US20150376738A1 - Titanium sheet - Google Patents
Titanium sheet Download PDFInfo
- Publication number
- US20150376738A1 US20150376738A1 US14/764,738 US201414764738A US2015376738A1 US 20150376738 A1 US20150376738 A1 US 20150376738A1 US 201414764738 A US201414764738 A US 201414764738A US 2015376738 A1 US2015376738 A1 US 2015376738A1
- Authority
- US
- United States
- Prior art keywords
- carbon
- titanium sheet
- titanium
- grain boundaries
- mass percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C14/00—Alloys based on titanium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/16—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of other metals or alloys based thereon
- C22F1/18—High-melting or refractory metals or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/16—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of other metals or alloys based thereon
- C22F1/18—High-melting or refractory metals or alloys based thereon
- C22F1/183—High-melting or refractory metals or alloys based thereon of titanium or alloys based thereon
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F28—HEAT EXCHANGE IN GENERAL
- F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
- F28F21/00—Constructions of heat-exchange apparatus characterised by the selection of particular materials
- F28F21/08—Constructions of heat-exchange apparatus characterised by the selection of particular materials of metal
- F28F21/081—Heat exchange elements made from metals or metal alloys
- F28F21/086—Heat exchange elements made from metals or metal alloys from titanium or titanium alloys
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F28—HEAT EXCHANGE IN GENERAL
- F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
- F28F3/00—Plate-like or laminated elements; Assemblies of plate-like or laminated elements
- F28F3/02—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations
- F28F3/04—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element
- F28F3/042—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element in the form of local deformations of the element
- F28F3/046—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element in the form of local deformations of the element the deformations being linear, e.g. corrugations
Definitions
- the present invention relates to a titanium sheet having both high strength and satisfactory formability.
- Titanium materials generally have high specific strength and excellent corrosion resistance. Because of these properties, the titanium materials are used in exterior trim parts of camera bodies and other optical equipment, and of household electrical appliances; materials for ornaments such as eye glasses and watches; components of consumer products such as kitchen equipment; components of transportation equipment such as motorcycles and automobiles; and components of heat exchangers in chemical, power-generating, food manufacturing, and other plants.
- the titanium materials have been more widely used in the heat exchangers, in particular in plates of plate heat exchangers. These are demanded to have a larger surface area by press forming into a corrugated shape so as to have higher heat exchange efficiency that is necessary as a prescribed property.
- titanium sheets for use in the heat exchangers, in particular in plates of plate heat exchangers are demanded to have excellent formability so as to be corrugated more deeply.
- Such titanium sheets heavily used in these uses are prescribed in Japanese Industrial Standard (JIS) H 4600 (enacted on Jul. 1, 1964).
- the titanium sheets prescribed herein are further classified into grades such as Grade 1, Grade 2, and Grade 3 typically by the amounts (contents) of impurities such as iron (Fe) and oxygen (O), and the strength. With an increasing grade, the titanium sheets show higher minimum strength.
- the titanium sheets are used in different uses depending on the Japanese Industrial Standard grade.
- Titanium sheets having low iron and oxygen contents as in JIS Grade 1 have low strength, but high ductility. For this reason, pure titanium sheets of JIS Grade 1 have conventionally been used for components that require excellent formability.
- Industrial pure titanium sheets prescribed in JIS are metal materials each mainly including alpha-phase grain microstructures including hexagonal crystal (hexagonal close-packed; HCP) structure.
- primary slip system of the alpha phase of titanium is prismatic slip ⁇ 10-10 ⁇ 11-20>, and the slip systems further include basal slip ⁇ 0001 ⁇ 11-20> and pyramidal slip.
- a ⁇ 11-22 ⁇ 11-23> twin can act in deformation upon press forming. Titanium, however, includes a smaller amount of active slip systems and does not allow two or more slip systems to act easily, as compared with iron/steel materials having a body-centered cubic structure (BCC) and aluminum materials having a face-centered cubic structure (FCC). Titanium is therefore known to be less plastic deformation.
- BCC body-centered cubic structure
- FCC face-centered cubic structure
- known processes for allowing titanium materials to have higher strength include two processes, i.e., a process of mainly increasing the contents of impurity elements such as oxygen and iron in a titanium material so as to offer higher strength; and a process of performing grain refinement of a titanium material so as to offer higher strength.
- Patent Literature 1 proposes a method for producing a pure titanium sheet.
- the method employs a pure titanium material containing Fe, Ni, and Cr in such contents (in weight percent) as to meet a condition specified by a predetermined relational expression, and oxygen (O) in a content of 900 ppm or less, with the remainder consisting of Ti and inevitable impurities.
- the pure titanium material is subjected sequentially to cold rolling and annealing (heat treatment) at 600° C. to 850° C.
- the pure titanium sheet is then subjected to acid wash with an aqueous nitric hydrofluoric acid solution meeting a condition as specified by a predetermined relational expression.
- PTL 2 proposes a titanium sheet having excellent ductility.
- the titanium sheet has a chemical composition containing H, O, N, and Fe in contents as prescribed in JIS H 4600 Grade 1 or Grade 2, and carbon (C) in a content of 50 to 800 ppm, with the remainder consisting of titanium and inevitable impurities.
- JP-A Japanese Unexamined Patent Application Publication No. 2002-317234
- the titanium sheets proposed in PTL 1 and PTL 2 when having higher contents of impurity elements such as oxygen and iron or when undergoing grain refinement so as to have higher strength, have low ductility and thereby have significantly inferior formability.
- the present invention has been made in consideration of the problems or disadvantages and has an object to provide a titanium sheet that has strength and formability both at satisfactory levels.
- the present inventors found that, although there is a limit in improvement of ductility in a titanium sheet by containing carbon and aluminum in combination according to conventional techniques, the titanium sheet can have better ductility by finely controlling the amounts of iron, oxygen, and carbon to be added.
- the present inventors have also found that the distribution of carbon at grain boundaries affects the ductility improving effect, and that the titanium sheet can have still better ductility by finely controlling the degree of segregation (concentrating) of carbon at grain boundaries.
- the titanium sheet has increasing strength with an increasing carbon content.
- the titanium sheet can effectively enjoy better ductility by the presence of carbon when having a carbon content within a certain optimal range.
- the present inventors made further investigations finely and found that the optimal range depends also on the contents of iron and oxygen.
- oxygen makes the titanium sheet not only have significantly effectively higher strength, but also have inferior ductility.
- the oxygen content is preferably minimized in order to allow carbon to exhibit its effects more efficiently.
- the present inventors had a finding regarding iron as follows.
- the titanium sheet, when containing carbon can more effectively have a better balance between strength and formability with an increasing iron content.
- the present inventors found that carbon allows the titanium sheet to have a better balance between strength and ductility with an increasing degree of segregation of carbon at grain boundaries in the grain microstructure of the titanium sheet even at an identical carbon content, where the degree of segregation indicates the position or distribution of carbon present in the microstructure.
- the present inventors made intensive investigations based on the findings and have found that the controls of the contents of iron, oxygen, and carbon, and the ratio among them allow the titanium sheet to have a better balance between strength and formability; and that the control of the titanium sheet to have a high degree of segregation of carbon at grain boundaries allows the titanium sheet to have still better formability.
- the present invention has been made based on these findings.
- the present invention provides, according to an embodiment, a titanium sheet having a grain microstructure of alpha phase.
- the titanium sheet contains iron (Fe) in a content of 0.020 to 0.150 mass percent, oxygen (O) in a content of 0.020 to 0.150 mass percent, and carbon (C) in a content of 0.002 to 0.100 mass percent, with the remainder consisting of titanium and inevitable impurities.
- the total contents (in mass percent) of iron and carbon is equal to or more than 0.80 time the content (in mass percent) of oxygen.
- a carbon concentration at grain boundaries is 1.0 mass percent or more.
- the titanium sheet as having the configuration, has controlled contents of iron, oxygen, and carbon and a controlled ratio among them so as to allow two or more slip systems/twin systems to act, and has a better balance between strength and formability.
- the titanium sheet as having a carbon concentration at grain boundaries of 1.0 mass percent or more, has still better formability.
- the titanium sheet according to the present invention preferably has an average grain size of 5 to 80 ⁇ m.
- the titanium sheet when having such configuration, may more readily undergo dislocation slip deformation and/or twinning deformation upon forming while having strength held at certain level. This titanium sheet may therefore have still better formability.
- the titanium sheet according to the present invention is usable in a plate heat exchanger.
- the plate heat exchanger when using the titanium sheet according to the present invention, can act as a plate heat exchanger having high strength and satisfactory formability.
- the titanium sheet according to the present invention as having a predetermined chemical composition and a specific carbon concentration at grain boundaries, has strength and formability both at satisfactory levels.
- FIG. 1( a ) is a plan view of a forming tool used in formability evaluation of a titanium sheet according to the present invention
- FIG. 1( b ) is a cross-sectional view of the forming tool along the line E-E.
- the titanium sheet according to the present invention has an alpha-phase (HCP structure) grain microstructure and contains Fe in a content of 0.020 to 0.150 mass percent, O in a content of 0.020 to 0.150 mass percent, and C in a content of 0.002 to 0.100 mass percent, with the remainder consisting of titanium and inevitable impurities.
- the total of contents (in mass percent) of Fe and C is equal to or more than 0.80 time the content (in mass percent) of 0.
- the titanium sheet according to the present invention has a carbon concentration at grain boundaries of 1.0 mass percent or more.
- Iron is an important element that allows the titanium sheet to have higher strength and better formability.
- the titanium sheet if having an iron content less than 0.020 mass percent, may have insufficient strength. This may require a larger amount of strain to be introduced so as to allow the titanium sheet to have higher strength, resulting in lower formability of the titanium sheet. To prevent this, the iron content is controlled to 0.020 mass percent or more.
- the titanium sheet if having an iron content greater than 0.150 mass percent, may be produced with inferior productivity because of higher degree of iron segregation in the ingot.
- this titanium sheet may undergo titanium grain refinement due to a larger amount of formed beta phase and may thereby have lower formability.
- the iron content is controlled to 0.150 mass percent or less.
- the iron content is preferably 0.100 mass percent or less.
- the iron content is more preferably 0.080 mass percent or less.
- Oxygen (O) is an element that allows the titanium sheet to have higher strength, but causes the titanium sheet to have inferior formability.
- the titanium sheet if having an oxygen content less than 0.020 mass percent, may have lower strength. This may require a larger amount of strain to be introduced so as to allow the titanium sheet to have higher strength, resulting in lower formability of the titanium sheet. To prevent this, the oxygen content is controlled to 0.020 mass percent or more.
- the titanium sheet if having an oxygen content greater than 0.150 mass percent, may become brittle and have lower formability. In addition, this titanium sheet may be susceptible to cracking or breakage and may have lower productivity.
- the oxygen content is controlled to 0.150 mass percent or less.
- the oxygen content is preferably 0.125 mass percent or less.
- the oxygen content is more preferably 0.100 mass percent or less.
- Carbon (C) is an element that allows the titanium sheet to have higher strength and better formability.
- the titanium sheet if having a carbon content less than 0.002 mass percent, may hardly have a carbon concentration at grain boundaries at the predetermined level, may fail to have an effectively better balance between strength and formability, and may have lower strength. To prevent this, the carbon content is controlled to 0.002 mass percent or more.
- the titanium sheet if having a carbon content greater than 0.100 mass percent, may have strength higher than necessary and may have inferior formability.
- the carbon content is controlled to 0.100 mass percent or less.
- the carbon content is preferably 0.090 mass percent or less.
- the carbon content is more preferably 0.080 mass percent or less.
- the “inevitable impurities” in the titanium sheet according to the present invention refers to impurity elements that are inevitably contained in an industrial pure titanium sheet.
- the impurity elements are representatively exemplified by nitrogen, hydrogen, chromium, and nickel.
- the inevitable impurities further include hydrogen and other elements that may be possibly contained in the product during production processes.
- the titanium sheet if containing impurities in large contents, may hardly have strength and formability both at satisfactory levels. To prevent this, the titanium sheet is desirably one having contents of inevitable impurities as reduced as appropriate.
- the titanium sheet can have lower contents of inevitable impurities by using alloy raw materials containing impurities in low contents.
- Compositional index R 0.80 or more
- the titanium sheet can have a better balance between strength and formability by controlling the correlation among the iron, oxygen, and carbon contents in addition to the control of these contents individually.
- the total of iron and carbon contents (in mass percent) is controlled to equal to or more than 0.80 time the oxygen content (in mass percent).
- compositional index R as specified by Formula (1) is 0.80 or more
- Formula (1) is expressed as follows, in which [Fe], [C], and [O] represent the contents (in mass percent) respectively of iron, oxygen, and carbon in the titanium sheet:
- the compositional index R may be controlled by adding Fe, O, and C in appropriate amounts depending on the iron, oxygen, and carbon contents in titanium scrap to be used as a raw material to produce the titanium sheet, so as to control the iron, oxygen, and carbon contents in the titanium sheet.
- iron may be added typically in the form of iron powder; oxygen may be added typically in the form of titanium oxide; and carbon may be added typically in the form of titanium carbide TiC.
- the titanium sheet has increasing strength with an increasing carbon content.
- the titanium sheet may have effectively satisfactory ductility due to the presence of carbon in a certain optimal range of the carbon content.
- the optimal range of the carbon content may depend also on the iron and oxygen contents.
- oxygen significantly effectively contributes to higher strength of the titanium sheet, but also causes the titanium sheet to have inferior ductility.
- the oxygen content is preferably minimized so as to allow the titanium sheet to have more efficient effects of the presence of carbon.
- an increasing iron content is effective so as to allow the titanium sheet to more efficiently have a better balance between strength and formability due to the presence of carbon.
- compositional index R is controlled to 0.80 or more in terms of lower limit.
- the titanium sheet when having a compositional index R of 0.80 or more, can allow two or more slip systems/twinning systems to act and can have a better balance between strength and formability.
- compositional index R is preferably 0.85 or more.
- compositional index R is more preferably 0.90 or more.
- the titanium sheet if having a compositional index R less than 0.80, may fail to allow two or more slip systems/twinning systems to act and may have inferior formability.
- compositional index R is preferably 12.5 or less in terms of upper limit, within the ranges of the iron, oxygen, and carbon contents.
- the titanium sheet if having a compositional index R greater than 12.5, has a content of any of the elements iron, oxygen, and carbon out of the preferred range and may thereby have inferior balance between strength and formability as compared with a titanium sheet having a compositional index R of 12.5 or less.
- compositional index R is more preferably 10.0 or less.
- compositional index R is furthermore preferably 6.0 or less.
- oxygen and iron are dissolved in the titanium matrix.
- oxygen and iron are present in different forms even in an identical solute state, because oxygen is an interstitial element, but iron is a substitutional element.
- iron has a smaller solid solubility limit in the titanium sheet as compared with oxygen and causes the formation of beta phase at an iron content at certain level or more (about 0.05 mass percent or more). Based on these, oxygen and iron affect carbon probably in different ways.
- the titanium sheet as having iron, oxygen, and carbon contents meeting the condition specified by Formula (1), may have a better balance between strength and formability.
- Carbon concentration at grain boundaries 1.0 mass percent or more
- the concentration of carbon at grain boundaries may affect the ductility improvement effects of the titanium sheet. Fine control of the carbon concentration at grain boundaries (segregation of carbon at grain boundaries) may allow the titanium sheet to have better ductility. In addition, the fine control of the carbon concentration at grain boundaries more contributes to a balance between strength and formability of the titanium sheet, as compared with other solutions for higher strength (increase in content of oxygen, grain refinement, and impartment of prestrain).
- the titanium sheet if having a carbon concentration at grain boundaries less than 1.0 mass percent, may fail to have an effectively improved balance between strength and formability even when containing carbon in a predetermined content as a whole.
- the carbon concentration at grain boundaries is controlled to 1.0 mass percent or more.
- the carbon concentration at grain boundaries is preferably 2.0 mass percent or more.
- the carbon concentration at grain boundaries is more preferably 5.0 mass percent or more.
- the control of the carbon concentration at grain boundaries may be performed by an after-mentioned production method. Specifically, the control is performed by controlling a cold rolling reduction in a cold rolling process before final annealing. In addition, the control is also performed by controlling the annealing temperature and annealing time in the final annealing process.
- the cold rolling process before final annealing when performed at a low cold rolling reduction, may allow carbon to be more readily segregated (distributed) actively at grain boundaries.
- the final annealing process when performed at a high annealing temperature, may allow carbon to be actively segregated at grain boundaries.
- the final annealing process when performed for a long annealing time, may allow carbon to be actively segregated at grain boundaries.
- Carbon acts as an interstitial element in the grain microstructure of the titanium sheet and is present as a solute when contained in a content within the range specified in the present invention.
- the titanium sheet has a better balance between strength and formability with an increasing degree of segregation (distribution concentration) of carbon at titanium grain boundaries, even when carbon is present in an identical carbon content in the titanium sheet as a whole.
- Average grain size 5 to 80 ⁇ m
- the average grain size affects the formability of the titanium sheet.
- the titanium sheet according to the present invention when having an average grain size within a common range (2 to 150 ⁇ m), can have advantageous effects of the present invention. Even when the average grain size falls within the common range, the titanium sheet, if having an average grain size less than 5 ⁇ m, may resist twinning deformation upon introduction of strain into the titanium sheet: and in contrast, the titanium sheet, if having an average grain size greater than 80 ⁇ m, may suffer from orange peel surfaces. Typically for these reasons, the titanium sheet in both cases may have somewhat low formability. To prevent this, the average grain size is preferably controlled to 5 to 80 ⁇ m. The titanium sheet, when having an average grain size in the range of 5 to 80 ⁇ m, may have better formability so as to have a higher formability index F as mentioned below, as compared with a titanium sheet having an average grain size out of the range.
- the average grain size is more preferably 10 to 60 ⁇ m.
- the control of the average grain size may be performed by the production method. Specifically, the control is performed by controlling the cold rolling reduction of the cold rolling before the final annealing process, and the annealing temperature and annealing time in the final annealing process.
- the cold rolling before the final annealing process when performed at a lower cold rolling reduction, may allow the titanium sheet to have a larger average grain size.
- the final annealing process when performed at a higher annealing temperature, may allow the titanium sheet to have a larger average grain size.
- the final annealing process if performed at an excessively high annealing temperature and excessively approaching the beta transformation temperature (T ⁇ ), may adversely affect the grain growth due to beta phase newly formed.
- the final annealing process if performed for a longer annealing time, may cause the titanium sheet to have a larger average grain size.
- the average grain size can be measured typically by orientation analysis of the microstructure by electron back scattered diffraction pattern (EBSD) analysis, where the microstructure is observed and analyzed by scanning electron microscopy (SEM).
- EBSD electron back scattered diffraction pattern
- SEM scanning electron microscopy
- a sample is irradiated with an electron beam, and a crystal orientation is identified using an electron backscattered diffraction pattern (Kikuchi pattern) formed upon irradiation.
- the average grain size may be determined in the following manner.
- a boundary having a misorientation of 5° or more in the SEM/EBSD measurement data is defined as a grain boundary.
- the diameter of the circle is defined as an equivalent circle diameter of the grain.
- the equivalent circle diameters of grains in a number of 100 or more are averaged to give an average equivalent circle diameter.
- This measurement procedure is further performed at multiple points (e.g., five or more points) to give average equivalent circle diameters, and the average of the average equivalent circle diameters is defined as the average grain size.
- the plate for plate heat exchanger according to the present invention is one obtained by working the titanium sheet according to the present invention into a predetermined shape such as a deeply corrugated shape by a known technique such as press forming.
- the titanium sheet according to the present invention has the chemical composition and carbon distribution at grain boundaries as described above and thereby has strength and formability both at satisfactory levels.
- the titanium sheet according to the present invention therefore has excellent formability typically without cracking even when worked into a deeply corrugated shape upon working (forming) into a plate for plate heat exchanger.
- the plate for plate heat exchanger according to the present invention has satisfactory strength and can endure a severe use environment such as use in a heat exchanger for a long time.
- the titanium sheet according to the present invention can be produced by a conventional production method.
- the production method may include melting process and remelting process by consumable-electrode vacuum arc remelting (VAR), casting process, hot forging process, hot rolling process, process annealing process, cold rolling process, and final annealing process.
- VAR vacuum arc remelting
- Ways to control the carbon concentration at grain boundaries (ways to induce carbon segregation) in the production processes of the titanium sheet according to the present invention are as follows.
- Oxygen, iron, and carbon are added to a molten metal in the melting process.
- carbon is preferably added to the molten metal not alone, but in the form of titanium carbide (TiC). This allows the titanium sheet to easily contain carbon even upon melting by VAR, which is a common mass production technique.
- cold rolling and annealing are repeated while selecting a rolling reduction and annealing conditions as appropriate according to cold rolling properties (e.g., edge cracking susceptibility and deformation load) of the material.
- Cold rolling immediately before the final annealing process may be performed at such a rolling reduction (e.g., a rolling reduction of 30% or more) as to ensure a sufficient amount of processing so that the material will be recrystallized in the final annealing process.
- the cold rolling process before the final annealing is preferably performed at a cold rolling reduction of 85% or less. This condition restrains the growth of a recrystallization texture after the final annealing to give a smaller proportion of small angle grain boundaries and to give a larger proportion of large angle grain boundaries, where carbon is segregated with difficulty at the small angle grain boundaries, but easily segregated at the large angle grain boundaries.
- the cold rolling reduction is preferably set lower and is more preferably 70% or less.
- the cold rolling reduction is furthermore preferably 60% or less.
- the final annealing process carbon diffuses during annealing in a promoted manner and is thereby actively segregated at grain boundaries.
- the final annealing is preferably performed at a high temperature for a long time.
- the final annealing process will be described below separately in the case using a continuous annealing furnace and in the case using a batch annealing furnace (vacuum furnace).
- the final annealing using a continuous annealing furnace is preferably performed at an annealing temperature of 600° C. to 890° C.
- the final annealing if performed at an annealing temperature lower than 600° C., may fail to sufficiently cause the segregation of carbon at grain boundaries and may fail to allow the titanium sheet to have a carbon concentration at grain boundaries of 1.0 mass percent or more.
- the final annealing if performed at an annealing temperature higher than 890° C., may cause significant grain growth subsequent to recrystallization occurred during the annealing, and a specific orientation is accumulated at a higher degree. This may increase the proportion of small angle grain boundaries at which carbon is hardly segregated, impede the segregation of carbon at grain boundaries contrarily, and cause the titanium sheet to hardly have a carbon concentration at grain boundaries of 1.0 mass percent or more.
- the final annealing using the continuous annealing furnace is more preferably performed at an annealing temperature of 700° C. to 890° C.
- Holding of the workpiece in the final annealing using the continuous annealing furnace is not essential (the workpiece may be held for zero minute), but the holding, when performed, is preferably performed for a holding time of 10 minutes or shorter.
- the holding if performed for a time longer than 10 minutes, may cause significant grain growth subsequent to recrystallization occurred during annealing, and a specific orientation may be present at a higher degree of accumulation (in a higher density). This may increase the proportion of small angle grain boundaries at which carbon is hardly segregated, impede the segregation of carbon at grain boundaries contrarily, and cause the titanium sheet to hardly have a carbon concentration at grain boundaries of 1.0 mass percent or more.
- the holding in the final annealing using the continuous annealing furnace is more preferably performed for a holding time of 1 to 10 minutes.
- the final annealing using the batch annealing furnace is preferably performed at an annealing temperature of 550° C. to 700° C.
- the final annealing if performed at an annealing temperature lower than 550° C., may fail to invite sufficient segregation of carbon at grain boundaries and may cause the titanium sheet to fail to have a carbon concentration at grain boundaries of 1.0 mass percent or more.
- the final annealing if performed at an annealing temperature higher than 700° C., may cause significant grain growth subsequent to recrystallization occurred during annealing, and a specific orientation may be present at a higher degree of accumulation. This may increase the proportion of small angle grain boundaries at which carbon is hardly segregated, impede the segregation of carbon at grain boundaries contrarily, and cause the titanium sheet to hardly have a carbon concentration at grain boundaries of 1.0 mass percent or more.
- the final annealing using the batch annealing furnace is more preferably performed at an annealing temperature of 600° C. to 700° C.
- Holding in the final annealing using the batch annealing furnace is preferably performed for a time of 30 minutes to 4 hours.
- the holding if performed for a time of shorter than 30 minutes, may fail to cause sufficient segregation of carbon at grain boundaries and may cause the titanium sheet to fail to have a carbon concentration at grain boundaries of 1.0 mass percent or more.
- the holding if performed for a time longer than 4 hours, may cause significant grain growth subsequent to recrystallization occurred during annealing, and a specific orientation may be present at a higher degree of accumulation. This may increase the proportion of small angle grain boundaries at which carbon is hardly segregated, impede the segregation of carbon at grain boundaries contrarily, and cause the titanium sheet to hardly have a carbon concentration at grain boundaries of 1.0 mass percent or more.
- Holding in the final annealing using the batch annealing furnace is more preferably performed for a time of 1 to 4 hours.
- the titanium sheet after annealing, when bearing scale deposited on the surface is preferably subjected to a descaling process such as salt bath heat treatment and/or acid wash treatment.
- the titanium materials were hot-forged at 1000° C. for 30 minutes, then hot-rolled at 800° C., and yielded a series of hot-rolled sheets having a thickness of 4.0 mm.
- the hot-rolled sheets were subjected to cold rolling and process annealing (at 750° C. for 5 minutes in a continuous annealing furnace).
- the workpieces were subjected to descaling by immersing in a salt bath in furnace and subjected to acid wash.
- the workpieces were subjected to cold rolling and final annealing under conditions given in Table 1, and yielded a series of test samples (Test Sample Nos. 1 to 27) each having a thickness of 0.5 mm.
- the final annealing was performed in a continuous annealing furnace or a batch annealing furnace (vacuum furnace). This allowed the test samples to have a carbon concentration at grain boundaries of 1.0 mass percent or more.
- the sample was immersed in a salt bath in furnace, descaled by acid wash, and cold rolling reductions before and after process annealing were adjusted so as to give a sheet thickness of 0.5 mm.
- the evaluation of carbon concentration at grain boundaries was performed using a field emission transmission electron microscope (FE-TEM) and an energy dispersive X-ray spectrometer (EDX). Specifically, using JOEL JEM-2010F (FE-TEM) equipped with Noran Vantage (EDX), a test sample was inclined so that grain boundaries of the test sample were perpendicular to the observation direction, and a point analysis was performed on each grain boundary at an acceleration voltage of 200 kV and at 1000000-fold magnification while reducing the diameter of the electron beam to about 1 nm, and an EDX spectrum was measured. The electron beam was applied for a time of 30 seconds for the EDX spectrum measurement. Based on the spectrum, the carbon concentration at a grain boundary was analyzed. The carbon concentration at the grain boundary was analyzed at ten points in each field of view, and the average of measured carbon concentrations was calculated. The measurement was performed in five fields of view per test sample, the average of measured data was calculated, and was defined as the carbon concentration at grain boundaries.
- FE-TEM field emission
- Microstructure observation was performed using an electron back scattered diffraction pattern (EBSD) detector (Oxford Instruments Nordlys II). The observation was performed on observation objects of the test sample each as an area of 0.5 mm in the rolling direction and 0.5 mm in the transverse direction (width direction) in the rolling plane in each of a surface layer portion, a portion one-fourth the thickness t, and a central portion all in the thickness direction of the test sample.
- EBSD electron back scattered diffraction pattern
- test specimen prescribed in JIS Z 2241 (enacted on Jul. 22, 1952) was sampled from each test sample in such a direction that the rolling direction of the test sample met the loading axis.
- test specimen was subjected to a tensile test according to JIS H 4600 at mom temperature so as to measure 0.2% yield strength (YS).
- a test sample having 0.2% yield strength (YS) of the test specimen of 200 MPa or more was evaluated as accepted.
- the formability was evaluated by performing press forming, where the press forming simulated the forming into a plate (heat-exchanging unit) of a plate heat exchanger.
- tools used herein had a forming portion of 100 mm by 100 mm.
- the forming portion had four ridges having a maximum height of 6.5 mm and being disposed at a pitch of 17 mm.
- the ridges each had a vertex having a shape with a radius R of curvature of 2.5.
- the ridges each had one bent portion in an intermediate portion, where the bent portion was bent in one direction.
- the ridges extend linearly from the bent portion toward both ends.
- the ridges were arranged in the forming portion from the intermediate bent portion to the both ends diagonally with respect to the edges of the forming portion, thus resembling a corrugated shape.
- a pressing machine used herein was a 80-ton pressing machine (Universal Plastic Working Machine supplied by AMINO Inc.).
- the press forming was performed by the following procedure. Initially, each test sample was coated with a rust preventive oil (R303P). Next, each test sample was placed on the lower tool (die) so that the rolling direction of the test sample met the upward and downward direction (vertical direction) in FIG. 1( a ), and the flange portion was held by a blank holder. The upper tool (punch) was then indented at a press forming rate of 1 mm per second.
- R303P rust preventive oil
- the tool was indented into each test sample by 0.1 mm, and a maximum indentation depth X at which no cracking occurred in each test sample was determined.
- a formability index F specified by Formula (2) was determined, and a test sample having a positive formability index F was evaluated as accepted. Evaluation results are indicated in Table 1.
- Formula (2) is expressed as follows:
- Test Sample Nos. 1 to 16 were titanium sheets that met all the conditions (chemical composition, compositional index R, and carbon concentration at grain boundaries) specified in the present invention and had excellent balance between strength and press formability.
- Test Sample Nos. 17 to 27 failed to meet the conditions specified in the present invention, in particular failed to meet the condition for the carbon concentration at grain boundaries, and had poor balance between strength and press formability.
- Test Sample Nos. 17 to 20 underwent low-level segregation of carbon at grain boundaries, had a carbon concentration at grain boundaries out of the specified range, and each had poor balance between strength and formability of the titanium sheet.
- Test Sample Nos. 18 to 20 had characteristics as follows.
- Test Sample No. 18 had a carbon content greater than the range as specified in the present invention and had excessively high strength higher than necessary.
- Test Sample No. 19 had an iron content greater than the range as specified in the present invention, thereby underwent the formation of a larger amount of beta phase, and underwent titanium grain refinement.
- Test Sample No. 20 had an oxygen content greater than the range as specified in the present invention, had excessively high strength higher than necessary, and became brittle.
- Test Sample No. 21 had a compositional index R lower than the range as specified in the present invention, underwent low-level segregation of carbon at grain boundaries, thereby had a carbon concentration at grain boundaries lower than the specified range, and thereby had poor formability due to its brittleness, although having high strength.
- Test Sample No. 22 underwent final cold rolling performed at a high cold rolling reduction, underwent low-level segregation of carbon at grain boundaries, had a carbon concentration at grain boundaries lower than the specified range, and thereby had poor formability.
- Test Sample No. 23 underwent final annealing performed at a low annealing temperature, underwent low-level segregation of carbon at grain boundaries, had a carbon concentration at grain boundaries lower than the specified range, and thereby had poor formability.
- Test Sample No. 24 underwent final annealing performed at a high annealing temperature, underwent low-level segregation of carbon at grain boundaries, had a carbon concentration at grain boundaries lower than the specified range, and thereby had insufficient strength and poor formability.
- Test Sample No. 25 underwent final annealing performed for a short time, thereby underwent insufficient annealing and low-level segregation of carbon at grain boundaries, had a carbon concentration at grain boundaries lower than the specified range, and thereby had poor formability.
- Test Sample No. 26 underwent final annealing performed for a long time, underwent low-level segregation of carbon at grain boundaries, had a carbon concentration at grain boundaries lower than the specified range, and thereby had poor formability.
- Test Sample No. 27 underwent final annealing performed for a long time, thus received excessive annealing, underwent low-level segregation of carbon at grain boundaries, had a carbon concentration at grain boundaries lower than the specified range, and thereby had poor formability.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Crystallography & Structural Chemistry (AREA)
- General Engineering & Computer Science (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Manufacture And Refinement Of Metals (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2013056549 | 2013-03-19 | ||
JP2013-056549 | 2013-03-19 | ||
PCT/JP2014/054550 WO2014148211A1 (fr) | 2013-03-19 | 2014-02-25 | Tôle de titane |
Publications (1)
Publication Number | Publication Date |
---|---|
US20150376738A1 true US20150376738A1 (en) | 2015-12-31 |
Family
ID=51579903
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US14/764,738 Abandoned US20150376738A1 (en) | 2013-03-19 | 2014-02-25 | Titanium sheet |
Country Status (5)
Country | Link |
---|---|
US (1) | US20150376738A1 (fr) |
JP (1) | JP6263040B2 (fr) |
KR (1) | KR101743380B1 (fr) |
CN (1) | CN105308199B (fr) |
WO (1) | WO2014148211A1 (fr) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20160363395A1 (en) * | 2014-02-27 | 2016-12-15 | Kaboshiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) | Plate for use as heat exchange plate and method for manufacturing such base plate |
RU2752094C1 (ru) * | 2018-04-10 | 2021-07-22 | Ниппон Стил Корпорейшн | Титановый сплав и способ его получения |
Families Citing this family (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP6577707B2 (ja) * | 2014-11-28 | 2019-09-18 | 株式会社神戸製鋼所 | チタン板、熱交換器用プレート、燃料電池用セパレータおよびチタン板の製造方法 |
US20180047996A1 (en) * | 2015-03-23 | 2018-02-15 | Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) | Titanium plate, plate for heat exchanger, and separator for fuel cell |
JP6156597B1 (ja) * | 2016-06-30 | 2017-07-05 | 新日鐵住金株式会社 | チタン薄板及びその製造方法 |
TWI650428B (zh) * | 2018-04-10 | 2019-02-11 | 日商新日鐵住金股份有限公司 | 鈦合金及其製造方法 |
JP7385941B2 (ja) * | 2019-08-23 | 2023-11-24 | 国立大学法人東京海洋大学 | チタン材、該チタン材を加工してなるチタン製品及び該チタン材の製造方法 |
CN115216667A (zh) * | 2022-07-18 | 2022-10-21 | 西安秦钛智造科技有限公司 | 一种金属隔膜用钛板及其加工方法 |
Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20110017369A1 (en) * | 2008-03-25 | 2011-01-27 | Sumitomo Metal Industries, Ltd. | Titanium plate and method of producing the same |
JP2012082457A (ja) * | 2010-10-08 | 2012-04-26 | Kobe Steel Ltd | 成形性に優れたチタン板およびそのチタン板の製造方法 |
Family Cites Families (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2002003968A (ja) * | 2000-06-21 | 2002-01-09 | Sumitomo Metal Ind Ltd | 成形性に優れたチタン板とその製造方法 |
JP2005105387A (ja) * | 2003-10-01 | 2005-04-21 | Kobe Steel Ltd | 表面性状に優れたチタン板 |
JP5427154B2 (ja) * | 2010-09-29 | 2014-02-26 | 株式会社神戸製鋼所 | 高強度で成形性に優れたチタン板 |
JP5700650B2 (ja) * | 2011-01-28 | 2015-04-15 | 株式会社神戸製鋼所 | プレス成形性と強度のバランスに優れた純チタン板 |
JP5937865B2 (ja) * | 2011-05-30 | 2016-06-22 | 株式会社神戸製鋼所 | プレス成形性と強度のバランス、及び耐食性に優れた純チタン板の製造方法 |
-
2014
- 2014-02-05 JP JP2014020503A patent/JP6263040B2/ja not_active Expired - Fee Related
- 2014-02-25 KR KR1020157025191A patent/KR101743380B1/ko active IP Right Grant
- 2014-02-25 WO PCT/JP2014/054550 patent/WO2014148211A1/fr active Application Filing
- 2014-02-25 CN CN201480015891.6A patent/CN105308199B/zh not_active Expired - Fee Related
- 2014-02-25 US US14/764,738 patent/US20150376738A1/en not_active Abandoned
Patent Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20110017369A1 (en) * | 2008-03-25 | 2011-01-27 | Sumitomo Metal Industries, Ltd. | Titanium plate and method of producing the same |
JP2012082457A (ja) * | 2010-10-08 | 2012-04-26 | Kobe Steel Ltd | 成形性に優れたチタン板およびそのチタン板の製造方法 |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20160363395A1 (en) * | 2014-02-27 | 2016-12-15 | Kaboshiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) | Plate for use as heat exchange plate and method for manufacturing such base plate |
RU2752094C1 (ru) * | 2018-04-10 | 2021-07-22 | Ниппон Стил Корпорейшн | Титановый сплав и способ его получения |
Also Published As
Publication number | Publication date |
---|---|
KR20150119301A (ko) | 2015-10-23 |
JP6263040B2 (ja) | 2018-01-17 |
CN105308199A (zh) | 2016-02-03 |
JP2014205904A (ja) | 2014-10-30 |
WO2014148211A1 (fr) | 2014-09-25 |
CN105308199B (zh) | 2017-11-24 |
KR101743380B1 (ko) | 2017-06-02 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20150376738A1 (en) | Titanium sheet | |
TWI629369B (zh) | 鋼板及鍍敷鋼板 | |
TWI481729B (zh) | A hot-pressed steel sheet, a method for manufacturing the same, and a hot-pressed steel sheet member | |
CN104736736B (zh) | 高强度冷轧钢板及其制造方法 | |
KR101943253B1 (ko) | 타이타늄판, 열 교환기용 플레이트 및 연료 전지용 세퍼레이터 | |
CN107148486A (zh) | 高强度钢板、高强度热镀锌钢板、高强度热镀铝钢板和高强度电镀锌钢板、以及它们的制造方法 | |
CN104160050A (zh) | 热冲压用钢板及其制造方法和热冲压钢材 | |
US20110168303A1 (en) | High tensile strength steel for container and producing method of the same | |
KR20120087837A (ko) | 프레스 성형성과 강도의 밸런스가 우수한 순타이타늄판 | |
CN112912521B (zh) | 钢板及其制造方法 | |
EP3231885A1 (fr) | Tôle d'acier destinée à l'estampage à chaud, et composant moulé par estampage à chaud utilisant ladite tôle d'acier | |
JP6577707B2 (ja) | チタン板、熱交換器用プレート、燃料電池用セパレータおよびチタン板の製造方法 | |
WO2017175569A1 (fr) | Plaque de titane, plaque d'échangeur de chaleur et séparateur de pile à combustible | |
US11739400B2 (en) | Magnesium alloy and method for manufacturing the same | |
JP2014012881A (ja) | チタン板およびその製造方法 | |
JP2017190480A (ja) | チタン板 | |
TW201942385A (zh) | 鋼板及鋼板的製造方法 | |
CN117836458A (zh) | 钢板、构件和它们的制造方法 | |
JP5444182B2 (ja) | 成形性に優れたチタン板 | |
JP5427154B2 (ja) | 高強度で成形性に優れたチタン板 | |
JP2017078220A (ja) | マグネシウム合金圧延材およびその製造方法ならびにプレス成型品 | |
JP2016108652A (ja) | チタン板、熱交換器用プレートおよび燃料電池用セパレータ | |
TWI796118B (zh) | 鈦合金板及鈦合金捲材暨鈦合金板之製造方法及鈦合金捲材之製造方法 | |
JP2016023315A (ja) | チタン板およびその製造方法 | |
EP4317483A1 (fr) | Tôle d'acier et son procédé de production |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: KABUSHIKI KAISHA KOBE SEIKO SHO (KOBE STEEL, LTD.) Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MATSUMOTO, KATSUSHI;ITO, YOSHINORI;REEL/FRAME:036218/0173 Effective date: 20150115 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |