US20120190273A1 - Polishing method and polishing apparatus - Google Patents
Polishing method and polishing apparatus Download PDFInfo
- Publication number
- US20120190273A1 US20120190273A1 US13/348,859 US201213348859A US2012190273A1 US 20120190273 A1 US20120190273 A1 US 20120190273A1 US 201213348859 A US201213348859 A US 201213348859A US 2012190273 A1 US2012190273 A1 US 2012190273A1
- Authority
- US
- United States
- Prior art keywords
- polishing
- polishing pad
- temperature
- pad
- gas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 238000005498 polishing Methods 0.000 title claims abstract description 575
- 238000000034 method Methods 0.000 title claims abstract description 42
- 239000000758 substrate Substances 0.000 claims abstract description 96
- 238000007664 blowing Methods 0.000 claims abstract description 33
- 238000012544 monitoring process Methods 0.000 claims abstract description 21
- 238000001816 cooling Methods 0.000 claims description 78
- 239000002002 slurry Substances 0.000 claims description 30
- 238000004140 cleaning Methods 0.000 claims description 29
- 229910052751 metal Inorganic materials 0.000 claims description 21
- 239000002184 metal Substances 0.000 claims description 21
- 230000008859 change Effects 0.000 claims description 8
- 238000003825 pressing Methods 0.000 claims description 8
- 230000007547 defect Effects 0.000 claims description 6
- 239000003595 mist Substances 0.000 claims description 6
- 230000003287 optical effect Effects 0.000 claims description 5
- 238000001514 detection method Methods 0.000 claims description 2
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 10
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 description 9
- 229910052802 copper Inorganic materials 0.000 description 9
- 239000010949 copper Substances 0.000 description 9
- 239000007788 liquid Substances 0.000 description 9
- 230000004888 barrier function Effects 0.000 description 8
- 238000012546 transfer Methods 0.000 description 8
- 229910052721 tungsten Inorganic materials 0.000 description 7
- 230000002093 peripheral effect Effects 0.000 description 6
- WFKWXMTUELFFGS-UHFFFAOYSA-N tungsten Chemical compound [W] WFKWXMTUELFFGS-UHFFFAOYSA-N 0.000 description 6
- 239000010937 tungsten Substances 0.000 description 6
- 229910052681 coesite Inorganic materials 0.000 description 5
- 229910052906 cristobalite Inorganic materials 0.000 description 5
- 230000007423 decrease Effects 0.000 description 5
- 230000000694 effects Effects 0.000 description 5
- 230000008569 process Effects 0.000 description 5
- 239000000377 silicon dioxide Substances 0.000 description 5
- 229910052682 stishovite Inorganic materials 0.000 description 5
- 229910052905 tridymite Inorganic materials 0.000 description 5
- 230000007246 mechanism Effects 0.000 description 4
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 4
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 description 3
- 238000010586 diagram Methods 0.000 description 3
- 239000004744 fabric Substances 0.000 description 3
- 239000004065 semiconductor Substances 0.000 description 3
- 229910052710 silicon Inorganic materials 0.000 description 3
- 239000010703 silicon Substances 0.000 description 3
- 239000000654 additive Substances 0.000 description 2
- 230000000996 additive effect Effects 0.000 description 2
- 230000002411 adverse Effects 0.000 description 2
- 238000010276 construction Methods 0.000 description 2
- 239000012530 fluid Substances 0.000 description 2
- 238000012545 processing Methods 0.000 description 2
- 238000005507 spraying Methods 0.000 description 2
- 239000000126 substance Substances 0.000 description 2
- 238000013461 design Methods 0.000 description 1
- 238000001035 drying Methods 0.000 description 1
- 238000011065 in-situ storage Methods 0.000 description 1
- 238000002955 isolation Methods 0.000 description 1
- 238000005259 measurement Methods 0.000 description 1
- 238000012986 modification Methods 0.000 description 1
- 230000004048 modification Effects 0.000 description 1
- 229910021420 polycrystalline silicon Inorganic materials 0.000 description 1
- 229920005591 polysilicon Polymers 0.000 description 1
- 230000002035 prolonged effect Effects 0.000 description 1
- 230000005855 radiation Effects 0.000 description 1
- 239000011347 resin Substances 0.000 description 1
- 229920005989 resin Polymers 0.000 description 1
Images
Classifications
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
- H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
- H01L21/04—Manufacture or treatment of semiconductor devices or of parts thereof the devices having potential barriers, e.g. a PN junction, depletion layer or carrier concentration layer
- H01L21/18—Manufacture or treatment of semiconductor devices or of parts thereof the devices having potential barriers, e.g. a PN junction, depletion layer or carrier concentration layer the devices having semiconductor bodies comprising elements of Group IV of the Periodic Table or AIIIBV compounds with or without impurities, e.g. doping materials
- H01L21/30—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26
- H01L21/302—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26 to change their surface-physical characteristics or shape, e.g. etching, polishing, cutting
- H01L21/304—Mechanical treatment, e.g. grinding, polishing, cutting
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B24—GRINDING; POLISHING
- B24B—MACHINES, DEVICES, OR PROCESSES FOR GRINDING OR POLISHING; DRESSING OR CONDITIONING OF ABRADING SURFACES; FEEDING OF GRINDING, POLISHING, OR LAPPING AGENTS
- B24B37/00—Lapping machines or devices; Accessories
- B24B37/005—Control means for lapping machines or devices
- B24B37/015—Temperature control
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B24—GRINDING; POLISHING
- B24B—MACHINES, DEVICES, OR PROCESSES FOR GRINDING OR POLISHING; DRESSING OR CONDITIONING OF ABRADING SURFACES; FEEDING OF GRINDING, POLISHING, OR LAPPING AGENTS
- B24B37/00—Lapping machines or devices; Accessories
- B24B37/04—Lapping machines or devices; Accessories designed for working plane surfaces
- B24B37/07—Lapping machines or devices; Accessories designed for working plane surfaces characterised by the movement of the work or lapping tool
- B24B37/10—Lapping machines or devices; Accessories designed for working plane surfaces characterised by the movement of the work or lapping tool for single side lapping
Definitions
- the present invention relates to a polishing method and apparatus for polishing a surface (surface to be polished) of a substrate, such as a semiconductor wafer, by pressing the surface of the substrate against a polishing surface of a polishing pad while moving the surface of the substrate and the polishing surface relative to each other.
- a chemical mechanical polishing (CMP) apparatus which polishes a surface to be polished of a substrate, such as a semiconductor wafer, into a flat surface by a method comprising pressing the surface of the substrate, held by a polishing head (substrate holding mechanism), against a polishing surface of a polishing pad, attached to an upper surface of a polishing table, while rotating the polishing table and the polishing head to move the surface of the substrate and the polishing surface relative to each other, and supplying a slurry to the polishing surface.
- CMP chemical mechanical polishing
- the temperature of a polishing pad changes with time as polishing progresses, and the temperature change in the polishing pad affects the polishing rate, the polishing profile after polishing, etc.
- the applicant has proposed a method which uses a fluid blowing mechanism for blowing a gas, such as a compressed gas, toward a polishing surface and which involves controlling the fluid blowing mechanism, based on the results of measurement of the distribution of the temperature of the polishing surface, so that the polishing surface is brought into a predetermined temperature distribution (see Japanese Patent Laid-Open Publication No. 2007-181910).
- the present invention has been made in view of the above situation. It is therefore an object of the present invention to provide a polishing method and apparatus which makes it possible to polish a surface (surface to be polished) of a substrate at a sufficient polishing rate and obtain a desired polishing profile while preventing an unpolished portion from remaining on the surface of the substrate after polishing.
- the present invention provides a polishing method for polishing a surface to be polished with a polishing pad while controlling the temperature of the polishing pad by blowing a gas toward the polishing pad.
- the polishing method comprises monitoring the polishing state of the surface to be polished during polishing while PID-controlling the flow rate or the blow direction of the gas, and changing the control temperature of the polishing pad when a predetermined thickness of a film to be polished is reached.
- the polishing state of the surface to be polished is the thickness of a film to be polished, for example.
- the temperature of the polishing pad is controlled so that the maximum polishing rate can be achieved before a predetermined thickness of a film to be polished is reached, for example, before a film thickness, at which surface irregularities of the surface to be polished are removed, is reached and, after the predetermined film thickness is reached, the temperature of the polishing pad is controlled so that surface irregularities of the surface to be polished, the number of defects or the amount of unpolished metal can be minimized. This can prevent an unpolished portion from remaining in a scattered state on the surface to be polished after polishing without entailing a significant lowering of the polishing rate.
- a dry gas is used as the gas before the predetermined film thickness is reached, and a mist is used as the gas after the predetermined film thickness is reached.
- the dry gas may be supplied to the polishing pad by blowing compressed air as the dry gas toward the polishing pad from a cooling nozzle, or by blowing air as the dry gas toward the polishing pad by rotating a cooling fan.
- the use of a mist to control the temperature of the polishing pad can increase the effect of cooling the polishing pad.
- polishing is carried out at a first polishing pressure before the predetermined film thickness is reached and, after the predetermined film thickness is reached, polishing is carried out at a second polishing pressure which is lower than the first polishing pressure.
- This manner of polishing can increase the polishing rate during the polishing before the predetermined film thickness is reached.
- the monitoring of the surface to be polished during polishing may be performed by using an eddy current sensor, an optical sensor or a torque current sensor.
- the present invention provides another polishing method for polishing a surface to be polished with a polishing pad while controlling the temperature of the polishing pad by blowing a gas toward the polishing pad.
- the polishing method comprises: a first polishing step of polishing the surface to be polished while controlling the temperature of the polishing pad at a temperature corresponding to that elastic modulus of the polishing pad which achieves the maximum polishing rate, based on data on a correlation between the elastic modulus of the polishing pad and the temperature of the polishing pad as well as data on a correlation between the elastic modulus of the polishing pad and the polishing rate or data on a correlation between the elastic modulus of the polishing pad and at least one of planarities, the number of defects and the amount of unpolished metal; and a second polishing step of polishing the surface to be polished while controlling, based on the correlation data, the temperature of the polishing pad at a temperature corresponding to that elastic modulus of the polishing pad which achieves desired planarities.
- the present invention provides yet another polishing method for polishing a surface to be polished with a polishing pad while controlling the temperature of the polishing pad by blowing a gas toward the polishing pad.
- the polishing method comprises monitoring the polishing state of the surface to be polished during polishing and, when a predetermined thickness of a film to be polished is reached, predicting a polishing end time, and controlling the blowing of the gas so that the temperature of the polishing pad reaches a predetermined temperature at the polishing end time.
- the present invention also provides a polishing apparatus for polishing a substrate comprising: a gas blow section for blowing a gas toward a polishing pad to control the temperature of the polishing pad; a controller for PID-controlling the flow rate or the blow direction of the gas blowing from the gas blow section; and a monitor for monitoring the polishing state of a surface to be polished.
- a recipe which indicates a relationship between the control temperature of the polishing pad and the thickness of a film to be polished, is stored in the controller, and the controller and the monitor are configured to operate based on the recipe and change the control temperature of the polishing pad according to the thickness of the film.
- the polishing apparatus further comprises a cleaning tool for cleaning the gas blow section.
- the cleaning tool can clean the gas blow section to remove dirt, such as a slurry, from the gas blow section, thereby preventing the dirt, adhering to the gas blow section, from adversely affecting the next substrate.
- the cooling device is comprised of at least one of a cooling nozzle for blowing compressed air as the dry gas toward the polishing pad and a cooling fan for blowing air as the dry gas toward the polishing pad.
- the polishing apparatus may further comprises a temperature sensor for detecting the temperature of the polishing pad, and a temperature controller for controlling, based on a detection value of the temperature sensor, an amount of the dry gas to be supplied from the gas blow section to the polishing pad.
- the present invention also provides a method for polishing a substrate by bringing the substrate into sliding contact with a polishing pad.
- the method comprises: rotating a polishing table holding the polishing pad; pressing a surface of the substrate against the polishing pad; supplying a slurry to the polishing pad; blowing a gas toward the polishing pad while controlling a flow rate or a blow direction of the gas by PID-control so that a temperature of the polishing pad becomes a first control temperature; monitoring a polishing state of the substrate; and blowing a gas toward the polishing pad while controlling a flow rate or a blow direction of the gas by PID-control so that a temperature of the polishing pad becomes a second control temperature after the polishing state is detected to be a predetermined state.
- the present invention makes it possible to polish a surface (surface to be polished) of a substrate at a sufficient polishing rate and obtain a desired polishing profile while preventing an unpolished portion from remaining on the surface of the substrate after polishing.
- FIG. 1 is a schematic view of a polishing apparatus according to an embodiment of the present invention
- FIG. 2 is an enlarged view of a cooling nozzle and its vicinity in the polishing apparatus shown in FIG. 1 ;
- FIG. 3 is a diagram showing a polishing head and head cleaning nozzles, provided in the polishing apparatus shown in FIG. 1 ;
- FIG. 4 is a schematic view of a slurry supply nozzle with a windshield plate attached thereto;
- FIG. 5 is a schematic view of a polishing apparatus according to another embodiment of the present invention.
- FIG. 6 is a schematic plan view of a polishing apparatus according to yet another embodiment of the present invention.
- FIG. 7 is a graph showing an exemplary relationship between the temperature of a polishing pad and polishing rate
- FIG. 8 is a cross-sectional diagram showing an exemplary substrate to be polished by a polishing apparatus according to the present invention.
- FIG. 9 is a cross-sectional diagram showing another exemplary substrate to be polished by a polishing apparatus according to the present invention.
- FIG. 1 schematically shows the overall construction of a polishing apparatus according to an embodiment of the present invention.
- the polishing apparatus 10 includes a rotatable polishing table 12 , a polishing pad 14 attached to an upper surface of the polishing table 12 and whose upper surface serves as a polishing surface 14 a, a polishing head 16 as a substrate holding mechanism for holding a substrate, such as a semiconductor wafer, and pressing the substrate against the polishing surface 14 a, and a slurry supply nozzle 20 , disposed above the polishing pad 14 , for supplying a slurry 18 to the polishing pad 14 .
- This polishing apparatus 10 is configured to polish a surface (surface to be polished) of a substrate (not shown) by pressing the surface of the substrate against the polishing surface 14 a of the polishing pad 14 while rotating the polishing table 12 and the polishing head 16 , holding the substrate on the lower surface, to move the substrate and the polishing surface 14 a of the polishing pad 14 relative to each other and supplying the slurry 18 as a polishing liquid from the slurry supply nozzle 20 to the polishing pad 14 .
- the elastic modulus of the polishing pad 14 used in this embodiment changes from 10 GPa to 10 MPa in the temperature range of 0° C. to 80° C.
- a resin polishing pad for example, generally increases its hardness when it is cooled, and therefore improves the planarities by cooling the polishing pad.
- polishing of the intended film can be performed while controlling the elastic modulus of the polishing pad by adjusting the temperature of the polishing pad according to the progress of polishing.
- the polishing head 16 is coupled to a free end of a not-shown vertically movable pivot arm and configured to move horizontally between a polishing position above the polishing table 12 and a substrate transfer position where a substrate is transferred to and from, e.g., a pusher of a linear transporter.
- a nozzle support arm 22 which extends parallel to the polishing surface 14 a of the polishing pad 14 approximately in the radial direction of the polishing pad 14 .
- cooling nozzles 24 as a cooling device, which communicate with the interior of the nozzle support arm 22 and cool the polishing pad 14 by blowing compressed air as a dry gas toward the polishing pad 14 .
- Each cooling nozzle 24 has a nozzle opening 24 a with a predetermined opening angle a so that compressed air can be blown toward the entire substrate passage area of the polishing surface 14 a to make the temperature of that area uniform.
- the number, the positions, etc. of the cooling nozzles 24 can be arbitrarily set depending on the process conditions, etc.
- the nozzle support arm 22 is connected to a compressed air supply line 26 extending from a compressed air supply source.
- a pressure control valve 28 and a flow meter 30 are interposed in the compressed air supply line 26 .
- the pressure of compressed air (dry gas) is controlled when it passes through the pressure control valve 28 and the flow rate of the compressed air is measured when it passes through the flow meter 30 .
- compressed air flows into the nozzle support arm 22 and is blown toward the polishing pad 14 from the openings 24 a of the cooling nozzles 24 .
- the nozzle support arm 22 is rotatable about its own axis by a servomotor 31 .
- the blow direction of compressed air (dry gas), blown from the nozzle openings 24 a of the cooling nozzles 24 can be adjusted by rotating the nozzle support arm 22 .
- thermometer 32 e.g., a radiation thermometer, for detecting the temperature of the polishing pad 14 .
- the thermometer 32 is connected to a temperature controller 34 for setting a target temperature (i.e., control temperature) of the polishing pad 14 .
- the temperature controller 34 is connected to the pressure control valve 28 and the servomotor 31 , so that the pressure control valve 28 and the servomotor 31 can be PID-controlled by an output signal from the temperature controller 34 .
- a plurality of PID parameters are stored in the temperature controller 34 . Based on a difference between a set temperature (i.e., control temperature) of the polishing pad 14 , set in the temperature controller 34 , and the actual temperature of the polishing pad 14 detected by the thermometer 32 , a particular PID parameter is selected from the plurality of PID parameters and, based on information on the temperature of the polishing pad 14 detected by the thermometer 32 , the valve position of the pressure control valve 28 and the rotation angle of the servomotor 31 are controlled by an electropneumatic regulator (not shown) so that the polishing pad 14 becomes a predetermined temperature (i.e., control temperature).
- a set temperature i.e., control temperature
- the valve position of the pressure control valve 28 is controlled so that the flow rate of compressed air, blown from the cooling nozzles 24 toward the polishing pad 14 , becomes 50 to 1000 L/min, for example. It is possible to set at least one predetermined PID parameter in advance.
- the nozzle support arm 22 rotates by the rotation of the servomotor 31 .
- the rotation angle of the servomotor 31 is PID-controlled such that the blow direction of compressed air (dry gas), blown from the nozzle openings 24 a of the cooling nozzles 24 , can be adjusted.
- the rotation angle of the servomotor 31 is PID-controlled so that the angle of the blow direction of compressed air (dry gas), blown from the nozzle openings 24 a of the cooling nozzles 24 , with respect to the plane of the polishing pad 14 becomes larger and the cooling effect increases.
- the rotation angle of the servomotor 31 is PID-controlled so that the angle of the blow direction of compressed air with respect to the plane of the polishing pad 14 becomes smaller and the cooling effect decreases.
- valve position of the pressure control valve 28 and the rotation angle of the servomotor 31 are PID-controlled, it is possible to PID-control only one of the valve position of the pressure control valve 28 and the rotation angle of the servomotor 31 . This holds true for the below-described embodiments.
- the servomotor 31 is omitted in the below-described embodiments.
- cleaning nozzles 40 as a cleaning tool for cleaning the cooling nozzles 24 by spraying a cleaning liquid onto the cooling nozzles 24 are mounted to the nozzle support arm 22 via a bracket 42 .
- Each of the cleaning nozzles (cleaning tool) 40 has a nozzle opening 40 a with a predetermined opening angle ⁇ so that the cleaning liquid can be sprayed onto the entire area of the nozzle opening 24 a and its vicinity of each cooling nozzle 24 .
- the entire area of the nozzle opening 24 a and its vicinity of each cooling nozzle 24 is mainly cleaned with the cleaning liquid sprayed from each cleaning nozzle 40 .
- the polishing head 16 As shown in FIG. 3 , beside the polishing head 16 are provided two cleaning nozzles 44 , disposed above and below the polishing head 16 , for cleaning the polishing head 16 by jetting a cleaning liquid toward the peripheral end surface of the polishing head 16 from above and below.
- the slurry 18 which has been supplied onto the polishing pad 14 , is blown away by the compressed air and adheres to the peripheral end surface of the polishing head 16 .
- the slurry adhering to the peripheral end surface of the polishing head 16 can be removed by jetting the cleaning liquid from the head cleaning nozzles 44 toward the peripheral end surface of the polishing head 16 .
- the polishing apparatus is provided with a torque current monitor for monitoring the torque or current of the polishing table 12 to monitor the polishing state of a film to be polished, such as the thickness of the film.
- a torque current monitor for monitoring the torque or current of the polishing table 12
- a windshield plate 46 between the cooling nozzles 24 and the slurry supply nozzle 20 . This can prevent variation from being produced in the distribution of the slurry 18 to be supplied onto the polishing pad 14 from the slurry supply nozzle 20 , due to the influence of compressed air blown toward the polishing pad 14 from the cooling nozzles 24 , thereby preventing variation in the polishing performance.
- FIG. 5 schematically shows the overall construction of a polishing apparatus according to another embodiment of the present invention.
- This embodiment differs from the embodiment shown in FIGS. 1 through 3 in that a cooling fan 50 as a cooling device for blowing air as a dry gas toward the polishing pad 14 is disposed above the polishing table 12 so that the polishing pad 14 can be further cooled by the air blown from the cooling fan 50 .
- the provision of the cooling fan 50 in addition to the cooling nozzles 24 can increase the effect of cooling the polishing pad 14 . It is also possible to provide only the cooling fan 50 .
- FIG. 6 is a schematic plan view of a polishing apparatus according to yet another embodiment of the present invention.
- the polishing apparatus of this embodiment is configured to be capable of simultaneously polishing two substrates on one polishing table 12 .
- the polishing apparatus of this embodiment includes the polishing table 12 with a polishing pad 14 attached to the upper surface, and two polishing heads 16 .
- Positioned above the polishing pad 14 are disposed two sets of a nozzle support arm 22 provided with cooling nozzles 24 , a thermometer 32 and a slurry supply nozzle 20 , arranged in this order along a direction opposite to the direction of rotation of the polishing table 12 .
- the polishing pad 14 is brought into contact with the surfaces (to be polished) of two substrates, held by the polishing heads 16 , after a slurry 18 begins to be supplied from the slurry supply nozzles 20 , the temperature of the polishing pad 14 is measured with the thermometers 32 and the polishing pad 14 begins to be cooled by compressed air blown from the cooling nozzles 24 .
- the positional relationship between the nozzle support arm 22 provided with the cooling nozzles 24 , the thermometer 32 and the slurry supply nozzle 20 in each set is, of course, not limited to that of this embodiment.
- FIG. 7 shows an exemplary relationship between the temperature of a polishing pad and polishing rate.
- a specific temperature fastest polishing temperature
- the polishing rate decreases from the maximum polishing rate with decrease or increase in the temperature of the polishing pad from the fastest polishing temperature.
- Polishing of a surface (surface to be polished) of a substrate by the polishing apparatus shown in FIGS. 1 through 3 will now be described in the following three exemplary cases.
- a substrate W is prepared which, as shown in FIG. 8 , has insulating films 902 , 903 having via holes 904 and trenches 905 , a barrier film 906 formed on the insulating films 902 , 903 , and a metal film 907 formed on the barrier film 906 .
- Those portions of the metal film 907 which are embedded in the via holes 904 and the trenches 905 , constitute metal interconnects.
- the metal film is a copper film and the metal interconnects are copper interconnects.
- the supply pressure of compressed air to be supplied to the cooling nozzles 24 is confirmed. If this supply pressure is less than a specified pressure, a warning is issued and processing of subsequent substrates is stopped. When this supply pressure is not less than a specified pressure, the polishing head 16 in the substrate transfer position receives a substrate W, e.g., from a pusher and holds the substrate W by attraction. The substrate W held by the polishing head 16 is then moved horizontally from the substrate transfer position to the polishing position just above the polishing table 12 .
- thermometer 32 monitoring of the temperature of the polishing pad 14 with the thermometer 32 is started. Even when the temperature of the polishing pad 14 is then more than a set temperature, blowing of compressed air from the cooling nozzles 24 toward the polishing pad 14 is not started in order to prevent compressed air from directly hitting the substrate W, held by the polishing head 16 , before contact with the polishing head 14 .
- polishing head 16 While supplying a slurry 18 from the slurry supply nozzle 20 to the polishing pad 14 , the polishing head 16 is rotated and lowered to bring the surface (surface to be polished) of the substrate W, held by the polishing head 16 , into contact with the polishing surface 14 a of the polishing pad 14 on the rotating polishing table 12 . Thereafter, the substrate W is released from the attraction to the polishing head 16 , and the surface of the substrate W is pressed against the polishing surface 14 a at a first polishing pressure. Polishing of the metal film (copper film) 907 shown in FIG. 8 is thus started (first polishing step).
- control of the temperature of the polishing pad 14 with the cooling nozzles 24 is started when the substrate W comes into contact with the polishing surface 14 a.
- control of the temperature of the polishing pad 14 with the cooling nozzle 24 is started simultaneously with the start of rotation of the polishing table 12 .
- the flow rate and the blow direction of compressed air, blown from the cooling nozzles 24 toward the polishing pad 14 are PID-controlled to control the temperature of the polishing pad 14 at a predetermined first temperature which can achieve the maximum polishing rate.
- the first polishing step is intended to shorten the total polishing time by using a high polishing pressure in combination with the cooling of the polishing pad 14 .
- the control temperature of the polishing pad 14 is set, e.g., at 50° C.
- the temperature of the polishing pad 14 if not cooled, would rise up to, e.g., 60° C.
- the first polishing step is terminated when surface irregularities of the metal film (copper film) 907 have been removed, as shown by the imaginary line A in FIG. 8 , and the barrier film 906 , underlying the metal film 907 , begins to be exposed, for example, when the torque current monitor detects that a predetermined thickness of the metal film (copper film) 907 , e.g., 100 nm to 300 nm, is reached.
- the flow rate and the blow direction of compressed air, blown from the cooling nozzles 24 toward the polishing pad 14 are PID-controlled to control the temperature of the polishing pad 14 at a predetermined second temperature which can achieve best planarities of the surface of the substrate or can achieve the minimum number of defects or the minimum amount of unpolished film, and polishing is continued while thus controlling the temperature of the polishing pad 14 (second polishing step).
- polishing may be carried out in a low-pressure polishing manner by pressing the surface of the substrate W against the polishing surface 14 a at a second polishing pressure which is lower than the first polishing pressure, as necessary. Furthermore, the maximum possible cooling of the polishing pad 14 may be performed, e.g., at a set temperature of 0° C.
- the second polishing step is terminated when the torque current monitor detects that the extra metal film (copper film) 907 lying outside the trenches 905 has been polished away and the surface of the underlying barrier film 906 has become completely exposed, as shown by the imaginary line B in FIG. 8 .
- the temperature of the polishing pad 14 may be controlled in such a manner that a desired temperature is reached at the time when the surface of the barrier film 906 has become completely exposed.
- the end of the first polishing step is detected by in-situ monitoring of the polishing state (the polishing rate, the polishing amount, the thickness of the remaining film, etc.) and, after the polishing is shifted to the second polishing step, the remaining polishing time until the end of polishing is calculated from monitored values.
- the temperature of the polishing pad 14 is then controlled so that the current temperature of the polishing pad 14 gradually changes and reaches a desired temperature after the remaining polishing time. This can reduce the influence of the rapid temperature change in the polishing pad 14 on the polishing.
- the first polishing step is shifted to the second polishing step when the film thickness detected, e.g., by an eddy current sensor or an optical sensor has reached a target thickness.
- the film thickness at the start of the second polishing step is thus known.
- the polishing rate in the second step can be determined by monitoring change with time in the thickness of the remaining film for an appropriate amount of time (about a few seconds) and differentiating the change.
- the remaining polishing time can be determined from the polishing rate and the thickness of the remaining film.
- the program is designed to enable input of target temperatures at the start and the end of the second polishing step.
- the remaining polishing time can be determined as described above.
- the polishing pad 14 can be brought into a predetermined temperature after a predetermined amount of time.
- the number of PID target temperatures, which vary with time, and the time intervals between them can be set arbitrarily.
- water polishing of the substrate W is carried out by supplying pure water to the polishing pad 14 .
- the polishing head 16 attracts the substrate W after polishing and detaches it from the polishing surface 14 a.
- the stoppage of blowing of compressed air from the cooling nozzle 24 is continued while the substrate W lies above the polishing table 12 in order to prevent compressed air from hitting and drying the surface of the substrate W lying above the polishing table 12 .
- the polishing head 16 holding the substrate W is raised and then moved horizontally from the polishing position to the substrate transfer position, where the substrate W after polishing is transferred to, e.g., a pusher.
- self-cleaning of the cooling nozzles 24 is carried out by spraying a cleaning liquid (water) from the cleaning nozzles 40 onto the cooling nozzles 24 , in particular the nozzle openings 24 a and their vicinity.
- the cleaning liquid may be caused to flow rapidly on the polishing table 12 so as to prevent dirt, such as the slurry, that has fallen off the cooling nozzles 24 onto the polishing table 12 from remaining on the polishing table 12 (polishing surface 14 a ) and adversely affecting processing of the next substrate.
- the nozzle support arm 22 It is possible to design the nozzle support arm 22 to be movable to a stand-by position beside the polishing table 12 , and to carry out cleaning of the cooling nozzles 24 by the cleaning nozzles 40 at the stand-by position. This can prevent dirt such as the slurry, attached to the cooling nozzles 24 , from falling onto the polishing table 12 .
- a cleaning liquid water
- a cleaning liquid water
- a substrate W as shown in FIG. 8 which is similar to the substrate W of the above-described case 1, is prepared.
- the metal film 907 is a tungsten film and the metal interconnects are tungsten interconnects.
- the supply pressure of compressed air, to be supplied to the cooling nozzles 24 is confirmed.
- this supply pressure is not less than a specified pressure
- the polishing head 16 in the substrate transfer position receives a substrate W, e.g., from a pusher and holds the substrate W by attraction.
- the substrate W held by the polishing head 16 is then moved horizontally from the substrate transfer position to the polishing position just above the polishing table 12 .
- thermometer 32 Next, monitoring of the temperature of the polishing pad 14 with the thermometer 32 is started. As with the case 1, blowing of compressed air from the cooling nozzles 24 toward the polishing pad 14 is not yet started.
- polishing head 16 While supplying a slurry 18 from the slurry supply nozzle 20 to the polishing pad 14 , the polishing head 16 is rotated and lowered to bring the surface (surface to be polished) of the substrate W, held by the polishing head 16 , into contact with the polishing surface 14 a of the polishing pad 14 on the rotating polishing table 12 . Thereafter, the substrate W is released from the attraction to the polishing head 16 , and the surface of the substrate W is pressed against the polishing surface 14 a at a first polishing pressure. Polishing of the metal film (tungsten film) 907 , shown in FIG. 8 , is thus started (first polishing step).
- control of the temperature of the polishing pad 14 with the cooling nozzle 24 is started when the substrate W comes into contact with the polishing surface 14 a.
- control of the temperature of the polishing pad 14 with the cooling nozzle 24 is started simultaneously with the start of rotation of the polishing table 12 .
- the flow rate and the blow direction of compressed air, blown from the cooling nozzles 24 toward the polishing pad 14 are PID-controlled to control the temperature of the polishing pad 14 at a predetermined first temperature which can achieve the maximum polishing rate.
- the first polishing step is intended to shorten the total polishing time by using a high polishing pressure in combination with the cooling of the polishing pad 14 .
- the control temperature of the polishing pad 14 is set, e.g., at 0° C. and the maximum possible cooling of the polishing pad 14 is performed.
- the temperature of the polishing pad 14 if not cooled, would rise up to, e.g., 70° C.
- the first polishing step is terminated when surface irregularities of the metal film (tungsten film) 907 have been removed, as shown by the imaginary line A in FIG. 8 , and the barrier film 906 , underlying the metal film 907 , begins to be exposed, for example, when the torque current monitor detects that a predetermined thickness of the metal film (tungsten film) 907 , e.g., 100 nm to 300 nm, is reached.
- polishing may be carried out in a low-pressure polishing manner by pressing the surface of the substrate W against the polishing surface 14 a at a second polishing pressure which is lower than the first polishing pressure, as necessary.
- the maximum possible cooling of the polishing pad 14 may be performed, e.g., at a set temperature of 0° C.
- the second polishing step is terminated when the torque current monitor detects that the extra metal film (tungsten film) 907 lying outside the trenches 905 has been polished away and the surface of the underlying barrier film 906 has become completely exposed, as shown by the imaginary line B in FIG. 8 .
- the case 3 is applicable to an STI (shallow trench isolation) process, a polysilicon removal process, a barrier layer removal process, etc.
- a substrate W is prepared.
- the substrate W comprises a silicon wafer 100 having trenches, a pad oxide film 104 which covers the surface of the silicon wafer 100 , an SiN film 103 formed on the pad oxide film 104 and lying outside the trenches, and an SiO 2 film 102 of a insulating film which fills the trenches of the silicon wafer 100 and covers an entire surface of the substrate W.
- the supply pressure of compressed air, to be supplied to the cooling nozzle 24 is confirmed.
- this supply pressure is not less than a specified pressure
- the polishing head 16 in the substrate transfer position receives a substrate W, e.g., from a pusher and holds the substrate W by attraction.
- the substrate W held by the polishing head 16 is then moved horizontally from the substrate transfer position to the polishing position just above the polishing table 12 .
- thermometer 32 Next, monitoring of the temperature of the polishing pad 14 with the thermometer 32 is started. As with the case 1, blowing of compressed air from the cooling nozzles 24 toward the polishing pad 14 is not yet started.
- polishing head 16 While supplying a slurry 18 from the slurry supply nozzle 20 to the polishing pad 14 , the polishing head 16 is rotated and lowered to bring the surface (surface to be polished) of the substrate W, held by the polishing head 16 , into contact with the polishing surface 14 a of the polishing pad 14 on the rotating polishing table 12 . Thereafter, the substrate W is released from the attraction to the polishing head 16 , and the surface of the substrate W is pressed against the polishing surface 14 a at a first polishing pressure. Polishing of the SiO 2 film (insulating film) 102 shown in FIG. 9 is thus started (first polishing step).
- control of the temperature of the polishing pad 14 with the cooling nozzles 24 is started when the substrate W comes into contact with the polishing surface 14 a.
- control of the temperature of the polishing pad 14 with the cooling nozzles 24 is started simultaneously with the start of rotation of the polishing table 12 .
- the flow rate and the blow direction of compressed air, blown from the cooling nozzles 24 toward the polishing pad 14 are PID-controlled to control the temperature of the polishing pad 14 at a predetermined first temperature which can achieve the maximum polishing rate.
- the first polishing step is intended to shorten the total polishing time by using a high polishing pressure in combination with the cooling of the polishing pad 14 .
- the control temperature of the polishing pad 14 is set, e.g., at 50° C.
- the temperature of the polishing pad 14 if not cooled, would rise up to, e.g., 60° C.
- the first polishing step is terminated when the torque current monitor detects that surface irregularities of the SiO 2 film 102 have been removed, as shown by the imaginary line C in FIG. 9 .
- the flow rate and the blow direction of compressed air, blown from the cooling nozzles 24 toward the polishing pad 14 are PID-controlled to control the temperature of the polishing pad 14 at a predetermined second temperature which can best remove surface irregularities, and polishing is continued while thus controlling the temperature of the polishing pad 14 (second polishing step).
- second polishing step a low additive flow rate is used to increase the polishing rate for the SiO 2 film 102 .
- the maximum possible cooling of the polishing pad 14 may be performed, e.g., at a set temperature of 0° C. to improve the planarities.
- the cooling of the polishing pad 14 in the second polishing step may decrease the polishing rate. However, a prolonged total polishing time can be avoided by the use of a low additive flow rate which can increase the polishing rate.
- the second polishing step is terminated when the torque current monitor detects that the extra SiO 2 film 102 lying outside the trenches has been polished away and the surface of the underlying SiN film 103 has become completely exposed, as shown by the imaginary line D in FIG. 9 .
- the temperature of the polishing pad 14 is adjusted in the second polishing step by supplying a dry gas, such as compressed air, to the polishing pad 14 , it is also possible to adjust the temperature of the polishing pad 14 by supplying a mist to the polishing pad 14 .
- a mist for the adjustment of the temperature of the polishing pad 14 can increase the effect of cooling the polishing pad 14 .
- PID control is used for the adjustment of the temperature of the polishing pad 14 in the second polishing step, it is also possible to perform the maximum possible cooling of the polishing pad 14 without using PID control, e.g., by maximizing the valve position of an electropneumatic regulator which may be PID-controlled in the first polishing step.
- the temperature of the polishing pad 14 is controlled (cooled) in the first polishing step, it is possible to carry out the first polishing step without controlling (cooling) the temperature of the polishing pad 14 , and to cool the polishing pad 14 to below a predetermined temperature in the second polishing step.
- the control (cooling) temperature of the polishing pad 14 is changed between the first polishing step and the second polishing step, it is also possible to cool the polishing pad 14 such that the temperature of the polishing pad 14 is kept constant throughout the first and second polishing steps.
- a target control temperature in the second polishing step may be set also in the first polishing step. This may lead to a lowering of the polishing rate in the first polishing rate.
- the efficiency of polishing in the second polishing step can be increased because of no time lag of the polishing pad temperature associated with change of pad control temperature.
Landscapes
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Physics & Mathematics (AREA)
- Condensed Matter Physics & Semiconductors (AREA)
- General Physics & Mathematics (AREA)
- Manufacturing & Machinery (AREA)
- Computer Hardware Design (AREA)
- Microelectronics & Electronic Packaging (AREA)
- Power Engineering (AREA)
- Mechanical Treatment Of Semiconductor (AREA)
- Finish Polishing, Edge Sharpening, And Grinding By Specific Grinding Devices (AREA)
- Constituent Portions Of Griding Lathes, Driving, Sensing And Control (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2011009612A JP2012148376A (ja) | 2011-01-20 | 2011-01-20 | 研磨方法及び研磨装置 |
JP2011-009612 | 2011-01-20 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20120190273A1 true US20120190273A1 (en) | 2012-07-26 |
Family
ID=45507413
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/348,859 Abandoned US20120190273A1 (en) | 2011-01-20 | 2012-01-12 | Polishing method and polishing apparatus |
Country Status (6)
Country | Link |
---|---|
US (1) | US20120190273A1 (zh) |
EP (1) | EP2478999A2 (zh) |
JP (1) | JP2012148376A (zh) |
KR (1) | KR20120084671A (zh) |
CN (1) | CN102601719A (zh) |
TW (1) | TW201248707A (zh) |
Cited By (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN103659575A (zh) * | 2012-09-24 | 2014-03-26 | 株式会社荏原制作所 | 研磨方法及研磨装置 |
US20150352686A1 (en) * | 2012-02-14 | 2015-12-10 | Taiwan Semiconductor Manufacturing Co., Ltd. | Chemical mechanical polishing (cmp) platform for local profile control |
WO2019099399A1 (en) * | 2017-11-14 | 2019-05-23 | Applied Materials, Inc. | Temperature control of chemical mechanical polishing |
US20190389032A1 (en) * | 2018-06-21 | 2019-12-26 | Illinois Tool Works Inc. | Methods and apparatus to control a fluid dispenser on a metallurgical specimen preparation machine |
WO2020172215A1 (en) * | 2019-02-20 | 2020-08-27 | Applied Materials, Inc. | Apparatus and method for cmp temperature control |
US20210046604A1 (en) * | 2019-08-13 | 2021-02-18 | Applied Materials, Inc. | Apparatus and method for cmp temperature control |
US20210402552A1 (en) * | 2020-06-30 | 2021-12-30 | Applied Materials, Inc. | Gas entrainment during jetting of fluid for temperature control in chemical mechanical polishing |
WO2022187023A1 (en) * | 2021-03-03 | 2022-09-09 | Applied Materials, Inc. | Temperature controlled rate of removal in cmp |
US11446711B2 (en) | 2019-05-29 | 2022-09-20 | Applied Materials, Inc. | Steam treatment stations for chemical mechanical polishing system |
WO2022256059A1 (en) * | 2021-06-02 | 2022-12-08 | Revasum, Inc. | Polishing pad surface cooling by compressed gas |
US11597052B2 (en) | 2018-06-27 | 2023-03-07 | Applied Materials, Inc. | Temperature control of chemical mechanical polishing |
US11628478B2 (en) | 2019-05-29 | 2023-04-18 | Applied Materials, Inc. | Steam cleaning of CMP components |
US11633833B2 (en) | 2019-05-29 | 2023-04-25 | Applied Materials, Inc. | Use of steam for pre-heating of CMP components |
US11697187B2 (en) | 2019-04-18 | 2023-07-11 | Applied Materials, Inc. | Temperature-based assymetry correction during CMP and nozzle for media dispensing |
US11752589B2 (en) | 2019-04-18 | 2023-09-12 | Applied Materials, Inc. | Chemical mechanical polishing temperature scanning apparatus for temperature control |
US11826872B2 (en) | 2020-06-29 | 2023-11-28 | Applied Materials, Inc. | Temperature and slurry flow rate control in CMP |
US11833637B2 (en) | 2020-06-29 | 2023-12-05 | Applied Materials, Inc. | Control of steam generation for chemical mechanical polishing |
US11897079B2 (en) | 2019-08-13 | 2024-02-13 | Applied Materials, Inc. | Low-temperature metal CMP for minimizing dishing and corrosion, and improving pad asperity |
US11919123B2 (en) | 2020-06-30 | 2024-03-05 | Applied Materials, Inc. | Apparatus and method for CMP temperature control |
US11986921B2 (en) | 2020-10-16 | 2024-05-21 | Samsung Electronics Co., Ltd. | Chemical mechanical polishing apparatus, chemical mechanical polishing method and method for fabricating semiconductor device |
Families Citing this family (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN103586772B (zh) * | 2012-08-16 | 2016-01-06 | 鸿富锦精密工业(深圳)有限公司 | 压力检测装置 |
EP2910334A4 (en) * | 2012-10-03 | 2016-08-03 | Fujimi Inc | POLISHING METHOD AND METHOD FOR PRODUCING AN ALLOYING MATERIAL |
JP5890768B2 (ja) * | 2012-11-19 | 2016-03-22 | 株式会社東京精密 | 半導体ウエハ加工装置 |
JP5890767B2 (ja) * | 2012-11-19 | 2016-03-22 | 株式会社東京精密 | 半導体ウエハの厚み測定方法及び半導体ウエハ加工装置 |
TWI517935B (zh) * | 2013-04-16 | 2016-01-21 | 國立台灣科技大學 | 氣體添加硏磨液的供應系統及其方法 |
CN103223638B (zh) * | 2013-04-28 | 2016-04-13 | 上海华力微电子有限公司 | 化学机械研磨设备 |
JP6270345B2 (ja) * | 2013-06-05 | 2018-01-31 | キヤノン株式会社 | 光学素子の製造方法 |
JP6161999B2 (ja) | 2013-08-27 | 2017-07-12 | 株式会社荏原製作所 | 研磨方法および研磨装置 |
JP6139420B2 (ja) * | 2014-01-10 | 2017-05-31 | 株式会社東芝 | 研磨装置および研磨方法 |
JP6353266B2 (ja) * | 2014-04-17 | 2018-07-04 | 株式会社荏原製作所 | 冷却装置、及び、基板処理装置 |
CN104044055A (zh) * | 2014-05-30 | 2014-09-17 | 京东方科技集团股份有限公司 | 基板研磨方法及装置 |
KR101700869B1 (ko) * | 2015-03-12 | 2017-01-31 | 주식회사 케이씨텍 | 화학 기계적 연마 장치 및 이에 사용되는 온도조절패드 |
CN107520751A (zh) * | 2016-06-22 | 2017-12-29 | 汪超 | 一种立式玻璃四边磨边机的玻璃边缘探测装置 |
JP6736404B2 (ja) * | 2016-07-26 | 2020-08-05 | 株式会社ディスコ | 研削装置 |
JP6823541B2 (ja) * | 2017-05-30 | 2021-02-03 | 株式会社荏原製作所 | キャリブレーション方法およびキャリブレーションプログラム |
CN107088825A (zh) * | 2017-06-06 | 2017-08-25 | 上海华力微电子有限公司 | 化学机械研磨机台、温度控制系统及其温度控制方法 |
CN109262446B (zh) * | 2017-07-12 | 2021-03-19 | 中芯国际集成电路制造(上海)有限公司 | 一种化学机械研磨方法和化学机械研磨装置 |
JP6847811B2 (ja) * | 2017-10-24 | 2021-03-24 | 株式会社荏原製作所 | 研磨方法および研磨装置 |
JP7397617B2 (ja) * | 2019-10-16 | 2023-12-13 | 株式会社荏原製作所 | 研磨装置 |
CN113070809B (zh) * | 2019-12-17 | 2022-07-05 | 大量科技股份有限公司 | 化学机械研磨装置的研磨垫检测方法与研磨垫检测装置 |
CN114012597A (zh) * | 2021-12-01 | 2022-02-08 | 浙江晶越半导体有限公司 | 一种碳化硅研磨的装置和方法 |
CN117260429B (zh) * | 2023-11-22 | 2024-02-02 | 铭扬半导体科技(合肥)有限公司 | 一种抛光设备的控制方法 |
Citations (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5722875A (en) * | 1995-05-30 | 1998-03-03 | Tokyo Electron Limited | Method and apparatus for polishing |
US6524165B1 (en) * | 1998-11-02 | 2003-02-25 | Applied Materials, Inc. | Method and apparatus for measuring substrate layer thickness during chemical mechanical polishing |
US6562185B2 (en) * | 2001-09-18 | 2003-05-13 | Advanced Micro Devices, Inc. | Wafer based temperature sensors for characterizing chemical mechanical polishing processes |
US6568989B1 (en) * | 1999-04-01 | 2003-05-27 | Beaver Creek Concepts Inc | Semiconductor wafer finishing control |
US20030186623A1 (en) * | 2002-03-29 | 2003-10-02 | Lam Research Corp. | Method and apparatus for heating polishing pad |
US6899609B2 (en) * | 2002-10-22 | 2005-05-31 | Samsung Electronics Co., Ltd. | CMP equipment for use in planarizing a semiconductor wafer |
US20070010168A1 (en) * | 2004-03-09 | 2007-01-11 | Micron Technology, Inc. | Methods and systems for planarizing workpieces, e.g., microelectronic workpieces |
US7220164B1 (en) * | 2003-12-08 | 2007-05-22 | Beaver Creek Concepts Inc | Advanced finishing control |
US20070135020A1 (en) * | 2005-12-09 | 2007-06-14 | Osamu Nabeya | Polishing apparatus and polishing method |
US20090191795A1 (en) * | 2008-01-24 | 2009-07-30 | Jsr Corporation | Composition for forming polishing layer of chemical mechanical polishing pad, chemical mechanical polishing pad and chemical mechanical polishing method |
Family Cites Families (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3132111B2 (ja) * | 1991-11-29 | 2001-02-05 | ソニー株式会社 | 半導体装置の製造方法及びこれに用いるポリッシュパッド |
JP4051116B2 (ja) * | 1997-12-25 | 2008-02-20 | 不二越機械工業株式会社 | ウェーハの研磨装置 |
US7041599B1 (en) | 1999-12-21 | 2006-05-09 | Applied Materials Inc. | High through-put Cu CMP with significantly reduced erosion and dishing |
JP2001310256A (ja) * | 2000-04-26 | 2001-11-06 | Hitachi Chem Co Ltd | 半導体用基板の研磨方法 |
ATE313412T1 (de) * | 2001-06-26 | 2006-01-15 | Lam Res Corp | System zur endpunktbestimmung beim chemisch- mechanischen polieren |
JP2003037089A (ja) * | 2001-07-26 | 2003-02-07 | Shin Etsu Handotai Co Ltd | ウェーハの研磨方法 |
JP4799122B2 (ja) | 2005-10-20 | 2011-10-26 | 株式会社東芝 | Cu膜の研磨方法および半導体装置の製造方法 |
JP2010272635A (ja) * | 2009-05-20 | 2010-12-02 | Fujifilm Corp | 化学的機械的研磨方法 |
-
2011
- 2011-01-20 JP JP2011009612A patent/JP2012148376A/ja active Pending
-
2012
- 2012-01-04 TW TW101100305A patent/TW201248707A/zh unknown
- 2012-01-12 US US13/348,859 patent/US20120190273A1/en not_active Abandoned
- 2012-01-18 EP EP12000278A patent/EP2478999A2/en not_active Withdrawn
- 2012-01-18 CN CN2012100211639A patent/CN102601719A/zh active Pending
- 2012-01-18 KR KR1020120005466A patent/KR20120084671A/ko not_active Application Discontinuation
Patent Citations (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5722875A (en) * | 1995-05-30 | 1998-03-03 | Tokyo Electron Limited | Method and apparatus for polishing |
US6524165B1 (en) * | 1998-11-02 | 2003-02-25 | Applied Materials, Inc. | Method and apparatus for measuring substrate layer thickness during chemical mechanical polishing |
US6568989B1 (en) * | 1999-04-01 | 2003-05-27 | Beaver Creek Concepts Inc | Semiconductor wafer finishing control |
US6562185B2 (en) * | 2001-09-18 | 2003-05-13 | Advanced Micro Devices, Inc. | Wafer based temperature sensors for characterizing chemical mechanical polishing processes |
US20030186623A1 (en) * | 2002-03-29 | 2003-10-02 | Lam Research Corp. | Method and apparatus for heating polishing pad |
US6899609B2 (en) * | 2002-10-22 | 2005-05-31 | Samsung Electronics Co., Ltd. | CMP equipment for use in planarizing a semiconductor wafer |
US7220164B1 (en) * | 2003-12-08 | 2007-05-22 | Beaver Creek Concepts Inc | Advanced finishing control |
US20070010168A1 (en) * | 2004-03-09 | 2007-01-11 | Micron Technology, Inc. | Methods and systems for planarizing workpieces, e.g., microelectronic workpieces |
US20070135020A1 (en) * | 2005-12-09 | 2007-06-14 | Osamu Nabeya | Polishing apparatus and polishing method |
US20090191795A1 (en) * | 2008-01-24 | 2009-07-30 | Jsr Corporation | Composition for forming polishing layer of chemical mechanical polishing pad, chemical mechanical polishing pad and chemical mechanical polishing method |
Cited By (31)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20150352686A1 (en) * | 2012-02-14 | 2015-12-10 | Taiwan Semiconductor Manufacturing Co., Ltd. | Chemical mechanical polishing (cmp) platform for local profile control |
US10065288B2 (en) * | 2012-02-14 | 2018-09-04 | Taiwan Semiconductor Manufacturing Co., Ltd. | Chemical mechanical polishing (CMP) platform for local profile control |
CN103659575A (zh) * | 2012-09-24 | 2014-03-26 | 株式会社荏原制作所 | 研磨方法及研磨装置 |
US9233448B2 (en) | 2012-09-24 | 2016-01-12 | Ebara Corporation | Adjusting a substrate polishing condition |
US9561575B2 (en) | 2012-09-24 | 2017-02-07 | Ebara Corporation | Adjusting a substrate polishing condition |
TWI630981B (zh) * | 2012-09-24 | 2018-08-01 | 荏原製作所股份有限公司 | Grinding method and grinding device |
WO2019099399A1 (en) * | 2017-11-14 | 2019-05-23 | Applied Materials, Inc. | Temperature control of chemical mechanical polishing |
CN111149196A (zh) * | 2017-11-14 | 2020-05-12 | 应用材料公司 | 化学机械研磨的温度控制 |
TWI825043B (zh) * | 2017-11-14 | 2023-12-11 | 美商應用材料股份有限公司 | 用於化學機械研磨的溫度控制的方法與系統 |
US20190389032A1 (en) * | 2018-06-21 | 2019-12-26 | Illinois Tool Works Inc. | Methods and apparatus to control a fluid dispenser on a metallurgical specimen preparation machine |
US11787007B2 (en) * | 2018-06-21 | 2023-10-17 | Illinois Tool Works Inc. | Methods and apparatus to control a fluid dispenser on a metallurgical specimen preparation machine |
US11597052B2 (en) | 2018-06-27 | 2023-03-07 | Applied Materials, Inc. | Temperature control of chemical mechanical polishing |
WO2020172215A1 (en) * | 2019-02-20 | 2020-08-27 | Applied Materials, Inc. | Apparatus and method for cmp temperature control |
US11697187B2 (en) | 2019-04-18 | 2023-07-11 | Applied Materials, Inc. | Temperature-based assymetry correction during CMP and nozzle for media dispensing |
US11752589B2 (en) | 2019-04-18 | 2023-09-12 | Applied Materials, Inc. | Chemical mechanical polishing temperature scanning apparatus for temperature control |
US11865671B2 (en) | 2019-04-18 | 2024-01-09 | Applied Materials, Inc. | Temperature-based in-situ edge assymetry correction during CMP |
US11446711B2 (en) | 2019-05-29 | 2022-09-20 | Applied Materials, Inc. | Steam treatment stations for chemical mechanical polishing system |
US11628478B2 (en) | 2019-05-29 | 2023-04-18 | Applied Materials, Inc. | Steam cleaning of CMP components |
US11633833B2 (en) | 2019-05-29 | 2023-04-25 | Applied Materials, Inc. | Use of steam for pre-heating of CMP components |
US20210046604A1 (en) * | 2019-08-13 | 2021-02-18 | Applied Materials, Inc. | Apparatus and method for cmp temperature control |
US11897079B2 (en) | 2019-08-13 | 2024-02-13 | Applied Materials, Inc. | Low-temperature metal CMP for minimizing dishing and corrosion, and improving pad asperity |
US11826872B2 (en) | 2020-06-29 | 2023-11-28 | Applied Materials, Inc. | Temperature and slurry flow rate control in CMP |
US11833637B2 (en) | 2020-06-29 | 2023-12-05 | Applied Materials, Inc. | Control of steam generation for chemical mechanical polishing |
CN115175786A (zh) * | 2020-06-30 | 2022-10-11 | 应用材料公司 | 用于化学机械抛光中温度控制的流体喷流期间的气体输送 |
US20210402552A1 (en) * | 2020-06-30 | 2021-12-30 | Applied Materials, Inc. | Gas entrainment during jetting of fluid for temperature control in chemical mechanical polishing |
US11577358B2 (en) * | 2020-06-30 | 2023-02-14 | Applied Materials, Inc. | Gas entrainment during jetting of fluid for temperature control in chemical mechanical polishing |
US11919123B2 (en) | 2020-06-30 | 2024-03-05 | Applied Materials, Inc. | Apparatus and method for CMP temperature control |
US11986921B2 (en) | 2020-10-16 | 2024-05-21 | Samsung Electronics Co., Ltd. | Chemical mechanical polishing apparatus, chemical mechanical polishing method and method for fabricating semiconductor device |
WO2022187023A1 (en) * | 2021-03-03 | 2022-09-09 | Applied Materials, Inc. | Temperature controlled rate of removal in cmp |
US20220388117A1 (en) * | 2021-06-02 | 2022-12-08 | Revasum, Inc. | Polishing pad surface cooling by compressed gas |
WO2022256059A1 (en) * | 2021-06-02 | 2022-12-08 | Revasum, Inc. | Polishing pad surface cooling by compressed gas |
Also Published As
Publication number | Publication date |
---|---|
EP2478999A2 (en) | 2012-07-25 |
TW201248707A (en) | 2012-12-01 |
KR20120084671A (ko) | 2012-07-30 |
JP2012148376A (ja) | 2012-08-09 |
CN102601719A (zh) | 2012-07-25 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20120190273A1 (en) | Polishing method and polishing apparatus | |
US10259098B2 (en) | Method and apparatus for polishing a substrate | |
US20230415296A1 (en) | Apparatus and method for cmp temperature control | |
TWI527106B (zh) | 研磨方法 | |
JP6030720B2 (ja) | 研磨装置および方法 | |
US9731401B2 (en) | Method and apparatus for conditioning polishing pad | |
US20200406310A1 (en) | Steam generation for chemical mechanical polishing | |
US11446711B2 (en) | Steam treatment stations for chemical mechanical polishing system | |
US11897079B2 (en) | Low-temperature metal CMP for minimizing dishing and corrosion, and improving pad asperity | |
US11628478B2 (en) | Steam cleaning of CMP components | |
US20210046603A1 (en) | Slurry temperature control by mixing at dispensing | |
US20230256562A1 (en) | Use of steam for pre-heating of cmp components | |
TWI826877B (zh) | 拋光基板及匹配拋光系統之間的拋光效能的方法 | |
US7166015B2 (en) | Apparatus and method for controlling fluid material composition on a polishing pad | |
JP2009033105A (ja) | 半導体装置の製造方法 | |
US20220359219A1 (en) | Chemical Mechanical Polishing With Die-Based Modification | |
US20220281070A1 (en) | Slurry-based temperature control for cmp | |
US20040214508A1 (en) | Apparatus and method for controlling film thickness in a chemical mechanical planarization system | |
WO2020243305A1 (en) | Use of steam for pre-heating or cleaning of cmp components |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: EBARA CORPORATION, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ONO, KATSUTOSHI;MATSUO, HISANORI;REEL/FRAME:027524/0225 Effective date: 20111227 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |