US20050240042A1 - Electrophoretic paint containing bismuth components - Google Patents
Electrophoretic paint containing bismuth components Download PDFInfo
- Publication number
- US20050240042A1 US20050240042A1 US10/518,098 US51809804A US2005240042A1 US 20050240042 A1 US20050240042 A1 US 20050240042A1 US 51809804 A US51809804 A US 51809804A US 2005240042 A1 US2005240042 A1 US 2005240042A1
- Authority
- US
- United States
- Prior art keywords
- composition
- binder
- pigments
- crosslinking
- groups
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/08—Anti-corrosive paints
- C09D5/082—Anti-corrosive paints characterised by the anti-corrosive pigment
- C09D5/086—Organic or non-macromolecular compounds
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/44—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes for electrophoretic applications
- C09D5/4488—Cathodic paints
- C09D5/4492—Cathodic paints containing special additives, e.g. grinding agents
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/47—Levelling agents
Definitions
- the present invention relates to novel electrocoat (EC) materials comprising bismuth compounds.
- the present invention also relates to the preparation of novel EC materials comprising bismuth compounds.
- the present invention further relates to the use of the novel EC materials comprising bismuth compounds for producing electrocoats.
- EC materials comprising bismuth compound catalysts are known.
- the bismuth compounds include a lower toxicity as compared with the tin compounds, as well as a high activity.
- DE 25 41 234 describes salts (carboxylates), among others, of bismuth as curing catalysts for electrocoat materials.
- EP 0 509 437 discloses electrocoat materials which crosslink by way of blocked isocyanate groups and which comprise at least one dialkyl salt of aromatic carboxylic acids and at least one bismuth compound or zirconium compound.
- European patent application EP 0 690 106 A1 discloses compositions which comprise water-soluble bismuth compounds, which are suitable as catalysts for the curing of EC materials. They include an epoxy-amine adduct in an amount such that the ratio of the number of bismuth atoms to the number of beta-hydroxyamine groups in the epoxy-amine adduct is from 1:10 to 10:1.
- the acid used for preparing the bismuth compounds is employed in an amount such that there are between 0.1 and less than 2 mol of dissociable protons per mole of bismuth.
- the numerous acids which can be used include salicylic acid. Further details, however, are lacking; in the examples, only dimethylolpropionic acid is used.
- European patent EP 0 739 389 describes a simplified process for preparing a corrosion protection coating by electrocoating, in which the electrocoat material comprises bismuth lactate or bismuth dimethylolpropionate.
- the electrocoat material comprises bismuth lactate or bismuth dimethylolpropionate.
- bismuth compounds including bismuth salicylate, are mentioned, but the document lacks further details; in particular, only the salts of lactic acid and dimethylolpropionic acid are used in the examples.
- Bismuth subsalicylate is not mentioned.
- the invention accordingly provides the novel electrocoat (EC) materials comprising bismuth compounds and further comprising
- the EC materials of the invention were easy to prepare, were stable on storage, featured an optimum particle size of the dispersed constituents, and possessed very good filterability. Their electrophoretic deposition on electrically conductive substrates was easy and trouble-free. The resultant electrocoats were very even, were free from surface defects and inhomogeneities, and afforded outstanding corrosion protection and edge protection.
- the deposited but uncured or only part-cured films of the EC materials of the invention can be overcoated wet on wet with aqueous coating materials, such as waterborne primers or waterborne surfacers, without defects and then baked together with said aqueous coating materials.
- the EC materials of the invention preferably have a solids content of from 5 to 50% by weight, more preferably from 5 to 35% by weight. Solids here are the fraction of an EC material which makes up the electrocoat produced from it.
- the EC materials of the invention comprise at least one binder (A).
- the binders (A) may be self-crosslinking and/or externally crosslinking.
- Self-crosslinking binders (A) contain reactive functional groups which are able to undergo thermal crosslinking reactions with themselves and/or with complementary reactive functional groups in the self-crosslinking binders (A).
- Externally crosslinking binders (A) contain reactive functional groups which are able to undergo thermal crosslinking reactions with complementary reactive functional groups in crosslinking agents (B).
- At least one externally crosslinking binder (A) in combination with at least one crosslinking agent (B).
- the binder (A) contains potentially cationic and/or cationic groups. Binders (A) of this kind are used in cathodically depositable electrocoat materials.
- Suitable potentially cationic groups which can be converted into cations by neutralizing agents and/or quaternizing agents are primary, secondary or tertiary amino groups, secondary sulfide groups or tertiary phosphine groups, especially tertiary amino groups or secondary sulfide groups.
- Suitable cationic groups are primary, secondary, tertiary or quaternary ammonium groups, tertiary sulfonium groups or quaternary phosphonium groups, preferably quaternary ammonium groups or tertiary sulfonium groups, but especially quaternary ammonium groups.
- Suitable neutralizing agents for the potentially cationic groups are inorganic and organic acids such as sulfuric acid, hydrochloric acid, phosphoric acid, formic acid, acetic acid, lactic acid, dimethylolpropionic acid or citric acid, especially formic acid, acetic acid or lactic acid.
- binders (A) for cathodically depositable electrocoat materials are known from documents EP 0 082 291 A1, EP 0 234 395 A1, EP 0 227 975 A1, EP 0 178 531 A1, EP 0 333 327, EP 0 310 971 A1, EP 0 456 270 A1, U.S. Pat. No.
- amine numbers preferably between 20 and 250 mg KOH/g and a weight-average molecular weight of from 300 to 10 000 daltons.
- amino (meth)acrylate resins amino epoxy resins, amino epoxy resins with terminal double bonds, amino epoxy resins with primary and/or secondary hydroxyl groups, amino polyurethane resins, amino-containing polybutadiene resins or modified epoxy resin-carbon dioxide-amine reaction products.
- the binder (A) may comprise anionic and/or potentially anionic groups. Binders (A) of this kind are used in anionically depositable electrocoat materials.
- Suitable potentially anionic groups which can be converted into anions by neutralizing agents are carboxylic, sulfonic or phosphonic acid groups, especially carboxylic acid groups.
- Suitable anionic groups are carboxylate, sulfonate or phosphonate groups, especially carboxylate groups.
- Suitable neutralizing agents for the potentially nonionic groups are ammonia, ammonium salts, such as ammonium carbonate or ammonium hydrogen carbonate, for example, and also amines, such as trimethylamine, triethylamine, tributylamine, dimethylaniline, diethylaniline, triphenylamine, dimethylethanolamine, diethylethanolamine, methyldiethanolamine, triethanolamine, and the like.
- binders (A) for anionically depositable electrocoat materials are known from German patent application DE 28 24 418 A1. They are preferably polyesters, epoxy resin esters, poly(meth)acrylates, maleate oils or polybutadiene oils having a weight-average molecular weight of from 300 to 10 000 daltons and an acid number of from 35 to 300 mg KOH/g.
- the amount of neutralizing agent is generally chosen such that from 1 to 100 equivalents, preferably from 50 to 90 equivalents, of the potentially cationic or potentially anionic groups of a binder (A) are neutralized.
- Suitable reactive functional groups are hydroxyl groups, thiol groups, and primary and secondary amino groups, especially hydroxyl groups.
- Suitable complementary reactive functional groups are blocked isocyanate groups, hydroxymethylene and alkoxymethylene groups, preferably methoxymethylene and butoxymethylene groups, and especially methoxymethylene groups. Preference is given to using blocked isocyanate groups.
- suitable blocking agents are those described below.
- the EC materials used are preferably cathodic.
- the amount of the above-described binders (A) in the EC materials of the invention is guided inparticular by their solubility and their dispersibility in the aqueous medium and by their functionality with regard to the crosslinking reactions with themselves or with the constituents (B), and may therefore be determined readily be the skilled worker on the basis of his or her general art knowledge, where appropriate with the assistance of simple preliminary tests.
- Suitable crosslinking agents (B) include all customary and known crosslinking agents which contain suitable complementary reactive functional groups.
- the crosslinking agents (B) are preferably selected from the group consisting of blocked polyisocyanates, melamine-formaldehyde resins, tris(alkoxycarbonylamino)triazines, and polyepoxides.
- the crosslinking agents (B) are more preferably selected from the group consisting of blocked polyisocyanates and highly reactive melamine-formaldehyde resins. With particular preference the blocked polyisocyanates are used.
- the blocked polyisocyanates (B) are prepared from customary and known paint polyisocyanates containing aliphatically, cycloaliphatically, araliphatically and/or aromatically attached isocyanate groups.
- paint polyisocyanates having from 2 to 5 isocyanate groups per molecule and having viscosities of from 100 to 10 000, preferably from 100 to 5000, and in particular from 100 to 2000 mPas (at 23° C.).
- the paint polyisocyanates may have been given a conventional hydrophilic or hydrophobic modification.
- paint polyisocyanates are described, for example, in “Methoden der organischen Chemie”, Houben-Weyl, Volume 14/2, 4 th edition, Georg Thieme Verlag, Stuttgart 1963, pages 61 to 70, and by W. Siefken, Liebigs Annalen der Chemie, Volume 562, pages 75 to 136.
- paint polyisocyanates are polyisocyanates containing isocyanurate, biuret, allophanate, iminooxadiazinedione, urethane, urea, carbodiimide and/or uretdione groups, which are obtainable from customary and known diisocyanates.
- diisocyanates it is preferred to use hexamethylene diisocyanate, isophorone diisocyanate, 2-isocyanatopropylcyclohexyl isocyanate, dicyclohexylmethane 2,4′-diisocyanate, dicyclohexylmethane 4,4′-diisocyanate or 1,3-bis(isocyanatomethyl)cyclohexane (BIC), diisocyanates derived from dimer fatty acids, 1,8-diisocyanato-4-isocyanatomethyloctane, 1,7-diisocyanato-4-isocyanatomethylheptane, 1-isocyanato-2-(3-isocyanatopropyl)cyclohexane, 2,4- and/or 2,6-tolylene diisocyanate, 4,4′-diphenylmethane diisocyanate, naphthalene diisocyanate or mixtures of these
- the EC materials of the invention comprise a water-insoluble pulverulent bismuth subsalicylate (C) of empirical formula C 7 H 5 O 4 Bi. It has a bismuth content according to DAB [German Pharmacopeia] 7 of from 56.5 to 60% by weight.
- Bismuth subsalicylate (C) is a commercial compound and is sold, for example, by MCP HEK GmbH, Lubeck, Germany. Based on their solids, the EC materials of the invention contain preferably from 0.05 to 5%, more preferably from 0.1 to 4%, and in particular from 0.2 to 3% by weight of bismuth subsalicylate (C).
- the EC materials of the invention may further comprise at least one customary and known additive (D) selected from the group consisting of catalysts other than bismuth Subsalicylate (C); pigments; anticrater additives; polyvinyl alcohols; thermally curable reactive diluents; molecularly dispersely soluble dyes; light stabilizers, such as UV absorbers and reversible free-radical scavengers (HALS); antioxidants; low-boiling and high-boiling (“long”) organic solvents; devolatilizers; wetting agents; emulsifiers; slip additives; polymerization inhibitors; thermolabile free-radical initiators; adhesion promoters; leveling agents; film-forming auxiliaries; flame retardants; corrosion inhibitors; flow aids; waxes; siccatives; biocides, and flatting agents, in effective amounts.
- D customary and known additive
- Pigments are preferably used as additives (D).
- the pigments (D) are preferably selected from the group consisting of customary and known color pigments, effect pigments, electrically conductive pigments, magnetically shielding pigments, fluorescent pigments, extender pigments, and anticorrosion pigments, organic and inorganic.
- the EC materials of the invention are prepared by mixing and homogenizing the above-described constituents (A), (B), (C) and (D) if desired, using customary and known mixing techniques and apparatus such as stirred tanks, stirred mills, extruders, kneading apparatus, Ultraturrax, inline dissolvers, static mixers, micromixers, toothed-gear dispersers, pressure relief nozzles and/or microfluidizers.
- the pigments are incorporated preferably in the form of pigment pastes or pigment preparations into the EC materials (cf. Römpp Lexikon Lacke und Druckmaschine, Georg Thieme Verlag, Stuttgart, N.Y., 1998, “Pigment preparations”, page 452).
- a further particular advantage of the bismuth Subsalicylate (C) used in accordance with the invention is that it lends itself outstandingly to incorporation into the pigment pastes and into the EC materials of the invention.
- the EC materials of the invention are applied conventionally by immersing an electrically conductive substrate in an electrocoating bath of the invention, connecting the substrate as the cathode or anode, preferably as the cathode, depositing an EC material film on the substrate using direct current, removing the coated substrate from the electrocoating bath, and subjecting the deposited EC material film to conventional thermal clearing (baking).
- the resulting electrocoat can then be overcoated with a surfacer or with an antistonechip primer and a solid-color topcoat material or, alternatively, with a basecoat material and a clearcoat material by the wet-on-wet technique.
- the surfacer film or antistonechip primer film and also the solid-color topcoat film are preferably each baked individually.
- the basecoat film and the clearcoat film are preferably baked together. This procedure results in multicoat paint systems having outstanding performance properties.
- the multicoat paint systems by wet-on-wet techniques wherein the deposited EC material film is not cured or is only partly cured thermally and is immediately overcoated with the other coating materials, especially aqueous coating materials, after which it is baked together with at least one of the films of the coating materials (EC material film+surfacer film; EC material film+surfacer film+solid-color topcoat film; EC material film+surfacer film+basecoat film, or EC material film+surfacer film+basecoat film+clearcoat film).
- the resulting multicoat paint systems have outstanding performance properties, the production processes being particularly economic and energy-saving. In the course of these processes it is found that the EC material films of the invention lend themselves particularly well to undisrupted overcoating by the wet-on-wet technique.
- electrocoats of the invention are obtained which exhibit very good leveling, are free from surface defects and inhomogeneities, and afford outstanding corrosion protection and edge protection.
- a reactor is charged under nitrogen with 10 462 parts of isomers and higher polyfunctional oligomers based on 4,4′-diphenylmethane diisocyanate, having an NCO equivalent weight of 135 g/eq (Lupranat® M20S from BASF AG; NCO functionality about 2.7; 2,2′- and 2,4′-diphenylmethanediisocyanate content less than 5%).
- 20 parts of dibutyltin dilaurate are added and 9626 parts of butyl diglycol are added dropwise at a rate such that the product temperature remains below 60° C. After the end of the addition, the temperature is held at 60° C.
- NCO equivalent weight 1 120 g/eq is determined (based on solid fractions).
- 867 parts of melted trimethylolpropane are added at a rate such that the temperature of the product does not exceed 100° C.
- stirring is continued for 60 minutes more.
- the mixture is cooled to 65° C. and diluted simultaneously with 963 parts of n-butanol and 300 parts of methyl isobutyl ketone.
- the solids content is 70.1% (1 h at 130° C.).
- the water of reaction is removed at from 110 to 140° C. from a 70% strength solution of diethylenetriamine in methyl isobutyl ketone.
- the product is subsequently diluted with methyl isobutyl ketone until the solution has an amine equivalent weight of 131 g/eq.
- Vacuum distillation removes the volatile solvents, which are then replaced in equal quantity by water.
- the characteristics of the dispersion are as follows: Solids content: 31.9% (1 hour at 130° C.) Base content: 0.69 meq/g solids Acid content: 0.32 meq/g solids pH: 6.2 Particle size: 113 nm
- an organic-aqueous solution of an epoxy-amine adduct is prepared by in a first stage reacting 2 598 parts of bisphenol A diglycidyl ether (epoxy equivalent weight (EEW): 188 g/eq), 787 parts of bisphenol A, 603 parts of dodecylphenol and 206 parts of butyl glycol in the presence of 4 parts of triphenylphosphine at 130° C. to an EEW of 865 g/eq. While the mixture cools, it is diluted with 849 parts of butyl glycol and 1 534 parts of D.E.R.
- EW epoxy equivalent weight
- the epoxy-amine adduct solution is used below to prepare an aqueous solution and/or dispersion of a grinding resin.
- a stable pigment paste is obtained which does not undergo sedimentation even after storage for two months at 40° C.
- An electrocoating bath is prepared from 2 053 parts by weight of deionized water, 2 348 parts by weight of the dispersion from preparation example 3 and 599 parts by weight of the pigment paste from example 1.
- the resulting electrocoat material has a solids content of about 20% with an ash content of 25%.
- the particle size of the dispersed constituents is optimized to the intended use.
- the filterability of the electrocoat material is very good and it is highly resistant to infestation to microorganisms.
Landscapes
- Chemical & Material Sciences (AREA)
- Life Sciences & Earth Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Wood Science & Technology (AREA)
- Organic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Molecular Biology (AREA)
- Paints Or Removers (AREA)
- Polymers With Sulfur, Phosphorus Or Metals In The Main Chain (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US12/407,327 US8152983B2 (en) | 2002-08-08 | 2009-03-19 | Electrophoretic paint containing bismuth components |
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE10236350.1 | 2002-08-08 | ||
DE10236350A DE10236350A1 (de) | 2002-08-08 | 2002-08-08 | Bismutverbindungen enthaltende Elektrotauchlacke (ETL) |
PCT/EP2003/007378 WO2004018580A1 (de) | 2002-08-08 | 2003-07-09 | Bismutverbindungen enthaltende elektrotauchlacke (etl) |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/407,327 Continuation US8152983B2 (en) | 2002-08-08 | 2009-03-19 | Electrophoretic paint containing bismuth components |
Publications (1)
Publication Number | Publication Date |
---|---|
US20050240042A1 true US20050240042A1 (en) | 2005-10-27 |
Family
ID=30469586
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/518,098 Abandoned US20050240042A1 (en) | 2002-08-08 | 2003-07-09 | Electrophoretic paint containing bismuth components |
US12/407,327 Expired - Lifetime US8152983B2 (en) | 2002-08-08 | 2009-03-19 | Electrophoretic paint containing bismuth components |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/407,327 Expired - Lifetime US8152983B2 (en) | 2002-08-08 | 2009-03-19 | Electrophoretic paint containing bismuth components |
Country Status (11)
Country | Link |
---|---|
US (2) | US20050240042A1 (es) |
EP (1) | EP1527145B1 (es) |
JP (1) | JP2005534795A (es) |
AT (1) | ATE372367T1 (es) |
AU (1) | AU2003253040A1 (es) |
BR (1) | BR0313229B1 (es) |
CA (1) | CA2494879A1 (es) |
DE (2) | DE10236350A1 (es) |
ES (1) | ES2293080T3 (es) |
MX (1) | MXPA05000698A (es) |
WO (1) | WO2004018580A1 (es) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US11466164B2 (en) | 2015-02-10 | 2022-10-11 | The Sherwin-Williams Company | Electrodeposition system |
CN115551954A (zh) * | 2020-05-25 | 2022-12-30 | 巴斯夫涂料有限公司 | 具有改进催化活性的含铋电泳涂料 |
US11896998B2 (en) | 2018-10-12 | 2024-02-13 | Basf Coatings Gmbh | Method for producing a multicoat paint system by postadditization of at least one basecoat with an aqueous dispersion comprising polyamides and/or amide waxes |
Families Citing this family (23)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102005012056A1 (de) | 2005-03-16 | 2006-09-28 | Basf Coatings Ag | Mehrschichtlackierungen, Verfahren zu ihrer Herstellung und deren Verwendung im Automobilbau |
EP1707601A1 (en) * | 2005-03-31 | 2006-10-04 | Institut Curie | Method for treating surfaces with copolymers |
DE102007038824A1 (de) | 2007-08-16 | 2009-02-19 | Basf Coatings Ag | Einsatz von Bismutsubnitrat in Elektrotauchlacken |
DE102008016220A1 (de) | 2008-03-27 | 2009-10-01 | Basf Coatings Ag | Elektrotauchlacke enthaltend Polymethylenharnstoff |
WO2012162359A2 (en) * | 2011-05-23 | 2012-11-29 | E. I. Du Pont De Nemours And Company | Anti-corrosion electrocoat |
RU2650969C2 (ru) | 2012-12-03 | 2018-04-18 | БАСФ Коатингс ГмбХ | Многослойная проявляющая и/или цветовая красочная система и способ ее получения и ее применение |
JP6374016B2 (ja) | 2013-11-18 | 2018-08-15 | ビーエーエスエフ コーティングス ゲゼルシャフト ミット ベシュレンクテル ハフツングBASF Coatings GmbH | Bi(III)含有組成物を使用して導電性基材をディップコーティングするための2段階法 |
JP6375385B2 (ja) | 2013-11-18 | 2018-08-15 | ビーエーエスエフ コーティングス ゲゼルシャフト ミット ベシュレンクテル ハフツングBASF Coatings GmbH | 溶解と非溶解両方のビスマスを含む導電性基材のための水性ディップコーティング組成物 |
ES2662416T3 (es) | 2013-11-19 | 2018-04-06 | Henkel Ag & Co. Kgaa | Composición acuosa de recubrimiento para el recubrimiento con pintura de inmersión de sustratos eléctricamente conductores que contienen óxido de aluminio |
JP6285045B2 (ja) | 2013-11-19 | 2018-02-28 | ビーエーエスエフ コーティングス ゲゼルシャフト ミット ベシュレンクテル ハフツングBASF Coatings GmbH | 酸化マグネシウムを含む導電性基材のための水性ディップコーティング組成物 |
US9982147B2 (en) | 2013-12-10 | 2018-05-29 | Basf Coatings Gmbh | Aqueous dip-coating composition for electroconductive substrates, comprising bismuth and a phosphorus-containing, amine-blocked compound |
EP2886207A1 (de) | 2013-12-18 | 2015-06-24 | BASF Coatings GmbH | Verfahren zur Herstellung einer Mehrschichtlackierung |
MX2016008064A (es) | 2013-12-18 | 2016-09-16 | Basf Coatings Gmbh | Metodo de produccion de un sistema de pintura multicapa. |
MX2016007692A (es) | 2013-12-18 | 2016-09-07 | Basf Coatings Gmbh | Metodo para producir un sistema de pintura multicapa. |
CN105828961B (zh) | 2013-12-18 | 2020-03-06 | 巴斯夫涂料有限公司 | 制备多涂层油漆体系的方法 |
JP6689883B2 (ja) | 2015-05-06 | 2020-04-28 | ビーエーエスエフ コーティングス ゲゼルシャフト ミット ベシュレンクテル ハフツングBASF Coatings GmbH | マルチコートペイント系を生成するための方法 |
CN105176313A (zh) * | 2015-10-20 | 2015-12-23 | 苏州赛斯德工程设备有限公司 | 一种水性防腐蚀涂料及其制备方法 |
US10920100B2 (en) | 2015-11-26 | 2021-02-16 | Basf Coatings Gmbh | Method for producing a multi-layered coating |
MX2021012611A (es) | 2019-04-15 | 2021-11-12 | Basf Coatings Gmbh | Composicion acuosa de recubrimiento por inmersion para sustratos electricamente conductores, que comprende bismuto mas litio. |
EP4003610A1 (en) | 2019-07-29 | 2022-06-01 | BASF Coatings GmbH | Process for producing a multilayer coating comprising a sparkling coat layer and multilayer coating obtained from said process |
MX2022003732A (es) | 2019-10-23 | 2022-05-02 | Basf Coatings Gmbh | Composicion de recubrimiento acuosa pigmentada con estabilidad mejorada frente a los poros. |
EP4186951A1 (de) | 2021-11-30 | 2023-05-31 | BASF Coatings GmbH | Verfahren zur herstellung einer mehrschichtlackierung |
WO2023117977A1 (en) | 2021-12-21 | 2023-06-29 | Basf Se | Chemical product passport |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4596842A (en) * | 1985-04-15 | 1986-06-24 | Inmont Corporation | Alkanolamine hydroxy-capped epoxy for cathodic electrocoat |
US5934127A (en) * | 1998-05-12 | 1999-08-10 | Ihly Industries, Inc. | Method and apparatus for reforming a container bottom |
US5965000A (en) * | 1994-11-30 | 1999-10-12 | Herberts Gmbh | Storage-stable, single-component concentrate, production and use thereof for the production of cathodically depositable electrocoating lacquer baths |
US6217811B1 (en) * | 1996-03-23 | 2001-04-17 | Dr. Mirtsch Gmbh | Process and apparatus for vault-structuring of thin material sheets |
US6730203B2 (en) * | 2000-09-20 | 2004-05-04 | Kansai Paint Co., Ltd. | Multi-layer coating film-forming method |
Family Cites Families (29)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3922253A (en) | 1971-10-28 | 1975-11-25 | Ppg Industries Inc | Self-crosslinking cationic electrodepositable compositions |
JPS538568B2 (es) | 1974-09-20 | 1978-03-30 | ||
AT352842B (de) | 1977-06-06 | 1979-10-10 | Herberts & Co Gmbh | Waesseriges ueberzugsmittel, insbesondere fuer die elektro-tauchlackierung, sowie verfahren zu seiner herstellung |
AT372099B (de) | 1981-11-26 | 1983-08-25 | Vianova Kunstharz Ag | Verfahren zur herstellung von waermehaertbaren, kationischen, wasserverduennbaren ueberzugsmitteln |
DE3300570A1 (de) | 1983-01-10 | 1984-07-12 | Basf Farben + Fasern Ag, 2000 Hamburg | Wasserdispergierbare bindemittel fuer kationische elektrotauchlacke und verfahren zu ihrer herstellung |
DE3322781A1 (de) * | 1983-06-24 | 1985-01-03 | Basf Farben + Fasern Ag, 2000 Hamburg | Selbstvernetzendes, hitzehaertbares reibharz |
DE3436345A1 (de) | 1984-10-04 | 1986-04-17 | Herberts Gmbh, 5600 Wuppertal | Kathodisch abscheidbares waessriges elektrotauchlack-ueberzugsmittel und dessen verwendung zum beschichten von gegenstaenden |
DE3518732A1 (de) | 1985-05-24 | 1986-11-27 | BASF Lacke + Farben AG, 4400 Münster | Wasserverduennbare bindemittel fuer kationische elektrotauchlacke und verfahren zu ihrer herstellung |
AT383821B (de) | 1985-12-20 | 1987-08-25 | Vianova Kunstharz Ag | Verfahren zur herstellung von selbstvernetzenden lackbindemitteln und deren verwendung fuer kathodisch abscheidbare elektrotauchlacke |
DE3624454A1 (de) | 1986-02-13 | 1987-08-20 | Hoechst Ag | Aminourethane, verfahren zu ihrer herstellung und ihre verwendung |
DE3615810A1 (de) | 1986-05-10 | 1987-11-12 | Herberts Gmbh | Kathodisch abscheidbares waessriges elektrotauchlackueberzugsmittel und seine verwendung |
DE3628121A1 (de) | 1986-08-19 | 1988-03-03 | Herberts Gmbh | Fremdvernetzende bindemittelkombination fuer mit wasser verduennbare lacke, kathodisch abscheidbares elektrotauchlackueberzugsmittel und dessen verwendung |
DE3733552A1 (de) | 1987-10-03 | 1989-04-13 | Herberts Gmbh | Kathodisch abscheidbares waessriges elektrotauchlack-ueberzugsmittel und dessen verwendung |
DE3738220A1 (de) | 1987-11-11 | 1989-05-24 | Basf Lacke & Farben | Verfahren zur herstellung kathodisch abscheidbarer bindemitteldispersionen mit vernetzern auf der basis von mit aminogruppen verkappten polyisocyanaten |
US4931157A (en) | 1988-02-18 | 1990-06-05 | Ppg Industries, Inc. | Epoxy resin advancement using urethane polyols and method for use thereof |
AT394197B (de) | 1989-08-23 | 1992-02-10 | Vianova Kunstharz Ag | Verfahren zur herstellung von bindemitteln fuer kathodisch abscheidbare lacke |
JPH0418460A (ja) | 1990-05-11 | 1992-01-22 | Kansai Paint Co Ltd | カチオン電着塗料用樹脂組成物 |
DE4126476C9 (de) | 1990-08-09 | 2004-10-21 | Kansai Paint Co., Ltd., Amagasaki | Verfahren zur Bildung eines Films aus einem Anstrichstoff |
AT394729B (de) | 1990-09-17 | 1992-06-10 | Vianova Kunstharz Ag | Verfahren zur herstellung von vernetzungskomponenten fuer kathodisch abscheidbarelackbindemittel |
JP2951406B2 (ja) | 1992-05-29 | 1999-09-20 | ヴィアノヴァ レジンズ アクチエンゲゼルシャフト | 触媒添加カチオンペイントバインダ,その製法およびその用途 |
DE4235778A1 (de) | 1992-10-23 | 1994-04-28 | Herberts Gmbh | Verfahren zur Herstellung von Mehrschichtlackierungen |
US5718817A (en) * | 1993-07-28 | 1998-02-17 | Elf Atochem North America, Inc. | Catalyst for low temperature cure of blocked isocyanates |
US5376457A (en) | 1993-08-19 | 1994-12-27 | Volvo Gm Heavy Truck Corporation | Vehicle coating process |
DE4330002C1 (de) * | 1993-09-04 | 1995-03-23 | Herberts Gmbh | Verfahren zur Lackierung von metallischen Substraten und Anwendung des Verfahrens |
DE4423139A1 (de) | 1994-07-01 | 1996-01-04 | Hoechst Ag | Härtung von kataphoretischen Tauchlacken mit Wismutkatalysatoren |
DE19512017C1 (de) | 1995-03-31 | 1996-07-18 | Herberts Gmbh | Verfahren zur Mehrschichtlackierung |
DE19618379A1 (de) | 1996-05-08 | 1997-11-13 | Basf Lacke & Farben | Mit Copolymeren des Vinylacetats modifizierte in Wasser dispergierbare Epoxidharze |
DE19703869A1 (de) | 1997-02-03 | 1998-08-06 | Basf Coatings Ag | Wäßrige Bindemitteldispersion für kationische Elektrotauchlacke |
DE10001222A1 (de) | 2000-01-14 | 2001-08-09 | Basf Coatings Ag | Beschichtung, enthaltend kolloidal verteiltes metallisches Bismut |
-
2002
- 2002-08-08 DE DE10236350A patent/DE10236350A1/de not_active Withdrawn
-
2003
- 2003-07-09 AU AU2003253040A patent/AU2003253040A1/en not_active Abandoned
- 2003-07-09 DE DE50308130T patent/DE50308130D1/de not_active Expired - Lifetime
- 2003-07-09 MX MXPA05000698A patent/MXPA05000698A/es active IP Right Grant
- 2003-07-09 ES ES03792184T patent/ES2293080T3/es not_active Expired - Lifetime
- 2003-07-09 WO PCT/EP2003/007378 patent/WO2004018580A1/de active IP Right Grant
- 2003-07-09 JP JP2004530006A patent/JP2005534795A/ja active Pending
- 2003-07-09 CA CA002494879A patent/CA2494879A1/en not_active Abandoned
- 2003-07-09 BR BRPI0313229-3B1A patent/BR0313229B1/pt active IP Right Grant
- 2003-07-09 US US10/518,098 patent/US20050240042A1/en not_active Abandoned
- 2003-07-09 EP EP03792184A patent/EP1527145B1/de not_active Expired - Lifetime
- 2003-07-09 AT AT03792184T patent/ATE372367T1/de not_active IP Right Cessation
-
2009
- 2009-03-19 US US12/407,327 patent/US8152983B2/en not_active Expired - Lifetime
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4596842A (en) * | 1985-04-15 | 1986-06-24 | Inmont Corporation | Alkanolamine hydroxy-capped epoxy for cathodic electrocoat |
US5965000A (en) * | 1994-11-30 | 1999-10-12 | Herberts Gmbh | Storage-stable, single-component concentrate, production and use thereof for the production of cathodically depositable electrocoating lacquer baths |
US6217811B1 (en) * | 1996-03-23 | 2001-04-17 | Dr. Mirtsch Gmbh | Process and apparatus for vault-structuring of thin material sheets |
US5934127A (en) * | 1998-05-12 | 1999-08-10 | Ihly Industries, Inc. | Method and apparatus for reforming a container bottom |
US6730203B2 (en) * | 2000-09-20 | 2004-05-04 | Kansai Paint Co., Ltd. | Multi-layer coating film-forming method |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US11466164B2 (en) | 2015-02-10 | 2022-10-11 | The Sherwin-Williams Company | Electrodeposition system |
US11896998B2 (en) | 2018-10-12 | 2024-02-13 | Basf Coatings Gmbh | Method for producing a multicoat paint system by postadditization of at least one basecoat with an aqueous dispersion comprising polyamides and/or amide waxes |
CN115551954A (zh) * | 2020-05-25 | 2022-12-30 | 巴斯夫涂料有限公司 | 具有改进催化活性的含铋电泳涂料 |
Also Published As
Publication number | Publication date |
---|---|
BR0313229B1 (pt) | 2013-09-03 |
AU2003253040A1 (en) | 2004-03-11 |
ES2293080T3 (es) | 2008-03-16 |
US20090258981A1 (en) | 2009-10-15 |
DE50308130D1 (de) | 2007-10-18 |
EP1527145A1 (de) | 2005-05-04 |
EP1527145B1 (de) | 2007-09-05 |
BR0313229A (pt) | 2005-06-14 |
MXPA05000698A (es) | 2005-04-08 |
ATE372367T1 (de) | 2007-09-15 |
CA2494879A1 (en) | 2004-03-04 |
US8152983B2 (en) | 2012-04-10 |
JP2005534795A (ja) | 2005-11-17 |
WO2004018580A1 (de) | 2004-03-04 |
DE10236350A1 (de) | 2004-02-19 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US8152983B2 (en) | Electrophoretic paint containing bismuth components | |
US10975252B2 (en) | Use of bismuth subnitrate in electro-dipping paints | |
US7504444B2 (en) | Aqueous electrocoat materials, their use in processes for coating electrically conductive substrates, and the use of bismuth compounds in these aqueous electrocoat materials | |
EP1246874B1 (de) | Beschichtung, enthaltend kolloidal verteiltes metallisches bismut | |
US8425747B2 (en) | Cathodic electrodeposition coatings containing polymethylene urea | |
US6825361B2 (en) | Cathodic electrocoating compositions containing hydroxyl-carbonate blocked polyisocyanate crosslinking agent | |
US20230193056A1 (en) | Bismuth Containing Electrocoating Material with Improved Catalytic Activity | |
EP1307519B1 (de) | Elektrotauchlacke, herstellbar durch schmelzeemulgierung | |
JP3814738B2 (ja) | 高耐食性電着塗膜被覆物 | |
WO2003074618A1 (de) | Von unlöslichen festkörpern freie elektrotauchlacke (etl) | |
WO2003074617A1 (de) | Von unlöslichen festkörpern freie elektrotauchlacke | |
JPH09235494A (ja) | カチオン電着塗料 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: BASF COATINGS AKTIENGESELLSCHAFT, GERMANY Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HARTUNG, MICHAEL;HEIMANN, ULRICH;GROßE-BRINKHAUS, KARL-HEINZ;AND OTHERS;REEL/FRAME:015634/0165;SIGNING DATES FROM 20041108 TO 20041123 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |
|
AS | Assignment |
Owner name: BASF COATINGS GMBH, GERMANY Free format text: CHANGE OF NAME;ASSIGNORS:HARTUNG, MICHAEL;HEIMANN, ULRICH;GROBE-BRINKHAUS, KARL-HEINZ;AND OTHERS;SIGNING DATES FROM 20041108 TO 20041123;REEL/FRAME:026921/0277 |