US20120177527A1 - Bearing steels - Google Patents

Bearing steels Download PDF

Info

Publication number
US20120177527A1
US20120177527A1 US13/386,346 US201013386346A US2012177527A1 US 20120177527 A1 US20120177527 A1 US 20120177527A1 US 201013386346 A US201013386346 A US 201013386346A US 2012177527 A1 US2012177527 A1 US 2012177527A1
Authority
US
United States
Prior art keywords
bearing
steel composition
composition
nitrogen
steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/386,346
Other languages
English (en)
Inventor
Aidan Michael Kerrigan
Mohamed Sherif
Henrik Karlsson
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SKF AB
Original Assignee
SKF AB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SKF AB filed Critical SKF AB
Assigned to AKTIEBOLAGET SKF reassignment AKTIEBOLAGET SKF ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KERRIGAN, AIDAN MICHAEL, KARLSSON, HENRIK, SHERIF, MOHAMED
Publication of US20120177527A1 publication Critical patent/US20120177527A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C21D1/25—Hardening, combined with annealing between 300 degrees Celsius and 600 degrees Celsius, i.e. heat refining ("Vergüten")
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/38—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for roll bodies
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/40—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for rings; for bearing races
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C33/00—Making ferrous alloys
    • C22C33/02—Making ferrous alloys by powder metallurgy
    • C22C33/0257—Making ferrous alloys by powder metallurgy characterised by the range of the alloying elements
    • C22C33/0278—Making ferrous alloys by powder metallurgy characterised by the range of the alloying elements with at least one alloying element having a minimum content above 5%
    • C22C33/0285—Making ferrous alloys by powder metallurgy characterised by the range of the alloying elements with at least one alloying element having a minimum content above 5% with Cr, Co, or Ni having a minimum content higher than 5%
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C33/00—Parts of bearings; Special methods for making bearings or parts thereof
    • F16C33/30—Parts of ball or roller bearings
    • F16C33/58—Raceways; Race rings
    • F16C33/62—Selection of substances
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C33/00—Parts of bearings; Special methods for making bearings or parts thereof
    • F16C33/30—Parts of ball or roller bearings
    • F16C33/58—Raceways; Race rings
    • F16C33/64—Special methods of manufacture
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2998/00—Supplementary information concerning processes or compositions relating to powder metallurgy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2998/00—Supplementary information concerning processes or compositions relating to powder metallurgy
    • B22F2998/10—Processes characterised by the sequence of their steps
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C2220/00—Shaping
    • F16C2220/20—Shaping by sintering pulverised material, e.g. powder metallurgy

Definitions

  • the present invention relates to the field of steels and bearings. More specifically, the present invention relates to a novel bearing steel composition and a method of forming a bearing.
  • Rolling element bearings are devices that permit constrained relative motion between two parts.
  • Rolling element bearings comprise inner and outer raceways and a plurality of rolling elements (balls or rollers) disposed therebetween.
  • rolling elements balls or rollers
  • Chromium is a common alloying element and is used to resist corrosion and rusting.
  • Stainless steels and surgical stainless steels contain a minimum of 10% chromium.
  • An example of a stainless steel composition is Böhler N360 Isoextra®.
  • This steel comprises 0.30 wt % carbon (C), 0.60 wt % silicon (Si), 0.40 wt % manganese (Mn), 15.00 wt % chromium (Cr), 1.00 wt % molybdenum (Mo) and 0.40 wt % nitrogen (N).
  • the steel is a corrosion resistant, martensitically hardened stainless steel which exhibits high hardness and compressive strength.
  • the Böhler N360 Isoextra® steel is produced using a pressurised electroslag remelting (P-ESR) process.
  • P-ESR pressurised electroslag remelting
  • a consumable electrode is dipped into a pool of slag in a water-cooled mould under a protective atmosphere.
  • An electric current usually AC
  • passes through the slag between the electrode and the ingot being formed and superheats the slag so that drops of metal are melted from the electrode.
  • the drops travel through the slag to the bottom of the water-cooled mould where they solidify.
  • the slag pool is carried upwards as the ingot forms.
  • the new ingot of refined material builds up slowly from the bottom of the mould.
  • the ingot formed is homogeneous and overcomes problems associated with core weakness in conventionally cast ingots as they solidify from the outside inwards.
  • the protective atmosphere used to produce Böhler N360 Isoextra® comprises nitrogen to increase the nitrogen content of the steel produced. Solid nitrogen-bearing additives are also added to the melt. Nitrogen is attractive as an inexpensive alloying element for enhancing the properties of steel. Due to the extremely short dwell time of the metal droplets in the liquid phase during remelting, the nitrogen pick-up via the gas phase is minimal but the high pressure in the system prevents the escape of nitrogen from additives introduced into the molten steel.
  • the present invention provides a bearing steel composition comprising:
  • Carbon about 0.4 to about 0.8 wt %; Nitrogen about 0.1 to about 0.2 wt %; Chromium about 12 to about 18 wt %; Molybdenum about 0.7 to about 1.3 wt %; Silicon about 0.3 to about 1 wt %; Manganese about 0.2 to about 0.8 wt %; and Iron about 78 to about 86.3 wt %.
  • the iron forms the balance of the composition, together with unavoidable impurities.
  • the present invention provides a bearing component formed from a composition as herein described.
  • the present invention provides a bearing comprising a bearing component according to the present invention.
  • the present invention provides a method of forming a steel bearing component.
  • the method comprises the steps of providing a powdered steel composition according to the present invention and subjecting it to hot isostatic pressing to form the component.
  • FIG. 1 shows a schematic diagram of an embodiment of the method of the present invention.
  • FIG. 2 shows a flowchart of the steps taken in an embodiment of the method of the present invention.
  • FIG. 3 shows a phase diagram of the composition of the present invention with changing carbon content and with a constant 0.15 wt % nitrogen content.
  • the bearing steel composition includes nitrogen in an amount of from 0.1 to 0.2 wt %, preferably from 0.11 to 0.18 wt % and more preferably from 0.13 to 0.17 wt %.
  • the nitrogen content serves to increase the hardness of the steel article.
  • the nitrogen concentration in austenite during steel processing at high temperature is dependent on the chromium, manganese and molybdenum concentrations and, accordingly, it is difficult to introduce more nitrogen into the composition unless the content of these alloying elements is increased. Additionally, resorting to pressure metallurgy can increase nitrogen solubility.
  • Carbon is included in an amount of from 0.4 to 0.8 wt %, preferably from 0.45 to 0.7 wt % and more preferably from 0.45 to 0.6 wt %.
  • the carbon serves to increase the hardness of the steel article formed. If there is less than 0.4% carbon then the steel will be insufficiently hard.
  • the carbon solubility is inversely related to the chromium concentration; if the chromium weight percent is increased then the carbon content in the final composition is likely to decrease.
  • the combined percentage of carbon and nitrogen present is from 0.5 to 1 wt %, more preferably from 0.5 to 0.88 wt %, more preferably from 0.5 to 0.77 wt % and most preferably from 0.5 to 0.7 wt %. These ranges have been found to provide the greatest hardness of the final steel composition.
  • the amount of carbon is preferably from 0.45 to 0.6 wt %. This helps provide the preferable total amount of carbon and nitrogen as noted above. This amount of carbon content with a nitrogen content of approximately 0.15 wt % allows a maximum amount of soluble interstitial atoms to be retained in the austenite, or martensite after hardening, to provide acceptable hardness/load carrying properties.
  • FIG. 3 shows a calculated pseudo-binary (isopleth) diagram for the composition of the present invention having a nitrogen content of 0.15 wt % and a variable carbon content.
  • a carbon content of 0.3 wt % the ⁇ -ferrite phase forms at about 1227° C.
  • the austenite region appears to be at its widest (in terms of temperature) with a carbon content of about 0.45 wt %, which allows for best workability.
  • FIG. 3 shows that the carbon content may be increased further as the ⁇ / ⁇ +L (liquid) phase line is not steeply decreasing.
  • Chromium is included in an amount of from 12 to 18 wt %, preferably from 15 to 17 wt % and more preferably from 15.5 to 16.5 wt %.
  • the chromium provides an improved corrosion resistance property to the steel.
  • the chromium leads to a hard oxide on the metal surface to inhibit corrosion.
  • Molybdenum is included in an amount of from 0.7 to 1.3 wt %, preferably from 0.9 to 1.1 wt %. Adding molybdenum to the steel imparts toughness for heavy service, and provides especially heat-resistant alloys. Conventional carbon steels have less than 0.5 wt % Mo, but having a greater amount of molybdenum in the present composition, in conjunction with the other alloying elements, improves mechanical properties such as hardness.
  • Silicon is included in an amount of from 0.3 to 1 wt %, preferably from 0.5 to 0.9 wt %.
  • Manganese is included in an amount of from 0.2 to 0.8 wt %, preferably from 0.3 to 0.6 wt %. The manganese increase hardenability and contributes to the steel's strength.
  • Iron is included in an amount of from 78 to 86.3 wt % and preferably as the balance of the composition, together with unavoidable impurities.
  • Other elements which may be present include oxygen, phosphorus and sulphur. It is preferred that these elements are present in an amount of 0.02 wt % or less.
  • the phosphorous content preferably does not exceed 0.01 wt %.
  • the sulphur content preferably does not exceed 0.002 wt %.
  • the oxygen content preferably does not exceed 0.0001 wt %.
  • the steel for use in the bearing component according to the present invention may contain unavoidable impurities, although, in total, these are unlikely to exceed 0.5 wt. % of the composition.
  • the alloys Preferably, contain unavoidable impurities in an amount of not more than 0.3 wt. % of the composition, more preferably not more than 0.1 wt. % of the composition.
  • the phosphorous and sulphur contents are preferably kept to a minimum.
  • the alloys according to the present invention may consist essentially of the recited elements. It will therefore be appreciated that in addition to those elements which are mandatory other non-specified elements may be present in the composition provided that the essential characteristics of the composition are not materially affected by their presence.
  • the steel according to the present invention will typically comprise austenite as the predominant phase. That is, at least 50 wt %, preferably at least 70 wt % and more preferably at least 90 wt % austenite.
  • the composition is substantially all austenite. That is, at least 95 wt %, more preferably 98 wt % and most preferably at least 99 wt % austenite.
  • Austenite is a metallic, non-magnetic solid solution of carbon and iron that forms in conventional steels above a critical temperature of 723° C. It has a face-centred cubic (FCC) structure that allows it to hold a high proportion of carbon in solution. When the steel composition is subjected to hardening and tempering it will exhibit a tempered martensite structure with some retained austenite as well as carbides/carbonitrides.
  • the phases and structures of steel are well known in the art.
  • austenite is cooled slowly, then the structure can break down into a mixture of ferrite and cementite (usually in the structural forms pearlite or bainite). Rapid cooling can result in martensite being formed. The rate of cooling determines the relative proportions of these phases and therefore the mechanical properties (e.g. hardness, tensile strength) of the steel. Quenching (to induce martensitic transformation), followed by tempering (to break down some martensite and retained austenite, as well as to precipitate some carbides/carbonitrides), is the most common heat treatment for high-performance steels. Deep cooling treatments after hardening and/or tempering stage(s) may also be applied.
  • the steel composition of the present invention preferably has a microstructure comprising martensite, any retained austenite and precipitated carbides and/or carbonitrides.
  • the method employed in the present invention is a form of powder metallurgy.
  • Powder metallurgy typically relies on a forming and fabrication technique comprising three major processing stages:
  • the method of the present invention forms at least a wear portion of a bearing component from a bearing steel composition as set out above.
  • the steel comprises a number of elements in specified amounts.
  • the composition used in the method preferably corresponds to the composition of the final article produced. However, while the weight percentage of most of the elements will remain essentially constant, the nitrogen content may decrease slightly, perhaps due to degassing. While the composition initially produced by the hot isostatic pressing step of the present invention is predominantly austenitic, the composition is preferably subjected to further processing steps to introduce a martensite phase. Accordingly, a bearing component made according to the present invention will generally comprise a martensitic microstructure having some retained austenite (1-30 wt %) and some carbides/carbonitrides ( ⁇ 5 wt %).
  • the powdered steel composition is first formed by conventional techniques, for example, by melting suitable ingredients in a melting crucible. The melted components can then be powdered for use in the method of the present invention.
  • Suitable ingredients include the raw elements or oxides or salts of the ingredients which can be decomposed on heating.
  • the ingredients are preferably melted at a temperature in excess of 1500° C. to ensure that the composition is fully molten. If the temperature is lower then precipitation of a solid fraction such as ⁇ -ferrite or the like may occur.
  • the melt can be produced in an induction furnace and/or tapped into an induction heated ladle where further alloying elements can be added in a protective atmosphere.
  • the melt can be stirred and temperature controlled throughout the process. Prior to the atomisation the melt can be tapped into a tundish where the melt is protected by, for example, a protective slag cover or an inert atmosphere.
  • a first step is to provide a powder of the steel composition.
  • a powder is a dry, bulk solid composed of a large number of very fine particles that may flow freely when shaken or tilted. Powders are a special sub-class of granular materials. In particular, powders refer to those granular materials that have the finer grain sizes, and that therefore have a greater tendency to form clumps when flowing.
  • the powder of the steel composition preferably has a particle size of from 1 ⁇ m to 1000 ⁇ m, preferably 10 ⁇ m to 250 ⁇ m and most preferably 50 ⁇ m to 125 ⁇ m.
  • One technique for producing the powder is atomisation. This technique is especially preferred as it allows the trapping of a particularly preferred phase from a molten steel composition.
  • Other techniques are known, such as comminution, grinding, chemical reactions, centrifugal disintegration, or electrolytic deposition.
  • Atomization may be accomplished by, for example, forcing a molten metal stream through an orifice at moderate pressures or by disintegration of a molten metal stream by a high pressure gas stream in an atomisation chamber. As it contacts the gas or a nozzle or an orifice the composition may drop in temperature; this can favour austenite formation.
  • the chamber is filled with gas to promote further turbulence of the molten metal jet.
  • the atomisation is caused by contacting the molten steel composition with one or more jets of gas, preferably air, nitrogen or an inert gas, for example.
  • simple atomization may be used by forcing a liquid metal through an orifice at a sufficiently high velocity to provide the necessary turbulent flow to produce powder.
  • Nozzle vibration, nozzle asymmetry, multiple impinging streams, or molten-metal injection into ambient gas can all be used to increase the extent of the atomization.
  • the steel composition can optionally be stored under inert gas hermetically-sealed vessels. Alternatively, it can be used with minimal delay.
  • a mould In a second step the powder is placed in a mould.
  • this comprises canning the powder in capsules of mild steel, which are produced by sheet metal forming and welding.
  • Such a mould or capsule would be designed to give the end product the desired shape.
  • the mould may be formed of heat resistant materials that are known in the art.
  • Compound products can be produced by designing capsules or moulds with separate compartments for different powders or enclosing parts of solid material together with the powder.
  • the mould is preferably subjected to elevated temperature and a very high vacuum to remove air and moisture from the powder.
  • the mould is then preferably sealed before being hot isostatically pressed.
  • the application of high inert gas pressures and elevated temperatures results in the removal of internal voids and creates a strong metallurgical bond throughout the material. The result is a clean homogeneous material with a uniformly fine grain size and a near 100% density.
  • HIP hot isostatic pressing
  • the HIP parameters of pressure, temperature and time are predetermined in order to give the material full density and the required properties.
  • Suitable temperatures are those where the composition is in the y phase (e.g. the y region in the phase diagram in FIG. 3 ). That is, from about 1350 to 1100° C., more preferably from 1300 to 1200° C.
  • Suitable pressures may be up to 200 MPa but ideally are about 100 MPa.
  • the pressure may be in the range of from 10 to 150 MPa and most preferably from 95 to 105 MPa.
  • Treatment times from a cold start are preferably from 1 minute to 24 hours, more preferably from 1 hour to 10 hours and most preferably from 2 hours to 8 hours.
  • the step of hot isostatic pressing is conducted under an inert atmosphere.
  • Suitable inert atmospheres include noble gases such as argon.
  • the hot isostatic pressing is conducted under air to avoid overly complicating the method and apparatus.
  • the method can further comprise a step of nitriding (or case hardening) the hot isostatically pressed bearing component (article).
  • nitriding or case hardening
  • the nitriding may serve to harden at least a surface portion of the article.
  • the finished article or composition can therefore be provided with a higher nitrogen content than could otherwise be achieved.
  • Suitable nitriding processes are well known in the art and include: gas nitriding; liquid or salt bath nitriding; and ion or plasma nitriding.
  • gas nitriding the donor is a nitrogen rich gas usually ammonia (NH 3 ) which is contacted with the pre-heated article. Preferably this is performed at 200 to 800° C. and is allowed to dwell for at least 30 minutes. When ammonia comes into contact with the heated work piece it disassociates into nitrogen and hydrogen. The nitrogen then diffuses from the surface into the core of the material.
  • NH 3 ammonia
  • the nitrogen donating medium is a nitrogen containing salt such as cyanide salt.
  • the temperature used is typically 550-600° C.
  • Plasma nitriding relies on a plasma of nitrogen ions and allows for focused and specific nitriding.
  • the method of the present invention can further comprise finishing steps and/or tempering and/or annealing steps.
  • another possible step can be stress relief annealing of a hardened article.
  • Such steps are well known in the art.
  • the products may be heat treated, machined and subjected to various types of quality control, such as ultra-sonic inspection, dye penetrant testing, testing of mechanical properties, etc. If a mild steel sheet is used as the mould then it can be removed by machining or by acid pickling.
  • finishing steps include grinding and polishing.
  • tempering steps include tempering at between 100 and 500° C., more preferably 200 to 450° C., for 10 minutes to 24 hours, more preferably 30 minutes to three hours. If a hardening step such as nitriding is used then it may be desirable to cool the article to a sub-zero temperature (preferably ⁇ 70° C. to ⁇ 80° C.) after hardening and before tempering. Preferably the subzero treatment is at ⁇ 80° C. for 2 hours under air. Preferably tempering, which can be conducted without other hardening steps, is performed at 200° C. for two hours under air.
  • Hot working refers to processes where metals are plastically deformed above their recrystallization temperature. Being above the recrystallization temperature allows the material to recrystallize during deformation. This is important because recrystallization keeps the materials from strain hardening, which ultimately keeps the yield strength and hardness low and ductility high.
  • the processing temperature is commonly 0.6 of the materials melting temperature. Hot rolling is not especially preferred but may be used to arrive at the final desired dimensions.
  • Hot rolling is a hot working metalworking process where large pieces of metal, such as slabs or billets, are heated above their recrystallization temperature and then deformed between rollers to form thinner cross sections. Hot rolling produces thinner cross sections than cold rolling processes with the same number of stages. Hot rolling, due to recrystallization, will reduce the average grain size of a metal while maintaining an equiaxed microstructure.
  • the method of the present invention provides a number of advantages over conventional methods.
  • the reduced porosity of hot isostatically pressed materials enables improved mechanical properties and increased workability.
  • the HIP process eliminates internal voids and creates clean, firm bonds and fine, uniform microstructures. These characteristics are not possible with welding, casting or P-ESR.
  • the virtual elimination of internal voids enhances part performance and improves fatigue strength.
  • a further advantage of the HIP process is its ability to create near-net shapes that require little machining.
  • phase rule In melting operations the “phase rule” applies to all pure and combined elements and strictly dictates the distribution of liquid and solid phases which can exist for specific compositions. However, by using powder metallurgy considerations of solid-liquid phase changes can be ignored, so the process is more flexible than casting, extrusion, or forging techniques. It is therefore possible to fabricate components which otherwise would decompose or disintegrate.
  • the stable austenitic phase of the desired composition is narrow (in terms of temperature) under conventional processes (welding, casting or P-ESR) and the presently claimed powder metallurgical process allows for the production of a stable phase without the likely impurities that would otherwise arise.
  • the claimed manufacturing process produces very little scrap metal and allows for the production of different product shapes.
  • the tolerances that this process can do are very precise, ranging from +/ ⁇ 0.02 cm for axial dimensions and +/ ⁇ 0.05 cm for radial dimensions.
  • the method and composition of the present invention can be used to produce steel products such as bearing components.
  • the bearing component will typically have been formed by a process involving hardening and tempering.
  • the microstructure will generally comprise martensite, together with any retained austenite and also carbides and/or carbonitrides.
  • the bearing component may be substantially austenitic with just the surface wear portion subjected to martensitic through-hardening.
  • the whole product may be tempered and hardened by conventional methods to produce a martensitically hardened product.
  • the present invention also provides for a bearing component formed by the method or made of the steel composition as herein described.
  • the bearing component may be at least one of a rolling element, an inner ring, and an outer ring.
  • At least a wear portion of the bearing component is formed by the method or made of the steel composition as herein described.
  • the wear portion for example, the raceway of a bearing ring, may be formed separately from the body of the bearing ring and then joined by conventional joining techniques such as diffusion joining or welding.
  • the present invention also provides for a bearing comprising a bearing component as herein described.
  • Bearings may be used in many different types of machinery to retain and support rotating components such as, for example, a wheel on a vehicle, a vane on a windmill or a drum in a washing machine.
  • the present invention is particularly suited for the manufacture of bearing rings for large-size bearings (LSB).
  • LSBs have an outside diameter of 450 cm or greater.
  • the bearing of the present invention is particularly suitable for use as a turbine bearing, in particular a wind turbine or wind mill bearing. Under such applications the high corrosion resistance and strength characteristics are key.
  • the method of the present invention can be used to adhere a wear portion of a bearing to the body of a bearing component. That is, the body of the bearing component forms a part of the mould and the wear portion is clad onto the surface using hot isostatic pressing.
  • a less expensive material can be coated with a thin layer of powdered steel composition to create a suitable surface for withstanding rolling contact fatigure. This reduces costs by placing expensive, wear resistant materials only where they are needed. As a result, wear resistant properties are improved without incurring unnecessary cost penalties.
  • An additional benefit of cladding is that it can create bonds between otherwise incompatible materials such as metal, intermetallic, and ceramic powders.
  • the hardness of the steel composition as an article is preferably 50 HRC or more, and most preferably 55 HRC or 58 HRC or more.
  • the hardness is measured according to the Rockwell hardness test which is well known in the art. HRC is measured with a minor load of 98 N and a diamond cone major load of 1372N.
  • a steel composition 6 was prepared in an induction furnace 5 .
  • Ingredients 2 necessary for providing the desired composition were fed into the induction furnace 5 .
  • Two electrodes 4 connected to an alternating power supply, and placed within the induction furnace 5 were used to heat the ingredients 2 to provide a molten steel composition 6 .
  • the molten composition 6 could have been held in a tundish (not shown) under a protective atmosphere prior to atomisation.
  • the ingredients 2 were selected to provide the following steel composition 6 .
  • the steel composition 6 was slowly discharged from the induction furnace 5 into an expansion chamber 10 .
  • the molten steel composition 6 was contacted with nitrogen air jets provided from a blower 8 .
  • the blown steel composition 6 became a number of finely dispersed lines of steel 12 , which became increasingly fragmented within the expansion chamber 10 due to turbulence and formed a powder 14 .
  • the powder 14 was collected in the base of the expansion chamber 10 .
  • a packing step 16 the powder 14 was loaded into mild steel moulds 18 shaped to form the body of a bearing component and lightly compressed to form a weak cohesive structure.
  • a hot isostatic pressing step 20 the filed moulds were subjected to a temperature of 1200° C. and a pressure of 95 MPa for 3 hours. Hot isostatic pressing was conducted under an argon atmosphere.
  • a finishing treatment step 24 the mild steel moulds 18 were removed by pickling and the bearing component was removed.
  • the bearing was substantially all austenite.
  • the bearing component was then subjected to a step of tempering and hardening to form a martensitically hardened bearing component.
  • the bearing component was analysed to confirm its final composition and properties.
  • the final composition is shown in table 2.
  • the bearing component was found to exhibit excellent corrosion resistance, strength (tensile strength) and hardness.
  • the present invention enables the production of bearing components having particularly high corrosion resistance, strength and hardness.
  • the composition avoids defects and unwanted impurity phases, has a finer grain size and exhibits even greater corrosion resistance, strength and hardness.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Physics & Mathematics (AREA)
  • General Engineering & Computer Science (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Rolling Contact Bearings (AREA)
  • Manufacture Of Metal Powder And Suspensions Thereof (AREA)
  • Powder Metallurgy (AREA)
  • Treatment Of Steel In Its Molten State (AREA)
  • Solid-Phase Diffusion Into Metallic Material Surfaces (AREA)
US13/386,346 2009-07-21 2010-07-20 Bearing steels Abandoned US20120177527A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
GBGB0912669.9A GB0912669D0 (en) 2009-07-21 2009-07-21 Bearing steels
GB0912669.9 2009-07-21
PCT/GB2010/001373 WO2011010088A1 (en) 2009-07-21 2010-07-20 Bearing steels

Publications (1)

Publication Number Publication Date
US20120177527A1 true US20120177527A1 (en) 2012-07-12

Family

ID=41058298

Family Applications (1)

Application Number Title Priority Date Filing Date
US13/386,346 Abandoned US20120177527A1 (en) 2009-07-21 2010-07-20 Bearing steels

Country Status (8)

Country Link
US (1) US20120177527A1 (enExample)
EP (1) EP2456900B1 (enExample)
JP (1) JP5731500B2 (enExample)
CN (1) CN102498227B (enExample)
BR (1) BR112012001361A2 (enExample)
GB (1) GB0912669D0 (enExample)
IN (1) IN2012DN00594A (enExample)
WO (1) WO2011010088A1 (enExample)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015055187A1 (de) * 2013-10-15 2015-04-23 Schaeffler Technologies AG & Co. KG Lagerelement für ein wälz- oder gleitlager
US20150111404A1 (en) * 2013-10-21 2015-04-23 Ronald F. Seiler Remotely installed fire and smoke detector
US20150167122A1 (en) * 2013-12-13 2015-06-18 Glenn Glennon Method of hardening articles and articles comprising the same
EP2886892A1 (de) * 2013-12-19 2015-06-24 Aktiebolaget SKF Verfahren zum Herstellen einer Lagerkomponente, Lagerkomponente, Lageranordnung mit der Lagerkomponente sowie Verwendung der Lagerkomponente
WO2015139699A1 (de) * 2014-03-20 2015-09-24 Schaeffler Technologies AG & Co. KG Lagerelement für ein gleit- oder wälzlager
US20160303683A1 (en) * 2013-04-09 2016-10-20 Aktiebolaget Skf Bearing component and its manufacturing method
US20200040942A1 (en) * 2016-11-08 2020-02-06 Carrier Corporation Hybrid Bearings
US10808293B2 (en) 2015-07-15 2020-10-20 Ak Steel Properties, Inc. High formability dual phase steel
US11215230B2 (en) 2016-02-19 2022-01-04 Jtekt Corporation Rolling slide member, rolling bearing using same, and method for manufacturing rolling slide member
US20230175553A1 (en) * 2020-02-17 2023-06-08 Nsk Ltd. Rolling bearing and method for producing same
US12123464B2 (en) 2020-12-17 2024-10-22 Aktiebolaget Skf Bearing component and method of manufacturing thereof

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101915273A (zh) * 2010-08-13 2010-12-15 新兴铸管股份有限公司 新型轴承环材料及其生产工艺
CN104018083B (zh) * 2014-06-20 2016-01-06 重庆材料研究院有限公司 含氮不锈轴承钢及制备方法
CN104889399B (zh) * 2015-05-15 2017-10-10 安泰科技股份有限公司 粉末冶金工艺制备耐磨耐蚀合金管件的方法
CN109538634A (zh) * 2018-10-20 2019-03-29 夏小林 一种轴承内圈、其制备方法及轴承
JP2022147350A (ja) * 2021-03-23 2022-10-06 Ntn株式会社 波形保持器の製造方法
CN113528941B (zh) * 2021-06-16 2025-12-23 中国兵器科学研究院宁波分院 一种含氮马氏体不锈轴承钢及其制备方法

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2876715B2 (ja) * 1990-06-04 1999-03-31 日本精工株式会社 転がり軸受
JPH06279959A (ja) * 1993-03-30 1994-10-04 Toshiba Tungaloy Co Ltd 鉄系焼結合金およびその製造方法
NL9300901A (nl) * 1993-05-26 1994-12-16 Skf Ind Trading & Dev Werkwijze voor het carbonitreren van staal.
CA2131652C (en) * 1993-09-27 2004-06-01 William Stasko Sulfur-containing powder-metallurgy tool steel article
JP3588935B2 (ja) * 1995-10-19 2004-11-17 日本精工株式会社 転がり軸受その他の転動装置
JPH11303874A (ja) * 1997-04-16 1999-11-02 Nippon Seiko Kk 転動部材
JPH11100647A (ja) * 1997-09-26 1999-04-13 Ntn Corp 転がり軸受およびその製造方法
JP2000226641A (ja) * 1999-02-05 2000-08-15 Nsk Ltd 転動装置
JP2000337389A (ja) * 1999-03-19 2000-12-05 Nsk Ltd 転がり軸受
US20060249230A1 (en) * 2005-05-09 2006-11-09 Crucible Materials Corp. Corrosion and wear resistant alloy
JP4952888B2 (ja) * 2006-04-07 2012-06-13 大同特殊鋼株式会社 マルテンサイト鋼
CN101376948B (zh) * 2007-08-27 2011-03-30 宝山钢铁股份有限公司 一种低成本高纯净度汽车轮毂用中碳轴承钢及其制造方法

Cited By (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9878396B2 (en) * 2013-04-09 2018-01-30 Aktiebolaget Skf Bearing component and its manufacturing method
US10737354B2 (en) 2013-04-09 2020-08-11 Aktiebolaget Skf Bearing component
US20160303683A1 (en) * 2013-04-09 2016-10-20 Aktiebolaget Skf Bearing component and its manufacturing method
WO2015055187A1 (de) * 2013-10-15 2015-04-23 Schaeffler Technologies AG & Co. KG Lagerelement für ein wälz- oder gleitlager
US20150111404A1 (en) * 2013-10-21 2015-04-23 Ronald F. Seiler Remotely installed fire and smoke detector
US20150167122A1 (en) * 2013-12-13 2015-06-18 Glenn Glennon Method of hardening articles and articles comprising the same
US9988698B2 (en) * 2013-12-13 2018-06-05 The Abbott Ball Company Method of hardening articles and articles comprising the same
DE102013226556A1 (de) * 2013-12-19 2015-06-25 Aktiebolaget Skf Verfahren zum Herstellen einer Lagerkomponente, Lagerkomponente, Lageranordnung mit der Lagerkomponente sowie Verwendung der Lagerkomponente
EP2886892A1 (de) * 2013-12-19 2015-06-24 Aktiebolaget SKF Verfahren zum Herstellen einer Lagerkomponente, Lagerkomponente, Lageranordnung mit der Lagerkomponente sowie Verwendung der Lagerkomponente
WO2015139699A1 (de) * 2014-03-20 2015-09-24 Schaeffler Technologies AG & Co. KG Lagerelement für ein gleit- oder wälzlager
US10808293B2 (en) 2015-07-15 2020-10-20 Ak Steel Properties, Inc. High formability dual phase steel
US11215230B2 (en) 2016-02-19 2022-01-04 Jtekt Corporation Rolling slide member, rolling bearing using same, and method for manufacturing rolling slide member
US11268572B2 (en) 2016-02-19 2022-03-08 Jtekt Corporation Rolling slide member, rolling bearing using same, and method for manufacturing rolling slide member
US20200040942A1 (en) * 2016-11-08 2020-02-06 Carrier Corporation Hybrid Bearings
US10781857B2 (en) * 2016-11-08 2020-09-22 Carrier Corporation Hybrid bearings
US20230175553A1 (en) * 2020-02-17 2023-06-08 Nsk Ltd. Rolling bearing and method for producing same
US11788579B2 (en) * 2020-02-17 2023-10-17 Nsk Ltd. Rolling bearing and method for producing same
US12123464B2 (en) 2020-12-17 2024-10-22 Aktiebolaget Skf Bearing component and method of manufacturing thereof

Also Published As

Publication number Publication date
CN102498227B (zh) 2015-06-03
CN102498227A (zh) 2012-06-13
GB0912669D0 (en) 2009-08-26
BR112012001361A2 (pt) 2019-09-24
JP2012533688A (ja) 2012-12-27
EP2456900A1 (en) 2012-05-30
IN2012DN00594A (enExample) 2015-06-12
WO2011010088A1 (en) 2011-01-27
EP2456900B1 (en) 2013-05-08
JP5731500B2 (ja) 2015-06-10

Similar Documents

Publication Publication Date Title
EP2456900B1 (en) Bearing steels
KR102803220B1 (ko) 분말용 니켈계 합금 및 분말의 제조 방법
JP5671526B2 (ja) 高強度低合金焼結鋼
CN114892071B (zh) 一种新能源车用高温渗碳齿轮钢及制造方法
US20250025937A1 (en) Steel powder for use in additive manufacturing processes
US11767579B2 (en) Nickel based alloy for powder and method for producing a powder
KR100562759B1 (ko) 냉간 가공 공구용, 및 양호한 내마모성, 인성 및 열처리 특성을 갖는 부품용 강 재료와 그의 제조방법
JP4703005B2 (ja) スチール、該スチールの使用、該スチール製の製品および該スチールの製造方法
US20030156965A1 (en) Nitrogen alloyed steel, spray compacted steels, method for the production thereof and composite material produced from said steel
CN108950413A (zh) 一种模具钢材料及其制备方法与用途
WO2013120903A1 (en) A bearing steel composition
JP2006501368A (ja) フェライト鋼合金
EP1471155B1 (en) Method for fabricating a martensitic steel without any melting
Adishesha Effect of steel making and processing parameters on carbide banding in commercially produced ASTM A-295 52100 bearing steel
US12378645B2 (en) Iron-based mixed powder for powder metallurgy and iron-based sintered body
CN118668127A (zh) 一种高强韧高纯净冷冲模具钢及其制备方法
CN114318130A (zh) 沉淀硬化合金
KR20230098636A (ko) 마레이징 강
Sherif et al. Novel Tough Micro-Alloyed Bearing Steel with High Hardenability
RU2828779C2 (ru) Сталь для высокотемпературного цементированного вала шестерни и способ изготовления такой стали
US20160076591A1 (en) Bearing component
Švanda INFLUENCE OF WOOTZ STEEL MICROSTRUCTURE TO FORGING
Halilović et al. Microstructure and mechanical properties of nickel free austenitic stainless steels produced by addition of nitrided ferroalloys during melting in induction furnace
EP2814994B1 (en) A bearing steel composition
RU2250925C2 (ru) Способ производства катаных заготовок

Legal Events

Date Code Title Description
AS Assignment

Owner name: AKTIEBOLAGET SKF, SWEDEN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KERRIGAN, AIDAN MICHAEL;SHERIF, MOHAMED;KARLSSON, HENRIK;SIGNING DATES FROM 20120201 TO 20120321;REEL/FRAME:027947/0439

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION