US20160086851A1 - Hybrid wafer dicing approach using an adaptive optics-controlled laser scribing process and plasma etch process - Google Patents
Hybrid wafer dicing approach using an adaptive optics-controlled laser scribing process and plasma etch process Download PDFInfo
- Publication number
- US20160086851A1 US20160086851A1 US14/490,598 US201414490598A US2016086851A1 US 20160086851 A1 US20160086851 A1 US 20160086851A1 US 201414490598 A US201414490598 A US 201414490598A US 2016086851 A1 US2016086851 A1 US 2016086851A1
- Authority
- US
- United States
- Prior art keywords
- mask
- semiconductor wafer
- laser
- integrated circuits
- adaptive optics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- 1) Field
- Embodiments of the present invention pertain to the field of semiconductor processing and, in particular, to methods of dicing semiconductor wafers, each wafer having a plurality of integrated circuits thereon.
- 2) Description of Related Art
- In semiconductor wafer processing, integrated circuits are formed on a wafer (also referred to as a substrate) composed of silicon or other semiconductor material. In general, layers of various materials which are either semiconducting, conducting or insulating are utilized to form the integrated circuits. These materials are doped, deposited and etched using various well-known processes to form integrated circuits. Each wafer is processed to form a large number of individual regions containing integrated circuits known as dice.
- Following the integrated circuit formation process, the wafer is “diced” to separate the individual die from one another for packaging or for use in an unpackaged form within larger circuits. The two main techniques that are used for wafer dicing are scribing and sawing. With scribing, a diamond tipped scribe is moved across the wafer surface along pre-formed scribe lines. These scribe lines extend along the spaces between the dice. These spaces are commonly referred to as “streets.” The diamond scribe forms shallow scratches in the wafer surface along the streets. Upon the application of pressure, such as with a roller, the wafer separates along the scribe lines. The breaks in the wafer follow the crystal lattice structure of the wafer substrate. Scribing can be used for wafers that are about 10 mils (thousandths of an inch) or less in thickness. For thicker wafers, sawing is presently the preferred method for dicing.
- With sawing, a diamond tipped saw rotating at high revolutions per minute contacts the wafer surface and saws the wafer along the streets. The wafer is mounted on a supporting member such as an adhesive film stretched across a film frame and the saw is repeatedly applied to both the vertical and horizontal streets. One problem with either scribing or sawing is that chips and gouges can form along the severed edges of the dice. In addition, cracks can form and propagate from the edges of the dice into the substrate and render the integrated circuit inoperative. Chipping and cracking are particularly a problem with scribing because only one side of a square or rectangular die can be scribed in the <110> direction of the crystalline structure. Consequently, cleaving of the other side of the die results in a jagged separation line. Because of chipping and cracking, additional spacing is required between the dice on the wafer to prevent damage to the integrated circuits, e.g., the chips and cracks are maintained at a distance from the actual integrated circuits. As a result of the spacing requirements, not as many dice can be formed on a standard sized wafer and wafer real estate that could otherwise be used for circuitry is wasted. The use of a saw exacerbates the waste of real estate on a semiconductor wafer. The blade of the saw is approximate 15 microns thick. As such, to insure that cracking and other damage surrounding the cut made by the saw does not harm the integrated circuits, three to five hundred microns often must separate the circuitry of each of the dice. Furthermore, after cutting, each die requires substantial cleaning to remove particles and other contaminants that result from the sawing process.
- Plasma dicing has also been used, but may have limitations as well. For example, one limitation hampering implementation of plasma dicing may be cost. A standard lithography operation for patterning resist may render implementation cost prohibitive. Another limitation possibly hampering implementation of plasma dicing is that plasma processing of commonly encountered metals (e.g., copper) in dicing along streets can create production issues or throughput limits.
- Embodiments of the present invention include methods of, and apparatuses for, dicing semiconductor wafers.
- In an embodiment, a method of dicing a semiconductor wafer having a plurality of integrated circuits involves forming a mask above the semiconductor wafer, the mask composed of a layer covering and protecting the integrated circuits. The mask is then patterned with an adaptive optics-controlled laser scribing process to provide a patterned mask with gaps, exposing regions of the semiconductor wafer between the integrated circuits. The semiconductor wafer is then plasma etched through the gaps in the patterned mask to singulate the integrated circuits.
- In another embodiment, a method of dicing a semiconductor wafer including a plurality of integrated circuits involves laser scribing the semiconductor wafer with an adaptive optics-controlled laser scribing process to singulate the integrated circuits.
- In another embodiment, a system for dicing a semiconductor wafer having a plurality of integrated circuits includes a factory interface. A laser scribe apparatus is coupled with the factory interface and houses a laser beam generator and adaptive optics. A plasma etch chamber is coupled with the factory interface.
-
FIG. 1 is a Flowchart representing operations in a method of dicing a semiconductor wafer including a plurality of integrated circuits, in accordance with an embodiment of the present invention. -
FIG. 2A illustrates a cross-sectional view of a semiconductor wafer including a plurality of integrated circuits during performing of a method of dicing the semiconductor wafer, corresponding tooperation 102 of the Flowchart ofFIG. 1 , in accordance with an embodiment of the present invention. -
FIG. 2B illustrates a cross-sectional view of a semiconductor wafer including a plurality of integrated circuits during performing of a method of dicing the semiconductor wafer, corresponding tooperation 104 of the Flowchart ofFIG. 1 , in accordance with an embodiment of the present invention. -
FIG. 2C illustrates a cross-sectional view of a semiconductor wafer including a plurality of integrated circuits during performing of a method of dicing the semiconductor wafer, corresponding tooperation 108 of the Flowchart ofFIG. 1 , in accordance with an embodiment of the present invention. -
FIG. 3 is a schematic illustration of a laser process or assembly for controlling a laser scribing process with adaptive optics, in accordance with an embodiment of the present invention. -
FIG. 4 illustrates the effects of using a laser pulse width in the femtosecond range, picoseconds range, and nanosecond range, in accordance with an embodiment of the present invention. -
FIG. 5 illustrates a cross-sectional view of a stack of materials that may be used in a street region of a semiconductor wafer or substrate, in accordance with an embodiment of the present invention. -
FIGS. 6A-6D illustrate cross-sectional views of various operations in a method of dicing a semiconductor wafer, in accordance with an embodiment of the present invention. -
FIG. 7 illustrates a block diagram of a tool layout for laser and plasma dicing of wafers or substrates, in accordance with an embodiment of the present invention. -
FIG. 8 illustrates a block diagram of an exemplary computer system, in accordance with an embodiment of the present invention. - Methods of dicing semiconductor wafers, each wafer having a plurality of integrated circuits thereon, are described. In the following description, numerous specific details are set forth, such as adaptive optics-controlled laser scribing approaches and plasma etching conditions and material regimes, in order to provide a thorough understanding of embodiments of the present invention. It will be apparent to one skilled in the art that embodiments of the present invention may be practiced without these specific details. In other instances, well-known aspects, such as integrated circuit fabrication, are not described in detail in order to not unnecessarily obscure embodiments of the present invention. Furthermore, it is to be understood that the various embodiments shown in the Figures are illustrative representations and are not necessarily drawn to scale.
- A hybrid wafer or substrate dicing process involving an initial laser scribe and subsequent plasma etch may be implemented for die singulation. The laser scribe process may be used to cleanly remove a mask layer, organic and inorganic dielectric layers, and device layers. The laser etch process may then be terminated upon exposure of, or partial etch of, the wafer or substrate. The plasma etch portion of the dicing process may then be employed to etch through the bulk of the wafer or substrate, such as through bulk single crystalline silicon, to yield die or chip singulation or dicing. More specifically, one or more embodiments are directed to implementing an adaptive optics-controlled laser scribing process for, e.g., dicing applications.
- Generally, in accordance with one or more embodiments described herein, adaptive optics control is implemented for improving laser scribing processing in hybrid laser die singulation. Particular embodiments may be directed to initial femtosecond laser scribing and subsequent plasma etch hybrid technology for dicing wafers. For example, such a hybrid technology combining laser scribing and plasma etching can be advantageous in enabling precise thin semiconductor device die cutting from a silicon (Si) wafer. In one or more embodiment, an ultra-short laser and related optics are used for achieving the fine scribing of die streets to ultimately singulate the substrate wafer with a plasma etching process. By manipulating the optics, beam qualities such as depth of focus, laser beam spot size, laser beam shape, etc. are determined and are controllable. By contrast, most conventional optical system use well-specified optics, such as mirrors, lenses, etc. and a system specification is typically defined by one fixed configuration for the mirrors, lenses, etc.
- To provide further context, in a hybrid wafer or substrate dicing process involving an initial laser scribe and subsequent plasma etch, a femtosecond laser may be applied to remove the mask and device layers on the dicing street until the silicon substrate is exposed. A plasma etch follows to separate dies. One quality item or issue pertains to the die sidewall smoothness. The die sidewall can have a scallop pattern both along the die thickness and along the laser scribing direction. The depth-wise scallop pattern may be a result of iterative Bosch etch processing. Typically, the roughness is at the sub-micron level. Horizontal scalloping along the laser scribing direction can be caused by an imperfect spot overlap and a non-uniform distribution of non-silicon materials (e.g., metals, dielectrics, etc.) on the dicing street. By comparison, a roughness for a horizontal type of scallop can be on the order of a few microns.
- On the aspect of appearance, any imperfect opening of a mask layer can be inherited by the resulting sidewall during the subsequent etch process. Imperfections in sidewall smoothness (that is, sidewall roughness) can potentially reduce die strength, and can also provide a cosmetic issue that affects market penetration of the resulting product. Since the ablation threshold of each material is different, applying a laser beam of constant irradiation fluence inevitably causes different ablation spot size at different locations when material and/or pattern geometry varies. Process optimization may reduce the kerf width variation to some extent but total elimination can be difficult.
- However, in accordance with embodiments described herein, the spot overlap induced kerf width variation that causes the horizontal scallop can be significantly improved.
- More specifically, in accordance with one or more embodiments described herein, adaptive optics (such as a deformable mirror) can involve a change of the surface curvature of an optical component, e.g., by controlling with piezoelectric actuators. The spot size and depth of focus of laser scribing process may be adjusted in this way within a laser scribing system. In one such embodiment, the laser scribing process based on adaptive optics can be implemented to obtain the required roughness and smoothness control of a scribed trench. In addition, the kerf width may be controlled by adjusting the laser spot size. In additional embodiment, by merging with other laser beam control, such as spatial and temporal control of a laser beam, the synergetic effect on a scribing process can be achieved to provide high quality productivity.
- In accordance with one or more embodiments described herein, advantages of implementing an adaptive optics-controlled laser scribing process may include one or more of, (1) the ability to precisely scribe the mask coating/device layers on the silicon (Si) substrate, (2) the ability to readily control the laser scribing profile and shape, (3) the ability to enable the roughness control of a scribed section on the Si substrate, (4) the ability to obtain the smoothness of scribed sidewalls by adjusting the depth of focus of the laser beam, (5) the ability to enable kerf width control by tuning the laser spot size, (6) the ability to achieve multiple beneficial effects by combining adaptive optics with spatial and temporal laser control processes, (7) the ability to produce a uniform and effective etching process, and/or (8) the ability to achieve a uniform die cut by plasma etching following a regularly flattened surface cut from the laser scribing process. One or more embodiments of the invention may be applicable to improving the surface roughness and sidewall smoothness of the final singulated product.
- In an aspect of the present invention, a combination of an adaptive optics-controlled laser scribing process with a plasma etching process may be used to dice a semiconductor wafer into singulated integrated circuits.
FIG. 1 is aFlowchart 100 representing operations in a method of dicing a semiconductor wafer including a plurality of integrated circuits, in accordance with an embodiment of the present invention.FIGS. 2A-2C illustrate cross-sectional views of a semiconductor wafer including a plurality of integrated circuits during performing of a method of dicing the semiconductor wafer, corresponding to operations ofFlowchart 100, in accordance with an embodiment of the present invention. - Referring to
operation 102 ofFlowchart 100, and correspondingFIG. 2A , amask 202 is formed above a semiconductor wafer orsubstrate 204. Themask 202 is composed of a layer covering and protectingintegrated circuits 206 formed on the surface ofsemiconductor wafer 204. Themask 202 also covers interveningstreets 207 formed between each of theintegrated circuits 206. - In accordance with an embodiment of the present invention, forming the
mask 202 includes forming a layer such as, but not limited to, a photo-resist layer or an I-line patterning layer. For example, a polymer layer such as a photo-resist layer may be composed of a material otherwise suitable for use in a lithographic process. In one embodiment, the photo-resist layer is composed of a positive photo-resist material such as, but not limited to, a 248 nanometer (nm) resist, a 193 nm resist, a 157 nm resist, an extreme ultra-violet (EUV) resist, or a phenolic resin matrix with a diazonaphthoquinone sensitizer. In another embodiment, the photo-resist layer is composed of a negative photo-resist material such as, but not limited to, poly-cis-isoprene and poly-vinyl-cinnamate. - In another embodiment, forming the
mask 202 involves forming a layer deposited in a plasma deposition process. For example, in one such embodiment, themask 202 is composed of a plasma deposited Teflon or Teflon-like (polymeric CF2) layer. In a specific embodiment, the polymeric CF2 layer is deposited in a plasma deposition process involving the gas C4F8. - In another embodiment, forming the
mask 202 involves forming a water-soluble mask layer. In an embodiment, the water-soluble mask layer is readily dissolvable in an aqueous media. For example, in one embodiment, the water-soluble mask layer is composed of a material that is soluble in one or more of an alkaline solution, an acidic solution, or in deionized water. In an embodiment, the water-soluble mask layer maintains its water solubility upon exposure to a heating process, such as heating approximately in the range of 50-160 degrees Celsius. For example, in one embodiment, the water-soluble mask layer is soluble in aqueous solutions following exposure to chamber conditions used in a laser and plasma etch singulation process. In one embodiment, the water-soluble mask layer is composed of a material such as, but not limited to, polyvinyl alcohol, polyacrylic acid, dextran, polymethacrylic acid, polyethylene imine, or polyethylene oxide. In a specific embodiment, the water-soluble mask layer has an etch rate in an aqueous solution approximately in the range of 1-15 microns per minute and, more particularly, approximately 1.3 microns per minute. - In another embodiment, forming the
mask 202 involves forming a UV-curable mask layer. In an embodiment, the mask layer has a susceptibility to UV light that reduces an adhesiveness of the UV-curable layer by at least approximately 80%. In one such embodiment, the UV layer is composed of polyvinyl chloride or an acrylic-based material. In an embodiment, the UV-curable layer is composed of a material or stack of materials with an adhesive property that weakens upon exposure to UV light. In an embodiment, the UV-curable adhesive film is sensitive to approximately 365 nm UV light. In one such embodiment, this sensitivity enables use of LED light to perform a cure. - In an embodiment, semiconductor wafer or
substrate 204 is composed of a material suitable to withstand a fabrication process and upon which semiconductor processing layers may suitably be disposed. For example, in one embodiment, semiconductor wafer orsubstrate 204 is composed of a group IV-based material such as, but not limited to, crystalline silicon, germanium or silicon/germanium. In a specific embodiment, providingsemiconductor wafer 204 includes providing a monocrystalline silicon substrate. In a particular embodiment, the monocrystalline silicon substrate is doped with impurity atoms. In another embodiment, semiconductor wafer orsubstrate 204 is composed of a III-V material such as, e.g., a III-V material substrate used in the fabrication of light emitting diodes (LEDs). - In an embodiment, semiconductor wafer or
substrate 204 has disposed thereon or therein, as a portion of theintegrated circuits 206, an array of semiconductor devices. Examples of such semiconductor devices include, but are not limited to, memory devices or complimentary metal-oxide-semiconductor (CMOS) transistors fabricated in a silicon substrate and encased in a dielectric layer. A plurality of metal interconnects may be formed above the devices or transistors, and in surrounding dielectric layers, and may be used to electrically couple the devices or transistors to form theintegrated circuits 206. Materials making up thestreets 207 may be similar to or the same as those materials used to form theintegrated circuits 206. For example,streets 207 may be composed of layers of dielectric materials, semiconductor materials, and metallization. In one embodiment, one or more of thestreets 207 includes test devices similar to the actual devices of theintegrated circuits 206. - Referring to
operation 104 ofFlowchart 100, and correspondingFIG. 2B , themask 202 is patterned with an adaptive optics-controlled laser scribing process to provide apatterned mask 208 withgaps 210, exposing regions of the semiconductor wafer orsubstrate 204 between theintegrated circuits 206. As such, the laser scribing process is used to remove the material of thestreets 207 originally formed between theintegrated circuits 206. In accordance with an embodiment of the present invention, patterning themask 202 with the adaptive optics-controlled laser scribing process includes formingtrenches 212 partially into the regions of thesemiconductor wafer 204 between theintegrated circuits 206, as depicted inFIG. 2B . - As an example,
FIG. 3 is a schematic illustration of a laser process or assembly for controlling a laser scribing process with adaptive optics, in accordance with an embodiment of the present invention. - Referring to
FIG. 3 , alaser beam 304 is generated from a laser generator, such as a femtosecond (Fs) oscillatorlaser beam source 302. Thelaser beam 304 generated is transmitted through anadaptive optics assembly 306. Theadaptive optics assembly 306 may include a deformable mirror for laser beam reflection, a moveable lens for laser beam transmission, or both. Thelaser beam 308 output from theadaptive optics assembly 306 may then be directed to a work surface (such as a semiconductor wafer 312), or may first be transmitted through alens 310 and then onto the work surface, as is depicted inFIG. 3 . - In an embodiment, with respect to a laser scribing assembly, the laser beam assembly includes the
laser beam generator 302 and theadaptive optics assembly 306. In one such embodiment, theadaptive optics assembly 306 is configured to adjust a depth of focus of alaser beam 304 from thelaser beam generator 302 by tuning a deformable mirror surface curvature to change a mirror surface curvature with one or more piezoelectric actuators of theadaptive optics assembly 306. In one embodiment, theadaptive optics assembly 306 is configured to adjust a spot size of alaser beam 304 from thelaser beam generator 302 by changing a lens position with one or more piezoelectric actuators of theadaptive optics assembly 306 to tune a divergence of thelaser beam 308. In an embodiment, thelaser beam generator 302 is configured to generate a femtosecond-based laser beam. - In another embodiment, with respect to a laser scribing process, laser scribing of a semiconductor wafer is performed using an adaptive optics-controlled laser scribing process. In one such embodiment, the scribing involves adjusting a depth of focus of a
laser beam 304/308 by tuning a deformable mirror surface curvature. In a specific such embodiment, the deformable mirror surface curvature is tuned by changing a mirror surface curvature with one or more piezoelectric actuators. In another embodiment, the scribing involves adjusting a spot size of alaser beam 304/308 by tuning a divergence of the laser beam. In a specific such embodiment, the divergence of the laser beam is tuned by changing a position of a lens of an adaptive optics assembly with one or more piezoelectric actuators. - Perhaps more generally, then, embodiments described herein may involve the implementation of adaptive optics to adjust the depth of focus, laser beam spot size and to achieve fine roughness and smoothness control of a laser scribed trench structure. Depth of focus may be adjusted by tuning a deformable mirror surface curvature. The spot size may be controlled by tuning the laser beam divergence (e.g., by altering the positioning of one or more lens). Precise control is available using piezoelectric actuators which may have a step size on the order of 1 nanometer. Adaptive optics may be implemented as a real-time change during a scribing process, or between scribing processes or different work pieces.
- Perhaps more generally, adaptive optics can be viewed as a technology for improving the performance of optical systems by reducing the effect of wave front distortions. The deformations of an incoming wave front can be corrected by deforming a mirror in order to compensate for the distortion. Adaptive optics can also be implemented to reduce optical aberrations. Adaptive optics works by measuring the distortions in a wave front and compensating for them with a device that corrects those errors such as a deformable mirror or a liquid crystal array. Adaptive optics is not to be confused with active optics, which works on a longer timescale to correct a primary mirror geometry.
- In an embodiment, a femtosecond-based laser is used as a source for an adaptive optics-controlled laser scribing process. For example, in an embodiment, a laser with a wavelength in the visible spectrum plus the ultra-violet (UV) and infra-red (IR) ranges (totaling a broadband optical spectrum) is used to provide a femtosecond-based laser, i.e., a laser with a pulse width on the order of the femtosecond (10−15 seconds). In one embodiment, ablation is not, or is essentially not, wavelength dependent and is thus suitable for complex films such as films of the
mask 202, thestreets 207 and, possibly, a portion of the semiconductor wafer orsubstrate 204. -
FIG. 4 illustrates the effects of using a laser pulse width in the femtosecond range, picosecond range, and nanosecond range, in accordance with an embodiment of the present invention. Referring toFIG. 4 , by using a laser beam profile with contributions from the femtosecond range, heat damage issues are mitigated or eliminated (e.g., minimal to no damage 502C with femtosecond processing of a via 500C) versus longer pulse widths (e.g., significant damage 502A with nanosecond processing of a via 500A). The elimination or mitigation of damage during formation of via 500C may be due to a lack of low energy recoupling (as is seen for picosecond-based laser ablation of 500B/502B) or thermal equilibrium (as is seen for nanosecond-based laser ablation), as depicted inFIG. 4 . - Laser parameters selection, such as beam profile, may be critical to developing a successful laser scribing and dicing process that minimizes chipping, microcracks and delamination in order to achieve clean laser scribe cuts. The cleaner the laser scribe cut, the smoother an etch process that may be performed for ultimate die singulation. In semiconductor device wafers, many functional layers of different material types (e.g., conductors, insulators, semiconductors) and thicknesses are typically disposed thereon. Such materials may include, but are not limited to, organic materials such as polymers, metals, or inorganic dielectrics such as silicon dioxide and silicon nitride.
- A street between individual integrated circuits disposed on a wafer or substrate may include the similar or same layers as the integrated circuits themselves. For example,
FIG. 5 illustrates a cross-sectional view of a stack of materials that may be used in a street region of a semiconductor wafer or substrate, in accordance with an embodiment of the present invention. - Referring to
FIG. 5 , astreet region 500 includes thetop portion 502 of a silicon substrate, a firstsilicon dioxide layer 504, a firstetch stop layer 506, a first low K dielectric layer 508 (e.g., having a dielectric constant of less than the dielectric constant of 4.0 for silicon dioxide), a secondetch stop layer 510, a second low Kdielectric layer 512, a thirdetch stop layer 514, an undoped silica glass (USG)layer 516, a secondsilicon dioxide layer 518, and a layer of photo-resist 520, with relative thicknesses depicted.Copper metallization 522 is disposed between the first and third etch stop layers 506 and 514 and through the secondetch stop layer 510. In a specific embodiment, the first, second and third etch stop layers 506, 510 and 514 are composed of silicon nitride, while low Kdielectric layers - Under conventional laser irradiation (such as nanosecond-based irradiation), the materials of
street 500 behave quite differently in terms of optical absorption and ablation mechanisms. For example, dielectrics layers such as silicon dioxide, is essentially transparent to all commercially available laser wavelengths under normal conditions. By contrast, metals, organics (e.g., low K materials) and silicon can couple photons very easily, particularly in response to nanosecond-based irradiation. In an embodiment, an adaptive optics-controlled profile laser scribing process is used to pattern a layer of silicon dioxide, a layer of low K material, and a layer of copper by ablating the layer of silicon dioxide prior to ablating the layer of low K material and the layer of copper. - In case that the adaptive optics-controlled laser beam is a femtosecond-based laser beam, in an embodiment, suitable femtosecond-based laser processes are characterized by a high peak intensity (irradiance) that usually leads to nonlinear interactions in various materials. In one such embodiment, the femtosecond laser sources have a pulse width approximately in the range of 10 femtoseconds to 500 femtoseconds, although preferably in the range of 100 femtoseconds to 400 femtoseconds. In one embodiment, the femtosecond laser sources have a wavelength approximately in the range of 1570 nanometers to 200 nanometers, although preferably in the range of 540 nanometers to 250 nanometers. In one embodiment, the laser and corresponding optical system provide a focal spot at the work surface approximately in the range of 2 microns to 30 microns, though preferably approximately in the range of 5 microns to 10 microns or between 10-20 microns.
- In an embodiment, the laser source has a pulse repetition rate approximately in the range of 200 kHz to 10 MHz, although preferably approximately in the range of 500 kHz to 5 MHz. In an embodiment, the laser source delivers pulse energy at the work surface approximately in the range of 0.5 uJ to 100 uJ, although preferably approximately in the range of 1 uJ to 15 uJ. In an embodiment, the laser scribing process runs along a work piece surface at a speed approximately in the range of 50 mm/sec to 5 m/sec, although preferably approximately in the range of 300 mm/sec to 2 m/sec.
- The scribing process may be run in single pass only, or in multiple passes, but, in an embodiment, preferably 1-2 passes. In one embodiment, the scribing depth in the work piece is approximately in the range of 5 microns to 50 microns deep, preferably approximately in the range of 10 microns to 20 microns deep. In an embodiment, the kerf width of the laser beam generated is approximately in the range of 2 microns to 15 microns, although in silicon wafer scribing/dicing preferably approximately in the range of 6 microns to 10 microns, measured at the device/silicon interface.
- Laser parameters may be selected with benefits and advantages such as providing sufficiently high laser intensity to achieve ionization of inorganic dielectrics (e.g., silicon dioxide) and to minimize delamination and chipping caused by underlayer damage prior to direct ablation of inorganic dielectrics. Also, parameters may be selected to provide meaningful process throughput for industrial applications with precisely controlled ablation width (e.g., kerf width) and depth. In an embodiment, an adaptive optics-controlled laser scribing process is suitable to provide such advantages.
- It is to be appreciated that the dicing or singulation process could be stopped after the above described laser scribing in a case that the laser scribing is used to pattern the mask as well as to scribe fully through the wafer or substrate in order to singulate the dies. Accordingly, further singulation processing would not be required in such a case. However, the following embodiments may be considered in cases where laser scribing alone is not implemented for total singulation.
- Referring now to
optional operation 106 ofFlowchart 100, an intermediate post mask-opening cleaning operation is performed. In an embodiment, the post mask-opening cleaning operation is a plasma-based cleaning process. In a first example, as described below, the plasma-based cleaning process is reactive to the regions of thesubstrate 204 exposed by thegaps 210. In the case of a reactive plasma-based cleaning process, the cleaning process itself may form or extendtrenches 212 in thesubstrate 204 since the reactive plasma-based cleaning operation is at least somewhat of an etchant for thesubstrate 204. In a second, different, example, as is also described below, the plasma-based cleaning process is non-reactive to the regions of thesubstrate 204 exposed by thegaps 210. - In accordance with a first embodiment, the plasma-based cleaning process is reactive to exposed regions of the
substrate 204 in that the exposed regions are partially etched during the cleaning process. In one such embodiment, Ar or another non-reactive gas (or the mix) is combined with SF6 for a highly-biased plasma treatment for cleaning of scribed openings. The plasma treatment using mixed gases Ar+SF6 under high-bias power is performed for bombarding mask-opened regions to achieve cleaning of the mask-opened regions. In the reactive breakthrough process, both physical bombardment from Ar and SF6 along with chemical etching due to SF6 and F-ions contribute to cleaning of mask-opened regions. The approach may be suitable for photoresist or plasma-deposited Teflon masks 202, where breakthrough treatment leads to fairly uniform mask thickness reduction and a gentle Si etch. Such a breakthrough etch process, however, may not be best suited for water soluble mask materials. - In accordance with a second embodiment, the plasma-based cleaning process is non-reactive to exposed regions of the
substrate 204 in that the exposed regions are not or only negligible etched during the cleaning process. In one such embodiment, only non-reactive gas plasma cleaning is used. For example, Ar or another non-reactive gas (or the mix) is used to perform a highly-biased plasma treatment both for mask condensation and cleaning of scribed openings. The approach may be suitable for water-soluble masks or for thinner plasma-depositedTeflon 202. In another such embodiment, separate mask condensation and scribed trench cleaning operations are used, e.g., an Ar or non-reactive gas (or the mix) highly-biased plasma treatment for mask condensation is first performed, and then an Ar+SF6 plasma cleaning of a laser scribed trench is performed. This embodiment may be suitable for cases where Ar-cleaning is not sufficient for trench cleaning due to too thick of a mask material. Cleaning efficiency is improved for thinner masks, but mask etch rate is much lower, with almost no consumption in a subsequent deep silicon etch process. In yet another such embodiment, three-operation cleaning is performed: (a) Ar or non-reactive gas (or the mix) highly-biased plasma treatment for mask condensation, (b) Ar+SF6 highly-biased plasma cleaning of laser scribed trenches, and (c) Ar or non-reactive gas (or the mix) highly-biased plasma treatment for mask condensation. In accordance with another embodiment of the present invention, a plasma cleaning operation involves first use of a reactive plasma cleaning treatment, such as described above in the first aspect ofoperation 106. The reactive plasma cleaning treatment is then followed by a non-reactive plasma cleaning treatment such as described in association with the second aspect ofoperation 106. - Referring to
operation 108 ofFlowchart 100, and correspondingFIG. 2C , thesemiconductor wafer 204 is etched through thegaps 210 in the patternedmask 208 to singulate theintegrated circuits 206. In accordance with an embodiment of the present invention, etching thesemiconductor wafer 204 includes ultimately etching entirely throughsemiconductor wafer 204, as depicted inFIG. 2C , by etching thetrenches 212 initially formed with the adaptive optics-controlled laser scribing process. - In accordance with an embodiment of the present invention, the resulting roughness of mask opening from laser scribing can impact die sidewall quality resulting from the subsequent formation of a plasma etched trench. Lithographically opened masks often have smooth profiles, leading to smooth corresponding sidewalls of a plasma etched trench. By contrast, a conventional laser opened mask can have a very rough profile along a scribing direction if improper laser process parameters are selected (such as spot overlap, leading to rough sidewall of plasma etched trench horizontally). Although the surface roughness can be smoothened by additional plasma processes, there is a cost and throughput hit to remedying such issues. Accordingly, embodiments described herein may be advantageous in providing a smoother scribing process from the laser scribing portion of the singulation process.
- In an embodiment, etching the
semiconductor wafer 204 includes using a plasma etching process. In one embodiment, a through-silicon via type etch process is used. For example, in a specific embodiment, the etch rate of the material ofsemiconductor wafer 204 is greater than 25 microns per minute. An ultra-high-density plasma source may be used for the plasma etching portion of the die singulation process. An example of a process chamber suitable to perform such a plasma etch process is the Applied Centura® Silvia™ Etch system available from Applied Materials of Sunnyvale, Calif., USA. The Applied Centura® Silvia™ Etch system combines the capacitive and inductive RF coupling, which gives much more independent control of the ion density and ion energy than was possible with the capacitive coupling only, even with the improvements provided by magnetic enhancement. This combination enables effective decoupling of the ion density from ion energy, so as to achieve relatively high density plasmas without the high, potentially damaging, DC bias levels, even at very low pressures. This results in an exceptionally wide process window. However, any plasma etch chamber capable of etching silicon may be used. In an exemplary embodiment, a deep silicon etch is used to etch a single crystalline silicon substrate orwafer 204 at an etch rate greater than approximately 40% of conventional silicon etch rates while maintaining essentially precise profile control and virtually scallop-free sidewalls. In a specific embodiment, a through-silicon via type etch process is used. The etch process is based on a plasma generated from a reactive gas, which generally a fluorine-based gas such as SF6, C4F8, CHF3, XeF2, or any other reactant gas capable of etching silicon at a relatively fast etch rate. In an embodiment, themask layer 208 is removed after the singulation process, as depicted inFIG. 2C . In another embodiment, the plasma etching operation described in association withFIG. 2C employs a conventional Bosch-type dep/etch/dep process to etch through thesubstrate 204. Generally, a Bosch-type process consists of three sub-operations: deposition, a directional bombardment etch, and isotropic chemical etch which is run through many iterations (cycles) until silicon is etched through. - Accordingly, referring again to Flowchart 100 and
FIGS. 2A-2C , wafer dicing may be preformed by initial ablation using an adaptive optics-controlled laser scribing process to ablate through a mask layer, through wafer streets (including metallization), and partially into a silicon substrate. Die singulation may then be completed by subsequent through-silicon deep plasma etching. A specific example of a materials stack for dicing is described below in association withFIGS. 6A-6D , in accordance with an embodiment of the present invention. - Referring to
FIG. 6A , a materials stack for hybrid laser ablation and plasma etch dicing includes amask layer 602, adevice layer 604, and asubstrate 606. The mask layer, device layer, and substrate are disposed above a die attachfilm 608 which is affixed to abacking tape 610. In an embodiment, themask layer 602 is a water soluble layer such as the water soluble layers described above in association withmask 202. Thedevice layer 604 includes an inorganic dielectric layer (such as silicon dioxide) disposed above one or more metal layers (such as copper layers) and one or more low K dielectric layers (such as carbon-doped oxide layers). Thedevice layer 604 also includes streets arranged between integrated circuits, the streets including the same or similar layers to the integrated circuits. Thesubstrate 706 is a bulk single-crystalline silicon substrate. - In an embodiment, the bulk single-
crystalline silicon substrate 606 is thinned from the backside prior to being affixed to the die attachfilm 608. The thinning may be performed by a backside grind process. In one embodiment, the bulk single-crystalline silicon substrate 606 is thinned to a thickness approximately in the range of 50-100 microns. It is important to note that, in an embodiment, the thinning is performed prior to a laser ablation and plasma etch dicing process. In an embodiment, the photo-resistlayer 602 has a thickness of approximately 5 microns and thedevice layer 604 has a thickness approximately in the range of 2-3 microns. In an embodiment, the die attach film 608 (or any suitable substitute capable of bonding a thinned or thin wafer or substrate to the backing tape 610) has a thickness of approximately 20 microns. - Referring to
FIG. 6B , themask 602, thedevice layer 604 and a portion of thesubstrate 606 are patterned with an adaptive optics-controlledlaser scribing process 612 to formtrenches 614 in thesubstrate 606. Referring toFIG. 6C , a through-silicon deep plasma etch process 616 is used to extend thetrench 614 down to the die attachfilm 608, exposing the top portion of the die attachfilm 608 and singulating thesilicon substrate 606. Thedevice layer 604 is protected by themask layer 602 during the through-silicon deep plasma etch process 616. - Referring to
FIG. 6D , the singulation process may further include patterning the die attachfilm 608, exposing the top portion of thebacking tape 610 and singulating the die attachfilm 608. In an embodiment, the die attach film is singulated by a laser process or by an etch process. Further embodiments may include subsequently removing the singulated portions of substrate 606 (e.g., as individual integrated circuits) from thebacking tape 610. In one embodiment, the singulated die attachfilm 608 is retained on the back sides of the singulated portions ofsubstrate 606. Other embodiments may include removing themask layer 602 from thedevice layer 604. In an alternative embodiment, in the case thatsubstrate 606 is thinner than approximately 50 microns, the adaptive optics-controlledlaser scribing process 612 is used to completelysingulate substrate 606 without the use of an additional plasma process. - A single process tool may be configured to perform many or all of the operations in a hybrid adaptive optics-controlled laser beam ablation and plasma etch singulation process. For example,
FIG. 7 illustrates a block diagram of a tool layout for laser and plasma dicing of wafers or substrates, in accordance with an embodiment of the present invention. - Referring to
FIG. 7 , aprocess tool 700 includes a factory interface 702 (FI) having a plurality ofload locks 704 coupled therewith. Acluster tool 706 is coupled with thefactory interface 702. Thecluster tool 706 includes one or more plasma etch chambers, such asplasma etch chamber 708. Alaser scribe apparatus 710 is also coupled to thefactory interface 802. The overall footprint of theprocess tool 700 may be, in one embodiment, approximately 3500 millimeters (3.5 meters) by approximately 3800 millimeters (3.8 meters), as depicted inFIG. 7 . - In an embodiment, the
laser scribe apparatus 710 houses a laser assembly including a laser beam generator and an adaptive optics assembly. In an embodiment, the adaptive optics assembly is configured to adjust a depth of focus of a laser beam from the laser beam generator by tuning a deformable mirror surface curvature to change a mirror surface curvature with one or more piezoelectric actuators of the adaptive optics assembly. In an embodiment, the adaptive optics assembly is configured to adjust a spot size of a laser beam from the laser beam generator by changing a lens position with one or more piezoelectric actuators of the adaptive optics assembly to tune a divergence of the laser beam. In an embodiment, the laser beam generator is configured to generate a femtosecond-based laser beam. - In an embodiment, the laser is suitable for performing a laser ablation portion of a hybrid laser and etch singulation process, such as the laser ablation processes described above. In one embodiment, a moveable stage is also included in
laser scribe apparatus 710, the moveable stage configured for moving a wafer or substrate (or a carrier thereof) relative to the laser. In a specific embodiment, the laser is also moveable. The overall footprint of thelaser scribe apparatus 710 may be, in one embodiment, approximately 2240 millimeters by approximately 1270 millimeters, as depicted inFIG. 7 . - In an embodiment, the one or more
plasma etch chambers 708 is configured for etching a wafer or substrate through the gaps in a patterned mask to singulate a plurality of integrated circuits. In one such embodiment, the one or moreplasma etch chambers 708 is configured to perform a deep silicon etch process. In a specific embodiment, the one or moreplasma etch chambers 708 is an Applied Centura® Silvia™ Etch system, available from Applied Materials of Sunnyvale, Calif., USA. The etch chamber may be specifically designed for a deep silicon etch used to create singulate integrated circuits housed on or in single crystalline silicon substrates or wafers. In an embodiment, a high-density plasma source is included in theplasma etch chamber 708 to facilitate high silicon etch rates. In an embodiment, more than one etch chamber is included in thecluster tool 706 portion ofprocess tool 700 to enable high manufacturing throughput of the singulation or dicing process. - The
factory interface 702 may be a suitable atmospheric port to interface between an outside manufacturing facility withlaser scribe apparatus 710 andcluster tool 706. Thefactory interface 702 may include robots with arms or blades for transferring wafers (or carriers thereof) from storage units (such as front opening unified pods) into eithercluster tool 706 orlaser scribe apparatus 710, or both. -
Cluster tool 706 may include other chambers suitable for performing functions in a method of singulation. For example, in one embodiment, in place of an additional etch chamber, adeposition chamber 712 is included. Thedeposition chamber 712 may be configured for mask deposition on or above a device layer of a wafer or substrate prior to laser scribing of the wafer or substrate. In one such embodiment, thedeposition chamber 712 is suitable for depositing a photo-resist layer. In another embodiment, in place of an additional etch chamber, a wet/dry station 714 is included. The wet/dry station may be suitable for cleaning residues and fragments, or for removing a mask, subsequent to a laser scribe and plasma etch singulation process of a substrate or wafer. In yet another embodiment, in place of an additional deep silicon etch chamber, a plasma etch chamber is included and is configured for performing a plasma-based cleaning process. In an embodiment, a metrology station is also included as a component ofprocess tool 700. - Embodiments of the present invention may be provided as a computer program product, or software, that may include a machine-readable medium having stored thereon instructions, which may be used to program a computer system (or other electronic devices) to perform a process according to embodiments of the present invention. In one embodiment, the computer system is coupled with
process tool 700 described in association withFIG. 7 . A machine-readable medium includes any mechanism for storing or transmitting information in a form readable by a machine (e.g., a computer). For example, a machine-readable (e.g., computer-readable) medium includes a machine (e.g., a computer) readable storage medium (e.g., read only memory (“ROM”), random access memory (“RAM”), magnetic disk storage media, optical storage media, flash memory devices, etc.), a machine (e.g., computer) readable transmission medium (electrical, optical, acoustical or other form of propagated signals (e.g., infrared signals, digital signals, etc.)), etc. -
FIG. 8 illustrates a diagrammatic representation of a machine in the exemplary form of acomputer system 800 within which a set of instructions, for causing the machine to perform any one or more of the methodologies described herein, may be executed. In alternative embodiments, the machine may be connected (e.g., networked) to other machines in a Local Area Network (LAN), an intranet, an extranet, or the Internet. The machine may operate in the capacity of a server or a client machine in a client-server network environment, or as a peer machine in a peer-to-peer (or distributed) network environment. The machine may be a personal computer (PC), a tablet PC, a set-top box (STB), a Personal Digital Assistant (PDA), a cellular telephone, a web appliance, a server, a network router, switch or bridge, or any machine capable of executing a set of instructions (sequential or otherwise) that specify actions to be taken by that machine. Further, while only a single machine is illustrated, the term “machine” shall also be taken to include any collection of machines (e.g., computers) that individually or jointly execute a set (or multiple sets) of instructions to perform any one or more of the methodologies described herein. - The
exemplary computer system 800 includes aprocessor 802, a main memory 904 (e.g., read-only memory (ROM), flash memory, dynamic random access memory (DRAM) such as synchronous DRAM (SDRAM) or Rambus DRAM (RDRAM), etc.), a static memory 806 (e.g., flash memory, static random access memory (SRAM), etc.), and a secondary memory 818 (e.g., a data storage device), which communicate with each other via abus 830. -
Processor 802 represents one or more general-purpose processing devices such as a microprocessor, central processing unit, or the like. More particularly, theprocessor 802 may be a complex instruction set computing (CISC) microprocessor, reduced instruction set computing (RISC) microprocessor, very long instruction word (VLIW) microprocessor, processor implementing other instruction sets, or processors implementing a combination of instruction sets.Processor 802 may also be one or more special-purpose processing devices such as an application specific integrated circuit (ASIC), a field programmable gate array (FPGA), a digital signal processor (DSP), network processor, or the like. Processor 902 is configured to execute theprocessing logic 826 for performing the operations described herein. - The
computer system 800 may further include anetwork interface device 808. Thecomputer system 800 also may include a video display unit 810 (e.g., a liquid crystal display (LCD), a light emitting diode display (LED), or a cathode ray tube (CRT)), an alphanumeric input device 812 (e.g., a keyboard), a cursor control device 814 (e.g., a mouse), and a signal generation device 816 (e.g., a speaker). - The
secondary memory 818 may include a machine-accessible storage medium (or more specifically a computer-readable storage medium) 832 on which is stored one or more sets of instructions (e.g., software 822) embodying any one or more of the methodologies or functions described herein. Thesoftware 822 may also reside, completely or at least partially, within themain memory 804 and/or within theprocessor 802 during execution thereof by thecomputer system 800, themain memory 804 and theprocessor 802 also constituting machine-readable storage media. Thesoftware 822 may further be transmitted or received over anetwork 820 via thenetwork interface device 808. - While the machine-
accessible storage medium 832 is shown in an exemplary embodiment to be a single medium, the term “machine-readable storage medium” should be taken to include a single medium or multiple media (e.g., a centralized or distributed database, and/or associated caches and servers) that store the one or more sets of instructions. The term “machine-readable storage medium” shall also be taken to include any medium that is capable of storing or encoding a set of instructions for execution by the machine and that cause the machine to perform any one or more of the methodologies of the present invention. The term “machine-readable storage medium” shall accordingly be taken to include, but not be limited to, solid-state memories, and optical and magnetic media. - In accordance with an embodiment of the present invention, a machine-accessible storage medium has instructions stored thereon which cause a data processing system to perform a method of dicing a semiconductor wafer having a plurality of integrated circuits. The method includes forming a mask above the semiconductor wafer, the mask composed of a layer covering and protecting the integrated circuits. The mask is then patterned with an adaptive optics-controlled laser scribing process to provide a patterned mask with gaps, exposing regions of the semiconductor wafer between the integrated circuits. The semiconductor wafer is then plasma etched through the gaps in the patterned mask to singulate the integrated circuits.
- Thus, hybrid wafer dicing approaches using an adaptive optics-controlled laser scribing process and plasma etch process have been disclosed.
Claims (9)