TWI827651B - 用於製造硬質發泡體的快速固化環氧系統及該發泡體用於複合材料或作為絕緣材料之用途 - Google Patents
用於製造硬質發泡體的快速固化環氧系統及該發泡體用於複合材料或作為絕緣材料之用途 Download PDFInfo
- Publication number
- TWI827651B TWI827651B TW108129224A TW108129224A TWI827651B TW I827651 B TWI827651 B TW I827651B TW 108129224 A TW108129224 A TW 108129224A TW 108129224 A TW108129224 A TW 108129224A TW I827651 B TWI827651 B TW I827651B
- Authority
- TW
- Taiwan
- Prior art keywords
- epoxy resin
- foam
- patent application
- item
- ionic liquid
- Prior art date
Abstract
本發明係關於一種用於製造硬質環氧發泡體之新方法。此外，本發明還關於材料，尤其是用於進行此方法的新穎雙組分(two-component)環氧系統。
此新方法的特徵在於將環氧樹脂與發泡劑混合，尤其是與囊封發泡劑(encapsulated blowing agent)混合，然後與離子液體混合。令人驚訝的是，該反應(包括發泡)在很短的時間(如僅在2至3分鐘)後在室溫下開始。
綜上所述，本發明包含一種雙組分原地發泡(foam-in-place)結構材料及一種用於製造硬質環氧發泡體之方法。
Description
本發明係關於一種用於製造硬質環氧發泡體之新方法。此外，本發明還關於材料，尤其是用於進行此方法的新穎雙組分(two-component)環氧系統。
此新方法的特徵在於將環氧樹脂與發泡劑混合，尤其是與囊封發泡劑(encapsulated blowing agent)混合，然後與離子液體混合。令人驚訝的是，該反應(包括發泡)在很短的時間(如僅在2至3分鐘)後在室溫下開始。
綜上所述，本發明包含一種雙組分原地發泡(foam-in-place)結構材料及一種用於製造硬質環氧發泡體之方法。
除非上下文中有任何明顯不同，否則用語「複合系統」、「複合材料(composite material)」及「複合材料(composite)」在下文中同義地使用。
環氧樹脂系統以彼等的優異黏著性、耐化學性和耐熱性、非常好的機械性質、及良好的電絕緣性質而為人所熟知。
已發現固化環氧樹脂系統具有廣泛的應用，範圍從黏著劑、複合材料和塗料到建築及地板產品。
因此，黏著劑通常是基於雙組分環氧系統。
環氧複合材料常是用碳纖維和玻璃纖維強化所製成。
塗料應用的實例是用於金屬表面的保護性塗料。
在大多數應用中，環氧樹脂系統是由兩種組分組成，該兩種組分可彼此進行化學反應並且是在混合固化的環氧樹脂之後形成，該固化的環氧樹脂是堅硬的硬塑性(duroplastic)材料。此系統的第一組分是環氧樹脂，其包含環氧基團，且第二組分是固化劑，常稱為硬化劑。固化劑包括對這些環氧基團具有反應性的化合物，諸如胺、羧酸或硫醇。關於更多細節請參見H. Lee and K. Neville “Handbook of Epoxy Resins” McGraw Hill, New York, 1967, 第5-1頁至第5-24頁。固化或交聯方法是環氧樹脂中的環氧基團與固化劑中的反應性基團之化學反應。藉由將固化劑化學添加到環氧樹脂中，固化可將具有相對低分子量的環氧樹脂轉化成相對高分子量或甚至是交聯的材料。另外，固化劑可有助於固化的環氧材料之性質。
環境溫度下的快速固化及/或冷固化環氧系統在許多應用中是非常有用的，如上述討論的這些或其他應用，如水性組成物。當在環境溫度下固化時，改質胺(如曼尼希鹼(Mannich base))、三級胺或其鹽、(烷基)酚或路易士酸常用於這些應用中。快速環境固化環氧系統的另一個實例是含有促進的聚硫醇。
可使用環氧固化系統的另一個技術領域是環氧發泡體，該等環氧發泡體在技術上愈來愈重要。這些發泡體特別是用於如固體浮力材料、運動(如在滑雪板、網球布或輕型自行車中)、汽車和建築等應用中。這些硬質發泡體在對於機械穩定性有很高的要求而且價格比例如PMI發泡體(其具有較佳的耐熱性)更低的應用中可以是特別有用的。
EP 0 291 455描述一種固化的發泡體，其在120與180℃的溫度之間曝露於熱後具有高度封閉孔型結構(closed cellular structure)。該混合物含有環氧樹脂或者環氧樹脂、酚醛清漆(固化劑)、固化促進劑、化學發泡劑(其在100℃以上的溫度下分裂出氮氣)、及發泡體改質劑的混合物。
CN 2017/11268551描述發泡體環氧樹脂產物作為固體浮力材料之應用。它包含液體環氧樹脂、反應性稀釋劑、多胺固化劑、酸酐固化劑或聚醯胺固化劑、催化劑(如三級胺或咪唑)、中空玻璃微球、聚合物微球及其他組分(如偶合劑)。將該系統固化並在模具中在80至120℃的溫度下發泡。最終的固體浮力材料之密度為0.26至0.32 g/cm3
。
US 2006/0188726描述了基於環氧樹脂的膨脹性可熱固化組成物之設計，該組成物展現出由至少一種液體環氧樹脂、一種固體環氧樹脂、一種發泡劑、一種固化劑及 一種含雲母的填料所組成之混合物的高度膨脹。需要將組成物加熱到60℃與110℃之間、較佳地在70℃至90℃的溫度下，然後注入至模具中。固化的硬質發泡體之密度是在0.47與0.64 g/cm3
之間。
所有這些揭露皆描述了環氧系統，其在外部加熱下發泡。這導致了數個缺點。特別是當加熱更大的體積時，樹脂內的溫度分佈顯示出梯度。這或多或少導致不均勻的發泡體。可能還必須使用相當高的溫度來確保快速發泡。這甚至加劇了溫度梯度，並且亦可能導致發泡體結構的表面或內部區域損壞，特別是在溫度最高的區域。此外，額外加熱的成本高且費時。需要額外的時間來冷卻最終的發泡體物件，而發泡體物件本身就是絕熱體。
US 2002/0187305描述製造用於中空結構(諸如汽車腔體)的原地發泡結構強化之發泡產物的方法、材料及產物。這種雙組分系統，其中一種組分是由環氧樹脂、具有填充有溶劑核的熱塑性殼之發泡劑、及觸變填料所組成。第二種組分是胺及觸變填料以及包含填充有溶劑核的熱塑性殼之任選的粒子之混合物。當組合時，在環氧組分與胺組分之間產生放熱反應。在一個實施例中，由放熱反應產生的熱量使粒子的熱塑性殼軟化，並且粒子核中的溶劑可膨脹並用作為發泡劑。因此，組成物至少部分地同時固化及發泡，而無需添加任何外部熱量。最終產物的所得密度和發泡時間並未揭示。然而，從程序的角度來看，此方法需要很長的時間來發泡，尤其對產能效率(throughput efficiency)非常不利。
US 2005/0119372描述與US 2002/0187305的揭露內容類似的方法、材料及產物。在此使用哌𠯤及醯胺基胺(amidoamine)的混合物作為胺組分。
在完全不同的技術領域中，WO 2018/000125揭示離子液體在室溫下用於固化環氧樹脂之用途。這項新技術是用於製造黏著劑、塗料、密封劑、複合材料或類似物。對於製造環氧發泡體的影響既沒有討論也沒有任何建議。因為此系統具有非常高的反應性，故認為使含有離子液體的組成物發泡會得到硬質環氧發泡體，其可能會受到較高熱量的影響。由於溫度較高，可預期該程序會更快一些，但亦可預期發泡體可能是不均勻或甚至是不穩定的。
技術問題
因此，針對所討論的先前技術背景，本發明所解決的問題是提供一種新方法，藉由該方法可製造均勻且沒有任何結構破壞(尤其是在發泡體表面上)的環氧發泡體。
本發明所解決的一個具體問題是提供一種方法，其中此方法可非常快速地進行而不需任何過長的冷卻時間。
更詳細地，本發明所解決的問題是提供用於製造環氧發泡體的發泡程序，其中在不添加任何外部熱量的情況下開始發泡並處理。
此外，獨立於表示為問題的個別實施例，可藉由新方法來實現用於發泡的快速循環時間，例如低至小於10分鐘。
此外，獨立於表示為問題的個別實施例，與現有技術中已知的環氧發泡體相比，亦可藉由新方法使環氧發泡體具有相對較低的密度。
再者，本發明所解決的另一個問題是提供一種可用於此方法且在發泡後產生機械上非常穩定的硬質環氧發泡體之環氧樹脂系的系統。
本發明要解決的另一個問題是使該方法能夠產生原地形成的硬質環氧材料，因為調配物部分是液體。
此刻未明確討論的其他問題在下文中從先前技術、說明書、申請專利範圍或實施例中將是顯而易見的。
解決方案
藉由提供用於製造硬質環氧發泡體的新方法已解決這些問題。此新方法包含下列步驟：
a. 任選地將環氧樹脂與發泡劑混合，
a2. 任選地將包含離子液體及任選的第二固化劑之組成物A與發泡劑混合，
b. 將該環氧樹脂(其任選地包含該發泡劑)與組成物A混合以形成組成物B，及
c. 將包含該環氧樹脂、該發泡劑、該離子液體及任選的至少一種其他固化劑的組成物B發泡，藉此不需要額外加熱。
因此，尤佳地，該發泡劑是囊封發泡劑。
尤佳地進行方法步驟a而非a2。
有數個實施例來進行此新方法。在一個較佳的變異方法中，步驟a.及b.同時進行。
在替代性實施例中，方法步驟b.是在方法步驟a.之後進行。在此，若將發泡劑、離子液體及任選的其他固化劑作為一種混合物混合到環氧樹脂中則是尤佳的。
對於方法步驟c.，在模具中進行此方法步驟尤其是非常有用的實施例。
尤其令人驚訝的是，使含有離子液體的組成物發泡的方法步驟是非常快的，並且在小於10秒的時間內完成，有時甚至比5秒的時間短。與此相比，如於US 2002/0187305中所述，在沒有離子液體的情況下對相應的組成物進行發泡至少需要25秒。考慮到含有離子液體的環氧樹脂之放熱性固化應該更快，這種額外能量的影響只能解釋促進發泡的程度有限，可能需要15至20秒。因此，相關的較短發泡時間只能藉由離子液體對發泡劑或發泡方法本身的額外影響來解釋。
亦令人非常驚訝地發現，在對應於本發明的方法中，離子液體不僅在作為環氧樹脂固化劑方面顯示出非常好的性能，尤其是在作為快速固化劑或冷固化劑方面亦同。
當離子液體是由聚伸烷基多胺(以下簡稱為多胺)與有機酸反應形成的室溫離子液體(room temperature ionic liquid，RTIL)而時，藉由進行根據本發明的方法可獲得特別好的結果。
在對應於本發明的方法中使用的「室溫離子液體」(RTIL)鹽包括其中離子配位差的鹽。這使得這些化合物在大於約15℃的溫度下(尤其是在室溫下)處於穩定的液態。
在本發明之非常佳的實施例中，有機酸之pKa
小於6，且多胺具有下式的結構。
在此式中，x、y及z較佳地是2及/或3的整數，且m及n是1至3的整數。進一步較佳地，R1
、R2
及R3
彼此獨立地選自氫、包含1至12個C原子的直鏈或支鏈烷基、苄基衍生物、包含1至12個C原子及1至6個O原子的羥基烷基或醚基。此外，必須注意的是，兩個基團R1
、R2
及R3
中之各者可彼此不同，其意指例如兩個胺原子之間的序列可具有類似的結構。
尤佳的多胺是選自N,N’-雙-(3-胺基丙基)乙二胺、N,N,N’-參-(3-胺基丙基)乙二胺、三伸乙基四胺、四伸乙基五胺或其任何組合。
在尤佳的實施例中，多胺化合物是不同聚伸烷基多胺化合物的混合物。合適的不同聚伸烷基多胺化合物之實例包括但不限於N,N’-雙-(3-胺基丙基)乙二胺(Am4)和N,N,N’-參-(3-胺基丙基)乙二胺(Am5)、或Am4和三伸乙基四胺(TETA)、或Am4和四伸乙基五胺(TEPA)的組合。
所屬技術領域中具有通常知識者所熟知，通常可以錯合物混合物的形式獲得含有4或更多個氮原子的多胺。在這些錯合物混合物中。因此，這些化合物中的大多數包含相同數目的氮原子亦是典型的。這些混合物中的副產物大多稱為同類物(congener)。舉例而言，三伸乙基四胺(TETA)的錯合物混合物不僅含有線性TETA，而且還含有參-胺基乙基胺、N,N’-雙-胺基乙基哌𠯤及2-胺基乙基胺基乙基哌𠯤。
亦為所屬技術領域中具有通常知識者所熟知，多胺不僅可部分地質子化一次，還可部分地質子化兩次甚至是三次，並且以多離子的形式存在於混合物中。
包含PKa
低於6的對應有機酸較佳地是選自對甲苯磺酸(p-TSA)、三氟甲磺酸(CF3
SO3
H)、氟硫酸(FSO3
H)、柳酸、三氟乙酸(TFA)、2-乙基己酸(EHA)、四氟硼酸(HBF4
)、硫氰酸(HSCN)及其組合。
在本揭露的某些實施例中，形成反應產物的反應混合物中多胺與有機酸的莫耳比是大於0至1.8，尤其是0.1至1.8，且較佳的是在0.3與1.3之間。
離子液體鹽尤其包含在大於15℃的溫度下為穩定的液體之液體鹽，在大於15℃且至多約150℃；且在某些情況下大於15℃至多約200℃的溫度下是穩定的。關於本發明，用語「液體」描述在25℃的溫度下鹽具有約1000 cps至約300,000 cps之黏度的狀態。因此，用語「穩定的」描述在至少15℃的溫度下儲存超過1個月的時間液態鹽是穩定的(維持液態)。亦較佳的是，本發明的鹽之胺值(amine value)是在200 mg KOH/g與1600 mg KOH/g之間，特佳的是在400 mg KOH/g與900 mg KOH/g之間。
在本發明的一個任選的實施例中，最終組成物(尤其是主要組成物A的形式)可進一步含有至少一種其他固化劑，尤其是不同於前述多胺且被添加以形成離子液體的其他胺。這些其他胺亦可能具有一個以上的氮原子，但不會形成任何種類的離子液體。此外，這些胺可以是一級胺、二級胺或三級胺。亦可添加四級胺鹽或所有這些化合物的衍生物。這種其他胺的一個尤佳的實例是多官能胺。就本發明而言，多官能胺描述包含三或更多個活性胺氫鍵的化合物。
這些其他胺的實例包括但不限於聚伸烷基多胺(其不同於前述的聚伸烷基多胺)、環脂族胺、芳族胺、聚(環氧烷)二胺或三胺、曼尼希鹼衍生物、聚醯胺衍生物及其組合。作為具體實例之其他合適的其他胺包括但不限於作為二級胺之二乙醇胺、嗎啉及PC-23、作為三級胺之參-二甲基胺基甲基酚(可以Ancamine K54商購自Evonik Industries)、DBU及TEDA。此外，可固化環氧樹脂系組成物(尤其是組成物A)可包括這些胺或胺衍生物的組合。其他胺特別提供作為共固化劑的功能。此外，彼等可作用為增韌劑、稀釋劑及/或促進劑。另外合適的其他胺包括但不限於胺基乙基哌𠯤、異佛酮二胺(isophoronediamine, IPDA)、4,4’-亞甲基雙-(環己胺)PACM、氫化間伸茬基二胺(通常稱為1,3-BAC)、3,3’-二甲基-4,4’-二胺基二環己基甲烷(DMDC)、聚醚胺及其組合。此其他胺可例如以介於0與60重量%之間、尤其是介於10與40重量%之間的範圍存在於組成物A中。
在WO 2018/000125中可找到合適的其他胺之另外任選實例之更詳細列表。
作為前述其他胺的次佳替代方案，亦可將硫醇、一種以上的硫醇之混合物或硫醇和前述其他胺的混合物添加到環氧樹脂中，尤其是添加到組成物A中。
藉由使用離子液體和其他固化劑(尤其是其他胺，如脂族胺)的混合物，尤其有可能調整2K系統的適用期。
進一步較佳地，環氧樹脂及/或組成物A含有添加劑、穩定劑、染料、著色劑、纖維、顏料及/或填料。這些添加劑或穩定劑之特佳的實例是阻燃劑、UV穩定劑、UV吸收劑、發泡改質劑、助黏劑、觸變添加劑、流變改質劑、乳化劑或其至少兩者之混合物。所屬技術領域中具有通常知識者知道或可容易地辨識出可選擇哪些添加劑及/或穩定劑，尤其是在硬質發泡體製造或環氧樹脂的技術領域中已知者，並且對於根據本發明所使用的組成物而言哪些添加劑及/或穩定劑是最可行的 。
此外，較佳地，組成物A另外包含固化催化劑，其尤佳的是pKa
小於6的有機酸。此酸可以(但不一定要)與之前所述的有機酸相同，添加該酸以形成離子液體。殘留酸(尤其是如果過多的有機酸用於形成離子液體時)尤佳地作為其他固化催化劑。
環氧樹脂可以是脂族系、環脂族系、芳族系環氧樹脂或彼等的混合物。尤佳地，環氧樹脂平均包含多於一個環氧基團/每分子。環氧基團可以環氧丙基醚或環氧丙基酯基團的形式存在。環氧樹脂可以液態或固態來使用。
環氧樹脂例如可商購自(但不限於)雙酚A的二環氧丙基醚(DGEBA)、雙酚F或雙酚A/F(在此名稱A/F是指丙酮與甲醛的混合物，在其製備中作為反應物)的二環氧丙基醚。可商購的實例是以商品名Araldite GY 250、Araldite GY 282(兩者皆由Huntsman分銷)或D.E.R.331、D.E.R.330(兩者皆由Dow Chemicals分銷)或Epikote 828(由Hexion分銷)分銷。其他實例是苯酚酚醛清漆或甲酚酚醛清漆之二環氧丙基醚。這種環氧樹脂可以商品名EPN或ECN及Tactix R556商購自Huntsman或以D.E.N.產品系列商購自Dow Chemicals。其他實例是脂族系或環脂族系環氧樹脂。這種環氧樹脂可以商品名Epodil 741、Epodil 748、Epodil 777商購自Evonik Industries。
對於發泡劑，所屬技術領域中具有通常知識者可選擇多種潛在的有用替代品。對於特別合適的發泡劑所給(但不以任何形式限制本發明)的實例包括三級丁醇、正庚烷、MTBE、甲基乙基酮、具有一至六個碳原子的醇、水、甲二縮醛(methyal)及/或脲。
關於本發明，尤佳地是使用囊封發泡劑。這些囊封發泡劑是具有核殼結構的熱膨脹性微球。因此，殼較佳為熱塑性殼，其例如由丙烯酸類樹脂所組成，該等丙烯酸類樹脂諸如聚甲基丙烯酸甲酯、經丙烯酸改質之聚苯乙烯、聚偏二氯乙烯、苯乙烯/MMA共聚物或類似的熱塑性塑膠。囊封發泡劑之核是由諸如低分子量烴類的溶劑組成。有用的烴是例如乙烷、乙烯、丙烷、丙烯、正丁烷、異丁烷、丁烯、異丁烯、正戊烷、異戊烷、新戊烷、正己烷、庚烷及石油醚。另外的實例是氯氟烴、四烷基矽烷諸如四甲基矽烷、三甲基乙基矽烷、三甲基異丙基矽烷、及三甲基正丙基矽烷。對於核中液體之其他實例是上面所列的發泡劑。這些實例中尤佳的是異丁烷、正丁烷、正戊烷、異戊烷、正己烷、石油醚及其混合物。
對於組成物B以及如下所述之整體套組，下列更詳細的組成物是較佳的：
- 環氧樹脂的量較佳地在20與80重量%之間、尤佳地在30與70重量%之間、且甚至更佳地在40與60重量%之間。
- 離子液體的量較佳地在5與60重量%之間、尤佳地在10與50重量%之間、且甚至更佳地在15與45重量%之間。
- 發泡劑的量較佳地在0.1與40重量%之間、尤佳地在1與30重量%之間、且甚至更佳地在5與15重量%之間。
- 任選的其他胺的量較佳地至多30重量%、尤佳地在1與20重量%之間、且甚至更佳地在5與15重量%之間。
- 任選的添加劑和穩定劑的總量較佳地至多20重量%、尤佳地在0.1與15重量%之間、且甚至更佳地在1與10重量%之間。
因此，必須注意的是，組成物B不限於這些組分。還可以存在其他物質，如共黏合劑。但是這樣是不利的，因此除了以上所列的組分之外，最好不要添加更高量的其他組分。
由離子液體與環氧樹脂之間的反應所產生的熱量使囊封發泡劑的殼軟化，從而使溶劑核可膨脹。
囊封發泡劑可商購自例如但不限於Expancel
461DU20、461DU40、093 DU120、920DU40，所有均由Akzo Nobel products分銷。其他市售的實例是F-35D、F-36D、F-190D及F-78D，由Matsumoto products分銷。囊封發泡劑可以特定的核-殼材料或以數種這些微球的混合物形式提供。
組成物B中囊封發泡劑的量可以是總重量的至多40%，並且較佳地是在0.1重量%與40重量%之間。尤佳地是使用總重量的5至30%，絕佳地是總重量的10至20%。
對於方法步驟c)之發泡，下列令人驚訝的態樣亦是相關的：與現有技術相比，組成物可在不添加任何丙烯酸化學品的情況下快速固化及發泡。它在室溫下及沒有提供任何外部熱量的情況下運作良好。完全固化時間取決於組成物，從原料混合到發泡/固化方法結束需要2至7分鐘。因此，它提高了發泡及固化反應的效率，並且可節省能量。
在2K方法中將原料混合之後，由於環氧樹脂及超快固化劑反應，在短時間內釋放出熱量，直到整體溫度達到介於150與200℃之間。因此，與在室溫下用普通多胺、環脂族胺、脂族胺、聚醯胺及醯胺基胺的可膨脹環氧系統相比，該系統可達到更高的膨脹率和更低的密度(另請參見以下比較例)。這些胺中的大多數並未顯示出相同的反應行為，而且如果有的話，彼等也僅在高溫下顯示出該行為。
相較於已知的系統，最終的固化且發泡的產物沒有氣味。諸如雙酚A環氧樹脂的環氧樹脂及諸如離子液體的超快固化劑之混合物可在沒有催化劑的情況下非常快速地固化。所述系統的大部分催化劑是三級胺或酚系的三級胺，彼等具有很強的氣味。
由於反應是在室溫下進行，並且因為反應是放熱的，因此不需要其他的外部熱量之事實。結果，沒有檢測到顏色變化。那意味著材料在反應期間不會分解，相較於文獻中描述的許多已知的環氧發泡反應具有明顯的優勢。
本發明的方法還特別地具有主要優勢，即是可以非常短的循環時間來進行並因此可在大量生產中以非常好的結果使用。
非常佳的是藉由在模具中發泡的方式在模具中製造發泡體。藉由在發泡步驟中使用模具，可有利地使產物同時具有其最終形狀。此外，可使用具有冷卻罩的模具在很短時間內將最終發泡的工作物件冷卻，其亦可額外地縮短循環時間。
除了前面描述的方法之外，用於產生硬質環氧發泡體的套組亦是本發明的一部分。根據本發明，此套組包含環氧樹脂、囊封發泡劑及組分A，藉此組分A包含離子液體及任選的其他固化劑。因此，單一組分對應於以上所述。
對於此套組，尤佳地是它是由a)混合物及b)組分A組成，藉此混合物包含環氧樹脂及囊封發泡劑。
亦在本發明的替代性較佳實施例中，套組包含a)環氧樹脂，及b)囊封發泡劑與組分A之混合物。
最後(但並非最不重要)，新穎的硬質環氧發泡體之特徵在於該發泡體含有離子液體亦是本發明的一部分。
特佳地，對應的硬質環氧發泡體之密度範圍在20至550 kg/m3
內，較佳地在25至220 kg/m3
，且更佳地在50至110 kg/m3
。
本發明(尤其是在使用根據本發明的發泡體方面)可用於製造用於汽車工業、造船或航太工業、用於隔熱或隔音材料、用於建築以及用於製造運動器材如滑雪板或網球布的複合材料部件。所給的這些實例不以任何形式限制本發明。
實例
在本發明的上下文中，尤其是關於申請專利範圍、說明書及下列實例，經由微差掃描熱量法(differential
scanning calorimetry, DSC)測量玻璃轉移溫度。在本發明的上下文中，使用Perkin Elmer設備(DSC-8000, Perkin Elmer)來判定玻璃轉移溫度Tg。
詳細的DSC程序說明：
稱量樣本(精確到±1.0 mg)並在測試前用氮氣吹掃設備5分鐘。將樣本在-40℃的溫度下保持2分鐘，之後以20℃/min的加熱速率將其從-40℃加熱到200℃。在下一階段將樣本再次以20℃/min的冷卻速率從200℃冷卻到-40℃並在
-40℃下再保持2分鐘。然後將其以20℃/min的加熱速率再次從-40℃加熱到200℃。由此第二加熱循環判定最終Tg
。之後，用第二次DSC掃描確認Tg
判定的結果。這些測試條件是根據測試標準GB/T 19466.2-2004「塑料DSC測定玻璃化轉移溫度(plastics DSC determination of glass transition temperature)」。
實例1
下列實例用來說明本發明。Ancamine 2914UF是來自Evonik的超快離子液體固化劑。同時亦將脂族胺及環脂族胺用於研究(參見表1)。
方法說明1：
第一步驟是將環氧樹脂與發泡劑(囊封發泡劑)一起在室溫下用速度混合器(800 rpm)混合1分鐘以形成A部分。第二方法步驟是添加B部分(胺固化組分)並將其在室溫下用速度混合器(800 rpm)混合30秒。在室溫下混合後開始發泡及固化反應。
實例1.1：
根據所述程序將由25 g環氧樹脂及2.5 g發泡劑(
Microsphere F35D)一起組成的A部分在室溫下於速度混合器中與由12.5 g胺固化組分組成的B部分混合。發泡及固化反應在220秒後開始，並在321秒後結束。放熱反應的溫度是190℃。2K系統產生密度為0.095 g/cm3
的發泡體。
對於比較例1.2至1.6，該方法是與實例1.1(方法說明1)所述的方法相同。關於組成物的差異及反應的觀察結果列於表1中。
表1的數據顯示，基於離子液體Ancamine 2914UF的實例1.1遠比先前技術中揭示的其他胺(比較例1.2至1.6)更快地開始發泡/固化。硬質發泡體的密度是0.095 g/m3
，遠低於其他胺的密度。
實例2
對於實例2.7至2.9，根據實例1.1所述的方法產生發泡體。
表2中所列的結果顯示，來自不同供應商的熱膨脹性微球可用作離子液體調配物的發泡劑。最終發泡產物的發泡時間和密度受熱膨脹性微球發泡劑等級的影響。對於實例2.7至2.9，該方法是與實例1.1(方法說明1)相同。
實例3
對於實施例3.10至3.12，第一步驟是在室溫下用速度混合器將26.47 g環氧樹脂與0.26 g發泡劑(囊封發泡劑，
Microsphere F35D)一起混合。在第二方法步驟中，根據實例1所述的方法，將13.27 g胺固化組分離子液體添加到組成物中。在室溫下混合後開始發泡及固化反應。確切的組成物及結果列於表3中。
在表3中，可看出發泡劑濃度對最終發泡產物之密度的影響。如所預期的，密度隨著濃度的增加而降低。另一方面，發泡劑濃度對發泡時間或發泡溫度沒有明顯的影響。
實例4
方法說明2：
對於實例4.13，第一步驟是在室溫下用速度混合器(800 rpm；混合1分鐘)將25 g環氧樹脂及2.5 g囊封發泡劑混合。將混合物及固化劑分別在10℃、25℃及40℃的溫度下儲存至少1小時。第二方法步驟是將12.5 g離子液體作為胺固化組分添加到組成物中。之後將組成物在室溫下用速度混合器(800 rpm)混合30秒。如表4所示，在不同溫度下混合後開始發泡及固化反應。
表4中的這些結果表明該調配物可用於在相當寬的環境溫度範圍內發泡。因此，該系統易於在變化的條件或氣候下使用。它甚至可在僅10℃的低溫下發泡。較低的溫度只會導致更長的發泡時間及固化時間。
實例5
方法說明3：
對於實例5.15至5.19，第一步驟是在室溫下用速度混合器(800 rpm)將25 g環氧樹脂及2.5 g囊封發泡劑混合1分鐘。將所得A部分混合物分成數個樣本。將不同的樣本在23℃下儲存1天、7天、14天、21天及30天。在儲存不同期間後，將離子液體作為B部分添加到樣本中(第二方法步驟)。之後將組成物在室溫下用速度混合器(800 rpm)混合30秒。在室溫下混合後開始發泡及固化反應。結果顯示於表5。
在23℃下儲存介於1至30天的時間後，未檢測到發泡期間之發泡體密度、發泡時間及溫度的變化。對於一些樣本，在儲存期間可觀察到相分離。此相分離對發泡沒有顯著影響。
實例6
方法說明4：
在室溫下用速度混合器(800 rpm，1分鐘)將12.5 g離子液體固化劑與2.5 g囊封發泡劑混合以形成B部分。將不同的混合物樣本在23℃下分別儲存1天、7天、14天、21天、30天。在儲存環氧樹脂後，將A部分添加到單一樣本中。混合本身是在室溫下用速度混合器(800 rpm，30秒)進行。在室溫下混合後開始發泡及固化反應。結果顯示於表6。
在23℃下儲存介於1至30天的儲存時間後，未檢測到發泡期間發泡體密度、發泡時間及溫度的變化。對於一些樣本，在儲存期間可觀察到相分離，這沒有顯著影響。
實例7.1
方法說明5：
將實例1.1的樣本作為對照樣本儲存在暗色燒瓶中。將實例1.1的另一個樣本曝露在陽光下數天。
表7.1 在曝露於陽光下後的顏色穩定性測試，實例1.1
結果顯示，並未隨時間分解且顏色保持穩定。
比較例7.2
與實例1.1類似並根據程序1a，用常見固化劑TETA來製造硬質發泡體。在發泡及固化反應之後，將實例7.2的樣本作為對照樣本儲存在暗色的燒瓶中。將實例7.2的另一個樣本曝露在陽光下數天。結果顯示，發泡體會隨時間而黃化(參見表7.2)。
表7.2 在曝露於陽光下後的顏色穩定性測試，實例7.2 (TETA)
實例8.1
方法說明6：
根據本發明製造的硬質發泡體產物在發泡後冷卻到室溫後沒有氣味。在發泡和冷卻後以及在將這些樣本於封閉的玻璃瓶中儲存一天以上之後，由五個不同的人對根據實例1.1、3.10及3.12之發泡體樣本進行了潛在氣味研究。同樣地直接在樣本儲存之後，任何測試人員都沒有檢測到氣味。
比較例8.2：
與實例1.1類似並根據程序1a，用常見固化劑TETA來製造硬質發泡體。在此，氣味同樣是按照方法6進行測試。在直接發泡和冷卻後以及儲存這些樣本後，發現了明顯的氣味。從而，儲存後氣味稍微減少。
實例9.1
與實例3.11至3.12類似並根據程序1a，用離子液體固化劑來製造硬質發泡體。確切的組成物及結果列於表9.1中。表9.1中實例的抗壓強度是根據測試方法ISO844進行測試。
組成物中微球(囊封發泡劑)的量決定硬質發泡體的抗壓強度。使用的微球愈多密度愈低，但硬質發泡體的抗壓強度也愈低。因此，必須根據適當的最終應用需求來調整組成物。
Claims (18)
- 一種用於製造硬質環氧發泡體之方法，其特徵在於該方法包含下列步驟：a.將環氧樹脂與發泡劑混合，或a2.將包含離子液體及任選的第二固化劑之組成物A與發泡劑混合，及b.將任選地包含該發泡劑之該環氧樹脂與組成物A混合以形成組成物B，及c.將包含該環氧樹脂、該發泡劑、該離子液體及任選的至少一種其他固化劑的組成物B發泡，藉此不需要額外加熱。
- 根據申請專利範圍第1項之方法，其中，該發泡劑是囊封發泡劑。
- 根據申請專利範圍第1或2項之方法，其中，該離子液體是室溫離子液體，藉由多胺與有機酸反應而形成，藉此該有機酸之pKa小於6，且藉此該多胺具有下式，其中x、y及z是2及/或3的整數，m及n是1至3的整數，且R1、R2及R3彼此獨立地選自 氫、包含1至12個C原子的直鏈或支鏈烷基、苄基衍生物、包含1至12個C原子及1至6個O原子的羥基烷基或醚基，藉此該兩個基團R1、R2及R3中之各者可彼此不同。
- 根據申請專利範圍第3項之方法，其中，該有機酸是選自對甲苯磺酸、三氟甲磺酸、氟硫酸(fluorosulfuric acid)、柳酸、三氟乙酸、2-乙基己酸、四氟硼酸、硫氰酸及其組合。
- 根據申請專利範圍第3項之方法，其中，該多胺與該有機酸之間的比是在0.1與1.8之間。
- 根據申請專利範圍第3項之方法，其中，該多胺是選自N,N’-雙-(3-胺基丙基)乙二胺、N,N,N’-參-(3-胺基丙基)乙二胺、三伸乙基四胺、四伸乙基五胺或其任何組合。
- 根據申請專利範圍第1項之方法，其中，方法步驟a.及b.是同時進行。
- 根據申請專利範圍第1項之方法，其中，方法步驟b.是在方法步驟a.之後進行。
- 根據申請專利範圍第7項之方法，其中，將該發泡劑、該離子液體及任選的額外固化劑作為一種混合物混合 到該環氧樹脂中。
- 根據申請專利範圍第1項之方法，其中，方法步驟c是在模具中進行。
- 根據申請專利範圍第1項之方法，其中，環氧樹脂及/或組成物A含有添加劑、穩定劑、染料、著色劑、纖維、顏料及/或填料。
- 根據申請專利範圍第11項之方法，其中，該等添加劑或穩定劑是阻燃劑、UV穩定劑、UV吸收劑、發泡改質劑、助黏劑、觸變添加劑、流變改質劑、乳化劑或其中至少兩者之混合物。
- 根據申請專利範圍第1項之方法，其中，該第二固化劑是選自包含一級胺、二級胺、三級胺、四級胺化合物、硫醇及其組合之列表。
- 根據申請專利範圍第1至2和4至13項中任一項之方法，其中，組成物A另外包含固化催化劑。
- 一種用於製造硬質環氧發泡體之套組，其特徵在於該套組包含環氧樹脂、囊封發泡劑及組分A，藉此組分A包含離子液體及任選的額外固化劑。
- 根據申請專利範圍第15項之套組，其中，該套組包含a)該環氧樹脂與該囊封發泡劑之混合物，及b)該組分A。
- 根據申請專利範圍第15項之套組，其中，該套組包含a)該環氧樹脂，及b)該囊封發泡劑與該組分A之混合物。
- 一種硬質環氧發泡體，其特徵在於該發泡體含有離子液體。