Classifications

• • C—CHEMISTRY; METALLURGY
  • C21—METALLURGY OF IRON
  • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
  • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
  • C21D9/08—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for tubular bodies or pipes
  • C21D9/085—Cooling or quenching
• • C—CHEMISTRY; METALLURGY
  • C21—METALLURGY OF IRON
  • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
  • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
  • C21D9/38—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for roll bodies
• • C—CHEMISTRY; METALLURGY
  • C21—METALLURGY OF IRON
  • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
  • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
  • C21D1/18—Hardening; Quenching with or without subsequent tempering
• • C—CHEMISTRY; METALLURGY
  • C21—METALLURGY OF IRON
  • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
  • C21D2221/00—Treating localised areas of an article
  • C21D2221/10—Differential treatment of inner with respect to outer regions, e.g. core and periphery, respectively
• • C—CHEMISTRY; METALLURGY
  • C21—METALLURGY OF IRON
  • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
  • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
  • C21D9/08—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for tubular bodies or pipes
  • C21D9/14—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for tubular bodies or pipes wear-resistant or pressure-resistant pipes

Definitions

• the present invention relates to a method for making a roll shell and, more particularly, the invention relates to a method for making a roll shell of a heatable roll, i.e. a so-called thermo roll, which roll operates in practice as heated to a high temperature.
• a heatable roll i.e. a so-called thermo roll
• the invention relates to a method for making a roll shell of a roll used in the manufacture or further processing of paper and/or board, in which method a shell blank of the roll shell is made of steel and the shell blank is subjected to heat treatments comprising heating for hardening, quenching and tempering treatments.
• a long nip calender is generally meant a calender in which a nip is formed between a heatable steel roll and a belt.
• the nip pressure in the long nip calender can be regulated in the cross direction of the machine, i.e. in the CD direction, whereby, for example, the thickness of paper can be profiled.
• the long nip calender can be formed of a belt calender in which a belt is passed, while guided by auxiliary rolls, around one nip roll serving as a backing roll for a thermo roll.
• the long nip is formed between the thermo roll and said nip roll loading the belt.
• the most common long nip calender is a shoe calender in which the belt is arranged to run around a stationary support structure and in which the belt is loaded against a thermo roll by means of a loading shoe which is located inside the loop of the belt and supported on the support structure.
• the long nip is formed between the thermo roll and the shoe loading the belt.
• the loading shoe of the shoe calender determines the length of the nip.
• the length of the nip is typically in a range of 50-70 mm, i.e. the dwell time of the web in the nip is considerably below 10 ms.
• the surface temperature of the thermo roll serving as the backing roll of the shoe roll is in a range of 70-300° C., and the maximum pressure of the nip is in a range of 5-10 MPa.
• the hardness of the calender belt in the shoe calender is in a range of 70-100 ShA. Longer nips of about 270 mm have been used in presses that are based on a shoe roll.
• the method of making a roll according to the invention is not suitable for use in making rolls which are used in long nip calenders according to the state of the art.
• the aim of the present invention is to provide a novel method for making a roll shell, which method allows drawbacks and problems associated with the state of the art to be avoided or at least substantially reduced.
• the invention is mainly characterized in that in heat treatment, quenching is carried out such that hardening takes place in a directed manner from the outer surface of the roll shell inwards.
• a tubular shell of a thermo roll is made of an alloy steel, for example, of a quenching and tempering steel such that a wrought steel blank is first made which is heat-treated after that in a suitable manner in order to achieve desired properties.
• the heat treatment is carried out in a manner in which formation and decomposition of austenite occurs.
• the aim of the heat treatment is to provide the roll shell with a hard and wear-resistant surface so that the roll is suitable as such for use, for example, as a heatable roll in a calender.
• the surface produced and the basic structure of the material of the roll shall be such as to be suitable for being coated and/or uncoated.
• the properties of the material of the roll after heat treatment shall be such that in the roll shell there are no harmful stresses, which might cause the roll to break as a result of abrupt temperature variations.
• the roll shell according to the invention is manufactured of a well-hardening steel, for example, of a quenching and tempering alloy steel and, as one very usable grade, 34NiCrMo 6 steel is suitable for manufacture.
• the desired properties are attained such that, when the shell blank (steel blank) has been made, it is heat-treated such that the blank is subjected to heating for hardening to a high temperature above the temperature of formation of austenite, to a range of about 820-920° C.
• the quenching of the blank is performed after that in order to harden the blank, i.e. to form martensite in the structure.
• the quenching is carried out into a medium, for example, in a basin.
• the medium can be a liquid, for example, water or a liquid mixture, a gas mixture or a combination of a liquid and a gas mixture.
• the quenching can also be carried out by a fluidized bed method. It is essential that before quenching the ends of the shell blank are closed, or water or another quenching medium is prevented by some other means from getting into the interior of the blank, to the inner surface of the blank. This provides the benefit that in connection with quenching, hardening, i.e. formation of martensite begins only from the outer surface of the shell blank, from which cooling proceeds in a directed manner in the material inwards. Consequently, in the invention, the inner parts of the roll material are not hardened, as a rule, completely at any rate.
• the wear resistance of the roll material is improved. Tempering and relieving of residual stresses can be carried out after quenching.
• the roll shell is made metallurgically very stable. If the invention is intended particularly for the manufacture of a thermo roll shell, the shell shall be additionally provided with perforations for circulation of a heating medium. These holes or axial bores can be formed in the roll shell either before hardening or after hardening.
• the change of the microstructure of the material from a martensitic structure to a bainitic or a bainitic-martensitic or a bainitic-ferritic structure or to combinations of them occurs steplessly.
• This enables neutral or compression stress to be formed advantageously in the outer surface of the shell from which cooling begins, because with the progress of cooling the increase in the volume of material becomes smaller in the direction from the surface towards the interior. Since a neutral stress state or compression stress is created in the outer surface, the shell is not prone to damage or breakage even when abrupt variations of temperature occur in a finished roll which is in use. Such variations are possible if, for example, a liquid, e.g. water, is passed to a hot roll surface. If tensile stress remained in the surface, rapid cooling of a hot roll might cause the roll to break. The formation of tensile stress in the surface of the roll is prevented by means of the invention.
• the melting of steel takes place in an electric arc furnace (EAF) and the alloying proper as well as the setting of temperature take place in a holding furnace (LF), which is provided with electromagnetic stirring. Casting is carried out by up-running casting into an ingot mould. When the casting has solidified and cooled to about 600 ° C., it is moved to a forge, into a heating furnace in which it is heated to a temperature of about 1200-1285° C. at which forging is started and which is the temperature of the furnace.
• EAF electric arc furnace
• LF holding furnace
• the roll shell (tube) is made out of the casting by forging as a free forging.
• a sturdy hydraulic press is employed in forging, which makes it possible to use sturdy tools, by means of which the low density in the middle of the casting can be compressed.
• the low density portion in the middle is cut off so as to form a blank for a centre hole to be made. Slag materials and other defects collected in the casting are removed from the cast mass in connection with forging.
• the manufacture of a tubular forging takes place by pressing on a mandrel. When forged in the manner described above, the degree of deformation of the roll tube can be made uniformly good.
• heat treatments are carried out such that there is first cooling in the air. This is immediately followed by normalizing to 820-920° C., from which cooling takes place freely into the air. Immediately after that, soft annealing is carried out at about 630-700° C., which is followed by cooling to room temperature.
• the thus heat-treated steel is fine-grained, soft annealed for a quenching and tempering treatment.
• the blank Since the surface of the blank must become clean, the blank is subjected to rough machining before it is quenched and tempered to a desired strength/hardness level. In that connection, soft annealing is of advantage because normally a large amount of material has to be removed. Quenching and tempering, i.e. heating to the austenite range and tempering after hardening are carried out in a furnace. The quenching can be carried out into a liquid basin, for example, into an oil basin or water basin, or quenching can be carried out as air quenching. Since the strength level requirements of the piece are high, it is advantageous that the roll shell blanks are quenched into water. Tempering is carried out immediately after quenching at a temperature of about 340-660° C.
• the shell shall be provided further with substantially axial peripheral bores for circulation of a heating medium in the finished roll. These peripheral bores can be made when the shell is in a quenched and tempered state.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Organic Chemistry (AREA)
• Thermal Sciences (AREA)
• Crystallography & Structural Chemistry (AREA)
• Mechanical Engineering (AREA)
• Materials Engineering (AREA)
• Metallurgy (AREA)
• Physics & Mathematics (AREA)
• Heat Treatment Of Articles (AREA)
• Paper (AREA)
• Rolls And Other Rotary Bodies (AREA)
• Making Paper Articles (AREA)
• Perforating, Stamping-Out Or Severing By Means Other Than Cutting (AREA)
• Application Of Or Painting With Fluid Materials (AREA)
• Machines For Manufacturing Corrugated Board In Mechanical Paper-Making Processes (AREA)

Priority Applications (1)

Applications Claiming Priority (5)

Related Parent Applications (1)

Publications (1)

Family

ID=8559096

Family Applications (1)

Country Status (8)

Cited By (1)

Families Citing this family (2)

Citations (7)

Family Cites Families (5)

• 2000
  • 2000-09-15 FI FI20002045A patent/FI109720B/fi not_active IP Right Cessation
• 2001
  • 2001-09-12 EP EP01967378A patent/EP1379702B1/en not_active Expired - Lifetime
  • 2001-09-12 DE DE60112618T patent/DE60112618T2/de not_active Expired - Lifetime
  • 2001-09-12 JP JP2002529556A patent/JP2004510049A/ja active Pending
  • 2001-09-12 AT AT01967378T patent/ATE301728T1/de not_active IP Right Cessation
  • 2001-09-12 WO PCT/FI2001/000792 patent/WO2002024964A1/en active IP Right Grant
  • 2001-09-12 AU AU2001287766A patent/AU2001287766A1/en not_active Abandoned
  • 2001-12-28 US US10/034,986 patent/US20020084009A1/en not_active Abandoned