US20070020138A1 - Silver alloy excellent inreflectance maintenance property - Google Patents
Silver alloy excellent inreflectance maintenance property Download PDFInfo
- Publication number
- US20070020138A1 US20070020138A1 US10/575,332 US57533206A US2007020138A1 US 20070020138 A1 US20070020138 A1 US 20070020138A1 US 57533206 A US57533206 A US 57533206A US 2007020138 A1 US2007020138 A1 US 2007020138A1
- Authority
- US
- United States
- Prior art keywords
- silver alloy
- dopant element
- silver
- optical recording
- recording medium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The present invention is a silver alloy including silver as the main component and at least one element as a first dopant element higher than silver in melting point, and excellent in reflectance maintenance property. In the present invention, the first dopant element is preferably copper, manganese, silicon, nickel, cobalt, yttrium, iron, scandium, zirconium, niobium, molybdenum, tantalum and tungsten. Also, in the present invention, the silver alloy preferably includes, as a second dopant element, at least one element selected from platinum, gold, rhodium, iridium, ruthenium, palladium, chromium, germanium, indium, tin, lead, aluminum, calcium, gallium, bismuth, antimony, strontium, hafnium, gadolinium, samarium, neodymium, lanthanum, cerium, ytterbium and europium.
Description
- The present invention relates to a silver alloy suitable as a material for forming reflective films provided on optical recording media, displays and the likes. Particularly, the present invention relates to a silver alloy for reflective films capable of maintaining the reflectance thereof even in long-term use.
- Silver is recognized as a most preferable material as a material for reflective films to be used in optical recording media, displays and the like. This is because silver is high in reflectance, and additionally, lower in price than gold that is also high in reflectance. In the field of optical recording media in these years, transition to recordable/rewritable media (CD-R/RW, DVD-R/RW/RAM) takes place, and expanding importance of optical recording media attaches importance to silver that is high in reflectance and relatively low in cost as a central material for use in reflective films.
- On the other hand, silver involves a problem such that silver is poor in corrosion resistance and is degraded in reflectance by discoloration to black through corrosion. The root causes for the corrosion of reflective films may vary with products (recording media, displays and the like) to which the reflective films are applied, in such a way that, for example, reflective films of displays suffer from a fear that they are corroded due to the atmospheric humidity or the like.
- A reflective layer of an optical recording medium also suffers from a fear of corrosion due to the atmosphere such as the air, -and furthermore, requires a consideration of corrosion caused by the effects of the other constituent layers (the recording layer, dielectric layer and the like) in contact with the reflective layer in the recording medium. For example, a recordable optical disk (CD-R, DVD-R, DVD+R or the like) has a structure in which an organic azo or cyanine dye ink is coated on a polycarbonate substrate and dried to form a recording layer, a reflective layer is formed on the surface of the recording layer, and the recording layer with the reflective layer is bonded to another polycarbonate substrate with an ultraviolet cure adhesive. In this case, the organic dye ink in the recording layer and the ultraviolet cure adhesive, both in contact with the reflective layer, contain sulfur as a component thereof or as an impurity, and accordingly, the reflective layer is exposed to a fear of corrosion in the course of use thereof because silver is poor in resistance to sulfidation. On the other hand, a rewritable optical disk (CD-RW, DVD-RW, DVD+RW, DVD-RAM or the like) has a structure in which a derivative layer, a recording layer, a dielectric layer and a reflective layer are laminated in such a condition that the reflective layer is in contact with the dielectric layer. Various materials are available for the dielectric layer, but in these years, materials to which zinc sulfide (ZnS) is applied are being used (sometimes, for the purpose of controlling heat reserve, a material made of zinc sulfide doped with silicon oxide, namely, ZnS−20 mol % SiO2 or the like being applied). Consequently, also in this case, there is a fear of corrosion due to a sulfide. As described above, the reflective layer of an optical recording medium is in such an environment that the reflective layer is in contact with a layer containing sulfur or a sulfide, irrespective as to whether the optical recording medium is recordable or rewritable in type; thus, the resistance to sulfidation comes to be more significant than the corrosion caused by the atmosphere involving humidity or the like, and there is a fear that the reflectance of the reflective layer is degraded by the long-term use of the recording medium.
