US20110070121A1 - Beta-based titanium alloy with low elastic modulus - Google Patents
Beta-based titanium alloy with low elastic modulus Download PDFInfo
- Publication number
- US20110070121A1 US20110070121A1 US12/994,083 US99408308A US2011070121A1 US 20110070121 A1 US20110070121 A1 US 20110070121A1 US 99408308 A US99408308 A US 99408308A US 2011070121 A1 US2011070121 A1 US 2011070121A1
- Authority
- US
- United States
- Prior art keywords
- titanium alloy
- elastic modulus
- beta
- titanium
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C14/00—Alloys based on titanium
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
- A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
- A61L27/02—Inorganic materials
- A61L27/04—Metals or alloys
- A61L27/06—Titanium or titanium alloys
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/16—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of other metals or alloys based thereon
- C22F1/18—High-melting or refractory metals or alloys based thereon
- C22F1/183—High-melting or refractory metals or alloys based thereon of titanium or alloys based thereon
Definitions
- the present disclosure relates to a titanium alloy with a low elastic modulus, including no elements harmful to the human body, and more particularly, to a beta-based titanium alloy with a low elastic modulus, including titanium (Ti), niobium (Nb) and zirconium (Zr), and further including tantalum (Ta), hafnium (Hf), molybdenum (Mo), tin (Sn), and the like.
- Titanium is widely used in the fields of aerospace, weaponry, nuclear power, sports and leisure, biomedicine and the like due to its high specific strength (strength/weight), high corrosion resistance, excellent mechanical properties including high temperature properties, and excellent biocompatibility.
- Biomedical metals have been developed for use in implants for replacing bones, joints, teeth, and the like.
- the biomedical metals are used for manufacturing a variety of prostheses such as artificial bones, artificial joints, and dental prostheses.
- biomedical metals should be excellent in biocompatibility as well as mechanical properties, corrosion resistance, and chemical resistance. That is, biomedical metals should be non-toxic and not induce allergies in the human body.
- Titanium and titanium alloys have been used as biomaterial for replacing stainless steel. In the beginning, pure titanium and titanium alloy such as Ti-6Al-4V were used as biomaterial.
- biocompatible titanium alloys that have been developed to solve the problem of cytotoxicity are Ti-6Al-7Nb and Ti-5Al-2.5Fe, which are second-generation titanium alloys.
- the stress shield effect is caused by elastic modulus difference between natural bone with a low elastic modulus and biocompatible material with a high elastic modulus.
- a metal implant with a high elastic modulus bears most of the load applied to the region around the implant, and the natural bone in the region does not bear any tension, compression and bending for a long time.
- the thickness and the weight of the natural bone are reduced gradually, causing serious problems such as osteoporosis around the implant.
- This phenomenon is referred to as the “stress shield effect.”
- the bonding strength between the natural bone and the artificial implant also decreases, resulting in decreased service life of the implant.
- Ti-13Nb-13Zr (ASTM F1713), Ti-12Mo-6Zr-2Fe (ASTM F1813), Ti-15Mo (ASTM F2066), and the like have been developed throughout the world to solve the above mentioned problems.
- a variety of alloys such as Ti-35Nb-5Ta-7Zr and Ti-16Nb-13Ta-4Mo in a similar composition range are being developed.
- the titanium alloys hitherto developed have an elastic modulus of approximately 60 GPa to approximately 80 GPa, which is still much higher than the elastic modulus of natural bones that range from approximately 10 GPa to approximately 30 GPa. Accordingly, the problem of “stress shield effect” has not been completely solved yet. Therefore, there is a considerable demand for a material that is not harmful to the human body and, at the same time, has a lower elastic modulus.
- the present disclosure provides a titanium alloy composition that is not harmful to the human body, has an elastic modulus as low as bones of the human body, and at the same time, is melted and cast easily and cost-effectively.
- a beta phase generally has a low elastic modulus
- the inventors selected alloying elements of titanium alloy on the basis of whether they can serve as a beta stabilizer in titanium alloy to lower the elastic modulus of titanium alloy.
- the inventors selected the alloying elements of titanium alloy on the basis of whether they are harmless to the human body in terms of biochemical suitability, and whether the density, melting temperature and boiling temperature thereof are economically suitable when compared to titanium. Resultantly, as beta stabilizers satisfying the above requirements, niobium (Nb) and zirconium (Zr) were selected.
- the inventors designed a titanium alloy composition having a low elastic modulus using a semi-experimental method for designing and developing an alloy.
- the method includes calculating the covalent bond order and the energy level of the electrons according to the content of each alloying element, using the electronic state, which is the core of the discrete variational (DV)-Xa molecular orbital method.
- micro-properties of the material can be analyzed approximately from the electronic state of the material by interpreting the Schrodinger equation and the like.
- the inventors calculated the bonding order, B o and the energy level of the electrons, M d of the above-described alloying elements through the DV-Xa molecular orbital method, and discovered a beta-based titanium alloy composition with a low elastic modulus from there-among.
- the titanium alloy with a low elastic modulus includes from 37 wt. % to 41 wt. % niobium (Nb), from 5 wt. % to 8 wt. % zirconium (Zr), and a balance of titanium, with unavoidable impurities.
- the titanium alloy has an elastic modulus of 55 GPa or lower.
- Zirconium has very high corrosion resistance in hot water under acidic or basic atmosphere. Zirconium forms oxide film even in air, showing high corrosion resistance. Zirconium is a biocompatible metal without the cytotoxic effect. It is preferable that zirconium is contained in the titanium alloy in a range from 5 wt. % to 8 wt. %. This is because the elastic modulus of the ternary alloy of titanium, niobium and zirconium increases considerably outside this range, so that it cannot be applied to a living body. It is more preferable that zirconium is contained in the titanium alloy in a range from 5 wt. % to 7 wt. %.
- the elastic modulus of the titanium alloy it is possible to lower the elastic modulus of the titanium alloy to 50 GPa or lower, as well as to 55 GPa or lower.
- one or more elements selected from tantalum (Ta), hafnium (Hf), molybdenum (Mo), and tin (Sn) may be further added in the titanium alloy in a range of 3 wt. % or lower. It is preferable that they are added in a range from 1 wt. % to 3 wt. % in view of the elastic modulus factor. In this case, it is preferable that the content of niobium is from 37 wt. % to 39 wt. %, and the content of zirconium is from 5 wt. % to 7 wt. %.
- Tantalum (Ta) is ductile, and has high mechanical strength even at high temperature. Tantalum forms a stable film with high electric resistance so that it is relatively free from oxidation in air. In addition, tantalum is highly resistant to acid, and has excellent compatibility with the human body, so that it can be used for cementing bones. Tantalum, when alloyed in titanium, serves as a major beta stabilizer.
- Hafnium (Hf) has characteristics very similar to zirconium, and has excellent corrosion-resistance and bio-compatibility. It serves as a beta stabilizer when alloyed in titanium.
- Molybdenum (Mo) has a relatively high melting point. However, it has excellent thermal conductivity, high corrosion resistance even in strong acid, and very favorable mechanical properties over a wide temperature range. It serves as a beta stabilizer when alloyed in titanium.
- Tin (Sn) is stable in an air and has excellent ductility. It is soluble in acids and alkalis, and has a very low melting temperature of about 232° C. It is stable in the human body and thus widely used in the fields of table ware, plating and the like. It may also serve as a beta stabilizer when alloyed in titanium.
- Addition of the above elements in an amount greater than 3 wt. % may affect the titanium-niobium-zirconium ternary system to increase the elastic modulus. Accordingly, the maximum content of the above-mentioned elements in the titanium alloy is set to 3 wt. % or lower.
- the titanium alloy in accordance with the exemplary embodiments can be fabricated by various melting or casting methods such as vacuum induction melting (VIM), vacuum arc remelting (VAR), induction skull melting (ISM), plasma arc melting (PAM), electron beam melting (EBM) and the like.
- VIM vacuum induction melting
- VAR vacuum arc remelting
- ISM induction skull melting
- PAM plasma arc melting
- EBM electron beam melting
- the beta-based titanium alloy in accordance with the exemplary embodiments of the present invention has low elastic modulus and excellent mechanical properties. Therefore, it can be used in a variety of applications, for example, as a material for medical devices, such as artificial bones, artificial teeth and artificial hip joints, as a material for general civilian goods such as eyewear frames and headsets, and as a material for sports and leisure goods such as golf clubs.
- FIG. 1 is a photograph of an ingot prepared by melting and casting a titanium alloy in accordance with an exemplary embodiment.
- FIG. 2 is a photograph of a cylinder-shaped product prepared by drawing the ingot of FIG. 1 .
- FIGS. 3 and 4 are micrographs, each showing a microstructure of a titanium alloy in accordance with Embodiment 1.
- FIG. 5 is a micrograph showing a microstructure of a titanium alloy in accordance with Embodiment 2.
- Ti—Nb—Zr ternary alloys having compositions as listed in Table 1 were prepared by a vacuum arc remelting (VAR) process.
- a Ti—Nb master alloy was used to cast beta-based titanium alloys.
- the titanium alloys melted by the VAR process in accordance with the embodiment were cast into ingots as shown in FIG. 1 . Then, the ingots were processed into bars having a diameter of 15 mm as shown in FIG. 2 , through a drawing process.
- the ingot had an excellent appearance. Surface crack, fracture and the like that are often generated during the drawing process were not observed in the surface of the bar. Accordingly, it can be concluded that the titanium alloys in accordance with the embodiment have good formability and good workability.
- the alloy bar fabricated in accordance with the embodiment was cut into a section perpendicular to the drawing direction and a section parallel to the drawing direction.
- the cut surface was first macro-polished with abrasive papers of up to 2400 grit and then micro-polished with a diamond paste.
- the cut surface was etched with Kroll etchant (H 2 O 100 ml+HNO 3 5 ml+HF 3 ml) and then the microstructure of the cut surface was observed using an optical microscope.
- FIG. 3 is a micrograph (at 200 ⁇ magnification) of a surface of the specimen No. 4 (Table 1) cut perpendicular to the drawing direction.
- FIG. 4 is a micrograph (at 200 ⁇ magnification) of a surface of the specimen No. 4 (Table 1) cut parallel to the drawing direction.
- the beta-based titanium alloy fabricated in accordance with the embodiment had uniform grain size, and showed no segregations and no defects.
- the ternary titanium alloy in accordance with the embodiment can achieve the ultra-low elastic modulus, which has been difficult to achieve even in related art quaternary titanium alloys.
- a titanium alloy in accordance with Embodiment 2 further includes tantalum (Ta) as shown in Table 2, so as to improve mechanical properties while still maintaining the low elastic modulus and including no elements harmful to the human body.
- the titanium alloys were melted by the vacuum arc remelting (VAR) process, cast into ingots, and then drawn into bars, as described in Embodiment 1.
- Specimens were cut from the alloy bars and polished mechanically. After etching the specimen, the microstructure was observed at a magnification of 50 ⁇ using an optical microscope. As shown in FIG. 5 , there were no segregations and no defects visible in the microstructure of the alloy.
- the titanium alloys in accordance with Embodiment 2 were not increased in the elastic modulus in comparison with the titanium alloys in accordance with Embodiment 1. Accordingly, the titanium alloy in accordance with Embodiment 2 can be used to achieve the required mechanical properties as well as the elastic modulus.
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Organic Chemistry (AREA)
- Metallurgy (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Engineering & Computer Science (AREA)
- General Health & Medical Sciences (AREA)
- Thermal Sciences (AREA)
- Animal Behavior & Ethology (AREA)
- Epidemiology (AREA)
- Public Health (AREA)
- Veterinary Medicine (AREA)
- Physics & Mathematics (AREA)
- Life Sciences & Earth Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Transplantation (AREA)
- Oral & Maxillofacial Surgery (AREA)
- Medicinal Chemistry (AREA)
- Dermatology (AREA)
- Inorganic Chemistry (AREA)
- Materials For Medical Uses (AREA)
- Manufacture And Refinement Of Metals (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR20080049737 | 2008-05-28 | ||
KR1020080049737 | 2008-05-28 | ||
PCT/KR2008/007693 WO2009145406A1 (en) | 2008-05-28 | 2008-12-24 | Beta-based titanium alloy with low elastic modulus |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/KR2008/007693 A-371-Of-International WO2009145406A1 (en) | 2008-05-28 | 2008-12-24 | Beta-based titanium alloy with low elastic modulus |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US14/076,136 Continuation-In-Part US20140112820A1 (en) | 2008-05-28 | 2013-11-08 | Beta-based titanium alloy with low elastic modulus |
Publications (1)
Publication Number | Publication Date |
---|---|
US20110070121A1 true US20110070121A1 (en) | 2011-03-24 |
Family
ID=41377259
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/994,083 Abandoned US20110070121A1 (en) | 2008-05-28 | 2008-12-24 | Beta-based titanium alloy with low elastic modulus |
Country Status (5)
Country | Link |
---|---|
US (1) | US20110070121A1 (ja) |
EP (1) | EP2297370B1 (ja) |
JP (1) | JP5204301B2 (ja) |
KR (1) | KR100971649B1 (ja) |
WO (1) | WO2009145406A1 (ja) |
Cited By (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100086794A1 (en) * | 2008-09-23 | 2010-04-08 | Susanne Norgren | Titanium-based alloy |
WO2013154629A1 (en) * | 2012-02-15 | 2013-10-17 | Rti International Metals, Inc. | Titanium alloys |
WO2014078670A1 (en) * | 2012-11-16 | 2014-05-22 | The Texas A&M University System | Self-adaptive, ultra-low elastic modulus shape memory alloys |
US9758846B2 (en) | 2011-09-05 | 2017-09-12 | University Of Tsukuba | Super elastic zirconium alloy for biological use, medical instrument and glasses |
CN114150183A (zh) * | 2021-12-17 | 2022-03-08 | 西安稀有金属材料研究院有限公司 | 一种核反应堆压力容器部件用合金材料及其制备方法 |
CN114836650A (zh) * | 2022-04-27 | 2022-08-02 | 北京航空航天大学 | 具有完全等轴晶组织和超高屈服强度的钛合金 |
CN115852203A (zh) * | 2022-12-28 | 2023-03-28 | 西安聚能医工科技有限公司 | 一种抗骨质疏松的多孔径种植体用钛铌锆铜合金、制备方法及种植体表面处理方法 |
Families Citing this family (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8639352B2 (en) | 2009-04-06 | 2014-01-28 | Medtronic, Inc. | Wire configuration and method of making for an implantable medical apparatus |
US8340759B2 (en) | 2011-04-22 | 2012-12-25 | Medtronic, Inc. | Large-pitch coil configurations for a medical device |
US9409008B2 (en) | 2011-04-22 | 2016-08-09 | Medtronic, Inc. | Cable configurations for a medical device |
US8660662B2 (en) | 2011-04-22 | 2014-02-25 | Medtronic, Inc. | Low impedance, low modulus wire configurations for a medical device |
KR101389020B1 (ko) * | 2011-09-05 | 2014-04-25 | 한국기계연구원 | Ti-Nb-X계 타이타늄 합금의 에칭방법 |
KR20130076438A (ko) * | 2011-12-28 | 2013-07-08 | 오스템임플란트 주식회사 | 고강도와 저탄성 계수의 내식성 티타늄계 합금 |
WO2014159102A1 (en) * | 2013-03-14 | 2014-10-02 | Reading Alloys, Inc. | Radiolucent molybdenum-containing master alloys |
WO2014159085A1 (en) * | 2013-03-14 | 2014-10-02 | Reading Alloys, Inc. | Aluminum-molybdenum-zirconium-tin master alloys |
KR20180046514A (ko) * | 2016-10-28 | 2018-05-09 | (주)폴리바이오텍 | 플렉시블 샤프트 |
CN112020569A (zh) * | 2018-02-27 | 2020-12-01 | 奥克斯梅特科技有限公司 | 一种为增材制造而优化的生物相容性钛合金 |
KR102301567B1 (ko) | 2018-06-11 | 2021-09-14 | 순천대학교 산학협력단 | 낮은 탄성계수와 높은 항복강도를 갖는 타이타늄 합금 |
KR20200121944A (ko) | 2019-04-16 | 2020-10-27 | 한국생산기술연구원 | 저탄성계수와 고강도를 갖는 생체 적합성이 우수한 타이타늄 합금 |
Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7261782B2 (en) * | 2000-12-20 | 2007-08-28 | Kabushiki Kaisha Toyota Chuo Kenkyusho | Titanium alloy having high elastic deformation capacity and method for production thereof |
Family Cites Families (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
ZA9010217B (en) * | 1989-12-21 | 1991-10-30 | Smith & Nephew Richards Inc | Biocompatible low modulus titanium alloy for medical implants |
AU705336B2 (en) * | 1994-10-14 | 1999-05-20 | Osteonics Corp. | Low modulus, biocompatible titanium base alloys for medical devices |
US6767418B1 (en) | 1999-04-23 | 2004-07-27 | Terumo Kabushiki Kaisha | Ti-Zr type alloy and medical appliance formed thereof |
JP4547797B2 (ja) * | 2000-12-19 | 2010-09-22 | 大同特殊鋼株式会社 | 生体用Ti合金およびその製造方法 |
JP4350443B2 (ja) * | 2003-07-14 | 2009-10-21 | 山八歯材工業株式会社 | チタン合金 |
JP4302604B2 (ja) * | 2004-09-27 | 2009-07-29 | 株式会社古河テクノマテリアル | 生体用超弾性チタン合金 |
-
2008
- 2008-12-24 WO PCT/KR2008/007693 patent/WO2009145406A1/en active Application Filing
- 2008-12-24 JP JP2011511491A patent/JP5204301B2/ja active Active
- 2008-12-24 US US12/994,083 patent/US20110070121A1/en not_active Abandoned
- 2008-12-24 EP EP08874499.0A patent/EP2297370B1/en active Active
- 2008-12-24 KR KR1020080133938A patent/KR100971649B1/ko active IP Right Grant
Patent Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7261782B2 (en) * | 2000-12-20 | 2007-08-28 | Kabushiki Kaisha Toyota Chuo Kenkyusho | Titanium alloy having high elastic deformation capacity and method for production thereof |
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100086794A1 (en) * | 2008-09-23 | 2010-04-08 | Susanne Norgren | Titanium-based alloy |
US8492002B2 (en) | 2008-09-23 | 2013-07-23 | Sandvik Intellectual Property Ab | Titanium-based alloy |
US9758846B2 (en) | 2011-09-05 | 2017-09-12 | University Of Tsukuba | Super elastic zirconium alloy for biological use, medical instrument and glasses |
WO2013154629A1 (en) * | 2012-02-15 | 2013-10-17 | Rti International Metals, Inc. | Titanium alloys |
WO2014078670A1 (en) * | 2012-11-16 | 2014-05-22 | The Texas A&M University System | Self-adaptive, ultra-low elastic modulus shape memory alloys |
US9752219B2 (en) | 2012-11-16 | 2017-09-05 | The Texas A&M University System | Self-adaptive, ultra-low elastic modulus shape memory alloys |
CN114150183A (zh) * | 2021-12-17 | 2022-03-08 | 西安稀有金属材料研究院有限公司 | 一种核反应堆压力容器部件用合金材料及其制备方法 |
CN114836650A (zh) * | 2022-04-27 | 2022-08-02 | 北京航空航天大学 | 具有完全等轴晶组织和超高屈服强度的钛合金 |
CN115852203A (zh) * | 2022-12-28 | 2023-03-28 | 西安聚能医工科技有限公司 | 一种抗骨质疏松的多孔径种植体用钛铌锆铜合金、制备方法及种植体表面处理方法 |
Also Published As
Publication number | Publication date |
---|---|
EP2297370B1 (en) | 2013-12-04 |
WO2009145406A1 (en) | 2009-12-03 |
KR100971649B1 (ko) | 2010-07-22 |
KR20090123762A (ko) | 2009-12-02 |
EP2297370A1 (en) | 2011-03-23 |
JP2011521110A (ja) | 2011-07-21 |
JP5204301B2 (ja) | 2013-06-05 |
EP2297370A4 (en) | 2011-10-26 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2297370B1 (en) | Beta-based titanium alloy with low elastic modulus | |
Liu et al. | Binary titanium alloys as dental implant materials—a review | |
Ozan et al. | New Ti-Ta-Zr-Nb alloys with ultrahigh strength for potential orthopedic implant applications | |
Hermawan et al. | Metals for biomedical applications | |
US7722805B2 (en) | Titanium alloy with extra-low modulus and superelasticity and its producing method and processing thereof | |
Wong et al. | Structure and properties of Ti-rich Ti–Zr–Nb–Mo medium-entropy alloys | |
WO2022257915A1 (zh) | 生物医用非晶合金及其应用 | |
JP5924825B2 (ja) | 生体用超弾性ジルコニウム合金、医療用器具および眼鏡 | |
Mat-Baharin et al. | Influence of alloying elements on cellular response and in-vitro corrosion behavior of titanium-molybdenum-chromium alloys for implant materials | |
Hsu et al. | Structure and mechanical properties of as-cast Ti–5Nb–xCr alloys | |
Guo et al. | Preparation and characterization of metastable β-type titanium alloys with favorable properties for orthopedic applications | |
KR100653160B1 (ko) | 생체 적합성이 우수한 저탄성계수 티타늄기 합금소재 및 그제조방법 | |
CN101760668B (zh) | 一种低弹性模量的生物医用钛合金 | |
Ozdemir et al. | Understanding the enhanced corrosion performance of two novel Ti-based biomedical high entropy alloys | |
Rokaya et al. | Modification of titanium alloys for dental applications | |
JP4212945B2 (ja) | 機能性医療機器及びその製造方法 | |
KR100959197B1 (ko) | 저탄성계수와 고강도를 갖는 생체적합성이 우수한 타이타늄합금 | |
US20140112820A1 (en) | Beta-based titanium alloy with low elastic modulus | |
JP3779368B2 (ja) | 生体用複合インプラント材 | |
US20240002982A1 (en) | Superelastic alloys | |
JP2014194083A (ja) | 低弾性チタン合金 | |
Hsu et al. | Effect of thermomechanical treatment on structure and properties of metastable Ti-25Nb-8Sn alloy | |
JP5572794B2 (ja) | 低弾性チタン合金 | |
KR20020047981A (ko) | 티타늄 합금 조성물 | |
Zheng¹ et al. | New kind of titanium alloys for biomedical application |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: KOREA INSTITUTE OF MACHINERY & MATERIALS, KOREA, R Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:LEE, DONG GEUN;LEE, YONG TAE;MI, XUJUN;AND OTHERS;SIGNING DATES FROM 20101001 TO 20101011;REEL/FRAME:025393/0483 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |