Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
  • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
  • B41M5/50—Recording sheets characterised by the coating used to improve ink, dye or pigment receptivity, e.g. for ink-jet or thermal dye transfer recording
  • B41M5/52—Macromolecular coatings
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41J—TYPEWRITERS; SELECTIVE PRINTING MECHANISMS, i.e. MECHANISMS PRINTING OTHERWISE THAN FROM A FORME; CORRECTION OF TYPOGRAPHICAL ERRORS
  • B41J11/00—Devices or arrangements  of selective printing mechanisms, e.g. ink-jet printers or thermal printers, for supporting or handling copy material in sheet or web form
  • B41J11/0015—Devices or arrangements  of selective printing mechanisms, e.g. ink-jet printers or thermal printers, for supporting or handling copy material in sheet or web form for treating before, during or after printing or for uniform coating or laminating the copy material before or after printing
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
  • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
  • B41M5/0011—Pre-treatment or treatment during printing of the recording material, e.g. heating, irradiating
  • B41M5/0017—Application of ink-fixing material, e.g. mordant, precipitating agent, on the substrate prior to printing, e.g. by ink-jet printing, coating or spraying
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
  • B41M7/00—After-treatment of prints, e.g. heating, irradiating, setting of the ink, protection of the printed stock
  • B41M7/0018—After-treatment of prints, e.g. heating, irradiating, setting of the ink, protection of the printed stock using ink-fixing material, e.g. mordant, precipitating agent, after printing, e.g. by ink-jet printing, coating or spraying
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/16—Nitrogen-containing compounds
  • C08K5/29—Compounds containing one or more carbon-to-nitrogen double bonds
  • C08K5/31—Guanidine; Derivatives thereof
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D179/00—Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing nitrogen, with or without oxygen, or carbon only, not provided for in groups C09D161/00 - C09D177/00
• • D—TEXTILES; PAPER
  • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
  • D06P—DYEING OR PRINTING TEXTILES; DYEING LEATHER, FURS OR SOLID MACROMOLECULAR SUBSTANCES IN ANY FORM
  • D06P1/00—General processes of dyeing or printing textiles, or general processes of dyeing leather, furs, or solid macromolecular substances in any form, classified according to the dyes, pigments, or auxiliary substances employed
  • D06P1/44—General processes of dyeing or printing textiles, or general processes of dyeing leather, furs, or solid macromolecular substances in any form, classified according to the dyes, pigments, or auxiliary substances employed using insoluble pigments or auxiliary substances, e.g. binders
  • D06P1/52—General processes of dyeing or printing textiles, or general processes of dyeing leather, furs, or solid macromolecular substances in any form, classified according to the dyes, pigments, or auxiliary substances employed using insoluble pigments or auxiliary substances, e.g. binders using compositions containing synthetic macromolecular substances
  • D06P1/5264—Macromolecular compounds obtained otherwise than by reactions involving only unsaturated carbon-to-carbon bonds
  • D06P1/5285—Polyurethanes; Polyurea; Polyguanides
• • D—TEXTILES; PAPER
  • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
  • D06P—DYEING OR PRINTING TEXTILES; DYEING LEATHER, FURS OR SOLID MACROMOLECULAR SUBSTANCES IN ANY FORM
  • D06P1/00—General processes of dyeing or printing textiles, or general processes of dyeing leather, furs, or solid macromolecular substances in any form, classified according to the dyes, pigments, or auxiliary substances employed
  • D06P1/44—General processes of dyeing or printing textiles, or general processes of dyeing leather, furs, or solid macromolecular substances in any form, classified according to the dyes, pigments, or auxiliary substances employed using insoluble pigments or auxiliary substances, e.g. binders
  • D06P1/64—General processes of dyeing or printing textiles, or general processes of dyeing leather, furs, or solid macromolecular substances in any form, classified according to the dyes, pigments, or auxiliary substances employed using insoluble pigments or auxiliary substances, e.g. binders using compositions containing low-molecular-weight organic compounds without sulfate or sulfonate groups
  • D06P1/642—Compounds containing nitrogen
  • D06P1/649—Compounds containing carbonamide, thiocarbonamide or guanyl groups
  • D06P1/6494—Compounds containing a guanyl group R-C-N=, e.g. (bi)guanadine, dicyandiamid amidines
• • D—TEXTILES; PAPER
  • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
  • D06P—DYEING OR PRINTING TEXTILES; DYEING LEATHER, FURS OR SOLID MACROMOLECULAR SUBSTANCES IN ANY FORM
  • D06P5/00—Other features in dyeing or printing textiles, or dyeing leather, furs, or solid macromolecular substances in any form
  • D06P5/30—Ink jet printing
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
  • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
  • B41M5/0041—Digital printing on surfaces other than ordinary paper
  • B41M5/0047—Digital printing on surfaces other than ordinary paper by ink-jet printing
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
  • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
  • B41M5/0041—Digital printing on surfaces other than ordinary paper
  • B41M5/0058—Digital printing on surfaces other than ordinary paper on metals and oxidised metal surfaces
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
  • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
  • B41M5/0041—Digital printing on surfaces other than ordinary paper
  • B41M5/0064—Digital printing on surfaces other than ordinary paper on plastics, horn, rubber, or other organic polymers
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
  • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
  • B41M5/0041—Digital printing on surfaces other than ordinary paper
  • B41M5/007—Digital printing on surfaces other than ordinary paper on glass, ceramic, tiles, concrete, stones, etc.
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
  • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
  • B41M5/50—Recording sheets characterised by the coating used to improve ink, dye or pigment receptivity, e.g. for ink-jet or thermal dye transfer recording
  • B41M5/502—Recording sheets characterised by the coating used to improve ink, dye or pigment receptivity, e.g. for ink-jet or thermal dye transfer recording characterised by structural details, e.g. multilayer materials
  • B41M5/508—Supports
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
  • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
  • B41M5/50—Recording sheets characterised by the coating used to improve ink, dye or pigment receptivity, e.g. for ink-jet or thermal dye transfer recording
  • B41M5/52—Macromolecular coatings
  • B41M5/5218—Macromolecular coatings characterised by inorganic additives, e.g. pigments, clays
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
  • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
  • B41M5/50—Recording sheets characterised by the coating used to improve ink, dye or pigment receptivity, e.g. for ink-jet or thermal dye transfer recording
  • B41M5/52—Macromolecular coatings
  • B41M5/5236—Macromolecular coatings characterised by the use of natural gums, of proteins, e.g. gelatins, or of macromolecular carbohydrates, e.g. cellulose
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
  • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
  • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
  • B41M5/50—Recording sheets characterised by the coating used to improve ink, dye or pigment receptivity, e.g. for ink-jet or thermal dye transfer recording
  • B41M5/52—Macromolecular coatings
  • B41M5/5245—Macromolecular coatings characterised by the use of polymers containing cationic or anionic groups, e.g. mordants

Definitions

• This invention relates to a coating compositions, to recording materials and to processes for making and using recording materials.
• IJP Ink-jet printing
• IJP is a non-impact printing technique in which droplets of ink are ejected through a fine nozzle onto a recording material without bringing the nozzle into contact with the recording material.
• the images prepared by IJP desirably meet many demanding requirements. For example, they should be sharp and non-feathered and should also exhibit high water-fastness, light-fastness, humidity-fastness and optical density without suffering from significant hue shift. Both the ink and recording material used in forming the image play a key role in ensuring these requirements are met.
• Recording material used in ink-jet printing can be plain paper, coated paper, plastic film, cloth, and any other coated or uncoated material that can absorb ink and form a good image.
• the recording material usually comprises a substrate carrying a dry coating layer obtained from a specially formulated coating composition.
• These coating layers can be divided into two major categories: fully dense coatings (also known as swellable coatings) and porous coatings.
• the fully dense coatings are mainly comprised of film-forming polymers, with at least one of the polymers being hydrophilic. This hydrophilic polymer is either water soluble or water swellable. Sometimes a small amount of pigment is incorporated into these coatings, but the weight ratio of pigment to binder in the coating composition is usually 1:1 or less. Fully dense coatings give a glossy surface and are usually transparent. They absorb ink and form an image through rapid swelling of the coating itself. However, they often display poor wet-fastness and rub-fastness.
• porous coatings have the advantage over fully dense coatings in that they allow faster “drying” of the ink.
• certain coating compositions are useful for preparing recording materials having beneficial properties.
• a coating composition comprising pigment, medium and binder comprising a poly(C 3-18 -hydrocarbyl mono guanidine) and characterised in that the weight ratio of pigment to binder in the composition is at least 2:1.
• the poly(C 3-18 -hydrocarbyl mono guanidine) (“PMG”) preferably comprises a plurality of groups of Formula (1) and/or groups of Formula (2) or salts thereof:
• each m independently is 0 or 1;
• each Y independently is a C 3-18 -hydrocarbyl group
• a and B are hydrocarbyl groups which together comprise a total of 3 to 18 carbon atoms;
• each R independently is hydrogen, optionally substituted alkyl or optionally substituted alkoxy.
• each m is 0.
• the hydrocarbyl groups in the PMG and represented by Y, A and B are optionally interrupted by one or more hetero atoms or groups and optionally carry one or more substituents other than hydrogen.
• Preferred interrupting atoms and groups are —O—, —S—, —NH—, —C( ⁇ O)— and phenylene.
• Preferred optional substituents are hydroxy; C 1-4 -alkoxy; halo, especially chloro or bromo; nitro; amino; substituted amino; and acid groups, especially carboxy, sulpho phosphato, guanidino and substituted guanidino.
• hydrocarbyl group represented by Y, A or B is an alkylene group it is preferably straight chain or branched chain.
• the hydrocarbyl groups in the PMG and represented by Y are C 3-18 -alkylene (more preferably C 4-16 -alkylene, especially C 6-12 -alkylene, more especially C 6 -alkylene); C 3-12 -arylene more preferably C 6-10 -arylene, especially phenylene or naphthylene; C 7-12 -arakylene (more preferably C 7-11 -arylene, especially benzylene or xylyene); or a combination thereof, optionally interrupted by one or more —O—, —S—, —NH— or —C( ⁇ O)— groups.
• the hydrocarbyl groups represented by A and B are each independently C 2-6 -alkylene, optionally interrupted by one or more —O—, —S—, —NH— or —C( ⁇ O)— groups, with the proviso that A and B comprise a total of 2 to 12 carbon atoms, preferably 3 to 6 carbon atoms, more preferably 3 or 4 carbon atoms.
• one of A or B is —CH 2 — or —(CH 2 ) 2 — and the other is —(CH 2 ) 2 —, more especially both A and B are —(CH 2 ) 2 —
• Examples of preferred-hydrocarbyl groups represented by Y include —CH 2 C 6 H 4 CH 2 —, —CH 2 OC 6 H 4 OCH 2 —, —CH 2 OC 6 H 10 OCH 2 —, —(CH 2 ) 3 O(CH 2 ) 3 —, and —(CH 2 ) 2 S(CH 2 ) 2 —.
• Examples of particularly preferred -hydrocarbyl groups represented by Y include —(CH 2 ) 6 —, —(CH 2 ) 8 —, —(CH 2 ) 9 —, —(CH 2 ) 12 —, —CH 2 CH(—CH 3 )(CH 2 ) 4 CH 3 , 1,4-2,3- and 1,3-butylene, 2,5-hexylene, 2,7-heptylene, 3-methyl-1,6-hexylene.
• all groups represented by Y are the same and are C 4-16 -alkylene, more preferably C 4-12 -alkylene, especially C 4-8 -alkylene more especially 1,6-hexylene.
• each R independently is H, C 1-4 -alkyl, C 1-4 -alkoxy or C 1-4 -alkoxy-OH, more preferably H or methyl, especially H.
• the PMG consists essentially of groups of Formula (1).
• R More preferably all groups represented by R are H.
• terminating groups on the PMG are amino and guanidinino.
• the PMG preferably comprises one or more groups of Formula (3) or salts thereof:
• n is 2 to 100, preferably 2 to 50, especially 3 to 25.
• the PMGs may be prepared by the reaction of guanidine hydrochloride with a diamine, for example of the formula H 2 N—Y—NH 2 , HN(—A—)(—B—)NH or with a mixture of such diamines, wherein Y, A and B are as defined above.
• the PMG may be either a single discrete species or a mixture of polymers of varying chain length containing one or more repeat units of Formula (1) and or (2).
• the PMG is a mixture of polymers of varying chain length then preferably it comprises a single type of repeat unit of Formula (1) or (2).
• the PMG may also contain repeating units other than repeat units of Formula (1) and (2).
• the number of biguanide groups is less than 70%, more preferably less than 60%, and in one embodiment less than 10%, in each case relative to the total number of biguanide and monoguanidine groups in the PMG.
• the PMG substantially comprises repeat units of Formula (1) and/or (2).
• the PMG is preferably in the form of a salt.
• Preferred salts are those with organic or inorganic acids, especially water-soluble salts, for example the gluconate, acetate, phosphate or hydrochloride salt.
• the PMG is preferably colourless, or substantially colourless.
• the pigment preferably comprises clay, calcium carbonate, magnesium carbonate, silica (especially surface modified silica), zeolite, alumina or a combination of two or more thereof.
• the pigment comprises alumina or surface modified silica or a mixture thereof.
• the pigment is a porous pigment because this improves the porosity and water-fastness of recording materials prepared from the composition.
• Examples of preferred porous pigments include fumed and precipitated silicas.
• the pigment has a BET surface area greater than 25 m 2 /g, more preferably greater than 50 m 2 /g.
• the binder comprises a PMG and one or more further binders.
• the additional binder is preferably a polymeric binder, more preferably a water-soluble or water-dissipatable polymeric binder.
• the preferred water-soluble polymeric binders include starches, preferably hydroxy alkyl starches, for example hydroxyethylstarch; celluloses, for example cellulose, methylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, hydroxyethyl methyl cellulose, carboxymethlycellulose (and salts thereof) and cellulose acetate butyrate; gelatin; gums, for example guar, xanthan gum and gum arabic; polyvinylalcohol; polyvinylphosphate; polyvinylpyrrolidone; polyethylene glycol; hydrolysed polyvinylacetate; polyethylene imine; polyacrylamides, for example polyacrylamide and poly(N,N-dimethyl acrylamide) and polyacrylamido-2-methyl propane sulphonic acid); acrylamide-acrylic acid copolymers; polyvinylpyridine; polyvinylphosphate; vinylpyrrolidone-vinyl acetate copolymers; vinyl pyrroli
• Preferred water-dissipatable polymeric binders are: latex polymers, for example cationic, non-ionic and anionic styrene-butadiene latexes; vinyl acetate-acrylic copolymer latexes; acrylic copolymer latexes which carry amino groups, for example containing copolymerised dimethylaminoethyl (meth)acrylate; and dispersions of polyester, polyurethane, (meth)acrylate or vinyl polymers and copolymers thereof.
• the polymer dispersions are preferably prepared by emulsion polymerisation or by dispersion into water of polymers prepared by suspension, bulk or solution polymerisation.
• a combination of water-soluble polymeric binders and water-dissipatable polymeric binders can be beneficial in terms of improved mechanical strength, reduced tendency for sheets to stick together and good ink absorbency.
• the additional binder is polyvinylalcohol, methylcellulose, polyvinylpyrrolidone, or any combination thereof.
• the binder comprises a PMG comprising a repeat unit of Formula (1) and polyvinylalcohol.
• the polyvinyl alcohol is obtained by hydrolysis of polyvinylacetate, more preferably the hydrolysis value is greater than 70%. It is also preferred that the molecular weight of the polyvinyl alcohol is greater than 10,000 more preferably greater than 50,000.
• the weight ratio of pigment to binder in the composition is from 2:1 to 10:1.
• the weight ratio of pigment to binder in the composition is at least 3:1 and more preferably at least 4:1, especially at least 5:1 and more especially at least 6:1.
• the medium is a liquid medium since this makes it easier to apply the composition to the substrate.
• the binder that comprises a cationic polymer comprising a repeat unit of Formula (1) and any additional binder(s) are preferably dispersed or more preferably dissolved in the liquid medium.
• the liquid medium is preferably selected from water; organic solvent and a mixture of water and organic solvent.
• the organic solvent may comprise a mixture of one or more different organic solvents.
• the organic solvent is preferably water-soluble organic solvent.
• the liquid medium comprises a mixture of water and organic solvent that the organic solvent is less than 20% more preferably less than 10% by weight.
• Preferred water-soluble organic solvents include C, 1-6 -alkanols, preferably methanol, ethanol, n-propanol, isopropanol, n-butanol, sec-butanol, tert-butanol, n-pentanol, cyclopentanol and cyclohexanol; linear amides, preferably dimethylformamide or dimethylacetamide; ketones and ketone-alcohols, preferably acetone, methyl ether ketone, cyclohexanone and diacetone alcohol; diols, preferably diols having from 2 to 12 carbon atoms, for example pentane-1,5-diol, ethylene glycol, propylene glycol, butylene glycol, pentylene glycol, hexylene glycol and thiodiglycol and oligo- and poly-alkyleneglycols, preferably diethylene glycol, triethylene
• Especially preferred water-soluble organic solvents are cyclic amides, especially 2-pyrrolidone, N-methyl-pyrrolidone; diols, especially 1,5-pentane diol, ethyleneglycol, thiodiglycol, diethyleneglycol and triethyleneglycol; and mono- C 1-4 -alkyl and C 1-4 -alkyl ethers of diols, more preferably mono-C 1-4 -alkyl ethers of diols having 2 to 12 carbon atoms, especially 2-methoxy-2-ethoxy-2-ethoxyethanol.
• cyclic amides especially 2-pyrrolidone, N-methyl-pyrrolidone
• diols especially 1,5-pentane diol, ethyleneglycol, thiodiglycol, diethyleneglycol and triethyleneglycol
• mono- C 1-4 -alkyl and C 1-4 -alkyl ethers of diols more preferably mono-C
• liquid medium comprises only organic solvent it is preferred that it is free from water, (i.e. less than 1% water by weight).
• the liquid medium comprises only organic solvent it is also preferred that the solvent has a boiling point of from 30° to 200° C., more preferably of from 40° to 150° C., especially from 50 to 125° C.
• the organic solvent may be water-immiscible, water-soluble or a mixture of such solvents.
• Preferred water-soluble organic solvents are any of the hereinbefore described water-soluble organic solvents and mixtures thereof.
• Preferred water-immiscible solvents include, for example: aliphatic hydrocarbons; esters, preferably ethyl acetate; chlorinated hydrocarbons, preferably CH 2 Cl 2 ; and ethers, preferably diethyl ether; and mixtures thereof.
• the liquid medium comprises water or a mixture of water and one or more water-soluble organic solvent(s).
• composition may also comprise further ingredients if desired, for example catalysts (e.g. to accelerate cross-linking of the binder), polymeric fillers (e.g. polymethylmethacrylate particles of 10 to 50 ⁇ m diameter), primers, drying-time accelerants, adhesion promoters, defoamers, biocides, surfactants, cationic or anionic salts to name but a few.
• catalysts e.g. to accelerate cross-linking of the binder
• polymeric fillers e.g. polymethylmethacrylate particles of 10 to 50 ⁇ m diameter
• primers e.g. polymethylmethacrylate particles of 10 to 50 ⁇ m diameter
• drying-time accelerants e.g. to accelerate cross-linking of the binder
• adhesion promoters e.g. polymethylmethacrylate particles of 10 to 50 ⁇ m diameter
• defoamers e.g. polymethylmethacrylate particles of 10 to 50 ⁇ m diameter
• surfactants e.
• the composition also contains a cross-linker, preferably in an amount that causes from 0.1 to 5%, more preferably 0.15 to 4%, especially 0.2 to 2% cross-linking of cross-linkable components of the composition.
• a cross-linker preferably in an amount that causes from 0.1 to 5%, more preferably 0.15 to 4%, especially 0.2 to 2% cross-linking of cross-linkable components of the composition.
• Preferred cross-linkers include boric acid, isocyanate and blocked isocyanates, aziridines, carbodiimides and salts of divalent and trivalent metals (e.g. calcium and magnesium acetate).
• a preferred coating composition comprises:
• a more preferred coating composition comprises:
• a binder comprising 0.5 to 15 parts of PMG's comprising a plurality of groups of Formula (1) and 5 to 24.5 parts of a further binder comprising or consisting essentially of polyvinylalcohol, methylcellulose, polyvinylpyrrolidone, or any combination thereof;
• compositions may contain further components in addition to (a), (b) and (c) as described above:
• Preferred substrates include paper, plastic, a textile, metal or glass, more preferably paper, a textile or a plastic film (especially a transparent film, for example an overhead projector slide). It is especially preferred that the substrate is plain paper, coated paper or a transparent plastic film.
• composition may be applied to the substrate using any convenient method, for example by dip coating, reverse roller coating, K-bar coating, spraying or by means of an ink-jet printer. After application of the composition to the substrate it is preferred that the composition is dried and/or polymerised (e.g. cross-linked). Any suitable drying method may be used, for example hot air drying
• a recording material obtained from applying a composition according to the first aspect of the invention to a substrate.
• the composition may be applied to part or all of the recording material.
• the composition according to the first aspect of the invention is optionally applied to one or both sides thereof, more preferably to one side of the sheet.
• the process by which the recording material has been obtained preferably further comprises the step of drying the composition during or after it has been applied to the substrate, thereby forming a dry coating (a layer obtained in this way is hereinafter abbreviated as a “Coating Layer”) on the substrates.
• a dry coating a layer obtained in this way is hereinafter abbreviated as a “Coating Layer”.
• the dry coating has a total pore volume in the range 20 to 95% more preferably 30 to 75% relative to the total volume of the dry coating.
• the pigment is a cationic pigment, i.e. the zeta potential of the pigment is positive at the pH of the composition.
• the binder is non-ionic or cationic (or both) at the pH of the coating composition prior to coating.
• the Coating Layer may be the sole layer of a single layer coating on the substrate, or a layer that forms part of a multi-layer coating on the substrate.
• the Coating Layer may be at any position of the multi-layer coating, for example it may optionally be the inner-most layer in direct contact with the substrate, the outer-most layer, a layer between the inner-most and outer-most layers, or Coating Layers may be present at two or more of such positions.
• the outer-most layer is not a Coating Layer the layers that are further away from the substrate than the Coating Layer should be permeable or porous to allow ink to come into contact with the Coating Layer. It is however preferred that a Coating Layer is present as the only layer or the outer-most layer of a multi-layer coating on a substrate (i.e. the layer furthest away from the substrate) because this ensures good contact with inks during ink-jet printing.
• the substrate is plain paper, treated paper or a transparent plastic film.
• the recording material preferably has a thickness of from 10 to 1000 ⁇ m, more preferably from 50 to 500 ⁇ m.
• the substrate preferably has a thickness of from 9 to 990 ⁇ m, more preferably from 49 to 499 ⁇ m.
• the coating whether single- or multi-layered, preferably has an overall thickness of from 0.1 to 100 ⁇ m, more preferably from 5 to 50 ⁇ m, especially from 10 to 40 ⁇ m.
• composition is preferably applied to the substrate by the methods described above in relation to the first aspect of the invention.
• the recording materials may be used as ink receptive sheets in a wide range of printing processes, especially ink-jet printing. They are able to provide excellent quality images, often of near photographic quality, having good wet-fastness, light-fastness, gloss and low sticking and cracking properties.
• the resultant prints usually have good optical density, even with black pigment inks that often suffer from a drop in optical density, an unsightly grey appearance and poor image quality when printed onto conventional recording materials.
• the humidity fastness is also good.
• the sheets benefit from good storage stability and a low susceptibility to microbial decay.
• the recording material is white or transparent.
• a process for forming a recording material that comprises applying a composition according to the first aspect of the invention to a substrate.
• composition is preferably applied as described in the second aspect of the invention.
• Preferred substrates in the third aspect of the invention are as described in the second aspect of the invention.
• an ink-jet printing process that comprises applying ink to a recording material according to the second aspect of the invention by means of an ink-jet printer.
• the resultant monoguanidine was of Formula (3) as hereinbefore defined with an average value for n of 5, as determined by 1 H NMR end group analysis.
• the following fixing compositions were prepared using polyvinyl alcohol (MowiolTM 40-88 supplied by Harlow Chemical Company Ltd.) as a 10% by weight stock solution in de-ionised water, alumina pigment dispersion in water (40% solids by weight, PG003, Cabot Chemical Co.), PHMG hydrochloride (25% by weight aqueous solution), prepared as in Stage 1 above, and PEI (LupasolTM FG supplied by BASF).
• polyvinyl alcohol MovTM 40-88 supplied by Harlow Chemical Company Ltd.
• alumina pigment dispersion in water 40% solids by weight, PG003, Cabot Chemical Co.
• PHMG hydrochloride 5% by weight aqueous solution
• the recording materials from Stage 3 were then inkjet printed using a Canon BJC8200 colour ink-jet printer using the standard ink-set supplied by Canon for this printer i.e. cyan, magenta, yellow and black ink.
• the prints were made in the form of a grid consisting of 2 mm parallel lines separated by unprinted areas of 7 mm.
• PMG's were prepared by the general method of Example 1 Stage1 except that in place of 1,6-hexamethylenediamine there was used the linking amine shown in Table A below in an equimolar amount to guanidine hydrochloride to give the desired PMG.
• Hydrochloride salts were converted to the corresponding acetate, phosphate and propionate salts using the general methods described above for PMG 2, 3, 8, 15 and 22.
• Further media compositions according to the invention may be prepared by preparing the known media described in Table B, column 2 and including the PMG's shown in table A. In column 3 of Table B the PMG and amount used (shown in brackets; parts by weight relative to 100 parts by weight of the composition) is shown.
• Example 2 PMG 6 (8) 4 Example 3 PMG 7 (11) 5 Example 4 PMG 8 (5) 6 Example 5 PMG 9 (15) 7 Example 6 PMG 10 (3) 8 Example 7 PMG 11 (20) 9 Example 8 PMG 12 (7) 10 Example 9 PMG 13 (4) US5985076 11 Example 1 PMG 14 (5) 12 Example 4 PMG 15 (10) US5104730 13 Example 1 PMG 16 (5) 14 Example 2 PMG 17 (10) 15 Example 3 PMG 18 (3) 16 Example 4 PMG 19 (15) 17 Example 5 PMG 20 (7) 18 Example 6 PMG 21 (20) 19 Example 7 PMG 22 (6) 20 Example 8 PMG 23 (12) EP0696516 21 Example 1 PMG 1 (15) 22 Example 2 PMG 6 (3) 23 Example 3 PMG 7 (5) EP0705710 24 Example 1 PMG 1 (10) 25 Example 2 PMG 15 (5) 26 Example 3 PMG 22 (7) 27 Example 4 PMG 9 (12)

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Textile Engineering (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Organic Chemistry (AREA)
• Life Sciences & Earth Sciences (AREA)
• Polymers & Plastics (AREA)
• Medicinal Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Materials Engineering (AREA)
• Wood Science & Technology (AREA)
• Ink Jet Recording Methods And Recording Media Thereof (AREA)
• Inks, Pencil-Leads, Or Crayons (AREA)
• Ink Jet (AREA)
• Paints Or Removers (AREA)
• Particle Formation And Scattering Control In Inkjet Printers (AREA)

Applications Claiming Priority (5)

Publications (1)

Family

ID=26245393

Family Applications (2)

Family Applications After (1)

Country Status (8)

Cited By (7)

Families Citing this family (19)

Citations (16)

Family Cites Families (14)

• 2001
  • 2001-12-06 DE DE60109055T patent/DE60109055T2/de not_active Expired - Lifetime
  • 2001-12-06 JP JP2002547732A patent/JP3947467B2/ja not_active Expired - Fee Related
  • 2001-12-06 EP EP01999483A patent/EP1341674B1/en not_active Expired - Lifetime
  • 2001-12-06 AU AU2002222130A patent/AU2002222130A1/en not_active Abandoned
  • 2001-12-06 US US10/433,504 patent/US20040058202A1/en not_active Abandoned
  • 2001-12-06 JP JP2002547731A patent/JP2004522615A/ja active Pending
  • 2001-12-06 AT AT01999482T patent/ATE272502T1/de not_active IP Right Cessation
  • 2001-12-06 EP EP01999482A patent/EP1341673B1/en not_active Expired - Lifetime
  • 2001-12-06 AT AT01999483T patent/ATE289548T1/de not_active IP Right Cessation
  • 2001-12-06 DE DE60104718T patent/DE60104718T2/de not_active Expired - Fee Related
  • 2001-12-06 US US10/433,566 patent/US6932466B2/en not_active Expired - Fee Related
  • 2001-12-06 WO PCT/GB2001/005393 patent/WO2002045971A1/en not_active Ceased
  • 2001-12-06 WO PCT/GB2001/005381 patent/WO2002045970A1/en not_active Ceased
  • 2001-12-06 AU AU2002252799A patent/AU2002252799A1/en not_active Abandoned
  • 2001-12-07 TW TW090130387A patent/TW588098B/zh not_active IP Right Cessation