US20040168779A1 - Multilayered fibrous product and process for the production thereof - Google Patents

Multilayered fibrous product and process for the production thereof Download PDF

Info

Publication number
US20040168779A1
US20040168779A1 US10/475,773 US47577304A US2004168779A1 US 20040168779 A1 US20040168779 A1 US 20040168779A1 US 47577304 A US47577304 A US 47577304A US 2004168779 A1 US2004168779 A1 US 2004168779A1
Authority
US
United States
Prior art keywords
layer
filler
top layer
fibre
fibrous product
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/475,773
Other languages
English (en)
Inventor
Petri Silenius
Leena Yliniemi
Jari Meuronen
Markku Leskela
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Metsa Board Oyj
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Assigned to M-REAL OYJ reassignment M-REAL OYJ ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: LESKELA, MARKKU, MEURONEN, JARI, SILENIUS, PETRI, YLINIEMI, LEENA
Publication of US20040168779A1 publication Critical patent/US20040168779A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
    • D21H17/63—Inorganic compounds
    • D21H17/67—Water-insoluble compounds, e.g. fillers, pigments
    • D21H17/69—Water-insoluble compounds, e.g. fillers, pigments modified, e.g. by association with other compositions prior to incorporation in the pulp or paper
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H27/00—Special paper not otherwise provided for, e.g. made by multi-step processes
    • D21H27/30—Multi-ply
    • D21H27/38—Multi-ply at least one of the sheets having a fibrous composition differing from that of other sheets
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H11/00—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only
    • D21H11/16—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only modified by a particular after-treatment
    • D—TEXTILES; PAPER
    • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
    • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
    • D21H15/00—Pulp or paper, comprising fibres or web-forming material characterised by features other than their chemical constitution
    • D21H15/02—Pulp or paper, comprising fibres or web-forming material characterised by features other than their chemical constitution characterised by configuration
    • D21H15/10—Composite fibres
    • D21H15/12—Composite fibres partly organic, partly inorganic

Definitions

  • the present invention concerns a multi-layer fibrous product according to the preamble of claim 1 .
  • This kind of a product comprises at least two overlapping fibrous layers, of which at least the layer forming the operating surface of the product is light and essentially opaque (non-transparent), covering the fibre layer under it.
  • the top layer contains filler and possibly conventional additives and auxiliary agents for paper.
  • the present invention relates also to a process according to claim 12 for producing of multi-layer fibrous product.
  • a multilayered fibrous product usually consisting of two or three layer is called a “liner”.
  • a liner can be completely brown (kraft-liner) or partially white (white-lined liner) or its top layer can be coated.
  • the liner can be made of virgin fibre or recycled fibre or both.
  • a liner is used as a surface of a background liner in a corrugate board package.
  • the special characteristics of kraft-liners are strength, uniform quality and product safety. Strength is with kraft-liners a very important competitive advantage when comparing with recycled fibre-based products. The advantages of using test liners that contain recycled fibre are low price and the ecological values that support recycling.
  • the products called “Kemiart Graph” and “Kemiart Lite” and the uncoated “Kemiart Brite” of Oy Metsä-Botnia Ab can be mentioned as examples of commercial coated liners.
  • the liner product of Oy Metsä-Botnia Ab is a kraft-liner that has two fibre layers, the base layer being high yield softwood sulphate pulp and the top layer of bleached birch and softwood sulphate pulp. The fillers are used in the top layer to give the surface more brightness and smoothness, which improves the pritability properties.
  • the coating is added to the coated products with an on-line coating unit.
  • the coating is, for example, a combination of kaolin, carbonate and latex which improves significantly the printability of the product.
  • the final gloss and smoothness of the final product are obtained with calendering.
  • the method of producing the top layer of the white lined linerboard (cover layer) is considerably more expensive than the method of producing brown back layer.
  • the product can be optimised by changing, for example, the strengths of the fibre layers. In that case it would be reasonable to produce the liner the top layer of which is as lightweight as possible. So far, however, the attempts to reduce the weight of the cover while maintaining a sufficient brightness of a liner without making the cover too weak, have been unsuccessful. The amount of the white fibre cannot be decreased easily, without the brown fibre showing through.
  • the top layer does also need to have a good formation, which shows directly as good printability. Thus bad formation is visible especially well in grey scales of offset printing and as mottled print quality.
  • the present invention is based on the idea that a composite filler consisting of fibrils and mineral pigments is used as a filler of the top layer of the fibre product mentioned in the introduction.
  • Finnish Patent Specification No. 100729 discloses a papermaking filler comprising porous aggregates formed by precipitated calcium carbonate particles on the surface of fines. What characterises this new kind of filler is that, according to the patent specification, the calcium carbonate is precipitated on fine fibrils produced by refining cellulose fibres and/or mechanical pulp fibres. The size distribution of the fines fraction corresponds mainly to the wire screen fraction P100.
  • the present invention it has been found that when the top layer of a multi-layer product is filled with the filler described above, the opacity of the surface increases so drastically that the grammage of the cover can be reduced significantly.
  • the top layer containing the new filler covers very efficiently the brown background despite the lower grammage.
  • fillers consisting at least partly of cellulose or lignocellulose fibrils, over which light scattering material particles has been precipitated, can be used as fillers.
  • These particles are typically inorganic salts precipitating in an aqueous phase, such as calcium carbonate, calcium sulphate, barium sulphate and calcium oxalate.
  • GB Patent No. 628603 describes a multi-layer paper or board, the top layer of which contains modified fibre bulk.
  • the bulk has been produced by impregnating the pulp with calcium chloride, after which the manipulated bulk is put in contact with carbonate compound, which causes the calcium carbonate to precipitate on the fibres—not on the fibrils.
  • the bulk has considerably poor strength properties. It is stated in the publication, that it would not be possible to produce paper from this material. Moreover, the bulk has very poor retention.
  • the fibre product according to the present invention is mainly characterised by what is stated in the characterising part of the claim 1 .
  • a white lined liner can be prepared with a lighter top layer without compromising the strength of the surface.
  • the proportions of the white and brown layers can be changed much more easily.
  • the filler content can be increased and as the filler is extremely white, the amount of the white layer can be significantly decreased.
  • the commercial manufactures of liners can also decrease the total grammage of the liner.
  • the grammage of the top layer according to the present invention can be at least about 5% by weight, preferably at least 10% by weight smaller than a top layer that has a corresponding opacity and formation and is prepared from the same fibre material and mineral pigment.
  • the filler has been found to improve the formation and stiffness of the top layer.
  • the better retention helps also to optimise/decrease the dosage of other paper making additives. Purity helps the operation of the machine and generally the operation efficiency of the machine improves, as the frequency of breaking down is smaller.
  • FIG. 1 present a side view of the principal structure of a two-layer fibre product and FIG. 1 b the corresponding four-layer fibre product,
  • FIG. 2 shows the light scattering factor of a two-layer fibre product produced according to the present invention and two reference products as a function of the Mullen indices with two different filling factors
  • FIG. 3 shows corresponding results as a function of the bonding power (ScottBond).
  • FIG. 4 shows corresponding results as a function of the tensile index
  • FIG. 5 uses bar graphs to present the brightness of four two-layer fibre products, wherein two has top layers that contain filler according to the present invention, and two other contain reference filler.
  • composite filler comprising cellulose fibrils, on which light scattering pigments have been precipitated, is added as filler to the top layer of the multi-layer fibre product.
  • Fibrils can originate from chemical pulp or mechanical pulp or mixtures thereof.
  • chemical pulp reference is herein made to a pulp, which has been treated with cooking chemicals to delignify cellulose fibres.
  • the fibrils are obtained by refining pulps produced with the sulphate process or with some other alkaline cooking method.
  • fibrils can originate also from chemi-mechanical or mechanical pulps.
  • the average thickness of cellulose or lignocellulose fibrils is smaller than 5 ⁇ m, conventionally smaller than 1 ⁇ m.
  • the fibrils are characterized by at least one of the following criteria:
  • their average thickness is 0.01-10 ⁇ m (preferably at maximum 5 ⁇ m and in particular at maximum 1 ⁇ m) and their average length is 10-1500 ⁇ m.
  • the source material for the fibrils i.e. the fines based on cellulose or other fibers, is fibrillated by beating it in a pulp refiner.
  • the desired fraction may, when necessary, be separated by using a screen, but fines need not always be screened.
  • Suitable fibril fractions include wire screen fractions P50-P400.
  • refiners with grooved blades are used.
  • the light-scattering material particles in the filler are inorganic or organic salts that can be formed from their source materials by precipitation in an aqueous medium.
  • Such compounds include calcium carbonate, calcium oxalate, calcium sulphate, barium sulphate, and mixtures thereof.
  • the material particles are deposited on the fibrils.
  • the amount of an inorganic salt compound in proportion to the fibril amount is approx. 0.0001-95% by weight, preferably approx. 0.1-90% by weight, most suitably approx. 60-80% by weight, calculated from the amount of filler, and approx. 0.1-80% by weight, preferably approx. 0.5-50% by weight, of the paper.
  • the filler is produced by precipitating a mineral pigment on the surface of fine fibrils prepared from cellulose fibres and/or mechanical pulp fibres.
  • the precipitation of calcium carbonate can be carried out by feeding into an aqueous slush of fibrils an aqueous calcium hydroxide solution which possibly contains a solid calcium hydroxide, and a compound which contains carbonate ions and is at least partly dissolved in water (e.g. sodium carbonate or ammonium carbonate). It is also possible to introduce into the aqueous phase carbon dioxide gas that, in the presence of calcium hydroxide, produces calcium carbonate There are formed string-of-pearls-like calcium carbonate crystal aggregates, which are held together by fibrils, i.e.
  • the diameter of the calcium carbonate particles in the aggregates is about 0.1 to 5 ⁇ m, typically about 0.2 to 3 ⁇ m.
  • the fibrils correspond to wire screen fractions P50 (or P100) to P400.
  • filler 1 to 90% by weight (dry weight), typically about 5 to 50% by weight, of this kind of filler is added to the top layer of a multi-layer product.
  • the filler described form at least 5% by weight, most suitably from 10 to 100% by weight of the filler of the base web and respectively 10 to 50% by weight of the fibre material of the base web.
  • the present filler can form 1 to 100% by weight of fibre material of the base web.
  • part of the filler can consist of conventional fillers, such as calcium carbonate. However, preferably at least 80%, especially preferably at least 90% of the precipitated light scattering pigment particles are attached into the fibrils.
  • FIGS. 1 a and 1 b illustrate the structures of the multi-layer products containing two and four layers, respectively.
  • FIG. 1 a illustrates a typical white lined liner board and
  • FIG. 1 b illustrates so called test liner.
  • the grammage of the fibre product according to the present invention is preferably about 50 to 500 g/m 2 , typically about 80 to 350 g/m 2 . Usually its grammage is over 125 g/m 2 , but products having a grammage below 100 g/m 2 qualify for small packages.
  • the liner according to the present invention comprises a two-layer product (see FIG. 1 a ), that has a surface of a cover layer 1 and a back layer 2.
  • the top layer covers the back layer so that the back layer cannot be seen through the top layer.
  • the number of layers in a layer product has no upper limit, there can be even up to 5, 6 or 7 layers.
  • the top layer contains filler described more precisely hereinbefore, so that the top layer covers the layers under it, the layers that can be produced from raw materials of cheap costs.
  • test liner type four-layer products of FIG. 1 b having a top layer 3, a layer 4 under the top layer, intermediate layer 5 and a back layer 6, are to be mentioned.
  • the virgin fibre can originate from softwood or hardwood (wood chips) or it can originate from cuttings.
  • Especially preferably virgin pulp is used in the top layer. This is most suitably produced by sulphate cooking (kraft pulp), because sulphate cooking gives a mass having especially good strength properties, as the name suggests.
  • the recycled fibre can originate e.g. from used corrugated board packages (OCC) or mixed fibres. Recycled fibres are used especially for the production of test liners.
  • the surface and back layer(s) can be produced from similar raw materials or from different source fibres.
  • the mass of the back layer can be cooked in high yield, after which a mild refining is performed on it.
  • the pulp of the back layer is cooked to a kappa value of 30 to 70 and the pulp of the top layer to lower kappa value of 25 (the kappa number of the unbleached pulp).
  • Bleaching can be performed in a manner known per se, e.g. as ECF of TCF bleaching.
  • Retention agents can be added to the slush e.g. in about 0.5 to 3% of the amount of the fibre material.
  • the liner is stuff or surface sized to improve the moisture resistance. If a low quality recycled fibre is used as raw material, it is preferable to use a surface-size press to produce a product that has sufficient strength. According to the machine the distribution of the base weight between the top and the back layer is about 20/80 . . . 40/60, typically about 30/70.
  • the grammage of the top layer is generally about 20 to 125 g/m 2 (see below).
  • the grammage of the top layer can be decreased over 10%, up to 20% or more, without deteriorating the optical or mechanical properties of the cover.
  • the layer product is produced in a manner known per se. According to one preferred embodiment both or all layers are produced first from slush of their own and spread on the Fourdriner wire. After this, the layers are couched fastened into each other. With regard to the production process, a reference is made to a text by Ari Kiviranta “Board Grades”, in a book series Paper Making Science and Technology, Book 18, Paper and Board Grades, Fapet Oy, Jyvaskyla 2000, pages 68 and 69.
  • a planar fibre product according to the present invention can be used as a top layer of different corrugate board packages.
  • the solution according to the present invention is especially preferably suitable for white lined top liner and coated white lined liner, both of which are used for demanding printing works.
  • the surface of the liner according to the invention is extremely smooth and uniform, and has at the same time high opacity and brightness can be made use of.
  • the grammage of the top layer is about 20 to 125 g/m 2 , most suitably about 50 to 80 g/m 2 , especially preferably about 55 to 70 g/m 2 , and bleached chemical cellulose pulp is used of the top layer.
  • mainly hardwood is used in the top layer.
  • typically over 80% of fibre material of pulp is hardwood and the rest softwood.
  • the fibre material of pulp can consist totally of hardwood.
  • Conventional coating mixtures can be used for coating of the coated white lined top layer product.
  • Precipitated calcium carbonate, ground calcium carbonate, calcium sulphate, calcium oxalate, aluminium silicate, kaolin (hydrous aluminium silicate), aluminium hydroxide, magnesium silicate, talc (hydrous magnesium silicate), titanium dioxide and barium sulphate, and mixtures thereof can be used as pigments.
  • Synthetic pigments can also be used.
  • the main pigments are kaolin, calcium carbonate, precipitated calcium carbonate and gypsum, which in general constitute over 50% of the dry solids in the coating mix.
  • Calcined kaolin, titanium dioxide, satin white, aluminium hydroxide, sodium silicoaluminate and plastics pigments are additional pigments, and their amounts are in general less than 25% of the dry solids in the mix.
  • Special-quality kaolins and calcium carbonates, as well as barium sulphate and zinc oxide of the special pigments should be mentioned as examples.
  • any known binders generally used in paper production can be used as binders in the coating composition. Besides the individual binders, it is also possible to use mixtures of binders. Examples of typical binders include synthetic latexes made up of polymers or copolymers of ethylenically unsaturated compounds, e.g. copolymers of the butadienestyrene type, and polyvinyl acetate having comonomers that contain carboxyl groups. Together with the materials mentioned above, it is possible to use, for example, water-soluble polymers, starch, CMC, hydroxyethyl cellulose and polyvinyl alcohol as binders.
  • additives and auxiliary agents such as dispersants, agents affecting the viscosity and water retention of the mix, lubricants, hardeners used for improving water-resistance, optical auxiliary agents, anti-foaming agents, pH control agents, and preservatives can be used in the coating composition.
  • the coating mix can be applied to the material web in a manner known per se.
  • the coating can be done before couching. Preferably it is done after forming the multi-layer structure.
  • the method according to the present invention for coating paper and/or board can be carried out with a conventional coating apparatus, in other words by blade coating, or by film coating or JET application. Coating can be done on-line or off-line.
  • the amount of grammage of the coating layer varies from 5 to 30 g/m 2 .
  • the above-described filler does not only improve opacity of the top layer but the filled layer is also very easy to be coated.
  • the amount of pigment or amounts of coatings required for the desired brightness can be decreased with the filler.
  • the opacity is significantly improved with the filler.
  • Birch sulphate pulp was refined with a Valmet JC-01 refiner to produce pulp that is suitable for production of filler.
  • the consistency of refining was about 4% and the total energy consumption was 343 kWh/t and specific edge load was 0.5 J/m.
  • Carbonating was performed in tap water according to the FI Patent Specification No. 100729. Water slurry that has dry matter content of 2.22% was produced. The final product had CaCO 3 content of 69.7% and a specific surface area of 10.6 m 2 /kg.
  • Fibre layers suitable for cover layer of two-layer white lined liner was produced from chemical pulp that contained 70% by weight of birch pulp and 30% by weight of pine pulp. Filler was added from the pulp in the slush in various amounts: 13 and 20% by weight, respectively, of filler described in example 1 (SuperFill), 14 and 16% by weight, respectively, precipitated calcium carbonate (PCC, Albacar LO, ref. 1) and 14% by weight of mixture of chalk and calcined kaolin (ref. 2).
  • Filler was added from the pulp in the slush in various amounts: 13 and 20% by weight, respectively, of filler described in example 1 (SuperFill), 14 and 16% by weight, respectively, precipitated calcium carbonate (PCC, Albacar LO, ref. 1) and 14% by weight of mixture of chalk and calcined kaolin (ref. 2).
  • FIGS. 2 to 4 illustrate the light scattering ability of the obtained fibre layers as a function of mechanical strength properties.
  • the figures show that the light scattering factor is at least 25% and about 20% greater with the SuperFill filler when compared with references 1 and 2 in constant strengths.
  • Consequence of this is that the grammage of the surface can be decreased by about 20%, which decreases significantly production costs of liner.
  • FIG. 5 shows a result in which the above presented results are substantiated.
  • the result is from a liner test run made by pilot machine (FEX) of STFI in Sweden, wherein the grammage of the surface was decreased from the normal level of 75 g/m 2 to a level of 65 g/m 2 .
  • FEX pilot machine
  • FIG. 5 shows that the top layer lightened 10 g/m 2 with Superfill, generates brightness which is 4 brightness units greater as compared with the reference 2, in which the grammage is 75 g/m 2 .
  • the result is extremely good and it suggests that the grammage of the surface can be decreased even lower than 10 g/m 2 .

Landscapes

  • Chemical & Material Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Paper (AREA)
US10/475,773 2001-04-24 2002-04-24 Multilayered fibrous product and process for the production thereof Abandoned US20040168779A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
FI20010848A FI117871B (fi) 2001-04-24 2001-04-24 Monikerroksinen kuitutuote ja menetelmä sen valmistamiseksi
FI20010848 2001-04-24
PCT/FI2002/000342 WO2002092910A1 (en) 2001-04-24 2002-04-24 Multilayered fibrous product and a process for the production thereof

Publications (1)

Publication Number Publication Date
US20040168779A1 true US20040168779A1 (en) 2004-09-02

Family

ID=8561048

Family Applications (1)

Application Number Title Priority Date Filing Date
US10/475,773 Abandoned US20040168779A1 (en) 2001-04-24 2002-04-24 Multilayered fibrous product and process for the production thereof

Country Status (9)

Country Link
US (1) US20040168779A1 (https=)
EP (1) EP1392923B1 (https=)
JP (1) JP4582998B2 (https=)
CN (1) CN100396848C (https=)
AU (1) AU2002249300B2 (https=)
CA (1) CA2445100C (https=)
FI (1) FI117871B (https=)
NZ (1) NZ529159A (https=)
WO (1) WO2002092910A1 (https=)

Cited By (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20030127202A1 (en) * 2002-01-05 2003-07-10 Reinheimer Horst Alfred Multiply tissue product
US20040007340A1 (en) * 2000-12-09 2004-01-15 Watson Mark Victor Security paper
US20040168781A1 (en) * 2002-08-05 2004-09-02 Petri Silenius Noil for use in paper manufacture, method for its production, and paper pulp and paper containing such noil
US20040244927A1 (en) * 2001-06-06 2004-12-09 Fabienne Pianta Method for manufacturing a multi-layered pulp product comprising a filler between layers
US20060032596A1 (en) * 2002-10-24 2006-02-16 Markku Leskela Method for producing fiber product
US20060060318A1 (en) * 2002-10-24 2006-03-23 Petri Silenius Method for manufacturing paper and board
US20060065379A1 (en) * 2004-09-29 2006-03-30 Babcock Bruce W White top paperboard
US20100000693A1 (en) * 2006-10-31 2010-01-07 Basf Se Method for producing a multi layer fiber web from cellulose fibers
JP2018040070A (ja) * 2016-09-05 2018-03-15 王子ホールディングス株式会社 段ボール用白色ライナー及びその製造方法、並びに白色段ボール
US10011528B2 (en) 2014-10-10 2018-07-03 Fpinnovations Compositions, panels and sheets comprising mineral fillers and methods to produce the same
US20190368121A1 (en) * 2016-11-28 2019-12-05 Nippon Paper Industries Co., Ltd. Method for producing composite body of fibers and inorganic particles, and laminate containing composite body of fibers and inorganic particles
CN111335067A (zh) * 2020-04-14 2020-06-26 联盛纸业（龙海）有限公司 一种提高纸面l值亮度的牛卡纸、其面层及生产方法
CN111655928A (zh) * 2017-12-28 2020-09-11 克拉宾股份公司 由短化学纤维制成的牛皮纸
US11268241B2 (en) 2017-03-31 2022-03-08 Nippon Paper Industries Co., Ltd Method for manufacturing inorganic particle composite fiber sheet
US11441268B2 (en) * 2018-01-05 2022-09-13 International Paper Company Paper products having increased bending stiffness and cross-direction strength and methods for making the same
US20240125052A1 (en) * 2021-01-27 2024-04-18 Klabin S.A. White top kraftliner paper, production process of said paper, use of paper and packaging

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
RU2360059C2 (ru) * 2004-07-14 2009-06-27 Интернэшнл Пэйпа Кампани Способ производства бумаги
FI20055380A7 (fi) * 2005-07-01 2007-01-02 M Real Oyj Menetelmä selluloosahiukkasten pinnoittamiseksi, pinnoitetut selluloosahiukkaset ja niiden käyttö paperin- ja kartonginvalmistuksessa
US20070202283A1 (en) * 2006-02-27 2007-08-30 John Meazle Reducing top ply basis weight of white top linerboard in paper or paperboard
FI118809B (fi) * 2006-09-11 2008-03-31 M Real Oyj Menetelmä kuitutuotteen valmistamiseksi
FI20085767A7 (fi) * 2008-08-11 2010-02-12 Kemira Oyj Kipsituote
JP5528760B2 (ja) * 2009-09-30 2014-06-25 日本製紙株式会社 セルロースナノファイバーを添加して抄紙した紙およびその製造方法
CN102535251B (zh) * 2011-12-30 2013-11-06 淄博欧木特种纸业有限公司 无尘埃耐磨纸及其制作方法
AT524998B1 (de) * 2021-04-21 2023-02-15 Mondi Ag Bedruckbares, mehrlagiges Papier für Verpackungen und Verfahren zu dessen Herstellung
AT526619A1 (de) 2022-11-08 2024-05-15 Mondi Ag Verfahren zur Herstellung einer bedruckbaren Linerbahn für Verpackungen sowie bedruckbarer Liner für Verpackungen
AT526620A1 (de) 2022-11-08 2024-05-15 Mondi Ag Verfahren zur Herstellung einer bedruckbaren Linerbahn für Verpackungen sowie bedruckbarer Liner für Verpackungen

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4210490A (en) * 1976-07-14 1980-07-01 English Clays Lovering Pochin & Company, Limited Method of manufacturing paper or cardboard products
US5223090A (en) * 1991-03-06 1993-06-29 The United States Of America As Represented By The Secretary Of Agriculture Method for fiber loading a chemical compound
US5824364A (en) * 1992-04-07 1998-10-20 International Paper Company Methods of manufacture for highly loaded fiber-based composite material
US6156118A (en) * 1997-11-21 2000-12-05 Metsa-Serla Corporation Filler for use in paper manufacture and method for producing it

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR935128A (fr) * 1946-01-28 1948-06-10 Vanderbilt Co R T Perfectionnements à la fabrication du papier
CA2195300C (en) * 1995-05-18 2001-06-12 Michael C. Withiam Method for preparation of pigmented paper fibers and fiber products
FI100729B (fi) * 1995-06-29 1998-02-13 Metsae Serla Oy Paperinvalmistuksessa käytettävä täyteaine ja menetelmä täyteaineen va lmistamiseksi
FI100670B (fi) * 1996-02-20 1998-01-30 Metsae Serla Oy Menetelmä täyteaineen lisäämiseksi selluloosakuituperäiseen massaan

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4210490A (en) * 1976-07-14 1980-07-01 English Clays Lovering Pochin & Company, Limited Method of manufacturing paper or cardboard products
US5223090A (en) * 1991-03-06 1993-06-29 The United States Of America As Represented By The Secretary Of Agriculture Method for fiber loading a chemical compound
US5824364A (en) * 1992-04-07 1998-10-20 International Paper Company Methods of manufacture for highly loaded fiber-based composite material
US6156118A (en) * 1997-11-21 2000-12-05 Metsa-Serla Corporation Filler for use in paper manufacture and method for producing it

Cited By (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20040007340A1 (en) * 2000-12-09 2004-01-15 Watson Mark Victor Security paper
US7431798B2 (en) * 2000-12-09 2008-10-07 Arjo Wiggins Fine Papers Ltd. Security paper
US20040244927A1 (en) * 2001-06-06 2004-12-09 Fabienne Pianta Method for manufacturing a multi-layered pulp product comprising a filler between layers
US20030127202A1 (en) * 2002-01-05 2003-07-10 Reinheimer Horst Alfred Multiply tissue product
US7211171B2 (en) * 2002-01-05 2007-05-01 The Procter & Gamble Company Multiply tissue product
US20040168781A1 (en) * 2002-08-05 2004-09-02 Petri Silenius Noil for use in paper manufacture, method for its production, and paper pulp and paper containing such noil
US20110061826A1 (en) * 2002-10-24 2011-03-17 Markku Leskela Method for producing fiber product
US20060032596A1 (en) * 2002-10-24 2006-02-16 Markku Leskela Method for producing fiber product
US20060060318A1 (en) * 2002-10-24 2006-03-23 Petri Silenius Method for manufacturing paper and board
US8608905B2 (en) 2002-10-24 2013-12-17 Markku Leskela Method for producing fiber product
US8491755B2 (en) * 2002-10-24 2013-07-23 M-Real Oyj Method for manufacturing paper and board
US20060065379A1 (en) * 2004-09-29 2006-03-30 Babcock Bruce W White top paperboard
US7491293B2 (en) * 2004-09-29 2009-02-17 Meadwestvaco Corporation White top paperboard
US20100000693A1 (en) * 2006-10-31 2010-01-07 Basf Se Method for producing a multi layer fiber web from cellulose fibers
US10011528B2 (en) 2014-10-10 2018-07-03 Fpinnovations Compositions, panels and sheets comprising mineral fillers and methods to produce the same
JP2018040070A (ja) * 2016-09-05 2018-03-15 王子ホールディングス株式会社 段ボール用白色ライナー及びその製造方法、並びに白色段ボール
US20190368121A1 (en) * 2016-11-28 2019-12-05 Nippon Paper Industries Co., Ltd. Method for producing composite body of fibers and inorganic particles, and laminate containing composite body of fibers and inorganic particles
US11268241B2 (en) 2017-03-31 2022-03-08 Nippon Paper Industries Co., Ltd Method for manufacturing inorganic particle composite fiber sheet
CN111655928A (zh) * 2017-12-28 2020-09-11 克拉宾股份公司 由短化学纤维制成的牛皮纸
US20200370243A1 (en) * 2017-12-28 2020-11-26 Klabin S/A Kraftliner paper made of short chemical fibres
US11441268B2 (en) * 2018-01-05 2022-09-13 International Paper Company Paper products having increased bending stiffness and cross-direction strength and methods for making the same
US12146264B2 (en) 2018-01-05 2024-11-19 International Paper Company Paper products having increased bending stiffness and cross-direction strength and methods for making the same
CN111335067A (zh) * 2020-04-14 2020-06-26 联盛纸业（龙海）有限公司 一种提高纸面l值亮度的牛卡纸、其面层及生产方法
US20240125052A1 (en) * 2021-01-27 2024-04-18 Klabin S.A. White top kraftliner paper, production process of said paper, use of paper and packaging

Also Published As

Publication number Publication date
EP1392923B1 (en) 2018-07-25
FI20010848L (fi) 2002-10-25
JP2004525282A (ja) 2004-08-19
JP4582998B2 (ja) 2010-11-17
WO2002092910A1 (en) 2002-11-21
NZ529159A (en) 2005-07-29
FI20010848A0 (fi) 2001-04-24
CA2445100A1 (en) 2002-11-21
CA2445100C (en) 2012-12-18
CN1516770A (zh) 2004-07-28
AU2002249300B2 (en) 2008-04-24
FI117871B (fi) 2007-03-30
EP1392923A1 (en) 2004-03-03
CN100396848C (zh) 2008-06-25

Similar Documents

Publication Publication Date Title
EP1392923B1 (en) Multilayered fibrous product and a process for the production thereof
AU2002249300A1 (en) Multilayered fibrous product and a process for the production thereof
US8608905B2 (en) Method for producing fiber product
CA2444795C (en) Fibrous web and process for the preparation thereof
EP1392920B1 (en) Coated fibrous web and process for the production thereof
AU2002247793A1 (en) Coated fibrous web and process for the production thereof
CA2611272C (en) Method of producing a fibrous web comprising a filler
CN100585074C (zh) 纸和纸板制造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: M-REAL OYJ, FINLAND

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SILENIUS, PETRI;YLINIEMI, LEENA;MEURONEN, JARI;AND OTHERS;REEL/FRAME:015443/0988

Effective date: 20031112

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION