US20100059105A1 - Use of polyamide as an encapsulating material for photovoltaic modules - Google Patents

Use of polyamide as an encapsulating material for photovoltaic modules Download PDF

Info

Publication number
US20100059105A1
US20100059105A1 US12/597,346 US59734608A US2010059105A1 US 20100059105 A1 US20100059105 A1 US 20100059105A1 US 59734608 A US59734608 A US 59734608A US 2010059105 A1 US2010059105 A1 US 2010059105A1
Authority
US
United States
Prior art keywords
polyamide
photovoltaic module
module according
film
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/597,346
Other languages
English (en)
Inventor
Harald Muckenhuber
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Isovoltaic AG
Original Assignee
Isovolta AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Isovolta AG filed Critical Isovolta AG
Assigned to ISOVOLTA AG reassignment ISOVOLTA AG ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: MUCKENHUBER, HARALD
Publication of US20100059105A1 publication Critical patent/US20100059105A1/en
Assigned to ISOVOLTAIC GMBH reassignment ISOVOLTAIC GMBH ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: ISOVOLTA AG
Assigned to ISOVOLTAIC AG reassignment ISOVOLTAIC AG CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: ISOVOLTAIC GMBH
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/34—Layered products comprising a layer of synthetic resin comprising polyamides
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/06—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B27/08—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/04—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof adapted as photovoltaic [PV] conversion devices
    • H01L31/042—PV modules or arrays of single PV cells
    • H01L31/048—Encapsulation of modules
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/04—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof adapted as photovoltaic [PV] conversion devices
    • H01L31/042—PV modules or arrays of single PV cells
    • H01L31/048—Encapsulation of modules
    • H01L31/0481—Encapsulation of modules characterised by the composition of the encapsulation material
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/04—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof adapted as photovoltaic [PV] conversion devices
    • H01L31/042—PV modules or arrays of single PV cells
    • H01L31/048—Encapsulation of modules
    • H01L31/049—Protective back sheets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2377/00—Polyamides
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02B—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO BUILDINGS, e.g. HOUSING, HOUSE APPLIANCES OR RELATED END-USER APPLICATIONS
    • Y02B10/00—Integration of renewable energy sources in buildings
    • Y02B10/10—Photovoltaic [PV]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E10/00—Energy generation through renewable energy sources
    • Y02E10/50—Photovoltaic [PV] energy
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31551—Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]
    • Y10T428/31562—Next to polyamide [nylon, etc.]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31551—Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]
    • Y10T428/31565—Next to polyester [polyethylene terephthalate, etc.]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31678—Of metal
    • Y10T428/31681—Next to polyester, polyamide or polyimide [e.g., alkyd, glue, or nylon, etc.]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31725—Of polyamide
    • Y10T428/31736—Next to polyester
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31725—Of polyamide
    • Y10T428/3175—Next to addition polymer from unsaturated monomer[s]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31786—Of polyester [e.g., alkyd, etc.]

Definitions

  • the invention relates to the use of polyamide as an encapsulating material for photovoltaic modules.
  • Photovoltaic modules are used to generate electrical power.
  • part of the structure of photovoltaic modules comprises solar cells which, by exposure to sunlight, generate electrical charges which can be drawn off as current.
  • these solar cells are sensitive to mechanical influences or weathering influences to different extents.
  • Encapsulating materials are used in order to protect said solar cells from these influences. These materials can consist of one or more layer(s), made of glass and/or plastic composites.
  • composites of fluoropolymer materials and polyester (PET) are used as standard for encapsulating materials.
  • a fluoropolymer layer on the outside guarantees weathering resistance
  • the PET film in the core guarantees the mechanical stability and the electrical insulation
  • another fluoropolymer layer on the inside guarantees the connection to the embedding material of the solar cells.
  • the adhesion to the embedding material e.g. ethylvinyl acetate (EVA) is low.
  • EVA ethylvinyl acetate
  • relatively thick composites are required to ensure the desired electrical insulation. This is attributable on the one hand to the low insulating capacity of fluoropolymer layers and on the other hand, to the adhesive layers used as standard between the films.
  • the smallest irregularities or inclusions in the adhesive layers have the result that high currents flow in a punctiform manner. This phenomenon must be counteracted by a larger thickness of the PET film in the core as a precaution.
  • the present invention wishes to remedy this.
  • polyamide as an encapsulating material for the production of photovoltaic modules is provided according to the invention.
  • polyamide is advantageously effected as a film or as a film composite containing polyamide (PA).
  • PA polyamide
  • plastic composite comprising a carrier material selected from the group of polyethylene terephthalate (PET), polyethylene naphthenate (PEN) or ethylene tetrafluoroethylene copolymer (ETFE), as well as polyamide-12 layers adjoining the carrier material on both sides.
  • PET polyethylene terephthalate
  • PEN polyethylene naphthenate
  • ETFE ethylene tetrafluoroethylene copolymer
  • polyamide makes it possible to achieve very good adhesion to the embedding material which, as described above, can be, for example, EVA.
  • the electrical insulation can be improved significantly by using a polyamide single film with the same thickness as compared to a composite comprising fluoropolymer layers and PET. It is not possible for high currents to flow in a punctiform manner via defects or inclusions in the adhesive layers.
  • Polyamide films can likewise be designed as weather- and UV-stabilised so that values comparable to those when using fluoropolymers can also be achieved with regard to these properties.
  • Various colour combinations can also be adjusted by means of pigmentation.
  • two production steps i.e. the production of the PET/fluoropolymer layer composite and the fluoropolymer layer/PET/fluoropolymer layer composite can be saved.
  • FIGS. 1 to 5 The invention is explained in detail hereinafter with reference to possible embodiments—see FIGS. 1 to 5 —as well as with reference to a possible exemplary embodiment.
  • FIG. 1 shows the exemplary structure of a photovoltaic module which is encapsulated with the material 1 used according to the invention.
  • the encapsulating material 1 comprises a weather-resistant film which at the same time serves as an adhesion promoter to the embedding material 2 .
  • the embedding material 2 produces the non-positive connection to the solar cells 3 and to the embedding material 2 ′.
  • the embedding material 2 ′ further ensures the non-positive connection to the encapsulating material 4 .
  • FIG. 2 shows the exemplary structure of a photovoltaic module which is encapsulated with the material 1 used according to the invention.
  • the encapsulating material 1 is used on both sides of the solar cells 3 .
  • FIG. 3 shows the exemplary structure of a photovoltaic module which is encapsulated with the material 1 used according to the invention.
  • a fluoropolymer layer 5 is used as an additional layer to the encapsulating material 1 on the side facing away from the solar cells 3 .
  • the fluoropolymer layer 5 and the encapsulating material 4 thus constitute the respectively outermost layer of the photovoltaic module.
  • FIG. 4 shows the use according to the invention of a plastic composite 1 , 1 ′ with the polyamide 12 layers 12 which are disposed on both sides of the carrier material 13 .
  • the carrier material consists of polyethylene terephthalate or polyethylene naphthenate or ethylene tetrafluoroethylene copolymer.
  • FIG. 5 shows a possible laminating device for producing a non-positive composite 6 from the materials 1 and 5 according to FIG. 3 .
  • the encapsulating material 1 which is selected according to the exemplary embodiment is coated with adhesive by means of the applicator unit 7 and after passing through a drier 10 is adhesively bonded to the fluoropolymer layer 5 .
  • the contact between the two films is controlled by the pressing pressure between the rollers 11 .
  • the material 1 can be pre-treated by means of physical media 9 before each production step.
  • the non-positive connection between the encapsulating material 1 and the fluoropolymer layer 5 can also be produced by co-extrusion. In this case, it is also possible to insert an adhesion promoter layer between the materials 1 and 5 and thus produce a triple-layer co-extrudate.
  • the encapsulating material 1 itself can comprise a monolayer or likewise a co-extrudate of several layers.
  • the material 1 Before using the encapsulating material 1 according to the invention or also before adhesive bonding with the fluoropolymer layer 5 , the material 1 can be pre-treated by means of chemical or physical media. This pre-treatment can be implemented on one or also on both sides of the encapsulating material 1 .
  • Encapsulating material 1 as film polyamides (PA) of the type polyamide 6, polyamide 66, polyamide 7, polyamide 9, polyamide 10, polyamide 11, polyamide 12, polyamide 69, polyamide 6 10, polyamide 6 12, PA-6-3-T, PA 6I, polyphthalamide (PPA) as well as other possible aromatic, partially aromatic and co-polyamides comprising these types.
  • PA polyamides
  • PA polyphthalamide
  • Embedding material 2 , 2 ′ ethylvinylacetate (EVA), polyvinylbutyral (PVB), ionomers, polymethylmethacrylate (PMMA), polyurethane, polyester, hotmelt or silicone elastomers.
  • EVA ethylvinylacetate
  • PVB polyvinylbutyral
  • PMMA polymethylmethacrylate
  • polyurethane polyester, hotmelt or silicone elastomers.
  • Encapsulating material 4 glass
  • PVDF polyvinylfluoride
  • ECTFE ethylenechloro trifluoroethylene
  • PCTFE polychlorotrifluoroethylene
  • ETFE ethylenetetra-fluoroethylene
  • PTFE polytetrafluoroethylene-hexafluoropropylene-vinylidenefluoride
  • Fluoropolymer layer 5 as coating fluoropolymer from the group of selectively soluble fluoropolymers.
  • the photovoltaic modules constructed from the aforesaid components are extremely stable when used outside which can be attributed, inter alia, to the good adhesion of polyamide to the embedding material.
US12/597,346 2007-05-10 2008-05-08 Use of polyamide as an encapsulating material for photovoltaic modules Abandoned US20100059105A1 (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
ATA734/2007 2007-05-10
AT0073407A AT505186A1 (de) 2007-05-10 2007-05-10 Verwendung eines kunststoffverbundes für die herstellung photovoltaischer module
ATA2087/2007 2007-12-20
AT0208707A AT505199A1 (de) 2007-05-10 2007-12-20 Verwendung von polyamid als einkapselungsmaterial für photovoltaische module
PCT/AT2008/000158 WO2008138021A2 (de) 2007-05-10 2008-05-08 Verwendung von polyamid als einkapselungsmaterial für photovoltaische module

Publications (1)

Publication Number Publication Date
US20100059105A1 true US20100059105A1 (en) 2010-03-11

Family

ID=39592809

Family Applications (2)

Application Number Title Priority Date Filing Date
US12/597,346 Abandoned US20100059105A1 (en) 2007-05-10 2008-05-08 Use of polyamide as an encapsulating material for photovoltaic modules
US12/597,597 Expired - Fee Related US8318316B2 (en) 2007-05-10 2008-05-08 Use of a polymer composite for the production of photovoltaic modules

Family Applications After (1)

Application Number Title Priority Date Filing Date
US12/597,597 Expired - Fee Related US8318316B2 (en) 2007-05-10 2008-05-08 Use of a polymer composite for the production of photovoltaic modules

Country Status (22)

Country Link
US (2) US20100059105A1 (es)
EP (2) EP2143148B1 (es)
JP (2) JP2010528454A (es)
KR (2) KR20100014415A (es)
CN (2) CN101715608A (es)
AR (3) AR066506A1 (es)
AT (5) AT505186A1 (es)
BR (2) BRPI0811432A8 (es)
CA (2) CA2684637A1 (es)
CL (2) CL2008001371A1 (es)
CY (1) CY1111856T1 (es)
DK (1) DK2143148T3 (es)
ES (1) ES2366685T3 (es)
HR (1) HRP20110691T1 (es)
MX (2) MX2009010922A (es)
PE (2) PE20090085A1 (es)
PL (1) PL2143148T3 (es)
PT (1) PT2143148E (es)
RS (1) RS51813B (es)
RU (2) RU2438210C2 (es)
SI (1) SI2143148T1 (es)
WO (2) WO2008138022A1 (es)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100119841A1 (en) * 2007-05-10 2010-05-13 Isovolta Ag Use of a polymer composite for the production of photovoltaic modules
US20130092233A1 (en) * 2011-10-14 2013-04-18 Andreas Pawlik Multilayer film with polyamide and polyester layers for the production of photovoltaic modules
WO2013079861A1 (fr) 2011-11-30 2013-06-06 Arkema France Film multicouche à base de polyamides pour panneau arrière de module photovoltaïque
EP3109906A1 (en) 2014-01-08 2016-12-28 Suzhou Sunshine New Materials Technology Co., Ltd. Humidity-resistant and heat-resistant solar cell backsheet and manufacturing method therefor
US9786803B2 (en) 2011-09-02 2017-10-10 Arkema Inc. Multilayer polyvinylidene films structures
US10665742B2 (en) 2014-07-04 2020-05-26 Dsm Ip Assets B.V. Co-extruded backsheet for solar cell modules

Families Citing this family (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA2712664A1 (en) * 2008-02-02 2009-08-06 Renolit Belgium N.V. Profiles for fixing rigid plates
WO2010143882A2 (en) * 2009-06-09 2010-12-16 Skc Co., Ltd. Biaxially oriented polyester film and preparation method thereof
ES2371319T5 (es) * 2009-06-18 2016-03-14 Ems-Patent Ag Monolámina de módulo fotovoltaico, procedimiento para su producción así como su utilización en el caso de la producción de módulos fotovoltaicos
WO2011009568A1 (en) 2009-07-23 2011-01-27 Renolit Belgium N.V. Photovoltaic modules with polypropylene based backsheet
JP5639798B2 (ja) * 2009-07-24 2014-12-10 三菱樹脂株式会社 太陽電池モジュール
US8188363B2 (en) * 2009-08-07 2012-05-29 Sunpower Corporation Module level solutions to solar cell polarization
AT509091B1 (de) * 2009-12-01 2011-09-15 Isovoltaic Ag Solarmodul
EP2422976B1 (de) 2010-07-30 2017-03-08 Ems-Patent Ag Photovoltaikmodul-Mehrschichtrückfolie sowie deren Herstellung und Verwendung bei der Produktion photovoltaischer Module
JP2012182316A (ja) * 2011-03-01 2012-09-20 Ube Ind Ltd 太陽電池バックフィルム
DE102011084519A1 (de) * 2011-10-14 2013-04-18 Evonik Industries Ag Verwendung einer Mehrschichtfolie für die Herstellung photovoltaischer Module
DE102011084523A1 (de) 2011-10-14 2013-04-18 Evonik Industries Ag Verwendung einer Mehrschichtfolie mit Sauerstoffpermeationssperre für die Herstellung photovoltaischer Module
DE102011084520A1 (de) 2011-10-14 2013-04-18 Evonik Industries Ag Rückfolie für Photovoltaikmodule mit verbesserter Pigmentdispergierung
DE102011084521A1 (de) * 2011-10-14 2013-04-18 Evonik Industries Ag Verwendung einer Mehrschichtfolie mit Polyamid- und Polypropylenschichten für die Herstellung photovoltaischer Module
CN102627852B (zh) * 2012-03-27 2013-08-14 江苏明昊新材料科技有限公司 太阳能光伏组件框架材料的制备方法
WO2013156319A1 (de) 2012-04-20 2013-10-24 Isovoltaic Ag Rückfolie und verbundfolie für ein photovoltaikmodul
WO2013187236A1 (ja) * 2012-06-12 2013-12-19 富士電機株式会社 太陽電池モジュールおよび接着層
CN102779904B (zh) * 2012-08-17 2016-01-20 常州天合光能有限公司 防止晶硅太阳能模块的有害极化和黑线现象发生的方法
US10720539B2 (en) * 2012-09-25 2020-07-21 Tomark-Worthen, Llc Coextruded solar panel backsheet and method of manufacture
US9412921B2 (en) 2012-11-20 2016-08-09 Industrial Technology Research Institute Module structure
CN102963090A (zh) * 2012-11-21 2013-03-13 江苏创景科技有限公司 太阳能光伏组件用绝缘背板及其制备方法
CN103066141B (zh) * 2012-12-28 2015-07-15 苏州度辰新材料有限公司 一种改性聚丙烯树脂组合物及由其制造的太阳能背板
CN103937439B (zh) * 2013-01-22 2016-06-29 烟台海泰化工科技有限公司 一种液体预涂型螺纹紧固件防松密封胶
CN106232724A (zh) 2014-04-29 2016-12-14 纳幕尔杜邦公司 具有改善的背板的太阳能电池模块
CN106232725A (zh) 2014-04-29 2016-12-14 纳幕尔杜邦公司 具有改善的背板的光伏电池
WO2015168068A1 (en) 2014-04-29 2015-11-05 E. I. Du Pont De Nemours And Company Photovoltaic cells with improved multilayer backsheet
CN106299003B (zh) * 2016-09-30 2017-08-25 苏州融硅新能源科技有限公司 一种太阳能电池板及其制备工艺
CN106960891A (zh) * 2017-03-09 2017-07-18 杭州福斯特应用材料股份有限公司 一种光伏用透明复合膜及其制备方法与应用

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020050287A1 (en) * 1998-10-13 2002-05-02 Dai Nippon Printing Co., Ltd. Protective sheet for solar battery module, method of fabricating the same and solar battery module
US20020128412A1 (en) * 1997-06-23 2002-09-12 Daikin Industries Ltd. Tetrafluoroethylene copolymer and use thereof
US20020129848A1 (en) * 2000-07-03 2002-09-19 Bridgestone Corporation Backside covering material for a solar cell module and its use
US20030029493A1 (en) * 2000-03-09 2003-02-13 Albert Plessing Method for producing photovoltaic thin film module
WO2005091379A2 (en) * 2004-03-16 2005-09-29 Vhf Technologies Sa Electric energy generating modules with a two-dimensional profile and method of fabricating the same
US20060106193A1 (en) * 2002-10-31 2006-05-18 Toray Industries,. Alicyclic or aromatic polyamides, polyamide films, optical members made by using the same, and polyamide copolymers
US20090151774A1 (en) * 2005-07-21 2009-06-18 Isovolta Ag Method for Producing Weather-Resistant Laminates for Encapsulating Solar Cell Systems

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE4112668A1 (de) 1991-04-18 1992-10-22 Huels Chemische Werke Ag Thermoplastische mehrschichtverbunde
RU2069920C1 (ru) * 1992-07-06 1996-11-27 Государственное научно-производственное предприятие "Квант" Модуль фотоэлектрический
JP2756082B2 (ja) 1994-04-28 1998-05-25 キヤノン株式会社 太陽電池モジュールの製造方法
JPH0888384A (ja) * 1994-09-20 1996-04-02 Fuji Electric Co Ltd 薄膜太陽電池
DE19643143C2 (de) 1996-10-18 2002-06-20 Inventa Ag Haftvermittler für Polyamid-Verbunde, Verfahren zu deren Herstellung sowie deren Verwendung
DE19720317A1 (de) 1997-05-15 1998-11-19 Huels Chemische Werke Ag Haftvermittler für einen Mehrschichtverbund
CN100556689C (zh) * 1998-03-06 2009-11-04 大金工业株式会社 含氟粘合性材料和用其制成的层压体
EP1054456A3 (en) * 1999-05-17 2007-01-03 Dai Nippon Printing Co., Ltd. Protective sheet for solar battery module, method of fabricating the same and solar battery module
WO2001018142A1 (fr) * 1999-09-08 2001-03-15 Daikin Industries, Ltd. Matiere adhesive fluorochimique et produit stratifie obtenu au moyen de celle-ci
JP4233071B2 (ja) * 1999-10-20 2009-03-04 三井・デュポンポリケミカル株式会社 太陽電池封止材料及び太陽電池モジュール
JP4357912B2 (ja) * 2003-09-18 2009-11-04 大日本印刷株式会社 バリア性フィルム
AT505186A1 (de) * 2007-05-10 2008-11-15 Isovolta Verwendung eines kunststoffverbundes für die herstellung photovoltaischer module

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020128412A1 (en) * 1997-06-23 2002-09-12 Daikin Industries Ltd. Tetrafluoroethylene copolymer and use thereof
US20020050287A1 (en) * 1998-10-13 2002-05-02 Dai Nippon Printing Co., Ltd. Protective sheet for solar battery module, method of fabricating the same and solar battery module
US20030029493A1 (en) * 2000-03-09 2003-02-13 Albert Plessing Method for producing photovoltaic thin film module
US20020129848A1 (en) * 2000-07-03 2002-09-19 Bridgestone Corporation Backside covering material for a solar cell module and its use
US6521825B2 (en) * 2000-07-03 2003-02-18 Bridgestone Corporation Backside covering material for a solar cell module and its use
US20060106193A1 (en) * 2002-10-31 2006-05-18 Toray Industries,. Alicyclic or aromatic polyamides, polyamide films, optical members made by using the same, and polyamide copolymers
WO2005091379A2 (en) * 2004-03-16 2005-09-29 Vhf Technologies Sa Electric energy generating modules with a two-dimensional profile and method of fabricating the same
US20090151774A1 (en) * 2005-07-21 2009-06-18 Isovolta Ag Method for Producing Weather-Resistant Laminates for Encapsulating Solar Cell Systems

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100119841A1 (en) * 2007-05-10 2010-05-13 Isovolta Ag Use of a polymer composite for the production of photovoltaic modules
US8318316B2 (en) * 2007-05-10 2012-11-27 Isovoltaic Ag Use of a polymer composite for the production of photovoltaic modules
US9786803B2 (en) 2011-09-02 2017-10-10 Arkema Inc. Multilayer polyvinylidene films structures
US20130092233A1 (en) * 2011-10-14 2013-04-18 Andreas Pawlik Multilayer film with polyamide and polyester layers for the production of photovoltaic modules
US10350865B2 (en) * 2011-10-14 2019-07-16 Evonik Degussa Gmbh Multilayer film with polyamide and polyester layers for the production of photovoltaic modules
WO2013079861A1 (fr) 2011-11-30 2013-06-06 Arkema France Film multicouche à base de polyamides pour panneau arrière de module photovoltaïque
EP3109906A1 (en) 2014-01-08 2016-12-28 Suzhou Sunshine New Materials Technology Co., Ltd. Humidity-resistant and heat-resistant solar cell backsheet and manufacturing method therefor
US10665742B2 (en) 2014-07-04 2020-05-26 Dsm Ip Assets B.V. Co-extruded backsheet for solar cell modules

Also Published As

Publication number Publication date
AT10898U1 (de) 2009-12-15
RU2009145717A (ru) 2011-06-20
WO2008138021A3 (de) 2009-07-09
RU2444807C2 (ru) 2012-03-10
KR20100014682A (ko) 2010-02-10
CN101715608A (zh) 2010-05-26
MX2009009561A (es) 2009-09-16
CY1111856T1 (el) 2015-11-04
AT10899U1 (de) 2009-12-15
PL2143148T3 (pl) 2011-11-30
KR20100014415A (ko) 2010-02-10
AR066506A1 (es) 2009-08-26
AT505186A1 (de) 2008-11-15
CA2681835A1 (en) 2008-11-20
RU2438210C2 (ru) 2011-12-27
CN101669214A (zh) 2010-03-10
CN101669214B (zh) 2011-12-14
EP2143148A1 (de) 2010-01-13
JP2010527142A (ja) 2010-08-05
PE20090085A1 (es) 2009-04-24
US8318316B2 (en) 2012-11-27
JP2010528454A (ja) 2010-08-19
ES2366685T3 (es) 2011-10-24
AT505199A1 (de) 2008-11-15
CL2008001371A1 (es) 2008-08-22
ATE515065T1 (de) 2011-07-15
AR066507A1 (es) 2009-08-26
PE20090122A1 (es) 2009-05-03
CA2684637A1 (en) 2008-11-20
BRPI0811432A8 (pt) 2015-11-24
EP2143148B1 (de) 2011-06-29
PT2143148E (pt) 2011-09-06
RU2009145726A (ru) 2011-06-20
RS51813B (en) 2011-12-31
DK2143148T3 (da) 2011-10-03
WO2008138022A1 (de) 2008-11-20
MX2009010922A (es) 2009-10-29
HRP20110691T1 (hr) 2011-10-31
EP2150987A2 (de) 2010-02-10
BRPI0811286A2 (pt) 2015-01-20
CL2008001370A1 (es) 2008-08-22
BRPI0811432A2 (pt) 2015-08-04
AR079922A1 (es) 2012-02-29
SI2143148T1 (sl) 2011-10-28
WO2008138021A2 (de) 2008-11-20
US20100119841A1 (en) 2010-05-13

Similar Documents

Publication Publication Date Title
US20100059105A1 (en) Use of polyamide as an encapsulating material for photovoltaic modules
KR101780925B1 (ko) 폴리비닐리덴 플루오라이드 배면시트를 구비한 태양광 모듈
JP5301107B2 (ja) 太陽電池モジュール用バックシート及びこれを用いた太陽電池モジュール
JP2012039086A (ja) 光起電力モジュール用多層バックシートおよびその製造方法並びに光起電力モジュール製造への使用
CN108198884B (zh) 耐湿热的太阳能电池背板及其制造方法
JP2009267294A (ja) 太陽電池用バックシート
EP2093804A1 (en) Solar cell system with encapsulant
WO2009157545A1 (ja) 太陽電池用積層シート及びこれを用いた太陽電池モジュール
KR20190060886A (ko) 광기전 모듈 및 라미네이트
JP2008085293A (ja) 太陽電池モジュール用バックシート及びこれを用いた太陽電池モジュール
JP5156172B2 (ja) 太陽電池モジュール用バックシート及びこれを用いた太陽電池モジュール
JP2008108948A (ja) 太陽電池裏面封止用シートおよび太陽電池モジュール
CN104465836B (zh) 一种太阳能电池绝缘背材、组件及其生产工艺
CN107757028A (zh) 多层膜和光电模块
CN101979247A (zh) 太阳能光伏电池用封装背板
JP6686291B2 (ja) 太陽電池モジュール用封止材シート及びそれを用いてなる封止材一体型裏面保護シート
KR20140015373A (ko) 광기전 백시트 라미네이트, 광기전 백시트 라미네이트를 포함하는 광기전 모듈, 및 광기전 백시트 라미네이트의 제조방법
TW201505195A (zh) 後觸點型太陽能電池模組
ES2700349T3 (es) Lámina posterior coextruida para módulos de células solares
WO2023238844A1 (ja) 集電シート用樹脂フィルム、集電シート用フィルム、集電シート、集電シート付き太陽電池素子、および太陽電池
EA038590B1 (ru) Конструкция
JP2018508999A (ja) ソーラーモジュール用裏面フィルム
WO2023043448A1 (en) Bendable photovoltaic device packaging structures and encapsulant material containing cured silicone
JP2017017261A (ja) 太陽電池モジュール用の封止材一体型裏面保護シート及びそれを用いてなる太陽電池モジュール

Legal Events

Date Code Title Description
AS Assignment

Owner name: ISOVOLTA AG,AUSTRIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:MUCKENHUBER, HARALD;REEL/FRAME:023468/0039

Effective date: 20090914

AS Assignment

Owner name: ISOVOLTAIC GMBH, AUSTRIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:ISOVOLTA AG;REEL/FRAME:025143/0333

Effective date: 20100820

AS Assignment

Owner name: ISOVOLTAIC AG, AUSTRIA

Free format text: CHANGE OF NAME;ASSIGNOR:ISOVOLTAIC GMBH;REEL/FRAME:026357/0187

Effective date: 20101123

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION