 熱接着性複合繊維、これを用いた不織布及び吸収性物品
JPH10273863A (ja) 1997-03-28 1998-10-13 Toray Ind Inc タフテッドカーペット用基布およびタフテッドカーペット
JP4267158B2 (ja) 1999-12-24 2009-05-27 ユニチカ株式会社 タフテッドカーペット用基布およびその製造方法
US6815383B1 (en) 2000-05-24 2004-11-09 Kimberly-Clark Worldwide, Inc. Filtration medium with enhanced particle holding characteristics
KR100397621B1 (ko) 2001-05-14 2003-09-13 주식회사 효성 카페트용 폴리(트리메틸렌 테레프탈레이트) ｂｃｆ이형단면사
EP1476598A1 (de) 2002-02-15 2004-11-17 Colbond B.V. Primäre teppichrückbeschichtung
US20030175475A1 (en) 2002-03-13 2003-09-18 Higgins Kenneth B. Textile constructions, components or materials and related methods
NZ542075A (en) 2003-01-30 2007-06-29 Tac Fast Systems Sa Carpet tile, installation, and methods of manufacture and installation thereof
JP4906237B2 (ja) 2004-03-31 2012-03-28 ユニチカ株式会社 タフテッドカーペット一次基布およびタフテッドカーペット
ATE446395T1 (de) 2005-12-06 2009-11-15 Invista Tech Sarl Im profil sechslappige filamente mit drei grösseren lappen und drei kleineren lappen, tufting-teppich aus garn mit derartigen filamenten sowie kapillare spinndüse zur herstellung derartiger filamente
KR101036856B1 (ko) 2006-01-25 2011-05-25 아사히 가세이 셍이 가부시키가이샤 열접착성 적층 부직포
JP2007224474A (ja) 2006-02-27 2007-09-06 Unitika Ltd タフテッドカーペット用一次基布
US20070254130A1 (en) 2006-05-01 2007-11-01 Cheek Glenn E Laminates with sound absorbing porperties
JP4774558B2 (ja) * 2007-04-17 2011-09-14 根来産業株式会社 機能性異型再生ポリエチレンテレフタレート繊維およびその製造方法
TWI374952B (en) * 2009-07-07 2012-10-21 Shinkong Synthetic Fibers Corp Fiber with 4t cross section, and spinneret and method for producing the same
US20110210081A1 (en) * 2010-02-26 2011-09-01 Clarcor Inc. Fine fiber liquid particulate filter media
US9474994B2 (en) 2013-06-17 2016-10-25 Donaldson Company, Inc. Filter media and elements
EP3127594B1 (de) * 2014-03-31 2018-11-28 Unitika Ltd. Luftfiltermaterial

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002001020A (ja) * 2000-04-10 2002-01-08 Toray Ind Inc 濾 材
JP2013076182A (ja) * 2011-09-30 2013-04-25 Unitika Ltd ポリエステル長繊維不織布及びその製造方法

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10610814B2 (en) * 2014-03-31 2020-04-07 Unitika Ltd. Air filter material
JP2017222120A (ja) * 2016-06-17 2017-12-21 ユニチカ株式会社 高空隙積層ボードの製造方法
US20190276686A1 (en) * 2016-09-23 2019-09-12 Devan Chemicals Textile coating composition
US11952510B2 (en) * 2016-09-23 2024-04-09 Devan Chemicals Textile coating composition
US11470505B2 (en) * 2019-08-30 2022-10-11 Parallel Wireless, Inc. Support for linking of packet detection rules (PDR) for optimizing throughput of combined serving gateway (SGW)/packet gateway (PGW) architecture

Also Published As

Publication number Publication date
EP3127594A1 (de) 2017-02-08
US20190184317A1 (en) 2019-06-20
US10610814B2 (en) 2020-04-07
EP3127594A4 (de) 2017-12-06
EP3127594B1 (de) 2018-11-28
JP6249537B2 (ja) 2017-12-20
WO2015151168A1 (ja) 2015-10-08
JPWO2015151168A1 (ja) 2017-04-13

Similar Documents

Publication Publication Date Title
US10610814B2 (en) Air filter material
JP2022046702A (ja) 積層体の製造方法および積層体
JP5688012B2 (ja) 積層不織布
KR100452179B1 (ko) 정밀도가높은실린더형필터
JP6102932B2 (ja) ポリフェニレンスルフィド複合繊維および不織布
JP5082365B2 (ja) フィルター用不織布
KR20200014743A (ko) 필터용 스펀본드 부직포 및 그의 제조 방법
JPWO2020004007A1 (ja) フィルター用スパンボンド不織布およびその製造方法
JP6133035B2 (ja) 静電フィルター
JP6095461B2 (ja) ポリエステル積層不織布およびその製造方法
JP6278792B2 (ja) 自動車エンジン用濾材並びにその製造方法
JP3767502B2 (ja) フィルター基材およびフィルター
JP6201558B2 (ja) ポリフェニレンスルフィド繊維および不織布
JP2001248056A (ja) 複合長繊維不織布およびそれからなるフィルター
JP3970624B2 (ja) 差別化シートおよびその製造方法
JPH01201566A (ja) 嵩高スパンボンド不織布
WO2019181827A1 (ja) 長繊維不織布およびそれを用いたフィルター補強材
JPH07207566A (ja) 積層不織布及びその製造方法
JP2015193955A (ja) 浮き出し模様を持つ三層構造不織布及びその製造方法
WO2014171042A1 (ja) タフトカーペット一次基布
JP2006182838A (ja) 通気性シート状接着材及びその製造方法
JP2007118229A (ja) 包装材
JP6102141B2 (ja) ポリフェニレンスルフィド繊維不織布
JP2004275934A (ja) 集塵用濾過材
JP6591884B2 (ja) 嵩高性積層不織布

Legal Events

Date Code Title Description
AS Assignment

Owner name: UNITIKA LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:KIHARA, YUKIHIRO;REEL/FRAME:039880/0557

Effective date: 20160831

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION