TWI824585B - 高分子聚合膜 - Google Patents
高分子聚合膜 Download PDFInfo
- Publication number
- TWI824585B TWI824585B TW111123965A TW111123965A TWI824585B TW I824585 B TWI824585 B TW I824585B TW 111123965 A TW111123965 A TW 111123965A TW 111123965 A TW111123965 A TW 111123965A TW I824585 B TWI824585 B TW I824585B
- Authority
- TW
- Taiwan
- Prior art keywords
- content
- polymer
- moisturizing
- polymeric film
- component
- Prior art date
Abstract
一種高分子聚合膜，是由膠體組成物所製得，該膠體組成物包含水、液體多元醇、包括葡甘露聚醣、鹿角菜膠、羅望子膠、環糊精、水性陰離子聚合物及聚丙烯酸類化合物的膠體組分，及交聯劑組分。其中，以該膠體組成物的總量為100wt%計，該液體多元醇的含量範圍為3wt%至10wt%，該膠體組分的含量範圍為0.01wt%至3wt%，該交聯劑組分的含量範圍為0.5wt%至1wt%。透過使用包括葡甘露聚醣、鹿角菜膠、羅望子膠、環糊精、水性陰離子聚合物及聚丙烯酸類化合物的膠體組分，該高分子聚合膜能夠有效地提升肌膚的保濕度。
Description
本發明是有關於一種聚合膜，特別是指一種用於肌膚保濕的高分子聚合膜。
水凝膜是一種目前市面上常見用於作為肌膚保濕的保養品，現有的水凝膜主要是由包含水、多元醇、葡甘露聚醣、鹿角菜膠、氯化鉀、檸檬酸鈉及氯化鈣的組分所形成。
然而，現有的水凝膜存在有保濕效果不佳的問題，以至於使用者在使用該水凝膜後無法有效地提升肌膚的保濕度。
因此，本發明的目的，即在提供一種能夠提高肌膚保濕度的高分子聚合膜。
於是，本發明高分子聚合膜，是由膠體組成物所製得，該膠體組成物包含：
水；
液體多元醇；
膠體組分，包括葡甘露聚醣、鹿角菜膠、羅望子膠、環糊精、水性陰離子聚合物及聚丙烯酸類化合物；及
交聯劑組分；
其中，以該膠體組成物的總量為100wt%計，該液體多元醇的含量範圍為3wt%至10wt%，該膠體組分的含量範圍為0.01wt%至3wt%，該交聯劑組分的含量範圍為0.5wt%至1wt%。
本發明的功效在於：透過使用包括葡甘露聚醣、鹿角菜膠、羅望子膠、環糊精、水性陰離子聚合物及聚丙烯酸類化合物的膠體組分，使得該高分子聚合膜具有較好的保濕效果，從而能夠有效地提升肌膚的保濕度。
以下對本發明進行詳細說明。
本發明高分子聚合膜適用於肌膚的保養，且是由膠體組成物所製得。該肌膚包含但不限於臉部肌膚或手臂肌膚。該高分子聚合膜後續可被應用於製作成眼膜、唇膜或手膜等。
該膠體組成物包含水、液體多元醇、膠體組分及交聯劑組分。該膠體組分包括葡甘露聚醣、鹿角菜膠、羅望子膠、環糊精、水性陰離子聚合物及具有聚丙烯酸類化合物。其中，以該膠體組成物的總量為100wt%計，該液體多元醇的含量範圍為3wt%至10wt%，該膠體組分的含量範圍為0.01wt%至3wt%，該交聯劑組分的含量範圍為0.5wt%至1wt%。
〈液體多元醇〉
該液體多元醇能夠賦予該高分子聚合膜具有好的保濕效果，同時，還能作為防腐劑。此外，該液體多元醇還能夠作為助溶劑，以使該膠體組分能夠溶解於水中。該液體多元醇包含但不限於1,3-丁二醇、1,2-己二醇、丙三醇等。在本發明的一些實施態樣中，該液體多元醇是選自於1,3-丁二醇、1,2-己二醇、丙三醇，或上述任意的組合。在本發明中，該液體多元醇的含量小於3wt%時，該液體多元醇無法發揮助溶劑的作用，則該膠體組分無法溶解於水中；該液體多元醇的含量大於10wt%時，該高分子聚合膜的質地不佳，以至於該高分子聚合膜敷於肌膚時的感受不佳。
〈膠體組分〉
該膠體組分是用以賦予該高分子聚合膜具有較好的保濕效果，同時，還能使該高分子聚合膜兼具有好的韌性、好的回彈性及好的柔軟度。
該葡甘露聚醣能夠維持該高分子聚合膜的回彈性，以使該高分子聚合膜不會因拉扯而破損或變形，同時，還賦予該高分子聚合膜具有適當的韌性。
該鹿角菜膠能夠賦予該高分子聚合膜具有好的回彈性及適當的韌性，以使該高分子聚合膜經拉扯後不會破損或變形。
該羅望子膠能夠使該高分子聚合膜具有好的韌性及好的柔軟度，且還能使該高分子聚合膜於-15℃至50℃的環境下具有好的溫度耐受性。
該環糊精能夠賦予該高分子聚合膜具有好的保濕效果並維持該高分子聚合膜的韌性。
該水性陰離子聚合物能夠賦予該高分子聚合膜具有好的保濕效果，同時，還能夠賦予該高分子聚合膜具有好的成膜性及好的柔軟度。該水性陰離子聚合物包含但不限於聚丙烯醯胺基甲基丙烷磺酸。在本發明的一些實施態樣中，該水性陰離子聚合物為聚丙烯醯胺基甲基丙烷磺酸。
該聚丙烯酸類化合物能夠賦予該高分子聚合膜具有好的回彈性及好的柔軟度。該聚丙烯酸類化合物包含但不限於聚丙烯酸鹽。該聚丙烯酸鹽包含但不限於聚丙烯酸鈉。
在本發明中，該膠體組分的含量小於0.01wt%時，該高分子聚合膜的放水度不佳而無法提供適量的水分供肌膚吸收；該膠體組分的含量大於3wt%時，該高分子聚合膜的稠度高，以至於該高分子聚合膜敷於肌膚時具有令人感受不佳的黏膩感，此外，該高分子聚合膜也會因稠度高，導致該高分子聚合膜後續進行量產時的產率不佳。
〈交聯劑組分〉
該交聯劑組分是用以使該膠體組分中的成分進行交聯反應，以獲得具有適當的韌性及柔軟度的高分子聚合膜。該交聯劑組分包含但不限於氯化鉀、檸檬酸鈉、氯化鈣等。在本發明的一些實施態樣中，該交聯劑組分是選自於氯化鉀、檸檬酸鈉、氯化鈣，或上述任意的組合。其中，透過控制該氯化鉀及該氯化鈣的含量，該高分子聚合膜能夠具有好的韌性；透過控制該檸檬酸鈉的含量，該高分子聚合膜能夠具有好的柔軟度。
在本發明中，該交聯劑組分的含量小於0.5wt%時，該膠體組分中的成分間的交聯程度不佳，以至於該膠體組成物無法順利成膜；該交聯劑組分的含量大於1wt%時，該高分子聚合膜的柔軟度不佳而無法服貼於肌膚的表面。
〈柔韌助劑〉
在本發明中，柔韌助劑是指用來進一步調整該高分子聚合膜的韌性及柔軟度的助劑。為了賦予該高分子聚合膜具有更佳的韌性或更佳的柔軟度，在本發明的一些實施態樣中，該膠體組成物還包含柔韌助劑。該柔韌助劑包含但不限於瓜耳膠、黃原膠、結蘭膠等。在本發明的一些實施態樣中，該柔韌助劑是選自於瓜耳膠、黃原膠、結蘭膠，或上述任意的組合。在本發明的一些實施態樣中，為使該高分子聚合膜具有更佳的韌性及柔軟度，從而使該高分子聚合膜不易破損或變形，且能夠更服貼於肌膚的表面，以該膠體組成物的總量為100wt%計，該柔韌助劑的含量範圍為0.1wt%至1wt%。
該瓜耳膠又稱關華豆膠，是由印度、巴基斯坦的乾燥地帶栽培的一年生豆科植物─瓜爾的種子(即，瓜爾豆)的胚乳經乾燥、研磨、加壓、水解等處理步驟，並利用包含濃度為20vol%的乙醇的乙醇水溶液進行沉澱，接著，經由離心分離、乾燥、粉碎等步驟所製得的一種天然膠體。該瓜耳膠具有好的水溶性，且能分散於水中形成黏度高的天然膠體溶液，從而能夠被應用於化妝品、食品及個人保健品等產品，或是，製藥、石油、造紙及紡織印染等產業中，作為增稠劑、絮凝劑、浮選劑、成膜劑或上漿劑使用。在本發明中，該瓜耳膠能夠賦予該高分子聚合膜具有更佳的柔軟度。
該黃原膠又稱三仙膠、玉米糖漿或漢生膠，且為一種具有特徵性氣味的白色至微黃色粉末，且是經由野油菜黃單胞菌 (
Xanthomonas campestris)發酵而成的多醣聚合物。該黃原膠廣泛地被應用於食品、水產養殖、藥品、化妝品及保養品，於食品應用中常作為增稠劑，有助於穩定食品製品之結構，亦可改善食物、飲品入口後的口感；於藥品應用中可作為穩定、有效的賦形劑，於化妝品及保養品應用中可作為乳化穩定劑、增稠劑或懸浮劑。該化妝品及該保養品包含肌膚護理品、頭髮護理品、沐浴清潔品、定型用造型品及口腔護理品等。在本發明中，該黃原膠能夠賦予該高分子聚合膜具有更佳的韌性及更佳的柔軟度。
該結蘭膠是一種由假單胞桿菌屬的細菌(
Pseudomonas elodea)產生的高分子多醣，且依據該結蘭膠中的醯基的含量，該結蘭膠可以分為高醯基結蘭膠及低醯基結蘭膠。其中，該高醯基結蘭膠是直接經由微生物發酵所獲得的水溶性多醣，且能夠被用來製備一種具有柔軟性及彈性且黏著力強的凝膠；該低醯基結蘭膠是利用強鹼物質對該高醯基結蘭膠進行去醯化處理所獲得，且能夠被用來製備一種強度高、堅實且不具有彈性的脆性凝膠。該結蘭膠可被應用於化妝品、藥品、食品中作為增稠劑、凝膠劑或穩定劑使用。此外，當結蘭膠應用於食品中時，還能夠與其他可食用膠體一起使用，從而賦予食品具有不同的質地及口感，該食品例如果醬、果凍、飲料及優酪乳等。在本發明中，該結蘭膠能夠賦予該高分子聚合膜具有更佳的韌性。
〈保濕助劑〉
在本發明中，保濕助劑是指用來進一步調整該高分子聚合膜的保濕效果的助劑。為使該高分子聚合膜具有更佳的保濕效果，在本發明的一些實施態樣中，該膠體組成物還包含保濕助劑。該保濕助劑包含但不限於普魯蘭多醣、山梨醣醇、甘胺酸甜菜鹼等。在本發明的一些實施態樣中，該保濕助劑是選自於普魯蘭多醣、山梨醣醇、甘胺酸甜菜鹼，或上述任意的組合。在本發明的一些實施態樣中，為使該高分子聚合膜具有更佳的保濕效果及較佳的質地，以該膠體組成物的總量為100wt%計，該保濕助劑的含量範圍為0.05wt%至15wt%。
該普魯蘭多醣是由出芽短梗霉(
Aureobasidium pullulans)發酵所產生的一種胞外水溶性黏質多醣。該普魯蘭多醣具有好的水溶性、分散性、成膜性、阻氣性、可塑性、黏性及吸濕性，且無毒性，因此，該普魯蘭多醣已被廣泛地應用於化妝品中的保濕劑或增稠劑、醫藥品及保健品的膠囊、食品的品質改良劑與增稠劑，或用於防止氧化的水溶性包裝材料等。此外，該普魯蘭多醣能夠於自然界被微生物降解利用，從而不會對環境造成危害，因此，該普魯蘭多醣被譽為無公害塑料。
該山梨醣醇已被廣泛地應用於化妝品、食品、醫藥品或日用化學品(例如護髮品)中作為保濕劑、賦形劑、增稠劑、防腐劑、甜味劑、螯合劑或食品品質改良劑使用。其中，該山梨糖醇應用於化妝品作為保濕劑時，有助於保持化妝品對於肌膚水分平衡及滋潤皮膚的效果，此外，該山梨糖醇還能夠提升化妝品中的乳化劑的伸展性與潤滑性，同時，該山梨糖醇亦於化妝品中扮演防腐劑的角色，從而延長化妝品的保存時間；該山梨糖醇應用於食品時，該山梨糖醇還具有低熱量且低糖的優點，以及防止齲齒形成的功效。值得一提的是，該山梨糖醇還能夠作為生產維生素C的主要原料。
該甘胺酸甜菜鹼，又稱三甲基甘胺酸(trimethylglycine)，是在19世紀時從甜菜中發現的一種生物鹼，為最早被發現的甜菜鹼種類。一般來說，甜菜鹼是一種兼具正離子及負離子的天然兩性界面活性劑，而具有抗靜電、殺菌、易起泡、易乳化、易分散及不易受溫度影響的優點。該甘胺酸甜菜鹼常被應用於化妝品、護膚品或護髮品中。當該甘胺酸甜菜鹼應用於化妝品時，該甘胺酸甜菜鹼能夠賦予化妝品具有好的穩定性、水溶性及保濕性。當該甘胺酸甜菜鹼應用於護膚品時，該甘胺酸甜菜鹼能夠賦予該護膚品具有保濕、抗發炎、抗老化及舒緩皮膚的效果。當該甘胺酸甜菜鹼應用於護髮品時，該甘胺酸甜菜鹼能夠賦予護髮品具有軟化角質層、增加並維持角質層的水分的效果。
本發明將就以下實施例來作進一步說明，但應瞭解的是，所述實施例僅為例示說明之用，而不應被解釋為本發明實施之限制。
[實施例1] 高分子聚合膜
將92.89wt%的水、4.13wt%的液體多元醇(包括1,3-丁二醇、1,2-己二醇及丙三醇)、總含量為2.26wt%的膠體組分(包括葡甘露聚醣、鹿角菜膠、羅望子膠、環糊精、聚丙烯醯胺基甲基丙烷磺酸及聚丙烯酸鈉)、總含量為0.72wt%的交聯劑組分(包括純度大於90%的氯化鉀、純度大於90%的檸檬酸鈉及純度大於90%的無水氯化鈣)進行混合，獲得膠體組成物。
使該膠體組成物於25℃下進行第一次的交聯反應，獲得非均相混合物，該非均相混合物包括呈均勻分散且是由該膠體組分及該交聯劑組分反應所形成的聚合物。然後，將該非均相混合物隔水加熱，並在溫度大於95℃下進行第二次的交聯反應，以使該聚合物能夠完全溶解而獲得均相混合物。接著，待該均相混合物的溫度降到75℃至95℃時，將該均相混合物塗佈於一膜具並使溫度降至25℃，獲得一高分子聚合膜。
[實施例2至3] 高分子聚合膜
實施例2至3是以與實施例1類似的方法獲得高分子聚合膜，差別在於：改變膠體組成物的組成及各組成的含量，如表1所示。其中，實施例2的膠體組成物還包含總含量為0.16wt%的柔韌助劑及總含量為3.05wt%的保濕助劑，實施例3的膠體組成物還包含總含量為0.14wt%的柔韌助劑及總含量為3.1wt%的保濕助劑。在實施例2至3中，該柔韌助劑包括瓜耳膠、黃原膠及結蘭膠；該保濕助劑包括普魯蘭多醣、山梨醣醇及甘胺酸甜菜鹼。
[比較例1至2]
比較例1至2為市售的水凝膜。其中，比較例1的水凝膜包含水、山梨醣醇、甜菜鹼、丁二醇、甘油、結蘭膠、鹿角菜膠、葡甘露聚醣、檸檬酸鈉、氯化鉀及氯化鈣；比較例2的水凝膜包含水、山梨醣醇、丁二醇、甘油、鹿角菜膠、甜菜鹼、黃原膠及結蘭膠。要說明的是，市售的水凝膜的外包裝僅揭示其組成，並未揭示各組成的含量，因此，於表1中是以「O」表示添加；以「X」表示未添加。
[評價項目]
以下以實施例1的高分子聚合膜為例說明，實施例2至3及比較例1至2是以相同的方式進行。
放水度：利用一電子秤(廠商：A&D艾安得；型號：GF-300)秤取實施例1的高分子聚合膜(長度為3公分，寬度為3公分)的重量(W
0)，接著，將實施例1的高分子聚合膜放置於溫度為22℃至25℃且濕度為65%至70%的環境下，並於放置時間為15分鐘、30分鐘、60分鐘、90分鐘及120分鐘時，分別以該電子秤秤取實施例1的高分子聚合膜的重量(W
n)，進而計算出實施例1的高分子聚合膜於不同放置時間下的放水度。結果如表2所示。
放水度(g/cm
2)=(W
0-W
n)/實施例1的高分子聚合膜的面積
肌膚保濕度增加率：利用肌膚保濕度測試儀(廠商：Aram Huvis；型號：Aramo-MC)量測受試者的手臂的一區域的肌膚保濕度(M
0)，接著，將實施例1的高分子聚合膜(長度為3公分，寬度為3公分)貼覆於該區域15分鐘，然後，將該實施例1的高分子聚合膜自該區域移除，並以該肌膚保濕度測試儀量測該區域的肌膚保濕度(M
n)，進而計算出肌膚保濕度增加率。結果如表2所示。
肌膚保濕度增加率(%)=[(M
n-M
0)/M
0]×100%
表1
| 單位(wt%) | 實施例 | 比較例 | |||
| 1 | 2 | 3 | 1 | 2 | |
| 水 | 92.89 | 87.9 | 83.61 | O | O |
| 液體多元醇 | 4.13 | 6 | 10 | O | O |
| 膠體組分 | 2.26 | 2.18 | 2.32 | O | O |
| 交聯劑組分 | 0.72 | 0.71 | 0.83 | O | X |
| 柔韌助劑 | 0 | 0.16 | 0.14 | O | O |
| 保濕助劑 | 0 | 3.05 | 3.1 | O | O |
表2
| 實施例 | 比較例 | |||||
| 1 | 2 | 3 | 1 | 2 | ||
| 放水度(g/cm 2) | 15分鐘 | 0.0025 | 0.0040 | 0.0036 | 0.0014 | 0.0020 |
| 30分鐘 | 0.0048 | 0.0084 | 0.0068 | 0.0037 | 0.0027 | |
| 60分鐘 | 0.0093 | 0.0125 | 0.0102 | 0.0074 | 0.0069 | |
| 90分鐘 | 0.0141 | 0.0194 | 0.0160 | 0.0116 | 0.0094 | |
| 120分鐘 | 0.0191 | 0.0262 | 0.0220 | 0.0142 | 0.0120 | |
| 肌膚保濕度增加率(%) | 45.44 | 34.98 | 31.07 | 32.43 | 25.99 |
參閱表2，透過使用該膠體組分，實施例1至3的高分子聚合膜具有高的放水度，此表示實施例1至3的高分子聚合膜能夠有效地釋放出水分，藉此提供較適量的水分供肌膚吸收。此外，由肌膚保濕度增加率的結果可知，實施例1至3的高分子聚合膜具有31.07%至45.44%的肌膚保濕度增加率，此表示實施例1至3的高分子聚合膜確實能夠有效地提升肌膚的保濕度。
反觀比較例1至2，由於比較例1至2並未使用該膠體組分，因此，比較例1至2的水凝膜的放水度低，此表示比較例1至2的水凝膜釋放出水分的效果不佳，而無法提供較適量的水分供肌膚吸收。此外，比較例1至2的水凝膜僅有25.99%至32.43%的肌膚保濕度增加率，此表示比較例1至2的水凝膜的肌膚保濕度提升效果有限。
綜上所述，透過使用包括葡甘露聚醣、鹿角菜膠、羅望子膠、環糊精、水性陰離子聚合物及聚丙烯酸類化合物的膠體組分，本發明高分子聚合膜具有好的保濕效果，因此，該高分子聚合膜能夠有效地提升肌膚的保濕度，此外，本發明高分子聚合膜還具有好的韌性及好的柔軟度，以至於使用該高分子聚合膜時，該高分子聚合膜能夠服貼於不同部位的肌膚，且不會發生因拉扯而破損或變形的問題，故確實能達成本發明的目的。
惟以上所述者，僅為本發明的實施例而已，當不能以此限定本發明實施的範圍，凡是依本發明申請專利範圍及專利說明書內容所作的簡單的等效變化與修飾，皆仍屬本發明專利涵蓋的範圍內。
無。
Claims (7)
- 一種高分子聚合膜，是由膠體組成物所製得，該膠體組成物包含：水；液體多元醇；膠體組分，包括葡甘露聚醣、鹿角菜膠、羅望子膠、環糊精、聚丙烯醯胺基甲基丙烷磺酸及聚丙烯酸鈉；及交聯劑組分；其中，以該膠體組成物的總量為100wt%計，該液體多元醇的含量範圍為4.13wt%至10wt%，該膠體組分的含量範圍為2.18wt%至2.32wt%，該交聯劑組分的含量範圍為0.71wt%至0.83wt%。
- 如請求項1所述的高分子聚合膜，其中，該交聯劑組分是選自於氯化鉀、檸檬酸鈉、氯化鈣，或上述任意的組合。
- 如請求項1所述的高分子聚合膜，其中，該液體多元醇是選自於1,3-丁二醇、1,2-己二醇、丙三醇，或上述任意的組合。
- 如請求項1所述的高分子聚合膜，還包含柔韌助劑，且該柔韌助劑是選自於瓜耳膠、黃原膠、結蘭膠，或上述任意的組合。
- 如請求項4所述的高分子聚合膜，其中，以該膠體組成物的總量為100wt%計，該柔韌助劑的含量範圍為0.1wt%至1wt%。
- 如請求項1所述的高分子聚合膜，還包含保濕助劑，且該 保濕助劑是選自於普魯蘭多醣、山梨醣醇、甘胺酸甜菜鹼，或上述任意的組合。
- 如請求項6所述的高分子聚合膜，其中，以該膠體組成物的總量為100wt%計，該保濕助劑的含量範圍為0.05wt%至15wt%。