US20110180229A1 - Crucible For Use In A Directional Solidification Furnace - Google Patents
Crucible For Use In A Directional Solidification Furnace Download PDFInfo
- Publication number
- US20110180229A1 US20110180229A1 US13/014,932 US201113014932A US2011180229A1 US 20110180229 A1 US20110180229 A1 US 20110180229A1 US 201113014932 A US201113014932 A US 201113014932A US 2011180229 A1 US2011180229 A1 US 2011180229A1
- Authority
- US
- United States
- Prior art keywords
- base
- crucible
- directional solidification
- plate
- solidification furnace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application claims priority to U.S. Provisional Application No. 61/299,133 filed Jan. 28, 2010, the entire disclosure of which is hereby incorporated by reference in its entirety.
- This invention generally relates to directional solidification furnaces and, more specifically, to a directional solidification furnace for improving the solidification rate.
- Directional solidification furnaces, such as those shown in
FIG. 1 and referred to generally at 100, are often used in the production of multi-crystalline silicon ingots. Thedirectional solidification furnace 100 ofFIG. 1 comprises acrucible 102 supported by acrucible support 103 having graphite support walls that add structural rigidity to the crucible. Thecrucible 102 includes walls 104 (crucible support walls) and abase 106. Thecrucible 102 is typically constructed of quartz, or another suitable material that can withstand high temperatures while remaining essentially inert. - Together with a
lid 112, thecrucible 102 andcrucible support 103 form aninner assembly 105. Thisinner assembly 105 may also include aheat exchanger 107 disposed beneath thebase 106.Heaters 108 are positioned around thewalls 104 and within acontainment vessel 110. Theheaters 108 may suitably be radiant heaters configured to apply the heat necessary to melt charge material within the crucible. The charge material of this embodiment is silicon, though other materials are contemplated. -
Side insulation 109 is disposed around the crucible and may be partially opened, such as by vertical movement. Once the silicon charge has melted, a cooling medium may be introduced to theheat exchanger 107 and/or theinsulation 109 may be raised to aid in the directional solidification of the silicon. The heat output of theheaters 108 may be adjusted so that less heat is applied to themelt 111. The position of theheaters 108 may also be adjusted relative to the crucible by moving them away from thecrucible 102, especially away from thecrucible base 106. - After the
crucible 102 has been charged with silicon, the area surrounding the crucible is sealed from the outside ambient environment. To aid in the separation of thecrucible 102 from the outside environment, the crucible is placed within thecontainment vessel 110 that forms part of the furnace. The pressure within thecontainment vessel 110 is then reduced. The content of the atmosphere within thecontainment vessel 110 can also be monitored and controlled. - The
crucible 102 and the charge are then heated to a temperature sufficient to melt the silicon. After the charge has completely melted it is cooled at a controlled rate to achieve a directional solidification structure. The controlled rate of cooling is established by any combination of reducing the amount and location of heat applied by theheaters 108, the movement of or the opening of a heat vent ininsulation 109 surrounding thecrucible 102, or the circulation of a cooling medium through the heat exchanger 107 (e.g., a cooling plate). Any of these methods transfer heat away from the surface of thecrucible 102. If the rate of cooling of thebase 106 of thecrucible 102 is greater than that of thewalls 104 of the crucible, then a relatively flat, horizontal solidification isotherm with predominately axial thermal gradients is generated. The ingot thereby solidifies in the region closest to the cooler side of thecrucible 102 and proceeds in a direction away from that side of the crucible. The last portion of themelt 111 to solidify is generally at the top of the ingot. - A significant concern in the production of multi-crystalline silicon ingots in directional solidification furnaces is the amount of time required to generate an ingot from raw silicon. The rate at which the ingot solidifies directly affects the amount of time required to form the ingot from the raw materials.
- This Background section is intended to introduce the reader to various aspects of art that may be related to various aspects of the present disclosure, which are described and/or claimed below. This discussion is believed to be helpful in providing the reader with background information to facilitate a better understanding of the various aspects of the present disclosure. Accordingly, it should be understood that these statements are to be read in this light, and not as admissions of prior art.
- A first aspect of the disclosure is a directional solidification furnace comprising a crucible assembly. The crucible assembly includes a crucible for containing a melt, the crucible including walls and a base, the base having an opening therein. A crucible support supports the crucible and a lid covers the crucible. A plate is received in the opening in the base. The plate has a higher thermal conductivity than that of the base.
- Another aspect of the disclosure is a directional solidification furnace comprising a crucible assembly. The crucible assembly includes a crucible for containing a melt, the crucible including walls and a composite base. A crucible support supports the crucible and a lid covers the crucible. The composite base includes an additive such that the composite base has a higher thermal conductivity than a comparable base without the additive.
- Yet another aspect of the disclosure is a method of producing an ingot in a directional solidification furnace. The method comprises melting a silicon charge in a crucible of the furnace to form a liquid melt. The crucible includes a base having a first portion and a second portion. The first portion has a higher thermal conductivity than the second portion. Heat is then transferred from the melt through the base of the crucible. Heat is transferred through the first portion of the base at an increased rate compared to the second portion. The transfer of heat from the melt results in the solidification of the melt and production of the ingot.
- Various refinements exist of the features noted in relation to the above-mentioned aspects. Further features may also be incorporated in the above-mentioned aspects as well. These refinements and additional features may exist individually or in any combination. For instance, various features discussed below in relation to any of the illustrated embodiments may be incorporated into any of the above-described aspects, alone or in any combination.
-
FIG. 1 is a partially schematic cross-section of a directional solidification furnace in accordance with one embodiment; -
FIG. 2 is a top plan view of a first embodiment of a crucible for use in the directional solidification furnace ofFIG. 1 ; -
FIG. 3 is a cross-section of the crucible ofFIG. 2 taken along line 3-3 inFIG. 2 ; -
FIG. 4 is an enlarged portion ofFIG. 3 ; -
FIG. 5 is a top plan view of a second embodiment of a crucible for use in the directional solidification furnace ofFIG. 1 ; -
FIG. 6 is a cross-section of the crucible ofFIG. 5 taken along line 6-6 inFIG. 5 ; -
FIG. 7 is a top plan view of a third embodiment of a crucible for use in the directional solidification furnace ofFIG. 1 ; -
FIG. 8 is a cross-section of the crucible ofFIG. 7 taken along line 8-8 inFIG. 7 ; -
FIG. 9 is a top plan view of a fourth embodiment of a crucible for use in the directional solidification furnace ofFIG. 1 ; -
FIG. 10 is a cross-section of the crucible ofFIG. 9 taken along line 10-10 ofFIG. 9 ; -
FIG. 11 is an enlarged portion ofFIG. 10 ; and -
FIG. 12 is a flow diagram depicting a method of producing an ingot in a directional solidification furnace using any of the crucibles shown inFIGS. 2-11 . - Like reference symbols in the various drawings indicate like elements.
-
FIGS. 2 , 3, and 4 show respective top plan, cross-sectional, and enlarged views of a first embodiment of acrucible 200 for use in any directional solidification furnace, such as thefurnace 100 shown inFIG. 1 . Thecrucible 200 has a base 206 (generally, a “second portion”) and fourwalls 204 extending upward from the base. Thebase 206 andwalls 204 may be integrally formed together or joined together such that the melt 111 (FIG. 1 ) is contained therein. Thebase 206 has anupper surface 208 and alower surface 210 and anopening 220 extending between the upper and lower surfaces. - The
opening 220 is defined by a void formed in thecrucible 200 that is bounded by foursides 222. In other embodiments, theopening 220 may be a shape other than rectangular, such as circular, oval, or any other suitable shape and theplate 250 placed therein is shaped accordingly. Theopening 220 may be formed in thecrucible 200 by machining or otherwise removing a section ofbase 206. In other embodiments, theopening 220 may be formed during manufacture of thecrucible 200. - The
opening 220 has a length L and a width W adjacent theupper surface 208 of thebase 206 and a length L′ and a width W′ adjacent thelower surface 210. Each of thesides 222 slopes inward away from thewalls 204 of thecrucible 200 such that the length L is greater than the length L′ and the width W is greater than the width W′. In some embodiments, the length L, length L′, width W, and width W′ may be between 50 mm and 630 mm. As more clearly seen inFIG. 4 , thesides 222 are angled at approximately 45 degrees with respect to thelower surface 210 of thebase 206. However, thesides 222 may be oriented at a different angle without departing from the scope of the embodiments. For example, in some embodiments, thesides 222 may be oriented at approximately 35 degrees with respect to thelower surface 210 of thebase 206. - A plate 250 (generally, a “first portion”) having four
sides 252 is sized for positioning within theopening 220. While the embodiments herein disclose placing theplate 250 in thebase 206 of thecrucible 200, additional plates may be placed within any or all of thewalls 204. Moreover, in some embodiments theplate 250 may not be used, and instead plates similar to theplate 250 may be placed within any or all of thewalls 204. - The
plate 250 is formed from a material having a higher thermal conductivity than thebase 206 of thecrucible 200. In one embodiment, theplate 250 may be formed from fused quartz. In some embodiments, theplate 250 has a thermal conductivity (k) that is approximately -
- compared to a typical thermal conductivity of the
base 206 of -
- In other embodiments, the
plate 250 is formed from any material having a thermal conductivity greater than thebase 206 of thecrucible 200 that has a higher melting point than themelt 111. For example, theplate 250 may be formed from MgO, AlN, SiC, graphite, or a composite of MgO and SiC. According to some embodiments, theplate 250 may only be used one time, after which it is removed and repaired or discarded. In other embodiments, theplate 250 is used multiple times before removal. - The
plate 250 has a thickness T1 that is substantially the same as a thickness T2 of thebase 206 of thecrucible 200 adjacent theplate 250. In some embodiments, T1 may be equal to between 5 mm and 25 mm and T2 may be equal to between 5 mm and 25 mm. In other embodiments, the thickness T1 of theplate 250 may be greater or less than the thickness T2 of thebase 206. As seen inFIG. 4 , theplate 250 has foursides 252 with a sloped profile that corresponds to thesides 222 of theopening 220 such that the plate is in registry with the sides of the opening. The slopedsides 222 of the opening form a first angle that is complementary a second angle formed by the sloped profile of the foursides 252 of theplate 250. The geometry of thesides 222 of theopening 220 and thesides 252 of theplate 250 thus result in the weight of themelt 111 pressing the sides of the plate against the sides of the opening. A bonding agent may be used to further secure theplate 250 within thesides 222 of theopening 220 such that themelt 111 is not able to pass between opening and the plate. - In some embodiments, the bonding agent is a slip
cast silica compound 256. The size of the joint 254 and amount of slip castsilica compound 256 contained therein shown inFIG. 4 is greatly exaggerated for illustration. Prior to use of thecrucible 200, a joint 254 between theplate 250 and thelower surface 210 of the base 206 may be sealed with tape or other material. Slip castsilica 256 in a fluid state is the poured into the joint 254 adjacent theupper surface 208 of thebase 206. The solvent in the fluid slip castsilica 256 then evaporates, and the silica remains as a joint filler. Thecrucible 200 may then be fired to cure the slip castsilica 256 in the joint 254. -
FIGS. 5 and 6 show respective top plan and cross-sectional views of a second embodiment of acrucible 300 for use in any directional solidification furnace, such as thefurnace 100 shown inFIG. 1 . Thecrucible 300 has a base 306 (generally, a “second portion”) and fourwalls 304 extending upward from the base. Thebase 306 andwalls 304 may be integrally formed together or joined together such that the melt 111 (FIG. 1 ) is contained therein. Thebase 306 has anupper surface 308 and alower surface 310. Arecess 320 extends upward from thelower surface 310 towards theupper surface 308, but does not pass through theupper surface 308 of thebase 306. - A plate 350 (generally, a “first portion”) having four
sides 352 is sized for positioning within therecess 320. In other embodiments, therecess 320 andplate 250 may not be rectangular, and instead be circular, oblong, or any other suitable shape. While the embodiments herein disclose placing theplate 350 in therecess 320 in thebase 306 of thecrucible 300, additional plates may be placed within any or all of thewalls 304. Moreover, theplate 350 may not be used, and instead plates may be placed within any or all of thewalls 304. - A
portion 360 of thebase 306 separates theplate 350 from the melt disposed in the crucible. Theportion 360 prevents the melt from damaging, wearing, or corroding theplate 350. According to some embodiments theportion 360 may have a thickness TPORTION between 1 mm and 20 mm while theplate 350 may have a thickness TPLATE between 1 mm and 20 mm and the base 306 may have a thickness TBASE between 1 mm and 20 mm. Moreover, while the thicknesses of the plate TPLATE and portion TPORTION are shown as being uniform, the thicknesses may vary. As theplate 350 is shielded from themelt 111 by theportion 360 of thebase 306, the plate may thus be used multiple times before replacement. - The
plate 350 is attached to thebase 306 by any bonding mechanism, such as adhesive or fasteners. In some embodiments, slip cast silica is used to fasten theplate 360 to therecess 320. In other embodiments, a friction fit between therecess 320 and theplate 350 retains the plate in the recess. - The
plate 350 is formed from a material having a higher thermal conductivity than thebase 306 of thecrucible 300. In one embodiment, theplate 350 may be formed from fused quartz. In these embodiments theplate 250 and theportion 360 of the base 306 have a combined effective thermal conductivity (keff) that is up to approximately -
- compared to a typical thermal conductivity of the
base 306 of -
- In other embodiments, the
plate 350 is formed from any material having a thermal conductivity greater than thebase 306 of thecrucible 300. For example, theplate 350 may be formed from MgO, AlN, SiC, graphite, or composites of MgO and SiC, SiO2 and AlN, SiO2 and MgO, and SiO2 and TiO2. Moreover, as theplate 350 is shielded from themelt 111 by theportion 360, materials that would otherwise not be suitable for contact with the melt may be used in its construction (e.g., TiO2). -
TABLE 1 TBASE TPORTION TPLATE kPORTION kPLATE keff 20 5 15 1 3 2 20 10 10 1 3 1.5 20 15 5 1 3 1.2 20 5 15 1 50 3.77 20 10 10 1 50 1.96 20 15 5 1 50 1.32 20 2 18 1 50 8.47 - As shown in Table 1 above, the effective thermal conductivity (keff) of the
base 306 is dependent on the thermal conductivities of the portion 360 (kPORTION) and the plate 350 (kPLATE) and their thicknesses, TPORTION and TPLATE. The combined effective thermal conductivity (keff) of theplate 350 and theportion 360 is dependent on the composition of the plate and the thicknesses of the plate and the portion. The combined thermal conductivity (Keff) of thebase 206 is expressed as: -
-
FIGS. 7 and 8 show respective top plan and cross-sectional views of a third embodiment of acrucible 400 for use in any directional solidification furnace, such as thefurnace 100 shown inFIG. 1 . Thecrucible 400 has a base 406 (generally, a “second portion”) and fourwalls 404 extending upward from the base. Thebase 406 andwalls 404 may be integrally formed together or joined together such that the melt 111 (FIG. 1 ) is contained therein. Thebase 406 has anupper surface 408 and alower surface 410. - The
base 406 has a portion 450 (generally, a “first portion”) of increased thermal conductivity. While the embodiments herein disclose placing theportion 450 in thebase 406 of thecrucible 400, additional portions may be placed within any or all of thewalls 404. Moreover, theportion 450 may not be used, and instead portions of increased thermal conductivity are placed within any or all of thewalls 404. - The
portion 450 includes one or moreadditive materials 452 that are intermixed with the material from which thebase 406 is formed to form a composite. The number ofadditive materials 452 shown inFIG. 7 is greatly reduced for the sake of clarity and the relative size of the additive materials is likewise greatly increased for clarity. Theadditive materials 452 have a greater thermal conductivity than the material from which thebase 406 is formed. The thermal conductivity of theportion 450 of the base 406 having the increased thermal conductivity is thus generally in the range of three to ten times greater than that of the remainder of the base and thewalls 404 of thecrucible 400. Theadditive materials 452 in theportion 450 may be selected from any material that is capable of being intermixed with the material from which thebase 406 is formed during construction of the base. For example, theadditive materials 452 may be any one of or a combination of MgO, SiC, AlN, or TiO2. -
FIGS. 9 , 10, and 11 show respective top plan, cross-sectional, and enlarged views of a fourth embodiment of acrucible 500 for use in any directional solidification furnace, such as thefurnace 100 shown inFIG. 1 . Thecrucible 500 has a base 506 (generally, a “second portion”) and fourwalls 504 extending upward from the base. Thebase 506 andwalls 504 may be integrally formed together or joined together such that the melt 111 (FIG. 1 ) is contained therein. Thebase 506 has anupper surface 508 and alower surface 510. Anopening 520 extends between theupper surface 508 and thelower surface 510. - The
opening 520 is defined by a void formed in thecrucible 500 that is bounded by four sides 522. Theopening 520 may be formed in thecrucible 500 by machining or otherwise removing a section ofbase 506. In other embodiments, theopening 520 may be formed during manufacture of thecrucible 500 such that a section of the base is not removed to form the opening. - A
portion 530 of thebase 506 extends inward from the sides 522 of theopening 520 and away from thewalls 504. Theportion 530 has a thickness T3, measured from thebottom surface 510, which is less than a thickness T4 of thebase 506. Theportion 530 thus extends out from thebase 506 and forms a ledge structure. - A plate 550 (generally, a “first portion”) is sized for placement within the
opening 520. In other embodiments, theopening 520 andplate 550 may not be rectangular, and instead be circular, oblong, or any other suitable shape. While the embodiments herein disclose placing theplate 550 in thebase 506 of thecrucible 500, additional plates may be placed within any or all of thewalls 504. Moreover,plate 550 may not be used, and instead plates may be placed within any or all of thewalls 504. - The
plate 550 is formed from a material having a higher thermal conductivity than thebase 506 of thecrucible 500. In one embodiment, theplate 550 may be formed from fused quartz. In some embodiments, theplate 550 has a thermal conductivity (k) that is approximately -
- compared to a typical thermal conductivity of the
base 506 of -
- In other embodiments, the
plate 550 is formed from any material having a thermal conductivity greater than thebase 506 of thecrucible 500 that has a higher melting point than themelt 111. For example, theplate 550 may be formed from MgO, AlN, SiC, graphite, or a composite of MgO and SiC. - The
plate 550 has alip portion 552 extending outward from the remainder of the plate along its circumference. The lip portion has a width W1 approximately equal to a width W2 of theportion 530 extending from the sides 522 of thebase 506. During use, thelip portion 552 is positioned directly above theportion 530 of thebase 506. Thelip portion 552 andportion 530 of the base 506 thus together form a lap joint. The lap joint of theplate 550 andbase 506 thus result in the weight of themelt 111 pressing the plate into contact with the base. A bonding agent may be used to further secure theplate 550 within theopening 520 such that themelt 111 is not able to pass between the opening and the plate. In some embodiments, the bonding agent is a slip cast silica compound 556. Prior to use of thecrucible 500, a joint 554 between theplate 550 and thelower surface 510 of the base 506 may be sealed with tape or other material. Slip cast silica 556 in a fluid state is the poured into the joint 554 adjacent theupper surface 508 of thebase 506. The solvent in the fluid slip cast silica 556 then evaporates, and the silica remains as a joint filler. Thecrucible 500 may then be fired to cure the slip cast silica 556 in the joint 554. - The increased thermal conductivity of the bases of the crucibles described above in
FIGS. 2 through 11 results in an increased thermal flux (i.e., flow of thermal energy) through the respective bases. The increased heat flux through the base of the crucible results in an increase in the solidification rate of the melt contained within the crucible. In some embodiments, the solidification rate may increase by two to three times that shown in conventional crucibles. - The increase in the solidification rate of the melt thus reduces the amount of time required for the melt to cool and form the solidified ingot. The reduction in the amount of time required to form the melt increases the rate (i.e., throughput) at which ingots can be produced in directional solidification furnaces using crucibles like those described above.
-
FIG. 12 depicts anexemplary method 600 for producing an ingot in a directional solidification furnace using any of the crucibles shown inFIGS. 2-11 . As described above, the furnace includes a crucible having a base with a first portion (e.g., theplate 250, theplate 350, theportion 450, or the plate 550) and a second portion (e.g., thebase 206, thebase 306, thebase 406, or the base 506). The first portion has a higher thermal conductivity than the second portion. In the exemplary embodiment, the first portion has a thermal conductivity that is at least double that of the second portion. - The crucible is first loaded with a silicon charge. The
method 600 then begins inblock 610 with the melting of the silicon charge to form a liquid melt. Inblock 620, heat is transferred from the melt through at least the base of the crucible. Heat is transferred through the first portion at an increased rate compared to the rate at which it is transferred through the second portion. The transfer of heat from the melt solidifies the melt into an ingot. - While the invention has been described in terms of various specific embodiments, it will be recognized that the invention can be practiced with modification within the spirit and scope of the claims.
- When introducing elements of the present disclosure or the embodiments thereof, the articles “a”, “an”, “the” and “said” are intended to mean that there are one or more of the elements. The terms “comprising”, “including” and “having” are intended to be inclusive and mean that there may be additional elements other than the listed elements. The use of terms indicating a particular orientation (e.g., “top”, “bottom”, “side”, etc.) is for convenience of description and does not require any particular orientation of the item described.
- As various changes could be made in the above constructions and methods without departing from the scope of the disclosure, it is intended that all matter contained in the above description and shown in the accompanying drawings shall be interpreted as illustrative and not in a limiting sense.
Claims (20)