US20080001320A1 - Optical Material and Method for Modifying the Refractive Index - Google Patents

Optical Material and Method for Modifying the Refractive Index Download PDF

Info

Publication number
US20080001320A1
US20080001320A1 US11/745,746 US74574607A US2008001320A1 US 20080001320 A1 US20080001320 A1 US 20080001320A1 US 74574607 A US74574607 A US 74574607A US 2008001320 A1 US2008001320 A1 US 2008001320A1
Authority
US
United States
Prior art keywords
optical
laser
refractive index
acrylate
methacrylate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/745,746
Other languages
English (en)
Inventor
Wayne H. Knox
Li Ding
Jay Friedrich Kunzler
Dharmendra M. Jani
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Rochester
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to US11/745,746 priority Critical patent/US20080001320A1/en
Priority to EP07798742A priority patent/EP2032102B1/en
Priority to AU2007265218A priority patent/AU2007265218B2/en
Priority to CN200780024664XA priority patent/CN101489509B/zh
Priority to AT07798742T priority patent/ATE475389T1/de
Priority to JP2009518456A priority patent/JP5385136B2/ja
Priority to PCT/US2007/071538 priority patent/WO2008002796A2/en
Priority to DE602007008095T priority patent/DE602007008095D1/de
Priority to CA2655229A priority patent/CA2655229C/en
Priority to KR1020087031661A priority patent/KR101372742B1/ko
Assigned to BAUSCH & LOMB INCORPORATED reassignment BAUSCH & LOMB INCORPORATED ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: JANI, DHARMENDRA M., KUNZLER, JAY FRIEDRICH
Assigned to UNIVERSITY OF ROCHESTER reassignment UNIVERSITY OF ROCHESTER ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KNOX, WAYNE, DING, LI
Assigned to CREDIT SUISSE reassignment CREDIT SUISSE SECURITY AGREEMENT Assignors: B & L DOMESTIC HOLDINGS CORP., B&L CRL INC., B&L CRL PARTNERS L.P., B&L FINANCIAL HOLDINGS CORP., B&L MINORITY DUTCH HOLDINGS LLC, B&L SPAF INC., B&L VPLEX HOLDINGS, INC., BAUSCH & LOMB CHINA, INC., BAUSCH & LOMB INCORPORATED, BAUSCH & LOMB INTERNATIONAL INC., BAUSCH & LOMB REALTY CORPORATION, BAUSCH & LOMB SOUTH ASIA, INC., BAUSCH & LOMB TECHNOLOGY CORPORATION, IOLAB CORPORATION, RHC HOLDINGS, INC., SIGHT SAVERS, INC., WILMINGTON MANAGEMENT CORP., WILMINGTON PARTNERS L.P., WP PRISM, INC.
Priority to US11/948,298 priority patent/US7789910B2/en
Publication of US20080001320A1 publication Critical patent/US20080001320A1/en
Assigned to BAUSCH & LOMB INCORPORATED reassignment BAUSCH & LOMB INCORPORATED RELEASE BY SECURED PARTY (SEE DOCUMENT FOR DETAILS). Assignors: CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH
Assigned to CITIBANK N.A., AS ADMINISTRATIVE AGENT reassignment CITIBANK N.A., AS ADMINISTRATIVE AGENT SECURITY AGREEMENT Assignors: BAUSCH & LOMB INCORPORATED, EYEONICS, INC.
Priority to US13/686,952 priority patent/US8932352B2/en
Priority to US13/782,257 priority patent/US10543076B2/en
Assigned to BAUSCH & LOMB INCORPORATED, ISTA PHARMACEUTICALS, WP PRISM INC. (N/K/A BAUSCH & LOMB HOLDINGS INC.) reassignment BAUSCH & LOMB INCORPORATED RELEASE OF SECURITY INTEREST Assignors: CITIBANK N.A., AS ADMINISTRATIVE AGENT
Assigned to GOLDMAN SACHS LENDING PARTNERS LLC, AS COLLATERAL AGENT reassignment GOLDMAN SACHS LENDING PARTNERS LLC, AS COLLATERAL AGENT SECURITY AGREEMENT Assignors: BAUSCH & LOMB INCORPORATED
Assigned to UNIVERSITY OF ROCHESTER reassignment UNIVERSITY OF ROCHESTER ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BAUSCH & LOMB INCORPORATED
Priority to US14/564,207 priority patent/US9622912B2/en
Assigned to BARCLAYS BANK PLC, AS SUCCESSOR AGENT reassignment BARCLAYS BANK PLC, AS SUCCESSOR AGENT NOTICE OF SUCCESSION OF AGENCY Assignors: GOLDMAN SACHS LENDING PARTNERS, LLC
Priority to US15/455,870 priority patent/US10299909B2/en
Priority to US15/923,443 priority patent/US10806567B2/en
Assigned to BAUSCH & LOMB INCORPORATED reassignment BAUSCH & LOMB INCORPORATED RELEASE OF SECURITY INTEREST IN SPECIFIED PATENTS Assignors: BARCLAYS BANK PLC, AS COLLATERAL AGENT
Priority to US16/388,992 priority patent/US10893936B2/en
Priority to US17/150,546 priority patent/US20210128294A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F2/00—Filters implantable into blood vessels; Prostheses, i.e. artificial substitutes or replacements for parts of the body; Appliances for connecting them with the body; Devices providing patency to, or preventing collapsing of, tubular structures of the body, e.g. stents
    • A61F2/02—Prostheses implantable into the body
    • A61F2/14—Eye parts, e.g. lenses, corneal implants; Implanting instruments specially adapted therefor; Artificial eyes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29D—PRODUCING PARTICULAR ARTICLES FROM PLASTICS OR FROM SUBSTANCES IN A PLASTIC STATE
    • B29D11/00—Producing optical elements, e.g. lenses or prisms
    • B29D11/00009—Production of simple or compound lenses
    • B29D11/00432—Auxiliary operations, e.g. machines for filling the moulds
    • B29D11/00461—Adjusting the refractive index, e.g. after implanting
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F2/00—Filters implantable into blood vessels; Prostheses, i.e. artificial substitutes or replacements for parts of the body; Appliances for connecting them with the body; Devices providing patency to, or preventing collapsing of, tubular structures of the body, e.g. stents
    • A61F2/02—Prostheses implantable into the body
    • A61F2/14—Eye parts, e.g. lenses, corneal implants; Implanting instruments specially adapted therefor; Artificial eyes
    • A61F2/16—Intraocular lenses
    • A61F2/1613—Intraocular lenses having special lens configurations, e.g. multipart lenses; having particular optical properties, e.g. pseudo-accommodative lenses, lenses having aberration corrections, diffractive lenses, lenses for variably absorbing electromagnetic radiation, lenses having variable focus
    • A61F2/1624—Intraocular lenses having special lens configurations, e.g. multipart lenses; having particular optical properties, e.g. pseudo-accommodative lenses, lenses having aberration corrections, diffractive lenses, lenses for variably absorbing electromagnetic radiation, lenses having variable focus having adjustable focus; power activated variable focus means, e.g. mechanically or electrically by the ciliary muscle or from the outside
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F2/00—Filters implantable into blood vessels; Prostheses, i.e. artificial substitutes or replacements for parts of the body; Appliances for connecting them with the body; Devices providing patency to, or preventing collapsing of, tubular structures of the body, e.g. stents
    • A61F2/02—Prostheses implantable into the body
    • A61F2/14—Eye parts, e.g. lenses, corneal implants; Implanting instruments specially adapted therefor; Artificial eyes
    • A61F2/16—Intraocular lenses
    • A61F2/1613—Intraocular lenses having special lens configurations, e.g. multipart lenses; having particular optical properties, e.g. pseudo-accommodative lenses, lenses having aberration corrections, diffractive lenses, lenses for variably absorbing electromagnetic radiation, lenses having variable focus
    • A61F2/1624—Intraocular lenses having special lens configurations, e.g. multipart lenses; having particular optical properties, e.g. pseudo-accommodative lenses, lenses having aberration corrections, diffractive lenses, lenses for variably absorbing electromagnetic radiation, lenses having variable focus having adjustable focus; power activated variable focus means, e.g. mechanically or electrically by the ciliary muscle or from the outside
    • A61F2/1627—Intraocular lenses having special lens configurations, e.g. multipart lenses; having particular optical properties, e.g. pseudo-accommodative lenses, lenses having aberration corrections, diffractive lenses, lenses for variably absorbing electromagnetic radiation, lenses having variable focus having adjustable focus; power activated variable focus means, e.g. mechanically or electrically by the ciliary muscle or from the outside for changing index of refraction, e.g. by external means or by tilting
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F2/00—Filters implantable into blood vessels; Prostheses, i.e. artificial substitutes or replacements for parts of the body; Appliances for connecting them with the body; Devices providing patency to, or preventing collapsing of, tubular structures of the body, e.g. stents
    • A61F2/02—Prostheses implantable into the body
    • A61F2/14—Eye parts, e.g. lenses, corneal implants; Implanting instruments specially adapted therefor; Artificial eyes
    • A61F2/16—Intraocular lenses
    • A61F2/1613—Intraocular lenses having special lens configurations, e.g. multipart lenses; having particular optical properties, e.g. pseudo-accommodative lenses, lenses having aberration corrections, diffractive lenses, lenses for variably absorbing electromagnetic radiation, lenses having variable focus
    • A61F2/1624—Intraocular lenses having special lens configurations, e.g. multipart lenses; having particular optical properties, e.g. pseudo-accommodative lenses, lenses having aberration corrections, diffractive lenses, lenses for variably absorbing electromagnetic radiation, lenses having variable focus having adjustable focus; power activated variable focus means, e.g. mechanically or electrically by the ciliary muscle or from the outside
    • A61F2/1635—Intraocular lenses having special lens configurations, e.g. multipart lenses; having particular optical properties, e.g. pseudo-accommodative lenses, lenses having aberration corrections, diffractive lenses, lenses for variably absorbing electromagnetic radiation, lenses having variable focus having adjustable focus; power activated variable focus means, e.g. mechanically or electrically by the ciliary muscle or from the outside for changing shape
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F9/00—Methods or devices for treatment of the eyes; Devices for putting-in contact lenses; Devices to correct squinting; Apparatus to guide the blind; Protective devices for the eyes, carried on the body or in the hand
    • A61F9/007—Methods or devices for eye surgery
    • A61F9/008—Methods or devices for eye surgery using laser
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F9/00—Methods or devices for treatment of the eyes; Devices for putting-in contact lenses; Devices to correct squinting; Apparatus to guide the blind; Protective devices for the eyes, carried on the body or in the hand
    • A61F9/007—Methods or devices for eye surgery
    • A61F9/008—Methods or devices for eye surgery using laser
    • A61F9/00825—Methods or devices for eye surgery using laser for photodisruption
    • A61F9/00834—Inlays; Onlays; Intraocular lenses [IOL]
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29D—PRODUCING PARTICULAR ARTICLES FROM PLASTICS OR FROM SUBSTANCES IN A PLASTIC STATE
    • B29D11/00—Producing optical elements, e.g. lenses or prisms
    • B29D11/02—Artificial eyes from organic plastic material
    • B29D11/023—Implants for natural eyes
    • G—PHYSICS
    • G02—OPTICS
    • G02C—SPECTACLES; SUNGLASSES OR GOGGLES INSOFAR AS THEY HAVE THE SAME FEATURES AS SPECTACLES; CONTACT LENSES
    • G02C7/00—Optical parts
    • G02C7/02—Lenses; Lens systems ; Methods of designing lenses
    • G02C7/04—Contact lenses for the eyes
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F2/00—Filters implantable into blood vessels; Prostheses, i.e. artificial substitutes or replacements for parts of the body; Appliances for connecting them with the body; Devices providing patency to, or preventing collapsing of, tubular structures of the body, e.g. stents
    • A61F2/02—Prostheses implantable into the body
    • A61F2/14—Eye parts, e.g. lenses, corneal implants; Implanting instruments specially adapted therefor; Artificial eyes
    • A61F2/16—Intraocular lenses
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F9/00—Methods or devices for treatment of the eyes; Devices for putting-in contact lenses; Devices to correct squinting; Apparatus to guide the blind; Protective devices for the eyes, carried on the body or in the hand
    • A61F9/007—Methods or devices for eye surgery
    • A61F9/008—Methods or devices for eye surgery using laser
    • A61F2009/00842—Permanent Structural Change [PSC] in index of refraction; Limit between ablation and plasma ignition
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
    • A61F9/00—Methods or devices for treatment of the eyes; Devices for putting-in contact lenses; Devices to correct squinting; Apparatus to guide the blind; Protective devices for the eyes, carried on the body or in the hand
    • A61F9/007—Methods or devices for eye surgery
    • A61F9/008—Methods or devices for eye surgery using laser
    • A61F2009/00897—Scanning mechanisms or algorithms
    • G—PHYSICS
    • G02—OPTICS
    • G02C—SPECTACLES; SUNGLASSES OR GOGGLES INSOFAR AS THEY HAVE THE SAME FEATURES AS SPECTACLES; CONTACT LENSES
    • G02C2202/00—Generic optical aspects applicable to one or more of the subgroups of G02C7/00
    • G02C2202/14—Photorefractive lens material

Definitions

  • the present invention relates to a method of using a laser to modify the refractive index of an optical device, and the resulting optical device.
  • intraocular lenses there are two types. One type replaces the eye's natural lens, usually to replace a cataractous lens. The other type is used to supplement an existing lens and functions as a permanent corrective lens.
  • This type of lens (referred to as a phakic IOL) is implanted in the anterior or posterior chamber to correct refractive errors of the eye.
  • the power for either type of IOL required for enmetropia i.e., point focus on the retina from light originating at infinity
  • the power of the implanted lens is selected based on pre-operative measurements of ocular length and corneal curvature to enable the patient to see without or with little vision correction.
  • the light-adjustable lens is said to comprise (i) a first polymer matrix and (ii) a refraction modulating composition (RMC) that is capable of stimulus-induced polymerization.
  • RMC refraction modulating composition
  • the first polymer matrix and the RMC are selected such that the components that comprise the RMC are capable of diffusion within the first polymer matrix. Put another way, a loose first polymer matrix will tend to be paired with larger RMC components and a tight first polymer matrix will tend to be paired with smaller RMC components.
  • an appropriate energy source e.g., heat or light
  • the RMC Upon exposure to an appropriate energy source (e.g., heat or light), the RMC typically forms a second polymer matrix in the exposed region of the optical element. After exposure, the RMC in the unexposed region will migrate into the exposed region over time. The amount of RMC migration into the exposed region is time dependent and may be precisely controlled.
  • the RMC components will re-equilibrate and redistribute throughout the lens material (i.e., the first polymer matrix, including the exposed region).
  • the region is re-exposed to the energy source, the RMC that has since migrated into the region polymerizes to further increase the formation of the second polymer matrix.
  • This process (exposure followed by an appropriate time interval to allow for diffusion) may be repeated until the exposed region of the optical element has reached the desired property (e.g., power, refractive index, or shape).
  • the entire optical element is then exposed to an energy source to “lock-in” the desired lens property by polymerizing the remaining RMC in the lens material.
  • the power of the lens is changed by a shape change caused by the migrating of the RMC and subsequent polymerization(s).
  • U.S. Pat. No. 7,105,110 describes a method and instrument to irradiate a light adjustable lens with an appropriate amount of radiation in an appropriate pattern.
  • the method is said to include aligning a source of the modifying radiation so as to impinge the radiation onto the lens in a pattern, and controlling the quantity of the impinging radiation.
  • the quantity of the impinging radiation is controlled by controlling the intensity and duration of the irradiation.
  • the invention is directed to a method for modifying the refractive index of an optical, polymeric material.
  • the method comprises irradiating select regions of the optical, polymeric material with a focused, visible or near-IR laser having a pulse energy from 0.05 nJ to 1000 nJ.
  • the irradiation results in the formation of refractive structures, which exhibit little or no scattering loss.
  • the invention is also directed to an optical device comprising an optical polymeric material with select regions that have been irradiated with a focused, visible or near-IR laser having a pulse energy from 0.05 nJ to 1000 nJ.
  • the irradiation results in the formation of refractive structures, which exhibit little or no scattering loss and are characterized by a positive change in refractive index.
  • the invention is also directed to a method for modifying the refractive index of an intraocular lens following surgical insertion of the intraocular lens in a human eye.
  • the method includes identifying and measuring the aberrations caused by the intraocular lens resulting from the surgical procedure, and determining the position and shape of structures to be written into the lens to correct for the aberrations. Once the type and location of structures to be written are determined, select regions of the lens are irradiated with a focused, visible or near-IR laser having a pulse energy from 0.05 nJ to 1000 nJ. The irradiation results in the formation of refractive structures, which exhibit little or no scattering loss and are characterized by a positive change in refractive index.
  • FIG. 1 is a microscope photograph of a line grating written in an optical, polymeric material produced by laser irradiation
  • FIG. 2 is a microscope photograph of a line grating written above and orthogonal to another line grating in an optical, polymeric material produced by laser irradiation;
  • FIG. 3 is a microscope photograph of an array of cylinders etched in an optical, polymeric material produced by laser irradiation
  • FIG. 4 is a microscope photograph of one array of cylinders (20 ⁇ 20) etched above and slightly offset to another array of cylinders (20 ⁇ 20) in an optical, polymeric material produced by laser irradiation;
  • FIG. 5 is a schematic representation of a three-dimensional structure in an optical, polymeric material that can be produced by laser irradiation
  • FIG. 6 is a schematic representation of creating a convex, plano or concave structure in an optical, polymeric material to yield a positive or negative correction
  • FIG. 7 is a schematic representation of the laser and optical system used to write the structures shown in FIGS. 1 to 4 ;
  • FIG. 8 shows schematically an arrangement of a sample for modification by a laser.
  • the high intensity of light at the focus point causes a nonlinear absorption of photons (typically multi-photon absorption) and leads to a change in the refractive index of the material at the focus point.
  • the region of the material just outside the focal region is minimally affected by the laser light. Accordingly, select regions of an optical, polymeric material can be modified with a laser resulting in a positive change in the refractive index in these regions.
  • the invention is directed to a method for modifying the refractive index of an optical device.
  • the method comprises irradiating select regions of an optical, polymeric material of the device with a focused, visible or near-IR laser having a pulse energy from 0.05 nJ to 1000 nJ. Also, the irradiated regions exhibit little or no scattering loss, which means that the structures formed in the irradiated regions are not clearly visible under appropriate magnification without contrast enhancement.
  • the pulse energy of the focused laser used in the method will in-part depend on the type of optical material that is being irradiated, how much of a change in refractive index is desired and the type of structures one wants to imprint within the material.
  • the selected pulse energy will also depend upon the scan rate at which the structures are written into the optical material. Typically, greater pulse energies will be needed for greater scan rates. For example, some materials will call for a pulse energy from 0.2 nJ to 100 nJ, whereas other optical materials will call for a pulse energy from 0.5 nJ to 10 nJ.
  • the pulse width must be preserved so that the pulse peak power is strong enough to exceed the nonlinear absorption threshold of the optical material.
  • the glass of the focusing objective(s) significantly increases the pulse width due to the positive dispersion of the glass.
  • a compensation scheme is used to provide a corresponding negative dispersion that can compensate for the positive dispersion introduced by the focusing objective(s).
  • focused in this application refers to the focusing of light from a laser within an optical, polymeric material using a compensation scheme to correct for the positive dispersion introduced by the focusing objective(s).
  • the compensation scheme can include an optical arrangement selected from the group consisting of at least two prisms and at least one mirror, at least two diffraction gratings, a chirped mirror and dispersion compensating mirrors to compensate for the positive dispersion introduced by the focus objective.
  • the compensation scheme comprises at least one prism, in many cases at least two prisms, and at least one mirror to compensate for the positive dispersion of the focusing objective. In another embodiment, the compensation scheme comprises at least two gratings to compensate for the positive dispersion of the focusing objective. Any combination of prisms, gratings and/or mirrors can be used for the compensation scheme.
  • the use of the compensation scheme with the focusing objective can generate pulses with a pulse energy from 0.01 nJ to 100 nJ, or from 0.01 nJ to 50 nJ, and a pulse width of from 4 fs to 200 fs.
  • the laser will generate light with a wavelength in the range from violet to near-infrared radiation.
  • the wavelength of the laser is in the range from 400 nm to 1500 nm, from 400 nm to 1200 nm or from 600 nm to 900 nm.
  • the laser is a pumped Ti:sapphire laser with an average power of 10 mW to 1000 mW.
  • a laser system will generate light with a wavelength of approximately 800 nm.
  • an amplified fiber laser that can generate light with a wavelength from 1000 nm to 1600 nm can be used
  • the laser will have a peak intensity at focus of greater than 10 13 W/cm 2 . At times, it may be advantageous to provide a laser with a peak intensity at focus of greater than 10 14 W/cm 2 , or greater than 10 15 W/cm 2 .
  • the method of the invention provides an opportunity for an ocular surgeon to modify the refractive index of an optical device, e.g., an intraocular lens or corneal inlay, after the device has been implanted into the eye of a patient.
  • the method allows the surgeon to correct any aberrations as a result of the surgery.
  • the method also allows the surgeon to adjust the power of the lens or inlay by increasing the refractive index in the irradiated regions. For example, starting from a lens of selected power (will vary according to the ocular requirements of the patient), the surgeon can further adjust the refractive properties of the lens to correct a patients vision based upon the individual needs of the patient.
  • an intraocular lens would essentially function like contact lenses or glasses to individually correct for the refractive error of a patient's eye.
  • the implanted lens can be adjusted by increasing the refractive index of select regions of the lens, post-operative refractive errors resulting from pre-operative measurement errors, variable lens positioning during implantation and wound healing (aberrations) can be corrected or fine tuned in-situ.
  • cataract surgery typically requires that the natural lens of each eye be replaced with an intraocular lens (IOL).
  • IOL intraocular lens
  • the surgeon can correct for aberrations resulting from the surgery or correct for slight misplacement of the IOL.
  • the patient would return to the surgeon to have select regions of the IOL irradiated. These irradiated regions would experience a positive change in refractive index, which would correct for the aberrations as well as the patients needs for vision correction.
  • the surgeon would be able to adjust the IOL in one eye for distance and adjust the IOL in the opposite eye for reading.
  • the irradiated portions of the optical material will exhibit a positive change in refractive index of about 0.01 or more.
  • the refractive index of the region will increase by about 0.03 or more.
  • applicants have measured a positive change in refractive index in an optical material of about 0.06.
  • the method of the invention modifies the optical properties of the material not by casting an optical material with nonreacted monomer (refraction modulation composition) followed by laser irradiation to promote additional polymerization chemistry as described in the Calhoun patent, but rather by changing the refractive index of an already completely polymerized optical material.
  • the term “completely polymerized” when used to characterize the optical materials used in the method means that the optical materials are 95% or more polymerized.
  • One way to measure the completeness of a polymerized optical material is by near infra-red spectroscopy, which is used to qualitatively determine the vinyl content of the material. Simple gravimetric weight analysis can also be used.
  • the irradiated regions of the optical device formed by the method of the invention can be defined by two- or three-dimensional structures.
  • the two- or three-dimensional structures can comprise an array of discrete cylinders.
  • the two- or three-dimensional structures can comprise a series of lines (a grating) or a combination of an array of cylinders and a series of lines.
  • the two- or three-dimensional structures can comprise area or volume filled structures, respectively. These area or volume filled structures are formed by continuously scanning the laser over a select region of the polymeric material.
  • Nanometer-sized structures can also be formed by the zone-plate-array lithography method describe by R. Menon et al., Proc. SPIE, Vol. 5751, 330-339 (May 2005); Materials Today, p. 26 (February 2005).
  • the irradiated regions of the optical device are defined by a series of lines in a two dimensional plane having a width from 0.2 ⁇ m to 3 ⁇ m, preferably a width from 0.6 ⁇ m to 1.5 ⁇ m and a height from 0.4 ⁇ m to 8 ⁇ m, preferably a height from 1.0 ⁇ m to 4 ⁇ m (height is measured in the z direction of the material, which is parallel to direction of the laser light).
  • a line grating comprising a plurality of lines with each line of any desired length, about 0.8 ⁇ m to about 1.5 ⁇ m in width and about 2 ⁇ m to 5 ⁇ m in height.
  • the lines can be separated by as little as 1.0 ⁇ m (0.5 ⁇ m spacing), and any number of lines can be incorporated into the material.
  • the grating can be positioned at any selected depth (z-direction), and any number of line gratings can be generated at various depths into the material.
  • FIG. 1 is a microscope photograph with contrasting background of a line grating comprising 20 lines written into an optical material. Each line is about 100 ⁇ m in length, about 1 ⁇ m in width with a line separation of about 5 ⁇ m. The lines have a height of about 3 ⁇ m and were written into the material at a distance of about 100 ⁇ m from the top surface of the material. Similar microscope photographs exhibiting line gratings were obtained at a distance of about 200 ⁇ m and 400 ⁇ m from the top surface of the material, thereby demonstrating that structures can be written into the optical material at any selected depth.
  • FIG. 2 is a microscopic photograph with contrasting background of one line grating written above and orthogonal to another line grating.
  • Each of the gratings has a similar dimensional structure to that described for FIG. 1 above.
  • One line grating is positioned about 100 ⁇ m into the material, and the other line grating is positioned about 110 ⁇ m into the material for a center-line, grating separation of about 10 ⁇ m.
  • each of these line structures has a height (depth) of about 3 ⁇ m.
  • FIG. 3 is a microscopic photograph with contrasting background of an array of cylinders written into an optical material.
  • Each cylinder is about 1 ⁇ m in diameter with a height of about 3 ⁇ m.
  • the cylinders are separated by about 5 ⁇ m.
  • the cylinders were etched into the material at a distance of about 100 ⁇ m from the top surface of the material.
  • FIG. 4 is a microscopic photograph with contrasting background of one array of cylinders (20 ⁇ 20) written above and slightly offset to another array of cylinders (20 ⁇ 20).
  • Each of the cylinders has a similar dimensional structure to that described for FIG. 3 above.
  • One array is positioned about 100 ⁇ m into the material, and the other array is positioned about 105 ⁇ m into the material for a center-line separation of about 5 ⁇ m.
  • Each of the cylinders has a height (depth) of about 3 ⁇ m.
  • the area-filled or volume-filled two- or three-dimensional structures can be formed by continuously scanning the laser over selected regions of the optical, polymeric material.
  • Refractive-type optical devices can be micro-machined inside the volume of an optical, polymer material by repeatedly scanning a tightly focused beam of femtosecond pulses in an area segment. The area of the segment can be changed correspondingly with the depth of the scan, so as to produce three-dimensionally shaped lenses with spheric, aspheric, toroidal or cylindrical shapes as shown in FIG. 5 .
  • these refractive corrective lenses can be made in various combinations of convex, plano- or concave to yield a positive correction, or negative correction, as shown in FIG. 6 .
  • the devices can be stacked vertically, written separately in different planes, so as to act as a single lens. Additional corrective layers can be written as desired.
  • a non-limiting embodiment of a laser system 10 for irradiating an optical, polymeric material with a laser to modify the refractive index of the material in select regions is illustrated in FIG. 7 .
  • a laser source comprises a Kerr-lens mode-locked Ti:Sapphire laser 12 (Kapteyn-Murnane Labs, Boulder, Colo.) pumped by 4 W of a frequency-doubled Nd:YVO 4 laser 14 .
  • the laser generates pulses of 300 mW average power, 30 fs pulse width and 93 MHz repetition rate at wavelength of 800 nm.
  • the measured average laser power at the objective focus on the material is about 120 mW, which indicates the pulse energy for the femtosecond laser is about 1.3 nJ.
  • the pulse width must be preserved so that the pulse peak power is strong enough to exceed the nonlinear absorption threshold of the materials. Because a large amount of glass inside the focusing objective significantly increases the pulse width due to the positive dispersion inside of the glass, an extra-cavity, compensation scheme is used to provide the negative dispersion that compensates for the positive dispersion introduced by the focusing objective.
  • Two SF10 prisms 24 and 28 and one ending mirror 32 form a two-pass one-prism-pair configuration. We used a 37.5 cm separation distance between the prisms to compensate the dispersion of the microscope objective and other optics within the optical path.
  • a collinear autocorrelator 40 using third-order harmonic generation is used to measure the pulse width at the objective focus. Both 2 nd and 3 rd harmonic generation have been used in autocorrelation measurements for low NA or high NA objectives.
  • the THG signal is generated at the interface of air and an ordinary cover slip 42 (Corning No. 0211 Zinc Titania glass), and measured with a photomultiplier 44 and a lock-in amplifier 46 .
  • a concave mirror pair 50 and 52 is added into the optical path in order to adjust the dimension of the laser beam so that the laser beam can optimally fills the objective aperture.
  • a 3D 100 nm resolution DC servo motor stage 54 (Newport VP-25 ⁇ A linear stage) and a 2D 0.7 nm resolution piezo nanopositioning stage (PI P-622.2CD piezo stage) are controlled and programmed by a computer 56 as a scanning platform to support and locate the samples.
  • the servo stages have a DC servo-motor so they can move smoothly between adjacent steps.
  • An optical shutter controlled by the computer with 1 ms time resolution is installed in the system to precisely control the laser exposure time.
  • the optical shutter could be operated with the scanning stages to micro-machine different patterns in the materials with different scanning speed at different position and depth and different laser exposure time.
  • a CCD camera 58 along with a monitor 62 is used beside the objective 20 to monitor the process in real time.
  • the method and optical apparatus described above can be used to modify the refractive index of an intraocular lens following the surgical implantation of the intraocular lens in a human eye.
  • the invention is directed to a method comprising identifying and measuring the aberrations resulting from the surgical procedure.
  • this information is processed by a computer.
  • information related to the requisite vision correction for each patient can also be identified and determined, and this information can also be processed by a computer.
  • diagnostic systems that are used to measure the aberrations.
  • common wavefront sensors used today are based on the Schemer disk, the Shack Hartmann wavefront sensor, the Hartmann screen, and the Fizeau and Twymann-Green interferometers.
  • the Shack-Hartmann wavefront measurement system is known in the art and is described in-part by U.S. Pat. Nos. 5,849,006; 6,261,220; 6,271,914 and 6,270,221.
  • Such systems operate by illuminating a retina of the eye and measuring the reflected wavefront.
  • the computer programs determine the position and shape of the optical structures to be written into the lens material to correct for those aberrations. These computer programs are well known to those of ordinary skill in the art.
  • the computer than communicates with the laser-optical system and select regions of the lens are irradiated with a focused, visible or near-IR laser having a pulse energy from 0.05 nJ to 1000 nJ.
  • optical, polymeric materials that can be irradiated by a visible or near-IR laser according to the methods described in this application can be any optical, polymeric material known to those of ordinary skill in the polymeric lens art, particularly those in the art familiar with optical materials used to make intraocular lenses.
  • the optical, polymeric materials are of sufficient optical clarity, and will have a relatively high refractive index of approximately 1.40 or greater. Many of these materials are also characterized by a relatively high elongation of approximately 80 percent or greater.
  • a method of the present invention can be applied to a wide variety of optical materials.
  • Non-limiting examples of such materials include those used in the manufacture of ophthalmic devices, such as contact lenses and IOLs.
  • the method of the present invention can be applied to siloxy-containing polymers, acrylic polymers, other hydrophilic or hydrophobic polymers, copolymers thereof, and mixtures thereof.
  • siloxy-containing polymers that can be used as optical materials are described in U.S. Pat. Nos. 6,762,271; 6,770,728; 6,777,522; 6,849,671; 6,858,218; 6,881,809; 6,908,978; 6,951,914; 7,005,494; 7,022,749; 7,033,391; and 7,037,954.
  • hydrophilic polymers include polymers comprising units of N-vinylpyrrolidone, 2-hydroxyethyl methacrylate, N,N-dimethylacrylamide, methacrylic acid, poly(ethylene glycol monomethacrylate), 1,4-butanediol monovinyl ether, 2-aminoethyl vinyl ether, di(ethylene glycol) monovinyl ether, ethylene glycol butyl vinyl ether, ethylene glycol monovinyl ether, glycidyl vinyl ether, glyceryl vinyl ether, vinyl carbonate, and vinyl carbamate.
  • Non-limiting examples of hydrophobic polymers include polymers comprising units of C 1 -C 10 alkyl methacrylates (e.g., methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, octyl methacrylate, or 2-ethylhexyl methacrylate; preferably, methyl methacrylate to control mechanical properties), C 1 -C 10 alkyl acrylates (e.g., methyl acrylate, ethyl acrylate, propyl acrylate, or hexyl acrylate; preferably, butyl acrylate to control mechanical properties), C 6 -C 40 arylalkyl acrylates (e.g., 2-phenylethyl acrylate, benzyl acrylate, 3-phenylpropyl acrylate, 4-phenylbutyl acrylate, 5-phenylpentyl acrylate, 8-phenylocty
  • the method of the invention is particularly suited for modifying the refractive index in select regions of an optical, polymeric silicone hydrogel, or an optical, non-silicone hydrogel.
  • a silicone hydrogel that can absorb about 36% by weight water (based on the total hydrated weight).
  • hydrogel refers to an optical, polymeric material that can absorb greater than 20% by weight water based on the total hydrated weight.
  • irradiated silicon hydrogel optical materials commercially under the trade name BalafilconTM.
  • This silicone hydrogel system is based on a vinyl carbamate substituted TRIS derivative, that is, tris(trimethylsiloxy)silylpropyl vinylcarbamate) (TPVC).
  • TPVC tris(trimethylsiloxy)silylpropyl vinylcarbamate
  • the TPVC molecule contains the hydrophobic silicone portion and a vinyl carbamate group.
  • the direct hydrophilic attachment of the carbamate provides the silicone monomer with sufficient hydrophilic character.
  • the vinyl carbamate group provides a polymerizable vinyl group for the attachment of hydrophilic monomers.
  • the resulting silicon hydrogels are transparent, exhibit high Dk and low modulus materials that are insoluble in water.
  • a hydrogel copolymer that comprises about 90% (by weight) N-vinylpyrrolidone (NVP) and about 10% (by weight) 4-t-butyl-2-hydroxycyclohexyl methacrylate.
  • NVP N-vinylpyrrolidone
  • HEMA B which is a poly(2-hydroxyethyl methacrylate) cross-linked with about 0.9% (by weight) of ethylene glycol dimethacrylate (“EGDMA”).
  • EGDMA ethylene glycol dimethacrylate
  • This HEMA-hydrogel can absorb about 37% (by weight) water.
  • Other optical, polymeric materials that can have its refractive index modified by irradiating select regions with a laser are provided as follows.
  • the optical polymeric material can be prepared as a copolymer from at least three monomeric components.
  • the first monomeric component is present in the copolymer in an amount of at least 70% by weight, and its homopolymer will have a refractive index of at least 1.50, preferably at least 1.52 or at least 1.54.
  • the second monomeric component is present in the copolymer in an amount from 3% to 20% or from 3% to 10%, by weight, and its homopolymer will have a glass transition temperature of less than about 300° C., preferably less than about 220° C.
  • the first and second monomeric components together represent at least 80% by weight of the copolymer.
  • homopolymer refers to a polymer that is derived substantially completely from the respective monomeric component. Minor amounts of catalysts, initiators and the like can be included, as is conventionally the case, in order to facilitate the formation of the homopolymer. In addition, the homopolymers of both the first and the second monomeric components have sufficiently high molecular weights or degrees of polymerization so as to be useful as IOL materials.
  • Particularly useful first monomeric components include styrene, vinyl carbazole, vinyl naphthalene, benzyl acrylate, phenyl acrylate, naphthyl acrylate, pentabromophenyl acrylate, 2-phenoxyethyl acrylate, 2-phenoxyethyl methacrylate, 2,3-dibromopropyl acrylate and mixtures thereof.
  • Particularly useful second monomeric components include n-butyl acrylate, n-hexyl acrylate, 2-ethylhexyl acrylate, 2-ethoxyethyl acrylate, 2,3-dibromopropyl acrylate, n-1,1-dihydroperfluorobutyl acrylate and mixtures thereof.
  • the third monomeric component is best described as a cross-linking monomeric constituent that can form cross-links with the first or the second monomeric components.
  • the cross-linking monomeric component is multi-functional and can chemically react with both the first and second monomeric components.
  • the third component is present in an amount effective to facilitate returning a deformed IOL made by polymerizing the three monomeric components to its original shape in the human eye.
  • the third or crosslinking monomeric component is often present in a minor amount relative to the amounts of the first and second monomeric components.
  • the third component is present in the copolymer in an amount of less than about 1% by weight of the copolymer.
  • useful crosslinking monomeric components include ethylene glycol dimethacrylate, propylene glycol dimethacrylate, ethylene glycol diacrylate and the like and mixtures thereof.
  • the copolymer can further include a fourth component derived from a hydrophilic monomeric component.
  • This fourth component is present in an amount, from 2% to 20% by weight of the copolymer.
  • the fourth component is preferably present in an amount of less than about 15% by weight of the copolymer.
  • Copolymers which include about 15% by weight or more of a constituent derived from hydrophilic monomeric components tend to form hydrogels if exposed to water.
  • hydrophilic monomeric component refers to compounds which produce hydrogel-forming homopolymers, that is homopolymers which become associated with at least 20% of water, based on the weight of the homopolymer, if placed in contact with an aqueous solution.
  • useful hydrophilic monomeric components include N-vinyl pyrrolidone; hydroxyalkyl acrylates and hydroxyalkyl methacrylates, such as 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 3-hydroxypropyl acrylate, 3-hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, 4-hydroxybutyl methacrylate, 2,3-dihydroxypropyl acrylate, 2,3-dihydroxypropyl methacrylate and the like; acrylamide; N-alkyl acrylamides such as N-methyl acrylamide, N-ethyl acrylamide, N-propyl acrylamide, N-butyl acrylamide and the like; acrylic acid; methacrylic acid; and the like and mixtures thereof.
  • optical, polymeric materials can also be prepared from monomers having the formula:
  • R is H or CH 3 ; m is 0-10;
  • Ar is any aromatic ring, such as benzene, which can be unsubstituted or substituted with H, CH 3 , C 2 H 5 , n-C 3 H 7 , iso-C 3 H 7 , OCH 3 , C 6 H 11 , Cl, Br, phenyl or benzyl; and
  • the optical material will have a glass transition temperature not greater than 37° C. and an elongation of at least 150%.
  • Exemplary monomers include, but are not limited to: 2-ethylphenoxy methacrylate, 2-ethylphenoxy acrylate, 2-ethylthiophenyl methacrylate, 2-ethylthiophenyl acrylate, 2-ethylaminophenyl methacrylate, phenyl methacrylate, benzyl methacrylate, 2-phenylethyl methacrylate, 3-phenylpropyl methacrylate, 4-phenylbutyl methacrylate, 4-methylphenyl methacrylate, 4-methylbenzyl methacrylate, 2-2-methylphenylethyl methacrylate, 2-3-methylphenylethyl methacrylate, 2-4-methylphenylethyl methacrylate, 2-(4-propylphenyl)ethyl methacrylate, 2-(4-(1-methylethyl)phenyl)ethyl methacrylate, 2-(4-methoxyphenyl)
  • the copolymerizable cross-linking agent can be any terminally ethylenically unsaturated compound having more than one unsaturated group.
  • Suitable cross-linking agents include, for example: ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, allyl methacrylate, 1,3-propanedioldimethacrylate, allylmethacrylate 1,6-hexanediol dimethacrylate, 1,4-butanediol dimethacrylate, and the like.
  • a preferred cross-linking agent is 1,4-butanediol diacrylate.
  • the aryl acrylate/methacrylate based optical materials will generally comprise a greater mole percent of acrylate ester residues than of methacrylate ester residues. It is preferred that the aryl acrylate monomers constitute from about 60 mole percent to about 95 mole percent of the polymer, while the aryl methacrylate monomers constitute from about 5 mole percent to about 40 mole percent of the polymer. Most preferred is a polymer comprising about 60-70 mole percent 2-phenylethyl acrylate and about 30-40 mole percent 2-phenylethyl methacrylate.
  • the optical, polymeric materials can also be prepared from a reinforced cross-linked silicone elastomer which includes a polymer containing 12 to 18 mol percent of aryl substituted siloxane units of the formula R 4 R 5 —SiO.
  • R 4 and R 5 are the same or different and represent phenyl, mono-lower alkyl substituted phenyl groups, or di-lower alkyl substituted phenyl groups.
  • both R 4 and R 5 are phenyl.
  • the polymer has end blockers containing siloxane units of the formula R 1 R 2 R 3 —SiO 5 wherein R 1 and R 2 are alkyl, aryl or substituted alkyl or substituted aryl groups, and R 1 and R 2 can be the same or different.
  • the R 3 group of the end blocking siloxane units is an alkenyl group.
  • the end blocker is a dimethylvinyl siloxane unit.
  • the balance of the polymer consists of dialkyl siloxane units of the formula R 6 R 7 —SiO wherein R 6 and R 7 are the same or different from and are methyl or ethyl groups, and the polymer has a degree of polymerization from 100 to 2000.
  • R 6 and R 7 are both methyl, and the degree of polymerization is approximately 250.
  • a trimethyl silyl treated silica reinforcer is finely dispersed in the polymer, in a weight ratio of approximately 15 to 45 parts of the reinforcer to 100 parts of the polymer. Preferably, there is approximately 27 parts of reinforcer to 100 parts of the copolymer.
  • optical, polymeric material can also be prepared by polymerizing the following monomeric components: (A) 5-25% by weight of acrylate represented by the general formula
  • Ar represents an aromatic ring of which hydrogen atom may be substituted by a substitutional group
  • X represents an oxygen atom or a direct bonding
  • m represents an integer of 1 to 5
  • B 50 to 90% by weight of 2-hydroxyethyl (meth)acrylate
  • C 5 to 45% by weight of a (meth)acrylate monomer though not of the formula that represent monomer (A) and not 2-hydroxyethyl (meth)acrylate.
  • the coefficient of water absorption of the homopolymer of monomer (C) is not more than 30% by weight.
  • W represents a weight of the specimen in equilibrium state of water
  • W o represents a weight of the specimen in a dry state
  • An exemplary listing of (meth)acrylate monomer (C) include an alkyl (meth)acrylate containing a straight chain, a branched chain or cyclic chain such as methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, butyl (meth)acrylate, pentyl (meth)acrylate, hexyl meth)acrylate, heptyl (meth)acrylate, nonyl (meth)acrylate, stearyl meth)acrylate, octyl (meth)acrylate, decyl (meth)acrylate, lauryl (meth)acrylate, pentadecyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, cyclopentyl (meth)acrylate, (meth)acrylate, cyclohexyl (meth)acrylate: an alkyl (meth)acrylate containing 1 to
  • optical, polymeric material can also be prepared by copolymerizing a specific monomer mixture comprising perfluorooctylethyloxypropylene (meth)acrylate, 2-phenylethyl (meth)acrylate, an alkyl (meth)acrylate monomer having the following general formula,
  • R is hydrogen or methyl and R 1 is a linear or branched C 4 -C 12 alkyl group, and a crosslinking monomer.
  • alkyl (meth)acrylate monomer include n-butyl acrylate, isobutyl acrylate, isoamyl acrylate, hexyl acrylate, 2-ethylhexyl acrylate, octyl acrylate, isooctyl acrylate, decyl acrylate, isodecyl acrylate, and the like.
  • the perfluorooctylethyloxypropylene (meth)acrylate is present from 5% to 20% by weight, the 2-phenylethyl (meth)acrylate is present from 40% to 60% by weight, the alkyl (meth)acrylate monomer is present from 30% to 50% by weight and the crosslinking agent is present from 0.5% to 4% by weight.
  • the optical, polymeric material can also be prepared from a first (meth)acrylate monomer, a second aromatic monomer, and a third, high water content hydrogel-forming monomer.
  • the first monomeric component is present from 30% to 50% by weight
  • the second monomeric component is present from 10% to 30% by weight
  • the third monomeric component is present from 20% to 40% by weight.
  • a crosslinking agent is also used to prepare the material.
  • the first monomeric component is an aryl acrylate or an aryl methacrylate, and are commonly referred to as aryl (meth)acrylate monomers.
  • aryl implies that the compound contains at least one aromatic group.
  • Exemplary aryl (meth)acrylate monomers include ethylene glycol phenyl ether acrylate (EGPEA), poly(ethylene glycol phenyl ether acrylate) (polyEGPEA), phenyl methacrylate, 2-ethylphenoxy methacrylate, 2-ethylphenoxy acrylate, hexylphenoxy methacrylate, hexylphenoxy acrylate, benzyl methacrylate, 2-phenylethyl methacrylate, 4-methylphenyl methacrylate, 4-methylbenzyl methacrylate, 2-2-methyphenylethyl methacrylate, 2-3-methylphenylethyl methacrylate, 2-4-methylphenylethyl methacrylate
  • the second monomeric component includes a monomer having an aromatic ring with a substituent having at least one site of ethylenic unsaturation.
  • this second monomeric component is not an acrylate.
  • Such monomers have the general formula:
  • X is H or CH 3
  • Ar is a substituted or unsubstituted aromatic ring.
  • Representative second monomeric components include, for example, substituted and unsubstituted styrene compounds. These compounds may be substituted with hydrogen, halogen (e.g. Br, Cl, F), lower alkyl groups (e.g. methyl, ethyl, propyl, butyl, isopropyl), and/or lower alkoxy groups.
  • Suitable aromatic monomers include, for example: styrene, methoxy styrene, and chlorostyrene.
  • the third monomeric component comprises a high water content hydrogel-forming monomer.
  • the third monomeric component includes a methacrylate without an aromatic substituent.
  • Suitable high water content hydrogel-forming monomers include, for example: hydroxyethyl methacrylate (HEMA), hydroxyethoxyethyl methacrylate (HEEMA), hydroxydiethoxyethyl methacrylate, methoxyethyl methacrylate, methoxyethoxyethyl methacrylate, methoxydiethoxyethyl methacrylate, ethylene glycol dimethacrylate, n-vinyl-2-pyrrolidone, methacrylic acid, vinyl acetate and the like and mixtures thereof.
  • HEMA and HEEMA are two of the more preferred third monomeric components.
  • the copolymer may also include a crosslinking agent.
  • the copolymerizable crosslinking agent(s) useful in forming the copolymeric material of the invention include any terminally ethylenically unsaturated compound having more than one unsaturated group.
  • the crosslinking agent includes a diacrylate or a dimethacrylate.
  • the crosslinking agent may also include compounds having at least two (meth)acrylate and/or vinyl groups. Particularly preferred crosslinking agents include diacrylate compounds
  • the optical, polymeric materials are prepared by generally conventional polymerization methods from the respective monomeric components.
  • a polymerization mixture of the monomers in the selected amounts is prepared and a conventional thermal free-radical initiator is added.
  • the mixture is introduced into a mold of suitable shape to form the optical material and the polymerization initiated by gentle heating.
  • Typical thermal, free radical initiators include peroxides, such as benzophenone peroxide, peroxycarbonates, such as bis-(4-t-butulcyclohexyl) peroxydicarbonate, azonitriles, such as azobisisobytyronitrile, and the like.
  • a preferred initiator is bis-(4-t-butylcyclohexyl) peroxydicarbonate (PERK).
  • the monomers can be photopolymerized by using a mold which is transparent to actinic radiation of a wavelength capable of initiating polymerization of these acrylic monomers by itself.
  • Conventional photoinitiator compounds e.g., a benzophenone-type photoinitiator, can also be introduced to facilitate the polymerization.
  • PV2526-164 is a silicone-containing hydrogel that can absorb about 36% (by total weight).
  • RD1817 is a hydrogel copolymer that comprises about 90% (by weight) N-vinylpyrrolidone (“NVP”) and about 10% (by weight) 4-t-butyl-2-hydroxycyclohexyl methacrylate and that can absorb about 80% (by weight) water. Its refractive index when hydrated is very close to the index of water.
  • HEMA B is poly(2-hydroxyethyl methacrylate) cross-linked with about 0.9% (by weight) of ethylene glycol dimethacrylate (“EGDMA”), also a hydrogel, which can absorb about 37% (by weight) water.
  • the refractive indices of PV2526-164, RD1817, and HEMA B are 1.422, 1.363, and 1.438, respectively, when they are in the hydrated state.
  • Each of the hydrogel samples was maintained in a solution (Bausch and Lomb “Renu” solution) between a microscope slide and a glass cover slip to maintain their water-content during micro-machining and subsequent optical measurements. The thickness of these hydrogel samples in the solution is about 700 ⁇ m.
  • the hydrated sample was mounted horizontally on the scanning platform, and the femtosecond laser beam was directed vertically downward through the high-numerical-aperture objective and was focused inside the bulk material, as shown in FIG. B, at a depth of about 100 ⁇ m from the upper surface of the sample.
  • Periodic gratings structures were created with a scanning speed of 0.4 ⁇ m/sec in an X-Y plane perpendicular to the laser beam.
  • An Olympus BX51 Model microscope was used to observe the gratings that were created inside these three materials.
  • the microscope images showed periodically parallel gratings inside the samples with 5- ⁇ m spacing.
  • the gratings were difficult to see in bright-field microscope, indicating that these gratings exhibit low scattering.
  • the width of the gratings was about 1 ⁇ m, which was significantly smaller than the laser focus diameter of 2.5 ⁇ m that was measured using a knife-edge method. Therefore, the modified region is still within the laser irradiation focus volume although there would be heat accumulation generated in the process.
  • a cross section of the PV2526-164 sample revealed that the cross section of the gratings was elliptical with the longer axis oriented in the direction of the laser beam, indicating that there was a larger laser intensity distribution in this direction.
  • ⁇ is the wavelength of the incident laser beam which here is 632.8 nm
  • d is the grating period
  • the diffraction efficiency of the grating can be measured, and since the efficiency is a function of the refractive index change, it may be used to calculate the refractive index change in the laser irradiation region.
  • the efficiency is a function of the refractive index change, it may be used to calculate the refractive index change in the laser irradiation region.
  • ⁇ is the grating line width
  • d is the groove spacing
  • ⁇ 2 and ⁇ 1 are the phase delays through the lines and ambient region respectively
  • b is the thickness of the grating line
  • n is the average refractive index of the material
  • ⁇ n is the average refractive index change in the grating lines
  • ⁇ is the incident light wavelength of the measurement (632.8 nm).
  • the grating line width is 1 ⁇ m and the thickness is 3 ⁇ m.
  • the index change within the laser effect region can be approximated to be uniform.
  • the convolution theorem can be used to calculate the spectrum of the grating such as
  • the intensity distribution of the grating diffraction pattern is:
  • I 0 ( 1 ⁇ ⁇ ⁇ z ) 2 ⁇ [ ( ⁇ ⁇ 2 ⁇ ⁇ ( n + ⁇ ⁇ ⁇ n ) ⁇ b ⁇ - ⁇ ⁇ 2 ⁇ ⁇ n ⁇ b ⁇ ) ⁇ a d + ⁇ ⁇ 2 ⁇ ⁇ n ⁇ b ⁇ ] 2 ( 5 )
  • I 1 ( 1 ⁇ ⁇ ⁇ z ) 2 ⁇ [ ( ⁇ ⁇ 2 ⁇ ⁇ ( n + ⁇ ⁇ ⁇ n ) ⁇ b ⁇ - ⁇ ⁇ 2 ⁇ ⁇ n ⁇ b ⁇ ) ⁇ a d ⁇ sin ⁇ ⁇ c ⁇ ( a d ) ] 2 ⁇ ⁇ and ( 6 )
  • I 2 ( 1 ⁇ ⁇ ⁇ z ) 2 ⁇ [ ( ⁇ ⁇ 2 ⁇ ⁇ ( n + ⁇ ⁇ ⁇ n ) ⁇ b ⁇ -
  • FIG. 3 shows the ratio of intensity of the 1 st and 2 nd diffraction order to 0 th order of the grating in PV2526-164 is 0.1374 and 0.0842 respectively, and the corresponding refractive index change determined by the analysis is about 0.06.
  • the average refractive index change in RD1817 and HEMA B was 0.05 ⁇ 0.0005 and 0.03 ⁇ 0.0005.
  • arrays of dots can be created by directing the laser beam at discrete points or spots within the material.
  • Such an array can be arranged substantially on one plane or several such arrays can be created at different depths within the material.
  • a material thus modified can be advantageously useful when light is not substantially scattered by the dots.

Landscapes

  • Health & Medical Sciences (AREA)
  • Ophthalmology & Optometry (AREA)
  • Engineering & Computer Science (AREA)
  • General Health & Medical Sciences (AREA)
  • Veterinary Medicine (AREA)
  • Heart & Thoracic Surgery (AREA)
  • Biomedical Technology (AREA)
  • Public Health (AREA)
  • Animal Behavior & Ethology (AREA)
  • Vascular Medicine (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Oral & Maxillofacial Surgery (AREA)
  • Cardiology (AREA)
  • Transplantation (AREA)
  • Optics & Photonics (AREA)
  • Nuclear Medicine, Radiotherapy & Molecular Imaging (AREA)
  • Surgery (AREA)
  • General Physics & Mathematics (AREA)
  • Manufacturing & Machinery (AREA)
  • Mechanical Engineering (AREA)
  • Prostheses (AREA)
  • Treatments Of Macromolecular Shaped Articles (AREA)
  • Materials For Medical Uses (AREA)
  • Glass Compositions (AREA)
US11/745,746 2006-06-28 2007-05-08 Optical Material and Method for Modifying the Refractive Index Abandoned US20080001320A1 (en)

Priority Applications (18)

Application Number Priority Date Filing Date Title
US11/745,746 US20080001320A1 (en) 2006-06-28 2007-05-08 Optical Material and Method for Modifying the Refractive Index
CA2655229A CA2655229C (en) 2006-06-28 2007-06-19 Optical material and method for modifying the refractive index
KR1020087031661A KR101372742B1 (ko) 2006-06-28 2007-06-19 광학 물질 및 굴절률 변경 방법
CN200780024664XA CN101489509B (zh) 2006-06-28 2007-06-19 用于改变光学材料和光学器件的折射率的方法
AT07798742T ATE475389T1 (de) 2006-06-28 2007-06-19 Optisches material und verfahren zur modifizierung des refraktionsindexes
JP2009518456A JP5385136B2 (ja) 2006-06-28 2007-06-19 光学材料および屈折率を修正する方法
PCT/US2007/071538 WO2008002796A2 (en) 2006-06-28 2007-06-19 Optical material and method for modifying the refractive index
DE602007008095T DE602007008095D1 (de) 2006-06-28 2007-06-19 Optisches material und verfahren zur modifizierung des refraktionsindexes
AU2007265218A AU2007265218B2 (en) 2006-06-28 2007-06-19 Optical material and method for modifying the refractive index
EP07798742A EP2032102B1 (en) 2006-06-28 2007-06-19 Optical material and method for modifying the refractive index
US11/948,298 US7789910B2 (en) 2006-06-28 2007-11-30 Optical material and method for modifying the refractive index
US13/686,952 US8932352B2 (en) 2006-06-28 2012-11-28 Optical material and method for modifying the refractive index
US13/782,257 US10543076B2 (en) 2006-06-28 2013-03-01 Optical material and method for modifying the refractive index
US14/564,207 US9622912B2 (en) 2006-06-28 2014-12-09 Method for modifying the refractive index of an optical material
US15/455,870 US10299909B2 (en) 2006-06-28 2017-03-10 Optical device and method for modifying the refractive index of an optical material
US15/923,443 US10806567B2 (en) 2006-06-28 2018-03-16 Optical material and method for modifying the refractive index
US16/388,992 US10893936B2 (en) 2006-06-28 2019-04-19 Optical device and method for modifying the refractive index of an optical material
US17/150,546 US20210128294A1 (en) 2006-06-28 2021-01-15 Optical Material and Method for Modifying the Refractive Index

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US81702706P 2006-06-28 2006-06-28
US11/745,746 US20080001320A1 (en) 2006-06-28 2007-05-08 Optical Material and Method for Modifying the Refractive Index

Related Child Applications (4)

Application Number Title Priority Date Filing Date
US11/948,298 Continuation-In-Part US7789910B2 (en) 2006-06-28 2007-11-30 Optical material and method for modifying the refractive index
US11/948,298 Continuation US7789910B2 (en) 2006-06-28 2007-11-30 Optical material and method for modifying the refractive index
US13/782,257 Division US10543076B2 (en) 2006-06-28 2013-03-01 Optical material and method for modifying the refractive index
US15/923,443 Continuation US10806567B2 (en) 2006-06-28 2018-03-16 Optical material and method for modifying the refractive index

Publications (1)

Publication Number Publication Date
US20080001320A1 true US20080001320A1 (en) 2008-01-03

Family

ID=38846404

Family Applications (3)

Application Number Title Priority Date Filing Date
US11/745,746 Abandoned US20080001320A1 (en) 2006-06-28 2007-05-08 Optical Material and Method for Modifying the Refractive Index
US13/782,257 Active 2031-09-06 US10543076B2 (en) 2006-06-28 2013-03-01 Optical material and method for modifying the refractive index
US15/923,443 Active US10806567B2 (en) 2006-06-28 2018-03-16 Optical material and method for modifying the refractive index

Family Applications After (2)

Application Number Title Priority Date Filing Date
US13/782,257 Active 2031-09-06 US10543076B2 (en) 2006-06-28 2013-03-01 Optical material and method for modifying the refractive index
US15/923,443 Active US10806567B2 (en) 2006-06-28 2018-03-16 Optical material and method for modifying the refractive index

Country Status (10)

Country Link
US (3) US20080001320A1 (zh)
EP (1) EP2032102B1 (zh)
JP (1) JP5385136B2 (zh)
KR (1) KR101372742B1 (zh)
CN (1) CN101489509B (zh)
AT (1) ATE475389T1 (zh)
AU (1) AU2007265218B2 (zh)
CA (1) CA2655229C (zh)
DE (1) DE602007008095D1 (zh)
WO (1) WO2008002796A2 (zh)

Cited By (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20080077121A1 (en) * 2006-09-07 2008-03-27 Sie Ag Surgical Instrument Engineering Ophthalmological apparatus for the refractive correction of an eye
US20090005764A1 (en) * 2007-06-26 2009-01-01 Knox Wayne H Method for Modifying the Refractive Index of Ocular Tissues
US20090118828A1 (en) * 2007-11-06 2009-05-07 Altmann Griffith E Light-adjustable multi-element ophthalmic lens
US20090143858A1 (en) * 2006-06-28 2009-06-04 Knox Wayne H Optical material and method for modifying the refractive index
US20090287306A1 (en) * 2008-05-19 2009-11-19 Thomas Smith Optical hydrogel material with photosensitizer and method for modifying the refractive index
US20100225014A1 (en) * 2009-03-04 2010-09-09 Aaren Scientific Inc. System for characterizing a cornea and obtaining an opthalmic lens
US20100228345A1 (en) * 2009-03-04 2010-09-09 Aaren Scientific Inc. System for forming and modifying lenses and lenses formed thereby
WO2010102155A1 (en) 2009-03-04 2010-09-10 Aaren Scientific Inc. System for forming and modifying lenses and lenses formed thereby
US20100298933A1 (en) * 2006-06-28 2010-11-25 Knox Wayne H Optical Material and Method for Modifying the Refractive Index
US20110071509A1 (en) * 2007-06-26 2011-03-24 University Of Rochester Method for modifying the refractive index of ocular tissues
WO2012166696A1 (en) 2011-06-02 2012-12-06 Bausch & Lomb Incorporated Method for modifying the refractive index of an optical material and resulting optical vision component
US20130178934A1 (en) * 2006-06-28 2013-07-11 Bausch & Lomb Incorporated Optical Material and Method for Modifying the Refractive Index
US9023257B2 (en) 2012-11-14 2015-05-05 Perfect Ip, Llc Hydrophilicity alteration system and method
US9545340B1 (en) * 2007-06-26 2017-01-17 University Of Rochester Multi-photon absorption for femtosecond micromachining and refractive index modification of tissues
WO2017106321A1 (en) 2015-12-15 2017-06-22 University Of Rochester Refractive corrector incorporating a continuous central phase zone and peripheral phase discontinuities
WO2017221068A1 (en) 2016-06-23 2017-12-28 Medicem Ophthalmic (Cy) Limited Light-adjustable hydrogel and bioanalogic intraocular lens
US9925621B2 (en) 2012-11-14 2018-03-27 Perfect Ip, Llp Intraocular lens (IOL) fabrication system and method
US10441676B2 (en) 2013-01-15 2019-10-15 Medicem Institute s.r.o. Light-adjustable hydrogel and bioanalogic intraocular lens
US10517761B2 (en) 2015-07-22 2019-12-31 Carl Zeiss Meditec Ag Postoperative modification of an intraocular lens
US10667903B2 (en) 2013-01-15 2020-06-02 Medicem Institute s.r.o. Bioanalogic intraocular lens
EP3667401A1 (en) * 2018-12-12 2020-06-17 Essilor International Method and device for manufacturing an ophthalmic lens
US10813791B2 (en) 2011-06-02 2020-10-27 University Of Rochester Method for modifying the refractive index of ocular tissues and applications thereof
EP3582720A4 (en) * 2017-02-16 2020-12-23 Perfect IP, LLC LENS INDIVIDUALIZATION SYSTEM AND METHOD
US10932901B2 (en) 2017-02-10 2021-03-02 University Of Rochester Vision correction with laser refractive index changes
WO2021108585A1 (en) 2019-11-25 2021-06-03 University Of Rochester Material and biological response of femtosecond photo-modification in hydrogel and cornea
US20210196520A1 (en) * 2018-05-14 2021-07-01 University Of Rochester Vision Correction With Laser Refractive Index Changes
WO2023107379A1 (en) 2021-12-06 2023-06-15 University Of Rochester Thin large-diameter optics foldable intraocular lens
US11693257B2 (en) 2019-07-19 2023-07-04 Clerio Vision, Inc. Myopia progression treatment
US11747650B2 (en) 2020-07-08 2023-09-05 Clerio Vision, Inc. Optimized multifocal wavefronts for presbyopia correction

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5550909B2 (ja) * 2006-11-10 2014-07-16 ラーセン， ラース マイケル 眼の非破壊的或いは低破壊的光操作のための方法及び装置
ES2537205T3 (es) * 2008-01-09 2015-06-03 Alcon Lensx, Inc. Fragmentación de tejido por láser fotodisruptor
DE102008005053A1 (de) * 2008-01-18 2009-07-30 Rowiak Gmbh Laserkorrektur von Sehfehlern an der natürlichen Augenlinse
US8020994B2 (en) * 2008-09-04 2011-09-20 Heidelberg Engineering Gmbh Custom phase plate
PL237446B1 (pl) * 2015-09-18 2021-04-19 Polskie Centrum Fotoniki I Swiatlowodow Urządzenie do pomiarów parametrów elementów fazowych i dyspersji światłowodów oraz sposób pomiaru parametrów elementu fazowego i dyspersji światłowodów
WO2017135035A1 (ja) * 2016-02-03 2017-08-10 株式会社ニデック 眼科用レーザ屈折矯正装置、眼科用フォトチューニング設定装置、眼科用フォトチューニングシステム、眼鏡用フォトチューニング設定装置、及びこれらに用いられるプログラム、眼科用レーザ手術装置
US20200025627A1 (en) * 2017-02-16 2020-01-23 Cornell University Multi-photon wavefront sensor, methods, and applications
CN107272195A (zh) * 2017-07-27 2017-10-20 英诺激光科技股份有限公司 一种利用激光校正光学系统波前分布的方法
DE102019211861A1 (de) * 2019-08-07 2021-02-11 Carl Zeiss Meditec Ag Planungsverfahren und Vorrichtungen zur präzisen Änderung eines Brechungsindex

Citations (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3896061A (en) * 1972-08-16 1975-07-22 Toray Industries Semi-permeable membranes, their preparation and their use
US3948248A (en) * 1974-09-05 1976-04-06 Zuckerman Joel L Method of measuring ocular pulse
US4731079A (en) * 1986-11-26 1988-03-15 Kingston Technologies, Inc. Intraocular lenses
US4907586A (en) * 1988-03-31 1990-03-13 Intelligent Surgical Lasers Method for reshaping the eye
US5104957A (en) * 1990-02-28 1992-04-14 Autogenesis Technologies, Inc. Biologically compatible collagenous reaction product and articles useful as medical implants produced therefrom
US5220359A (en) * 1990-07-24 1993-06-15 Johnson & Johnson Vision Products, Inc. Lens design method and resulting aspheric lens
US5964748A (en) * 1995-10-20 1999-10-12 Peyman; Gholam A. Intrastromal corneal modification
US6197057B1 (en) * 1998-10-27 2001-03-06 Gholam A. Peyman Lens conversion system for teledioptic or difractive configurations
US20020100990A1 (en) * 2000-09-26 2002-08-01 Platt Ben C. Delivery system for post-operative power adjustment of adjustable lens
US6450642B1 (en) * 1999-01-12 2002-09-17 California Institute Of Technology Lenses capable of post-fabrication power modification
US6489589B1 (en) * 1994-02-07 2002-12-03 Board Of Regents, University Of Nebraska-Lincoln Femtosecond laser utilization methods and apparatus and method for producing nanoparticles
US20040015236A1 (en) * 1991-11-18 2004-01-22 Sarfarazi Faezeh M. Sarfarazi elliptical accommodative intraocular lens for small incision surgery
US20040243111A1 (en) * 2003-06-02 2004-12-02 Mark Bendett Method and apparatus for precision working of material
US20050018130A1 (en) * 2002-09-06 2005-01-27 Ali Dahi Hybrid contact lens system and method
US6857744B2 (en) * 2001-09-17 2005-02-22 Menicon Co., Ltd. Method of marking ophhalmic lens by using laser radiation of femtosecond pulse width
US20050187622A1 (en) * 1999-01-12 2005-08-25 Calhoun Vision Light adjustable multifocal lenses
US20060017990A1 (en) * 2000-10-11 2006-01-26 Calhoun Vision, Inc. Light adjustable aberration conjugator
US20060106126A1 (en) * 2001-12-28 2006-05-18 Calhoun Vision, Inc Light adjustable lenses capable of post-fabrication power modification via multi-photon processes
US20060135952A1 (en) * 2004-12-21 2006-06-22 Curatu Eugene O Corrective intraocular lens and associated methods
US7074840B2 (en) * 2002-12-19 2006-07-11 Calhoun Vision Light adjustable lenses capable of post-fabrication power modification via multi-photon processes
US7085469B2 (en) * 2002-11-25 2006-08-01 Nitto Denko Corporation Process for producing three-dimensional polyimide optical waveguide
US20090143858A1 (en) * 2006-06-28 2009-06-04 Knox Wayne H Optical material and method for modifying the refractive index
US20090287306A1 (en) * 2008-05-19 2009-11-19 Thomas Smith Optical hydrogel material with photosensitizer and method for modifying the refractive index

Family Cites Families (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4669466A (en) * 1985-01-16 1987-06-02 Lri L.P. Method and apparatus for analysis and correction of abnormal refractive errors of the eye
JPS62175418U (zh) * 1986-04-23 1987-11-07
US4871785A (en) * 1986-08-13 1989-10-03 Michael Froix Clouding-resistant contact lens compositions
CA2032581C (en) * 1989-12-20 2002-03-12 Karel Ulbrich Hydrolytically degradable hydrophilic gels and the method for preparation thereof
US5050981A (en) * 1990-07-24 1991-09-24 Johnson & Johnson Vision Products, Inc. Lens design method and resulting aspheric lens
EP0575885B1 (en) * 1992-06-17 1998-02-04 Nitto Denko Corporation Process for producing polymerization or crosslinking rate-distributed article and process for producing lens, lens array or waveguide using the process
US5849006A (en) 1994-04-25 1998-12-15 Autonomous Technologies Corporation Laser sculpting method and system
US5526171A (en) * 1995-01-18 1996-06-11 The Trustees Of Princeton University Laser pulse shaper
US5824719A (en) * 1995-06-07 1998-10-20 Bausch & Lomb Incorporated Polymer compositions for contact lenses
US6271914B1 (en) 1996-11-25 2001-08-07 Autonomous Technologies Corporation Objective measurement and correction of optical systems using wavefront analysis
DE69902549T2 (de) 1998-08-19 2003-04-17 Alcon, Inc. Gerät und verfahren zur messung von fehlsichtigkeiten eines menschlichen auges
JP4326646B2 (ja) 1999-11-22 2009-09-09 株式会社トリケミカル研究所 光学素子及びその製造方法
EP2042125A3 (en) 2000-03-20 2009-04-15 California Institute of Technology Application of wavefront sensor to lenses capable of post-fabrication power modification
JP4565754B2 (ja) * 2001-02-26 2010-10-20 日東電工株式会社 プラスチック構造体
ATE339930T1 (de) * 2001-03-16 2006-10-15 Novartis Pharma Gmbh Verfahren zum giessformen von opthalmischen linsen
JP4069358B2 (ja) * 2001-04-26 2008-04-02 三菱瓦斯化学株式会社 第３級水酸基を有するビニル重合性モノマー
US20050182489A1 (en) 2001-04-27 2005-08-18 Peyman Gholam A. Intraocular lens adapted for adjustment via laser after implantation
SE0102543D0 (sv) * 2001-07-16 2001-07-16 Pharmacia Groningen Bv Compositions capable of forming hydrogels in the eye
JP2003075876A (ja) * 2001-08-30 2003-03-12 Nidek Co Ltd 角膜手術装置
US20030208189A1 (en) * 2001-10-19 2003-11-06 Payman Gholam A. Integrated system for correction of vision of the human eye
US6730767B2 (en) 2001-11-02 2004-05-04 Bausch & Lomb Incorporated High refractive index aromatic-based siloxane monofunctional macromonomers
US7241009B2 (en) 2001-11-21 2007-07-10 Calhoun Vision, Inc. Crosslinking of silicones presence of functionalized silicones
JP2003185820A (ja) * 2001-12-21 2003-07-03 Jsr Corp 感放射線性屈折率変化性組成物および屈折率変化法
US6851804B2 (en) * 2001-12-28 2005-02-08 Jagdish M. Jethmalani Readjustable optical elements
US6846892B2 (en) * 2002-03-11 2005-01-25 Johnson & Johnson Vision Care, Inc. Low polydispersity poly-HEMA compositions
JP3953891B2 (ja) * 2002-06-05 2007-08-08 日東電工株式会社 プラスチック構造体の製造方法および該製造方法により作製されたプラスチック構造体
US7381221B2 (en) * 2002-11-08 2008-06-03 Advanced Medical Optics, Inc. Multi-zonal monofocal intraocular lens for correcting optical aberrations
JP4172355B2 (ja) 2003-07-30 2008-10-29 ミツミ電機株式会社 電圧生成回路
US7033391B2 (en) 2003-09-08 2006-04-25 Bausch & Lomb Incorporated High refractive index silicone-containing prepolymers with blue light absorption capability
JP2005141083A (ja) * 2003-11-07 2005-06-02 National Institute Of Advanced Industrial & Technology 光部品用材料およびその製造方法、並びに光部品
JP4869734B2 (ja) * 2005-04-25 2012-02-08 オリンパス株式会社 多光子励起走査型レーザ顕微鏡
US7857848B2 (en) * 2005-05-05 2010-12-28 Key Medical Technologies, Inc. Infinite refractive index gradient (IRIG) polymers for ocular implant and contact lens applications
DE102005032041A1 (de) * 2005-07-08 2007-01-18 Carl Zeiss Meditec Ag Vorrichtung und Verfahren zum Ändern einer optischen und/oder mechanischen Eigenschaft einer in ein Auge implantierten Linse
JP2009537870A (ja) 2006-05-18 2009-10-29 スリーエム イノベイティブ プロパティズ カンパニー 抽出構造体を備えた導光体の製造方法及びその方法で製造された導光体
US20080001320A1 (en) 2006-06-28 2008-01-03 Knox Wayne H Optical Material and Method for Modifying the Refractive Index
WO2009070438A1 (en) * 2007-11-30 2009-06-04 Bausch & Lomb Incorporated Optical material and method for modifying the refractive index
US20090287305A1 (en) 2008-05-19 2009-11-19 Amalaha Leonard D Wholly implantable non-natural heart for humans
US9023257B2 (en) * 2012-11-14 2015-05-05 Perfect Ip, Llc Hydrophilicity alteration system and method

Patent Citations (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3896061A (en) * 1972-08-16 1975-07-22 Toray Industries Semi-permeable membranes, their preparation and their use
US3948248A (en) * 1974-09-05 1976-04-06 Zuckerman Joel L Method of measuring ocular pulse
US4731079A (en) * 1986-11-26 1988-03-15 Kingston Technologies, Inc. Intraocular lenses
US4907586A (en) * 1988-03-31 1990-03-13 Intelligent Surgical Lasers Method for reshaping the eye
US5104957A (en) * 1990-02-28 1992-04-14 Autogenesis Technologies, Inc. Biologically compatible collagenous reaction product and articles useful as medical implants produced therefrom
US5220359A (en) * 1990-07-24 1993-06-15 Johnson & Johnson Vision Products, Inc. Lens design method and resulting aspheric lens
US20040015236A1 (en) * 1991-11-18 2004-01-22 Sarfarazi Faezeh M. Sarfarazi elliptical accommodative intraocular lens for small incision surgery
US6489589B1 (en) * 1994-02-07 2002-12-03 Board Of Regents, University Of Nebraska-Lincoln Femtosecond laser utilization methods and apparatus and method for producing nanoparticles
US5964748A (en) * 1995-10-20 1999-10-12 Peyman; Gholam A. Intrastromal corneal modification
US6197057B1 (en) * 1998-10-27 2001-03-06 Gholam A. Peyman Lens conversion system for teledioptic or difractive configurations
US6813097B2 (en) * 1999-01-12 2004-11-02 California Institute Of Technology Lenses capable of post-fabrication modulus change
US6450642B1 (en) * 1999-01-12 2002-09-17 California Institute Of Technology Lenses capable of post-fabrication power modification
US20050187622A1 (en) * 1999-01-12 2005-08-25 Calhoun Vision Light adjustable multifocal lenses
US20020100990A1 (en) * 2000-09-26 2002-08-01 Platt Ben C. Delivery system for post-operative power adjustment of adjustable lens
US7105110B2 (en) * 2000-09-26 2006-09-12 Calhoun Vision, Inc. Delivery system for post-operative power adjustment of adjustable lens
US20050192563A1 (en) * 2000-09-26 2005-09-01 Calhoun Vision, Inc. Delivery system for post-operative power adjustment of adjustable lens
US20060017990A1 (en) * 2000-10-11 2006-01-26 Calhoun Vision, Inc. Light adjustable aberration conjugator
US6857744B2 (en) * 2001-09-17 2005-02-22 Menicon Co., Ltd. Method of marking ophhalmic lens by using laser radiation of femtosecond pulse width
US20060106126A1 (en) * 2001-12-28 2006-05-18 Calhoun Vision, Inc Light adjustable lenses capable of post-fabrication power modification via multi-photon processes
US20050018130A1 (en) * 2002-09-06 2005-01-27 Ali Dahi Hybrid contact lens system and method
US7085469B2 (en) * 2002-11-25 2006-08-01 Nitto Denko Corporation Process for producing three-dimensional polyimide optical waveguide
US7074840B2 (en) * 2002-12-19 2006-07-11 Calhoun Vision Light adjustable lenses capable of post-fabrication power modification via multi-photon processes
US20040243111A1 (en) * 2003-06-02 2004-12-02 Mark Bendett Method and apparatus for precision working of material
US20060135952A1 (en) * 2004-12-21 2006-06-22 Curatu Eugene O Corrective intraocular lens and associated methods
US20090143858A1 (en) * 2006-06-28 2009-06-04 Knox Wayne H Optical material and method for modifying the refractive index
US20090287306A1 (en) * 2008-05-19 2009-11-19 Thomas Smith Optical hydrogel material with photosensitizer and method for modifying the refractive index

Non-Patent Citations (5)

* Cited by examiner, † Cited by third party
Title
Ding et al "Characterization of index changes in silicone- and nonsilicone-based hydrogel polymers induced by femtosecond micro machining; CLEO 2007 May 6, 2007 2 pages *
Ding et al "Intrastromal refractive index change induced in cat corneas by femtosecond laser micromachining", Opt. Soc. Am., Frontiers in Optics, San Jose, California, USA, Sept. 16-2007 *
Ding et al "Large Refractive index change in silicone-based hydrogels"; Optics Express; Vol. 14, No. 24; 11-27-2006; pp 11901-11909 *
Ding et al, "Large enhancement of femtosecond laser micromachining speed of doped hydrogels", Optics Express, Vol. 16, pp 21914-21921, Dec. 27, 2008 *
Sowa et al; "Symmetric waveguide in poly(methyl methacrylate) fabricated by femtosecond laser pulses"; Oics Express; Vol. 14, No. 1; pp 291-297; January 9, 2006 *

Cited By (78)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20150126979A1 (en) * 2006-06-28 2015-05-07 University Of Rochester Method for Modifying the Refractive Index of an Optical Material
US8932352B2 (en) 2006-06-28 2015-01-13 University Of Rochester Optical material and method for modifying the refractive index
US9622912B2 (en) * 2006-06-28 2017-04-18 University Of Rochester Method for modifying the refractive index of an optical material
US20130178934A1 (en) * 2006-06-28 2013-07-11 Bausch & Lomb Incorporated Optical Material and Method for Modifying the Refractive Index
US8337553B2 (en) 2006-06-28 2012-12-25 Bausch & Lomb Incorporated Optical material and method for modifying the refractive index
US7789910B2 (en) * 2006-06-28 2010-09-07 Bausch & Lomb Incorporated Optical material and method for modifying the refractive index
US20090143858A1 (en) * 2006-06-28 2009-06-04 Knox Wayne H Optical material and method for modifying the refractive index
US10543076B2 (en) * 2006-06-28 2020-01-28 University Of Rochester Optical material and method for modifying the refractive index
US20100298933A1 (en) * 2006-06-28 2010-11-25 Knox Wayne H Optical Material and Method for Modifying the Refractive Index
US20080077121A1 (en) * 2006-09-07 2008-03-27 Sie Ag Surgical Instrument Engineering Ophthalmological apparatus for the refractive correction of an eye
US10548770B2 (en) * 2006-09-07 2020-02-04 Sie Ag Surgical Instrument Engineering Ophthalmological apparatus for the refractive correction of an eye
US20110071509A1 (en) * 2007-06-26 2011-03-24 University Of Rochester Method for modifying the refractive index of ocular tissues
US8486055B2 (en) 2007-06-26 2013-07-16 Bausch & Lomb Incorporated Method for modifying the refractive index of ocular tissues
US20130226162A1 (en) * 2007-06-26 2013-08-29 University Of Rochester Method for Modifying the Refractive Index of Ocular Tissues
US8617147B2 (en) * 2007-06-26 2013-12-31 University Of Rochester Method for modifying the refractive index of ocular tissues
US20090005764A1 (en) * 2007-06-26 2009-01-01 Knox Wayne H Method for Modifying the Refractive Index of Ocular Tissues
US9545340B1 (en) * 2007-06-26 2017-01-17 University Of Rochester Multi-photon absorption for femtosecond micromachining and refractive index modification of tissues
US20090118828A1 (en) * 2007-11-06 2009-05-07 Altmann Griffith E Light-adjustable multi-element ophthalmic lens
KR20110020231A (ko) * 2008-05-19 2011-03-02 보오슈 앤드 롬 인코포레이팃드 감광제를 갖는 안내 렌즈 및 안내 렌즈의 굴절률 개질 방법
JP2011520561A (ja) * 2008-05-19 2011-07-21 ボーシュ アンド ローム インコーポレイティド 光増感剤を含む眼内レンズ及びそのレンズの屈折率の変更方法
US8901190B2 (en) * 2008-05-19 2014-12-02 University Of Rochester Optical hydrogel material with photosensitizer and method for modifying the refractive index
KR101761079B1 (ko) * 2008-05-19 2017-07-24 유니버시티 오브 로체스터 감광제를 갖는 안내 렌즈 및 안내 렌즈의 굴절률 개질 방법
US20090287306A1 (en) * 2008-05-19 2009-11-19 Thomas Smith Optical hydrogel material with photosensitizer and method for modifying the refractive index
KR101636588B1 (ko) * 2008-05-19 2016-07-05 로체스터 인스티튜트 오브 테크놀로지 감광제를 갖는 안내 렌즈 및 안내 렌즈의 굴절률 개질 방법
US20130268072A1 (en) * 2008-05-19 2013-10-10 Bausch & Lomb Incorporated Optical Hydrogel Material with Photosensitizer and Method for Modifying the Refractive Index
US9060847B2 (en) * 2008-05-19 2015-06-23 University Of Rochester Optical hydrogel material with photosensitizer and method for modifying the refractive index
CN105105869A (zh) * 2009-03-04 2015-12-02 完美Ip有限公司 用于形成和修改晶状体的方法
US8152302B2 (en) 2009-03-04 2012-04-10 Aaren Scientific, Inc. System for characterizing a cornea and obtaining an ophthalmic lens
US20100225014A1 (en) * 2009-03-04 2010-09-09 Aaren Scientific Inc. System for characterizing a cornea and obtaining an opthalmic lens
US8646916B2 (en) 2009-03-04 2014-02-11 Perfect Ip, Llc System for characterizing a cornea and obtaining an opthalmic lens
US8292952B2 (en) 2009-03-04 2012-10-23 Aaren Scientific Inc. System for forming and modifying lenses and lenses formed thereby
CN102438549A (zh) * 2009-03-04 2012-05-02 安伦科技股份有限公司 用于形成和修改晶状体的系统以及由此形成的晶状体
US20150076723A1 (en) * 2009-03-04 2015-03-19 Perfect Ip, Llc System for forming and modifying lenses and lenses formed thereby
US20150112203A1 (en) * 2009-03-04 2015-04-23 Perfect Ip, Llc Method for characterizing a cornea and obtaining an ophthalmic lens
US20100228345A1 (en) * 2009-03-04 2010-09-09 Aaren Scientific Inc. System for forming and modifying lenses and lenses formed thereby
US20110130677A1 (en) * 2009-03-04 2011-06-02 Bille Josef F System for characterizing a conrea and obtaining an ophthalmic lens
US20110210459A1 (en) * 2009-03-04 2011-09-01 Bille Josef F System for forming and modifying lenses and lenses formed thereby
US8568627B2 (en) * 2009-03-04 2013-10-29 Perfect Ip, Llc Method for forming and modifying lenses
US9192292B2 (en) * 2009-03-04 2015-11-24 Perfect Ip, Llc System for forming and modifying lenses and lenses formed thereby
US20110212205A1 (en) * 2009-03-04 2011-09-01 Bille Josef F System for forming and modifying lenses and lenses formed thereby
CN105105918A (zh) * 2009-03-04 2015-12-02 完美Ip有限公司 用于形成和修改晶状体的系统以及由此形成的晶状体
US20110128501A1 (en) * 2009-03-04 2011-06-02 Bille Josef F System for characterizing a cornea and obtaining an ophthalmic lens
WO2010102155A1 (en) 2009-03-04 2010-09-10 Aaren Scientific Inc. System for forming and modifying lenses and lenses formed thereby
US20110128500A1 (en) * 2009-03-04 2011-06-02 Bille Josef F System for characterizing a cornea and obtaining an ophthalmic lens
US11690759B2 (en) 2011-06-02 2023-07-04 University Of Rochester Method for modifying the refractive index of ocular tissues and applications thereof
US12076278B2 (en) 2011-06-02 2024-09-03 University Of Rochester Method for modifying the refractive index of ocular tissues and applications thereof
US10813791B2 (en) 2011-06-02 2020-10-27 University Of Rochester Method for modifying the refractive index of ocular tissues and applications thereof
US9939558B2 (en) 2011-06-02 2018-04-10 University Of Rochester Method for modifying the refractive index of an optical material and resulting optical vision component
US9144491B2 (en) 2011-06-02 2015-09-29 University Of Rochester Method for modifying the refractive index of an optical material
WO2012166696A1 (en) 2011-06-02 2012-12-06 Bausch & Lomb Incorporated Method for modifying the refractive index of an optical material and resulting optical vision component
US10649115B2 (en) 2011-06-02 2020-05-12 University Of Rochester Method for modifying the refractive index of an optical material and resulting optical vision component
EP3040051A1 (en) 2012-11-14 2016-07-06 Perfect IP, LLC Hydrophilicity alteration method
EP3040052A1 (en) 2012-11-14 2016-07-06 Perfect IP, LLC An optical lens
US9925621B2 (en) 2012-11-14 2018-03-27 Perfect Ip, Llp Intraocular lens (IOL) fabrication system and method
US11090151B2 (en) 2012-11-14 2021-08-17 Perfect Ip, Llc Hydrophilicity alteration system and method
US9023257B2 (en) 2012-11-14 2015-05-05 Perfect Ip, Llc Hydrophilicity alteration system and method
US10441676B2 (en) 2013-01-15 2019-10-15 Medicem Institute s.r.o. Light-adjustable hydrogel and bioanalogic intraocular lens
US11793908B2 (en) 2013-01-15 2023-10-24 Medicem Institute s.r.o Light-adjustable hydrogel and bioanalogic intraocular lens
US10667903B2 (en) 2013-01-15 2020-06-02 Medicem Institute s.r.o. Bioanalogic intraocular lens
US10517761B2 (en) 2015-07-22 2019-12-31 Carl Zeiss Meditec Ag Postoperative modification of an intraocular lens
US20210063769A1 (en) * 2015-12-15 2021-03-04 University Of Rochester Refractive corrector incorporating a continuous central phase zone and peripheral phase discontinuities
WO2017106321A1 (en) 2015-12-15 2017-06-22 University Of Rochester Refractive corrector incorporating a continuous central phase zone and peripheral phase discontinuities
WO2017221068A1 (en) 2016-06-23 2017-12-28 Medicem Ophthalmic (Cy) Limited Light-adjustable hydrogel and bioanalogic intraocular lens
US12090043B2 (en) 2017-02-10 2024-09-17 University Of Rochester Vision correction with laser refractive index changes
US11896478B2 (en) 2017-02-10 2024-02-13 University Of Rochester Vision correction with laser refractive index changes
US10932901B2 (en) 2017-02-10 2021-03-02 University Of Rochester Vision correction with laser refractive index changes
EP3582720A4 (en) * 2017-02-16 2020-12-23 Perfect IP, LLC LENS INDIVIDUALIZATION SYSTEM AND METHOD
US20210196520A1 (en) * 2018-05-14 2021-07-01 University Of Rochester Vision Correction With Laser Refractive Index Changes
CN113164247A (zh) * 2018-05-14 2021-07-23 罗切斯特大学 采用激光折射率改变的视力矫正
US11369515B2 (en) * 2018-05-14 2022-06-28 University Of Rochester Vision correction with laser refractive index changes
US11833081B2 (en) * 2018-05-14 2023-12-05 University Of Rochester Vision correction with laser refractive index changes
WO2020120687A1 (en) * 2018-12-12 2020-06-18 Essilor International Method and device for manufacturing an ophthalmic lens
CN113196145A (zh) * 2018-12-12 2021-07-30 依视路国际公司 用于制造眼科镜片的方法和装置
EP3667401A1 (en) * 2018-12-12 2020-06-17 Essilor International Method and device for manufacturing an ophthalmic lens
US11693257B2 (en) 2019-07-19 2023-07-04 Clerio Vision, Inc. Myopia progression treatment
WO2021108585A1 (en) 2019-11-25 2021-06-03 University Of Rochester Material and biological response of femtosecond photo-modification in hydrogel and cornea
US11747650B2 (en) 2020-07-08 2023-09-05 Clerio Vision, Inc. Optimized multifocal wavefronts for presbyopia correction
WO2023107379A1 (en) 2021-12-06 2023-06-15 University Of Rochester Thin large-diameter optics foldable intraocular lens

Also Published As

Publication number Publication date
US10543076B2 (en) 2020-01-28
CN101489509B (zh) 2013-03-13
JP2009542361A (ja) 2009-12-03
EP2032102A2 (en) 2009-03-11
AU2007265218B2 (en) 2012-09-20
CN101489509A (zh) 2009-07-22
JP5385136B2 (ja) 2014-01-08
US20180206979A1 (en) 2018-07-26
CA2655229C (en) 2012-10-09
WO2008002796A8 (en) 2008-04-03
KR101372742B1 (ko) 2014-03-10
US10806567B2 (en) 2020-10-20
US20130178934A1 (en) 2013-07-11
CA2655229A1 (en) 2008-01-03
KR20090024197A (ko) 2009-03-06
DE602007008095D1 (de) 2010-09-09
WO2008002796A3 (en) 2008-07-24
WO2008002796A2 (en) 2008-01-03
ATE475389T1 (de) 2010-08-15
AU2007265218A1 (en) 2008-01-03
EP2032102B1 (en) 2010-07-28

Similar Documents

Publication Publication Date Title
US10893936B2 (en) Optical device and method for modifying the refractive index of an optical material
US10806567B2 (en) Optical material and method for modifying the refractive index
US7789910B2 (en) Optical material and method for modifying the refractive index
US10649115B2 (en) Method for modifying the refractive index of an optical material and resulting optical vision component
US9060847B2 (en) Optical hydrogel material with photosensitizer and method for modifying the refractive index

Legal Events

Date Code Title Description
AS Assignment

Owner name: UNIVERSITY OF ROCHESTER, NEW YORK

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KNOX, WAYNE;DING, LI;REEL/FRAME:019814/0706;SIGNING DATES FROM 20070621 TO 20070709

Owner name: BAUSCH & LOMB INCORPORATED, NEW YORK

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KUNZLER, JAY FRIEDRICH;JANI, DHARMENDRA M.;REEL/FRAME:019814/0737

Effective date: 20070430

Owner name: UNIVERSITY OF ROCHESTER, NEW YORK

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KNOX, WAYNE;DING, LI;SIGNING DATES FROM 20070621 TO 20070709;REEL/FRAME:019814/0706

AS Assignment

Owner name: CREDIT SUISSE, NEW YORK

Free format text: SECURITY AGREEMENT;ASSIGNORS:BAUSCH & LOMB INCORPORATED;B&L CRL INC.;B&L CRL PARTNERS L.P.;AND OTHERS;REEL/FRAME:020122/0722

Effective date: 20071026

Owner name: CREDIT SUISSE,NEW YORK

Free format text: SECURITY AGREEMENT;ASSIGNORS:BAUSCH & LOMB INCORPORATED;B&L CRL INC.;B&L CRL PARTNERS L.P.;AND OTHERS;REEL/FRAME:020122/0722

Effective date: 20071026

AS Assignment

Owner name: BAUSCH & LOMB INCORPORATED, NEW YORK

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH;REEL/FRAME:028726/0142

Effective date: 20120518

AS Assignment

Owner name: CITIBANK N.A., AS ADMINISTRATIVE AGENT, DELAWARE

Free format text: SECURITY AGREEMENT;ASSIGNORS:BAUSCH & LOMB INCORPORATED;EYEONICS, INC.;REEL/FRAME:028728/0645

Effective date: 20120518

AS Assignment

Owner name: WP PRISM INC. (N/K/A BAUSCH & LOMB HOLDINGS INC.), NEW YORK

Free format text: RELEASE OF SECURITY INTEREST;ASSIGNOR:CITIBANK N.A., AS ADMINISTRATIVE AGENT;REEL/FRAME:030995/0444

Effective date: 20130805

Owner name: ISTA PHARMACEUTICALS, NEW YORK

Free format text: RELEASE OF SECURITY INTEREST;ASSIGNOR:CITIBANK N.A., AS ADMINISTRATIVE AGENT;REEL/FRAME:030995/0444

Effective date: 20130805

Owner name: WP PRISM INC. (N/K/A BAUSCH & LOMB HOLDINGS INC.),

Free format text: RELEASE OF SECURITY INTEREST;ASSIGNOR:CITIBANK N.A., AS ADMINISTRATIVE AGENT;REEL/FRAME:030995/0444

Effective date: 20130805

Owner name: BAUSCH & LOMB INCORPORATED, NEW YORK

Free format text: RELEASE OF SECURITY INTEREST;ASSIGNOR:CITIBANK N.A., AS ADMINISTRATIVE AGENT;REEL/FRAME:030995/0444

Effective date: 20130805

AS Assignment

Owner name: GOLDMAN SACHS LENDING PARTNERS LLC, AS COLLATERAL AGENT, NEW YORK

Free format text: SECURITY AGREEMENT;ASSIGNOR:BAUSCH & LOMB INCORPORATED;REEL/FRAME:031156/0508

Effective date: 20130830

Owner name: GOLDMAN SACHS LENDING PARTNERS LLC, AS COLLATERAL

Free format text: SECURITY AGREEMENT;ASSIGNOR:BAUSCH & LOMB INCORPORATED;REEL/FRAME:031156/0508

Effective date: 20130830

AS Assignment

Owner name: UNIVERSITY OF ROCHESTER, NEW YORK

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:BAUSCH & LOMB INCORPORATED;REEL/FRAME:033538/0812

Effective date: 20131231

AS Assignment

Owner name: BARCLAYS BANK PLC, AS SUCCESSOR AGENT, NEW YORK

Free format text: NOTICE OF SUCCESSION OF AGENCY;ASSIGNOR:GOLDMAN SACHS LENDING PARTNERS, LLC;REEL/FRAME:034749/0689

Effective date: 20150108

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION

AS Assignment

Owner name: BAUSCH & LOMB INCORPORATED, NEW JERSEY

Free format text: RELEASE OF SECURITY INTEREST IN SPECIFIED PATENTS;ASSIGNOR:BARCLAYS BANK PLC, AS COLLATERAL AGENT;REEL/FRAME:048259/0134

Effective date: 20190204