US20040144203A1 - Sintered body and production method thereof - Google Patents

Sintered body and production method thereof Download PDF

Info

Publication number
US20040144203A1
US20040144203A1 US10/758,113 US75811304A US2004144203A1 US 20040144203 A1 US20040144203 A1 US 20040144203A1 US 75811304 A US75811304 A US 75811304A US 2004144203 A1 US2004144203 A1 US 2004144203A1
Authority
US
United States
Prior art keywords
sintered body
metal powder
sintered
powder mixture
production method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/758,113
Other languages
English (en)
Inventor
Shigeru Unami
Satoshi Uenosono
Yutaka Mabuchi
Akira Fujiki
Yukihiro Maekawa
Takashi Murata
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Steel Corp
Nissan Motor Co Ltd
Original Assignee
JFE Steel Corp
Nissan Motor Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JFE Steel Corp, Nissan Motor Co Ltd filed Critical JFE Steel Corp
Assigned to NISSAN MOTOR CO., LTD., JFE STEEL CORPORATION reassignment NISSAN MOTOR CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: FUJIKI, AKIRA, MABUCHI, YUTAKA, MAEKAWA, YUKIHIRO, MURATA, TAKASHI, UENOSONO, SATOSHI, UNAMI, SHIGERU
Publication of US20040144203A1 publication Critical patent/US20040144203A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C33/00—Making ferrous alloys
    • C22C33/02—Making ferrous alloys by powder metallurgy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F1/00—Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
    • B22F1/10—Metallic powder containing lubricating or binding agents; Metallic powder containing organic material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F1/00—Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
    • B22F1/10—Metallic powder containing lubricating or binding agents; Metallic powder containing organic material
    • B22F1/105—Metallic powder containing lubricating or binding agents; Metallic powder containing organic material containing inorganic lubricating or binding agents, e.g. metal salts
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/02—Compacting only
    • B22F2003/023—Lubricant mixed with the metal powder
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/02—Compacting only
    • B22F2003/026—Mold wall lubrication or article surface lubrication
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2998/00—Supplementary information concerning processes or compositions relating to powder metallurgy

Definitions

  • the present invention relates to a powder metallurgy technique for producing a sintered metal body. More particularly, the present invention relates to a sintered metal body having excellent fatigue strength and abrasion resistance to be suitable for use in a sprocket of a silent chain, a high-strength part of an internal combustion engine (e.g. a connecting rod, a piston pin or a rocker arm) or the like and a method for producing such a sintered metal body at low cost.
  • an internal combustion engine e.g. a connecting rod, a piston pin or a rocker arm
  • a sintered body is produced by compacting a metal powder material repeatedly and then sintering the compacted powder material repeatedly.
  • a sintered body is produced by warm-compacting a metal powder material and sintering the compacted powder material at elevated temperatures.
  • the former technique results in relatively high production cost.
  • the latter technique may allow cost reduction, but has a limitation of improvement in sinter strength.
  • sinter strength notably fatigue strength and abrasion resistance
  • the proposed techniques are not always effective in pore size reduction and particle-to-particle bond strengthening and are no more than the modifications of the compacting and sintering processes.
  • a sintered body comprising: sintered metal particles forming a sintered structure and having a maximum particle size of 100 ⁇ m or smaller; and carbon being dispersed in the sintered structure in an amount of 0.05 to 1.0% by mass based on a total mass of the sintered body.
  • a sintered body having a sintered structure derived from a metal powder and containing carbon dispersed in the sintered structure in an amount of 0.05 to 1.0% by mass based on a total mass of the sintered body, the metal powder having a particle size of 75 ⁇ m or smaller.
  • a sintered body produced from a metal powder mixture, the metal powder mixture including a metal powder having a particle size of 75 ⁇ m or smaller, a graphite powder in an amount 0.1 to 1.0% by mass and a powder lubricant in an amount of 0.05 to 0.80% by mass based on a total mass of the metal powder mixture.
  • a production method of a sintered body comprising: preparing a metal powder mixture, the metal powder mixture including a fine metal powder having a particle size of 75 ⁇ m or smaller, a graphite powder in an amount of 0.1 to 1.0% by mass and a powder lubricant in an amount of 0.05 to 0.80% by mass based on a total mass of the metal powder mixture; compacting the metal powder mixture to provide a green compact; and sintering the green compact.
  • FIG. 1 is a graph showing the abrasion performance of sintered bodies of Examples 1 to 4 according to the present invention.
  • FIG. 2 is a graph showing the abrasion performance of sintered bodies of Comparative Examples 1 to 4 according to the earlier technology.
  • FIG. 3 is an optical micrograph of the sintered body of Example 3.
  • FIG. 4 is an optical micrograph of the sintered body of Comparative Example 3.
  • the present inventors have found that the use of a fine powder as a raw material allows substantial reduction of the size of pores in a sintered body in addition to increase in the compactness of a green compact.
  • the present inventors have also found that the use of such a fine powder strengthens particle-to-particle bonding of the sintered body, because the fine powder allows promoted diffusion of powder particles during sintering due to a large particle surface.
  • the fine powder is generally low in compactibility
  • the present inventors have found that the compactibility of the fine powder can be improved by the combination of die lubrication and warm compaction. Further, the present inventors have found that the sintering of the compacted fine powder at a high temperature maximizes the particle diffusion, thereby attaining sinter strength higher than ever before.
  • the present invention has been made based on the above findings.
  • a sintered body is produced by preparing a metal powder mixture, compacting the metal powder mixture to provide a green compact, and then, sintering the green compact.
  • the metal powder mixture includes a fine metal powder, a graphite powder and a powder lubricant.
  • the fine metal powder usable in the metal powder mixture is not particularly restricted and can be selected among various powder metallurgical materials, such as carbon steel powders and alloyed steel powders, depending on the performance required of the sintered body.
  • the metal powder may be in the form of a completely alloyed steel powder (prepared by the melting and powdering of a desired steel composition), a partially diffusion-alloyed steel powder (prepared by the diffusion joining of alloying metal grains to iron grains), or a blend of a steel powder and an alloying metal powder optionally together with a partially diffusion-alloyed steel powder.
  • an iron-based powder such as an atomized pure iron powder with an iron content of 90% or more
  • an alloying metal powder such as a ferrous alloy powder, a Ni powder, a Cu powder or a Mo powder
  • a partially diffusion-alloyed steel powder thereof so as to attain higher compactibility than that attained by a completely alloyed steel powder or the like.
  • the metal powder preferably has a primary particle size of 75 ⁇ m or smaller.
  • the primary particles of the metal powder are larger than 75 ⁇ m in size, the driving force for sintering becomes so weak that that there arise large pores in the sintered body.
  • an alloying metal powder such as a Ni powder a Cu powder or a Mo powder
  • alloying metal elements do not diffuse properly in the sintering process.
  • the sintered body cannot be hardened to a sufficient degree even when heat-treated by e.g. gas carburizing, bright annealing or induction hardening for further improvement in strength, so that the sintered body has a relatively soft and rough ferrite or pearlite structure that can result in fatigue failure.
  • the fatigue strength of the sintered body thus becomes low.
  • the metal powder has been granulated using a binder (such as alumina sol or water glass), or by diffusion joining, so as to agglomerate the primary particles into secondary particles having a particle size of 180 ⁇ m or smaller.
  • a binder such as alumina sol or water glass
  • the granulation of the metal powder increases the apparent particle size and fluidity of the metal powder.
  • the mechanical properties of the sintered body depends on the primary particle size of the raw material, the fatigue strength of the sintered body does not become lowered as compared with a case where the metal powder has not been granulated.
  • the secondary particles of the metal powder are larger than 180 ⁇ m in size, the packability of the metal powder into a thin area becomes low.
  • the metal powder can be classified by screening for control of the primary and secondary particle sizes. Namely, the primary particle size of the metal powder can be controlled to 75 ⁇ m or smaller by, before the granulation process, passing the metal powder through a screen mesh having a mesh size of 75 ⁇ m (200 mesh) as defined by JIS Z8801. Further, the secondary particle size of the metal powder can be controlled to 180 ⁇ m or smaller by passing the granulated metal powder through a screen mesh having a mesh size of 180 ⁇ m (80 mesh) as defined by JIS Z8801.
  • the graphite powder is contained in the metal powder mixture in an amount of 0.05 to 1.0% based on the total mass of the metal powder mixture, such that graphite becomes dispersed throughout the sintered body for solid-solution strengthening.
  • the amount of graphite powder exceeds 1.0%, the green compact becomes low in density.
  • the amount of graphite powder is less than 0.1%, the graphite powder fails to provide a sufficient solid-solution strengthening effect.
  • the powder lubricant is contained in the metal powder mixture in an amount of 0.05 to 0.80% based on the total mass of the metal powder mixture, so as to increase the mobility of the solid particles of the metal powder mixture and thereby improve the compactibility of the metal powder mixture.
  • the amount of powder lubricant is less than 0.05%, the powder lubricant fails to provide sufficient lubricity so that the green compact becomes low in density.
  • the compact is susceptible to green cracking.
  • the amount of powder lubricant exceeds 0.80%, the powder lubricant keeps the powder mixture from plastic deformation rather than provides lubricity. The density of the green compact thus becomes so low that the sintered body decreases in density.
  • the powder lubricant usable in the metal powder mixture is not particularly restricted and can be selected from various lubricating materials to be released in the sintering process.
  • Specific examples of the powder lubricant include metallic soaps such as zinc stearate, lithium stearate and calcium stearate, and waxes such as ethylene-bis-stearoamide. These lubricant compounds can be used alone or in any combination thereof.
  • the metal powder mixture is desirably compacted while being heated to e.g. 100° C. or higher, so as to density the green compact and thereby reduce the size of pores between the particles and increase contact between the particles.
  • the highest temperature of the metal powder mixture in the compacting process is thus preferably limited to 150° C.
  • the metal powder mixture becomes cooled.
  • the die is preferably preheated to a temperature higher than the temperature of the metal powder mixture, e.g. 120° C. or higher.
  • the metal powder mixture is desirably compacted with a die lubricant applied to an inner surface of the die, so as to minimize the amount of powder lubricant contained in the metal powder mixture and thereby increase the density and strength of the sintered body.
  • the die lubricant usable is basically the same as the powder lubricant, such as zinc stearate, lithium stearate and calcium stearate or ethylene-bis-stearamide. In the case of applying the die lubricant by an electrostatic method, the die lubricant needs to be selected in view of its electrostatic property.
  • the process of applying the die lubricant to the die is not particularly restricted.
  • the die lubricant can be electrostatically adhered to the die by injecting a charged solid powder of die lubricant into the die.
  • the amount of die lubricant applied to the die is desirably 5 to 100 g/m 2 .
  • the amount of die lubricant is less than 5 g/m 2 , the above-mentioned effects cannot be obtained due to inadequate die lubrication.
  • the force to remove the compact from the die becomes large.
  • the amount of die lubricant exceeds 100 g/cm 2 ; the die lubricant remains on a surface of the green compact, thereby resulting in deteriorated appearance.
  • the green compact is desirably sintered at a temperature of 1180° C. or higher in an endothermic gas atmosphere (RX atmosphere), a hydrogen-containing nitrogen atmosphere or an ammonolysis atmosphere, or in a vacuum.
  • RX atmosphere endothermic gas atmosphere
  • the sintering of the green compact at such a high temperature effectively promote the diffusion of the particles in the sintering process so as to form stronger bonding between the particles and to densify the sintered body.
  • the cost of sintering increases with increase in the sintering temperature. It is thus necessary to select the sintering temperature appropriately for strength/cost tradeoffs.
  • the sintered body may be given any heat treatment as needed so as to increase in surface hardness and thereby obtain a further improvement in strength.
  • the heat treatment is not particularly restricted and can be a known treatment, such as gas carburizing, bright annealing or induction hardening.
  • the thus-produced sintered body has a sintered structure derived from the fine metal powder, i.e., a coherent bonded structure formed of sintered metal particles.
  • the “sintered metal particles” are herein defined as including agglomerates of pluralities of powder particles formed in the sintering process.)
  • the sintered metal particles have a maximum particle size of 100 ⁇ m or smaller.
  • the “maximum particle size” refers to the largest diameter of the particles.
  • the pore size of the sintered body is too large so that the initial defect of the sintered body that can result in exfoliation abrasion increases in size. The sintered body thus becomes low in strength and abrasion resistance.
  • the sintered body contains 0.05 to 1.0% of carbon derived from the graphite powder and carbon of the metal powder and dispersed in the sintered structure, based on the total mass of the sintered body. It is noted that a maximum of 0.05% of carbon is burned down in the sintering process. When the amount of carbon in the sintered body is less than 0.05%, the sintered body cannot attain desired strength and abrasion resistance. When the amount of carbon in the sintered body exceeds 1.0%, the sintered body is so hard as to be susceptible to sintering crack and embrittlement.
  • the produced sintered body advantageously shows excellent fatigue strength and abrasion resistance to be fit for a wide range of uses, such as a sprocket of an silent chain and a high-strength part of an internal combustion engine (e.g. a connecting rod, a piston pin or a rocker arm).
  • a sprocket of an silent chain and a high-strength part of an internal combustion engine (e.g. a connecting rod, a piston pin or a rocker arm).
  • teeth of the sprocket are susceptible to abrasion as the sprocket teeth receive, from the silent chain, a high surface pressure and a large impactive load accompanied by slippage.
  • the abrasion of the sprocket teeth is classified as “exfoliation abrasion” in which cracking occurs and develops due to the link-up of pores in the sprocket to cause exfoliation in a surface of the sprocket teeth. It becomes however possible to effectively protect the sprocket from such exfoliation abrasion by applying the above sintered body to the sprocket, because the sintered body is small in pore size, large in particle-to-particle contact and high in particle-to-particle bond strength.
  • the above sintered body may be applied only to the teeth of the sprocket while applying a low-priced material to other portions of the sprocket.
  • the sprocket may be produced by classifying a powder metal into a fine powder having a primary particle size of 75 ⁇ m or smaller and a residual powder, and then, using the fine powder for the teeth of the outer peripheral portion of the sprocket while using the residual powder for the inner peripheral portion of the sprocket, thereby reducing the cost of raw materials.
  • a partially diffusion-alloyed steel powder (as a fine metal powder) comprised of 4% of Ni, 0.5% of Mo, 1.5% of Cu and the balance being Fe was mixed with a graphite powder and ethylene-bis-stearamide (as a powder lubricant) by the use of a V-blender, thereby providing a metal powder mixture as a raw material.
  • the partially diffusion-alloyed steel powder had been formed by classifying an atomized pure iron powder by screening, blending the classified iron powder with a powder of Ni, Mo and Cu (having a particle size of 1 to 10 ⁇ m), heat-treating the blend at 850° C.
  • a die was preheated to a given temperature. Then, the metal powder mixture was heated to a given temperature and compacted in the preheated die by the application of a pressure of 686 MPa (7 t/cm 2 ), thereby forming a green compact with a length of 80 mm, a width of 15 mm and a height of 15 mm.
  • a pressure of 686 MPa (7 t/cm 2 ) Prior to the compacting process, zinc stearate (as a die lubricant) was electrostatically adhered to an inner surface of the die in Examples 2 and 3 and Comparative Examples 2 to 4. The amount of die lubricant applied to the die was 10 g/m 2 .
  • the green compact was sintered at a given temperature for 1 hour in an N 2 atmosphere containing 10 vol % of H 2 , thereby providing an iron-based sintered compact.
  • the heat temperatures of the metal powder mixture and the die in the compacting process and the sintering temperature were controlled as indicated in TABLE.
  • test sample having a parallel portion diameter of 8 mm and a straight portion length of 15.4 mm was cut from the sintered compact and then heat-treated under the following conditions.
  • Example 1 and Comparative Example 1 subjected to bright annealing, i.e., heated at 900° C. for 1 hour, oil-quenched at 60° C., and then, tempered at 180° C. for 1 hour.
  • Examples 2 to 4 and Comparative Examples 3 and 4 subjected to gas carburizing, i.e., heated at 900° C. for 2 hours in a carburizing atmosphere with a carbon potential of 0.9%.
  • Example 3 and Comparative Examples 3 and 4 were cut in half, and then, the resultant sample pieces were embedded in resinous sample stages and polished.
  • the thus-obtained samples were microscopically examined to observe sintered structures of Example 3 and Comparative Examples 3 and 4 and determine a maximum size of the sintered metal particles of each sintered structure in a observation field of 63 mm ⁇ 92 mm. The results are shown in TABLE and FIGS. 3 and 4.
  • the sintered sprocket and the other sprocket were linked by a 5- by 4-row silent chain (pitch: 6.35 mm, effective width: 10.9 mm), and then, the crankshaft was driven by an electric motor under the following conditions to examine an abrasion loss of the teeth of the sprocket of each example.
  • the test results are indicated in FIGS. 1 and 2.
  • the abrasion loss of the sprockets of Examples 2 to 4 and Comparative Examples 1 to 4 are indicated with respect to the abrasion loss of the sprocket of Example 1 as being represented by 1 (one).
  • the metal powder mixture was prepared by mixing the metal powder having a primary particle size of 75 ⁇ m of smaller and a secondary particle size of 180 ⁇ m or smaller with the above-specific amounts of graphite powder and powder lubricant, compacted and then sintered.
  • the sintered metal particles of the resultant sintered body of Example 3 had a maximum particle size of 100 ⁇ m or smaller, although the primary particle size of the metal powder of Example 3 was larger than those of Examples 1, 2 and 4. It is estimated that the sintered metal particles of the sintered bodies of Examples 1, 2 and 4 also had a maximum particle size of 100 ⁇ m or smaller in consideration of the interrelationship between the primary particle size and the maximum sintered metal particle size.
  • the sintered bodies of Examples 1 to 4 had high fatigue strength and abrasion resistance as indicated in TABLE and FIGS. 1 and 2.
  • the temperature of the metal powder mixture in the compacting process was lower in Example 4 than in Examples 1 to 3, and die lubrication was not performed in Example 4. This resulted in lower green density and sintered density.
  • the sintered body of Example 4 however had high fatigue strength and abrasion resistance, benefiting from the effect of using the above-mentioned fine metal powder as a raw material.
  • the metal powders of Comparative Examples 1 and 2 had a primary particle size larger than 75 ⁇ m.
  • Comparative Example 3 it is estimated that the sintered metal particles of the sintered bodies of Comparative Examples 1 and 2 had a maximum size exceeding 100 ⁇ m.
  • the sintered bodies of Comparative Examples 1 and 2 were therefore low in fatigue strength and abrasion resistance.
  • the metal powder of Comparative Example 4 also had a primary particle size larger than 75 ⁇ m. Further, the amount of powder lubricant added in the metal powder mixture was too much in Comparative Example 4. This resulted in low sintered density and a maximum sintered metal particle size exceeding 100 ⁇ m. Thus, the sintered body of Comparative Example 4 was also low in fatigue strength and abrasion resistance.
  • the sintered body of Comparative Example 3 had a maximum sintered metal particle size larger than 100 ⁇ m.
  • the fatigue strength of the sintered body of Comparative Example 3 was thus similar to those of the low-density sintered bodies of Comparative Examples 1, 2 and 4, although the sintered body of Comparative Example 3 was relatively high in density. Further, the abrasion resistance of the sintered body of Comparative Example 3 was low.
  • the sintered body can be produced by preparing the metal powder mixture from the fine metal powder, the graphite powder and the powder lubricant, warm-compacting the metal powder mixture optionally with die lubrication, and then, sintering the compacted powder mixture at a relatively high temperature in the present invention. If necessary, the metal powder may be granulated to a desired particle size. This makes it possible to provide the sintered body with a very small pore size, maximized particle-to-particle contact, strong particle-to particle bonding and high sintered density, thereby effectively preventing the occurrence and development of cracking in the sintered body effectively. In addition, there is no need to repeat the compaction and sintering processes for increased green density and sintered density. The sintered body is therefore produced at relatively low cost while attaining significantly improved fatigue strength and abrasion resistance to be suitable for use in a sprocket of a silent chain or a high-strength part of an internal combustion engine.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Powder Metallurgy (AREA)
US10/758,113 2003-01-17 2004-01-16 Sintered body and production method thereof Abandoned US20040144203A1 (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2003-009483 2003-01-17
JP2003009483A JP2004218041A (ja) 2003-01-17 2003-01-17 焼結部材及びその製造方法

Publications (1)

Publication Number Publication Date
US20040144203A1 true US20040144203A1 (en) 2004-07-29

Family

ID=32588561

Family Applications (1)

Application Number Title Priority Date Filing Date
US10/758,113 Abandoned US20040144203A1 (en) 2003-01-17 2004-01-16 Sintered body and production method thereof

Country Status (5)

Country Link
US (1) US20040144203A1 (de)
EP (1) EP1440751B1 (de)
JP (1) JP2004218041A (de)
CN (1) CN1517165A (de)
DE (1) DE602004005247T2 (de)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110193217A1 (en) * 2010-02-08 2011-08-11 Georg Meyer-Berg Manufacturing of a Device Including a Semiconductor Chip
CN105695847A (zh) * 2016-04-06 2016-06-22 郑邦宪 一种电力电网复合排管
CN106255563A (zh) * 2014-05-29 2016-12-21 株式会社神户制钢所 粉末冶金用混合粉末
US20160369881A1 (en) * 2013-07-02 2016-12-22 Takahiro Okuno Sintered machine part and method of manufacturing the same
US20170108045A1 (en) * 2014-03-20 2017-04-20 Ntn Corporation Bearing ring and roller bearing having said bearing ring
US11992880B1 (en) * 2019-07-22 2024-05-28 Keystone Powdered Metal Company Acoustical dampening powder metal parts

Families Citing this family (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102477496B (zh) * 2010-11-27 2015-06-10 湖南特力新材料有限公司 一种无铅易切削黄铜的制备方法
CN102477513B (zh) * 2010-11-27 2013-11-13 湖南特力新材料有限公司 一种无铅易切削钢的制备方法
CN102477515B (zh) * 2010-11-27 2013-06-12 湖南特力新材料有限公司 一种高强度无铅易切削钢的制备方法
CN102296225B (zh) * 2011-09-20 2013-06-12 中南大学 一种烧结无铅易切削钢的制备方法
CN102601355A (zh) * 2012-03-20 2012-07-25 昆明理工大学 一种提高铜金粉耐腐蚀性的表面改性方法
JP5967010B2 (ja) * 2013-05-08 2016-08-10 信越化学工業株式会社 希土類焼結磁石の製造方法
CN105899315A (zh) * 2014-01-22 2016-08-24 Ntn株式会社 烧结机械部件及其制造方法
CN104325134B (zh) * 2014-11-14 2016-08-24 武汉钢铁(集团)公司 含有纳米氧化亚铁的纳米铁粉烧结体及其制备方法
CN109856360A (zh) * 2018-12-31 2019-06-07 武汉新锐合金工具有限公司 一种测定混合料线收缩系数的试验方法
CN111957950B (zh) * 2020-08-11 2022-12-30 山东鲁银新材料科技有限公司 一种vvt链轮用无偏析预混合铁粉的生产方法
AT526261B1 (de) 2022-07-05 2024-03-15 Miba Sinter Austria Gmbh Verfahren zur Herstellung eines Bauteils aus einem Sinterpulver
CN116160004A (zh) * 2022-12-30 2023-05-26 扬州立德粉末冶金有限公司 一种结构经过改进的粉末冶金摇臂及该摇臂的制造工艺

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2637671A (en) * 1948-03-13 1953-05-05 Simonds Saw & Steel Co Powder metallurgy method of making steel cutting tools
US3460940A (en) * 1967-03-09 1969-08-12 Charles Robert Talmage Method of producing wrought high purity steels by powder metallurgy
US4588441A (en) * 1983-02-08 1986-05-13 Yutaka Ikenoue Process for the preparation of sintered alloys for valve mechanism parts for internal combustion engines
US5069867A (en) * 1990-02-22 1991-12-03 Miba Sintermetall Aktiengesellschaft Process of manufacturing high-strength sintered members
US5370725A (en) * 1992-11-30 1994-12-06 Nippon Piston Ring Co., Ltd. Synchronizer ring
US6068813A (en) * 1999-05-26 2000-05-30 Hoeganaes Corporation Method of making powder metallurgical compositions
US6120575A (en) * 1996-12-10 2000-09-19 Hoganas Ab Agglomerated iron-based powders
US6261514B1 (en) * 2000-05-31 2001-07-17 Höganäs Ab Method of preparing sintered products having high tensile strength and high impact strength
US6344169B2 (en) * 1998-11-05 2002-02-05 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Method for compaction of powders for powder metallurgy

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07505679A (ja) * 1992-12-21 1995-06-22 スタックポール　リミテッド ベアリングの製造方法
JP4183346B2 (ja) * 1999-09-13 2008-11-19 株式会社神戸製鋼所 粉末冶金用混合粉末ならびに鉄系焼結体およびその製造方法
JP2003096533A (ja) * 2001-07-19 2003-04-03 Kawasaki Steel Corp 温間成形用鉄基粉末混合物および温間金型潤滑成形用鉄基粉末混合物ならびにこれらを用いた鉄基焼結体の製造方法

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2637671A (en) * 1948-03-13 1953-05-05 Simonds Saw & Steel Co Powder metallurgy method of making steel cutting tools
US3460940A (en) * 1967-03-09 1969-08-12 Charles Robert Talmage Method of producing wrought high purity steels by powder metallurgy
US4588441A (en) * 1983-02-08 1986-05-13 Yutaka Ikenoue Process for the preparation of sintered alloys for valve mechanism parts for internal combustion engines
US5069867A (en) * 1990-02-22 1991-12-03 Miba Sintermetall Aktiengesellschaft Process of manufacturing high-strength sintered members
US5370725A (en) * 1992-11-30 1994-12-06 Nippon Piston Ring Co., Ltd. Synchronizer ring
US6120575A (en) * 1996-12-10 2000-09-19 Hoganas Ab Agglomerated iron-based powders
US6344169B2 (en) * 1998-11-05 2002-02-05 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Method for compaction of powders for powder metallurgy
US6068813A (en) * 1999-05-26 2000-05-30 Hoeganaes Corporation Method of making powder metallurgical compositions
US6261514B1 (en) * 2000-05-31 2001-07-17 Höganäs Ab Method of preparing sintered products having high tensile strength and high impact strength

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110193217A1 (en) * 2010-02-08 2011-08-11 Georg Meyer-Berg Manufacturing of a Device Including a Semiconductor Chip
US8193040B2 (en) * 2010-02-08 2012-06-05 Infineon Technologies Ag Manufacturing of a device including a semiconductor chip
US20160369881A1 (en) * 2013-07-02 2016-12-22 Takahiro Okuno Sintered machine part and method of manufacturing the same
US10107376B2 (en) * 2013-07-02 2018-10-23 Ntn Corporation Sintered machine part and method of manufacturing the same
US20170108045A1 (en) * 2014-03-20 2017-04-20 Ntn Corporation Bearing ring and roller bearing having said bearing ring
CN106255563A (zh) * 2014-05-29 2016-12-21 株式会社神户制钢所 粉末冶金用混合粉末
CN105695847A (zh) * 2016-04-06 2016-06-22 郑邦宪 一种电力电网复合排管
US11992880B1 (en) * 2019-07-22 2024-05-28 Keystone Powdered Metal Company Acoustical dampening powder metal parts

Also Published As

Publication number Publication date
CN1517165A (zh) 2004-08-04
JP2004218041A (ja) 2004-08-05
EP1440751A1 (de) 2004-07-28
EP1440751B1 (de) 2007-03-14
DE602004005247T2 (de) 2007-12-20
DE602004005247D1 (de) 2007-04-26

Similar Documents

Publication Publication Date Title
US20040144203A1 (en) Sintered body and production method thereof
JP2687125B2 (ja) エンジン用バルブ部品に用いる焼結金属コンパクトおよびその製造方法。
JP4183346B2 (ja) 粉末冶金用混合粉末ならびに鉄系焼結体およびその製造方法
JP5992402B2 (ja) 窒化焼結コンポーネントの製造方法
US20050252338A1 (en) Iron-based sintered alloy with dispersed hard particles
US8038761B2 (en) Iron-based sintered material and production method thereof
US7384446B2 (en) Mixed powder for powder metallurgy
JP2003268414A (ja) バルブシート用焼結合金、バルブシート及び製造方法
CN104711472A (zh) 低合金钢粉
EP2778243A1 (de) Gesintertes Gleitteil auf Basis einer Eisenlegierung und dessen Herstellungsmethode
EP2781283A1 (de) Gesintertes Gleitstück auf Eisen-Basis und dessen Herstellung
JPH1171651A (ja) バルブシート用鉄系焼結合金
JP2005042812A (ja) サイレントチェーン用焼結スプロケットおよびその製造方法
JP2001295915A (ja) サイレントチェーン用焼結スプロケットおよびその製造方法
JP2007023383A (ja) 焼結バルブシートおよびその製造方法
US20050039575A1 (en) Sintered sprocket for silent chain and production method therefor
CA2476836C (en) Alloy steel powder for powder metallurgy
JP6077499B2 (ja) 焼結合金用成形体、耐摩耗性鉄基焼結合金、およびその製造方法
JP3794452B2 (ja) バルブシート用鉄基焼結合金材
JP2004143526A (ja) 焼結歯車部品およびその製造方法
WO2000039353A1 (fr) Melange de poudre metallique destine a la metallurgie des poudres
JP3303030B2 (ja) 疲労強度および靱性に優れたコンロッドおよびその製造方法
JP3942136B2 (ja) 鉄基焼結合金
JP4093070B2 (ja) 合金鋼粉
JPH09256120A (ja) 耐摩耗性に優れた粉末冶金材料

Legal Events

Date Code Title Description
AS Assignment

Owner name: NISSAN MOTOR CO., LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:UNAMI, SHIGERU;UENOSONO, SATOSHI;MABUCHI, YUTAKA;AND OTHERS;REEL/FRAME:014897/0424;SIGNING DATES FROM 20031226 TO 20040109

Owner name: JFE STEEL CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:UNAMI, SHIGERU;UENOSONO, SATOSHI;MABUCHI, YUTAKA;AND OTHERS;REEL/FRAME:014897/0424;SIGNING DATES FROM 20031226 TO 20040109

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO PAY ISSUE FEE