US20040175466A1 - Multilayer barrier structures, methods of making the same and packages made therefrom - Google Patents
Multilayer barrier structures, methods of making the same and packages made therefrom Download PDFInfo
- Publication number
- US20040175466A1 US20040175466A1 US10/735,366 US73536603A US2004175466A1 US 20040175466 A1 US20040175466 A1 US 20040175466A1 US 73536603 A US73536603 A US 73536603A US 2004175466 A1 US2004175466 A1 US 2004175466A1
- Authority
- US
- United States
- Prior art keywords
- multilayer structure
- layer
- polyamide
- weight
- package
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B27/00—Layered products comprising a layer of synthetic resin
- B32B27/06—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material
- B32B27/08—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B27/00—Layered products comprising a layer of synthetic resin
- B32B27/16—Layered products comprising a layer of synthetic resin specially treated, e.g. irradiated
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B27/00—Layered products comprising a layer of synthetic resin
- B32B27/30—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers
- B32B27/306—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers comprising vinyl acetate or vinyl alcohol (co)polymers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B27/00—Layered products comprising a layer of synthetic resin
- B32B27/32—Layered products comprising a layer of synthetic resin comprising polyolefins
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B27/00—Layered products comprising a layer of synthetic resin
- B32B27/34—Layered products comprising a layer of synthetic resin comprising polyamides
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B65—CONVEYING; PACKING; STORING; HANDLING THIN OR FILAMENTARY MATERIAL
- B65D—CONTAINERS FOR STORAGE OR TRANSPORT OF ARTICLES OR MATERIALS, e.g. BAGS, BARRELS, BOTTLES, BOXES, CANS, CARTONS, CRATES, DRUMS, JARS, TANKS, HOPPERS, FORWARDING CONTAINERS; ACCESSORIES, CLOSURES, OR FITTINGS THEREFOR; PACKAGING ELEMENTS; PACKAGES
- B65D65/00—Wrappers or flexible covers; Packaging materials of special type or form
- B65D65/38—Packaging materials of special type or form
- B65D65/40—Applications of laminates for particular packaging purposes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B65—CONVEYING; PACKING; STORING; HANDLING THIN OR FILAMENTARY MATERIAL
- B65D—CONTAINERS FOR STORAGE OR TRANSPORT OF ARTICLES OR MATERIALS, e.g. BAGS, BARRELS, BOTTLES, BOXES, CANS, CARTONS, CRATES, DRUMS, JARS, TANKS, HOPPERS, FORWARDING CONTAINERS; ACCESSORIES, CLOSURES, OR FITTINGS THEREFOR; PACKAGING ELEMENTS; PACKAGES
- B65D71/00—Bundles of articles held together by packaging elements for convenience of storage or transport, e.g. portable segregating carrier for plural receptacles such as beer cans or pop bottles; Bales of material
- B65D71/06—Packaging elements holding or encircling completely or almost completely the bundle of articles, e.g. wrappers
- B65D71/08—Wrappers shrunk by heat or under tension, e.g. stretch films or films tensioned by compressed articles
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B65—CONVEYING; PACKING; STORING; HANDLING THIN OR FILAMENTARY MATERIAL
- B65D—CONTAINERS FOR STORAGE OR TRANSPORT OF ARTICLES OR MATERIALS, e.g. BAGS, BARRELS, BOTTLES, BOXES, CANS, CARTONS, CRATES, DRUMS, JARS, TANKS, HOPPERS, FORWARDING CONTAINERS; ACCESSORIES, CLOSURES, OR FITTINGS THEREFOR; PACKAGING ELEMENTS; PACKAGES
- B65D85/00—Containers, packaging elements or packages, specially adapted for particular articles or materials
- B65D85/70—Containers, packaging elements or packages, specially adapted for particular articles or materials for materials not otherwise provided for
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B38/00—Ancillary operations in connection with laminating processes
- B32B38/0036—Heat treatment
- B32B2038/0048—Annealing, relaxing
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B38/00—Ancillary operations in connection with laminating processes
- B32B2038/0052—Other operations not otherwise provided for
- B32B2038/0076—Curing, vulcanising, cross-linking
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2307/00—Properties of the layers or laminate
- B32B2307/50—Properties of the layers or laminate having particular mechanical properties
- B32B2307/514—Oriented
- B32B2307/518—Oriented bi-axially
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2307/00—Properties of the layers or laminate
- B32B2307/70—Other properties
- B32B2307/732—Dimensional properties
- B32B2307/734—Dimensional stability
- B32B2307/736—Shrinkable
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2323/00—Polyalkenes
- B32B2323/04—Polyethylene
- B32B2323/046—LDPE, i.e. low density polyethylene
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2439/00—Containers; Receptacles
- B32B2439/70—Food packaging
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2597/00—Tubular articles, e.g. hoses, pipes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B65—CONVEYING; PACKING; STORING; HANDLING THIN OR FILAMENTARY MATERIAL
- B65D—CONTAINERS FOR STORAGE OR TRANSPORT OF ARTICLES OR MATERIALS, e.g. BAGS, BARRELS, BOTTLES, BOXES, CANS, CARTONS, CRATES, DRUMS, JARS, TANKS, HOPPERS, FORWARDING CONTAINERS; ACCESSORIES, CLOSURES, OR FITTINGS THEREFOR; PACKAGING ELEMENTS; PACKAGES
- B65D2275/00—Details of sheets, wrappers or bags
- B65D2275/02—Sheets wrappers or bags provided with protective or puncture resistant patches, specially adapted for meat on the bone, e.g. patch bags
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/13—Hollow or container type article [e.g., tube, vase, etc.]
- Y10T428/1352—Polymer or resin containing [i.e., natural or synthetic]
Definitions
- Multilayer structures, methods of making the same and packages made therefrom useful for packaging products such as bone-in meat, cheese and other like products are provided. More specifically, the present invention relates to multilayer structures, methods of making the same, and packages made therefrom useful for bone-in meat packaging, cook-in packaging, shrink film packaging, packaging for case ready meats, hot-fill applications, pet food, retort or lidding, and other like packaging.
- the multilayer structures are coextruded and have sufficient durability, strength, tear resistance and puncture resistance, while also providing a high degree of oxygen barrier protection.
- the present invention relates to multilayer barrier structures, methods of making the same, and packages made therefrom useful for packaging that is biaxially oriented so as to be heat-shrinkable around products.
- thermoplastic multilayer structures such as films, sheets or the like
- typical products packaged with thermoplastic multilayer structures include perishable products, such as food.
- meats and cheeses are typically packaged in thermoplastic structures.
- cook-in structures may be utilized to package food products, whereby the products are then heated to cook the food products contained within the packages.
- shrink films are known for packaging food products, such as meat and cheese.
- Bone-in meat products often contain sharp bones that protrude outwardly from the meat.
- Typical cuts of bone-in meat include a half carcass cut, hindquarter cut, round with shank, bone-in shank, full loin, bone-in ribs, forequarter, shoulder and/or other like cuts of meat.
- the protruding bones often can puncture or tear the packaging materials.
- This puncturing or tearing of the packaging material by the protruding bones can occur at the initial stage of packaging or at the later stage of evacuation of the packaging, which may expose the bone-in meat products to oxygen and moisture, thereby having deleterious effects on the bone-in meat product.
- U.S. Pat. 6,171,627 to Bert discloses a bag arrangement and packaging method for packaging bone-in meat using two bags to provide a double wall of film surrounding the cut of meat for bone puncture resistance.
- U.S. Pat. No. 6,015,235 to Kraimer discloses a puncture resistant barrier pouch for the packaging of bone-in meat and other products.
- U.S. Pat. No. 6,183,791 to Williams discloses an oriented heat-shrinkable, thermoplastic vacuum bag having a protective heat-shrinkable patch wherein the heat-shrinkable patch substantially covers all areas exposed to bone, thereby protecting the bag from puncture.
- U.S. Pat. No, 5,020,922 to Schirmer discloses a seamless puncture resistant bag which includes a length of lay-flat seamless tubular film folded to a double lay-flat configuration. The configuration forms a seamless envelope with one face thickened integrally to triple thickness.
- U.S. Pat. No. 5,534,276 to Ennis discloses an oriented heat-shrinkable, thermoplastic vacuum bag having a protective heat-shrinkable reverse printed patch attached to the bag.
- the art teaches many techniques for addressing the problem of bone puncture or tear in the packaging of bone-in meat products.
- Many of the solutions typically include a film structure or bag having patches, double-walled thicknesses or the like.
- One solution for packaging bone-in meat entails the utilization of coextruded multilayer structures having sufficient strength, durability, tear resistance, puncture resistance, and optical properties.
- the formation of coextruded multilayer structures having these properties is difficult without laminating the structures to provide double-walled structures and/or laminating or otherwise adhering patches to the structures.
- Laminating structures together to form double-walled structures or otherwise adhering patches to the structures requires multiple complicated processes, thereby requiring additional time and money.
- known coextruded structures that may be useful for the present invention require very thick coextrusions to provide adequate puncture resistance for bone-in meat.
- This requires the use of large quantities of fairly expensive polymeric materials to provide the protection against puncture and tearing.
- This problem is typically solved, as noted above, by laminating structures together to form patches in the areas of the structures most susceptible to breaking or puncturing. These patches, while allowing the use of less thermoplastic material, can be unsightly in that the surface of the films are interrupted by the patches.
- the lamination process of adding the patches to the films can cause decreased optical characteristics, in that patches can become hazy or yellow.
- the areas of the patches also suffer from decreased optical properties due to the thicknesses of the patches and the patches tend to interfere with the shrink characteristics of the structures. Still further, the application of the patches requires extra steps in addition to the steps of making the structures, including precisely positioning the patches where bony protrusions are likely to be.
- thicker structures tend to have a decrease in optical properties compared to relatively thinner structures.
- a structure's thickness is directly related to haze. Thicker structures, therefore, tend to have an increase in haze, thereby contributing to a decrease in the clarity of the structures.
- thicker structures tend to be more difficult to orient. Thicker structures tend to have a lower shrink energy, thereby requiring an increase in orientation ratio to provide similar shrink characteristics as compared to thinner structures.
- a need therefore, exists for coextruded multilayer structures having superior strength, durability, tear resistance and puncture resistance that are significantly thinner than known structures while maintaining superior optical properties, such as low haze, low yellowness, and high clarity.
- a need exists for coextruded multilayer structures that are orientable to provide packages that are heat shrinkable around products.
- coextruded multilayer structures are needed having superior sealability as compared to known structures, while still maintaining the superior strength, durability, puncture resistance, tear resistance and optical properties.
- methods of making the multilayer structures and packages made therefrom are needed.
- Multilayer structures, methods of making the same and packages made therefrom useful for packaging products such as bone-in meat, cheese and other like products are provided. More specifically, the present invention relates to multilayer structures, methods of making the same, and packages made therefrom useful for bone-in meat packaging, cook-in packaging, shrink film packaging, packaging for case ready meats, hot-fill applications, pet food, retort or lidding, and other like packaging.
- the multilayer structures are coextruded and have sufficient durability, strength, tear resistance and puncture resistance, while also providing oxygen barrier protection.
- the present invention relates to multilayer barrier structures, methods of making the same, and packages made therefrom useful for packaging that is biaxially oriented so as to be heat-shrinkable around products.
- Multilayer structures methods of making the same and packages made therefrom are provided. More specifically, the multilayer structures can be utilized for packaging products having bony protrusions or the like that would easily tear or puncture other structures.
- a multilayer structure for packaging bone-in meat comprises an outer layer comprising a blend of linear low density polyethylene and low density polyethylene, a first polyamide layer comprising a blend of between about 70% by weight and about 99% by weight semi-crystalline polyamide and about 1% by weight to about 30% by weight amorphous polyamide, a first tie layer disposed between said outer layer and said first polyamide layer, a barrier layer disposed adjacent said first polyamide layer wherein said barrier layer comprises ethylene vinyl alcohol copolymer having an ethylene content of between about 27 mol % and about 42 mol %, a second polyamide layer disposed adjacent said barrier layer comprising a blend of between about 70% by weight and about 99% by weight semi-crystalline polyamide, and between about 1% by weight and about 30% by weight amorphous polyamide, a sealant layer comprising a blend of linear low density polyethylene and low density polyethylene wherein said sealant layer comprises a greater volume percent than said
- the first and second polyamide layers each may comprise a blend of between about 85% by weight and about 99% by weight semi-crystalline polyamide and between about 1% by weight and about 15% by weight amorphous polyamide.
- said first and second polyamide layers each may comprise a blend of between about 60% by weight and about 80% by weight of a first semi-crystalline polyamide, between about 10% by weight and about 30% by weight of a second semi-crystalline polyamide, and between about 1% by weight and about 30% by weight amorphous polyamide.
- the first and said second polyamide layers may comprise about an equal percent by volume of the multilayer structure.
- the outer layer may be between about 15% by volume and about 20% by volume of the multilayer structure and the heat sealant layer may be between about 25% by volume and about 30% by volume of the multilayer structure.
- the multilayer structure may be oriented. Further, the multilayer structure may be annealed. Still further, the multilayer structure may be moisturized by the application of water to said multilayer structure. The multilayer structure may further be plasticized. In addition, the multilayer structure may be irradiated to promote crosslinking between the layers of said multilayer structure and/or within a layer of said multilayer structure.
- all layers of the multilayer structure of the present embodiment may be coextruded to form said multilayer structure.
- the multilayer structure may be between about 1 mil and about 8 mils thick. Most preferably, the multilayer structure may be between about 1.5 mils and about 5 mils thick.
- a package for bone-in meat comprises a first wall comprising a multilayer structure comprising an outer layer comprising a blend of linear low density polyethylene and low density polyethylene; a first polyamide layer comprising a blend of about 70% by weight to about 99% by weight semi-crystalline polyamide and about 1% by weight to about 30% by weight amorphous polyamide; a first tie layer disposed between said outer layer and said first polyamide layer; a barrier layer disposed adjacent to said first polyamide layer wherein said barrier layer comprises ethylene vinyl alcohol copolymer having an ethylene content of between about 27 mol % and about 42 mol %; a second polyamide layer disposed adjacent said barrier layer comprising a blend of about 70% by weight to about 99% by weight semi-crystalline polyamide and about 1% by weight to about 30% by weight amorphous polyamide; a sealant layer comprising a blend of linear low density polyethylene and low density polyethylene wherein said sealant layer comprises a greater volume percent
- the package further comprises a bone-in meat product within the package and the multilayer structure may be heat-shrunk around said bone-in meat product.
- the first and second polyamide layers each may comprise a blend of between about 85% by weight and about 99% by weight semi-crystalline polyamide and between about 1% by weight and about 15% by weight amorphous polyamide.
- the first and second polyamide layers each may comprise a blend of between about 60% by weight and about 80% by weight of a first semi-crystalline polyamide, between about 10% by weight and about 30% by of a second semi-crystalline polyamide, and between about 1% by weight and about 30% by weight amorphous polyamide.
- the first and second polyamide layers may comprise about an equal percent by volume of the multilayer structure.
- the outer layer may be between about 15% by volume and about 20% by volume of the multilayer structure and the heat sealant layer may be between about 25% by volume and about 30% by volume of the multilayer structure.
- the multilayer structure of the package of the present invention may be oriented and heat-shrinkable. Further, the multilayer structure may be annealed. Still further, the multilayer structure may be moisturized by the application of water to said multilayer structure. Moreover, the multilayer structure may be irradiated to promote crosslinking between the layers of said multilayer structure and/or within a layer of said multilayer structure. In addition, the multilayer structure may be plasticized and all the layers of the multilayer structure may be coextruded to form the multilayer structure.
- the multilayer structure of the package of the present invention may be between about 1 mil and about 8 mils thick. Most preferably, the multilayer structure of the package of the present embodiment may be between about 1.5 mils and about 5 mils thick.
- the package may further be in the form of a tube having a space therein for bone-in meat.
- the first wall may be heat-sealed to a second wall wherein the first wall and the second wall form a space for bone-in meat.
- a method of making a multilayer for packaging bone-in meat comprises the steps of coextruding a multilayer structure comprising an outer layer comprising a blend of linear low density polyethylene and low density polyethylene; a first polyamide layer comprising a blend of between about 70% by weight and about 99% by weight semi-crystalline polyamide and about 1% by weight to about 30% by weight amorphous polyamide; a first tie layer disposed between said outer layer and said first polyamide layer; a barrier layer disposed adjacent said first polyamide layer wherein said barrier layer comprises ethylene vinyl alcohol copolymer having an ethylene content of between about 27 mol % and about 42 mol %; a second polyamide layer disposed adjacent said barrier layer comprising a blend of between about 70% by weight and about 99% by weight semi-crystalline polyamide, and between about 1% by weight and about 30% by weight amorphous polyamide; a sealant layer comprising a blend of linear low density polyethylene and low density polyethylene where
- the outer layer may be between about 15% by volume and about 20% by volume of the multilayer structure and the heat sealant layer may be between about 25% by volume and about 30% by volume of the multilayer structure.
- the method of the present embodiment further comprises the step of annealing said multilayer structure. Still further, the method of the present embodiment comprises the step of irradiating said multilayer structure to promote crosslinking between the layers of said multilayer structure and/or within a layer of said multilayer structure. The method further comprises the step of moisturizing said multilayer structure by applying water to said multilayer structure.
- the multilayer structure of the method of the present embodiment may be between about 1 mil and about 8 mils thick. Most preferably, the multilayer structure of the method of the present embodiment may be between about 1.5 mils and about 5 mils thick.
- Multilayer structures and packages made from multilayer structures are provided that can be economically and cost-effectively manufactured. More specifically, the multilayer structures can be made via coextrusion of the layers together. The multilayer structures are, therefore, easy to produce and can be made quickly and efficiently.
- multilayer structures and packages made from the multilayer structures are provided that can be oriented, thereby providing increased strength, especially when utilized as packaging for bone-in meat products and the like.
- multilayer structures, methods of making the same and package made therefrom are provided wherein the multilayer structures have superior strength, durability, tear resistance and puncture resistance while being significantly thinner than known structures having comparable strength, durability, tear resistance and puncture resistance.
- Thinner coextruded multilayer structures have the additional advantages of having superior optical properties, such as low haze and yellowness.
- thinner coextruded multilayer structures have the additional advantage of being easily heat-sealable and heat-shrinkable.
- thinner structures contribute to the utilization of less materials, which contributes to cost efficiencies and to a reduction of waste products, both during production of the structures, and after the structures are utilized for packages.
- the multilayer structures described herein use less materials, thereby contributing to an overall decrease in materials required to be shipped and stored. Less materials contributes to a reduction in waste products as well, thereby reducing the impact to the environment. Moreover, less boxes, pallets and warehouse space is therefore required. In addition, the decrease in materials utilized further allows more packages to be shipped and stored in specific areas, such as in truckloads and the like.
- multilayer structures methods of making the same, and packages made therefrom are provided wherein the multilayer structures have increased stiffness.
- multilayer structures, methods of making the same and packages made therefrom are provided made from multilayer structures having improved durability, strength, tear resistance and puncture resistance that may be made by a coextrusion process, without needing extra series of steps for laminating other structures thereto. Therefore, multilayer structures are provided that may be formed into packages that do not have double walls or patches. In addition, the multilayer structures provided herein do not require the extra steps, time and money to precisely position patches to strengthen a structure where bony protrusions and the like may damage the structure.
- FIG. 1 illustrates a cross-sectional view of a seven-layer structure in an embodiment of the present invention.
- Multilayer structures, methods of making the same and packages made therefrom are provided wherein the multilayer structures are useful for packaging meat products having bony protrusions and other like products having sharp protrusions.
- the bony protrusions make it difficult to utilize structures without some form of reinforcing material, such as a double-walled film structure or patches or the like.
- a multilayer coextruded structure made without double-walling or without the use of patches may be formed that has sufficient rigidity, strength, tear resistance and puncture resistance to hold bone-in meat products, while also protecting the products from the deleterious effects of oxygen.
- the multilayer structures of the present invention typically have at least one layer of nylon and a heat-sealant layer that preferably allows the film to be heat-sealed to itself or to another film to form a package having a space therein for bone-in meat.
- the packages made from the multilayer structures further comprise an oxygen barrier layer to protect the product contained therein from the deleterious effects of oxygen.
- the term “inner layer” refers to the layer of a package made from the coextruded multilayer structure that directly contacts the inner space of the package and/or directly contacts the product contained therein, especially when heat-shrunk around the product, as described in more detail below.
- the term “outer layer” refers to a layer of the coextruded multilayer structure disposed on the external surface thereof. Specifically, if a package is made from a non-laminated coextruded structure, the outer layer is disposed on the external surface of the package.
- the outer layer of the multilayer structures provides rigidity and strength to the film, and further provides protection from punctures, tears and the like, and is often referred to as an “abuse layer”.
- Materials that may be useful in the outer layer are those typically used for abuse layers in multilayer structures, such as low density polyethylene (“LDPE”), or heterogeneous or homogeneous ethylene alpha-olefin copolymers, such as linear low density polyethylene (“LLDPE”) and medium density polyethylene (“MDPE”) made by typical polymeric processes, such as Ziegler-Natta catalysis and metallocene-based catalysis.
- ethylene copolymers may be utilized as well, such as ethylene vinyl acetate copolymer (“EVA”) and ethylene methyl acrylate copolymer (“EMA”).
- EVA ethylene vinyl acetate copolymer
- EMA ethylene methyl acrylate copolymer
- Other materials may include polypropylene (“PP”), polyamides, ionomers, polyesters or blends of any of these materials.
- PP polypropylene
- polyamides polyamides
- ionomers ionomers
- polyesters or blends of any of these materials may be included in addition.
- an amount of slip and/or antiblock may be added to aid the outer layer in forming and to provide desirable characteristics.
- the outer layer comprises a blend of octene-based LLDPE and LDPE.
- a preferable range of LLDPE and LDPE utilized in the outer layer may be between about 50% by weight and about 90% by weight LLDPE and about 10% by weight and about 50% by weight LDPE.
- the blend of LLDPE and LDPE may be about 70% by weight LLDPE and about 30% by weight LDPE.
- the blend of the outer layer may comprise a small amount of antiblock and/or slip agent.
- the outer layer may comprise a polyamide or blend of polyamide materials.
- the coextruded multilayer structures of the present invention typically have at least one internal layer.
- An “internal layer” is a layer disposed within a multilayer structure, and is bonded on both sides to other layers.
- a preferred material that is useful as an internal layer is a polyamide.
- polyamide materials that are useful for the at least one internal layer include, but are not limited to, nylon 6, nylon 6,69, nylon 6,66, nylon 12, nylon 6,12, nylon 6, IPD,I, amorphous polyamide, or blends of any of these materials.
- the at least one internal layer is a blend of polyamide materials, such as, for example, a blend of semi-crystalline polyamide and amorphous polyamide, although amorphous polyamide is not necessary in the at least one internal layer.
- the internal layer may comprise nylon 6 or nylon 6,66 and amorphous polyamide, or a blend of nylon 6, nylon 6,69 and amorphous polyamide. It is preferable to utilize a blend of a large amount of semi-crystalline polyamide, such as about 70% by weight to about 99% by weight semi-crystalline polyamide, such as nylon 6 or nylon 6,66 or a blend of nylon 6 and nylon 6,69, with a small amount of amorphous polyamide, such as between about 1% by weight and about 30% by weight amorphous polyamide.
- the internal layer may comprise about 85% by weight to about 99% by weight semi-crystalline polyamide, such as nylon 6 or nylon 6,66 or a blend of nylon 6 and nylon 6,69, with about 1% by weight to about 15% by weight amorphous polyamide. Most preferably, the internal layer may comprise about 90% by weight to about 99% by weight semi-crystalline polyamide and about 1% by weight and about 10% by weight amorphous polyamide.
- the polyamide layers of the present invention may comprise a blend of a first semi-crystalline polyamide, a second semi-crystalline polyamide, and an amorphous polyamide.
- the polyamide layers may comprise between about 60% by weight and about 80% by weight of the first semi-crystalline polyamide, between about 10% by weight and about 30% by weight of the second semi-crystalline polyamide, and between about 1% by weight and about 30% by weight of the amorphous polyamide.
- polyamide blends described herein allow the internal layer of polyamide to retain softness and ease of processability while still imparting high puncture resistance, strength and stiffness to the film structure.
- polyamide blends comprising a small amount of amorphous polyamide have improved orientation and, therefore, shrink characteristics.
- a small amount of amorphous polyamide in the polyamide blend with semi-crystalline polyamide improves both out-of-line orientation and in-line orientation.
- the coextruded multilayer structures of the present invention may have a plurality of polyamide layers.
- structures may have an outer layer comprising polyamide and an internal layer comprising polyamide.
- the structures may have two or more internal layers of polyamide.
- the two or more layers of polyamide may preferably be separated by an internal core layer, such as an oxygen barrier layer, as described below, and may further be useful in bonding the oxygen barrier layer to other layers within the multilayer structure.
- the two or more layers of polyamide may be the same polyamide.
- the two layers may be different.
- the two or more layers of polyamide are identical, such as an identical blend of semi-crystalline polyamide and amorphous polyamide.
- the internal core layer of the present invention may be a barrier layer to provide protection from oxygen that may deleteriously affect oxygen-sensitive products that may be contained within packages made by the coextruded multilayer structures of the present invention, such as bone-in meat products.
- Materials that may be utilized as the barrier layers of the structures include, but are not limited to, ethylene vinyl alcohol copolymer (EVOH) and EVOH blends, such as EVOH blended with polyamide, EVOH blended with polyolefin, such as LLDPE, EVOH blended with ionomer, polyglycolic acid, blends thereof and other like oxygen barrier materials.
- EVOH ethylene vinyl alcohol copolymer
- EVOH blends such as EVOH blended with polyamide, EVOH blended with polyolefin, such as LLDPE, EVOH blended with ionomer, polyglycolic acid, blends thereof and other like oxygen barrier materials.
- Other barrier materials may include amorphous polyamide and polyvinylidene chloride-
- a preferable EVOH material utilized in the structures described herein has an ethylene content of between about 24 mol % and about 52 mol %. More preferably, the EVOH material utilized in the structures of the present invention have an ethylene content of between about 27 mol % and about 42 mol %. The decreased ethylene content of EVOH copolymers allows the structures to have greater barrier protection at relative humidity of less than about 93%.
- the multilayer structures of the present invention may further have a heat-sealant layer that may form heat-seals when heat and/or pressure is applied to the package.
- the structures of the present invention may be folded over onto themselves and sealed around edges to create a package with the bone-in meat products contained therein.
- the structures may be formed as a tube, whereby ends of the tube may be heat-sealed together to create a package for the product.
- a first structure of the present invention may be disposed adjacent a second structure of the present invention and sealed around edges of the structures to form a package for the bone-in meat or other like products.
- the heat-sealant layer materials include, but are not limited to, various polyolefins, such as low density polyethylene, linear low density polyethylene and medium density polyethylene.
- the polyethylenes may be made via a single site catalyst, such as a metallocene catalyst, or a Ziegler-Natta catalyst, or any other polyolefin catalyst system.
- other materials include, but are not limited to, polypropylene, ionomer, propylene-ethylene copolymer or blends of any of these materials.
- acid modified polyolefins and tie resins or concentrates such as, for example, anhydride modified polyethylene, may be utilized in the heat sealant layer, which may be useful for meat adhesion when the multilayer structure is heat shrunk about a bone-in meat product.
- the heat-sealant layer of the structure of the present invention may comprise a blend of octene-based linear low density polyethylene and low density polyethylene. More specifically, the heat-sealant layer may comprise between about 50% by weight and about 90% by weight LLDPE and between about 10% by weight and about 50% by weight LDPE. Most specifically, the heat-sealant layer comprises about 70% by weight LLDPE and about 30% by weight LDPE. Optionally, the heat-sealant layer comprises a small amount of slip and/or antiblock.
- the above-identified materials may be combined into a structure having at least three layers that has sufficient puncture resistance, strength and optical properties to form packages that are useful for packaging bone-in meat or other like products.
- the coextruded multilayer structures of the present invention are preferably coextruded and biaxially oriented via a double bubble process, whereby each layer of each of the multilayer structures is coextruded as a bubble and then cooled.
- Typical cooling processes include air cooling, water cooling or cooling via non-contact vacuum sizing.
- the coextruded multilayer structures may then be reheated and oriented in both the longitudinal and transverse directions.
- the coextruded multilayer structures of the present invention may be oriented via other orienting processes, such as tenter-frame orientation.
- the oriented multilayer structures are then heated to an annealing temperature and cooled while the multilayer structures maintain their oriented dimensions in a third bubble, thereby annealing the multilayer structures to relax residual stress and provide stability and strength to the multilayer structures while maintaining the heat shrinkability and superior optical characteristics of oriented multilayer structures.
- Use of a third bubble for purposes of annealing the oriented structures is often referred to as a triple-bubble process.
- the structures of the present invention may be partially or completely annealed. Annealing the multilayer structure allows for precise control over the degree of shrink and/or over the stability of the multilayer structure, and is typically done at a temperature between room temperature and the anticipated temperature at which the multilayer structure is desired to shrink.
- multilayer structures of the present invention may be further processed to get desirable characteristics.
- multilayer structures of the present invention may be cross-linked via known cross-linking processes, such as by electron-beam cross-linking either before or after orientation of the multilayer structure.
- Cross-linking may occur between layers (“inter-layer crosslinking”) of the structures or molecularly within at least one layer of a structure (“molecular cross-linking”).
- inter-layer crosslinking layers
- molecular cross-linking of EVOH occurs at about 6 megarads, which provides increased stiffness and barrier properties of the EVOH in the structures.
- any other radiation dosage may be utilized to promote inter-layer cross-linking or molecular cross-linking as may be apparent to one having ordinary skill in the art.
- the structures may be moisturized, by exposing the surfaces of the structures to water so that certain layers of the structures, such as the polyamide layers, absorb the water thus plasticizing the polyamide layers, thereby making the polyamide layers softer and stronger.
- Moisturizing the structures typically occurs by exposing the surface of the structures to water, such as a mist, prior to rolling the structures for storage. During storage of the structures, the water is absorbed by the layers of the structures, such as the polyamide layers, thereby plasticizing the structure.
- other methods for plasticizing the structures are contemplated by the present invention, and the invention should not be limited as described herein.
- the structures of the present invention have a thickness of between about 1 and about 8 mils. Most preferably, the structures of the present invention have a thickness of between about 1.5 mils and about 5 mils A balance must be reached between having a cost-effective package, thereby minimizing the thickness of the structures, and having a package that provides adequate puncture and tear resistance for bone-in meat or other like products. It is believed that a combination of materials used in the structures contributes to the advantageous properties of the structures of the present invention, such as puncture resistance, strength, durability, and optical properties, without requiring relatively thick structures.
- the structures of the present invention are utilized to make heat shrinkable bags, such as by coextruding heat shrinkable tubes, cutting said tubes to the desired sizes, placing product within said tubes, sealing the open ends of the tubes, and heat-shrinking the tubes around the products.
- packages may be made by folding structures so that the heat-sealant layers of the structures are in face-to-face contact.
- packages may be made by heat-sealing first walls of first multilayer structures to second walls of second multilayer structures to form a space for a product to be contained therein.
- any other method of making said packages are contemplated by the present invention.
- Machinery contemplated as being used to make the bags or packages of the present invention include intermittent motion bag-making machines, rotary bag-making machines, or multibaggers, which are described in U.S. Pat. No. 6,267,661 to Melville, the disclosure of which is expressly incorporated herein in its entirety.
- tubes are produced using a double-bubble or a triple-bubble process, as described above.
- the surfaces of the tubes may be lightly dusted with starch.
- An open end of the tube is then heat-sealed with one end of the tube left open for adding the product to the package.
- Other types of packages and uses are contemplated by the present invention, such as vertical form, fill and seal packages and lidstock for rigid or semi-rigid trays.
- the structures of the present invention may be useful as cook-in bags or the like.
- the tubes then have product placed therein, such as bone-in meat.
- the tubes are then evacuated of air and the open end of each is heat-sealed.
- the tubes that have been evacuated of air and heat-sealed are then shrunk around the product by sending the tubes through an oven, a hot water tunnel or other similar heat-shrink apparatus.
- the structures of the present invention may have at least three layers, but preferably contain four, five, six or more layers. Most preferably, the structures comprise seven layers. In addition, structures having greater than seven layers are contemplated by the present invention.
- Each structure preferably has a heat-sealant layer, a polyamide layer, and a barrier layer of, preferably, EVOH copolymer.
- Examples 1-2 illustrate five-layer structures of the present invention.
- the five-layer structures each comprise an outer layer of polyamide, a barrier layer of EVOH copolymer, an internal layer of polyamide, such that the outer layer of polyamide and the internal layer of polyamide are disposed adjacent to the barrier layer of EVOH copolymer.
- a tie layer is disposed adjacent to the internal layer of polyamide, which binds the internal layer of polyamide to the heat-sealant layer, comprising a blend of LLDPE and LDPE.
- the 5-layer structures of Examples 1 and 2 were about 4.1 mils thick.
- Example 3 includes the 5-layer structure of Example 2 that was moisturized by the application of water to the structure, thereby plasticizing the structure. Specifically, the water was applied as a mist or spray to the 5-layer structure of Example 2, and the 5-layer structure of Example 2 was wound on a roll and the water was allowed to penetrate the film structure to plasticize the film structure, specifically the polyamide layers.
- the 5-layer moisturized structure of Example 3 was about 5.6 mils thick.
- Table 1 illustrates comparative test data for Examples 1-3. TABLE 1 Test Ex. 1 Ex. 2 Ex. 3 Caliper (mil) 4.1 4.1 5.6 45° Gloss (units) 90.2 92.2 70.1 Haze (%) 4.0 3.6 9.0 Yellowness Index 1.1 1.1 1.1 MD Secant Modulus (psi) 237,900 243,900 32,200 CD Secant Modulus (psi) 250,800 246,800 36,400 Puncture Resistance (lb/mil) 21.2 22.2 11.5 MD Free Shrink @200° F. 19 18 19 CD Free Shrink @200° F. 28 28 20 OTR @ 73° F./0% RH 0.8 2.4 — (cc/m 2 /day/atm)
- the structures preferably comprise a first outer layer 10 , a first tie layer 12 , a first polyamide layer 14 , a barrier layer 16 , a second polyamide layer 18 , a second tie layer 20 and a heat-sealant layer 22 .
- first outer layer 10 a first outer layer 10
- first tie layer 12 a first polyamide layer 14
- barrier layer 16 a barrier layer 16
- second polyamide layer 18 a second tie layer
- a heat-sealant layer 22 a heat-sealant layer 22 .
- the outer layer 10 of the seven-layer structure illustrated in FIG. 2 provides rigidity and strength to the structure, and further provides protection from scratches, tears and the like.
- the outer layer 10 is between about 5% by volume and about 25% by volume of the entire structure.
- the outer layer 10 comprises about 17.5% by volume of the entire structure.
- the multilayer structures of the present invention may further comprise tie layers disposed between other layers of the multilayer structures.
- a “tie layer” is defined as an internal layer that provides adhesion or bonding to two layers of a coextruded structure and is typically disposed adjacent to and between the two layers of the coextruded structure.
- the multilayer structure 1 described with reference to FIG. 1 may include a first tie layer 12 and a second tie layer 20 , which are disposed adjacent the outer layer 10 and the heat-sealant layer 22 , respectively.
- the first and second tie layers may be utilized to bind the outer layer 10 and the heat-sealant layer 22 to other internal layers, such as the first polyamide layer 14 and/or second polyamide layer 18 .
- the first tie layer 12 and/or second tie layer 20 may comprise modified polyolefins, such as maleic anhydride modified polyolefins.
- Polyolefins useful as the first tie layer 12 and/or the second tie layer 20 of the present invention include, but are not limited to, anhydride modified linear low density polyethylene or any other maleic anhydride modified polyolefin polymer or copolymer, such as anhydride modified ethylene-vinyl acetate copolymer and/or anhydride modified ethylene methyl acrylate copolymer.
- the first tie layer 12 and/or the second tie layer 20 may comprise a material that is not typically utilized as a tie resin.
- first tie layer 12 and/or the second tie layer 20 may comprise materials that are not modified with maleic anhydride, such as ethylene vinyl acetate copolymer and ethylene methyl acrylate copolymer.
- Other polymeric materials that may be useful as tie layers include, but are not limited to, acid terpolymer comprising ethylene, acrylic acid and methyl acrylate, polyamide, and polystyrene block copolymers.
- the first tie layer 12 and/or the second tie layer 20 may comprise blends of tie resins with other polymeric material, such as polyolefins or the like.
- the first tie layer 12 and/or the second tie layer 20 comprise a maleic anhydride modified ethylene methyl acrylate copolymer, such as, for example, BYNEL® from DuPont.
- the first tie layer comprises maleic anhydride modified linear low density polyethylene, such as, for example, ADMER® from Mitsui.
- the first tie layer 12 and the second tie layer 20 may not be the same material, but may be different materials that are useful for tying together the outer layer 10 to an internal layer of polyamide and/or the sealant layer 22 to an internal layer of polyamide.
- first tie layer 12 and second tie layer 20 may be any thickness useful for the present invention, it is preferable that the first tie layer 12 and second tie layer 20 each comprise between about 2% by volume and about 15% by volume of the multilayer structures. Most preferably, the first tie layer 12 and/or the second tie layer 20 each comprise about 5% by volume of the entire multilayer structures.
- the first polyamide layer 14 and/or second polyamide layer 18 may be utilized to protect the barrier layer 16 , and to provide rigidity and strength to structures made from the present invention.
- the polyamide layers further provide ease of orientation, better shrink force and lower oxygen transmission rates through the multilayer structure.
- the first polyamide layer 14 and second polyamide layer 18 may not be the same material, and may be different depending on the desired characteristics of the structures.
- each of the first polyamide layer 14 and/or second polyamide layer 18 of the seven layer structures may be between about 10% by volume and about 60% by volume of the structures More specifically, each of the polyamide layers of the seven layer structures may be between about 10% by volume and about 40% by volume of the structures. Most preferably, each of the polyamide layers of the seven layer structures may be between about 15% and about 25% by volume of the structures.
- Both the first polyamide layer 14 and second polyamide layer 18 may together comprise between about 20% by volume and about 80% by volume of the structures. More specifically, both the first polyamide layer 14 and second polyamide layer 18 may together comprise between about 30% by volume and about 50% by volume of the structures. Most preferably, both of the first polyamide layer 14 and second polyamide layer 18 may together comprise about 40% by volume of the film. While it is preferable that the two polyamide layers 14 , 18 be of the same thickness, this is not necessary, and the first polyamide layer 14 and the second polyamide layer 18 may be different thicknesses.
- the heat-sealant layer 22 of the seven layer structure illustrated in FIG. 1 may be any thickness.
- the heat-sealant layer may comprise between about 20% by volume and about 30% by volume of the entire structure.
- the heat-sealant layer 22 of the present invention may comprise about 27.5% by volume of the entire structure, especially when the outer layer 10 comprises about 17.5% by volume of the entire structure. It is further preferable that the outer layer 10 and the heat-sealant layer 22 comprise different amounts of polymeric material, thereby creating an unbalanced structure.
- the entire structure will be thinner, thereby allowing a heat-sealing mechanism such as a heat-sealing bar, to heat the sealant layer 22 and more easily and effectively melt the sealant layer 22 to form a heat-seal.
- a heat-sealing mechanism such as a heat-sealing bar
- having more polymeric material in the heat-sealant layer 22 allows the heat-sealant layer 22 to more easily melt and flow, thereby forming a strong seal when heat-sealed to another structure or to itself.
- the seven-layer structures of the present invention are preferably coextruded and oriented thereby producing structures that are heat shrinkable.
- the total orientation factor of the seven-layer structures are preferably between about 6 and about 20. More preferably, the total orientation factor is between about 8 and about 13.
- the structures of the present invention may further be partially or completely annealed, preferably at a temperature of between room temperature and the temperature at which the structure is heat shrunk. Annealing the structures stabilizes the structures by removing residual stresses within the oriented structures. Typically, the structures are maintained in a third bubble and heated above their annealing temperatures, which allows residual stresses in the oriented structures to relax, thereby providing more stable multilayer structures.
- the seven layer structure of Example 4 was made by coextruding the seven layers together and biaxially orienting the resulting structure.
- the seven layer structure has a total orientation factor of about 11.7. Further, the structure was annealed to stabilize the structure. The coextrusion, orientation, and annealing of the seven layer structure of Example 4 were completed in a triple bubble process. The final structure thickness was about 3.3 mils.
- the seven-layer structure of Example 5 was made by coextruding the seven layers together and biaxially orienting the structure.
- the structure had a total orientation factor of about 11.4.
- the seven-layer structure of Example 5 was annealed to stabilize the final structure.
- the coextrusion, orientation, and annealing of the seven layer structure of Example 5 were completed in a triple bubble process.
- the final structure thickness was about 3.7 mils.
- Example 5 This structure of Example 5 is similar to the structure described in Example 4, except that the structure of Example 5 contains differing amounts of materials in the outer layer and the heat-sealant layer thereby creating an unbalanced structure. Specifically, the outer layer comprises about 17.5% by volume of the structure, and the sealant layer comprises about 27.5% by volume of the structure.
- the seven-layer structure of Example 6 was made by coextruding the seven layers together and biaxially orienting the structure.
- the structure had a total orientation factor of about 9.1.
- the seven layer structure of Example 6 was annealed to stabilize the final structure.
- the coextrusion, orientation, and annealing of the seven layer structure of Example 6 were completed in a triple bubble process.
- the final structure thickness was about 3.9 mils.
- the seven-layer structure of Example 6 is similar to the seven-layer structure of Example 5, including differing amounts of materials in the outer layer and the heat-sealant layer.
- the structure of Example 6 includes more polyamide material than the structure of Example 5. More specifically, each polyamide layer in the structure of Example 6 comprises about 25% by volume of the structure. The entire structure comprises about 50% by volume total of polyamide.
- the seven-layer structure of Example 7 was made by coextruding the seven layers together and biaxially orienting the structure.
- the structure had a total orientation factor of about 11.2.
- the seven-layer structure of Example 7 was annealed to stabilize the final structure.
- the coextrusion, orientation, and annealing of the seven layer structure of Example 7 were completed in a triple bubble process.
- the final structure thickness was about 3.7 mils.
- Example 7 The seven-layer structure of Example 7 is almost identical to the seven-layer structures of Example 5, except that the core layer comprises EVOH having an ethylene content of about 32 mol %, as opposed to about 48 mol %, as shown above with respect to Example 5.
- the seven-layer structure of Example 8 was made by coextruding the seven layers together and biaxially orienting the structure. In addition, the seven-layer structure of Example 8 was annealed to stabilize the final film. The coextrusion, orientation, and annealing of the seven layer structure of Example 8 were completed in a triple bubble process. The final structure thickness was about 4.0 mils.
- Each of the polyamide layers of the seven layer structure of Example 8 comprises a blend of about 92% by weight nylon 6 and about 8% by weight amorphous polyamide.
- the seven-layer structure of Example 9 was made by coextruding the seven layers together and biaxially orienting the structure. In addition, the seven-layer structure of Example 9 was annealed to stabilize the final film. The coextrusion, orientation, and annealing of the seven layer structure of Example 9 were completed in a triple bubble process. The final structure thickness was about 4.0 mils.
- Each of the polyamide layers of the seven layer structure of Example 9 comprises a blend of about 92% by weight nylon 6 and about 8% by weight amorphous polyamide.
- Table 2 provide comparative test data for each of the Examples 4-9: TABLE 2 Test Ex. 4 Ex. 5 Ex. 6 Ex. 7 Ex. 8 Ex. 9 Caliper (mil) 3.6 3.4 3.5 3.7 4.0 3.85 45° Gloss (units) 72.6 72.5 46 69.8 72.8 71.4 Haze (%) 7.8 10 25.7 9.6 7.9 8.6 Yellowness Index 0.16 0.19 0.12 0.20 0.22 0.13 MD Secant Modulus (psi) 111,500 130,400 145,200 132,700 131,900 121,500 CD Secant Modulus (psi) 120,300 131,900 160,000 144,800 157,400 156,000 Puncture Resistance (lb/mil) 16.8 17.9 21.9 14.5 18.2 15.3 MD Free Shrink @200° F. 24 25 26 26 24 28 CD Free Shrink @200° F. 30 29 35 30 29 29 OTR @ 73° F./0% RH 11.3 14.4 11.2 1.8 2.0 3.1 (ccc
Landscapes
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Wrappers (AREA)
- Laminated Bodies (AREA)
Priority Applications (12)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/735,366 US20040175466A1 (en) | 2003-03-07 | 2003-12-12 | Multilayer barrier structures, methods of making the same and packages made therefrom |
CA2518401A CA2518401C (fr) | 2003-03-07 | 2004-03-05 | Structures barrieres multicouches, procedes de fabrication de ces dernieres et emballages fabriques a partir desdites structures |
EP04717966A EP1603812A4 (fr) | 2003-03-07 | 2004-03-05 | Structures barrieres multicouches, procedes de fabrication de ces dernieres et emballages fabriques a partir desdites structures |
AU2004220068A AU2004220068B2 (en) | 2003-03-07 | 2004-03-05 | Multilayer barrier structures, methods of making the same and packages made therefrom |
NZ542355A NZ542355A (en) | 2003-03-07 | 2004-03-05 | Multilayer barrier structures, methods of making the same and packages made therefrom |
PCT/US2004/006639 WO2004080804A2 (fr) | 2003-03-07 | 2004-03-05 | Structures barrieres multicouches, procedes de fabrication de ces dernieres et emballages fabriques a partir desdites structures |
MXPA05009541A MXPA05009541A (es) | 2003-03-07 | 2004-03-05 | Estructuras de barreras multicapas, metodos de preparacion y envases realizados a partir de ellas. |
BRPI0408670-8A BRPI0408670A (pt) | 2003-03-07 | 2004-03-05 | estruturas de barreira de multicamada, seus métodos de fabricação e embalagens feitas das mesmas |
ARP040100717A AR043496A1 (es) | 2003-03-07 | 2004-03-05 | Estructuras de barreras multicapas, metodos de preparacion y envases realizados a partir de ellas |
EP12180844.8A EP2679517A1 (fr) | 2003-03-07 | 2004-03-05 | Structures barrieres multicouches, procedes de fabrication de ces dernieres et emballages fabriques a partir desdites structures |
US11/029,200 US9498936B2 (en) | 2003-03-07 | 2005-01-04 | Multilayer barrier structures, methods of making the same and packages made therefrom |
US15/297,909 US20170036426A1 (en) | 2003-03-07 | 2016-10-19 | Multilayer barrier structures, methods of making the same and packages made therefrom |
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US45274703P | 2003-03-07 | 2003-03-07 | |
US45364103P | 2003-03-11 | 2003-03-11 | |
US10/735,366 US20040175466A1 (en) | 2003-03-07 | 2003-12-12 | Multilayer barrier structures, methods of making the same and packages made therefrom |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/029,200 Continuation US9498936B2 (en) | 2003-03-07 | 2005-01-04 | Multilayer barrier structures, methods of making the same and packages made therefrom |
Publications (1)
Publication Number | Publication Date |
---|---|
US20040175466A1 true US20040175466A1 (en) | 2004-09-09 |
Family
ID=32931359
Family Applications (3)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/735,366 Abandoned US20040175466A1 (en) | 2003-03-07 | 2003-12-12 | Multilayer barrier structures, methods of making the same and packages made therefrom |
US11/029,200 Expired - Fee Related US9498936B2 (en) | 2003-03-07 | 2005-01-04 | Multilayer barrier structures, methods of making the same and packages made therefrom |
US15/297,909 Abandoned US20170036426A1 (en) | 2003-03-07 | 2016-10-19 | Multilayer barrier structures, methods of making the same and packages made therefrom |
Family Applications After (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/029,200 Expired - Fee Related US9498936B2 (en) | 2003-03-07 | 2005-01-04 | Multilayer barrier structures, methods of making the same and packages made therefrom |
US15/297,909 Abandoned US20170036426A1 (en) | 2003-03-07 | 2016-10-19 | Multilayer barrier structures, methods of making the same and packages made therefrom |
Country Status (8)
Country | Link |
---|---|
US (3) | US20040175466A1 (fr) |
EP (2) | EP2679517A1 (fr) |
AR (1) | AR043496A1 (fr) |
AU (1) | AU2004220068B2 (fr) |
BR (1) | BRPI0408670A (fr) |
CA (1) | CA2518401C (fr) |
NZ (1) | NZ542355A (fr) |
WO (1) | WO2004080804A2 (fr) |
Cited By (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20070092744A1 (en) * | 2005-10-13 | 2007-04-26 | Plasticos Dise S.A. | Polymer compositions and films and method of making |
US20080128416A1 (en) * | 2006-12-01 | 2008-06-05 | Cryovac, Inc. | Stress concentrator for opening a flexible container |
US20080182053A1 (en) * | 2007-01-29 | 2008-07-31 | Broadus Michael E | Shrink film containing semi-crystalline polyamide and process for making same |
US20080179780A1 (en) * | 2007-01-29 | 2008-07-31 | Broadus Michael E | Process for making shrink film comprising rapidly-quenched semi-crystalline polyamide |
US20080182051A1 (en) * | 2007-01-29 | 2008-07-31 | Cryovac, Inc. | Heat shrinkable retortable packaging article and process for preparing retorted packaged product |
US20080292225A1 (en) * | 2007-05-21 | 2008-11-27 | Dayrit Richard M | Bag made from high-strength heat-shrinkable film exhibiting directional tear, and process utilizing same |
US20080314465A1 (en) * | 2007-06-21 | 2008-12-25 | Samsung Electronics Co., Ltd. | Microfluidic valve, method of manufacturing the same, and microfluidic device comprising the microfluidic valve |
US20130172453A1 (en) * | 2011-12-29 | 2013-07-04 | Cheil Industries Inc. | Polyamide Resin Composition Having Improved Physical Properties Including Thin-wall Moldability |
US20140151937A1 (en) * | 2012-12-04 | 2014-06-05 | Pexcor Manufacturing Company Inc. | Production method of plastic pipe in layers |
US8957142B2 (en) | 2013-02-01 | 2015-02-17 | Cheil Industries Inc. | Polyamide resin composition having excellent photostability and discoloration resistance |
US8957146B2 (en) | 2010-12-15 | 2015-02-17 | Cheil Industries Inc. | Polyamide resin composition with excellent reflectivity, heat resistance, and water resistance |
US9018296B2 (en) | 2012-12-31 | 2015-04-28 | Cheil Industries Inc. | Thermoplastic resin composition having excellent surface gloss, reflectance, anti-yellowing property and moldability |
US9840610B2 (en) | 2014-09-30 | 2017-12-12 | Lotte Advanced Materials Co., Ltd. | Thermoplastic resin composition and molded article using the same |
WO2018145885A1 (fr) * | 2017-02-09 | 2018-08-16 | Constantia Hueck Folien Gmbh & Co. Kg | Film composite comportant une barrière aux huiles minérales |
US10131785B2 (en) | 2015-06-30 | 2018-11-20 | Lotte Advanced Materials Co., Ltd. | Polyester resin composition with excellent impact resistance and light reliability and molded article using the same |
US10202229B2 (en) | 2007-05-21 | 2019-02-12 | Cryovac, Inc. | Easy opening packaging article made from heat-shrinkable film exhibiting directional tear |
US10301449B2 (en) | 2013-11-29 | 2019-05-28 | Lotte Advanced Materials Co., Ltd. | Thermoplastic resin composition having excellent light stability at high temperature |
US10508190B2 (en) | 2014-12-17 | 2019-12-17 | Lotte Advanced Materials Co., Ltd. | Polyester resin composition and molded article manufactured therefrom |
US10636951B2 (en) | 2014-06-27 | 2020-04-28 | Lotte Advanced Materials Co., Ltd. | Thermoplastic resin composition having excellent reflectivity |
US10822490B2 (en) | 2013-12-30 | 2020-11-03 | Lotte Advanced Materials Co., Ltd. | Thermoplastic resin composition having excellent shock resistance and light resistance |
Families Citing this family (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20040175464A1 (en) | 2003-03-07 | 2004-09-09 | Blemberg Robert J. | Multilayer structures, packages, and methods of making multilayer structures |
US20040175466A1 (en) | 2003-03-07 | 2004-09-09 | Douglas Michael J. | Multilayer barrier structures, methods of making the same and packages made therefrom |
EP1827820B8 (fr) | 2004-12-10 | 2016-10-12 | Bemis Company, Inc. | Films d'emballage a compositions de melange de nylons |
WO2006116389A2 (fr) * | 2005-04-25 | 2006-11-02 | Advanced Technology Materials, Inc. | Conditionnements et methodes de stockage et de distribution de matieres |
US20100015423A1 (en) * | 2008-07-18 | 2010-01-21 | Schaefer Suzanne E | Polyamide structures for the packaging of moisture containing products |
LT3027534T (lt) * | 2013-08-02 | 2017-10-10 | Roquette Freres | Lankstusis kaupiklis, apimantis lankstųjį konteinerį ir vidinį įdėklą, jo gamybos būdas bei naudojimas |
USD809116S1 (en) | 2015-11-02 | 2018-01-30 | Pura Scents | Dispenser |
WO2018182712A1 (fr) * | 2017-03-31 | 2018-10-04 | Bemis Company, Inc. | Film récupérant après une stérilisation en autoclave |
WO2019177865A1 (fr) * | 2018-03-15 | 2019-09-19 | Advansix Resins & Chemicals Llc | Film stratifié, emballage et procédés pour matériaux sensibles à l'oxygène |
US20220048280A1 (en) * | 2019-10-07 | 2022-02-17 | Epl Limited | Multilayer film and implementations thereof |
JP6933242B2 (ja) * | 2019-12-18 | 2021-09-08 | 住友ベークライト株式会社 | 多層フィルム |
US20220380101A1 (en) * | 2021-05-28 | 2022-12-01 | CC-Pak LLC | Low temperature sealable bag |
Citations (65)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4469742A (en) * | 1983-01-31 | 1984-09-04 | W. R. Grace & Co., Cryovac Div. | Pasteurizable, cook-in shrink film |
US4534984A (en) * | 1983-08-16 | 1985-08-13 | W. R. Grace & Co., Cryovac Div. | Puncture-resistant bag and method for vacuum packaging bone-in meat |
US4561920A (en) * | 1984-02-08 | 1985-12-31 | Norchem, Inc. Formerly Northern Petrochemical Company | Biaxially oriented oxygen and moisture barrier film |
US4601929A (en) * | 1982-07-27 | 1986-07-22 | Naturin-Werk Becker & Company | Single-layer elastic tubular film of polyamide used for packaging paste substances and a process for the production of such film |
US4704101A (en) * | 1983-06-30 | 1987-11-03 | W.R. Grace & Co., Cryovac Div. | Method for making a puncture resistant bag |
US4735855A (en) * | 1986-08-04 | 1988-04-05 | W. R. Grace & Co., Cryovac Div. | Thermoformable laminate |
US4746562A (en) * | 1986-02-28 | 1988-05-24 | W. R. Grace & Co., Cryovac Div. | Packaging film |
US4753700A (en) * | 1986-02-28 | 1988-06-28 | W. R. Grace & Co., Cryovac Div. | Packaging film |
US4755419A (en) * | 1986-03-21 | 1988-07-05 | W. R. Grace & Co., Cryovac Div. | Oxygen barrier oriented shrink film |
US4755403A (en) * | 1985-06-03 | 1988-07-05 | W. R. Grace & Co., Cryovac Div. | Protective patch for shrinkable bag |
US4765857A (en) * | 1985-06-03 | 1988-08-23 | W. R. Grace & Co., Cryovac Div. | Protective patch for shrinkable bag |
US4770731A (en) * | 1985-06-03 | 1988-09-13 | W. R. Grace & Co.-Conn. | Method of making a patch for a shrinkable bag |
US4801486A (en) * | 1985-09-30 | 1989-01-31 | W. R. Grace & Co.-Conn. | Thermoplastic multi-layer packaging film and bags made therefrom |
US4851290A (en) * | 1988-01-06 | 1989-07-25 | Viskase Corporation | Multilayer thermoplastic film |
US4855178A (en) * | 1988-05-02 | 1989-08-08 | E. I. Du Pont De Nemours And Company | Composite chemical barrier fabric |
US4888223A (en) * | 1987-05-21 | 1989-12-19 | Noritsugu Sugimoto | Food-packaging material and process for preparing the same |
US4909726A (en) * | 1988-03-24 | 1990-03-20 | Grumman Aerospace Corporation | Impact-resistant film for chub packaging |
US4937112A (en) * | 1987-12-18 | 1990-06-26 | W. R. Grace & Co.-Conn. | High strength coextruded film for chub packaging |
US4977022A (en) * | 1988-03-15 | 1990-12-11 | W. R. Grace & Co.-Conn. | Barrier stretch film |
US4997710A (en) * | 1988-09-29 | 1991-03-05 | W. R. Grace & Co.-Conn. | Barrier coextruded film for cook-in applications |
US5004647A (en) * | 1986-03-21 | 1991-04-02 | W. R. Grace & Co.-Conn. | Oxygen barrier biaxially oriented film |
US5020922A (en) * | 1983-06-30 | 1991-06-04 | W. R. Grace & Co.-Conn. | Bone puncture resistant bag |
US5037683A (en) * | 1988-09-26 | 1991-08-06 | W. R. Grace & Co.-Conn. | High strength laminated film for chub packaging |
US5053259A (en) * | 1988-08-23 | 1991-10-01 | Viskase Corporation | Amorphous nylon copolymer and copolyamide films and blends |
US5079051A (en) * | 1989-12-08 | 1992-01-07 | W. R. Grace & Co.-Conn. | High shrink energy/high modulus thermoplastic multi-layer packaging film and bags made therefrom |
US5374459A (en) * | 1993-04-06 | 1994-12-20 | W. R. Grace & Co.-Conn. | Packaging material for long-term storage of food products |
US5402625A (en) * | 1993-05-04 | 1995-04-04 | W. R. Grace & Co.-Conn. | Bag loader for bone-in products |
US5447591A (en) * | 1993-08-04 | 1995-09-05 | W. R. Grace & Co.-Conn. | Trap printing method for bone-in meat containers |
US5482770A (en) * | 1992-11-03 | 1996-01-09 | W. R. Grace & Co.-Conn. | Highly oriented multilayer film |
US5482771A (en) * | 1992-09-18 | 1996-01-09 | W. R. Grace & Co.-Conn. | Moisutre barrier film |
US5491009A (en) * | 1990-08-03 | 1996-02-13 | W. R. Grace & Co.-Conn. | Amorphous nylon composition and films |
USRE35285E (en) * | 1985-09-30 | 1996-06-25 | W. R. Grace & Co.-Conn. | Thermoplastic multi-layer packaging film and bags made therefrom |
US5540646A (en) * | 1993-04-21 | 1996-07-30 | W. R. Grace & Co.-Conn. | Method of making a shrinkable bag with protective patch |
US5545419A (en) * | 1994-07-21 | 1996-08-13 | W. R. Grace & Co.-Conn. | Patch bag having supplemental seal |
US5549943A (en) * | 1992-09-23 | 1996-08-27 | Viskase Corporation | Heat shrinkable nylon food casing with a polyolefin core layer |
US5562996A (en) * | 1990-06-27 | 1996-10-08 | Gunze Limited | Multi-layer films |
US5595623A (en) * | 1990-11-16 | 1997-01-21 | W. R. Grace Co.-Conn. | Method for making a barrier film with improved extensibility for cheese packaging |
US5698279A (en) * | 1992-09-23 | 1997-12-16 | Viskase Corporation | Heat shrinkable nylon food casing having a functionalized ethylenic polymer core layer |
US5741566A (en) * | 1993-02-19 | 1998-04-21 | Pharmacia & Upjohn Aktiebolag | Autoclavable multilayer films |
US5763095A (en) * | 1995-11-29 | 1998-06-09 | W. R. Grace & Co.-Conn. | Breathable film for cheese packaging |
US5866214A (en) * | 1995-07-28 | 1999-02-02 | W. R. Grace & Co.-Conn. | Film backseamed casings therefrom, and packaged product using same |
US5910374A (en) * | 1992-09-18 | 1999-06-08 | Cryovac, Inc. | Moisture barrier film |
US5914164A (en) * | 1995-05-24 | 1999-06-22 | Cryovac, Inc. | Multilayer oxygen-barrier packaging film |
US6063417A (en) * | 1996-02-28 | 2000-05-16 | Cryovac, Inc. | Cheese packaging film |
US6068933A (en) * | 1996-02-15 | 2000-05-30 | American National Can Company | Thermoformable multilayer polymeric film |
US6106935A (en) * | 1994-07-13 | 2000-08-22 | Cryovac, Inc. | Heat sealable film |
US6150011A (en) * | 1994-12-16 | 2000-11-21 | Cryovac, Inc. | Multi-layer heat-shrinkage film with reduced shrink force, process for the manufacture thereof and packages comprising it |
US6206569B1 (en) * | 1997-03-07 | 2001-03-27 | Curwood, Inc. | Puncture-resistant barrier pouch |
US6210765B1 (en) * | 1996-01-11 | 2001-04-03 | Mitsui Petrochemical Industrie Ltd | Adhesive polyethylene compositions and multi-layer laminated films using the same |
US6221410B1 (en) * | 1992-09-25 | 2001-04-24 | Cryovac, Inc. | Backseamed casing and packaged product incorporating same |
US6221470B1 (en) * | 1996-02-23 | 2001-04-24 | Cryovac, Inc. | Multilayer oxygen barrier packaging film |
US6224956B1 (en) * | 1990-05-17 | 2001-05-01 | Cryovac, Inc. | Breathable abuse resistant film for packaging cheese |
US20010010846A1 (en) * | 1998-05-04 | 2001-08-02 | Frank M. Hofmeister | Multiple layer film with amorphous polyamide layer |
US6274228B1 (en) * | 1998-07-22 | 2001-08-14 | Cryovac, Inc. | Heat-shrinkable film with improved inter-ply adhesion |
US6287613B1 (en) * | 1994-12-12 | 2001-09-11 | Cryovac Inc | Patch bag comprising homogeneous ethylene/alpha-olefin copolymer |
US6291041B1 (en) * | 1999-05-10 | 2001-09-18 | Curwood, Inc. | Heat resistant nylon multi-layer film |
US6299984B1 (en) * | 1998-09-14 | 2001-10-09 | Cryovac, Inc. | Heat-shrinkable multilayer thermoplastic film |
US6333061B1 (en) * | 1996-11-22 | 2001-12-25 | Cryovac, Inc. | Packaging article |
US6346285B1 (en) * | 1996-08-16 | 2002-02-12 | Cryovac, Inc. | Article comprising film having polyamide sealant, polyamide core layer, and O2-barrier layer, and packaged product using same |
US20020055006A1 (en) * | 2000-04-14 | 2002-05-09 | Vogel Randall Allen | Multilayer, co-extruded, ionomeric decorative surfacing |
US6458469B1 (en) * | 1999-07-08 | 2002-10-01 | Exxonmobil Chemical Company | Multilayer oriented films with metallocene catalyzed polyethylene skin layer |
US20030087114A1 (en) * | 2001-11-06 | 2003-05-08 | Cryovac, Inc. | Irradiated multilayer film having seal layer containing hyperbranched polymer |
US6579584B1 (en) * | 1998-12-10 | 2003-06-17 | Cryovac, Inc. | High strength flexible film package utilizing thin film |
US6599639B2 (en) * | 2001-03-16 | 2003-07-29 | Cryovac, Inc. | Coextruded, retortable multilayer film |
US6663905B1 (en) * | 1998-03-16 | 2003-12-16 | Cryovac, Inc. | Patch bag having wrap-around patch |
Family Cites Families (154)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2664358A (en) | 1951-01-26 | 1953-12-29 | Edwin H Eichler | Canning whole food articles |
US3456044A (en) * | 1965-03-12 | 1969-07-15 | Heinz Erich Pahlke | Biaxial orientation |
US3694231A (en) | 1970-08-17 | 1972-09-26 | Gentry Corp | Process for preparing shelf-stable,free-flowing dehydrated cheese products in granulated or powdered form |
US3741253A (en) * | 1971-03-30 | 1973-06-26 | Grace W R & Co | Laminates of ethylene vinyl acetate polymers and polymers of vinylidene chloride |
US3997383A (en) * | 1975-03-10 | 1976-12-14 | W. R. Grace & Co. | Cross-linked amide/olefin polymeric laminates |
ES448091A1 (es) * | 1975-05-22 | 1977-07-01 | Grace W R & Co | Procedimiento para mejorar la resistencia a la deslaminacionde un laminado de peliculas estirado. |
US4178401A (en) * | 1978-01-09 | 1979-12-11 | W. R. Grace & Co. | Packaging film comprising a blended self-welding layer |
US4278738A (en) * | 1978-03-10 | 1981-07-14 | W. R. Grace & Co. | Ethylene-vinyl acetate copolymer film laminate |
JPS6043318B2 (ja) | 1978-07-18 | 1985-09-27 | 富士写真フイルム株式会社 | 感熱記録紙 |
US4457960A (en) * | 1982-04-26 | 1984-07-03 | American Can Company | Polymeric and film structure for use in shrink bags |
DE3306189A1 (de) | 1983-02-23 | 1984-08-23 | Hoechst Ag, 6230 Frankfurt | Mehrschichtige folie mit einer gas- und aroma-sperrschicht, verfahren zu ihrer herstellung und ihre verwendung |
US4501798A (en) | 1983-05-05 | 1985-02-26 | American Can Company | Unbalanced oriented multiple layer film |
JPS6035728A (ja) | 1983-07-20 | 1985-02-23 | Fuji Photo Film Co Ltd | 写真感光材料用包装材料 |
US4576844A (en) | 1983-11-28 | 1986-03-18 | C-I-L Inc. | Shipping bag |
US5069955A (en) | 1983-12-06 | 1991-12-03 | American National Can Company | Film and blends of polyetheramide block copolymer and ethylene vinyl alcohol |
CA1240247A (fr) | 1984-06-08 | 1988-08-09 | Matthew Koschak | Pellicule a couches multiples orientees, non equilibrees |
US4724185A (en) * | 1985-09-17 | 1988-02-09 | W. R. Grace & Co., Cryovac Div. | Oxygen barrier oriented film |
US4777095A (en) * | 1985-09-25 | 1988-10-11 | Okura Industrial Co., Ltd. | Chilled beef packaging film |
WO1987002933A1 (fr) | 1985-11-07 | 1987-05-21 | Showa Denko Kabushiki Kaisha | Film transparent en polyethylene haute densite et son procede de fabrication |
US4668571A (en) * | 1986-05-02 | 1987-05-26 | The Dow Chemical Company | Coextrustion tie layer and process for producing such tie layer |
US4729926A (en) | 1986-05-16 | 1988-03-08 | W. R. Grace & Co., Cryovac Div. | Packaging material for long-term storage of shelf stable food products and method of making same |
US4778634A (en) | 1986-08-04 | 1988-10-18 | El Paso Products Company | Process for the manufacture of porous film |
US4788105A (en) * | 1986-09-09 | 1988-11-29 | W. R. Grace & Co. | Oxygen barrier laminates |
US5160767A (en) | 1987-04-30 | 1992-11-03 | American National Can Company | Peelable packaging and sheet materials and compositions for use therein |
US4911963A (en) * | 1987-08-31 | 1990-03-27 | Viskase Corporation | Multilayer film containing amorphous nylon |
US5089308A (en) | 1987-12-31 | 1992-02-18 | American National Can Company | Coextruded film and methods comprising vinylidene chloride methyl acrylate copolymer |
US4939076A (en) * | 1988-03-15 | 1990-07-03 | W. R. Grace & Co.-Conn. | Barrier stretch film |
US5069964A (en) | 1989-05-23 | 1991-12-03 | Minnesota Mining And Manufacturing Company | Flexible, substrate-insular retroreflective sheeting |
US5055328A (en) | 1989-06-16 | 1991-10-08 | Viskase Corporation | Differentially cross-linked multilayer film |
US5112696A (en) * | 1989-07-20 | 1992-05-12 | E. I. Du Pont De Nemours And Company | Tough monolayer shrink film for products containing moisture |
WO1991011317A1 (fr) | 1990-01-30 | 1991-08-08 | Nippon Petrochemicals Co., Ltd. | Materiau d'emballage multicouche a orientation monoaxiale |
US20030134966A1 (en) | 1990-01-31 | 2003-07-17 | Kim Yong Joo | Barrier compositions and articles made therefrom |
US5023121A (en) | 1990-04-12 | 1991-06-11 | W. R. Grace & Co.-Conn. | Coextruded film with peelable sealant |
ZA913312B (en) | 1990-05-02 | 1992-04-29 | Zapata Industries Inc | Polymer compositions containing oxygen scavenging compounds |
US5256458A (en) | 1990-09-18 | 1993-10-26 | Viskase Corporation | Shirred thermoplastic casing having external non-oil based lubricating coating |
EP0736375B1 (fr) | 1991-03-20 | 2001-10-04 | Kuraray Co., Ltd. | Procédé pour la fabrication d'un film multicouche |
JP2648404B2 (ja) * | 1991-04-10 | 1997-08-27 | 出光石油化学株式会社 | ポリエチレン系多層延伸フィルム |
US5288531A (en) * | 1991-08-09 | 1994-02-22 | The Dow Chemical Company | Pouch for packaging flowable materials |
DE4130485A1 (de) | 1991-08-23 | 1993-02-25 | Wolff Walsrode Ag | Coextrudierte biaxial gereckte schlauchfolie |
DE69220193T2 (de) * | 1991-12-11 | 1997-11-06 | Mobil Oil Corp | Hoch sperrender Film |
DE69333773T2 (de) | 1992-11-13 | 2006-04-06 | Cryovac, Inc. | Wärmeschrumpfbare, durch Single-site-Katalyse hergestellte Copolymere enthaltende Folien. |
DE4306963A1 (de) | 1993-03-05 | 1994-09-08 | Wolff Walsrode Ag | Weiß-opake Sperrschichtfolie mit ausgezeichneter Planlage |
US5382470A (en) | 1993-04-09 | 1995-01-17 | Viskase Corporation | EVOH oxygen barrier stretched multilayer film |
CA2120895C (fr) | 1993-04-09 | 1999-03-30 | David Nicholas Edwards | Emballage de fromage, pellicule, sac et procede d'emballage de denrees alimentaires produisant du co2 |
US5565048A (en) | 1993-05-14 | 1996-10-15 | Dow Corning Corporation | Barrier film for packaging |
US6074715A (en) * | 1993-06-24 | 2000-06-13 | Pechiney Plastic Packaging, Inc. | Heat shrinkable barrier bags |
NZ284938A (en) * | 1994-04-18 | 1998-08-26 | Grace W R & Co | Multilayer films having an anhydride functionality in the outer layer and use thereof in packaging meat products |
US5460861A (en) * | 1994-05-10 | 1995-10-24 | Viskase Corporation | Multilayer stretch/shrink film |
US5558930A (en) | 1994-06-23 | 1996-09-24 | Tredegar Industries, Inc. | Heat sealable, high moisture barrier film and method of making same |
DE4431046B4 (de) | 1994-09-01 | 2005-12-29 | Empac Verpackungs-Gmbh | Kunststoffverpackungsbehälter mit verbesserter elektrostatischer Ableitfähigkeit |
US5707750A (en) * | 1994-10-24 | 1998-01-13 | Alliedsignal Inc. | Retortable, high oxygen barrier polymeric films |
DE4441848A1 (de) * | 1994-11-24 | 1996-05-30 | Wolff Walsrode Ag | Sterilisationsfähige, tiefziehbare, klebstofffreie und siegelbare Verbundfolie bestehend aus Polyolefinen und deren Copolymeren |
US6623821B1 (en) | 1995-03-31 | 2003-09-23 | E. I. Du Pont De Nemours And Company | Heat-shrinkable, heat-sealable polyester film for packaging |
US5874155A (en) | 1995-06-07 | 1999-02-23 | American National Can Company | Easy-opening flexible packaging laminates and packaging materials made therefrom |
US20020004112A1 (en) | 1995-07-24 | 2002-01-10 | Harry Muller | Composite films having biaxially oriented polyethylene sealing layers |
DE69606811T3 (de) * | 1995-07-31 | 2012-01-12 | Kureha Corp. | Mehrschichtfolie |
MY114798A (en) * | 1995-09-12 | 2003-01-31 | Dow Global Technologies Inc | Pouches for packaging flowable materials |
US6071626A (en) | 1996-04-29 | 2000-06-06 | Tetra Laval Holdings & Finance, Sa | Multilayer, high barrier laminate |
US5759648A (en) | 1996-07-05 | 1998-06-02 | Viskase Corporation | Multilayer plastic film, useful for packaging a cook-in foodstuff |
WO1998008891A1 (fr) * | 1996-08-26 | 1998-03-05 | Tetra Laval Holdings & Finance, S.A. | Film reticule de conditionnement de matieres fluides |
US5846620A (en) | 1997-02-06 | 1998-12-08 | W. R. Grace & Co.-Conn. | High strength flexible film package |
WO1998014370A2 (fr) | 1996-10-03 | 1998-04-09 | Machinery Developments Limited | Dispositif et procede pour emballer la viande |
EP0952999B1 (fr) | 1997-01-17 | 2002-10-02 | EG Technology Partners, LP | Composition a base d'acide organique insature et de polyamine, destinee a un revetement formant barriere |
US6667082B2 (en) | 1997-01-21 | 2003-12-23 | Cryovac, Inc. | Additive transfer film suitable for cook-in end use |
CN1248276A (zh) | 1997-02-25 | 2000-03-22 | 埃克森化学专利公司 | 具有优异摩擦系数的电晕放电处理膜 |
US5928740A (en) | 1997-02-28 | 1999-07-27 | Viskase Corporation | Thermoplastic C2 -α-olefin copolymer blends and films |
US6296886B1 (en) | 1997-03-17 | 2001-10-02 | Cryovac, Inc. | Method of film crease elimination and patch bag without crease within lay-flat bag side |
US6117541A (en) * | 1997-07-02 | 2000-09-12 | Tetra Laval Holdings & Finance, Sa | Polyolefin material integrated with nanophase particles |
US6610392B1 (en) * | 1998-03-04 | 2003-08-26 | Cryovac, Inc. | Heat-shrinkable multilayer packaging film comprising inner layer comprising a polyester |
US6010792A (en) * | 1998-03-31 | 2000-01-04 | American National Can Company | Poultry shrink bags |
US6777046B1 (en) * | 1998-07-07 | 2004-08-17 | Curwood, Inc. | Puncture resistant, high shrink films, blends, and process |
US6004599A (en) | 1998-08-10 | 1999-12-21 | Viskase Corporation | Bag for packaging bone-in cuts of meat |
US6287652B2 (en) | 1998-12-09 | 2001-09-11 | Color Prelude, Inc. | Fluid product sampler package with clear moisture vapor barrier film |
AU765233B2 (en) | 1998-12-18 | 2003-09-11 | Cryovac, Inc. | Highly bi-axially oriented, heat-shrinkable, thermoplastic, multi-layer film and process for the manufacture thereof |
JP2000188966A (ja) * | 1998-12-22 | 2000-07-11 | Mitsubishi Chem Mkv Co | 農業用多層フィルム |
US6211471B1 (en) | 1999-01-27 | 2001-04-03 | Caterpillar Inc. | Control system for automatically controlling a work implement of an earthmoving machine to capture, lift and dump material |
CA2299691C (fr) | 1999-03-01 | 2011-07-12 | Johnson & Johnson Vision Care, Inc. | Emballage pour dispositif medical |
US20020061982A1 (en) | 1999-06-11 | 2002-05-23 | Donald Robert J. | Compositions comprising hydrogenated block copolymers and end-use applications thereof |
US6534137B1 (en) | 1999-10-12 | 2003-03-18 | Cryovac, Inc. | Two-component, heat-sealable films |
US6703141B1 (en) | 1999-12-09 | 2004-03-09 | Exxonmobil Oil Corporation | Matte surface film |
JP4384317B2 (ja) * | 1999-12-14 | 2009-12-16 | 株式会社メイワパックス | 自動調圧機能を有する包装袋および包装体 |
EP1122060A1 (fr) | 2000-02-07 | 2001-08-08 | Atofina | Structure multicouche et tube ou conduit à structure multicouche et couche barrière en contact direct avec fluide contenu |
US6436498B1 (en) | 2000-03-03 | 2002-08-20 | Dow Corning Corporation | Reactive silicone/alkyleneimine barrier laminating adhesives having bis-silane additives |
US6743523B1 (en) * | 2000-03-16 | 2004-06-01 | Baxter International Inc. | Multiple layer film of a new non-PVC material |
US20020022144A1 (en) | 2000-05-19 | 2002-02-21 | Hu Yang | Enhanced oxygen barrier performance from modification of ethylene vinyl alcohol copolymers (EVOH) |
US6447892B1 (en) | 2000-05-23 | 2002-09-10 | Honeywell International Inc. | Lidding film for modified atmosphere packaging |
AU2001275203A1 (en) | 2000-06-08 | 2001-12-17 | Pechiney Emballage Flexible Europe | Laminated thermoformable film structures useful for packaging food products |
US20020164444A1 (en) | 2000-08-29 | 2002-11-07 | Hunt Thomas F. | Film structures containing oxygen scavenging compositions and method of application |
US7384679B2 (en) | 2000-08-29 | 2008-06-10 | Pechiney Emballage Flexible Europe | Encapsulated barrier for flexible films and a method of making and using the same |
US6500514B1 (en) | 2000-08-29 | 2002-12-31 | Pechiney Emballage Flexible Europe | Encapsulated barrier for flexible films and a method of making the same |
EP1193052A1 (fr) | 2000-09-29 | 2002-04-03 | Cryovac, Inc. | Nouveau film thermoplastique multicouche thermoretractable et container obtenu à partir de ce film |
US6450011B1 (en) * | 2000-11-24 | 2002-09-17 | Mocon, Inc. | Pressure measurement method for gas leakage from sealed packages |
US20030099851A1 (en) | 2000-12-05 | 2003-05-29 | Mount Eldridge M. | Multilayer metallized film having enhanced barrier and metal adhesion characteristics |
IL140543A0 (en) | 2000-12-25 | 2002-02-10 | Syfan Saad 99 Ltd | Multilayer barrier shrink films and process for their manufacture |
UA75116C2 (en) * | 2001-02-01 | 2006-03-15 | Becker & Co Naturinwerk | Five-layered, sealable tubular film for the packaging and wrapping of paste-like foodstuffs, meat and meat with bones, and a pack made thereof |
US20020164441A1 (en) | 2001-03-01 | 2002-11-07 | The University Of Chicago | Packaging for primary and secondary batteries |
US6682792B2 (en) * | 2001-03-26 | 2004-01-27 | M & Q Plastic Products, Inc. | Thermoplastic elastomer films |
US6825276B2 (en) * | 2001-04-17 | 2004-11-30 | Pliant Corporation | Nonoriented stiff packaging film with superior tear properties |
US6602590B2 (en) | 2001-05-08 | 2003-08-05 | Honeywell International Inc. | Lidding film for modified atmosphere packaging |
DE20109885U1 (de) | 2001-06-15 | 2001-10-18 | Elsässer, Manfred, Dr., Patsch | Gasgefüllte Noppenmatten für den Einsatz im Hoch-, Tief- und Grundbau |
US6831025B2 (en) | 2001-06-18 | 2004-12-14 | E. I. Du Pont De Nemours And Company | Multiple component spunbond web and laminates thereof |
US7135526B2 (en) | 2001-06-22 | 2006-11-14 | Univation Technologies, Llc | Very low density polyethylene and high density polyethylene blends |
CA2463958A1 (fr) | 2001-10-19 | 2003-04-24 | Dupont Canada Inc. | Structure de film composite pour produire des poches par scellement thermique rotatif |
US6824864B2 (en) | 2001-10-23 | 2004-11-30 | Exxonmobil Oil Corporation | Multi-layer, white cavitated bioriented polyethylene film with a high water vapor transmission rate |
US6607795B1 (en) | 2001-12-19 | 2003-08-19 | Chevron Phillips Chemical Company Lp | Oxygen scavenging compositions comprising polymers derived from aromatic difunctional monomers |
US6746622B2 (en) | 2002-02-08 | 2004-06-08 | Chevron Phillips Chemical Company Lp | Oxygen scavenging compositions comprising polymers derived from tetrahydrofurfuryl monomers |
US7323669B2 (en) | 2002-02-08 | 2008-01-29 | Graphic Packaging International, Inc. | Microwave interactive flexible packaging |
US7022258B2 (en) | 2002-02-14 | 2006-04-04 | Chevron Phillips Chemical Company, Lp | Oxygen scavenging compositions comprising polymers derived from benzenedimethanol monomers |
US6726968B2 (en) | 2002-02-22 | 2004-04-27 | Honeywell International Inc. | Antifog/barrier laminate for use in meat packaging |
US6846530B2 (en) | 2002-03-05 | 2005-01-25 | Honeywell International Inc. | Lamination for specialty meat packaging |
WO2003086757A1 (fr) * | 2002-04-15 | 2003-10-23 | Dsm Ip Assets B.V. | Film tubulaire a multiples couches et procede de production de ce dernier |
US6803113B2 (en) | 2002-09-13 | 2004-10-12 | Honeywell International Inc. | High barrier antifog laminate for case ready meat packaging |
DE10227580A1 (de) | 2002-06-20 | 2004-01-08 | Kuhne Anlagenbau Gmbh | Mehrschichtige flächen- oder schlauchförmige Nahrungsmittelhülle oder -folie |
US20040131805A1 (en) | 2002-06-20 | 2004-07-08 | Merical Rick L. | Films having a desiccant material incorporated therein and methods of use and manufacture |
DK175272B1 (da) | 2002-07-08 | 2004-08-02 | Amcor Flexibles Denmark As | Foliemateriale, emballage fremstillet deraf og anvendelse deraf til emballering |
WO2004005026A1 (fr) | 2002-07-09 | 2004-01-15 | Dsm Ip Assets B.V. | Procede pour appliquer une couche de polyamide ramifie sur un substrat |
US7029734B1 (en) | 2002-08-20 | 2006-04-18 | Curwood, Inc. | Packaging film, package and process for aseptic packaging |
US20040043167A1 (en) | 2002-09-04 | 2004-03-04 | Gianni Holzem | Failure-resistant receptacle and method of manufacture |
US6893730B2 (en) | 2002-09-24 | 2005-05-17 | Honeywell International Inc. | Barrier film with reduced dynamic coefficient of friction |
CN101724110B (zh) | 2002-10-15 | 2013-03-27 | 埃克森美孚化学专利公司 | 用于烯烃聚合的多催化剂体系和由其生产的聚合物 |
US7252878B2 (en) | 2002-10-23 | 2007-08-07 | Toray Plastics (America), Inc. | High barrier flexible packaging structure |
US7166671B2 (en) | 2002-12-10 | 2007-01-23 | Cellresin Technologies, Llc | Grafted cyclodextrin |
US20040175466A1 (en) | 2003-03-07 | 2004-09-09 | Douglas Michael J. | Multilayer barrier structures, methods of making the same and packages made therefrom |
US20040175464A1 (en) | 2003-03-07 | 2004-09-09 | Blemberg Robert J. | Multilayer structures, packages, and methods of making multilayer structures |
MXPA05011440A (es) | 2003-04-24 | 2006-05-31 | Rasmussen Olebendt | Metodo para fabricar peliculas orientadas a partir de polimeros termoplasticos combinados, aparato para tal fabricacion y sus productos. |
US20040234797A1 (en) | 2003-05-23 | 2004-11-25 | Cryovac, Inc. | Oxygen scavenging film with antifog properties |
US7588653B2 (en) | 2003-06-23 | 2009-09-15 | Ppg Industries Ohio, Inc. | Method of making an integrated window sash |
EP1651438B1 (fr) | 2003-07-30 | 2011-03-23 | Cryovac, Inc. | Film oriente multicouche a haut module |
US20050186414A1 (en) | 2003-10-01 | 2005-08-25 | Toray Plastics (America), Inc. | Polypropylene multi-layer barrier films |
US7862869B2 (en) | 2003-10-20 | 2011-01-04 | Milprint, Inc. | Tear initiation and directional tear films and packages made therefrom |
US7569276B2 (en) | 2003-12-22 | 2009-08-04 | Dupont Teijin Films U.S. Limited Partnership | Thermoformable polyester-containing laminates |
EP1555292B1 (fr) | 2004-01-13 | 2015-12-23 | Borealis Technology Oy | Polyéthylène pour le revêtement par extrusion |
US7767773B2 (en) | 2004-03-17 | 2010-08-03 | Exxonmobile Chemical Patents Inc. | Catalyst compounds are use thereof |
US8053047B2 (en) | 2004-04-02 | 2011-11-08 | Curwood, Inc. | Packaging method that causes and maintains the preferred red color of fresh meat |
DK1748936T3 (da) | 2004-05-05 | 2011-09-26 | Columbus E Aps | Brygningsanordning til engangsbrug |
CN1984952A (zh) | 2004-07-13 | 2007-06-20 | 埃克森美孚化学专利公司 | 聚合物制品改进的表面处理 |
US20060014002A1 (en) | 2004-07-14 | 2006-01-19 | Moulton Jeffrey D | High barrier antifog laminate for case ready meat packaging |
SE528263C2 (sv) | 2004-09-13 | 2006-10-03 | Tetra Laval Holdings & Finance | Förpackningsbehållare försedd med en remsa |
US7763095B2 (en) * | 2005-06-07 | 2010-07-27 | The Regents Of The University Of California | Internal gettering by metal alloy clusters |
US20070031546A1 (en) | 2005-08-05 | 2007-02-08 | Curwood, Inc. | Polyester and polyamide blend containing article for packaging a CO2 respiring foodstuff |
US7473439B2 (en) | 2005-08-15 | 2009-01-06 | Exxonmobil Oil Corporation | Coated polymeric films and coating solutions for use with polymeric films |
US7939150B2 (en) | 2005-08-16 | 2011-05-10 | Honeywell International Inc. | Lid stock using oriented fluoropolymers |
US7427430B2 (en) | 2005-12-29 | 2008-09-23 | Honeywell International Inc. | Polyamide blend composition having excellent gas barrier performance |
US20070292567A1 (en) | 2005-12-30 | 2007-12-20 | Lithotype Company, Inc. | E-beam cured packaging structure, packages, and methods of making |
US20070259142A1 (en) | 2006-05-03 | 2007-11-08 | Curwood, Inc. | Rigid and semirigid packaging articles |
US20080063759A1 (en) | 2006-09-13 | 2008-03-13 | Raymond Megan N | Packaging Method for Storage and Microwave Heating of Food Products |
US20080063760A1 (en) | 2006-09-13 | 2008-03-13 | Raymond Megan N | Packaging System for Storage and Microwave Heating of Food Products |
US7713614B2 (en) | 2006-09-19 | 2010-05-11 | Kuraray Co., Ltd. | Resin composition and multilayer structure |
US20080107899A1 (en) | 2006-11-07 | 2008-05-08 | Pang-Chia Lu | Metallized multi-layer films, methods of manufacture and articles made therefrom |
US20080145581A1 (en) | 2006-12-14 | 2008-06-19 | Stephen Robert Tanny | Peelable multilayer laminate for packaging |
US7713636B2 (en) | 2006-12-15 | 2010-05-11 | Exxonmobil Chemical Patents Inc. | Multi-layer films comprising propylene-based polymers |
US8263213B2 (en) | 2006-12-19 | 2012-09-11 | E I Du Pont De Nemours And Company | Painted composite thermoplastic articles |
US7687123B2 (en) | 2007-01-29 | 2010-03-30 | Cryovac, Inc. | Shrink film containing semi-crystalline polyamide and process for making same |
US20100015423A1 (en) | 2008-07-18 | 2010-01-21 | Schaefer Suzanne E | Polyamide structures for the packaging of moisture containing products |
-
2003
- 2003-12-12 US US10/735,366 patent/US20040175466A1/en not_active Abandoned
-
2004
- 2004-03-05 CA CA2518401A patent/CA2518401C/fr not_active Expired - Fee Related
- 2004-03-05 BR BRPI0408670-8A patent/BRPI0408670A/pt not_active Application Discontinuation
- 2004-03-05 NZ NZ542355A patent/NZ542355A/en not_active IP Right Cessation
- 2004-03-05 EP EP12180844.8A patent/EP2679517A1/fr not_active Withdrawn
- 2004-03-05 WO PCT/US2004/006639 patent/WO2004080804A2/fr active Application Filing
- 2004-03-05 AR ARP040100717A patent/AR043496A1/es active IP Right Grant
- 2004-03-05 AU AU2004220068A patent/AU2004220068B2/en not_active Expired
- 2004-03-05 EP EP04717966A patent/EP1603812A4/fr not_active Withdrawn
-
2005
- 2005-01-04 US US11/029,200 patent/US9498936B2/en not_active Expired - Fee Related
-
2016
- 2016-10-19 US US15/297,909 patent/US20170036426A1/en not_active Abandoned
Patent Citations (75)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4601929A (en) * | 1982-07-27 | 1986-07-22 | Naturin-Werk Becker & Company | Single-layer elastic tubular film of polyamide used for packaging paste substances and a process for the production of such film |
US4469742A (en) * | 1983-01-31 | 1984-09-04 | W. R. Grace & Co., Cryovac Div. | Pasteurizable, cook-in shrink film |
US4704101A (en) * | 1983-06-30 | 1987-11-03 | W.R. Grace & Co., Cryovac Div. | Method for making a puncture resistant bag |
US5020922A (en) * | 1983-06-30 | 1991-06-04 | W. R. Grace & Co.-Conn. | Bone puncture resistant bag |
US4534984A (en) * | 1983-08-16 | 1985-08-13 | W. R. Grace & Co., Cryovac Div. | Puncture-resistant bag and method for vacuum packaging bone-in meat |
US4561920A (en) * | 1984-02-08 | 1985-12-31 | Norchem, Inc. Formerly Northern Petrochemical Company | Biaxially oriented oxygen and moisture barrier film |
US4770731A (en) * | 1985-06-03 | 1988-09-13 | W. R. Grace & Co.-Conn. | Method of making a patch for a shrinkable bag |
US4755403A (en) * | 1985-06-03 | 1988-07-05 | W. R. Grace & Co., Cryovac Div. | Protective patch for shrinkable bag |
US4765857A (en) * | 1985-06-03 | 1988-08-23 | W. R. Grace & Co., Cryovac Div. | Protective patch for shrinkable bag |
USRE35285E (en) * | 1985-09-30 | 1996-06-25 | W. R. Grace & Co.-Conn. | Thermoplastic multi-layer packaging film and bags made therefrom |
US4801486A (en) * | 1985-09-30 | 1989-01-31 | W. R. Grace & Co.-Conn. | Thermoplastic multi-layer packaging film and bags made therefrom |
US4753700A (en) * | 1986-02-28 | 1988-06-28 | W. R. Grace & Co., Cryovac Div. | Packaging film |
US4746562A (en) * | 1986-02-28 | 1988-05-24 | W. R. Grace & Co., Cryovac Div. | Packaging film |
US5004647A (en) * | 1986-03-21 | 1991-04-02 | W. R. Grace & Co.-Conn. | Oxygen barrier biaxially oriented film |
US4755419A (en) * | 1986-03-21 | 1988-07-05 | W. R. Grace & Co., Cryovac Div. | Oxygen barrier oriented shrink film |
US4735855A (en) * | 1986-08-04 | 1988-04-05 | W. R. Grace & Co., Cryovac Div. | Thermoformable laminate |
US4888223A (en) * | 1987-05-21 | 1989-12-19 | Noritsugu Sugimoto | Food-packaging material and process for preparing the same |
US4937112A (en) * | 1987-12-18 | 1990-06-26 | W. R. Grace & Co.-Conn. | High strength coextruded film for chub packaging |
US4851290A (en) * | 1988-01-06 | 1989-07-25 | Viskase Corporation | Multilayer thermoplastic film |
US4977022A (en) * | 1988-03-15 | 1990-12-11 | W. R. Grace & Co.-Conn. | Barrier stretch film |
US4909726A (en) * | 1988-03-24 | 1990-03-20 | Grumman Aerospace Corporation | Impact-resistant film for chub packaging |
US4855178A (en) * | 1988-05-02 | 1989-08-08 | E. I. Du Pont De Nemours And Company | Composite chemical barrier fabric |
US5053259A (en) * | 1988-08-23 | 1991-10-01 | Viskase Corporation | Amorphous nylon copolymer and copolyamide films and blends |
US5037683A (en) * | 1988-09-26 | 1991-08-06 | W. R. Grace & Co.-Conn. | High strength laminated film for chub packaging |
US4997710A (en) * | 1988-09-29 | 1991-03-05 | W. R. Grace & Co.-Conn. | Barrier coextruded film for cook-in applications |
US5079051A (en) * | 1989-12-08 | 1992-01-07 | W. R. Grace & Co.-Conn. | High shrink energy/high modulus thermoplastic multi-layer packaging film and bags made therefrom |
US6224956B1 (en) * | 1990-05-17 | 2001-05-01 | Cryovac, Inc. | Breathable abuse resistant film for packaging cheese |
US5688456A (en) * | 1990-06-27 | 1997-11-18 | Gunze Limited | Process for preparation of multilayer films |
US5562996A (en) * | 1990-06-27 | 1996-10-08 | Gunze Limited | Multi-layer films |
US5491009A (en) * | 1990-08-03 | 1996-02-13 | W. R. Grace & Co.-Conn. | Amorphous nylon composition and films |
US5595623A (en) * | 1990-11-16 | 1997-01-21 | W. R. Grace Co.-Conn. | Method for making a barrier film with improved extensibility for cheese packaging |
US20010036555A1 (en) * | 1992-06-05 | 2001-11-01 | Ramesh Ram K. | Backseamed casing and packaged product incorporating same |
US6579621B1 (en) * | 1992-09-18 | 2003-06-17 | Cryovac, Inc. | Moisture barrier film |
US5910374A (en) * | 1992-09-18 | 1999-06-08 | Cryovac, Inc. | Moisture barrier film |
US5482771A (en) * | 1992-09-18 | 1996-01-09 | W. R. Grace & Co.-Conn. | Moisutre barrier film |
US5698279A (en) * | 1992-09-23 | 1997-12-16 | Viskase Corporation | Heat shrinkable nylon food casing having a functionalized ethylenic polymer core layer |
US5549943A (en) * | 1992-09-23 | 1996-08-27 | Viskase Corporation | Heat shrinkable nylon food casing with a polyolefin core layer |
US6221410B1 (en) * | 1992-09-25 | 2001-04-24 | Cryovac, Inc. | Backseamed casing and packaged product incorporating same |
US20010041201A1 (en) * | 1992-09-25 | 2001-11-15 | Ramesh Ram K. | Backseamed casing and packaged product incorporating same |
US5482770A (en) * | 1992-11-03 | 1996-01-09 | W. R. Grace & Co.-Conn. | Highly oriented multilayer film |
US5645788A (en) * | 1992-11-03 | 1997-07-08 | W.R. Grace & Co.-Conn. | Making highly oriented multilayer film |
US5741566A (en) * | 1993-02-19 | 1998-04-21 | Pharmacia & Upjohn Aktiebolag | Autoclavable multilayer films |
US5374459A (en) * | 1993-04-06 | 1994-12-20 | W. R. Grace & Co.-Conn. | Packaging material for long-term storage of food products |
US5540646A (en) * | 1993-04-21 | 1996-07-30 | W. R. Grace & Co.-Conn. | Method of making a shrinkable bag with protective patch |
US5402625A (en) * | 1993-05-04 | 1995-04-04 | W. R. Grace & Co.-Conn. | Bag loader for bone-in products |
US5447591A (en) * | 1993-08-04 | 1995-09-05 | W. R. Grace & Co.-Conn. | Trap printing method for bone-in meat containers |
US5534276A (en) * | 1993-08-04 | 1996-07-09 | W. R. Grace & Co.-Conn. | Bone-in meat containers |
US6106935A (en) * | 1994-07-13 | 2000-08-22 | Cryovac, Inc. | Heat sealable film |
US5545419A (en) * | 1994-07-21 | 1996-08-13 | W. R. Grace & Co.-Conn. | Patch bag having supplemental seal |
US6287613B1 (en) * | 1994-12-12 | 2001-09-11 | Cryovac Inc | Patch bag comprising homogeneous ethylene/alpha-olefin copolymer |
US6150011A (en) * | 1994-12-16 | 2000-11-21 | Cryovac, Inc. | Multi-layer heat-shrinkage film with reduced shrink force, process for the manufacture thereof and packages comprising it |
US5914164A (en) * | 1995-05-24 | 1999-06-22 | Cryovac, Inc. | Multilayer oxygen-barrier packaging film |
US5866214A (en) * | 1995-07-28 | 1999-02-02 | W. R. Grace & Co.-Conn. | Film backseamed casings therefrom, and packaged product using same |
US6110600A (en) * | 1995-07-28 | 2000-08-29 | Cryovac, Inc. | Film, backseamed casings therefrom, and packaged product using same |
US5763095A (en) * | 1995-11-29 | 1998-06-09 | W. R. Grace & Co.-Conn. | Breathable film for cheese packaging |
US6210765B1 (en) * | 1996-01-11 | 2001-04-03 | Mitsui Petrochemical Industrie Ltd | Adhesive polyethylene compositions and multi-layer laminated films using the same |
US20020119334A1 (en) * | 1996-02-15 | 2002-08-29 | Shepard Mary E. | Thermoformable multilayer polymeric film |
US20010003021A1 (en) * | 1996-02-15 | 2001-06-07 | Mary E. Shepard, Et Al | Thermoformable multilayer polymeric film |
US6068933A (en) * | 1996-02-15 | 2000-05-30 | American National Can Company | Thermoformable multilayer polymeric film |
US6221470B1 (en) * | 1996-02-23 | 2001-04-24 | Cryovac, Inc. | Multilayer oxygen barrier packaging film |
US6063417A (en) * | 1996-02-28 | 2000-05-16 | Cryovac, Inc. | Cheese packaging film |
US6346285B1 (en) * | 1996-08-16 | 2002-02-12 | Cryovac, Inc. | Article comprising film having polyamide sealant, polyamide core layer, and O2-barrier layer, and packaged product using same |
US6333061B1 (en) * | 1996-11-22 | 2001-12-25 | Cryovac, Inc. | Packaging article |
US6206569B1 (en) * | 1997-03-07 | 2001-03-27 | Curwood, Inc. | Puncture-resistant barrier pouch |
US6663905B1 (en) * | 1998-03-16 | 2003-12-16 | Cryovac, Inc. | Patch bag having wrap-around patch |
US20010010846A1 (en) * | 1998-05-04 | 2001-08-02 | Frank M. Hofmeister | Multiple layer film with amorphous polyamide layer |
US6562443B1 (en) * | 1998-07-22 | 2003-05-13 | Cryovac, Inc. | Cook-in package with tight appearance |
US6274228B1 (en) * | 1998-07-22 | 2001-08-14 | Cryovac, Inc. | Heat-shrinkable film with improved inter-ply adhesion |
US6299984B1 (en) * | 1998-09-14 | 2001-10-09 | Cryovac, Inc. | Heat-shrinkable multilayer thermoplastic film |
US6579584B1 (en) * | 1998-12-10 | 2003-06-17 | Cryovac, Inc. | High strength flexible film package utilizing thin film |
US6291041B1 (en) * | 1999-05-10 | 2001-09-18 | Curwood, Inc. | Heat resistant nylon multi-layer film |
US6458469B1 (en) * | 1999-07-08 | 2002-10-01 | Exxonmobil Chemical Company | Multilayer oriented films with metallocene catalyzed polyethylene skin layer |
US20020055006A1 (en) * | 2000-04-14 | 2002-05-09 | Vogel Randall Allen | Multilayer, co-extruded, ionomeric decorative surfacing |
US6599639B2 (en) * | 2001-03-16 | 2003-07-29 | Cryovac, Inc. | Coextruded, retortable multilayer film |
US20030087114A1 (en) * | 2001-11-06 | 2003-05-08 | Cryovac, Inc. | Irradiated multilayer film having seal layer containing hyperbranched polymer |
Cited By (31)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20070092744A1 (en) * | 2005-10-13 | 2007-04-26 | Plasticos Dise S.A. | Polymer compositions and films and method of making |
US20080128416A1 (en) * | 2006-12-01 | 2008-06-05 | Cryovac, Inc. | Stress concentrator for opening a flexible container |
US8522978B2 (en) | 2006-12-01 | 2013-09-03 | Cryovac, Inc. | Stress concentrator for opening a flexible container |
US7744806B2 (en) | 2007-01-29 | 2010-06-29 | Cryovac, Inc. | Process for making shrink film comprising rapidly-quenched semi-crystalline polyamide |
US20080182053A1 (en) * | 2007-01-29 | 2008-07-31 | Broadus Michael E | Shrink film containing semi-crystalline polyamide and process for making same |
US20080179780A1 (en) * | 2007-01-29 | 2008-07-31 | Broadus Michael E | Process for making shrink film comprising rapidly-quenched semi-crystalline polyamide |
US20080182051A1 (en) * | 2007-01-29 | 2008-07-31 | Cryovac, Inc. | Heat shrinkable retortable packaging article and process for preparing retorted packaged product |
US7687123B2 (en) | 2007-01-29 | 2010-03-30 | Cryovac, Inc. | Shrink film containing semi-crystalline polyamide and process for making same |
US10781022B2 (en) | 2007-05-21 | 2020-09-22 | Cryovac, Llc | Easy opening packaging article made from heat-shrinkable film exhibiting directional tear |
US20080292225A1 (en) * | 2007-05-21 | 2008-11-27 | Dayrit Richard M | Bag made from high-strength heat-shrinkable film exhibiting directional tear, and process utilizing same |
US10202229B2 (en) | 2007-05-21 | 2019-02-12 | Cryovac, Inc. | Easy opening packaging article made from heat-shrinkable film exhibiting directional tear |
US10189621B2 (en) | 2007-05-21 | 2019-01-29 | Cryovac, Inc. | Bag made from high-strength heat-shrinkable film exhibiting directional tear, and process utilizing same |
US20080314465A1 (en) * | 2007-06-21 | 2008-12-25 | Samsung Electronics Co., Ltd. | Microfluidic valve, method of manufacturing the same, and microfluidic device comprising the microfluidic valve |
US8957146B2 (en) | 2010-12-15 | 2015-02-17 | Cheil Industries Inc. | Polyamide resin composition with excellent reflectivity, heat resistance, and water resistance |
US20130172453A1 (en) * | 2011-12-29 | 2013-07-04 | Cheil Industries Inc. | Polyamide Resin Composition Having Improved Physical Properties Including Thin-wall Moldability |
US8865807B2 (en) * | 2011-12-29 | 2014-10-21 | Cheil Industries Inc. | Polyamide resin composition having improved physical properties including thin-wall moldability |
US9522496B2 (en) * | 2012-12-04 | 2016-12-20 | Pexcor Manufacturing Company Inc. | Production method of plastic pipe in layers |
US20140151937A1 (en) * | 2012-12-04 | 2014-06-05 | Pexcor Manufacturing Company Inc. | Production method of plastic pipe in layers |
US9018296B2 (en) | 2012-12-31 | 2015-04-28 | Cheil Industries Inc. | Thermoplastic resin composition having excellent surface gloss, reflectance, anti-yellowing property and moldability |
US8957142B2 (en) | 2013-02-01 | 2015-02-17 | Cheil Industries Inc. | Polyamide resin composition having excellent photostability and discoloration resistance |
US10301449B2 (en) | 2013-11-29 | 2019-05-28 | Lotte Advanced Materials Co., Ltd. | Thermoplastic resin composition having excellent light stability at high temperature |
US10822490B2 (en) | 2013-12-30 | 2020-11-03 | Lotte Advanced Materials Co., Ltd. | Thermoplastic resin composition having excellent shock resistance and light resistance |
US11355683B2 (en) | 2014-06-27 | 2022-06-07 | Lotte Chemical Corporation | Thermoplastic resin composition having excellent reflectivity |
US10636951B2 (en) | 2014-06-27 | 2020-04-28 | Lotte Advanced Materials Co., Ltd. | Thermoplastic resin composition having excellent reflectivity |
US9840610B2 (en) | 2014-09-30 | 2017-12-12 | Lotte Advanced Materials Co., Ltd. | Thermoplastic resin composition and molded article using the same |
US10508190B2 (en) | 2014-12-17 | 2019-12-17 | Lotte Advanced Materials Co., Ltd. | Polyester resin composition and molded article manufactured therefrom |
US10538661B2 (en) | 2015-06-30 | 2020-01-21 | Lotte Advanced Materials Co., Ltd. | Polyester resin composition with excellent impact resistance and light reliability and molded article using the same |
US10131785B2 (en) | 2015-06-30 | 2018-11-20 | Lotte Advanced Materials Co., Ltd. | Polyester resin composition with excellent impact resistance and light reliability and molded article using the same |
AT519653A4 (de) * | 2017-02-09 | 2018-09-15 | Constantia Hueck Folien Gmbh & Co Kg | Verbundfolie mit einer Mineralölbarriere |
AT519653B1 (de) * | 2017-02-09 | 2018-09-15 | Constantia Hueck Folien Gmbh & Co Kg | Verbundfolie mit einer Mineralölbarriere |
WO2018145885A1 (fr) * | 2017-02-09 | 2018-08-16 | Constantia Hueck Folien Gmbh & Co. Kg | Film composite comportant une barrière aux huiles minérales |
Also Published As
Publication number | Publication date |
---|---|
WO2004080804A2 (fr) | 2004-09-23 |
EP2679517A1 (fr) | 2014-01-01 |
NZ542355A (en) | 2007-02-23 |
AU2004220068B2 (en) | 2010-08-05 |
US20050118374A1 (en) | 2005-06-02 |
US9498936B2 (en) | 2016-11-22 |
EP1603812A2 (fr) | 2005-12-14 |
WO2004080804A3 (fr) | 2005-01-13 |
EP1603812A4 (fr) | 2008-03-26 |
CA2518401C (fr) | 2011-10-25 |
AR043496A1 (es) | 2005-08-03 |
BRPI0408670A (pt) | 2006-05-02 |
US20170036426A1 (en) | 2017-02-09 |
CA2518401A1 (fr) | 2004-09-23 |
AU2004220068A1 (en) | 2004-09-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20170036426A1 (en) | Multilayer barrier structures, methods of making the same and packages made therefrom | |
US20170036427A1 (en) | Multilayer structures, packages, and methods of making multilayer structures | |
US20040175592A1 (en) | Thermoplastic multilayer barrier structures | |
US20040173491A1 (en) | Packages made from thermoplastic multilayer barrier structures | |
EP3094494B2 (fr) | Films thermorétractables multicouches | |
US20040173944A1 (en) | Methods of making multilayer barrier structures | |
US20040175465A1 (en) | Thermoplastic multilayer structures | |
MXPA04001627A (es) | Embalaje por contraccion por calor. | |
US20090017239A1 (en) | Hermetically Sealable, Easy-Opeanable, Flexible Container of Heat-Shrinklable Thermoplastic Material | |
US20040175467A1 (en) | Packages made from multilayer structures | |
US20040173932A1 (en) | Methods of making multilayer structures | |
AU646144B2 (en) | High abuse ionomer bag | |
JP2001009993A (ja) | 熱収縮性積層フィルム及びそれからなる食品用包装フィルム | |
NZ722752B2 (en) | Multilayer pvdc barrier heat shrinkable films |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |