TWI763743B - 研磨用組成物 - Google Patents
研磨用組成物Info
- Publication number
- TWI763743B TWI763743B TW106140234A TW106140234A TWI763743B TW I763743 B TWI763743 B TW I763743B TW 106140234 A TW106140234 A TW 106140234A TW 106140234 A TW106140234 A TW 106140234A TW I763743 B TWI763743 B TW I763743B
- Authority
- TW
- Taiwan
- Prior art keywords
- less
- polishing
- weight
- polishing composition
- cellulose derivative
- Prior art date
Abstract
本發明提供一種研磨用組成物,其係包含纖維素衍生物之組成,且能有效減低研磨後之表面缺陷。本申請案提供一種研磨用組成物,其係包含磨粒、鹼性化合物及表面保護劑。上述表面保護劑包含纖維素衍生物,與乙烯基醇系分散劑。上述表面保護劑之分散性參數α未滿100。
Description
[0001] 本發明係關於研磨用組成物。本申請案係依據2016年11月22日提出申請之日本國專利申請案2016-226666號主張優先權,並將該申請案之全部內容導入於本說明書中作為參照內容。
[0002] 對於金屬或半金屬、非金屬、其之氧化物等之材料表面,實施使用含有磨粒之研磨用組成物之研磨。例如,在半導體製品之製造等所使用之矽基板之表面一般係經由精削(lapping)步驟與拋光(polishing)步驟來完成高品位之鏡面。上述拋光步驟典型上係包含預備拋光步驟與完工拋光步驟(完工研磨步驟)。作為關於在研磨矽晶圓等之半導體基板之目的上主要所使用之研磨用組成物之技術文獻,可舉出如專利文獻1、2。 [先前技術文獻] [專利文獻] [0003] [專利文獻1]日本國專利申請案公開2012-89862號公報 [專利文獻2]日本國專利申請案公開2015-124231號公報
[發明所欲解決之課題] [0004] 對於完工研磨(finish polishing)步驟所使用之研磨用組成物要求實現在研磨後霾度低且表面缺陷少之表面之性能。上述完工研磨步驟係例如可為矽晶圓等之半導體基板其他基板之完工研磨步驟。用於該用途之研磨用組成物諸多為包含磨粒及水,且在保護研磨對象物表面或提升濕潤性等之目的上更包含水溶性高分子者。其中作為泛用之水溶性高分子,可舉出如羥基乙基纖維素(HEC)。 [0005] 但,HEC所代表之纖維素衍生物由於係將天然物之纖維素作為原料,故品質容易參差不齊。因此,過往包含纖維素衍生物之組成之研磨用組成物難以精度良好地抑制可能成為表面缺陷原因之微細凝聚。專利文獻1、2雖然記載使用HEC之研磨用組成物去減低表面缺陷之技術,但即便藉由該技術,仍有無法充分對應關於在研磨後之表面品質上近年來所要求之程度的情況。 [0006] 因此,本發明之目的在於提用一種研磨用組成物,其係包含纖維素衍生物之組成,且能有效減低研磨後之表面缺陷。 [用以解決課題之手段] [0007] 由本說明書所提供之研磨用組成物包含磨粒、鹼性化合物及表面保護劑。前述表面保護劑包含纖維素衍生物,與乙烯基醇系分散劑。在此,前述表面保護劑之分散性參數α未滿100。藉由此種研磨用組成物,可活用因使用纖維素衍生物所得之優點,且可有效減低研磨後之表面缺陷。該研磨用組成物可有效減低例如被稱為無法清除光點缺陷(LPD-N,Light Point Defect Non-cleanable)之藉由研磨、洗淨、乾燥等之處理而仍無法解決之缺陷。 [0008] 前述纖維素衍生物之重量平均分子量(Mw)係可作成例如5×104
以上未滿50×104
。藉由Mw在上述範圍內之纖維素衍生物時,有可抑制分散性參數α,且適當發揮保護研磨對象物或提升濕潤性之功能的傾向。 [0009] 前述乙烯基醇系分散劑之Mw係可作成例如前述纖維素衍生物之Mw之90%以下。藉由此種構成,有使用乙烯基醇系分散劑所得之分散性參數α之減低效果更加良好受到發揮之傾向。 [0010] 前述乙烯基醇系分散劑之含量係在相對於前述纖維素衍生物100g而言,可作成例如0.1g以上80g以下。在此種組成中,可合適地發揮組合纖維素衍生物與乙烯基醇系分散劑之效果。 [0011] 前述纖維素衍生物與前述乙烯基醇系分散劑之合計含量在相對於前述磨粒100g而言,可作成例如1.5g以上20g以下。根據此種研磨用組成物,可抑制因研磨所產生之負荷而對研磨對象物所造成之新的缺陷,且可高品味地完成該研磨對象物之表面。 [0012] 前述表面保護劑可更包含氧伸烷基系(oxyalkylene)添加劑。在此種組成中,可適宜發揮因組合使用纖維素衍生物與乙烯基醇系分散劑所得之效果,且實現更加高品位之表面。 [0013] 在此揭示之研磨用組成物之一態樣中,前述氧伸烷基系添加劑可包含Mw未滿5000之氧伸烷基系添加劑OAL
。藉由使用氧伸烷基系添加劑OAL
,能更加減低研磨後之表面缺陷。 [0014] 作為在此揭示之技術中之磨粒,可較佳採用二氧化矽粒子。本發明係能在包含二氧化矽粒子作為磨粒之研磨用組成物之形態下適宜實施。 [0015] 在此揭示之研磨用組成物可使用於各種研磨對象物之研磨。其中能較佳使用於矽晶圓及其他之基板之研磨。特別係適合作為矽晶圓之完工研磨所使用之研磨用組成物。
[0016] 以下,說明本發明之適宜實施形態。尚且,本說明書中未特別敘及之事項以外之事物且係實施本發明之所必要之事物係能理解成本發明所屬技術領域具有通常知識者在根據本發明領域之先前技術而可達成之設計事項。本發明係可依據本說明書揭示之內容與本發明領域之技術常識來實施。 [0017] <磨粒> 在此揭示之研磨用組成物所包含之磨粒材質或物性並無特別限制,可因應研磨用組成物之使用目的或使用態樣等而適宜選擇。作為磨粒之例,可舉出如無機粒子、有機粒子、及有機無機複合粒子。作為無機粒子之具體例,可舉出如二氧化矽粒子、氧化鋁粒子、氧化鈰粒子、氧化鉻粒子、二氧化鈦粒子、氧化鋯粒子、氧化鎂粒子、二氧化錳粒子、氧化鋅粒子、紅殼(Bengala)粒子等之氧化物粒子;氮化矽粒子、氮化硼粒子等之氮化物粒子;碳化矽粒子、碳化硼粒子等之碳化物粒子;金剛石粒子;碳酸鈣或碳酸鋇等之碳酸鹽等。作為有機粒子之具體例,可舉出如聚甲基丙烯酸甲基(PMMA)粒子或聚(甲基)丙烯酸粒子、聚丙烯腈粒子等。此種磨粒係可單獨使用一種,亦可組合兩種以上使用。尚且,本說明書中(甲基)丙烯醯基係意指包括丙烯醯基及甲基丙烯醯基。同樣地本說明書中,(甲基)丙烯醯基係意指包括丙烯醯基及甲基丙烯醯基。 [0018] 作為上述磨粒,以無機粒子為佳,其中亦以由金屬或半金屬之氧化物所構成之粒子為佳,以二氧化矽粒子為特佳。在如後述矽晶圓等之具有由矽所構成之表面之研磨對象物之研磨,例如能使用於完工研磨之研磨用組成物中,採用二氧化矽粒子作為磨粒特別具有意義。在此揭示之技術係能在例如上述磨粒係實質上由二氧化矽粒子所構成之態樣下理想實施。在此「實質上」係意指構成磨粒之粒子之95重量%以上,較佳係98重量%以上,更佳係99重量%以上為二氧化矽粒子,且包括100重量%為二氧化矽粒子一事。 [0019] 作為二氧化矽粒子之具體例,可舉出如膠質二氧化矽、氣相二氧化矽、沉澱二氧化矽等。二氧化矽粒子係可單獨使用一種或可將兩種以上組合使用。在從研磨後可容易取得表面品位優異之研磨面之觀點,以使用膠質二氧化矽為特佳。作為膠質二氧化矽,可理想採用例如藉由離子交換法將水玻璃(矽酸Na)作為原料所製作之膠質二氧化矽,或烷氧化物法膠質二氧化矽。烷氧化物法膠質二氧化矽係指藉由烷氧基矽烷之水解縮合反應所製造之膠質二氧化矽。膠質二氧化矽係可單獨使用一種或亦可組合兩種以上使用。 [0020] 磨粒構成材料之真比重(真密度)係以1.5以上為佳,較佳為1.6以上,更佳為1.7以上。在此,磨粒構成材料之真比重係指例如由二氧化矽粒子所構成之磨粒中構成該二氧化矽粒子之二氧化矽之真比重。以下亦稱為磨粒之真比重。藉由增加磨粒之真比重,磨粒之物理性研磨能力有變高之傾向。磨粒之真比重之上限並無特別限定,典型為2.3以下,例如2.2以下。作為磨粒之真比重,可採用藉由使用乙醇作為取代液之液體取代法所得之測量值。上述磨粒係例如可為二氧化矽粒子。 [0021] 磨粒之BET徑並無特別限定,在從研磨效率等之觀點,以5nm以上為佳,較佳為10nm以上。在從取得更高研磨效果之觀點,例如在從更加良好發揮減少霾度或去除缺陷等之效果之觀點,上述BET徑例如係以15nm以上為佳,以20nm以上為較佳,亦可超過20nm。又,在從抑制磨粒對研磨對象物表面賦予之局部性壓力之觀點,磨粒之BET徑係以100nm以下為佳,較佳為50nm以下,更佳為40nm以下。在此揭示之技術在從變得容易取得更高品位之表面,例如LPD-N數少且霾度程度低之表面之觀點等,可在使用BET徑為35nm以下,較佳未滿35nm,更佳為32nm以下,例如未滿30nm之磨粒之態樣下實施。上述磨粒係例如可為二氧化矽粒子。 [0022] 尚且,本說明書中BET徑係指從藉由BET法所測量之比表面積(BET值),使用BET徑[nm]=6000/(真密度[g/cm3
]×BET值[m2
/g])之式所算出之粒子徑。例如在二氧化矽粒子之情況,可藉由BET徑[nm]=2727/BET值[m2
/g]算出BET徑。比表面積之測量係可使用例如Micromelitex公司製之表面積測量裝置,商品名「Flow Sorb II 2300」進行。 [0023] 磨粒之形狀(外形)可為球形,亦可為非球形。作為成為非球形之粒子之具體例,可舉出如花生形狀、繭型形狀、金平糖形狀、橄欖球形狀等。上述花生形狀係指即落花生之殼之形狀。可理想採用例如粒子之諸多為具有花生形狀或繭型形狀之磨粒。 [0024] 磨粒之平均長寬比,即磨粒之長徑/短徑比之平均值並非係受到特別限定者,但理論上為1.0以上,較佳為1.05以上,更佳為1.1以上。藉由增加平均長寬比,可實現更高研磨效率。又,磨粒之平均長寬比在從減少傷痕等之觀點,以3.0以下為佳,較佳為2.0以下,更佳為1.5以下。 [0025] 磨粒之形狀(外形)或平均長寬比係可藉由例如電子顯微鏡觀察來把握。作為判別平均長寬比之具體操作順序,可使用例如掃描型電子顯微鏡(SEM),對於可辨識獨立粒子之形狀之規定個數之二氧化矽粒子,描繪出外接於個別之粒子畫像之最小長方形。上述規定個數係指例如200個。且,關於針對各粒子畫像所描繪出之長方形,將其長邊之長度設為長徑之值,將短邊之長度設為短徑之值,將長徑之值除以短徑之值而得之值算出作為各磨粒之長徑/短徑比,即長寬比。藉由將上述規定個數之粒子之長寬比作成算術平均,而可求出平均長寬比。 [0026] <表面保護劑> 在此揭示之研磨用組成物含有纖維素衍生物及乙烯基醇系分散劑作為表面保護劑。上述表面保護劑係能以在以下所說明之分散性參數α未滿100之方式來構成。 [0027] (分散性參數α) 表面保護劑之分散性參數α係在以規定方法實施之吸引過濾中,從包含標準聚合物及氨且剩餘部分係由水所構成之標準液100g之過濾時間(通液時間)T0
,與包含表面保護劑及氨且剩餘部分係由水所構成之試驗液100g之過濾時間(通液時間)T1
,且藉由以下之式來算出者。 分散性參數α[%]=(T1
/T0
)×100 在此,上述標準液及上述試驗液之氨濃度皆作成0.1重量%。作為上述標準聚合物,使用重量平均分子量(Mw)為25×104
之羥基乙基纖維素(HEC)。上述標準液中之上述標準聚合物之濃度係作成0.17重量%。上述試驗液中之表面保護劑之濃度係設定成該表面保護劑所包含之纖維素衍生物之濃度會成為0.17重量%。 [0028] 上述通液時間T0
及T1
係藉由以下操作來測量。 [吸引過濾條件] 使用過濾器: 種類 膜過濾器(φ47mm,碟型) 材質 尼龍 孔徑 0.2μm 吸引壓力:0.005MPa [通液時間之測量手順] 將膜過濾器設置於吸引過濾器,在上述吸引壓力下吸引過濾去離子水100g,其後吸引過濾標準液100g。此時測量過濾標準液100g所需要之時間(通液時間)T0
。 其次,將膜過濾器交換成新品後,在上述吸引壓力下吸引過濾去離子水100g,其後吸引過濾試驗液100g。此時測量過濾試驗液100g所需要之時間(通液時間)T1
。 [0029] 藉此所求得之α係能有用作為估計上述包含表面保護劑之研磨用組成物中之纖維素衍生物之分散性程度的指標。使用α未滿100%之表面保護劑時,在研磨用組成物中能使上述表面保護劑所包含之纖維素衍生物適當地分散,且能高度抑制該纖維素衍生物所可能包含因凝聚所造之缺陷。在某些態樣中,α可為99%以下,例如可為98%以下。在使用α為96%以下之表面保護劑時,可發揮更高之效果。在此揭示之技術在α為90%以下,或85%以下,例如80%以下之態樣下仍能適宜地實施。α之下限並無特別限制,例如可為10%以上。從更加良好利用由纖維素衍生物所得之保護效果或表面濕潤性之提升效果之觀點等,α通常適當為30%以上,可為50%以上,可為60%以上,亦可為例如70%以上。α係可藉由選擇表面保護劑之構成成分之種類或分子量,該等之使用量比之設定等來進行調節。 [0030] (纖維素衍生物) 纖維素衍生物係包含β-葡萄糖單位作為主要重複單位之聚合物。作為纖維素衍生物之具體例,可舉出如羥基乙基纖維素(HEC)、羥基丙基纖維素、羥基乙基甲基纖維素、羥基丙基甲基纖維素、甲基纖維素、乙基纖維素、乙基羥基乙基纖維素、羧基甲基纖維素等。其中亦以HEC為佳。 [0031] 在此揭示之研磨用組成物中使用之纖維素衍生物之Mw並無特別限定,例如可為2×104
以上。從適宜發揮保護性或表面濕潤性等之功能之觀點,纖維素衍生物之Mw通常適當為5×104
以上,可為7×104
以上,可為10×104
以上,可為15×104
以上,亦可為例如20×104
以上。又,纖維素衍生物之Mw係可作成例如100×104
以下,從提升分散性之觀點,以70×104
以下為佳,以50×104
以下為更佳。在一種態樣中,可較佳採用Mw未滿50×104
,較佳未滿30×104
,例如28×104
以下之纖維素衍生物。 [0032] 尚且,本說明書中,作為研磨用組成物所能包含之水溶性有機物之重量平均分子量(Mw),可採用依據凝膠滲透層析(GPC)之值(水系、聚環氧乙烷換算)。 [0033] 表面保護劑中所佔之纖維素衍生物之比例並無特別限定,例如可為20重量%以上。上述比例例如可為20重量%以上未滿100重量%。從更加良好活用纖維素衍生物之使用效果之觀點,通常上述比例適當為30重量%以上,亦可為50重量%以上。在此揭示之技術係能在表面保護劑中所佔之纖維素衍生物之比例超過50重量%之態樣下適宜實施。上述纖維素衍生物之比例可為60重量%以上,可為70重量%以上,亦可為80%以上。又,表面保護劑中所佔之纖維素衍生物之比例在從活用乙烯基醇系分散劑之使用效果之觀點,通常適當作成99.9重量%以下,可作成99.5重量%以下,可作成99重量%以下,亦可作成98.5重量%以下。在一種態樣中,表面保護劑中所佔之纖維素衍生物之比例可為95重量%以下,亦可為90重量%以下。 [0034] 研磨用組成物中之纖維素衍生物之含量並非係受到特別限定者,該研磨用組成物中之磨粒每100g,可作成例如0.1g以上,亦可作成0.5g以上。從更加良好活用纖維素衍生物之使用效果之觀點,上述含量通常係適當作成1g以上,以作成2g以上為佳。在一種態樣中,上述含量可為3g以上,亦可為4g以上。在此種態樣中,能更加良好發揮使用本發明之意義。又,磨粒每100g之纖維素衍生物之含量在從研磨用組成物之過濾性或洗淨性之觀點,通常適當作成15g以下,可作成12g以下,可作成10g以下,可作成8g以下,亦可作成例如6g以下。 [0035] (乙烯基醇系分散劑) 在此揭示之表面保護劑包含乙烯基醇系分散劑。以下,有將乙烯基醇系分散劑標記為「分散劑VA」之情況。藉由組合使用纖維素衍生物與分散劑VA,可改善研磨用組成物中之纖維素衍生物之分散性,且可有效減低因使用該纖維素衍生物所造成之缺陷(例如,LPD-N)。 [0036] 作為分散劑VA,使用包含乙烯基醇單位作為其重複單位之水溶性有機物(典型為水溶性高分子)。在此,乙烯基醇單位(以下亦稱為「VA單位」)係藉由以下化學式:-CH2
-CH(OH)-;所表示之構造部分。VA單位係能藉由使例如乙酸乙烯基酯等之乙烯基酯系單體進行乙烯基聚合而成之構造之重複單位進行水解(亦稱為皂化)而生成。 [0037] 分散劑VA係可僅包含VA單位作為重複單位,亦可包含VA單及VA單位以外之重複單位(以下亦稱為「非VA單位」)。分散劑VA在包含非VA單位之態樣中,該非VA單位可為具有選自氧伸烷基、羧基、磺酸基、胺基、羥基、醯胺基、醯亞胺基、腈基、醚基、酯基、及該等鹽之至少一種構造之重複單位。分散劑VA可為包含VA單位與非VA單位之無規共聚物,亦可為嵌段共聚物或接枝共聚物。分散劑VA可為僅包含一種類非VA單位,亦可包含兩種類以上之非VA單位。 [0038] 構成分散劑VA之全重複單位之莫耳數所佔之VA單位莫耳數之比例例如可為5%以上,可為10%以上,可為20%以上,亦可為30%以上。並非係受到特別限定者,但在某些態樣中,上述VA單位之莫耳數之比例可為50%以上,可為65%以上,可為75%以上,可為80%以上,可為90%以上,亦可為例如95%以上或98%以上。構成分散劑VA之重複單位可為實質上100%為VA單位。在此「實質上100%」係指至少不故意使分散劑VA含有非VA單位。在其他之某些態樣中,構成分散劑VA之全重複單位之莫耳數所佔之VA單位莫耳數之比例例如可為95%以下,可為90%以下,可為80%以下,亦可為70%以下。 [0039] 分散劑VA中之VA單位之含量在重量基準下,例如可為5重量%以上,可為10重量%以上,可為20重量%以上,亦可為30重量%以上。並非係受到特別限定者,在某些態樣中,上述VA單位之含量可為50重量%以上或超過50重量%,可為70重量%以上,可為80重量%以上,可為90重量%以上,亦可為95重量%以上或98重量%以上。構成分散劑VA之重複單位實質上100重量%可為VA單位。在此「實質上100重量%」係指至少不故意使構成分散劑VA之重複單位含有非VA單位。在其他某些態樣中,分散劑VA中之VA單位之含量例如可為95重量%以下,可為90重量%以下,可為80重量%以下,可為70重量%以下。 [0040] 分散劑VA係可在同一分子內包含VA單位之含量相異之複數聚合物鏈。在此,聚合物鏈係指構成一分子聚合物之一部分之部分(鏈段)。例如,分散劑VA係可在同一分子內包含VA單位之含量高於50重量%之聚合物鏈A,與VA單位之含量低於50重量%之聚合物鏈B。VA單位之含量低於50重量%之聚合物鏈B係指,即非VA單位之含量多於50重量%之聚合物鏈B。 [0041] 聚合物鏈A可緊包含VA單位作為重複單位,亦可包含VA單位及非VA單位。聚合物鏈A中之VA單位之含量可為60重量%以上,可為70重量%以上,可為80重量%以上,亦可為90重量%以上。在某些態樣中,聚合物鏈A中之VA單位之含量可為95重量%以上,亦可為98重量%以上。構成聚合物鏈A之重複單位之實質上100重量%可為VA單位。 [0042] 聚合物鏈B可僅包含非VA單位作為重複單位,亦可包含非VA單位及VA單位。聚合物鏈B中之非VA單位之含量可為60重量%以上,可為70重量%以上,可為80重量%以上,亦可為90重量%以上。在某些態樣中,聚合物鏈B中之非VA單位之含量可為95重量%以上,亦可為98重量%以上。構成聚合物鏈B之重複單位之實質上100重量%可為非VA單位。 [0043] 作為在同一分子中包含聚合物鏈A與聚合物鏈B之分散劑VA之例,可舉出如包含此等聚合物鏈之嵌段共聚物或接枝共聚物。上述接枝共聚物可為在聚合物鏈A(主鏈)接枝聚合物鏈B(側鏈)而成之構造之接枝共聚物,亦可為在聚合物鏈B(主鏈)接枝聚合物鏈A(側鏈)而成之構造之接枝共聚物。在一種態樣中,可使用聚合物鏈A上接枝聚合物鏈B而成之構造之分散劑VA。 [0044] 作為聚合物鏈B之例,可舉出如將源自N-乙烯基型單體之重複單位作為主重複單位之聚合物鏈,將源自N-(甲基)丙烯醯基型單體脂重複單位作為主重複單位之聚合物鏈。尚且,本說明書中主重複單位在未特別註記之情況係指包含超過50重量%之重複單位。 [0045] 作為聚合物鏈B之一適宜例,可舉出如將N-乙烯基型單體作為主重複單位之聚合物鏈,即N-乙烯基系聚合物鏈。N-乙烯基系聚合物鏈中之源自N-乙烯基型單體之重複單位含量典型為超過50重量%,可為70重量%以上,可為85重量%以上,亦可為95重量%以上。聚合物鏈B可為實質上全部為源自N-乙烯基型單體脂重複單位。 [0046] N-乙烯基型單體之例係包括具有含氮雜環之單體及N-乙烯基鏈狀醯胺。上述雜環例如可為內醯胺環。作為N-乙烯基內醯胺型單體之具體例,可舉出如N-乙烯基吡咯啶酮、N-乙烯基哌啶酮、N-乙烯基嗎啉基、N-乙烯基己內醯胺、N-乙烯基-1,3-噁嗪-2-酮、N-乙烯基-3,5-嗎啉二酮等。作為N-乙烯基鏈狀醯胺之具體例,可舉出如N-乙烯基乙醯胺、N-乙烯基丙酸醯胺、N-乙烯基丁酸醯胺等。聚合物鏈B例如可為其重複單位之超過50重量%,例如70重量%以上或85重量%以上或95重量%以上為N-乙烯基吡咯啶酮單位之N-乙烯基系聚合物鏈。構成聚合物鏈B之重複單位之實質上全部可為N-乙烯基吡咯啶酮單位。 [0047] 作為聚合物鏈B之其他例,可舉出如將源自N-(甲基)丙烯醯基型單體之重複單位作為主重複單位之聚合物鏈,即N-(甲基)丙烯醯基系聚合物鏈。N-(甲基)丙烯醯基系聚合物鏈中之源自N-(甲基)丙烯醯基型單體之重複單位含量典型為超過50重量%,可為70重量%以上,可為85重量%以上,亦可為95重量%以上。聚合物鏈B之實質上全部可為源自N-(甲基)丙烯醯基型單體之重複單位。 [0048] N-(甲基)丙烯醯基型單體之例係包括具有N-(甲基)丙烯醯基之鏈狀醯胺及具有N-(甲基)丙烯醯基之環狀醯胺。作為具有N-(甲基)丙烯醯基之鏈狀醯胺之例,可舉出如(甲基)丙烯醯胺;N-甲基(甲基)丙烯醯胺、N-乙基(甲基)丙烯醯胺、N-丙基(甲基)丙烯醯胺、N-異丙基(甲基)丙烯醯胺、N-n-丁基(甲基)丙烯醯胺等之N-烷基(甲基)丙烯醯胺;N,N-二甲基(甲基)丙烯醯胺、N,N-二乙基(甲基)丙烯醯胺、N,N-二丙基(甲基)丙烯醯胺、N,N-二異丙基(甲基)丙烯醯胺、N,N-二(n-丁基)(甲基)丙烯醯胺等之N,N-二烷基(甲基)丙烯醯胺等。作為具有N-(甲基)丙烯醯基之環狀醯胺之例,可舉出如N-(甲基)丙烯醯基嗎啉、N-(甲基)丙烯醯基吡咯啶等。 [0049] 作為聚合物鏈B之其他例,可舉出如包含氧伸烷基單位作為主重複單位之聚合物鏈,即氧伸烷基系聚合物鏈。氧伸烷基系聚合物鏈中之氧伸烷基單位之含量典型為超過50重量%,可為70重量%以上,可為85重量%以上,亦可為95重量%以上。聚合物鏈B所包含之重複單位實質上全部可為氧伸烷基單位。 [0050] 作為氧伸烷基(oxyalkylene)單位之例,可舉出如氧伸乙基單位、氧伸丙基單位、氧伸丁基單位等。此種氧伸烷基單位可為分別源自對應之環氧烷之重複單位。氧伸烷基系鏈段所含之氧伸烷基單位可為單一種類,亦可為兩種類以上。例如,可為包含組合氧伸乙基單位與氧伸丙基單位之氧伸烷基系鏈段。在包含二種類以上之氧伸烷基單位之氧伸烷基系聚合物鏈中,該等之氧伸烷基單位可為所對應之環氧烷之環氧烷之無規共聚物,亦可為嵌段共聚物或接枝共聚物。 [0051] 分散劑VA之重量平均分子量(Mw)並無特別限定,例如可為2000以上,可為大於5000。從可容易適當地發揮分散性提升效果之觀點,分散劑VA之Mw可為7000以上,可為1×104
以上,可為1.2×104
以上。在一種態樣中,可較佳採用Mw為2×104
以上,例如3×104
以上或5×104
以上或7×104
以上之分散劑VA。又,分散劑VA之Mw係通常適當為100×104
以下,例如可為50×104
以下,可為30×104
以下,亦可為20×104
以下。從取較高分散性提升效果之觀點,在一種態樣中,可較佳採用Mw為17×104
以下,例如15×104
以下之分散劑VA。 [0052] 在此揭示之表面保護劑之與纖維素衍生物Mw之關係並非係受到特別限定者,係能較佳在包含較低Mw之分散劑VA之態樣下實施。依據該態樣時,有變得容易適宜發揮使用纖維素衍生物所得之優點的傾向。在一種態樣中,分散劑VA之Mw係可作成纖維素衍生物Mw之90%以下,即可作成0.9倍以下。分散劑VA之Mw係可作成纖維素衍生物之Mw之75%以下,可作成60%以下,亦可作成例如50%以下。又,分散劑VA之Mw係通常適當為作成纖維素衍生物Mw之0.5%以上,以作成1%以上為佳。在從容易使分散性提升效果適當發揮之觀點,在某些態樣中,分散劑VA之Mw可作成纖維素衍生物之Mw之2%以上,可作成3%以上,可作成5%以上,可作成10%以上,可作成20%以上,亦可作成30%以上。 [0053] 表面保護劑中所佔之分散劑VA之比例並無特別限定,能以取得所欲之分散性提升效果之方式進行設定。在一種態樣中,表面保護劑中所佔之分散劑VA之比例係可作成例如0.05重量%以上,通常係適當作成0.1重量%以上,從取得較高分散性提升效果之觀點,可作成0.5重量%以上,可作成1重量%以上,亦可作成1.5重量%以上。又,表面保護劑中所佔之分散劑VA之比例係可作成例如50重量%以下,從變得容易適宜發揮纖維素衍生物之使用效果之觀點,通常係適當作成30重量%以下,可作成20重量%以下,可作成15重量%以下,可作成10重量%以下,亦可作成例如7重量%以下。在此揭示之技術係在表面保護劑中所佔之分散劑VA之比例為5重量%以下,例如4重量%以下之態樣下仍能適宜實施。 [0054] 纖維素衍生物每100g之分散劑VA之含量並非係受到特別限定者,例如可作成0.1g以上,可作成0.2g以上,可作成0.5g以上,可作成1g以上,可作成1.5g以上,可作成2g以上。隨著分散劑VA之含量增加,而有變得容易取得較高分散性提升效果之傾向。又,纖維素衍生物每100g之分散劑VA之含量係可作成例如80g以下,從更加良好發揮纖維素衍生物之使用效果之觀點,通常係適當作成50g以下,以作成30g以下為佳,可作成20g以下,可作成15g以下,可作成10g以下,可作成7g以下,亦可作成例如5g以下。 [0055] 研磨用組成物中之分散劑VA之含量並非係受到特別限定者,以該研磨用組成物中之磨粒每100g,例如可作成0.0001g以上,可作成0.0005g以上,可作成0.001g以上,可作成0.005g以上,可作成0.01g以上,可作成0.02g以上,可作成0.05g以上,亦可作成0.07g以上。隨著分散劑VA之含量增加,而有變得容易取得較高分散性提升效果之傾向。在某些態樣中,研磨用組成物中之分散劑VA之含量係例如可作成0.1g以上,可作成0.2g以上,可作成1.2g以上,亦可作成2.5g以上。又,磨粒每100g之分散劑VA之含量在從洗淨性或經濟性之觀點,通常係適當作成10g以下,亦可作成5g以下。在某些態樣中,研磨用組成物中之分散劑VA之含量係例如可作成3g以下,可作成2g以下,可作成1g以下,亦可作成0.5g以下。 [0056] 研磨用組成物中之纖維素衍生物與分散劑VA之合計含量並非係受到特別限定者,以該研磨用組成物中之磨粒每100g,可作成例如1.1g以上,通常係適當作成1.5g以上,可作成2g以上,可作成2.5g以上,可作成3g以上,可作成3.5g以上,亦可作成4g以上。隨著上述合計含量增加,而有變得容易取得較高分散性提升效果之傾向。在某些態樣中,上述合計含量可為7g以上,亦可為10g以上。又,磨粒每100g之纖維素衍生物與分散劑VA之合計含量在從洗淨性或經濟性之觀點,通常係適當作成30g以下,以作成20g以下為佳,亦可作成15g以下。在某些態樣中,上述合計含量係例如可作成12g以下,亦可作成10g以下。在此揭示之技術在以磨粒每100g之纖維素衍生物與分散劑VA之合計含量為8g以下(例如6g以下)之態樣下仍能適宜實施。 [0057] (氧伸烷基系添加劑) 在此揭示之技術中之表面保護劑因應必要亦可更包含氧伸烷基系添加劑。作為氧伸烷基系添加劑,可適宜使用包含氧伸烷基單位超過50重量%之構造之水溶性有機物。作為氧伸烷基系添加劑,可單獨使用一種此種水溶性有機物,或可將二種以上組合使用。以非離子系之水溶性有機物為佳。以下,有將氧伸烷基系添加劑標註為「添加劑OA」之情況。 [0058] 作為能使用當作添加劑OA之水溶性有機物,可舉出例如聚環氧乙烷(PEO)、環氧乙烷(EO)與環氧丙烷(PO)或環氧丁烷(BO)之嵌段共聚物、EO與PO或BO之無規共聚物等。其中亦以EO與PO之嵌段共聚物或EO與PO之無規共聚物為佳。EO與PO之嵌段共聚物可為包含PEO嵌段與聚環氧丙烷(PPO)嵌段之二嵌段共聚物、三嵌段共聚物等。上述三嵌段共聚物之例係包括PEO-PPO-PEO型三嵌段共聚物及PPO-PEO-PPO型三嵌段共聚物。通常係以PEO-PPO-PEO型三嵌段共聚物為較佳。在EO與PO之嵌段共聚物或無規共聚物中,構成該共聚物之EO與PO之莫耳比(EO/PO)在從對水之溶解性或洗淨性等之觀點,以大於1為佳,以2以上為較佳,以3以上為更佳,亦可為例如5以上。 [0059] 作為能使用當作添加劑OA之水溶性有機物之其他例,可舉出如聚乙二醇、聚丙二醇、聚丁二醇等之氧伸烷基聚合物;聚氧乙烯烷基醚、聚氧乙烯烷基苯基醚、聚氧乙烯烷基胺、聚氧乙烯脂肪酸酯、聚氧乙烯甘油基醚脂肪酸酯、聚氧乙烯花楸丹脂肪酸酯等之聚氧伸烷基衍生物、例如聚氧伸烷基加成物。作為適宜例,可舉出如聚乙二醇及聚氧乙烯烷基醚。聚氧乙烯烷基醚係可為例如聚氧乙烯癸基醚。 [0060] 作為聚氧伸烷基衍生物之具體例,可舉出如聚氧乙烯丙基醚、聚氧乙烯丁基醚、聚氧乙烯戊基醚、聚氧乙烯己基醚、聚氧乙烯辛基醚、聚氧乙烯-2-乙基己基醚、聚氧乙烯壬基醚、聚氧乙烯癸基醚、聚氧乙烯異癸基醚、聚氧乙烯十三基醚、聚氧乙烯月桂基醚、聚氧乙烯十六基醚、聚氧乙烯硬脂醯基醚、聚氧乙烯異硬脂醯基醚、聚氧乙烯油醯基醚、聚氧乙烯苯基醚、聚氧乙烯辛基苯基醚、聚氧乙烯壬基苯基醚、聚氧乙烯十二基苯基醚、聚氧乙烯苯乙烯化苯基醚、聚氧乙烯月桂基胺、聚氧乙烯硬脂醯基胺、聚氧乙烯油醯基胺、聚氧乙烯單月桂酸酯、聚氧乙烯單硬脂酸酯、聚氧乙烯二脂酸酯、聚氧乙烯單油酸酯、聚氧乙烯二油酸酯、單月桂酸聚氧乙烯花楸丹、單棕櫚酸聚氧乙烯花楸丹、單硬脂酸聚氧乙烯花楸丹、單油酸聚氧乙烯花楸丹、三油酸聚氧乙烯花楸丹、四油酸聚氧乙烯山梨醇、聚氧乙烯蓖麻油、聚氧乙烯硬化蓖麻油等。 [0061] 添加劑OA之重量平均分子量(Mw)並無特別限定,從分散性之觀點,通常係適當作成10×104
以下,例如可為5×104
以下,可為3×104
以下,可為2×104
以下,可為1×104
以下,可為9500以下,可為例如未滿9000。又,添加劑OA之Mw在從提升研磨後之表面品位之觀點,通常係適當為200以上,以250以上,例如300以上為佳。添加劑OA之Mw之較佳範圍係亦能根據該添加劑OA之種類而相異。例如,添加劑OA在使用聚氧乙烯烷基醚或氧伸烷基聚合物(例如聚乙二醇)時,其之Mw係以未滿5000為佳,亦可為2500以下,例如1000以下。又,添加劑OA在使用例如PEO-PPO-PEO型之三嵌段共聚物時,其之Mw例如可為1000以上,可為3000以上,亦可為5000以上。 [0062] 表面保護劑中所佔之添加劑OA之比例並無特別限定。上述比例係可例如作成0.05重量%以上,亦可作成0.5重量%以上,從取得較高使用效果之觀點,可作成1重量%以上,亦可作成5重量%以上。又,從變得容易適宜發揮纖維素衍生物之使用效果之觀點,表面保護劑中所佔之添加劑OA之比例係通常適當作成30重量%以下,可作成25重量%以下,可作成20重量%以下,亦可作成15重量%以下。 [0063] 纖維素衍生物每100g之添加劑OA之含量並非係受到特別限定者,例如可作成0.1g以上,可作成1g以上,亦可作成3g以上。又,從變得容易適宜發揮纖維素衍生物之使用效果之觀點,纖維素衍生物每100g之添加劑OA之含量係通常適當作成100g以下,可作成70g以下,可作成50g以下,可作成30g以下,可作成20g以下,亦可作成15g以下。 [0064] 研磨用組成物中之添加劑OA之含量並非係受到特別限定者,以該研磨用組成物中之磨粒每100g,例如可作成0.0001g以上,可作成0.01g以上,亦可作成0.05g以上。又,磨粒每100g之添加劑OA之含量係通常適當作成5g以下,可作成3g以下,亦可作成1g以下。 [0065] 分散劑VA每1g之添加劑OA之含量並非係受到特別限定者,例如可作成0.01g以上,可作成0.1g以上,可作成0.3g以上。又,分散劑VA每1g之添加劑OA之含量通常係適當作成20g以下,可作成15g以下,可作成10g以下,可作成5g以下,亦可作成1g以下。 [0066] 在此揭示之技術之一種態樣中,上述表面保護劑係能組合包含分散劑VA,與重量平均分子量(Mw)未滿5000之氧伸烷基系添加劑(添加劑OAL
)。藉由使用添加劑OAL
,可更加減低研磨後之表面缺陷,例如LPD-N數。作為添加劑OAL
,可使用當作能使用作為添加劑OA之水溶性有機物所例示之上述材料中Mw未滿5000者。添加劑OAL
之Mw可為2500以下,可為1000以下,亦可為例如800以下。又,從適宜發揮表面缺陷低減效果之觀點,添加劑OAL
之Mw係適當為200以上,可為250以上,亦可為例如300以上。在一種態樣中,也可使用Mw為350以上之添加劑OAL
。可較佳使用作為添加劑OAL
之材料之非限定性例係能包括氧伸烷基聚合物及聚氧乙烯烷基醚。上述氧伸烷基聚合物係可為例如聚乙二醇。上述聚氧乙烯烷基醚係可為例如聚氧乙烯癸基醚。 [0067] 分散劑VA之每1g之添加劑OAL
之含量並非係受到特別限定者,例如可作成0.01g以上,可作成0.05g以上,可作成0.1g以上,亦可作成0.3g以上。又,分散劑VA每1g之添加劑OA之含量係通常適當作成10g以下,可作成5g以下,可作成3g以下,可作成2g以下,可作成1g以下,亦可作成例如0.7g以下。 [0068] <鹼性化合物> 鹼性化合物係能適宜選自具有、溶解於水而使水溶液之pH上昇之功能之各種鹼性化合物。可使用例如含氮之有機或無機之鹼性化合物、鹼金屬之氫氧化物、鹼土類金屬之氫氧化物、各種之碳酸鹽或碳酸氫鹽等。作為含氮之鹼性化合物之例,可舉出如第四級銨化合物、第四級鏻化合物、氨、胺等。作為上述胺,以水溶性胺為佳。此種鹼性化合物係可單獨使用一種或可將二種以上組合使用。 [0069] 作為鹼金屬之氫氧化物之具體例,可舉出如氫氧化鉀、氫氧化鈉等。作為碳酸鹽或碳酸氫鹽之具體例,可舉出如碳酸氫銨、碳酸銨、碳酸氫鉀、碳酸鉀、碳酸氫鈉、碳酸鈉等。作為胺之具體例,可舉出如甲基胺、二甲基胺、三甲基胺、乙基胺、二乙基胺、三乙基胺、乙二胺、單乙醇胺、N-(β-胺基乙基)乙醇胺、六亞甲基二胺、二伸乙三胺、三伸乙四胺、無水哌嗪、哌嗪六水合物、1-(2-胺基乙基)哌嗪、N-甲基哌嗪、胍、咪唑或三唑等之唑類等。作為第四級鏻化合物之具體例,可舉出如氫氧化四甲基鏻、氫氧化四乙基鏻等之氫氧化第四級鏻。 [0070] 作為第四級銨化合物,可較佳使用四烷基銨鹽、羥基烷基三烷基銨鹽等之第四級銨鹽。上述第四級銨鹽中之陰離子成分可為例如OH-
、F-
、Cl-
、Br-
、I-
、ClO4 -
、BH4 -
等。作為第四級銨鹽,以強鹼者為佳。其中作為較佳例,可舉出如陰離子為OH-
之第四級銨鹽,即氫氧化第四級銨。作為氫氧化第四級銨之具體例,可舉出如氫氧化四甲基銨、氫氧化四乙基銨、氫氧化四丙基銨、氫氧化四丁基銨、氫氧化四戊基銨及氫氧化四己基銨等之氫氧化四烷基銨;氫氧化2-羥基乙基三甲基銨(亦稱為膽鹼)等之氫氧化羥基烷基三烷基銨等。此等之中係以氫氧化四烷基銨為佳,其中亦以氫氧化四甲基銨(TMAH)為佳。 [0071] 作為在此揭示之技術中之鹼性化合物,以選自鹼金屬氫氧化物、氫氧化第四級銨及氨之至少一種鹼性化合物為佳。此等之中,以氫氧化四甲基銨等之氫氧化第四級銨及氨為較佳,以氨為特佳。 [0072] <水> 在此揭示之研磨用組成物典型為包含水。作為水,可較佳使用離子交換水(去離子水)、純水、超純水、蒸餾水等。所使用之水由於要極力迴避研磨用組成物所含有之其他成分之作用受到阻礙,故例如過渡金屬離子之合計含量係以100ppb以下為佳。例如,可藉由離子交換樹脂所成之雜質離子之去除、由過濾器所成之異物之去除、蒸餾等之操作來提高水之純度。 [0073] <其他成分> 在不顯著妨礙本發明之效果範圍內,在此揭示之研磨用組成物因應必要亦可更含有螯合劑、有機酸、有機酸鹽、無機酸、無機酸鹽、防腐劑、防黴劑等之研磨漿所能使用之公知添加劑。在此揭示之研磨用組成物係能在實質上不含有螯合物劑之態樣下適宜實施。上述添加劑可為例如矽晶圓之拋光步驟中使用之研磨漿所能用之公知添加劑。 [0074] 在此揭示之研磨用組成物係以實質上不包含氧化劑為佳。其係由於研磨用組成物中若包含氧化劑時,在例如將矽晶圓等之矽基板當作研磨對象物之研磨中,上述研磨對象物因被供給至研磨對象物而該研磨對象物之表面會受到氧化而產生氧化膜,因此而有導致研磨效率降低之可能性。作為在此所稱之氧化劑之具體例,可舉出如過氧化氫(H2
O2
)、過硫酸鈉、過硫酸銨、二氯異三聚氰酸鈉等。尚且,研磨用組成物實質上不包含氧化劑係指至少蓄意地不使其含有氧化劑。 [0075] 在此揭示之研磨用組成物在不顯著妨礙本發明效果之範圍內,亦可包含纖維素衍生物及分散劑VA以外之水溶性高分子(以下,亦稱任意聚合物)作為任意成分。作為該種任意聚合物,可使用例如澱粉衍生物、N-乙烯基型聚合物、N-(甲基)丙烯醯基型聚合物等。作為澱粉衍生物之例,可舉出如α化澱粉、支鏈澱粉(pullulan)、羧基甲基澱粉、環糊精等。N-乙烯基型聚合物之聚合物鏈B係可為如上述所例示之N-乙烯基型單體之均聚物或共聚物。作為N-乙烯基型聚合物之具體例,可舉出如N-乙烯基吡咯啶酮(VP)之均聚物,或VP之共聚合比例為70重量%以上之共聚物等。N-(甲基)丙烯醯基型聚合物之聚合物鏈B係可如上述所例示之N-(甲基)丙烯醯基型單體之均聚物或共聚物。作為N-(甲基)丙烯醯基型聚合物之具體例,可舉出如N-異丙基丙烯醯胺(NIPAM)之均聚物、NIPAM之共聚合比例為70重量%以上之共聚物、N-丙烯醯基嗎啉(ACMO)之均聚物、ACMO之共聚合比例為70重量%以上之共聚物等。任意聚合物係以非離子性為佳。任意聚合物之含量係以纖維素衍生物每100g作成為30g以下為適當,以作成10g以下為佳,亦可作成5g以下,亦可為1g以下。在此揭示之技術係能在實質上不含有此種任意聚合物之態樣下適宜實施。 [0076] <pH> 在此揭示之研磨用組成物之pH通常適當為8.0以上,以8.5以上為佳,較佳為9.0以上,更佳為9.5以上,例如10.0以上。研磨用組成物之pH若變高時,有研磨效率提升之傾向。另一方面,從防止磨粒例如二氧化矽粒子之溶解,因抑制該磨粒所造成之機械性研磨作用降低之觀點,研磨用組成物之pH適當為12.0以下,以11.8以下為佳,以11.5以下為較佳,以11.0以下為更佳。 [0077] 在此揭示之技術中,液狀組成物之pH係使用pH計,在使用標準緩衝液進行3點校正後,藉由將玻璃電極放入測量對象之組成物,測量經過2分鐘以上且安定後之值來取得。上述標準緩衝液為酞酸鹽pH緩衝液 pH:4.01(25℃)、中性磷酸鹽pH緩衝液 pH:6.86(25℃)、碳酸鹽pH緩衝液 pH:10.01(25℃)。作為pH計,可使用例如,堀場製作所製之玻璃電極式氫離子濃度指示計,型號F-23或其相當品。 [0078] <用途> 在此揭示之技術中之研磨用組成物係能適用於研磨具有各種材質及形狀之研磨對象物。研磨對象物之材質可為例如,矽、鋁、鎳、鎢、銅、鉭、鈦、不鏽鋼等之金屬或半金屬,或該等之合金;石英玻璃、鋁矽酸鹽玻璃、玻璃狀碳等之玻璃狀物質;氧化鋁、二氧化矽、藍寶石、氮化矽、氮化鉭、碳化鈦等之陶瓷材料;碳化矽、氮化鎵、砷化鎵等之化合物半導體基板材料;聚醯亞胺樹脂等之樹脂材料等。亦可為由此等之中複數之材質所構成之研磨對象物。 [0079] 在此揭示之技術中之研磨用組成物特別係理想適用在研磨例如矽晶圓等之由矽所構成之表面。在此所謂之矽晶圓之典型例為矽單結晶晶圓,例如,切割矽單結晶錠而得之矽單結晶晶圓。 [0080] 在此揭示之研磨用組成物係可理想適用於研磨對象物之拋光步驟,例如矽晶圓之拋光步驟。研磨對象物在由在此揭示之研磨用組成物所成之拋光步驟之前,亦可對研磨對象物施以在精削或蝕刻等之比拋光步驟還要上游之步驟中能適用於研磨對象物之一般處理。 [0081] 在此揭示之研磨用組成物係能理想使用於例如藉由上游步驟而調製成表面粗度0.01nm~100nm之表面狀態之研磨對象物例如矽晶圓之拋光。研磨對象物之表面粗度Ra係可使用例如Schmitt Measurement System Inc.公司製之雷射掃描式表面粗度計「TMS-3000WRC」進行測量。在最終拋光(完工研磨)或其之前之拋光下之使用則極具效果,特佳係使用於最終拋光用。在此,最終拋光係指目的物之製造製程中之最後拋光步驟,即係指在該步驟後不會實施進一步拋光之步驟。 [0082] <研磨用組成物> 在此揭示之研磨用組成物典型係在包含該研磨用組成物之研磨液之形態下供給至研磨對象物,而使用於該研磨對象物之研磨。上述研磨液可為例如將在此揭示之任一研磨用組成物予以稀釋調製而成者。研磨用組成物之稀釋典型係可藉由水來進行。或,亦可將該研磨用組成物直接使用作為研磨液。即,在此揭示之技術中之研磨用組成物之概念係包括,供給至研磨對象物而使用於研磨該研磨對象物之研磨液(亦稱為工作漿(working slurry)),進行稀釋而使用作為研磨液之濃縮液之雙方。上述濃縮液亦係能理解作為研磨液之原液。作為包含在此揭示之研磨用組成物之研磨液之其他例,可舉出調整該組成物之pH而成之研磨液。 [0083] (研磨液) 研磨液中之磨粒之含量並無特別限制,典型為0.01重量%以上,以0.05重量%以上為佳,較佳為0.10重量%以上,例如0.13重量%以上。伴隨磨粒之含量增加,可實現更高研磨速度。從實現較低霧度表面之觀點,通常上述含量適當為10重量%以下,以7重量%以下為佳,較佳為5重量%以下,更佳為2重量%以下,例如1重量%以下,可為0.5重量%以下,亦可為0.3重量%以下。 [0084] 研磨液中之表面保護劑之濃度並無特別限制,可作成例如0.0005重量%以上。從取得較高保護效果之觀點,較佳濃度為0.001重量%以上,更佳為0.002重量%以上。在某些態樣中,表面保護劑之濃度係例如可為0.003重量%以上,亦可為0.005重量%以上。又,表面保護劑之濃度係可作成例如1.0重量%以下,通常適當作成0.5重量%以下,可作成0.1重量%以下,可作成0.05重量%以下,亦可作成例如0.02重量%以下。 [0085] 研磨液中之纖維素衍生物之濃度並無特別限制,可作成例如0.0001重量%以上。從減低霧度等之觀點,較佳濃度為0.0005重量%以上,更佳為0.001重量%以上,例如可為0.003重量%以上,亦可為0.005重量%以上。又,從研磨效率等之觀點,纖維素衍生物之濃度係通常作成0.2重量%以下為佳,以作成0.1重量%以下為較佳,亦可作成0.05重量%以下,亦可作成例如0.01重量%以下。 [0086] 研磨液中之分散劑VA之濃度並無特別限制,可作成例如0.00001重量%以上,從取得較高分散性提升效果之觀點,可作成0.00005重量%以上,亦可作成0.0001重量%以上。在某些態樣中,分散劑VA之濃度可為0.0005重量%以上,亦可為0.001重量%以上。又,從研磨效率等之觀點,分散劑VA之濃度係通常作成0.1重量%以下為佳,可作成0.01重量%以下,可作成0.005重量%以下,可作成0.001重量%以下,亦可作成例如0.0005重量%以下。 [0087] 在此揭示之研磨用組成物包含鹼性化合物時,研磨液中之鹼性化合物之濃度並無特別限制。從提升研磨速度等之觀點,通常係將上述濃度作成研磨液之0.0005重量%以上為佳,以作成0.001重量%以上為較佳。又,從減低霧度等之觀點,上述濃度係適當作成未滿0.3重量%,以作成未滿0.1重量為佳,以作成未滿0.05重量%(例如0.03重量%)為較佳。 [0088] (濃縮液) 在此揭示之研磨用組成物在供給至研磨對象物之前亦可為經濃縮之形態。上述經濃縮之形態係指研磨液之濃縮液之形態,亦能理解作為研磨液之原液。在從製造、流通、保存等時之便利性或降低成本等之觀點,此種經濃縮形態之研磨用組成物較為有利。濃縮倍率並無特別限定,例如以體積換算可作成2倍~100倍程度,通常以5倍~50倍程度為適當,可為例如10倍~40倍程度。 [0089] 此種濃縮液係能以在所欲之時機下進行稀釋而調製成研磨液(工作漿),並將該研磨液供給至研磨對象物之態樣進行使用。上述稀釋係藉由例如對上述濃縮液添加水進行混合來進行。 [0090] 上述濃縮液中之磨粒之含量係可作成例如50重量%以下。上述濃縮液之操作性,從例如磨粒之分散安定性或過濾性等之觀點,通常上述濃縮液中之磨粒之含量係以45重量%以下為佳,亦可作成40重量%以下,例如30重量%以下。又,從製造、流通、保存等之便利性或成本減低等之觀點,磨粒之含量係可作成例如0.5重量%以上,以1重量%以上為佳,可作成2重量%以上,亦可作成3重量%以上。 [0091] (研磨用組成物之調製) 在此揭示之技術所使用之研磨用組成物可為單劑型,亦可為以兩劑型為首之多劑型。可為例如藉由將研磨用組成物之構成成分之中至少包含磨粒之部分A,與包含剩餘成分之至少一部分之部分B予以混合,因應必要將此等在適當時機下進行混合及稀釋而調製成研磨液之構成。 [0092] 研磨用組成物之調製方法並無特別限定。例如,使用翼式攪拌機、超音波分散機、均質混合機等之周知混合裝置,混合構成研磨用組成物之各成分為宜。混合該等成分之態樣並無特別限定,例如可將全成分一次地進行混合,亦可以適宜設定之順序進行混合。 [0093] <研磨> 在此揭示之研磨用組成物係例如在包含以下操作之態樣下使用於研磨對象物之研磨。以下,說明關於使用在此揭示之研磨用組成物對研磨對象物,例如矽晶圓進行研磨之方法之適合之一種態樣。 即,準備包含在此揭示之任一研磨用組成物之研磨液。準備上述研磨液係能包括對研磨用組成物施加稀釋等之濃度調整,或pH調整等之操作而製作研磨液。或,亦可將研磨用組成物直接使用作為研磨液。 [0094] 其次,將該研磨液供給至研磨對象物,藉由常法進行研磨。例如,在進行矽晶圓之完工研磨時,典型為將經過精削步驟之矽晶圓裝設在一般研磨裝置上,透過該研磨裝置之研磨墊對上述矽晶圓之研磨對象面供給研磨液。典型而言,連續供給上述研磨液,且同時將研磨墊壓向矽晶圓之研磨對象面,並使兩者相對地移動,例如旋轉移動。經過該研磨步驟而結束研磨對象物之研磨。 [0095] 上述研磨步驟所使用之研磨墊並無特別限定,可使用例如,發泡聚胺基甲酸酯型、不織布型、麂皮型等之研磨墊。各研磨墊可包含磨粒,亦可不包含磨粒通常係理想使用不包含磨粒之研磨墊。 [0096] 使用在此揭示之研磨用組成物所研磨之研磨對象物典型者為經洗淨者。洗淨係可使用適當洗淨液進行。使用之洗淨液並無特別限定,例如,在半導體等之領域中,可使用一般性SC-1洗淨液、SC-2洗淨液等。上述SC-1洗淨液為氫氧化銨(NH4
OH)與過氧化氫(H2
O2
)與水(H2
O)之混合液。上述SC-2洗淨液為HCl與H2
O2
與H2
O之混合液。洗淨液之溫度係可作成例如室溫以上,約90℃程度為止之範圍。上述室溫係典型為約15℃~25℃。從提升洗淨效果之觀點,可理想使用50℃~85℃程度之洗淨液。 [實施例] [0097] 以下,說明關於本發明之數個實施例,但並非係意圖將本發明侷限於該實施例所示者。尚且,以下之說明中,「%」除了在表示分散性參數之數值時,其他為重量基準。 [0098] <研磨用組成物之調製> (實施例1) 調製出在離子交換水中分別包含濃度0.175%之BET徑為25nm之膠質二氧化矽、濃度0.00125%之Mw為9000之PEO-PPO-PEO嵌段共聚物、濃度0.005%之氨,且更分別包含濃度0.0085%之Mw為25×104
之羥基乙基纖維素(HEC)、濃度0.0003%之Mw為13000之聚乙烯醇(PVA,皂化度95%以上)之研磨用組成物。 [0099] (實施例2) 在實施例1中,取代Mw為13000之PVA而改用Mw為106000之PVA。其他方面係與實施例1同樣地操作而調製出本例之研磨用組成物。 [0100] (實施例3) 在實施例1中,取代PVA,而改用將皂化度95%以上之聚乙烯醇(PVA)當作主鏈,且將聚乙烯吡咯啶酮(PVP)當作側鏈之Mw為175000之接枝共聚物(以下標記為「PVA-g-PVP」)。其他方面係與實施例1同樣地操作而調製出本例之研磨用組成物。 [0101] (實施例4) 在實施例1中,將PVA之濃度變更成0.0002%。又,使其更含有0.0001%濃度之Mw為600之聚乙二醇(PEG)。其他方面係與實施例1同樣地操作而調製出本例之研磨用組成物。 [0102] (實施例5) 調製出在離子交換水中分別包含濃度0.088%之BET徑為25nm之膠質二氧化矽、濃度0.0006%之Mw為400之聚氧乙烯癸基醚、濃度0.006%之氨,且更分別包含濃度0.0075%之Mw為25×104
之HEC、濃度0.004%之Mw為106000之聚乙烯醇(PVA,皂化度95%以上)之研磨用組成物。 [0103] (比較例1) 除了未使用PVA之外,其他係與實施例1同樣地操作而調製出本例之研磨用組成物。 [0104] (比較例2) 在實施例1中,取代PVA而改用Mw為45000之聚乙烯吡咯啶酮(PVP)。其他方面係與實施例1同樣地操作而調製出本例之研磨用組成物。 [0105] (比較例3,4) 除了未使用HEC之外,其他分別係與實施例1、2同樣地操作而調製出本例之研磨用組成物。 [0106] 以上述之方法測量該等之實施例及比較例之研磨用組成物之個別分散性參數α。作為實施例1~3及比較例1、2之試驗液,使用在構成表面保護材之HEC之濃度成為0.17%之濃度方式下包含各例之研磨用組成物之該表面保護材,更包含0.1%之氨,且剩餘部分係由水所構成之試驗液。具體而言,實施例1、2中使用以濃度計包含HEC 0.17%、Mw為13000或106000之PVA 0.006%、PEO-PPO-PEO 0.025%、氨0.1%,且剩餘部分係由水所構成之試驗液。實施例3中使用以濃度計包含HEC 0.17%、PVA-g-PVP 0.006%、PEO-PPO-PEO 0.025%、氨0.1%,且剩餘部分係由水所構成之試驗液。實施例4中使用以濃度計包含HEC 0.17%、PVA 0.004%、PEG 0.002%、PEO-PPO-PEO 0.025%、氨0.1%,且剩餘部分係由水所構成之試驗液。實施例5中使用以濃度計包含HEC 0.17%、PVA 0.091%、C10PEO 0.014%、氨0.1%,且剩餘部分係由水所構成之試驗液。比較例1中使用以濃度計包含HEC 0.17%、PEO-PPO-PEO 0.025%、氨0.1%,且剩餘部分係由水所構成之試驗液。比較例2中使用以濃度計包含HEC 0.17%、PEO-PPO-PEO 0.025%、PVP 0.006%、氨0.1%,且剩餘部分係由水所構成之試驗液。結果係如表1所示。尚且,關於不含有HEC之比較例3、4,將從實施例1、2之研磨用組成物之在分散性參數α之測量中所使用之各試驗液去除HEC之組成之試驗液,即將關於包含Mw為13000或106000之PVA 0.006%、PEO-PPO-PEO 0.025%、氨0.1%,且剩餘部分係由水所構成之試驗液之測量值記載於括弧內作為參考值。 [0107] <矽晶圓之研磨> (1)預備研磨步驟 調製出包含磨粒0.95%及鹼性化合物0.065%且剩餘部分係由水所構成之一次研磨用組成物。磨粒係使用BET徑35nm之膠質二氧化矽。鹼性化合物係使用氫氧化鉀(KOH)。將該一次研磨用組成物直接使用作為研磨液(工作漿),以下述研磨條件1去研磨作為研磨對象物之矽晶圓。矽晶圓係使用已結束精削及蝕刻之直徑200mm市售矽單結晶晶圓(傳導型:P型、結晶方位:<100>、抵抗率:1Ω・cm以上未滿100Ω・cm、無COP)。 [0108] [研磨條件1] 研磨裝置:股份有限公司岡本工作機械製作所製之葉片研磨機,型號「PNX-322」 研磨荷重:15kPa 定盤旋轉數:30rpm 載體旋轉數:30rpm 研磨墊:富士紡愛媛公司製、製品名「FP55」 研磨液供給速率:0.55公升/分 研磨液之溫度:20℃ 定盤冷卻水之溫度:20℃ 研磨時間:3分 [0109] (2)完工研磨步驟 分別將上述實施例及比較例之研磨用組成物直接使用作為研磨液(工作漿),以下述研磨條件2去研磨已結束上述預備研磨步驟之矽晶圓。 [0110] [研磨條件2] 研磨裝置:股份有限公司岡本工作機械製作所製之葉片研磨機,型號「PNX-322」 研磨荷重:15kPa 定盤旋轉數:30rpm 載體旋轉數:30rpm 研磨墊:富士紡愛媛公司製研磨墊,商品名「POLYPAS27NX」 研磨液供給速率:0.4公升/分 研磨液之溫度:20℃ 定盤冷卻水之溫度:20℃ 研磨時間:4分 [0111] 從研磨裝置取出研磨後之矽晶圓,使用NH4
OH(29%):H2
O2
(31%):去離子水(DIW)=1:1:15(體積比)之洗淨液進行洗淨(SC-1洗淨)。更具體而言,準備2個洗淨槽,分別在該等第1及第2洗淨槽中收容上述洗淨液,保持在60℃,將研磨後之矽晶圓浸漬於第1洗淨槽15分鐘,其後通過使用超純水與超音波之潤喜槽,在第2洗淨槽浸漬15分鐘後,使用旋轉乾燥機使其乾燥。 [0112] <LPD-N數測量> 使用KLA-Tencor公司製晶圓檢査裝置,商品名「SURFSCAN SP2」,在該裝置之DCO模式下測量存在於從上述各例所得之矽晶圓之表面(研磨面)上之LPD-N之個數。將關於各例之LPD-N數換算成將比較例1之LPD-N數設成100%之相對值,根據該換算值,使用以下之6階段來評價LPD-N數。結果係如表1所示。 A:未滿40% B:40%以上未滿50% C:50%以上未滿60% D:60%以上未滿100% E:100%以上未滿150% F:150%以上 [0113][0114] 如表1所示,在使用包含纖維素衍生物與乙烯基醇系分散劑,且包含分散性參數α未滿100之表面保護劑S1之實施例1~5之研磨用組成物時,與比較例1之研磨用組成物相比,可確認到完工研磨後之LPD-N數明顯降低。另一方面,在α超過100之比較例2之研磨用組成物時,並無法取得LPD-N數之減低效果。又,從實施例1、2之研磨用組成物去除纖維素衍生物之比較例3、4中,完工研磨後之表面品質大幅降低。 [0115] 以上,已詳細地說明本發明之具體例,但該等僅為例示,而並非係限制申請專利範圍者。申請專利範圍記載之技術係包含將以上例示之具體例予以各種變形、變更者。
Claims (8)
- 一種研磨用組成物,其係包含磨粒、鹼性化合物及表面保護劑之研磨用組成物,其中前述表面保護劑包含纖維素衍生物與乙烯基醇系分散劑,前述表面保護劑之分散性參數α未滿100,前述纖維素衍生物之重量平均分子量為5×104以上未滿50×104,前述研磨用組成物中之前述磨粒之含量為0.01重量%以上10重量%以下,前述研磨用組成物中之前述鹼性化合物之含量為0.0005重量%以上未滿0.3重量%,前述研磨用組成物中之前述表面保護劑之含量為0.0005重量%以上1.0重量%以下,前述研磨用組成物中之前述纖維素衍生物之含量為0.0001重量%以上0.2重量%以下,前述研磨用組成物中之前述乙烯基醇系分散劑之含量為0.00001重量%以上0.1重量%以下。
- 如請求項1之研磨用組成物,其中前述乙烯基醇系分散劑之重量平均分子量為前述纖維素衍生物之重量平均分子量之90%以下。
- 如請求項1或2之研磨用組成物,其中前述乙烯基醇系分散劑之含量係相對於前述纖維素衍生物100g為0.1g以上80g以下。
- 如請求項1或2之研磨用組成物,其中前述纖維素衍生物與前述乙烯基醇系分散劑之合計含量係相對於前述磨粒100g為1.5g以上20g以下。
- 如請求項1或2之研磨用組成物,其中前述表面保護劑更包含氧伸烷基系添加劑。
- 如請求項5之研磨用組成物,其中作為前述氧伸烷基系添加劑包含重量平均分子量未滿5000之氧伸烷基系添加劑OAL。
- 如請求項1或2之研磨用組成物,其中前述磨粒為二氧化矽粒子。
- 如請求項1或2之研磨用組成物,其係使用於研磨矽晶圓。