- Additionally, there is a problem that a reflective film made of silver is also thermally degraded in reflectance. The mechanism involved in the reflectance degradation due to heating is not yet elucidated, but it has been verified that heating of a thin silver film causes a phenomenon in which local agglomeration occurs in the thin film so as to expose the underlayer. Accordingly, the reflective film of an optical recording medium, a plasma display or the like is required to have a heat resistance because it possibly undergoes heating.
- For the purpose of coping with the reflectance degradation of the reflective film as described above, there have conventionally been developed silver alloys, for use in reflective films, that are improved in corrosion resistance and heat resistance while the reflectance being secured. These alloys mostly include silver as the main component, and are doped with one or more of various elements as dopant elements; examples of such disclosed alloys include, for example, an alloy in which silver is doped with 0.5 to 10 atomic % of ruthenium and 0.1 to 10 atomic % of aluminum, and another alloy in which silver is doped with 0.5 to 4.9 atomic % of palladium. It has been disclosed that these silver alloys are satisfactory in corrosion resistance, can maintain the reflectance in service environment, and consequently, suitable for reflective films (for the details of the conventional art, see
Patent Documents 1 and 2). - Patent Document 1: Japanese Patent Laid-Open No. Hei 11-134715
- Patent Document 2: Japanese Patent Laid-Open No. 2000-109943
- As for the above described silver alloys, improvements of the corrosion resistance and heat resistance have been developed to some extents. However, even these silver alloys are not absolutely free from deterioration in service environment. Additionally, the reflectance is not completely guaranteed against reflectance degradation, and materials that can maintain the reflectance at a higher level are desired.
- In the field of optical recording devices, at present, red semiconductor lasers (wavelength: 650 nm) are applied as recording light sources, but blue lasers (wavelength: 405 nm) have almost seen their way clear to practical use. Application of the blue laser can ensure a
memory capacity 5 to 6 times as large as the memory capacity of an optical recording device available at present, so that optical recording devices incorporating blue lasers applied thereto will conceivably form the mainstream of the next-generation optical recording devices. In this connection, according to the present inventors, it has been verified that the reflectance of a reflective film varies with the wavelength of the incident laser light; in particular, it has been verified that shorter-wavelength laser irradiation degrades the reflectance irrespective as to whether corrosion occurs or not, and makes the extent of the reflectance degradation due to corrosion frequently larger than the longer-wavelength laser irradiation. Consequently, for the purpose of producing recording media adaptable to the development of the future recording light sources, it is desired to develop a material that has a high reflectance even for the laser irradiation in a shorter wavelength region, and furthermore, can maintain the reflectance within a range of practical use. - The present invention has been achieved on the above described background, and is aimed at providing a material that is a silver alloy to form a reflective film of an optical recording medium or the like, and is workable without degrading the reflectance even in a long-term use. Additionally, the present invention provides a material that has a high reflectance even for a short wavelength laser light.
- In order to solve the above described problems, the present inventors selected appropriate dopant elements with silver as the main component similarly to the conventional art. Consequently, the present inventors have come up with the present invention by discovering that the addition of an element, as an dopant element, higher than silver in melting point is effective in maintaining the reflectance and is useful for improving the heat resistance, the moisture resistance or the resistance to sulfidation.
- The present invention is a silver alloy for use in a reflective film, including silver as a main element and at least one element, higher than silver in melting point, as a first dopant element.
- Here, the first dopant element higher than silver in melting point is selected depending on which of the properties of the thin film is considered as important. According to the present inventors, the high melting point metal elements useful for improving the performances of the silver alloy thin film are nickel, molybdenum, copper, cobalt, titanium, scandium, yttrium, manganese, silicon, iron, zirconium, niobium, tantalum and tungsten. Inclusion of at least one of these elements can lead to a silver thin film useful for maintaining the high reflectance.
- According to the investigations carried out by the present inventors, it has been verified that a silver alloy, doped with nickel, copper or molybdenum among the above described elements, can maintain the various properties required for a reflective film at specially high levels. Such a silver-nickel alloy and such a silver-molybdenum alloy are excellent both in corrosion resistance and in heat resistance, and are suitable not only for the reflective layer for use in an optical recording medium but also for the reflective film for use in a display.
- Further, in the present invention, the silver alloy is preferably an alloy doped with at least one element, as a second dopant element, selected from gallium, thulium, dysprosium, platinum, palladium, magnesium, zinc, terbium, gadolinium, erbium, gold, aluminum, neodymium, holmium, tin, bismuth, praseodymium, germanium, indium, samarium, ytterbium, strontium, boron, rhodium, iridium, ruthenium, chromium, lead, calcium, antimony, hafnium, lanthanum, cerium and europium. These elements have effects to improve, in cooperation with the first dopant element, the resistance to sulfidation, moisture resistance and heat resistance, and work in combination with the first dopant elements.
- In particular, a silver alloy doped with a second dopant element of gallium, thulium, dysprosium, platinum or palladium is a preferable alloy because such an alloy can effectively suppress the agglomeration phenomenon which possibly occur in a thin film material in a humidified environment.
- Additionally, the dopant element concentration, namely, total of the concentration(s) of the first dopant element(s) and the concentration(s) of the second dopant element(s) is preferably 0.01 to 5.0 atomic %. When the addition amount is less than 0.01 atomic %, no effect of the reflectance maintenance is found. When the dopant element concentration exceeds 5.0 atomic %, the reflectance degradation becomes large depending on the service environment and the incident laser light wavelength, and it becomes impossible to ensure the reflectance. The concentration is particularly preferably 0.01 to 3.5 atomic %, because this range of concentration can maintain the reflectance at a higher level irrespective of the service environment and the laser light wavelength.
- The above-described silver alloy, according to the present invention, as the material for use in a reflective film, can be produced by the melt casting method and the sintering method. The production based on the melt casting method involves no particular difficulties, and can produce the alloy by means of a general method in which individual raw materials are weighed out, mixed by melting, and the mixture is subjected to casting. The sintering method also involves no particular difficulties, and can produce the alloy by means of a general method in which individual raw materials are weighed out, and subjected to sintering.
- The silver alloy according to the present invention has properties favorable for a reflective film, and suppresses the reflectance degradation in the course of use. As described below, the silver alloy according to the present invention exhibits a more satisfactory reflectance and a more satisfactory maintenance of the reflectance than conventional materials for use in reflective films, even under irradiation with a short wavelength laser light. As described above, the sputtering method is generally applied to the production of reflective films of optical recording media and the like. Accordingly, sputtering targets made of the silver alloy according to the present invention can serve to produce optical recording media, displays and the like each provided with a reflective film having satisfactory properties.
- As described above, according to the present invention, a reflective film that is less degraded in reflectance even under long-term use can be produced, and various devices to which reflective films are applied, such as optical recording media, displays and the like, can be made to have a long operation life. The silver alloy according to the present invention also exhibits a more satisfactory reflectance and a more satisfactory maintenance of the reflectance than conventional materials for use in reflective films, even under irradiation with a short wavelength laser light. Accordingly, the silver alloy according to the present invention is compatible with recording media for use in optical recording devices each having a short wavelength laser as the light source, such recording devices being anticipated to form the mainstream of such devices.
- Hereinafter, a preferred embodiment of the present invention is described together with comparative examples. Here, binary and ternary silver alloys having various compositions with Ag as the main component were produced; targets were produced from these alloys, and thin films were formed therefrom by means of a sputtering method. These thin films were subjected to corrosion tests (accelerated tests) in various environments, and the reflectance variations as observed after the corrosion tests were examined.
- In the production of each of the silver alloys, individual metals were weighed out so as to give predetermined concentrations, mixed by melting in a high frequency melting furnace to yield an alloy. The molten alloy thus obtained was cast into a casting mold to be solidified to yield an ingot, the ingot was forged, rolled and heat treated, and thereafter shaped into a sputtering target.
- In the thin film production, a substrate (borosilicate glass) and a target were placed in a sputtering apparatus, the interior of the apparatus was evacuated to a vacuum of 5.0×10−3 Pa, and then argon gas was introduced into the interior of the apparatus so as to give a pressure of 5.0×10−1 Pa. Sputtering conditions were such that film formation was carried out with a direct current power of 4 kW for 8 seconds to attain a film thickness of 1200 Å. It is to be noted that the film thickness distribution fell within ±10%.
- The thin film products were evaluated with respect to heat resistance and moisture resistance. These properties were evaluated as follows: a thin film was exposed to each corresponding environment and the reflectance of the thin film after each test was measured at a varying wavelength in a spectrophotometer; and the observed reflectances at different wavelengths were compared differentially with the corresponding reflectances of silver as the reference levels, which were measured immediately after film formation.
- The heating test to examine the heat resistance of a thin film was carried out as follows: the thin film was placed on a hot plate, heated in an atmosphere at 250° C. for 1 hour, and the reflectance after heating was evaluated. The humidification test to examine the moisture resistance of a thin film was carried out as follows: the thin film was exposed to an atmosphere of a temperature of 100° C. and a humidity of 100%, and the reflectance after humidification was evaluated; the exposure time was varied to take two periods, namely, 24 hours (humidification test I) and 100 hours (humidification test II). The results of these corrosion tests are shown in Tables 1 to 3. The reflectances shown in these tables are relative values based on the reflectances of silver immediately after film formation which are set at 100. The measured reflectance values are the values measured at the wavelengths of 400 nm, 550 nm and 650 nm (respectively corresponding to the wavelengths of blue, yellow and red lasers). It is to be noted that each of these tables includes, for comparison, the test results obtained for a thin film produced from a target made of pure silver.
TABLE 1 Incident light wavelength: 400 nm Reflectance Immediately Hu- Hu- Sample after Heating midification midification composition (at %) deposition test test I test II Ag—1.7Cu 83.2 77.1 78.0 58.9 Ag—1.9Mn 80.5 49.8 35.9 25.9 Ag—3.7Si 100.5 72.0 94.5 94.1 Ag—1.8Ni 95.0 86.5 94.1 88.1 Ag—1.8Co 93.5 81.4 92.9 92.7 Ag—1.2Y 100.7 45.4 98.6 94.2 Ag—1.9Fe 93.2 60.8 89.9 90.7 Ag—2.4Sc 100.1 88.6 41.6 36.6 Ag—1.2Zr 98.6 65.5 96.7 94.4 Ag—1.2Nb 88.8 92.4 93.2 87.3 Ag—1.1Mo 93.1 6.6 80.6 78.8 Ag—0.6Ta 89.1 86.5 88.4 64.4 Ag—0.6W 92.8 82.0 89.3 84.4 Ag—1.1Ni—0.8Cr 99.3 63.8 96.1 70.9 Ag—0.8Cu—0.8Ga 103.6 101.9 48.9 39.4 Ag—1.7Cu—0.7Nd 89.0 87.8 71.9 61.9 Ag—0.85Cu—0.5In 96.3 85.6 89.6 82.2 Ag—0.4Cu—0.5Au 99.8 68.6 73.6 56.1 Ag—0.5Ni—0.5In 93.2 83.6 88.4 83.9 Ag—0.5Zr—0.5In 97.9 63.3 86.8 85.9 Ag—0.5Mo—0.5In 93.6 69.8 88.6 85.4 Ag (for comparison) 102.3 1.6 45.9 37.5 -
TABLE 2 Incident light wavelength: 550 nm Reflectance Immediately Hu- Hu- Sample after Heating midification midification composition (at %) deposition test test I test II Ag—1.7Cu 93.9 90.4 97.6 87.5 Ag—1.9Mn 93.2 67.7 51.4 43.6 Ag—3.7Si 100.0 85.9 99.3 97.6 Ag—1.8Ni 98.5 93.6 98.7 97.5 Ag—1.8Co 98.2 92.0 98.6 98.3 Ag—1.2Y 100.4 61.3 100.5 98.1 Ag—1.9Fe 97.4 79.3 97.4 96.6 Ag—2.4Sc 100.5 95.6 73.8 67.0 Ag—1.2Zr 100.2 81.4 99.5 99.0 Ag—1.2Nb 98.8 99.1 99.5 91.3 Ag—1.1Mo 98.3 23.1 97.1 97.5 Ag—0.6Ta 98.9 97.4 97.2 79.4 Ag—0.6W 97.5 96.0 97.1 94.8 Ag—1.1Ni—0.8Cr 100.2 80.7 99.1 80.7 Ag—0.8Cu—0.8Ga 101.1 101.8 58.4 47.8 Ag—1.7Cu—0.7Nd 95.7 95.5 85.2 75.1 Ag—0.85Cu—0.5In 98.6 92.5 95.4 91.9 Ag—0.4Cu—0.5Au 100.3 87.8 85.7 83.6 Ag—0.5Ni—0.5In 97.2 92.3 94.8 92.8 Ag—0.5Zr—0.5In 99.2 75.7 91.4 92.8 Ag—0.5Mo—0.5In 98.9 78.4 97.5 97.2 Ag (for comparison) 100.8 1.5 78.4 67.8 -
TABLE 3 Incident light wavelength: 650 nm Reflectance Immediately Hu- Hu- Sample after Heating midification midification composition (at %) deposition test test I test II Ag—1.7Cu 96.6 95.0 98.8 92.0 Ag—1.9Mn 95.2 73.9 62.9 61.3 Ag—3.7Si 99.9 90.4 99.7 97.8 Ag—1.8Ni 98.8 94.6 99.1 97.8 Ag—1.8Co 98.7 93.9 99.3 98.7 Ag—1.2Y 100.3 67.8 100.5 98.4 Ag—1.9Fe 98.0 84.6 98.6 97.1 Ag—2.4Sc 100.6 97.5 81.9 76.9 Ag—1.2Zr 100.3 86.1 99.6 99.5 Ag—1.2Nb 99.3 99.7 100.0 92.7 Ag—1.1Mo 99.0 36.8 98.3 98.9 Ag—0.6Ta 99.5 98.8 98.1 80.9 Ag—0.6W 98.1 97.9 97.6 95.7 Ag—1.1Ni—0.8Cr 100.3 85.0 99.2 80.9 Ag—0.8Cu—0.8Ga 100.9 101.6 62.1 51.8 Ag—1.7Cu—0.7Nd 96.9 97.3 87.0 76.0 Ag—0.85Cu—0.5In 98.9 94.7 96.2 92.7 Ag—0.4Cu—0.5Au 100.3 92.8 85.9 84.8 Ag—0.5Ni—0.5In 97.8 93.6 95.2 93.5 Ag—0.5Zr—0.5In 97.9 63.3 86.8 85.9 Ag—0.5Mo—0.5In 93.6 69.8 88.6 85.4 Ag (for comparison) 100.6 1.6 86.0 78.6 - As can be seen from these results, the thin films produced from the silver alloys according to the present example gave the reflectance values higher than those of silver to verify the effects of improving the heat resistance and the moisture resistance. As a general tendency, with decreasing incident light wavelength, the reflectance was lowered.
- Next, part of the produced thin films were subjected to a sulfidation test for the purpose of evaluating the resistance to sulfidation in such a way that the reflectance values after the test were evaluated. In the sulfidation test, each thin film was soaked in a 0.01% aqueous solution (temperature: 25° C.) of sodium sulfide for 1 hour. The results thus obtained are shown in Table 4; from these test results, it has been able to be verified that in all the wavelength regions, the resistance to sulfidation tends to be improved for the alloy thin films according to the present embodiment.
TABLE 4 Reflectance 400 nm 550 nm 650 nm Sample Immediately Immediately Immediately composition after after After after After (at %) deposition After test deposition test deposition test Ag—1.70Cu 83.2 62.4 93.9 73.5 96.6 78.6 Ag—0.85Cu—0.5In 96.3 51.0 98.6 66.1 98.9 75.7 Ag—0.5Mo—0.5In 93.6 51.2 98.9 65.1 99.2 73.7 Ag—0.5Zr—0.5In 97.9 37.7 99.2 50.2 99.3 62.5 Ag—0.4Cu—0.5Au 99.8 38.8 100.3 57.5 100.3 71.5 Ag—1.7Cu—0.5Zn 95.6 38.7 98.1 54.7 98.4 68.1 Ag (for 102.3 31.3 100.8 39.6 100.6 53.5 comparison) - Next, the applicability as a practical reflective film was evaluated for each silver alloy film according to the present invention. Actually, this evaluation was carried out on the basis of two evaluation methods: one was a convenient simulated evaluation method that was devised by the present inventors and the other was an evaluation method in which an optical recording medium was actually produced and the performance (presence or absence of error) thereof was examined. The reason why the former simulated evaluation was carried out in the present invention is as follows: in an optical recording medium taken as an example, the optical recording medium is composed of a large number of layers including, in addition to the reflective layer, a substrate and a recording layer, and including, depending on the type of the medium, a dielectric layer, a heat release layer and the like; and for the purpose of evaluating the adaptability of the reflective layer of the optical recording medium, it is necessary that these constituent layers are formed on the substrate to produce the recording medium, and then the recording medium is evaluated, and this is troublesome.
- For optical recording media in practical use, it is relatively easy to produce such media for an evaluation purpose. However, high-density large-capacity recording media under development for practical use in future, such as HD-DVD disks and Blu-lay disks, become more complex in structure and have reflective layers to work as semitransparent reflective layers that are anticipated to be used as further thinner films (the film thickness of the reflective layer of an optical recording medium currently used being around 1000 to 1200 Å, but the reflective layer of such a next generation optical recording medium being developed for a film thickness of 200 Å or less). As for such media to be complex as described above, it is difficult to actually produce and evaluate them.
- Consequently, for the purpose of evaluating the adaptability of a formed thin film as a reflective film without producing an optical recording medium, the present inventors has adopted a method, as a convenient method, in which such a film is exposed in a predetermined environment, and thereafter the surface appearance of the film is observed to evaluate the adaptability of the thin film to practical use.
- In this method, the humidification test is carried out as follows: first, a formed thin film is allowed to stand (for 20 to 30 minutes) in a cooling atmosphere set at a temperature (preferably 10° C.) lower than room temperature to be sufficiently cooled together with the substrate; the thus cooled thin film is exposed in a humidification environment; and the thin film is taken out and dried, and thereafter a surface appearance of the thin film is observed. The humidification environment is preferably an atmosphere at a temperature of 100° C. and with a humidity of 100%, and the exposure time in this case is preferably set at 20 minutes. In the heating test, a formed thin film is directly placed together with the substrate in a heating environment; the heating environment is preferably an air atmosphere at 250° C., and the exposure time in this case is preferably set at 60 minutes.
- The observation of the surface appearance is conducted to evaluate the evaluation of the degree of generation of silver agglomerates (hereinafter referred to as black spots) occurring as black spots on the thin film surface after having been exposed in each environment. This is based on the consideration that: as a form of deterioration of a heated silver alloy film, silver agglomerates are locally generated on the surface of the film; silver agglomerates conceivably affect the properties of a reflective film; and accordingly, the evaluation of the generation degree of the black spots allows the adaptability as a reflective film to be determined. In this evaluation, the black spots to be counted are preferably those each having a size of 1 to 10 μm. Such clear definition of the spots to be evaluated allows the evaluation to be facilitated. Such a size as described above matches the size of marks to be used for record reproduction in an optical recording medium.
- The evaluation of the generation degree of the black spots may be carried out, for example, by taking a photo of the surface of the thin film, and by subjecting the photo to image processing to derive the rate of the area of the black spots. As a more convenient method, there is one in which evaluation is carried out by taking as a reference the surface condition (in this case, almost no black spots being generated) of a silver thin film immediately after formation thereof and by assessing the surface condition of a thin film after heating, relatively to the reference, through classification into a few levels.
- In the present embodiment, the humidification environment was set to be an atmosphere at a temperature of 100° C. and with a humidity of 100%, with the exposure time set at 20 minutes. In the simulated evaluation of a thin film in the present embodiment, different types of 120 Å and 1200 Å silver alloy thin films were produced, and each thin film was cooled and thereafter exposed in the above described humidification environment to be subsequently subjected to optical microscopic observation of the surface appearance thereof. The surface condition of a silver thin film immediately after the production thereof was taken as a reference to be graded as “
level 1,” and the surface condition evaluation was carried out in terms of 5 grades degrading order of the surface condition from level 1 (in the order of increasing number of the black spots) in such a way that the properties of the films were assessed through classification intolevel 1 tolevel 5. The results thus obtained are shown in Table 5.TABLE 5 Samples (at %) Level Binary alloy Ternary alloy Film thickness: 120 Å 1 Ag—1.7Cu—2.0 Ga 2 3 Ag—0.2Mo 4 Ag—1.7Cu Ag—0.3Ni Ag—0.2Mo—2.0 Ga 5 Ag—0.3Ni—2.0Ga Film thickness: 1200 Å 1 2 Ag—0.3Ni Ag—0.2Mo Ag—1.0 Ni—1.0 Ga 3 4 Ag—1.7Cu Ag—1.0Co Ag—1.0Ti Ag—1.0Sc Ag—1.0Y Ag—1.0 Mn 5 Ag—0.1B Ag—0.25Si Ag—0.8Cu—0.5In Ag—1.7Fe Ag—1.0Zr Ag—1.0Nb Ag—0.5Ta Ag—0.5W
Level 1 refers to the surface condition of silver immediately after deposition.
- As a result of the simulated test, it is inferred that excellent, in properties, among the binary alloys are those containing molybdenum, copper or nickel, and excellent, in properties, among the ternary alloys is that containing gallium as the second dopant element.
- Next, DVD-R media having as a reflective layer thin films made of the silver alloys according to the present invention were actually produced and were evaluated for the properties as the reflective film of an optical recording medium. In this test, there were used as substrates polycarbonate substrates (120 mm in diameter, 0.6 mm in plate thickness, 0.17 μm in groove depth, 0.3 μm in groove width, and 0.74 μm in groove pitch) with preformatted pattern formed thereon, produced with an injection molding machine equipped with a stamper. On the upper side of each substrate, a metal-containing azo recording ink was coated by way of spin coating and dried, and thereafter, a reflective film was formed so as to have a film thickness of 1200 Å with a sputtering target produced in the present embodiment. To each substrate, a polycarbonate substrate the same in size as the substrate concerned was bonded with an ultraviolet curable resin to produce a DVD-R medium.
- Then, with an optical disk evaluation apparatus (optical disk evaluation apparatus, ODU1000, manufactured by Pulstec Industrial Co., Ltd.), the jitter values, Pl8 errors and PO errors of the thus produced DVD-R media in the initial condition subsequent to the production thereof were measured, and were verified to fall within the ranges of the DVD specifications. After the verification, the DVD-R media were subjected to an accelerated environment test in which the DVD-R media were exposed in an environment at a temperature of 80° C. and with a relative humidity of 85%, and the DVD-R media after the accelerated environment test were subjected to the measurement of the individual values by means of the evaluation apparatus.
- FIGS. 1 to 3 show relations between humidification time and jitter value, Pl8 error value and PO error, respectively, which were all measured in this test. These figures also show the results obtained by applying the same tests to a DVD-R medium having a reflective film made of pure silver and commercially available DVD-R media.
- As can be seen from these figures, it has been verified that the recording media each provided with a reflective film made of a silver alloy according to the present invention each clear the specifications for the individual values, and have a long-term stability, even after a long time humidification. On the contrary, the recording medium provided with a reflective film made of pure silver failed to be recognized by the recording device and became unusable after humidification for 150 hours. It was also verified that the jitter values of the commercially available products exceeded the specification, and although the error values of these commercial products were able to clear the specifications, the properties of these commercial products were inferior to those of the recording media according to the present embodiment.
- Additionally, Table 6 shows results obtained as follows: DVD-R media each provided with a reflective film made of a silver alloy different in composition from those examined above were produced; the DVD-R media thus produced were exposed in a humidification environment in the same manner as described above; and thereafter, the results shown in Table 6, namely, the jitter values, Pl8 errors and PO errors thereof were measured.
TABLE 6 Jitter value PI8 error PO error After After After exposure exposure exposure to to to Initially humidity Initially humidity Initially humidity Examples Au—0.2Mo—0.1Pr 7.7 7.8 64 257 6 27 Ag—0.2Y—1.0Tb 7.7 7.8 68 246 6 23 Ag—0.1Sc—1.0Zr 7.7 7.8 72 266 7 35 Ag—0.5Ti—1.7Cu 7.8 7.9 71 264 9 32 Ag—1.0Mn—1.0Yb 7.8 7.9 94 272 12 48 Comparative Ag 8.2 11.7 207 299 25 83 Examples Commercial product 8.6 10.7 224 305 31 73 from Company A Commercial product 8.3 ≧11.9 185 ≧318 45 ≧104 from Company B Specification 8.00 or less 280 or less 182 or less - Also from this table, it was verified that the individual values of the recording media each provided with a silver alloy according to the present invention as a reflective layer cleared the specifications even after the humidification, and each had a long-term stability. The evaluations carried out by producing these media coincided with the already performed, simulated test (evaluation results for 1200 Å), and the long-term stability was owned by each of the recording media, anticipated to have satisfactory properties in the simulated test, each provided with a reflective film containing at least any one of nickel, copper, molybdenum and gallium. Consequently, it has been verified that the simulated test carried out in the present embodiment is a convenient method for assessing the properties of a silver alloy without actually producing a recording medium.
-
FIG. 1 is a graph showing the results (jitter values) of an accelerated environment test carried out on DVD-R media each provided with one of the reflective films according to present Embodiment; -
FIG. 2 is a graph showing the results (Pl8 error values) of the accelerated environment test carried out on the DVD-R media each provided with one of the reflective films according to present Embodiment; and -
FIG. 3 is a graph showing the results (PO error values) of the accelerated environment test carried out on the DVD-R media each provided with one of the reflective films according to present Embodiment.
Claims (20)
1. A silver alloy for use in a reflective film, comprising silver as a main element and at least one element as a first dopant element higher than silver in melting point.
2. The silver alloy for use in a reflective film according to claim 1 , wherein the first dopant element comprises at least one of nickel and molybdenum.
3. The silver alloy for use in a reflective film according to claim 1 , wherein the first dopant element comprises at least one of copper, cobalt, titanium, scandium, yttrium, manganese, silicon, iron, zirconium, niobium, tantalum and tungsten.
4. The silver alloy for use in a reflective film according to claim 1 , comprising as a second dopant element at least one element selected from gallium, thulium and dysprosium.
5. The silver alloy for use in a reflective film according to claim 1 , comprising as a second dopant element at least one element selected from platinum, palladium, magnesium, zinc, terbium, gadolinium and erbium.
6. The silver alloy for use in a reflective film according to claim 1 , comprising as a second dopant element at least one element selected from gold, aluminum, neodymium, holmium, tin, bismuth and praseodymium.
7. The silver alloy for use in a reflective film according to claim 1 , comprising as a second dopant element at least one element selected from germanium, indium, samarium, ytterbium, strontium, boron, rhodium, iridium, ruthenium, chromium, lead, calcium, antimony, hafnium, lanthanum, cerium and europium.
8. The silver alloy for use in a reflective film according to claim 1 , wherein a total of the concentration of the first dopant element and the concentration of the second dopant element are 0.01 to 5.0 atomic %.
9. The silver alloy for use in a reflective film according to claim 8 , wherein the total of the concentration of the first dopant element and the concentration of the second dopant element are 0.01 to 3.5 atomic %.
10. A sputtering target, comprising the silver alloy as defined in claim 1 .
11. An optical recording medium comprising a substrate and a silver alloy on the substrate which silver alloy comprises silver and at least one element as a first dopant element having a melting point higher than silver.
12. The optical recording medium according to claim 11 wherein the silver alloy comprises a first dopant element comprising at least one of nickel and molybdenum.
13. The optical recording medium according to claim 11 wherein the silver alloy comprises a first dopant element comprising at least one of copper, cobalt, titanium, scandium, yttrium, manganese, silicon, iron, zirconium, niobium, tantalum and tungsten.
14. The optical recording medium according to claim 11 wherein the silver alloy comprises a second dopant element comprising at least one element selected from gallium, thulium and dysprosium.
15. The optical recording medium according to claim 11 wherein the silver alloy comprises a second dopant element comprising at least one element selected from platinum, palladium, magnesium, zinc, terbium, gadolinium and erbium.
16. The optical recording medium silver according to claim 11 wherein the silver alloy comprises a second dopant element comprising at least one element selected from gold, aluminum, neodymium, holmium, tin, bismuth and praseodymium.
17. The optical recording medium according to claim 11 wherein the silver alloy comprises a second dopant element comprising at least one element selected from germanium, indium, samarium, ytterbium, strontium, boron, rhodium, iridium, ruthenium, chromium, lead, calcium, antimony, hafnium, lanthanum, cerium and europium.
18. The optical recording medium according to claim 11 wherein a total of the concentration of the first dopant element and the concentration of the second dopant element in the silver alloy are 0.01 to 5.0 atomic %.
19. The optical recording medium according to claim 11 wherein a total of the concentration of the first dopant element and the concentration of the second dopant element in the silver alloy are 0.01 to 3.5 atomic %.
20. A method for producing an optical recording medium which comprises forming a film of a silver alloy on a substrate, which silver alloy comprises a first dopant element, selected from nickel, molybdenum, copper, cobalt, titanium, scandium, yttrium, manganese, silicon, iron, zirconium, niobium, tantalum, and tungsten, which silver alloy optionally further comprises a second dopant element selected from gallium, thulium, dysprosium, platinum, palladium, magnesium, zinc, terbium, gadolinium, erbium, gold, aluminum, neodymium, holmium, tin, bismuth and praseodymium, germanium, indium, samarium, ytterbium, strontium, boron, rhodium, iridium, ruthenium, chromium, lead, calcium, antimony, hafnium, lanthanum, cerium and europium.