US20040253520A1 - Polyimide matrix electrolyte and improved batteries therefrom - Google Patents
Polyimide matrix electrolyte and improved batteries therefrom Download PDFInfo
- Publication number
- US20040253520A1 US20040253520A1 US10/437,778 US43777803A US2004253520A1 US 20040253520 A1 US20040253520 A1 US 20040253520A1 US 43777803 A US43777803 A US 43777803A US 2004253520 A1 US2004253520 A1 US 2004253520A1
- Authority
- US
- United States
- Prior art keywords
- battery
- polyimide
- pme
- lithium
- cathode
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/05—Accumulators with non-aqueous electrolyte
- H01M10/056—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes
- H01M10/0564—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes the electrolyte being constituted of organic materials only
- H01M10/0565—Polymeric materials, e.g. gel-type or solid-type
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M6/00—Primary cells; Manufacture thereof
- H01M6/14—Cells with non-aqueous electrolyte
- H01M6/18—Cells with non-aqueous electrolyte with solid electrolyte
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/04—Construction or manufacture in general
- H01M10/0413—Large-sized flat cells or batteries for motive or stationary systems with plate-like electrodes
- H01M10/0418—Large-sized flat cells or batteries for motive or stationary systems with plate-like electrodes with bipolar electrodes
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/05—Accumulators with non-aqueous electrolyte
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/36—Selection of substances as active materials, active masses, active liquids
- H01M4/58—Selection of substances as active materials, active masses, active liquids of inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy; of polyanionic structures, e.g. phosphates, silicates or borates
- H01M4/581—Chalcogenides or intercalation compounds thereof
- H01M4/5815—Sulfides
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/62—Selection of inactive substances as ingredients for active masses, e.g. binders, fillers
- H01M4/621—Binders
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/62—Selection of inactive substances as ingredients for active masses, e.g. binders, fillers
- H01M4/621—Binders
- H01M4/622—Binders being polymers
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/411—Organic material
- H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/446—Composite material consisting of a mixture of organic and inorganic materials
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M6/00—Primary cells; Manufacture thereof
- H01M6/14—Cells with non-aqueous electrolyte
- H01M6/18—Cells with non-aqueous electrolyte with solid electrolyte
- H01M6/181—Cells with non-aqueous electrolyte with solid electrolyte with polymeric electrolytes
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M6/00—Primary cells; Manufacture thereof
- H01M6/42—Grouping of primary cells into batteries
- H01M6/46—Grouping of primary cells into batteries of flat cells
- H01M6/48—Grouping of primary cells into batteries of flat cells with bipolar electrodes
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/05—Accumulators with non-aqueous electrolyte
- H01M10/052—Li-accumulators
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/05—Accumulators with non-aqueous electrolyte
- H01M10/056—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes
- H01M10/0564—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes the electrolyte being constituted of organic materials only
- H01M10/0566—Liquid materials
- H01M10/0568—Liquid materials characterised by the solutes
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M2300/00—Electrolytes
- H01M2300/0017—Non-aqueous electrolytes
- H01M2300/0065—Solid electrolytes
- H01M2300/0082—Organic polymers
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M2300/00—Electrolytes
- H01M2300/0088—Composites
- H01M2300/0091—Composites in the form of mixtures
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/36—Selection of substances as active materials, active masses, active liquids
- H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
- H01M4/50—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese
- H01M4/505—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/36—Selection of substances as active materials, active masses, active liquids
- H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
- H01M4/52—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron
- H01M4/525—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/36—Selection of substances as active materials, active masses, active liquids
- H01M4/58—Selection of substances as active materials, active masses, active liquids of inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy; of polyanionic structures, e.g. phosphates, silicates or borates
- H01M4/5825—Oxygenated metallic salts or polyanionic structures, e.g. borates, phosphates, silicates, olivines
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M6/00—Primary cells; Manufacture thereof
- H01M6/14—Cells with non-aqueous electrolyte
- H01M6/16—Cells with non-aqueous electrolyte with organic electrolyte
- H01M6/162—Cells with non-aqueous electrolyte with organic electrolyte characterised by the electrolyte
- H01M6/166—Cells with non-aqueous electrolyte with organic electrolyte characterised by the electrolyte by the solute
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
- Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
- Y02E60/10—Energy storage using batteries
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
- Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
- Y02P70/50—Manufacturing or production processes characterised by the final manufactured product
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T29/00—Metal working
- Y10T29/49—Method of mechanical manufacture
- Y10T29/49002—Electrical device making
- Y10T29/49108—Electric battery cell making
Definitions
- the invention generally relates to polymer matrix electrolytes for use as an electrolyte or in primary and rechargeable lithium metal and lithium ion batteries.
- Lithium batteries have been introduced into the market because of their high energy densities. Lithium is atomic number three on the periodic table of elements, having the lightest atomic weight and highest energy density of any solid material. As a result, lithium is a preferred material for batteries, having very high energy density. Lithium batteries are also desirable because they have a high unit cell voltage of up to approximately 4.2 V, as compared to approximately 1.5 V for both Ni—Cd and Ni-MH cells.
- Lithium batteries can be either lithium ion batteries or lithium metal batteries.
- Lithium ion batteries intercalate lithium ions in a host material, such as graphite, to form the anode.
- lithium metal batteries use metallic lithium or lithium alloys for the anode.
- the electrolyte used in lithium batteries can be a liquid or a polymer based electrolyte.
- Lithium batteries including liquid electrolytes have been on the market for several years.
- Lithium ion rechargeable batteries having liquid electrolytes are currently mass produced for applications such as notebook computers, camcorders and cellular telephones.
- lithium batteries having liquid electrolyte technology have several major drawbacks. These drawbacks relate to cost and safety and stem from use of a liquid electrolyte.
- the liquid electrolyte generally requires packaging in rigid hermetically sealed metal “cans” which can reduce energy density.
- lithium ion rechargeable batteries and lithium-metal primary batteries having liquid electrolytes are designed to vent automatically when certain abuse conditions exist, such as a substantial increase in internal pressure which can be caused by internal or external overheating. If the cell is not vented under extreme pressure, it can explode because the liquid electrolyte used in liquid Li cells is extremely flammable.
- Lithium batteries having solid polymer electrolytes represent an evolving alternative to lithium batteries having liquid electrolytes.
- Solid polymer electrodes are generally gel type electrolytes which trap solvent and salt in pores of the polymer to provide a medium for ionic conduction.
- Typical polymer electrolytes comprise polyethylene oxide (PEO), polyether based polymers and other polymers which are configured as gels, such as polyacrylonitrile (PAN), polymethylmethacrylate (PMMA) and polyvinylidine fluoride (PVDF).
- PEO polyethylene oxide
- PAN polyacrylonitrile
- PMMA polymethylmethacrylate
- PVDF polyvinylidine fluoride
- the polymer electrolyte generally functions as a separator, being interposed between the cathode and anode films of the battery.
- a lithium battery having a polymer electrolyte is intrinsically safer than a lithium battery having a liquid electrolyte.
- polymer electrolytes eliminate the need for venting and package pressure control which are generally required for operation of lithium batteries having liquid electrolytes.
- polymer electrolytes make it possible to use a soft outer case such as a metal plastic laminate bag, resulting in improvement in weight and thickness, when compared to liquid electrolyte can-type Li batteries.
- Each cathode, separator and anode combination forms a unit battery cell.
- Practical lithium batteries such as those having polymer electrolytes, are generally prepared by stacking a number of battery cells in series and/or parallel to achieve desired battery capacity.
- Lithium metal polymer (LMP) rechargeable batteries offer improved performance as compared to Li ion batteries, particularly higher capacity.
- LMP batteries result from the lamination/assembly of three types of main thin films: a film of positive electrode comprising a mixture of a polymer and an electrochemically active material such as lithium vanadium oxide, an electrolyte film separator made of a polymer and a lithium salt, and a negative electrode film comprising metallic lithium or a lithium alloy.
- a known limitation of LMP batteries, especially for automotive applications is that the polymers presently used provide their peak ionic conductivity at elevated temperatures. These LMP batteries must therefore be heated to produce peak power output.
- Li metal and lithium alloy batteries A problem with Li metal and lithium alloy batteries is that lithium, in its metallic form, is highly reactive. As such, it presents unique difficulties in rechargeable configurations. Repeated charge/discharge cycles can cause a build-up of surface irregularities on the lithium metal electrode. External pressure is generally necessary for prolonged performance of a lithium metal battery.
- gel polymer electrolytes represent an improvement over liquid electrolytes in terms of safety and manufacturability
- safety issues remain because gel polymers trap solvent on its pores and under extreme conditions (e.g. heat and/or pressure) can still escape and cause injury.
- gel polymer electrolytes cannot generally operate over a broad temperature range because the gel generally freezes at low temperatures and reacts with other battery components or melts at elevated temperatures.
- electrode instability and resulting poor cycling characteristics, particularly for metallic lithium containing anodes limits possible applications for such batteries formed with gel polymer electrolytes.
- electrolytes disclosed by the '672 patent can be used to form a polymer electrolyte and a battery therefrom which provides an improved operating temperature range, ease of manufacture, and improved safety over batteries formed from conventional gel polymer electrolytes, it would be helpful if the electrolyte stability over temperature and pressure as well as the ionic conductivity could be improved.
- a battery includes an anode, a cathode, and a polymer matrix electrolyte (PME) separator disposed between the anode and the cathode.
- the PME separator includes a polyimide, at least one lithium salt in a concentration of at least 0.5 moles of lithium per mole of imide ring provided by the polyimide and at least one solvent, all intermixed.
- the PME is generally homogeneous as evidenced by its high level of optical clarity. As used herein, when the PME is referred to as being substantially optically clear.
- substantially optically clear refers to the PME being at least 90% clear (transmissive), preferably at least 95%, and most preferably being at least 99% clear as measured by a standard turbidity measurement, transmitting through a normalized 1 mil film using 540 nm light.
- the battery can be a lithium ion, lithium metal battery or a lithium metal alloy battery.
- a repeat unit weight per imide ring of the polyimide can be no more than 350, no more than 300, or no more than 250.
- the polyimide is preferably soluble at 25° C. in at least one solvent selected from the group consisting of N-methylpyrrolidinone (NMP), dimethylacetamide (DMAc) and dimethylformamide (DMF).
- the ionic conductivity of the polymer electrolyte at 25° C. is at least 1 ⁇ 10 ⁇ 4 S/cm, and preferable at least 3 ⁇ 10 ⁇ 4 S/cm.
- the Li salt can be selected from a variety of salts including LiCl, LiBr, Lil, LiClO 4 , LiBF 4 , LiAsF 6 , LiPF 6 , LiCF 3 SO 3 , LiBOB, LiN(CF 3 SO 2 ) 2 , and lithium bis(trifluorosulfonyl)imide (LiTFSI).
- the cathode can include an ion conducting polymeric binder intermixed with an intercalation material.
- the polymeric binder can include at least one polyimide, such as the polyimide used in the PME.
- the cathode can include an electrochemically active material selected from the group consisting of LiFePO 4 , Li x Ni y CO z O 2 , LiV x O y , Li x Mn y O z , LiV x O y , Li x Mn y O z , LiCoO 2 , LiNiO 2 and LiTiS 2 ,
- the PME permits the battery to be highly stable over temperature and pressure extremes.
- the battery can demonstrate no significant change in open circuit voltage (OCV) and capacity following heating at 125° C. for at least 5 minutes while under a pressure of at least 200 psi, or more preferably no significant change in OCV and capacity following heating at 140° C. for at least 10 minutes while under a pressure of at least 250 psi.
- OCV open circuit voltage
- the battery can be a bicell.
- the cathode having a PME coating thereon is preferably folded over to sandwich the anode.
- the salt complexes with the polyimide.
- Evidence for complexing is shown by the salt and polyimide not providing any absorption peaks between 1630 and 1690 cm ⁇ 1 , while the PME formed from the mixture provides at least one absorption between about 1630 and 1690 cm ⁇ 1 .
- the battery can be a packaged battery, wherein the package comprises packaging material surrounding the battery, the packaging material being laminated to all exterior surfaces of the battery.
- a frame is included in the packaging process, the frame having an opening to accommodate the battery therein, where the battery is disposed within the opening and the packaging material is disposed thereon.
- the packaged battery can provide a thickness uniformity throughout within ⁇ 1 mil.
- a method for forming a battery includes the steps of providing a cathode layer disposed on a cathode current collector, overcoating a mixture of polyimide, lithium salt and solvent on the cathode layer, drying the mixture to remove at least a portion of the solvent, wherein an electrolyte separator bonded to the cathode (electrolyte/cathode) is formed. An anode layer is then disposed on the electrolyte/cathode.
- the electrolyte separator is preferably a polymer matrix electrolyte (PME), wherein the polyimide, lithium salt and solvent are intermixed, the lithium salt in a concentration of at least 0.5 moles of lithium per mole of imide ring provided by the polyimide, the PME being substantially optically clear.
- the anode is preferably a lithium metal comprising anode, although it can be a Li ion anode.
- the battery can be formed by laminating only two layers, a first layer being the PME disposed on the cathode and a second layer being the anode.
- the PME coated cathode is then laminated with the anode to form the cell.
- the method can include the step of folding a PME coated cathode over the anode, wherein a bicell is formed.
- FIG. 1( a )-( m ) illustrates the repeat unit structure for several suitable polyimides, according to an embodiment of the invention.
- FIG. 2 is a table illustrating ionic conductivity and the resulting film composition at 20.5° C. for a PME comprising the polyimide shown in FIG. 1( m ), LiTFSi salt (2.2 ⁇ ) and the solvent gamma butyrolactone (GBL), according to an embodiment of the invention.
- FIG. 3( a )-( d ) are plots of the ionic conductivity of a PME comprising the polyimide shown in FIG. 1( m ) and the lithium salt LiTFSi (2.2 ⁇ ) as a function of solvent load and temperature for the solvents TMS, PC, GBL, and NMP, respectively.
- FIG. 4 is a plot of ionic conductivity of a PME comprising the polyimide shown in FIG. 1( m ) and a lithium salt (LiTFSi; 2.2 ⁇ ) as a function solvent/polyimide ratio at 20 C, where the solvent is GBL.
- LiTFSi lithium salt
- FIG. 5( a ) is FTIR data for an exemplary polyimide without the addition of a Li salt or any solvent.
- FIG. 5( b ) is FTIR data for an exemplary Li salt.
- FIG. 5( c ) is FTIR data for the exemplary polyimide whose FTIR data is shown in of FIG. 5( a ) intermixed with and the exemplary Li salt whose FTIR data is shown in FIG. 5( b ) evidencing the emergence of a doublet absorption peak at between about 1630 cm ⁇ 1 and 1690 cm ⁇ 1 .
- FIG. 6 is a table which includes dianhydrides and aromatic diamines that can be used for making polyimides presented herein.
- FIG. 7 shows an assembly process for forming an electrochemical bicell which is ready for packaging, according to an embodiment of the invention.
- FIG. 8 shows an assembly process for packaging the electrochemical bicell produced by the assembly process shown in FIG. 7.
- FIG. 9( a ) is a SEM evidencing a defect free PME.
- FIG. 9( b ) is a SEM showing a smooth and uniform interface between a PME disposed on a lithium vanadium oxide (LVO) comprising cathode layer.
- LVO lithium vanadium oxide
- FIG. 10 shows the charge/discharge profile of a typical cell according to the invention, the cell including a lithium vanadium oxide cathode, a Li metal anode and a PME separator, according to an embodiment of the invention.
- the invention describes a substantially optically clear electrolyte separator matrix which includes a polyimide, a lithium salt and some solvent.
- the lithium salt is in a concentration of at least 0.5 moles of lithium per mole of imide ring provided by the polyimide.
- the solvent is generally a low molecular weight, low viscosity liquid which swells the polyimide at low concentration and at a sufficiently high concentration allows the polyimide, salt and the solvent to become homogeneously mixed.
- the substantially optically clear electrolyte separator matrix is referred to as a “polymer matrix electrolyte” or PME.
- the PME can be used for batteries, supercapacitors and other applications.
- the high level of optical clarity provided by the PME evidences the homogeneity of the PME comprising its respective components (polymer, salt and the solvent) as any significant phase separation would reduce optical clarity.
- the PME can be used to form both lithium ion and lithium metal containing batteries. Unlike gel polymer electrolytes, once the PME is formed, there is generally no free solvent or identifiable pores. For example, using a SEM providing a 50 A resolution, no pores in the PME can be identified. Instead, the solvent is integrated with the polymer and the lithium salt in a homogeneous and substantially optically clear matrix. In addition, unlike conventional gel polymers where the polymer only provides mechanical support, the polymer together with the salt and the solvent participate in ionic conduction.
- the PME provides high current carrying capacity, cycling stability and maintains this performance level across a wide temperature range, such as at least from ⁇ 40° C. to 100° C.
- the PME can withstand high temperatures and pressures with small changes in open circuit voltage and capacity, such as the conditions generally used in the hot lamination processes used in credit card manufacturing, or even the more rigorous conditions associate with a typical injection molding process.
- hot lamination processes used in credit card assembly generally utilize a temperature of about 115-150° C. for 5 to 15 minutes under a pressure of about 200-250 psi.
- OCV open circuit voltage
- the phrase “no significant change in OCV and capacity” following a lamination or molding process refers to a battery including the PME which demonstrates an OCV and capacity which shifts less than 15%, preferably less than 10%, and more preferably less than a 5% following the lamination or molding process.
- a lithium metal battery having a lithium vanadium oxide comprising cathode was found to provide a shift in OCV of 1.4% and a commensurately small reduction in capacity following a lamination process comprising a temperature of 140 C for 15 minutes under a pressure of 220 psi.
- batteries formed using the PME are quite flexible and can exceed ISO standards ISO/IEC 10373 and 14443.
- PME based batteries are particularly well suited for use inside credit cards, smart labels, and other small devices which require high temperature/high pressure lamination processing and can benefit from an on board power supply.
- the high level of battery stability to both mechanical and thermal stresses provided by the PME permits batteries according to the invention to withstand harsh credit card processing conditions.
- the PME is generally based on one or more polyimides, which unlike other polymer-based electrolytes, participate in ionic conductivity through the presence of imide rings and other polar groups.
- Other polymer types which include highly polar groups having functional groups that can complex with lithium salts and participate in ionic conduction include polybenzimidazoles and polyamide-imides. Accordingly, these polymer types may also include species useful in forming a PME.
- Polyimides are reaction products of a condensation reaction between diamines and dianhydrides to initially form a poly (amic-acid) intermediate.
- Either or both the diamine and dianhydride reagent can be mixture of diamine or dianhydride species.
- the poly amic-acid intermediate is then converted to a fully imidized polyimide.
- polyimide formed depend on the selection of the particular diamines and dianhydride monomers.
- Polyimides are generally known to provide high thermal stability, chemical resistance and high glass transition temperatures, such as 200° C. to more than 400° C.
- the current invention includes the identification of polyimides distinct from those disclosed in the '672 patent and has found the addition of solvent to some of these distinct polyimides can result in the formation of a PME.
- Some of the polyimides identified herein provide represent newly synthesized polymers.
- the polymers disclosed herein form a substantially homogeneous matrix material (PME) when combined with an appropriate concentration of salt to achieve a practical ionic conductivity level and the solvent.
- PME substantially homogeneous matrix material
- the homogeneity of the PME is evidenced by the high level of optical clarity provided which is shown in Example 1.
- the electrolytes disclosed in '672 are non-homogeneous mixture, as evidenced by their opaqueness also shown in Example 1 which is indicative of phase separation of the respective components.
- the Inventors have identified and synthesized improved polyimides for use in forming PMEs by qualitatively relating certain polymer parameters to ionic conductivity. Imide ring density is believed to explain why polyimide films, when loaded with lithium salt, show significant ionic conductivity, even in the absence of solvent. Repeat unit weight per imide ring is one measure of imide ring density and is calculated by dividing the molecular weight of the entire repeat unit of the respective polyimides by the number of imide rings within the respective repeat units.
- Imide rings may provide the equivalent of a high dielectric constant to materials because of the high electron density provided by the rings. Accordingly, it is believed that the interaction between the imide rings and the lithium ion is a factor in determining the ionic conductivity of a PME.
- improved polyimides for use as PMEs can be generally selected for further consideration by first calculating the number of imide rings (and to a lesser degree other highly polar groups, such as sulfone, carbonyl and cyanide) per molecular repeat unit in a given polyimide. The more imide ring function present per unit weight, the higher the average dielectric strength equivalence of the polymer. Higher equivalent dielectric strength is believed to generally lead to improved salt interaction, which can improve the ionic conductivity of the PME.
- repeat unit weight per imide ring a quantity roughly inverse to imide ring density referred to as repeat unit weight per imide ring can be calculated to also compare the relative concentration of imide rings in polyimides.
- repeat weight per imide ring decreases, imide rings become an increasingly greater contributor to the repeat unit as a whole.
- the equivalent dielectric constant and ionic conductivity of the polyimide generally increase.
- Polyimides which provide high helium permeability may generally produce higher ionic conductivity and thus form better PMEs.
- the measured He permeability of most polyimides according to the invention has been found to be at least 20 barrers.
- the He permeability can be at least 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75 or 80 barrers, or more.
- Helium permeability may be measured in the following suggested manner.
- the gas permeability (GP) of a gas component through a given film having a thickness (I) and area (A) can be determined by applying a pressure (p) across the film which is equal to the upstream pressure minus the downstream pressure of the gas component and measuring the resulting steady state rate of gas flow (f) permeating through the film at STP.
- Preferred units for GP is (cm 2 )(sec) ⁇ 1 (cmHg), where 1 barrer is defined as the GP multiplied by 10 10 .
- the maximum ionic conductivity of the PME generally occurs when the polyimide/salt/solvent combination creates a completely homogenous, clear matrix. Any phase separation is expected to reduce the ionic conductivity values because phase separation would increase the tortuosity within the PME.
- the maximum electrolyte conductivity of the PME at a given temperature generally occurs when the polyimide/salt/solvent matrix has a ratio within a specified range.
- the optimum salt concentration is generally in the range of 0.5 to 2.0 moles Li per mole of imide ring for a polyimide. Too little salt generally does not provide a sufficient number of ions to contribute to the charge transfer. Too much salt generally leads to phase instability and possible precipitation of the polyimide and resulting loss of homogeneity which can be verified by a loss in optical clarity.
- the solvent is believed to play the role of a swelling agent for the polymer to move the backbone chains slightly apart and therefore enables greater ionic diffusion coefficients.
- the solvent also acts as a solvation carrier for the ions.
- the solvent is chosen to also be stable within the limitations of the type of battery chosen. For example, for a lithium ion type battery the solvent must be stable up to the reduction potential of lithium metal.
- the amount of solvent can be optimized depending upon the either the conductivity desired or the softening point of the matrix at some required temperature.
- Solvents can be selected from a group of solvents including gamma butyrolactone (GBL), propylene carbonate, N-methylpyrrolidinone (NMP), tetrahydrothiophen-1,1-dioxide (TMS), polycarbonate (PC) and dimethyl formamide (DM F).
- GBL gamma butyrolactone
- NMP N-methylpyrrolidinone
- TMS tetrahydrothiophen-1,1-dioxide
- PC polycarbonate
- DM F dimethyl formamide
- FIG. 1( a )-( m ) illustrates the repeat unit structure for several polyimides, according to an embodiment of the invention.
- the repeat unit for a polymer referred to as Polyimide A is shown in FIG. 1( a ).
- This polyimide can be formed by reacting PMDA [89-32-7] with TMMDA [4037-98-7].
- This high molecular weight polymer is soluble in NMP for a limited number of hours thus a lithium salt containing electrolyte could not be produced.
- Polyimide B The repeat unit for the polymer referred herein to as Polyimide B is shown in FIG. 1( b ).
- This polyimide can be formed by reacting 90 mole % PMDA [89-32-7], 10 mole % 6FDA [1107-00-2] dianhydrides and the diamine TMMDA [4037-98-7].
- the polymer formed was soluble indefinitely in NMP at 20% by weight.
- Polyimide C The repeat unit for the polymer referred herein to as Polyimide C is shown in FIG. 1( c ).
- This polyimide can be formed by reacting 85.7 mole % PMDA [89-32-7], 14.3 mole % 6FDA [1107-00-2] and TMMDA [4037-98-7].
- the polymer formed was soluble indefinitely in NMP at 20% by weight.
- Polyimide D The repeat unit for the polymer referred herein to as Polyimide D is shown in FIG. 1( d ).
- This polyimide can be formed by reacting 80 mole % PMDA [89-32-7], 20 mole % PSDA [2540-99-0] and TMMDA [4037-98-7]. The polymer formed was soluble indefinitely in NMP at 20% by weight.
- Polyimide E The repeat unit for the polymer referred herein to as Polyimide E is shown in FIG. 1( e ).
- This polyimide can be formed by reacting BPDA [2421-28-5] and 3,6 diaminodurene [3102-87-2]. The polymer formed was soluble indefinitely in NMP at 20% by weight.
- Polyimide F The repeat unit for the polymer referred herein to as Polyimide F is shown in FIG. 1( f ).
- This polyimide can be formed by reacting 6FDA [1107-00-2] and 3,6-diaminodurene [3102-87-2].
- the polymer formed was soluble indefinitely in NMP at 20% by weight and is also soluble in acetone, GBL, DMAc, and DMF.
- Polyimide G The repeat unit for the polymer referred herein to as Polyimide G is shown in FIG. 1( g ).
- This polyimide can be formed by reacting PSDA [2540-99-0] and TMMDA [4037-98-7].
- the polymer formed was soluble indefinitely in NMP at 20% by weight and is soluble in GBL.
- Polyimide H The repeat unit for the polymer referred herein to as Polyimide H is shown in FIG. 1( h ).
- This polyimide can be formed by reacting 6FDA [1107-00-2] and TMMDA [4037-98-7].
- the polymer formed was soluble indefinitely in NMP at 20% by weight and is soluble in acetone, GBL, DMAc, and DMF.
- Polyimide I The repeat unit for the polymer referred herein to as Polyimide I is shown in FIG. 1( i ).
- This polyimide can be formed by reacting BPDA [2421-28-5] and 4,4′-(9-fluorenylidene)dianiline [15499-84-0].
- the polymer formed was soluble indefinitely in NMP at 20% by weight.
- Polyimide J The repeat unit for the polymer referred herein to as Polyimide J is shown in FIG. 1( j ).
- This polyimide can be formed by reacting PMDA [89-32-7], 33.3 mole % TMPDA [22657-64-3] and 66.7 mole % TMMDA [4037-98-7].
- the polymer formed was soluble indefinitely in NMP at 20% by weight.
- Polyimide K The repeat unit for the polymer referred herein to as Polyimide K is shown in FIG. 1( k ).
- This polyimide can be formed by reacting PMDA [89-32-7] and DAMs [3102-70-3]. The polymer formed was soluble only for a short time in NMP.
- Polyimide L The repeat unit for the polymer referred to herein as Polyimide L is shown in FIG. 1( l ).
- This polyimide can be formed by reacting PMDA [89-32-7] and 4-isopropyl-m-phenylenediamine [14235-45-1].
- the polymer formed was soluble indefinitely in NMP at 20% by weight.
- Polyimide M The repeat unit for the polymer referred herein to as Polyimide M is shown in FIG. 1( m ).
- This polyimide can be formed by reacting PMDA [89-32-7], 33.3 mole % DAMs [3102-70-2] and 66.7 mole % TMMDA [4037-98-7].
- the polymer formed was soluble indefinitely in NMP at 20% by weight.
- the PME includes at least one lithium salt.
- High PME ion conductivities are generally achieved using a high salt content, such as from about 0.5 to 2.0 moles of Li per mole of imide ring for polyimide polymers.
- the concentration of lithium salt can be 0.6, 0.7, 0.8, 0.9, 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.3, 2.4 or 2.5 moles Li per mole of imide ring of the polyimide.
- Salt concentrations are also described herein as a ratio of the weight of the salt to weight of the polymer (e.g. polyimide) excluding the salt.
- a 1 ⁇ concentration corresponds to an equal amount of salt and polymer
- a 2 ⁇ salt concentration corresponds to twice the salt concentration as compared to the polymer concentration.
- the lithium salt can generally be any lithium salt known in the art.
- lithium salts are chosen from LiCl, LiBr, Lil, Li(ClO 4 ), Li(BF 4 ), Li(PF 6 ), Li(AsF 6 ), Li(CH 3 CO 2 ), Li(CF 3 SO 3 ), Li(CF 3 SO 2 ) 2 N, Li(CF 3 SO 2 ) 3 , Li(CF 3 CO 2 ), Li(B(C 6 H 5 ) 4 , Li(SCN), and Li(NO 3 ), lithium bis(trifluorosulfonyl)imide (LiTFSI), LiBOB, and LiSCN.
- the salt is either Li(PF 6 ) or LiTFSi.
- Polyimide structures other than the exemplary structures shown in FIG. 1 can be good candidates for use in forming a PME matrix.
- Characteristics that a good PI should display, such as solubility in NMP (or other suitable solvent) to at least 20 wt % and a low repeat unit weight per imide ring can be a first criteria.
- solubility of the PI itself or the solution stability when combined with a high concentration of a lithium salt applicable for battery applications is not easily predictable.
- Behavior in solution can not generally be ascertained by simply looking at the polymer repeat unit structure. However, it can be determined from looking at the structure whether the polymer will possibly be crystalline, or whether it would have a high or low relative density in the solid phase.
- the polyimides are preferably non-crystalline, low-density repeat structures because they would be most likely to be very soluble. However, changing a single side group from a methyl to an ethyl can cause the properties of the PI to be changed from useful to of no use.
- a suggested meaningful screening procedure for alternative polyimides for battery applications is to take a polyimide that is known to have a good solubility in the solvent itself and then try to introduce the lithium salt at 0.5 mole Li per imide ring or more and see if (i) the resulting PI/salt/solvent solution is clear and homogenous for a few hours and (ii) the film cast from that solution remains substantially clear when most of the solvent (e.g. 95%) has been evaporated.
- FIG. 2 is a table illustrating the ionic conductivity at 20.5° C. and the corresponding film composition for a polyimide based PME comprising the polyimide shown in FIG. 1( m ), LiTFSi salt (2.2 ⁇ ) and the solvent GBL, according to an embodiment of the invention.
- Room temperature ionic conductivity values for PME films were calculated from measured impedance using a complex impedance analyzer. Measurements using the impedance analyzer were made in the frequency range of 1 MHz to 0.1 Hz. A value for the resistance of the film, R, was taken as the intercept with the real axis of a Nyquist plot, or by an extrapolation of the high frequency portion of the response curve to the real axis. Measurements were also made on an LCR meter at a fixed frequency of 10 kHz where the resistance values were read directly. The ionic conductivity was calculated using the formula:
- t is film thickness in microns and R is the measured film resistance in Ohms.
- the maximum ionic conductivity at 20.5° C. was about 1 ⁇ 10 ⁇ 4 S/cm for a 1 ⁇ salt concentration and 4 ⁇ 10 ⁇ 4 S/cm for a 2.2 ⁇ concentration, where the PME film comprised 37.9% GBL.
- the lower table portion shown in FIG. 2 shows the minimum solvent level required to provide a conductivity of 1 ⁇ 10 ⁇ 4 S/cm for 1.0, 1.4, 1.8 and 2.2 ⁇ salt concentrations.
- the range of solvent in FIG. 2 is expressed as the solvent/PI ratio and runs from about 1 to about 2.
- the lower value is where one arbitrarily defines a conductivity as being high enough for a given application, such as 1.0E-4 S/cm.
- the maximum conductivity was found to occur between a solvent/PI ratio of 1.5 to 2.0 depending upon the salt concentration.
- the upper solvent/PI limit near 2 is controlled by the mechanical properties of the PME.
- the PME film becomes very soft and may not be usable over an extended temperature range as a separator for a battery.
- the solvent is chosen to be moderately stable against lithium metal, high boiling (>150 C), capable of dissolving the chosen salt and swelling the PI, and finally it should have a low viscosity which promotes a high conductivity for the salt/solvent combination by itself, as well as for the PME.
- a PI species is selected which is soluble in an appropriate solvent, such as NMP or GBL. All the polyimides shown in FIG. 1 except the polyimide shown in FIG. 1( k ), are soluble in NMP.
- a desired lithium salt is selected and an initial concentration is selected, such as a mass ratio that gives one lithium ion per imide ring provided by the selected PI.
- the solvent concentration can then be varied from a solvent/PI ratio of about 0.8 to 2.0 while measuring the ionic conductivity for several solvent/PI data points in between. This can be repeated at salt concentrations both higher and lower. There are generally several combinations of PI/salt/solvent by mass that will give similar ionic conductivities, such as within a factor of two.
- FIG. 3( a )-( d ) are plots of the ionic conductivity of a PME comprising the polyimide shown in FIG. 1( m ) and the lithium salt LiTFSi (2.2 ⁇ ) as a function of solvent load and temperature for the solvents TMS, PC, GBL, and NMP, respectively. These curves generally do not show a clear conductivity maximum because the salt content was 2.2 ⁇ , and as a result, the amount of solvent needed to provide the maximum ionic conductivity was large and generally impractical.
- FIG. 4 is a plot of ionic conductivity of a PME comprising the polyimide shown in FIG. 1( m ) the lithium salt (LiTFSi; 2.2 ⁇ ) as a function solvent/polyimide ratio at 20° C., where the solvent is GBL.
- the ionic conductivity is seen to increase for increasing solvent to polyimide ratio up to about a GBL/polyimide ratio of about 1.5, where the ionic conductivity levels off at a value of about 7 ⁇ 10 ⁇ 4 S/cm.
- the ionic conductivity of PMEs based on polyimides is believed to be related to the degree the polyimides associate with alkali salts, particularly Li salts. This association is likely related to the formation of complexes between polar groups (e.g. imide and benzene) of the polyimide and the salt. Evidence for this association can be found by measuring the absorption frequencies displayed by the polymer when intermixed with the salt and comparing this data to the absorption frequencies displayed by the polyimide and the salt by themselves.
- polar groups e.g. imide and benzene
- characteristic absorption frequencies are believed to be related to the imide rings and benzene rings that comprise the polyimide backbone. These absorption peaks are at about 1778 cm ⁇ 1 and 1721 cm ⁇ 1 for the imide ring and 730 cm ⁇ 1 for the benzene ring. Common Li salts, including LiPF 6 , LiBOB, Lil and LiTFSi do not show absorption at these frequencies, nor any absorption peaks between about 1630 and 1690 cm ⁇ 1 .
- the resulting polyimide/salt film show the emergence of a very strong doublet with a first peak at about 1672 cm ⁇ 1 and a second peak at about 1640 cm ⁇ 1 .
- the first absorption frequency is present when a significant concentration of salt is in the polyimide film, such as at least 33 wt. %, but does not change significantly with increasing salt concentration.
- this peak can be used to indicate the interaction, provided a sufficient salt concentration is present.
- the magnitude of the second peak is nearly proportional to the ratio of the Li ion concentration to the imide rings and can be used to assess the extent of the interaction between the polyimide and the salt.
- Polymers other than polyimides which provide a high relative local electron density (e.g. comparable to electron density adjacent to imide rings in polyimides) and the potential for charge separation due to multiple bond conjugation may form a polymer/salt complex and display characteristic absorption peaks based on the complex formed, provided they are soluble.
- absorption spectroscopy such as FTIR can be used to identify these soluble non-polyimide polymers which show evidence of complex formation for use as a PME.
- FIG. 5( a ) is FTIR data for an exemplary polyimide, the polyimide shown in FIG. 1( c ), without the addition of a Li salt or any solvent. Absorption peaks related to the imide rings are shown at about 1778 cm ⁇ 1 and 1721 cm ⁇ 1 and at 730 cm ⁇ 1 for the benzene ring. This polyimide does not show any detectable absorption peaks between about 1630 and 1690 cm ⁇ 1 .
- FIG. 5( b ) shows an FTIR for LiBOB confirming the absence of infrared absorption between about 1630 and 1690 cm ⁇ 1 .
- FIG. 5( c ) shows the FTIR the polyimide shown in FIG. 1( c ) combined with LiBOB.
- the resulting polyimide electrolyte shows a very strong doublet with a first peak at about 1672 cm ⁇ 1 and a second peak at 1640 cm ⁇ 1 .
- FTIR measurements taken from exemplary PMEs according to the invention provide evidence that the lithium salt forms a complex with the imide rings of the polyimide. This is likely one of the main reasons why the polyimide/lithium salt combination, in a dry film, has no apparent structure or crystallinity. The lack of crystallinity can be shown by a flat DCS trace. This evidence has also been found of an interaction between the lithium salt and the polyimide as the PME film is optically clear whether as a free standing film or as an overcoated film.
- the invention can be used in a wide variety of applications. Both primary and rechargeable batteries formed from either lithium ion or lithium metal anodes can be formed using the invention.
- a lithium metal battery having a PME is formed.
- the anode can be formed from lithium metal or a lithium alloy.
- Lithium alloys can include lithium-aluminum, lithium-aluminum-silicon, lithium-aluminum-cadmium, lithium-aluminum-bismuth, lithium-aluminum-tin or lithium-titanium oxide.
- the lithium content in these lithium alloys may be up to 99.98 wt. %.
- the overall lithium content in the anode is based on the required capacity of the battery.
- the cathode material for the lithium metal battery can comprise an ionic conductive polymer binder, such as the polyimides described herein, an electronically conductive material (e.g. graphite), and an electrochemically active material.
- the electrochemically active material is preferably selected from MnO 2 , the various lithium vanadium oxides (Li x V y O z ), lithium transition metal oxides, such as Li x Mn y O z (e.g. LiMn 2 O 4 ), LiCoO 2 , LiNiO 2 , Li 4 Ti 5 O 12 , LiV x O y , and other materials such as metal sulfides (e.g. TiS 2 ) and LiFePO 4 .
- cathodes and anodes in the case of Li ion batteries preferably include polyimides as binder matrices, such as those disclosed herein.
- the anode, cathode and PME separator can all include the same or different polyimides.
- Polyimides are generally prepared by reacting one or more diamines and one or more dianhydride monomers in a step-wise condensation reaction. Preferred diamines and dianhydrides are shown in FIG. 6.
- Aromatic diamines are known to be air sensitive. Thus, a purification process generally includes removing a portion of the oxidized diamine material. Following purification, aromatic diamines typically become white. However, absolutely pure diamines are difficult to achieve, and usually unnecessary. Recrystallization of the diamine from a mixture of alcohol and water has been found to be both effective and sufficient. The collected crystals are preferably dried under a vacuum because the water used for crystallization may not be easily removable at room temperature.
- Dianhydrides are also preferably purified and can be purified using at least two methods.
- a preferred purification method is recrystallization from acetic anhydride. Acetic anhydride closes reactive anhydride rings. However, removal of acetic acid produced is sometimes difficult. Washing with ether or MTBE can be used to remove the residual acetic acid.
- the dianhydride crystals generally require drying in a vacuum oven.
- An alternate method is to quickly wash the crystals with dry ethanol to remove open anhydride rings and then to rapidly dry the washed powder in a vacuum oven. This method works for purifying BPDA if the incoming purity is at least approximately 96%.
- the condensation reaction is performed to the poly (amic-acid) stage.
- One mole of diamine is reacted with about 1.005 to 1.01 equivalents of dianhydride.
- Excess dianhydride is generally preferably used to ensure that the dianhydride reagent determines the end group of the reaction product, the dianhydride excess ensuring that polymer chains are terminated with anhydride end groups which are known to maximize stability of the polymer product. In addition, such an excess compensates for traces of water which can react with anhydride groups.
- the solution is preferably about 15 to 20 weight % total in NMP solvent.
- the diamine is usually dissolved first, preferably under nitrogen, although this is not required for all diamines.
- the dianhydride is then added.
- a large scale reaction preferably adds the dianhydride in portions because there is some heat of reaction and it is desirable to keep the temperature below 40° C. For example, a small scale reaction of 50 grams could add the dianhydride all at once, provided there is good initial mixing.
- the dianhydride generally dissolves much more slowly than the diamine.
- the best and simplest way to perform the reaction is to use a cylindrical jar with a polytetrafluoroethylene sealed cap. This jar can be shaken by hand in the beginning and then put on a rolling mill at slow speed to turn the jar smoothly. The reaction proceeds best at room temperature over a two to twelve hour period. Once the initial reaction is complete, as evidenced by a substantially constant solution color and viscosity, the solution is ready for imide ring closure.
- the chemical reaction to form the polyimide from the poly (amic-acid) can be performed with 1.1 equivalents of acetic anhydride per imide ring and 1 equivalent of pyridine as a ring closure catalyst. Pyridine can be added and rolling preferably continued until mixed. The acetic anhydride can cause a portion of the amic-acid polymer to precipitate.
- the polymer should be redissolved before heating.
- the jar is put on a rolling mill to cool while turning. Once the solution returns to room temperature, a fully imidized polymer dissolved in NMP results.
- the solution generally also has some residual pyridine, acetic acid, and may include some acetic anhydride. The solution is expected to be stable for reasonable periods of time.
- a preferred method for collecting the product from a small-scale reaction is to precipitate the polymer into methyl alcohol. This removes the solvent load and traces of monomers that did not react. It also can be used, in conjunction with the observed viscosity, to estimate the quality of the polymerization. A good, high molecular weight polyimide will precipitate cleanly into methyl alcohol with little or no cloudiness. The viscosity should be high (e.g. 8000 to 10,000 cp).
- the precipitated polymer is preferably washed two or more times until the smell of pyridine is slight.
- the polymer can then be air dried for a few hours in a hood and then dried in a vacuum oven at 125° C. overnight.
- the volume of methyl alcohol is preferably about a gallon per 100 grams of polymer.
- a two piece battery assembly comprises overcoating an electrode with a PME to form an electrode/separator and subsequent assembly (e.g. lamination) with the other electrode.
- a cathode slurry of electrochemically active material, conductive carbon and binder is mixed in a bulk solvent with the solvent functioning as a plasticizer for the binder material.
- the slurry is coated upon a current collector substrate and the bulk solvent removed.
- the anode is typically carbonaceous and made from a slurry of graphite, binder and plasticizing solvent.
- the bulk solvent is removed after coating on the current collector.
- the separator is coated as a free standing film from a slurry of non-ionically conductive polymer binder, inorganic support filler material and plasticizing solvent.
- the cathode, separator and anode are placed together and laminated under heat and pressure.
- plasticizer is then removed via an extraction process typically utilizing a hot solvent.
- the cell is removed and a liquid electrolyte is introduced into the system to fill the “pores” created via removal of the plasticizer.
- the cell is then packaged in a foil packaging material.
- conventional assembly processes comprise the joining of three separate components.
- a cathode slurry of active material, conductive carbon, polyimide binder and lithium salt is mixed in a bulk solvent.
- the slurry is coated upon a metal current collector substrate and the solvent is removed.
- the coated cathode is overcoated with a PME comprising a mixture of polyimide, lithium salt and bulk solvent, and then dried to remove solvent with an effective amount of solvent retained for conductivity purposes, such as 5 to 50 weight % versus polyimide plus salt.
- the overcoated cathode has become both the cathode and the PME separator.
- An anode layer is then placed over the PME coated cathode, thus providing a battery assembly using only two components.
- FIG. 7 shows a preferred assembly “folding” process related to the two component battery assembly process described above.
- a PME coated cathode on a cathode current collector is first provided as described above.
- the surface of the PME overcoated cathode is sprayed with a small amount of solvent for adhesion purposes.
- a Li anode such as a Li metal strip having an area slightly less than the area of the PME coated cathode is then placed on the PME coated cathode.
- the anode could also be coated, dried, then overcoated on the PME coated cathode.
- An anode tab such as a nickel tab, is then placed on the anode in step 730 .
- a cell fold is then performed in step 740 by wrapping the PME coated cathode over the lithium metal anode (or graphitic anode) as shown in FIG. 7.
- a bicell battery 755 having an anode tab which is ready for packaging is produced. Bicells provide twice the capacity of conventional cells while having the same footprint of the conventional cell.
- FIG. 8 shows an assembly process for packaging the electrochemical bicell 755 produced by the assembly process shown in FIG. 7, where the steps of the assembly process shown in FIG. 7 are repeated on the top of FIG. 8 for convenient reference.
- the process shown in FIG. 8 is applied to a bicell battery, the described process is in no way limited to bicells.
- standard cells according to the invention can be packaged as shown in FIG. 8.
- step 810 packaging frame material is rolled out from a suitable roller, the frame material being a material such as PET, having a thickness substantially the same as the battery itself to fit around the battery.
- step 820 an opening is created in the frame material which is slightly larger than the cell 755 to be inserted using a window punch or equivalent.
- a registration hole is also shown which can be created in step 820 .
- Tab sealant is applied to the package frame material or pre-applied to the tab strip.
- a cathode tab is fed, cut and applied to the frame material.
- Lower packaging material having a low temperature heat sealant and moisture barrier is then applied to the frame.
- the interior heat sealant layer is a material that not only heat seals to itself, but also bonds strongly to the current collector of the battery, and preferably activates at between about 90 C to 100 C.
- the cell 755 is then preferably pick and placed into the cavity formed by the punched out package frame and onto the lower packaging material attached to the bottom of the frame in step 840 .
- the lower packaging material is preferably heated (e.g. 90 C) prior to placing the cell 755 thereon to promote adhesion.
- Upper packaging material having a low temperature heat sealant and moisture barrier which can be the same composition as lower packaging material, is then applied in step 850 .
- a binder material can be included on the outside of the lower and upper packaging material for applications such as the insertion into a credit card.
- the entire surface of the battery along with the perimeter of the packaging material is heat laminated in step 860 to form a finished bicell battery 865 having substantially the same thickness dimension throughout.
- the assembly process shown in FIG. 8 can package one or more cells in a single package.
- a lamination temperature such as 110° C. for typically 5 to 15 seconds under a pressure sufficient to produce a uniform heat seal but not too high as to distort the battery and/or the package is used to provide the lamination to form the finished bicell battery 865 .
- the substantially constant thickness of bicell 865 facilitates integration into a card, such as a credit card, and also reduces surface defects.
- substantially the same thickness dimension throughout the battery refers to a thickness over the entire area of the packaged battery being ⁇ 1 mil.
- a totally laminated battery with package 865 results which behaves as a single laminated layer.
- a step-down seal process which does not utilize a frame can be used. Instead, an elastomeric lamination plate set is used. This allows intimate contact of the packaging material all over the surface of the battery, the packaging material necking down to the side seal area where the packaging material laminates to itself.
- the battery package material is laminated to the entire battery.
- Previous lamination work discloses only lamination of a portion of the battery.
- the use of a frame to surround the cell permits production of highly planar batteries having substantially the same thickness dimension throughout.
- the purpose of this example is to demonstrate the homogenous nature of the PME formed from polyimides that have strong interactions with a lithium salt through demonstrated optical transmission.
- PME films were generated from polyimides shown in FIGS. 1 ( b ), ( c ) and ( m ), while a Matrimid 5218 p /salt/solvent was generated for comparison.
- the PMEs and Matrimid based film were cast upon a clear polyethylene terephthalate support film from NMP and dried for three hours in a vacuum oven at 120° C. The residual solvent content was approximately 4 wt %. All PME compositions and the Matrimid formulation were 32% polyimide, 64% LiTFSi salt, and the remainder being the small amount of solvent.
- the Matrimid polyimide does not form a clear homogenous composition when the lithium salt concentration is 64%. Moreover, the Matrimid polyimide does not form a clear homogenous composition even at substantially lower salt concentrations, such at a concentration of 0.5 moles of lithium salt per imide ring provided by the polyimide.
- Polyimides including a lithium salt in a concentration of 0.5 moles (or less) of lithium salt per imide ring provided by the polyimide generally lack sufficient minimum ionic conductivity to be a useful electrolyte separator for an electrochemical cell.
- the PME is a homogeneous or near homogeneous matrix material
- batteries formed using the PME exhibit a unique ability to handle exposure to high temperatures and pressures, and still maintain its performance characteristics.
- Cell assembly is typically performed at elevated temperatures (e.g. 140° C.) and pressure (e.g. 125 psi) for about 10 minutes, so subsequent exposures to similar or less rigorous conditions do not effect cells manufactured according to the invention.
- elevated temperatures e.g. 140° C.
- pressure e.g. 125 psi
- Typical card manufacturing techniques require hot lamination at 125° C. for 5 or more minutes in an hydraulic press exerting over 250 psi. Batteries according to the invention have demonstrated full function following this process with no significant change in open circuit voltage (OCV) or capacity following typical lamination processing. In contrast, other battery technologies currently available will fail to operate (e.g. short) following conventional lamination processing or significantly lose capacity and/or OCV.
- OCV open circuit voltage
- Batteries according to the invention can withstand conditions more rigorous than typical lamination processing.
- a battery according to the invention was subjected to an injection molding process to see if the battery could withstand the conditions encountered during an injection molding process.
- Injection molding process were investigated for molding the polymers polyethylene-terephthalate (PET) and polyvinyl chloride (PVC) to encapsulate batteries according to the invention.
- PET polyethylene-terephthalate
- PVC polyvinyl chloride
- Li battery systems with liquid electrolytes or gel polymers having solvent in the pores of the polymer raise safety issues.
- the PME based cells according to the invention generally include some solvent, the solvent is complexed with the polymer and salt, not trapped in a porous film (gel electrolyte) or freely available (liquid electrolyte).
- FIG. 9( a ) shows two (2) SEM micrographs of the PME alone which each evidence a substantially defect free and a porosity free film.
- the thickness of the PME films shown were both about 75 ⁇ m.
- FIG. 9( b ) shows a SEM of an interface between a PME film (20 ⁇ m) disposed on a lithium vanadium oxide/polyimide cathode layer (55 ⁇ m).
- the lower images are blowups of the interfaces shown at the top of FIG. 9( b ).
- the interfaces shown are quite uniform and smooth.
- FIG. 10 shows the charge/discharge profile of a typical cell according to the invention, the cell including a lithium vanadium oxide (LVO) cathode, a Li metal anode and a PME separator, according to an embodiment of the invention.
- the cell capacity was 25 mAh.
- the y-axis represents cell voltage, while the x-axis represents total time. The cell demonstrates good cycling stability during a cycling of over 300 hours.
Landscapes
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Electrochemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Manufacturing & Machinery (AREA)
- Inorganic Chemistry (AREA)
- Dispersion Chemistry (AREA)
- Condensed Matter Physics & Semiconductors (AREA)
- General Physics & Mathematics (AREA)
- Physics & Mathematics (AREA)
- Composite Materials (AREA)
- Materials Engineering (AREA)
- Secondary Cells (AREA)
- Cell Separators (AREA)
- Macromolecular Compounds Obtained By Forming Nitrogen-Containing Linkages In General (AREA)
- Battery Electrode And Active Subsutance (AREA)
- Conductive Materials (AREA)
- Sealing Battery Cases Or Jackets (AREA)
Priority Applications (9)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/437,778 US20040253520A1 (en) | 2003-05-13 | 2003-05-13 | Polyimide matrix electrolyte and improved batteries therefrom |
CNB2004800127825A CN100386912C (zh) | 2003-05-13 | 2004-05-12 | 聚酰亚胺基电解质和由其改进的电池 |
EP04750764.5A EP1639663B1 (en) | 2003-05-13 | 2004-05-12 | Polyimide based electrolyte and improved batteries therefrom |
CA002525668A CA2525668A1 (en) | 2003-05-13 | 2004-05-12 | Polyimide based electrolyte and improved batteries therefrom |
KR1020057021538A KR101186040B1 (ko) | 2003-05-13 | 2004-05-12 | 폴리이미드 기반 전해질 및 그것으로부터 제조된 개선된전지 |
JP2006532480A JP5074031B2 (ja) | 2003-05-13 | 2004-05-12 | ポリイミドに基づく電解質およびそれからなる改良された電池 |
PCT/US2004/013009 WO2004102694A2 (en) | 2003-05-13 | 2004-05-12 | Polyimide based electrolyte and improved batteries therefrom |
TW093113425A TWI307186B (en) | 2003-05-13 | 2004-05-12 | Polyimide based electrolyte and improved batteries therefrom |
US11/115,193 US7129005B2 (en) | 2003-05-13 | 2005-04-27 | Polyimide matrix electrolyte and improved batteries therefrom |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/437,778 US20040253520A1 (en) | 2003-05-13 | 2003-05-13 | Polyimide matrix electrolyte and improved batteries therefrom |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/115,193 Continuation US7129005B2 (en) | 2003-05-13 | 2005-04-27 | Polyimide matrix electrolyte and improved batteries therefrom |
Publications (1)
Publication Number | Publication Date |
---|---|
US20040253520A1 true US20040253520A1 (en) | 2004-12-16 |
Family
ID=33449728
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/437,778 Abandoned US20040253520A1 (en) | 2003-05-13 | 2003-05-13 | Polyimide matrix electrolyte and improved batteries therefrom |
US11/115,193 Expired - Lifetime US7129005B2 (en) | 2003-05-13 | 2005-04-27 | Polyimide matrix electrolyte and improved batteries therefrom |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/115,193 Expired - Lifetime US7129005B2 (en) | 2003-05-13 | 2005-04-27 | Polyimide matrix electrolyte and improved batteries therefrom |
Country Status (8)
Country | Link |
---|---|
US (2) | US20040253520A1 (ko) |
EP (1) | EP1639663B1 (ko) |
JP (1) | JP5074031B2 (ko) |
KR (1) | KR101186040B1 (ko) |
CN (1) | CN100386912C (ko) |
CA (1) | CA2525668A1 (ko) |
TW (1) | TWI307186B (ko) |
WO (1) | WO2004102694A2 (ko) |
Cited By (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20040229118A1 (en) * | 2003-05-13 | 2004-11-18 | Wensley C. Glen | Card with embedded IC and electrochemical cell |
US20050239917A1 (en) * | 2004-02-18 | 2005-10-27 | Solicore, Inc. | Lithium inks and electrodes and batteries made therefrom |
US20050263596A1 (en) * | 2004-05-12 | 2005-12-01 | Solicore, Inc. | Portable charger, including portable sleeve, for an electronically readable card |
US20060234124A1 (en) * | 2005-04-18 | 2006-10-19 | Kejha Joseph B | High rate primary lithium battery with solid cathode |
US20060257736A1 (en) * | 2004-05-31 | 2006-11-16 | Nissan Motor Co., Ltd. | Electrode, battery, and method of manufacturing the same |
WO2006130766A2 (en) * | 2005-06-01 | 2006-12-07 | Board Of Regents, The University Of Texas System | Cathodes for rechargeable lithium-ion batteries |
US20090188105A1 (en) * | 2008-01-28 | 2009-07-30 | Ming-Chin Chien | Slim battery packaging method |
US20110212361A1 (en) * | 2008-11-03 | 2011-09-01 | Youlchon Chemical Co., Ltd. | Cell packaging material and method for producing the same |
US20130011745A1 (en) * | 2011-07-06 | 2013-01-10 | Excellatron Solid State Llc | Solid, lithium-salt-doped, thermoset polyimide polymer electrolyte and electrochemical cell employing same |
US20140220454A1 (en) * | 2011-10-06 | 2014-08-07 | Sony Corporation | Battery and method of manufacturing the same |
US9528033B2 (en) | 2013-11-13 | 2016-12-27 | R.R. Donnelley & Sons Company | Electrolyte material composition and method |
EP3325539A4 (en) * | 2014-09-26 | 2019-05-08 | Uop Llc | HIGH PERMEABILITY POLYIMIDE MEMBRANES: ENHANCED GAS SELECTIVITY BY UV TREATMENT |
US10707531B1 (en) | 2016-09-27 | 2020-07-07 | New Dominion Enterprises Inc. | All-inorganic solvents for electrolytes |
US10707526B2 (en) | 2015-03-27 | 2020-07-07 | New Dominion Enterprises Inc. | All-inorganic solvents for electrolytes |
US10858482B2 (en) | 2015-02-12 | 2020-12-08 | Samsung Electronics Co., Ltd. | Composition of preparing poly(imide-benzoxazole) copolymer, poly(imide-benzoxazole) copolymer, article containing poly(imide-benzoxazole) copolymer, and display device including same |
US11319411B2 (en) * | 2012-04-11 | 2022-05-03 | Ionic Materials, Inc. | Solid ionically conducting polymer material |
US11611104B2 (en) | 2012-04-11 | 2023-03-21 | Ionic Materials, Inc. | Solid electrolyte high energy battery |
US11749833B2 (en) | 2012-04-11 | 2023-09-05 | Ionic Materials, Inc. | Solid state bipolar battery |
US11949105B2 (en) | 2012-04-11 | 2024-04-02 | Ionic Materials, Inc. | Electrochemical cell having solid ionically conducting polymer material |
US12074274B2 (en) | 2012-04-11 | 2024-08-27 | Ionic Materials, Inc. | Solid state bipolar battery |
Families Citing this family (30)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US10629947B2 (en) | 2008-08-05 | 2020-04-21 | Sion Power Corporation | Electrochemical cell |
EP1787344B1 (en) | 2004-07-22 | 2017-02-22 | BrightVolt, Inc. | Improved battery tab and packaging design |
WO2007147167A2 (en) | 2006-06-16 | 2007-12-21 | Porous Power Technologies, Llc | Optimized microporous structure of electrochemical cells |
US20090035657A1 (en) * | 2006-10-23 | 2009-02-05 | Buiel Edward R | Electrode for Hybrid Energy Storage Device and Method of Making Same |
US8540899B2 (en) * | 2007-02-07 | 2013-09-24 | Esionic Es, Inc. | Liquid composite compositions using non-volatile liquids and nanoparticles and uses thereof |
US20080318128A1 (en) * | 2007-06-22 | 2008-12-25 | Sion Power Corporation | Lithium alloy/sulfur batteries |
WO2009086441A2 (en) * | 2007-12-27 | 2009-07-09 | Zettacore, Inc. | Self-contained charge storage molecules for use in molecular capacitors |
WO2009103082A2 (en) * | 2008-02-17 | 2009-08-20 | Porous Power Technologies, Llc | Lamination configurations for battery applications using pvdf highly porous film |
US8927775B2 (en) | 2008-07-14 | 2015-01-06 | Esionic Es, Inc. | Phosphonium ionic liquids, salts, compositions, methods of making and devices formed there from |
US8778534B2 (en) * | 2008-07-14 | 2014-07-15 | Esionic Es, Inc. | Phosphonium ionic liquids, compositions, methods of making and batteries formed there from |
US8907133B2 (en) | 2008-07-14 | 2014-12-09 | Esionic Es, Inc. | Electrolyte compositions and electrochemical double layer capacitors formed there from |
WO2010135573A2 (en) | 2009-05-20 | 2010-11-25 | Porous Power Technologies, Llc | Treatment and adhesive for microporous membranes |
US20110311881A1 (en) * | 2010-06-21 | 2011-12-22 | Benicewicz Brian C | Lithium sulfonate polyazole solid polymer electrolytes in polymer electrolyte lithium ion batteries and supercapacitors, and processes of fabrication |
KR101251742B1 (ko) * | 2011-04-14 | 2013-04-05 | 경북대학교 산학협력단 | 유기라디칼 폴리이미드 전극 활물질 및 이를 포함하는 전기화학소자 |
CN102201568B (zh) * | 2011-04-18 | 2013-04-24 | 浙江大学 | 锂离子膜电极的制备方法及在锂离子电池制备中的应用 |
CN102290245B (zh) * | 2011-04-29 | 2012-11-21 | 深圳市惠程电气股份有限公司 | 一种聚酰亚胺电容电池及其制作方法 |
EP2721665B1 (en) | 2011-06-17 | 2021-10-27 | Sion Power Corporation | Plating technique for electrode |
US8936870B2 (en) | 2011-10-13 | 2015-01-20 | Sion Power Corporation | Electrode structure and method for making the same |
US9742008B2 (en) * | 2013-12-03 | 2017-08-22 | Ionic Materials, Inc. | Solid, ionically conducting polymer material, and methods and applications for same |
CN102738426A (zh) * | 2012-06-29 | 2012-10-17 | 西安大维精密机械有限公司 | 一种耐高温锂电池的制备方法 |
TWI466924B (zh) * | 2013-01-23 | 2015-01-01 | Mortech Corp | 聚醯亞胺膜及其聚醯亞胺積層板 |
CN106415908B (zh) | 2014-06-17 | 2019-02-12 | 美敦力公司 | 用于电池的半固体电解质 |
US20160023569A1 (en) * | 2014-07-28 | 2016-01-28 | Ford Global Technologies, Llc | Battery power capability estimation based on reduced order electrochemical models |
US10333173B2 (en) | 2014-11-14 | 2019-06-25 | Medtronic, Inc. | Composite separator and electrolyte for solid state batteries |
US11342559B2 (en) | 2015-06-08 | 2022-05-24 | Ionic Materials, Inc. | Battery with polyvalent metal anode |
US10324138B2 (en) | 2015-11-16 | 2019-06-18 | Massachusettes Institute Of Technology | Computing system for identification of solid-solid interphase products |
US10587005B2 (en) | 2016-03-30 | 2020-03-10 | Wildcat Discovery Technologies, Inc. | Solid electrolyte compositions |
US11715863B2 (en) | 2018-08-08 | 2023-08-01 | Brightvolt, Inc. | Solid polymer matrix electrolytes (PME) and methods and uses thereof |
US20210320331A1 (en) * | 2018-08-08 | 2021-10-14 | Brightvolt, Inc. | Solid polymer matrix electrolyte (pme) for rechargeable lithium batteries and batteries made therewith |
KR20230104159A (ko) * | 2020-10-06 | 2023-07-07 | 브라이트볼트, 인크. | 고체 중합체 매트릭스 전해질 (pme) 및 그의 방법 및 용도 |
Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5888672A (en) * | 1997-02-12 | 1999-03-30 | Gustafson; Scott D. | Polyimide battery |
Family Cites Families (60)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3226245A (en) * | 1958-02-05 | 1965-12-28 | Polymer Corp | Coating method and apparatus |
EP0294202A3 (en) | 1987-06-03 | 1989-10-18 | Kabushiki Kaisha Toshiba | Digital sound data storing device |
JP2692816B2 (ja) | 1987-11-13 | 1997-12-17 | 株式会社きもと | 薄型一次電池 |
JPH05169885A (ja) | 1991-12-26 | 1993-07-09 | Mitsubishi Electric Corp | 薄型icカード |
JP2691827B2 (ja) | 1992-04-15 | 1997-12-17 | 小原株式会社 | 電動機駆動による点溶接ガンの加圧力制御装置 |
JPH06131422A (ja) | 1992-10-15 | 1994-05-13 | Kubota Corp | 解析モデル作成システム |
JP3311402B2 (ja) | 1992-11-19 | 2002-08-05 | 三洋電機株式会社 | 二次電池 |
JPH0737604A (ja) * | 1993-07-26 | 1995-02-07 | Canon Inc | 電 池 |
JPH07320780A (ja) * | 1994-05-20 | 1995-12-08 | Sanyo Electric Co Ltd | 固体電解質二次電池 |
US6013393A (en) | 1995-05-09 | 2000-01-11 | Ricoh Company, Ltd. | Ionic conductive polymer gel and lithium-ion battery using the same |
CA2210040A1 (en) * | 1996-07-23 | 1998-01-23 | Rohm And Haas Company | Electrolyte and electrolytic cell |
US5897974A (en) | 1996-07-23 | 1999-04-27 | Rohm And Haas Company | Solid polymer electrolyte |
DE69734339T2 (de) | 1996-08-07 | 2006-06-01 | Mitsui Chemicals, Inc. | Ionenleitender gelierter Polymerelektrolyt und diesen Elektrolyt enthaltende Feststoffbatterie |
JPH10129213A (ja) | 1996-10-29 | 1998-05-19 | Bridgestone Corp | 悪路用大型空気入りラジアルタイヤ |
SE9604744D0 (sv) * | 1996-12-20 | 1996-12-20 | Pharmacia & Upjohn Ab | A modified coagulation agent |
JPH10188992A (ja) | 1996-12-24 | 1998-07-21 | Sony Corp | 非水電解液電池 |
JP3431785B2 (ja) | 1996-12-24 | 2003-07-28 | シャープ株式会社 | 直交周波数多重変調信号復調装置 |
US6096234A (en) | 1997-01-23 | 2000-08-01 | Shin-Etsu Chemical Co., Ltd. | Cross-linked polymer solid electrolyte, method of manufacturing cross-linked solid polymer electrolyte, composite solid electrolyte, and thin solid cell employing composite solid electrolyte |
ATE392018T1 (de) * | 1997-02-12 | 2008-04-15 | Solicore Inc | Polyamid batterie |
KR100527322B1 (ko) | 1997-05-06 | 2006-01-27 | 소니 가부시끼 가이샤 | 폴리머겔전해질형성용시트,이를사용한폴리머겔전해질및그의제법 |
US5895731A (en) | 1997-05-15 | 1999-04-20 | Nelson E. Smith | Thin-film lithium battery and process |
SG65094A1 (en) | 1997-09-11 | 1999-05-25 | Mitsui Chemicals Inc | Non-aqueous electrolytic solution for capacitor and capacitor containing non-aqueous electrolytic solution |
US5985122A (en) * | 1997-09-26 | 1999-11-16 | General Electric Company | Method for preventing plating of material in surface openings of turbine airfoils |
AU9451098A (en) | 1997-10-14 | 1999-05-03 | Patterning Technologies Limited | Method of forming an electronic device |
US5923456A (en) | 1997-12-19 | 1999-07-13 | Rockwell International Corporation | Reversible electrochemical mirror |
TW431009B (en) | 1998-05-22 | 2001-04-21 | Teijin Ltd | Electrolytic-solution-supporting polymer film and secondary battery |
US6406817B2 (en) | 1998-07-01 | 2002-06-18 | Ube Industries, Ltd. | Crosslinked polymer, electrolyte using the polymer, and nonaqueous secondary battery using the electrolyte |
US6109530A (en) | 1998-07-08 | 2000-08-29 | Motorola, Inc. | Integrated circuit carrier package with battery coin cell |
JP3257516B2 (ja) | 1998-07-23 | 2002-02-18 | 日本電気株式会社 | 積層型電解質及びそれを用いた電池 |
US7297441B2 (en) | 1998-10-23 | 2007-11-20 | Sony Corporation | Nonaqueous-electrolyte secondary battery |
JP3830008B2 (ja) | 1998-10-30 | 2006-10-04 | ソニー株式会社 | 非水電解質電池 |
JP2000243447A (ja) | 1999-02-19 | 2000-09-08 | Sony Corp | ゲル電解質及びゲル電解質電池 |
US6148503A (en) | 1999-03-31 | 2000-11-21 | Imra America, Inc. | Process of manufacturing porous separator for electrochemical power supply |
US6617074B1 (en) | 1999-06-30 | 2003-09-09 | Mitsubishi Materials Corporation | Lithium ion polymer secondary battery and gelatinous polymer electrolyte for sheet battery |
WO2001018898A1 (fr) | 1999-09-02 | 2001-03-15 | Dai-Ichi Kogyo Seiyaku Co., Ltd. | Polyelectrolyte, electrolyte non aqueuse et dispositif electrique les renfermant |
US6509123B1 (en) | 1999-09-30 | 2003-01-21 | Sony Corporation | Gel electrolyte and gel electrolyte cell |
JP3566891B2 (ja) | 1999-10-05 | 2004-09-15 | シャープ株式会社 | リチウム二次電池 |
US6451480B1 (en) * | 1999-10-18 | 2002-09-17 | Scott D. Gustafson | Polyimide-based lithium ion battery |
WO2001041248A1 (fr) | 1999-11-29 | 2001-06-07 | Matsushita Electric Industrial Co., Ltd. | Electrolyte non aqueux et pile a electrolyte non aqueux |
EP1209754B1 (en) | 1999-11-29 | 2011-10-05 | Panasonic Corporation | Non-aqueous electrolyte cell |
JP3656244B2 (ja) | 1999-11-29 | 2005-06-08 | 株式会社豊田中央研究所 | 高耐久性固体高分子電解質及びその高耐久性固体高分子電解質を用いた電極−電解質接合体並びにその電極−電解質接合体を用いた電気化学デバイス |
SE518564C2 (sv) | 1999-12-20 | 2002-10-22 | Ericsson Telefon Ab L M | Polymer elektrolyt, battericell innefattande elektrolyten, förfarande för framställning av elektrolyten samt användning av elektrolyten och battericellen |
JP2001229965A (ja) * | 2000-02-16 | 2001-08-24 | Sony Corp | ゲル状電解質電池の製造方法 |
WO2002013304A1 (en) | 2000-08-04 | 2002-02-14 | Southern Clay Products, Inc. | Gelled anode or electrolyte solution for an electrochemical cell |
US6519798B2 (en) * | 2000-10-05 | 2003-02-18 | Dreamwell, Ltd. | Mattress and bed assembly providing an enlarged sleeping surface area |
JPWO2002035636A1 (ja) * | 2000-10-20 | 2004-03-04 | 大日本インキ化学工業株式会社 | 高分子固体電解質及び該電解質を用いた電池 |
US6828062B2 (en) | 2000-12-23 | 2004-12-07 | Santa Fe Science And Technology, Inc. | Long-lived conjugated polymer electrochemical devices incorporating ionic liquids |
US20020160272A1 (en) | 2001-02-23 | 2002-10-31 | Kabushiki Kaisha Toyota Chuo | Process for producing a modified electrolyte and the modified electrolyte |
US7006846B2 (en) | 2001-03-08 | 2006-02-28 | Northrop Grumman Corporation | Credit card communication system |
JP3969077B2 (ja) | 2001-04-04 | 2007-08-29 | 住友化学株式会社 | 高分子電解質及びその製造方法 |
US20020153424A1 (en) | 2001-04-19 | 2002-10-24 | Chuan Li | Method and apparatus of secure credit card transaction |
KR100399788B1 (ko) | 2001-08-17 | 2003-09-29 | 삼성에스디아이 주식회사 | 졸 형태의 고분자 전해질 및 이를 채용한 리튬 전지 |
US7008722B2 (en) | 2002-04-10 | 2006-03-07 | Sui-Yang Huang | Polymer-gel lithium ion battery |
US20030222755A1 (en) | 2002-05-31 | 2003-12-04 | Kemper Jonathan Thomas | Credit card sized remote control transmitter application |
KR100911004B1 (ko) | 2002-07-09 | 2009-08-05 | 삼성에스디아이 주식회사 | 전지부와 이를 채용한 리튬이차전지 |
US6835493B2 (en) | 2002-07-26 | 2004-12-28 | Excellatron Solid State, Llc | Thin film battery |
US6936377B2 (en) | 2003-05-13 | 2005-08-30 | C. Glen Wensley | Card with embedded IC and electrochemical cell |
US20040229127A1 (en) | 2003-05-13 | 2004-11-18 | Wensley C. Glen | Polyimide matrix electrolyte |
US20050026042A1 (en) | 2003-07-29 | 2005-02-03 | Alain Vallee | Polyimide-based battery for a portable electronic appliance |
US7390336B2 (en) | 2003-07-29 | 2008-06-24 | Solicore, Inc. | Polyimide-based lithium metal battery |
-
2003
- 2003-05-13 US US10/437,778 patent/US20040253520A1/en not_active Abandoned
-
2004
- 2004-05-12 WO PCT/US2004/013009 patent/WO2004102694A2/en active Application Filing
- 2004-05-12 CA CA002525668A patent/CA2525668A1/en not_active Abandoned
- 2004-05-12 JP JP2006532480A patent/JP5074031B2/ja not_active Expired - Lifetime
- 2004-05-12 EP EP04750764.5A patent/EP1639663B1/en not_active Expired - Lifetime
- 2004-05-12 CN CNB2004800127825A patent/CN100386912C/zh not_active Expired - Lifetime
- 2004-05-12 KR KR1020057021538A patent/KR101186040B1/ko active IP Right Grant
- 2004-05-12 TW TW093113425A patent/TWI307186B/zh not_active IP Right Cessation
-
2005
- 2005-04-27 US US11/115,193 patent/US7129005B2/en not_active Expired - Lifetime
Patent Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5888672A (en) * | 1997-02-12 | 1999-03-30 | Gustafson; Scott D. | Polyimide battery |
Cited By (32)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6936377B2 (en) | 2003-05-13 | 2005-08-30 | C. Glen Wensley | Card with embedded IC and electrochemical cell |
US20040229118A1 (en) * | 2003-05-13 | 2004-11-18 | Wensley C. Glen | Card with embedded IC and electrochemical cell |
US7968233B2 (en) | 2004-02-18 | 2011-06-28 | Solicore, Inc. | Lithium inks and electrodes and batteries made therefrom |
US20050239917A1 (en) * | 2004-02-18 | 2005-10-27 | Solicore, Inc. | Lithium inks and electrodes and batteries made therefrom |
US9925813B2 (en) | 2004-02-18 | 2018-03-27 | Brightvolt, Inc. | Lithium inks and electrodes and batteries made therefrom |
US8318358B2 (en) | 2004-02-18 | 2012-11-27 | Solicore, Inc. | Lithium inks and electrodes and batteries made therefrom |
US20050263596A1 (en) * | 2004-05-12 | 2005-12-01 | Solicore, Inc. | Portable charger, including portable sleeve, for an electronically readable card |
US20060257736A1 (en) * | 2004-05-31 | 2006-11-16 | Nissan Motor Co., Ltd. | Electrode, battery, and method of manufacturing the same |
US20060234124A1 (en) * | 2005-04-18 | 2006-10-19 | Kejha Joseph B | High rate primary lithium battery with solid cathode |
WO2006130766A2 (en) * | 2005-06-01 | 2006-12-07 | Board Of Regents, The University Of Texas System | Cathodes for rechargeable lithium-ion batteries |
US20070082267A1 (en) * | 2005-06-01 | 2007-04-12 | Board Of Regents, The University Of Texas System | Cathodes for rechargeable lithium-ion batteries |
WO2006130766A3 (en) * | 2005-06-01 | 2009-04-16 | Univ Texas | Cathodes for rechargeable lithium-ion batteries |
US10290868B2 (en) * | 2005-06-01 | 2019-05-14 | Board Of Regents, The University Of Texas System | Cathodes for rechargeable lithium-ion batteries |
US20090188105A1 (en) * | 2008-01-28 | 2009-07-30 | Ming-Chin Chien | Slim battery packaging method |
US20110212361A1 (en) * | 2008-11-03 | 2011-09-01 | Youlchon Chemical Co., Ltd. | Cell packaging material and method for producing the same |
US20130011745A1 (en) * | 2011-07-06 | 2013-01-10 | Excellatron Solid State Llc | Solid, lithium-salt-doped, thermoset polyimide polymer electrolyte and electrochemical cell employing same |
US9240257B2 (en) * | 2011-07-06 | 2016-01-19 | Johnson IP Holding, Inc. | Solid, lithium-salt-doped, thermoset polyimide polymer electrolyte and electrochemical cell employing same |
US9917326B2 (en) * | 2011-10-06 | 2018-03-13 | Murata Manufacturing Co., Ltd. | Battery and method of manufacturing the same |
US20140220454A1 (en) * | 2011-10-06 | 2014-08-07 | Sony Corporation | Battery and method of manufacturing the same |
US12074274B2 (en) | 2012-04-11 | 2024-08-27 | Ionic Materials, Inc. | Solid state bipolar battery |
US11319411B2 (en) * | 2012-04-11 | 2022-05-03 | Ionic Materials, Inc. | Solid ionically conducting polymer material |
US11949105B2 (en) | 2012-04-11 | 2024-04-02 | Ionic Materials, Inc. | Electrochemical cell having solid ionically conducting polymer material |
US11749833B2 (en) | 2012-04-11 | 2023-09-05 | Ionic Materials, Inc. | Solid state bipolar battery |
US11611104B2 (en) | 2012-04-11 | 2023-03-21 | Ionic Materials, Inc. | Solid electrolyte high energy battery |
US9528033B2 (en) | 2013-11-13 | 2016-12-27 | R.R. Donnelley & Sons Company | Electrolyte material composition and method |
US10106710B2 (en) | 2013-11-13 | 2018-10-23 | R.R. Donnelley & Sons Company | Insulator material composition and method |
US9718997B2 (en) | 2013-11-13 | 2017-08-01 | R.R. Donnelley & Sons Company | Battery |
EP3325539A4 (en) * | 2014-09-26 | 2019-05-08 | Uop Llc | HIGH PERMEABILITY POLYIMIDE MEMBRANES: ENHANCED GAS SELECTIVITY BY UV TREATMENT |
US10858482B2 (en) | 2015-02-12 | 2020-12-08 | Samsung Electronics Co., Ltd. | Composition of preparing poly(imide-benzoxazole) copolymer, poly(imide-benzoxazole) copolymer, article containing poly(imide-benzoxazole) copolymer, and display device including same |
US11271248B2 (en) | 2015-03-27 | 2022-03-08 | New Dominion Enterprises, Inc. | All-inorganic solvents for electrolytes |
US10707526B2 (en) | 2015-03-27 | 2020-07-07 | New Dominion Enterprises Inc. | All-inorganic solvents for electrolytes |
US10707531B1 (en) | 2016-09-27 | 2020-07-07 | New Dominion Enterprises Inc. | All-inorganic solvents for electrolytes |
Also Published As
Publication number | Publication date |
---|---|
KR101186040B1 (ko) | 2012-09-25 |
US7129005B2 (en) | 2006-10-31 |
CN1788375A (zh) | 2006-06-14 |
CN100386912C (zh) | 2008-05-07 |
JP2007503104A (ja) | 2007-02-15 |
WO2004102694A2 (en) | 2004-11-25 |
US20050250015A1 (en) | 2005-11-10 |
TWI307186B (en) | 2009-03-01 |
TW200505072A (en) | 2005-02-01 |
EP1639663B1 (en) | 2015-01-07 |
CA2525668A1 (en) | 2004-11-25 |
JP5074031B2 (ja) | 2012-11-14 |
KR20060020625A (ko) | 2006-03-06 |
EP1639663A4 (en) | 2009-11-25 |
EP1639663A2 (en) | 2006-03-29 |
WO2004102694A3 (en) | 2005-04-07 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7129005B2 (en) | Polyimide matrix electrolyte and improved batteries therefrom | |
US6936377B2 (en) | Card with embedded IC and electrochemical cell | |
US7198870B2 (en) | Polyimide matrix electrolyte | |
US20160118638A1 (en) | Compositions for use as protective layers and other components in electrochemical cells | |
US6794089B2 (en) | Nonaqueous electrolyte and nonaqueous electrolyte secondary battery | |
KR100531724B1 (ko) | 올리고머 점성체 함침 다공막형 무용매 고분자 전해질 및이를 채용한 2차전지 | |
CN111837258B (zh) | 制造含聚合物固体电解质的电极的方法和由此获得的电极 | |
US20230291073A1 (en) | Solid electrolyte membrane and solid-state battery including the same | |
WO2023068312A1 (ja) | ポリマーイオン伝導膜、二次電池用ポリマーイオン伝導膜、複合イオン透過膜、電極複合体、及び二次電池 | |
CN116918119A (zh) | 非水电解液二次电池 | |
KR20030083250A (ko) | 리튬이차전지용 다공성 폴리아크릴로니트릴 멤브레인 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |