US20050064701A1 - Formation of low resistance via contacts in interconnect structures - Google Patents
Formation of low resistance via contacts in interconnect structures Download PDFInfo
- Publication number
- US20050064701A1 US20050064701A1 US10/665,584 US66558403A US2005064701A1 US 20050064701 A1 US20050064701 A1 US 20050064701A1 US 66558403 A US66558403 A US 66558403A US 2005064701 A1 US2005064701 A1 US 2005064701A1
- Authority
- US
- United States
- Prior art keywords
- substrate
- conductive material
- interconnect structure
- low
- dielectric layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
- H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
- H01L21/02041—Cleaning
- H01L21/02057—Cleaning during device manufacture
- H01L21/0206—Cleaning during device manufacture during, before or after processing of insulating layers
- H01L21/02063—Cleaning during device manufacture during, before or after processing of insulating layers the processing being the formation of vias or contact holes
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
- H01L21/70—Manufacture or treatment of devices consisting of a plurality of solid state components formed in or on a common substrate or of parts thereof; Manufacture of integrated circuit devices or of parts thereof
- H01L21/71—Manufacture of specific parts of devices defined in group H01L21/70
- H01L21/768—Applying interconnections to be used for carrying current between separate components within a device comprising conductors and dielectrics
- H01L21/76801—Applying interconnections to be used for carrying current between separate components within a device comprising conductors and dielectrics characterised by the formation and the after-treatment of the dielectrics, e.g. smoothing
- H01L21/76802—Applying interconnections to be used for carrying current between separate components within a device comprising conductors and dielectrics characterised by the formation and the after-treatment of the dielectrics, e.g. smoothing by forming openings in dielectrics
- H01L21/76814—Applying interconnections to be used for carrying current between separate components within a device comprising conductors and dielectrics characterised by the formation and the after-treatment of the dielectrics, e.g. smoothing by forming openings in dielectrics post-treatment or after-treatment, e.g. cleaning or removal of oxides on underlying conductors
Definitions
- the present invention generally relates to integrated circuits (ICs). More particularly, the present invention relates to interconnect structures, including multilevel interconnect structures fabricated by damascene methods in which the via contact resistance must be low.
- the present invention describes various methods and tooling for making improved interconnect structures based on copper damascene wiring having a reduced via contact resistance and stable resistance both during IC operation and reliability stress of the IC device.
- semiconductor devices include a plurality of circuits, which form an integrated circuit fabricated on a silicon single crystal substrate.
- a complex network of signal paths will normally be routed to connect the circuit elements distributed on the surface of the substrate. Efficient routing of these signals across the device requires the formation of multi-level or multi-layered interconnection schemes, such as, dual damascene wiring structures based on copper. Copper based interconnects are desirable due to their efficacy in providing high speed signal transmission between large numbers of transistors on a complex semiconductor chip.
- metal vias run perpendicular to the silicon substrate and metal lines run parallel to the silicon substrate. Further enhancement of the speed of signals and reduction of interaction of signals in adjacent copper lines (known as “cross-talk) is achieved in new IC product chips by surrounding the copper lines and vias in a low k or ultralow k dielectric.
- interconnect structures formed on an integrated circuit chip includes at least about 2 to 10 wiring levels fabricated at a minimum lithographic feature size designated about 1 ⁇ (referred to as “thinwires”) and above these levels are about 2 to 4 wiring levels fabricated at a larger size (referred to as “fatwires”).
- the thinwires are formed in a low dielectric constant (k) material having a dielectric constant between about 2 and about 3.5.
- the via contact resistance is high in prior structures due to contamination at the via to line interface.
- Contamination primarily includes oxygen and/or carbon and is in the form of copper oxide (Cu Oxide) or a carbon based residue (polymeric or amorphous carbon).
- the carbon residue commonly contains H or F and other undesired elements may be present at the via to line interface.
- a further problem during interconnect fabrication is that the shapes and dimensions of the etched via and trench openings are correct after etch, but the shapes and dimensions are distorted, enlarged, degraded or roughened during via cleaning.
- This problem is most acute when low modulus ultralow k (ULK) dielectrics (k ⁇ about 2.7) are used and the via cleaning includes Ar+ bombardment.
- the Ar+ ions enlarge the via dimensions and erode the bottom of the trenches and even cause roughening of the trench bottom. Pores in the ULK dielectric make this problem severe.
- the above objects can be achieved by cleaning the via contact surfaces during fabrication of an interconnect structure.
- the present invention provides a general method of making a BEOL interconnect structure including a porous or dense low k dielectric having low via contact resistance.
- the method includes the steps of:
- the present invention further provides a method of making a BEOL interconnect structure including a porous or dense low k dielectric having low via contact resistance.
- the method includes the steps of:
- the present invention still further provides a BEOL interconnect structure including a porous or dense low k dielectric having low via contact resistance prepared by the above methods of the present invention.
- the via contacts prepared by the methods of the present invention are very stable during thermal cycles and during operation of the semiconductor device. Further, the via contacts prepared by the methods described herein have a lower resistance than the vias described in the prior art.
- the vias are surrounded by a liner (for example, see element 6 in FIG. 1 ) and the adhesion of the liner is stronger than it is in the vias described in the prior art.
- the interconnect structures of the present invention are more reliable and more stable than the interconnect structures of the prior art, because stronger liner adhesion leads to more reliable and stable interconnect structures.
- FIG. 1 is a schematic cross-sectional view of a completed interconnect level having a first layer having a set of metallic lines and vias therein and a diffusion barrier layer thereon.
- FIG. 2 is a schematic cross-sectional view of the etched via and line openings before any metallization of the openings.
- the present invention provides a non-destructive pre-clean process methods for liner/barrier deposition on low-k dielectrics.
- an integrated circuit will have interconnect levels, each level including metallic lines and vias that are of a dual damascene (via plus next level conductor) wiring interconnect structure for use on the IC chip.
- the metallic lines and vias are composed of the same or different conductive material. Suitable materials for use herein include, but are not limited to, W, Cu, Al, Ag, Au and alloys thereof and the like. A particularly preferred material is Cu.
- the condensable cleaning agent can be a reducing agent; metal based reducing agent, metal hydride; mixed metal hydride such as, LiAIH, molecular source of fluorine or a source of hydrogen, or a source of both hydrogen and silicon.
- Examples of the latter include, but are not limited to disilane; trisilane; tetrasilane and other condensable silanes.
- Molecular sources of fluorine include metal fluorides, such as, AlF3, TiF4, WF6, TaF6 and include inorganic fluorine compounds, such as, SF6, XeF2 and a mixture thereof; organic fluorine sources such as hexafluoroproplyeneoxide, hexafluorobenzene, and include fluorinated higher silanes. Mixtures of the above compounds may be especially effective as the CCA.
- the hydrides and hydrogen sources are effective to remove oxide and oxygen containing residues, while fluorine sources are used to remove carbon containing residues.
- the activation step can be carried out by bombarding with He+ ions, H2+ ions and/or H+/H2+ mixtures.
- the activation step can be carried out by irradiating with electron beam or irradiating with an ultraviolet (UV) radiation.
- UV ultraviolet
- the activation step can be carried out by lifting the substrate off the cold chuck with lift pins and thereafter heating the substrate with heating lamps.
- the lifted substrate is heated to a temperature about 350° C. to about 400° C., more preferably, the lifted substrate is heated to a temperature about 200° C. to about 450° C.
- FIG. 1 an example of dual damascene level is described in which a substrate 10 and an etch stop/barrier layer 2 are shown. On the etch stop/barrier is deposited the ILD 3 and an optional hardmask 4 is atop the ILD. It should be noted that the hardmask can be composed of a single or multiple layers to form a composite hardmask film.
- a Cu conductor 5 is formed within the ILD, separated from the ILD by the liner/Cu diffusion barrier 6 .
- a second etch stop/barrier layer 7 forms the “cap” on the Cu conductor.
- Each of the metallic lines and vias 5 can optionally include a liner material 6 , which lines the metallic lines and vias.
- Suitable materials that can be used as liners include, but are not limited to, TiN, TaN, Ta, WN, W, TaSiN, TiSiN, WCN, Ru and the like and mixtures thereof.
- the liner can be a single layer or it can include multiple layers.
- openings for defining lines and vias are formed utilizing conventional lithography (including applying a photoresist to a surface of the low-k organic dielectric layer) and etching.
- the etching step includes a conventional dry etching, such as, reactive ion etching, ion beam etching or plasma etching.
- the photoresist is then stripped from the layer utilizing conventional stripping processes.
- a conductive material is deposited on the liner, if one is used, or on the exposed surfaces of the openings employing conventional deposition processes, such as, CVD, plasma-assisted CVD, sputtering, plating, evaporation or chemical solution deposition.
- the conductive metal filled structure is then subjected to a conventional planarization process in which any residual conductive metal and/or liner outside the opening is substantially removed.
- CMP may be used and after CMP the top horizontal portions of the metallic lines are approximately coplanar with the top surface of the first layer.
- a diffusion barrier layer 7 can then be deposited as a continuous layer on the top surface thereof to complete the interconnect level.
- Diffusion barrier layer 7 is composed of any insulating material that is capable of preventing one of the above mentioned conductive metals from diffusing into the first layers formed above this interconnect level.
- the present invention which is directed to cleaning of the via openings including the via contact to Cu line, is described in reference to FIG. 2 .
- dielectric layer 30 may be homogeneous, or it may be composed of multiple layers. If multiple layers are presented, the interface between the two layers does not have to be concurrent with the interface between the line opening 70 and the via opening 50 .
- the dielectric may have k from 3.5 to 2, as described below.
- a barrier/cap/etch stop layer 20 disposed atop a copper line below 100.
- the dielectric layer 30 may include an optional hardmask layer 40 which may be composed of a single or multiple layers to form a composite hardmask film.
- All of the above components are disposed on a substrate 110 .
- Opening 90 is known as the via bottom, where Cu 101 is exposed.
- the Cu surface may contain a Cu Oxide layer 120 due to Cu oxidation by the air, aqueous cleaning solution, partially oxygenated solvent cleaning solution, and other sources of oxygen such as the reactive feed gases used to form opening 90 in barrier/cap/etch stop layer 20 .
- the Cu Oxide layer 120 may contain carbon and other elements. Also present within the via opening may be a variable thickness of carbon residue 140 , which may contain H, F and other elements, may be polymeric or may be an amorphous carbon type material.
- the carbon residue 140 is commonly present at the via bottom although FIG. 2 shows the residue on the sidewalls.
- the residue 140 is removed by H atoms and other active species using a reducing H2 plasma or an oxidizing plasma, in a first cleaning step.
- Other common chemistries include one or more of the following gases: H2, O2, N2 and NH3.
- the Ar+ ions employed in the prior art typically have kinetic energies from about 100 eV to about 1000 eV are used to remove the Cu Oxide 120 in a second cleaning step.
- the ions cause damage to the exposed trench bottom 150 and to hardmask 40 , where the dielectric is directly exposed to Ar+ bombardment.
- Cu Oxide layer During removal of the Cu Oxide layer, Cu atoms are sputtered from the via bottom onto the via sidewalls 160 and onto the trench floor, where Cu on the trench floor is shown as 155 .
- the substrate 110 may be a semiconductor wafer or chip that can be composed of any silicon-containing semiconductor material, such as, for example, Si, SiGe, Si/SiGe, Si/SiO 2 /Si and the like.
- the substrate may be doped with dopants either n- or p-type depending on the desired device to be fabricated.
- the substrate may contain various isolation and/or device regions either formed in the substrate or on a surface thereof.
- the substrate may also contain metallic pads on the surface thereof.
- the substrate may be a circuit that includes CMOS devices therein.
- Suitable dielectrics for layer 30 are porous or dense inorganic materials including, but not limited to, silicon-containing materials such as compositions formed from one or more of Si, C, O, F and H, e.g., FSG, C doped oxide, F doped oxide, alloys of Si, C, O and H and the like.
- silicon-containing materials such as compositions formed from one or more of Si, C, O, F and H, e.g., FSG, C doped oxide, F doped oxide, alloys of Si, C, O and H and the like.
- PE CVD materials of the composition Si, C, O, and H include, but are not limited to, Black Diamond from Applied Materials, Coral from Novellus Systems and Aurora from ASM., all have k approximately 3.0, and include the range 2.8 to 3.2.
- SiCOH dielectrics containing porosity and having k from 2.7 down to 1.8 may be preferably used within this invention, including BDII and BDIII from Applied Materials, Aurora ULK and ELK from ASM, and other porous SiCOH films.
- a variety of spin applied films having the composition Si, C, O, H, such as, methylsilsesquioxanes, siloxanes and 5109, 5117, 5525, 5530 from Japan Synthetic Rubber (JSR), and Dendriglass may also be used.
- JSR Japan Synthetic Rubber
- the materials known as Orion and other materials from Trikon may also be used.
- first dielectric layer 30 on substrate 110 e.g., PE CVD or spin coating
- PECVD from a cyclic precursor and a second hydrocarbon precursor is one preferred method to make SiCOH dielectrics with k between 2 and 3, as disclosed in U.S. Pat. Nos. 6,312,793; 6,441,491; and 6,479,110 B2, the contents of which are incorporated herein by reference.
- the dielectric layer 30 may be a low-k organic materials such as the commercially available organic thermoset materials available from Dow Chemical Co. sold under the tradename SILKTM or polyarylene ethers and the like. Additionally, dielectric layer 30 may be porous-SiLKTM from Dow Chemical Company.
- Each of the present methods for via cleaning begins by placing the substrate containing elements 100 - 160 (see above) on a cooled wafer chuck at a temperature about ⁇ 200 to about 25° C. and then a condensable cleaning agent (CCA) is added to the process chamber for a period from about 1 second to about 100 seconds, a time sufficient to condense from 0.1 to 100 monolayers of CCA.
- CCA condensable cleaning agent
- the condensable cleaning agent is selected from reducing agents, molecular sources of fluorine, hydrogen sources and a source of both hydrogen and silicon.
- the reducing agents include metal based reducing agents, such as, metal hydride; mixed metal hydrides, such as, LiAlH.
- Examples of the source of both hydrogen and silicon include, but are not limited to, disilane; trisilane; tetrasilane and other condensable silanes.
- Molecular sources of fluorine include metal fluorides, such as, AlF3, TiF4, WF6, TaF6 and include inorganic fluorine compounds, such as, SF6, XeF2 and a mixture thereof; organic fluorine sources such as hexafluoroproplyeneoxide, hexafluorobenzene, and include fluorinated higher silanes.
- Mixtures of the above compounds may be especially effective as the CCA.
- the preferred CCA's include disilane, higher silanes such as trisilane, metal hydride compounds, metal fluoride compounds such as AlF3, TiF4, WF6, TaF6, inorganic fluorine compounds, such as, SF6 or XeF2, mixed fluorinated higher silanes, mixed metal hydrides and fluorides and the like.
- Metal based reducing agents such as LiAlH, is also preferred.
- the CCA is condensed on the cold wafer in the coating step, forming a thin layer in the via bottom (and roughly uniformly all across the wafer).
- the CCA is activated in the activation step, the carbon-based contamination is converted to volatile organic compounds and the Cu Oxide is removed from the Cu surfaces.
- the activation step is performed by He+ ion or He+ and H+/H2+ bombardment while the wafer remains cold and 1 process chamber is used.
- He, and optionally H2 are flowed into the process chamber at flow rates from about 1 sccm to about 10000 sccm with a preferable flow rate range of about 100 to about 500 sccm for each gas species.
- the activation step is performed by electron beam irradiation or UV irradiation while the wafer is cold and a single process chamber is used.
- an electron energy from about 0.5 eV to about 100 keV, a dose of about 10 to about 1,000 micro Curies/cm 2 and a time of about 1 second to about 10,000 seconds are employed.
- a typical condition for this treatment is an electron energy from about 1 to about 10 keV, a dose of about 50 to about 500 micro Curies/cm 2 .
- the activation step is performed by heating the wafer and a single process chamber is used. Specifically, the wafer is lifted off the cold chuck using lift pins and then heating lamps are used to heat the lifted wafer to a temperature of about 350° C. to about 400° C. and preferably from about 200° C. to about 450° C.
- the activation step is performed in a separate process module on a cluster tool.
- First the substrate containing elements 100 to 160 is placed on a cooled wafer chuck at a temperature of ⁇ 200° C. to about 25° C. in the process chamber described in the first embodiment and then, a condensable cleaning agent (CCA) is added to the process chamber for a period sufficient to condense (from about 1 to about 100 seconds), which is a time sufficient to condense from about 0.1 to about 100 monolayers of CCA.
- CCA condensable cleaning agent
- the substrate is moved to a second process chamber wherein the substrate is irradiated with He+ ion or He+ and H+/H2+ ions, with electron beam radiation, with UV radiation, with thermal energy, or with another energy source.
- the wafer may not be lifted off the chuck.
- the chuck may be heated, for example, resistively, with a heating fluid, or with heating lamps, to the desired temperature.
- the activation step is performed using a noble gas plasma and at least 1 grid is placed between the plasma and the substrate.
- the grid is biased positive in order to repel positive ions, so that the substrate containing the condensed layer of CCA is activated with VUV light and electrons from the plasma.
- a second grid is placed and biased negative to repel the electrons, so that only VUV light activates the CCA.
Landscapes
- Engineering & Computer Science (AREA)
- Physics & Mathematics (AREA)
- Condensed Matter Physics & Semiconductors (AREA)
- General Physics & Mathematics (AREA)
- Manufacturing & Machinery (AREA)
- Computer Hardware Design (AREA)
- Microelectronics & Electronic Packaging (AREA)
- Power Engineering (AREA)
- Internal Circuitry In Semiconductor Integrated Circuit Devices (AREA)
Priority Applications (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/665,584 US20050064701A1 (en) | 2003-09-19 | 2003-09-19 | Formation of low resistance via contacts in interconnect structures |
TW093126849A TWI339874B (en) | 2003-09-19 | 2004-09-06 | Formation of low resistance via contacts in interconnect structures |
CNB2004100771570A CN100345277C (zh) | 2003-09-19 | 2004-09-10 | 在互连结构中低电阻通道接触的形成 |
JP2004269168A JP2005094014A (ja) | 2003-09-19 | 2004-09-16 | 相互接続構造内での低抵抗バイア・コンタクトの形成 |
US11/182,445 US7378350B2 (en) | 2003-09-19 | 2005-07-15 | Formation of low resistance via contacts in interconnect structures |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/665,584 US20050064701A1 (en) | 2003-09-19 | 2003-09-19 | Formation of low resistance via contacts in interconnect structures |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/182,445 Division US7378350B2 (en) | 2003-09-19 | 2005-07-15 | Formation of low resistance via contacts in interconnect structures |
Publications (1)
Publication Number | Publication Date |
---|---|
US20050064701A1 true US20050064701A1 (en) | 2005-03-24 |
Family
ID=34312894
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/665,584 Abandoned US20050064701A1 (en) | 2003-09-19 | 2003-09-19 | Formation of low resistance via contacts in interconnect structures |
US11/182,445 Expired - Fee Related US7378350B2 (en) | 2003-09-19 | 2005-07-15 | Formation of low resistance via contacts in interconnect structures |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/182,445 Expired - Fee Related US7378350B2 (en) | 2003-09-19 | 2005-07-15 | Formation of low resistance via contacts in interconnect structures |
Country Status (4)
Country | Link |
---|---|
US (2) | US20050064701A1 (zh) |
JP (1) | JP2005094014A (zh) |
CN (1) | CN100345277C (zh) |
TW (1) | TWI339874B (zh) |
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20050184397A1 (en) * | 2004-02-19 | 2005-08-25 | International Business Machines Corporation | Structures and methods for intergration of ultralow-k dielectrics with improved reliability |
US20060081986A1 (en) * | 2004-10-14 | 2006-04-20 | International Business Machines Corporation | Modified via bottom structure for reliability enhancement |
US20060108320A1 (en) * | 2004-11-22 | 2006-05-25 | Lazovsky David E | Molecular self-assembly in substrate processing |
US20060189137A1 (en) * | 2005-02-24 | 2006-08-24 | International Business Machines Corporation | Method of forming damascene filament wires and the structure so formed |
US20070166992A1 (en) * | 2006-01-18 | 2007-07-19 | International Business Machines Corporation | Method for fabricating last level copper-to-c4 connection with interfacial cap structure |
US20070246792A1 (en) * | 2006-04-25 | 2007-10-25 | Chih-Chao Yang | Method for fabricating back end of the line structures with liner and seed materials |
US7745324B1 (en) | 2009-01-09 | 2010-06-29 | International Business Machines Corporation | Interconnect with recessed dielectric adjacent a noble metal cap |
US11171047B2 (en) | 2019-06-28 | 2021-11-09 | Applied Materials, Inc. | Fluorine-doped nitride films for improved high-k reliability |
Families Citing this family (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7253125B1 (en) | 2004-04-16 | 2007-08-07 | Novellus Systems, Inc. | Method to improve mechanical strength of low-k dielectric film using modulated UV exposure |
US9659769B1 (en) | 2004-10-22 | 2017-05-23 | Novellus Systems, Inc. | Tensile dielectric films using UV curing |
US8889233B1 (en) | 2005-04-26 | 2014-11-18 | Novellus Systems, Inc. | Method for reducing stress in porous dielectric films |
US8980769B1 (en) | 2005-04-26 | 2015-03-17 | Novellus Systems, Inc. | Multi-station sequential curing of dielectric films |
US8454750B1 (en) | 2005-04-26 | 2013-06-04 | Novellus Systems, Inc. | Multi-station sequential curing of dielectric films |
US20060251872A1 (en) * | 2005-05-05 | 2006-11-09 | Wang Jenn Y | Conductive barrier layer, especially an alloy of ruthenium and tantalum and sputter deposition thereof |
US7192878B2 (en) * | 2005-05-09 | 2007-03-20 | United Microelectronics Corp. | Method for removing post-etch residue from wafer surface |
US7695897B2 (en) * | 2006-05-08 | 2010-04-13 | International Business Machines Corporation | Structures and methods for low-k or ultra low-k interlayer dielectric pattern transfer |
US10037905B2 (en) * | 2009-11-12 | 2018-07-31 | Novellus Systems, Inc. | UV and reducing treatment for K recovery and surface clean in semiconductor processing |
US9050623B1 (en) | 2008-09-12 | 2015-06-09 | Novellus Systems, Inc. | Progressive UV cure |
TW201044462A (en) * | 2009-01-22 | 2010-12-16 | Tokyo Electron Ltd | A method for manufacturing semiconductor devices |
US8252699B2 (en) | 2010-11-22 | 2012-08-28 | Applied Materials, Inc. | Composite removable hardmask |
JP6040544B2 (ja) * | 2012-03-22 | 2016-12-07 | 日本電気株式会社 | 銅配線の表面処理方法及びその上に搭載する機能素子の製造方法 |
CN104143523A (zh) * | 2013-05-06 | 2014-11-12 | 中芯国际集成电路制造(上海)有限公司 | 一种半导体器件的制造方法 |
US9502255B2 (en) | 2014-10-17 | 2016-11-22 | Lam Research Corporation | Low-k damage repair and pore sealing agents with photosensitive end groups |
CN104392959A (zh) * | 2014-11-28 | 2015-03-04 | 上海集成电路研发中心有限公司 | 双大马士革结构的制造方法 |
US9847221B1 (en) | 2016-09-29 | 2017-12-19 | Lam Research Corporation | Low temperature formation of high quality silicon oxide films in semiconductor device manufacturing |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4884123A (en) * | 1987-02-19 | 1989-11-28 | Advanced Micro Devices, Inc. | Contact plug and interconnect employing a barrier lining and a backfilled conductor material |
US6312793B1 (en) * | 1999-05-26 | 2001-11-06 | International Business Machines Corporation | Multiphase low dielectric constant material |
US20010045651A1 (en) * | 2000-05-08 | 2001-11-29 | Tatsuyuki Saito | Semiconductor integrated circuit device and a method of manufacturing the same |
US6441491B1 (en) * | 2000-10-25 | 2002-08-27 | International Business Machines Corporation | Ultralow dielectric constant material as an intralevel or interlevel dielectric in a semiconductor device and electronic device containing the same |
Family Cites Families (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6153935A (en) * | 1999-09-30 | 2000-11-28 | International Business Machines Corporation | Dual etch stop/diffusion barrier for damascene interconnects |
US6337277B1 (en) * | 2000-06-28 | 2002-01-08 | Lam Research Corporation | Clean chemistry low-k organic polymer etch |
US6794292B2 (en) * | 2001-07-16 | 2004-09-21 | United Microelectronics Corp. | Extrusion-free wet cleaning process for copper-dual damascene structures |
CN1207771C (zh) * | 2001-12-24 | 2005-06-22 | 联华电子股份有限公司 | 使用氧化线层作为介电阻挡层的双镶嵌制程 |
US6848455B1 (en) * | 2002-04-22 | 2005-02-01 | Novellus Systems, Inc. | Method and apparatus for removing photoresist and post-etch residue from semiconductor substrates by in-situ generation of oxidizing species |
-
2003
- 2003-09-19 US US10/665,584 patent/US20050064701A1/en not_active Abandoned
-
2004
- 2004-09-06 TW TW093126849A patent/TWI339874B/zh not_active IP Right Cessation
- 2004-09-10 CN CNB2004100771570A patent/CN100345277C/zh not_active Expired - Fee Related
- 2004-09-16 JP JP2004269168A patent/JP2005094014A/ja active Pending
-
2005
- 2005-07-15 US US11/182,445 patent/US7378350B2/en not_active Expired - Fee Related
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4884123A (en) * | 1987-02-19 | 1989-11-28 | Advanced Micro Devices, Inc. | Contact plug and interconnect employing a barrier lining and a backfilled conductor material |
US6312793B1 (en) * | 1999-05-26 | 2001-11-06 | International Business Machines Corporation | Multiphase low dielectric constant material |
US6479110B2 (en) * | 1999-05-26 | 2002-11-12 | International Business Machines Corporation | Multiphase low dielectric constant material and method of deposition |
US20010045651A1 (en) * | 2000-05-08 | 2001-11-29 | Tatsuyuki Saito | Semiconductor integrated circuit device and a method of manufacturing the same |
US6441491B1 (en) * | 2000-10-25 | 2002-08-27 | International Business Machines Corporation | Ultralow dielectric constant material as an intralevel or interlevel dielectric in a semiconductor device and electronic device containing the same |
Cited By (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7088003B2 (en) * | 2004-02-19 | 2006-08-08 | International Business Machines Corporation | Structures and methods for integration of ultralow-k dielectrics with improved reliability |
US20050184397A1 (en) * | 2004-02-19 | 2005-08-25 | International Business Machines Corporation | Structures and methods for intergration of ultralow-k dielectrics with improved reliability |
US7282802B2 (en) * | 2004-10-14 | 2007-10-16 | International Business Machines Corporation | Modified via bottom structure for reliability enhancement |
US20060081986A1 (en) * | 2004-10-14 | 2006-04-20 | International Business Machines Corporation | Modified via bottom structure for reliability enhancement |
US20080220608A1 (en) * | 2004-10-14 | 2008-09-11 | International Business Machines Corporation | Modified via bottom structure for reliability enhancement |
US7906428B2 (en) | 2004-10-14 | 2011-03-15 | International Business Machines Corporation | Modified via bottom structure for reliability enhancement |
US20060108320A1 (en) * | 2004-11-22 | 2006-05-25 | Lazovsky David E | Molecular self-assembly in substrate processing |
US7309658B2 (en) * | 2004-11-22 | 2007-12-18 | Intermolecular, Inc. | Molecular self-assembly in substrate processing |
US20060189137A1 (en) * | 2005-02-24 | 2006-08-24 | International Business Machines Corporation | Method of forming damascene filament wires and the structure so formed |
US7915162B2 (en) | 2005-02-24 | 2011-03-29 | International Business Machines Corporation | Method of forming damascene filament wires |
US20070278624A1 (en) * | 2005-02-24 | 2007-12-06 | Anderson Brent A | Damascene filament wire structure |
US7309653B2 (en) * | 2005-02-24 | 2007-12-18 | International Business Machines Corporation | Method of forming damascene filament wires and the structure so formed |
US20080096384A1 (en) * | 2005-02-24 | 2008-04-24 | Anderson Brent A | Method of forming damascene filament wires |
US20070166992A1 (en) * | 2006-01-18 | 2007-07-19 | International Business Machines Corporation | Method for fabricating last level copper-to-c4 connection with interfacial cap structure |
US7863183B2 (en) * | 2006-01-18 | 2011-01-04 | International Business Machines Corporation | Method for fabricating last level copper-to-C4 connection with interfacial cap structure |
US20080242082A1 (en) * | 2006-04-25 | 2008-10-02 | Chih-Chao Yang | Method for fabricating back end of the line structures with liner and seed materials |
US7402883B2 (en) * | 2006-04-25 | 2008-07-22 | International Business Machines Corporation, Inc. | Back end of the line structures with liner and noble metal layer |
US20070246792A1 (en) * | 2006-04-25 | 2007-10-25 | Chih-Chao Yang | Method for fabricating back end of the line structures with liner and seed materials |
US8232195B2 (en) | 2006-04-25 | 2012-07-31 | International Business Machines Corporation | Method for fabricating back end of the line structures with liner and seed materials |
US7745324B1 (en) | 2009-01-09 | 2010-06-29 | International Business Machines Corporation | Interconnect with recessed dielectric adjacent a noble metal cap |
US20100176514A1 (en) * | 2009-01-09 | 2010-07-15 | International Business Machines Corporation | Interconnect with recessed dielectric adjacent a noble metal cap |
US11171047B2 (en) | 2019-06-28 | 2021-11-09 | Applied Materials, Inc. | Fluorine-doped nitride films for improved high-k reliability |
Also Published As
Publication number | Publication date |
---|---|
TW200512876A (en) | 2005-04-01 |
US7378350B2 (en) | 2008-05-27 |
CN100345277C (zh) | 2007-10-24 |
JP2005094014A (ja) | 2005-04-07 |
CN1624895A (zh) | 2005-06-08 |
US20050266681A1 (en) | 2005-12-01 |
TWI339874B (en) | 2011-04-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7378350B2 (en) | Formation of low resistance via contacts in interconnect structures | |
KR100516337B1 (ko) | 반도체 디바이스 및 그 제조 방법 | |
JP4328725B2 (ja) | 改良された信頼性を有する超低誘電率(k)誘電体を集積化する構造および方法 | |
US7737555B2 (en) | Semiconductor method having silicon-diffused metal wiring layer | |
US10854508B2 (en) | Interconnection structure and manufacturing method thereof | |
US7371461B2 (en) | Multilayer hardmask scheme for damage-free dual damascene processing of SiCOH dielectrics | |
US6797633B2 (en) | In-situ plasma ash/treatment after via etch of low-k films for poison-free dual damascene trench patterning | |
US7285853B2 (en) | Multilayer anti-reflective coating for semiconductor lithography and the method for forming the same | |
JP2010517325A (ja) | 窒化アルミニウムを使用することによる微細構造デバイス内の銅系メタライゼーション構造の信頼性向上 | |
US6720247B2 (en) | Pre-pattern surface modification for low-k dielectrics using A H2 plasma | |
US20080136037A1 (en) | Method for manufacturing semiconductor device and semiconductor device | |
US20090176367A1 (en) | OPTIMIZED SiCN CAPPING LAYER | |
US20140220777A1 (en) | Processing system for combined metal deposition and reflow anneal for forming interconnect structures | |
US20050026422A1 (en) | Method of forming an insulating structure having an insulating interlayer and a capping layer and method of forming a metal wiring structure using the same | |
US20060099802A1 (en) | Diffusion barrier for damascene structures | |
US20040152336A1 (en) | Semiconductor device and its manufacturing method | |
US20070155186A1 (en) | OPTIMIZED SiCN CAPPING LAYER | |
US20120276737A1 (en) | Post-etching treatment process for copper interconnecting wires | |
US20230041753A1 (en) | Semiconductor Device and Method of Manufacture | |
TW202348825A (zh) | 用於選擇性金屬沉積的選擇性抑制 | |
JP2006147895A (ja) | 半導体装置の製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: INTERNATIONAL BUSINESS MACHINES CORPORATION, NEW Y Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:DALTON, TIMOTHY J.;GATES, STEPHEN M.;REEL/FRAME:014551/0853 Effective date: 20030912 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |
|
AS | Assignment |
Owner name: GLOBALFOUNDRIES U.S. 2 LLC, NEW YORK Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:INTERNATIONAL BUSINESS MACHINES CORPORATION;REEL/FRAME:036550/0001 Effective date: 20150629 |
|
AS | Assignment |
Owner name: GLOBALFOUNDRIES INC., CAYMAN ISLANDS Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:GLOBALFOUNDRIES U.S. 2 LLC;GLOBALFOUNDRIES U.S. INC.;REEL/FRAME:036779/0001 Effective date: 20150910 |