TWI730067B - 環氧樹脂硬化劑、環氧樹脂組成物及碳纖維強化複合材 - Google Patents
環氧樹脂硬化劑、環氧樹脂組成物及碳纖維強化複合材 Download PDFInfo
- Publication number
- TWI730067B TWI730067B TW106109068A TW106109068A TWI730067B TW I730067 B TWI730067 B TW I730067B TW 106109068 A TW106109068 A TW 106109068A TW 106109068 A TW106109068 A TW 106109068A TW I730067 B TWI730067 B TW I730067B
- Authority
- TW
- Taiwan
- Prior art keywords
- epoxy resin
- resin composition
- carbon fiber
- hardener
- transfer molding
- Prior art date
Abstract
本發明提供一種環氧樹脂硬化劑,含有下列通式(1)表示之胺化合物(A)與苯酚化合物(B),相對於該(A)成分100質量份,該(B)成分之含量為8~35質量份;並提供含有該環氧樹脂硬化劑之環氧樹脂組成物、及包含該環氧樹脂組成物之硬化物與碳纖維之碳纖維強化複合材。 R1
HN-H2
C-A-CH2
-NHR2
(1) (式(1)中,R1
及R2
各自獨立地為氫原子、或碳數1~6之胺烷基。A為伸環己基或伸苯基。)
Description
本發明關於環氧樹脂硬化劑、含有該環氧樹脂硬化劑與環氧樹脂之環氧樹脂組成物、及包含該環氧樹脂組成物之硬化物與碳纖維之碳纖維強化複合材。
碳纖維強化複合材(以下亦稱為「CFRP(Carbon Fiber Reinforced Plastics)」)具有非常高的彈性模量、強度且質輕,故作為金屬替代材料備受矚目。據預計CFRP尤其在汽車結構材用途、風力發電葉片用途、壓力容器用途、航空航太用途的需求會加速,使用於CFRP之碳纖維、環氧樹脂等基質樹脂的需求近年來也正增大中。
在汽車結構材用途、風力發電葉片用途、壓力容器用途、航空航太用途中,CFRP的成形方法各不相同,故對於CFRP用之基質樹脂的要求特性也視用途而不同。 例如風力發電葉片係依照灌注成形(infusion molding)、真空輔助樹脂轉移造模法(Vacuum Assist Resin Transfer Molding)或輕量樹脂轉移造模法(light resin transfer molding)成形。該等方法中,係於例如使用膜、FRP的由上模具、下模具構成之模具內預先配置強化纖維,將該模具內抽真空,於常壓填充成為基質樹脂之環氧樹脂組成物並使其朝強化纖維進行含浸,然後,使該環氧樹脂硬化而成形。 依照灌注成形、真空輔助樹脂轉移造模法、輕量樹脂轉移造模法所為之成形,其成形法的特徵上,為了將環氧樹脂與環氧樹脂硬化劑混合而成之環氧樹脂組成物填充至模具內,通常花費數十分鐘左右。因此,對於使用在該等成形法之環氧樹脂組成物要求為低黏度且適用期(pot life)長。就環氧樹脂硬化劑而言,係使用異佛酮二胺、具聚醚骨架之多胺化合物等。
又,壓力容器用途之CFRP,係利用依照纖絲捲繞法(filament winding method)所為之成形。纖絲捲繞法係使用使環氧樹脂組成物等基質樹脂含浸於強化纖維絲線而成之強化纖維絲線來覆蓋內襯(liner)之外表面,然後使該基質樹脂硬化的方法。該方法所使用之環氧樹脂組成物,適用期短為快速硬化性的話,環氧樹脂在成形前之階段即會發生硬化。故纖絲捲繞法無法適用快速硬化性之環氧樹脂組成物。
反觀汽車結構材用途之CFRP,係依照高週期樹脂轉移造模法(high-cycle resin transfer molding)成形。該方法係將以往的樹脂轉移造模法進行改良而得。 以往的樹脂轉移造模法係使用上下一對之模具之密閉型成形的一種,為如下之方法:於該模具內配置纖維強化預成形體,將模具夾緊並密閉後,自注入孔將環氧樹脂組成物等樹脂注入模具內並使其含浸於纖維強化預成形體,然後使該樹脂硬化,之後進行脫模。但以往的樹脂轉移造模法,成形時間(預成形體的配置、樹脂含浸、樹脂硬化、及到脫模為止)需要數小時,故汽車結構材用途之CFRP的製造中係使用生產性更高的高週期樹脂轉移造模法。
利用高週期樹脂轉移造模法之成形技術,係纖維強化預成形體的配置時間、樹脂的含浸時間、樹脂的硬化時間、及脫模時間均大幅縮短,總成形時間縮短至10分鐘左右者。高週期樹脂轉移造模法中,就從樹脂之含浸開始直到硬化的步驟而言,在例如係高週期樹脂轉移造模法之一種的高壓樹脂轉移造模法中,係於上下一對之模具內配置強化纖維並密閉,將模具內進行減壓。然後,將係環氧樹脂組成物之主劑的環氧樹脂、及環氧樹脂硬化劑從各自的儲槽以霧氣狀態壓送至混合頭(mixing head),碰撞混合(collision mixing)後快速地注入模具內,使其含浸於碳纖維,並將環氧樹脂硬化。為了提高朝模具內之填充速度及朝碳纖維之含浸速度,碰撞混合後的環氧樹脂組成物係從多個注入孔予以高壓注入。
高週期樹脂轉移造模法中,將環氧樹脂與環氧樹脂硬化劑予以混合後快速地注入模具內,故係環氧樹脂與環氧樹脂硬化劑之混合物的環氧樹脂組成物的適用期沒那麼必要。另一方面,考量生產性的觀點,要求朝強化纖維之含浸性、朝模具之填充速度高,且要求硬化快,故對於使用在高週期樹脂轉移造模法之環氧樹脂組成物,要求為低黏度且為快速硬化性。
使用多胺化合物作為環氧樹脂硬化劑係已知,專利文獻1~3中揭示了含有雙(胺基甲基)環己烷作為多胺化合物的環氧樹脂硬化劑。 [先前技術文獻] [專利文獻]
[專利文獻1]日本特開2001-163955號公報 [專利文獻2]日本特開2011-6499號公報 [專利文獻3]日本特開2015-93948號公報
[發明所欲解決之課題] 但,關於使用在依照高週期樹脂轉移造模法等所為之成形的環氧樹脂硬化劑、及含有該硬化劑與環氧樹脂之環氧樹脂組成物,期望進一步的快速硬化性且低黏度。
本發明之課題在於提供為快速硬化性且低黏度、適合使用在依照高週期樹脂轉移造模法等所為之成形的環氧樹脂硬化劑及環氧樹脂組成物、以及包含該環氧樹脂組成物之硬化物與碳纖維之碳纖維強化複合材。 [解決課題之手段]
本案發明人等為了解決上述課題而進行努力研究的結果,發現藉由含有特定結構之胺化合物與預定量之苯酚化合物的環氧樹脂硬化劑,可解決上述課題。
亦即,本發明關於下列[1]~[13]。 [1]一種環氧樹脂硬化劑,含有下列通式(1)表示之胺化合物(A)與苯酚化合物(B),相對於該(A)成分100質量份,該(B)成分之含量為8~35質量份。 R1
HN-H2
C-A-CH2
-NHR2
(1) (式(1)中,R1
及R2
各自獨立地為氫原子、或碳數1~6之胺烷基。A為伸環己基或伸苯基。) [2]如上述[1]之環氧樹脂硬化劑,其中,該通式(1)中,R1
及R2
皆為氫原子。 [3]如上述[1]或[2]之環氧樹脂硬化劑,其中,該通式(1)中,A為伸環己基。 [4]如上述[1]~[3]中任一項之環氧樹脂硬化劑,其中,該苯酚化合物(B)係下列通式(2)表示之化合物。
(式(2)中,R5
及R6
各自獨立地為OH基、或碳數1~4之烷基。j及k各自獨立地為0~5之整數,且j+k為1以上。多數個R5
、及多數個R6
可皆為相同也可彼此不同,但至少其中一者為OH基。Z為單鍵、碳數1~6之伸烷基、碳數2~6之亞烷基、碳數5~10之環伸烷基、碳數5~10之環亞烷基、碳數7~15之芳基伸烷基、碳數7~15之芳基亞烷基、-S-、-SO-、-SO2
-、-O-、-CO-、-C(CF3
)2
-、-CH(CF3
)-、-CF2
-、-CONH-、或-COO-。) [5]如上述[4]之環氧樹脂硬化劑,其中,該苯酚化合物(B)係選自於由4,4’-(丙烷-2,2-二基)二苯酚、雙(4-羥基苯基)甲烷、1,1-雙(4-羥基苯基)乙烷、及苯乙烯化苯酚構成之群組中之至少1種。 [6]一種環氧樹脂組成物,含有如上述[1]~[5]中任一項之環氧樹脂硬化劑、及環氧樹脂。 [7]如上述[6]之環氧樹脂組成物,其中,該環氧樹脂係在分子內含有芳香環或脂環族結構之環氧樹脂。 [8]如上述[7]之環氧樹脂組成物,其中,該環氧樹脂係下列通式(3)表示之環氧樹脂。
(式(3)中,R21
~R24
各自獨立地為碳數1~6之烷基,p、q、r、及s各自獨立地為0~4之整數。多數個R21
、多數個R22
、多數個R23
、及多數個R24
可皆為相同,也可彼此不同。Y1
及Y2
各自獨立地為單鍵、-CH2
-、-CH(CH3
)-、或-C(CH3
)2
-。R25
為-CH2
CH(OH)-、或-CH(OH)CH2
-。m表示平均重複單元數,且為0~0.2之數。) [9]如上述[6]~[8]中任一項之環氧樹脂組成物,其於溫度40℃之黏度為400mPa‧s以下。 [10]如上述[6]~[9]中任一項之環氧樹脂組成物,係碳纖維強化複合材用。 [11]一種碳纖維強化複合材,含有如上述[6]~[10]中任一項之環氧樹脂組成物之硬化物、及碳纖維。 [12]如上述[11]之碳纖維強化複合材,係汽車用結構材。 [13]如上述[11]或[12]之碳纖維強化複合材之製造方法,具有依照低壓樹脂轉移造模法(low pressure resin transfer molding)、中壓樹脂轉移造模法(middle pressure resin transfer molding)、高壓樹脂轉移造模法(high pressure resin transfer molding)、壓縮樹脂轉移造模法(compression resin transfer molding)、液狀壓縮造模法、液狀淋澆法(liquid lay down method)、飛沫淋澆法(spray lay down method)、表面樹脂轉移造模法、預浸體壓縮造模法或液狀鑄塑法進行成形之步驟。 [發明之效果]
根據本發明,可提供能利用高週期樹脂轉移造模法等以良好的生產性製造汽車用結構材、建材等之CFRP的為快速硬化性且低黏度之環氧樹脂硬化劑及環氧樹脂組成物。將該環氧樹脂組成物作為CFRP之基質樹脂使用的話,朝碳纖維之含浸性優異,且為快速硬化性,故直至可從模具脫模為止的時間亦短,能提高CFRP的生產性。
[環氧樹脂硬化劑] 本發明之環氧樹脂硬化劑,係含有下列通式(1)表示之胺化合物(A)與苯酚化合物(B)的環氧樹脂硬化劑,其特徵為:相對於該(A)成分100質量份,該(B)成分之含量為8~35質量份。 R1
HN-H2
C-A-CH2
-NHR2
(1) (式(1)中,R1
及R2
各自獨立地為氫原子、或碳數1~6之胺烷基。A為伸環己基或伸苯基。)
(胺化合物(A)) 胺化合物(A)為前述通式(1)表示之化合物。本發明之環氧樹脂硬化劑藉由包含特定結構之胺化合物(A),可獲得低黏度且具有快速硬化性之環氧樹脂硬化劑及環氧樹脂組成物。 式(1)中,R1
及R2
各自獨立地為氫原子、或碳數1~6之胺烷基。R1
及R2
宜各自獨立地為氫原子、或碳數1~4之胺烷基較佳,為氫原子、或碳數2~4之胺烷基更佳,R1
及R2
皆為氫原子尤佳。 又,式(1)中,A為伸環己基或伸苯基,宜為伸環己基較佳。具體而言,A為選自於由1,2-伸環己基、1,3-伸環己基、1,4-伸環己基、1,2-伸苯基、1,3-伸苯基、及1,4-伸苯基構成之群組中之1種以上,考量耐熱性及耐候性的觀點,宜為選自於由1,2-伸環己基、1,3-伸環己基、及1,4-伸環己基構成之群組中之1種以上較佳,為1,3-伸環己基更佳。此外,本說明書中之伸環己基包括順式體、反式體中之任一者。
胺化合物(A)之具體例,例如,可列舉1,2-雙(胺基甲基)環己烷、1,3-雙(胺基甲基)環己烷、1,4-雙(胺基甲基)環己烷、鄰亞二甲苯二胺、間亞二甲苯二胺(MXDA)、對亞二甲苯二胺(PXDA)、及下列通式(1-1)~(1-4)表示之化合物等。
式(1-1)~(1-4)中,R3
及R4
各自獨立地為碳數1~6之伸烷基。R3
及R4
宜為碳數1~4之伸烷基較佳,為碳數2~4之伸烷基更佳,為碳數3之伸烷基尤佳。 上述中,就胺化合物(A)而言,宜為選自於由1,2-雙(胺基甲基)環己烷、1,3-雙(胺基甲基)環己烷、1,4-雙(胺基甲基)環己烷、鄰亞二甲苯二胺、間亞二甲苯二胺(MXDA)、對亞二甲苯二胺(PXDA)、前述通式(1-1)表示之化合物、及前述通式(1-2)表示之化合物構成之群組中之1種以上較佳,為選自於由1,2-雙(胺基甲基)環己烷、1,3-雙(胺基甲基)環己烷、1,4-雙(胺基甲基)環己烷、鄰亞二甲苯二胺、間亞二甲苯二胺、及對亞二甲苯二胺構成之群組中之1種以上更佳,考量耐熱性及耐候性的觀點,宜為選自於由1,2-雙(胺基甲基)環己烷、1,3-雙(胺基甲基)環己烷、及1,4-雙(胺基甲基)環己烷構成之群組中之1種以上尤佳,為1,3-雙(胺基甲基)環己烷又更佳。胺化合物(A)可單獨使用1種,亦可將2種以上組合使用。
(苯酚化合物(B)) 本發明之環氧樹脂硬化劑含有預定量的苯酚化合物(B)。藉此,可獲得兼顧低黏度與快速硬化性的環氧樹脂硬化劑及環氧樹脂組成物。 前述(A)成分單獨即可發揮作為環氧樹脂硬化劑之機能,但苯酚化合物(B)具有作為前述(A)成分之硬化促進劑的作用,故藉由摻合苯酚化合物(B),可獲得更具有快速硬化性的環氧樹脂硬化劑。據認為其理由為:由於來自(B)成分所具有之苯酚性羥基的質子,環氧樹脂之環氧基變得缺電子,該環氧基對於胺基的親電子性提高。 故,就苯酚化合物(B)而言,只要是在分子中具有至少1個苯酚性羥基之化合物,即可使用,並無特別限制。考量即使摻合量少亦可發揮效果的觀點、及與胺化合物(A)或後述環氧樹脂之混合性的觀點,宜為分子量未達1,000的苯酚化合物較佳,下列通式(2)表示之化合物更佳。
(式(2)中,R5
及R6
各自獨立地為OH基、或碳數1~4之烷基。j及k各自獨立地為0~5之整數,且j+k為1以上。多數個R5
、及多數個R6
可皆為相同也可彼此不同,但其中至少1者為OH基。Z為單鍵、碳數1~6之伸烷基、碳數2~6之亞烷基、碳數5~10之環伸烷基、碳數5~10之環亞烷基、碳數7~15之芳基伸烷基、碳數7~15之芳基亞烷基、-S-、-SO-、-SO2
-、-O-、-CO-、-C(CF3
)2
-、-CH(CF3
)-、-CF2
-、-CONH-、或-COO-。) 式(2)中,R5
及R6
宜為OH基較佳,j及k各自獨立地為0~2之整數,且j+k為1~3較佳。 式(2)中之Z中,碳數1~6之伸烷基可列舉亞甲基、伸乙基、三亞甲基、四亞甲基、六亞甲基,宜為碳數1~3之伸烷基較佳。碳數2~6之亞烷基可列舉亞乙基(-CH(CH3
)-)、亞丙基(-C(CH3
)2
-)等,宜為碳數2~3之亞烷基較佳。 碳數5~10之環伸烷基可列舉環戊烷二基、環己烷二基、環辛烷二基等。碳數5~10之環亞烷基可列舉環亞己基、3,5,5-三甲基環亞己基等。又,碳數7~15之芳基伸烷基及碳數7~15之芳基亞烷基的芳基部位,可列舉苯基、萘基、聯苯基、蒽基等成環碳數6~14之芳基。 上述中,Z宜為選自於由單鍵、碳數1~3之伸烷基、及碳數2~3之亞烷基構成之群組中之至少1種較佳,為單鍵、亞甲基、亞乙基、或亞丙基較佳,為亞甲基、亞乙基、或亞丙基更佳。
前述通式(2)表示之化合物之具體例,可列舉雙酚A[4,4’-(丙烷-2,2-二基)二苯酚]、雙酚F[雙(4-羥基苯基)甲烷]、雙酚AP[1,1-雙(4-羥基苯基)-1-苯基乙烷]、雙酚AF[2,2-雙(4-羥基苯基)六氟丙烷]、雙酚B[2,2-雙(4-羥基苯基)丁烷]、雙酚BP[雙(4-羥基苯基)二苯基甲烷]、雙酚S[雙(4-羥基苯基)碸]、雙酚E[1,1-雙(4-羥基苯基)乙烷]、苯乙烯化苯酚、羥基聯苯、二羥基聯苯等。該等中,考量對硬化劑之溶解性的觀點,宜為選自於由雙酚A[4,4’-(丙烷-2,2-二基)二苯酚]、雙酚F[雙(4-羥基苯基)甲烷]、雙酚E[1,1-雙(4-羥基苯基)乙烷]、及苯乙烯化苯酚構成之群組中之至少1種較佳,考量即使摻合量少亦可發揮效果的觀點,宜為選自於由雙酚A[4,4’-(丙烷-2,2-二基)二苯酚]、雙酚F[雙(4-羥基苯基)甲烷]、及雙酚E[1,1-雙(4-羥基苯基)乙烷]構成之群組中之至少1種更佳。 此外,苯乙烯化苯酚較佳為苯乙烯與苯酚之1:1加成物的下式(2-1)表示之化合物。就苯乙烯化苯酚而言,宜以下式(2-1)表示之化合物為主成分較佳,亦可含有苯乙烯與苯酚之2:1加成物、苯乙烯與苯酚之3:1加成物等多加成物。此外,本說明書中「主成分」係指令全部構成成分為100質量%時,其含量為50質量%以上,較佳為70質量%以上,更佳為80質量%以上(上限為100質量%)的成分。市售的苯乙烯化苯酚可列舉kumho Petrochemical製的「Kumanox-3110」、「Kumanox-3111」、「Kumanox-3114」、「Kumanox-3120」、「Kumanox-SP」等。
前述通式(2)表示之化合物以外,可作為該(B)成分使用之化合物,可列舉苯酚、甲酚、對苯二酚、1-萘酚、2-萘酚、間苯二酚、苯酚酚醛清漆樹脂、對異丙基苯酚、對第三丁基苯酚、壬基苯酚等。 苯酚化合物(B)可單獨使用1種,亦可將2種以上組合使用。
環氧樹脂硬化劑中之苯酚化合物(B)之含量,相對於前述(A)成分100質量份為8~35質量份。相對於前述(A)成分100質量份,該(B)成分之含量未達8質量份的話,無法獲得快速硬化性。又,超過35質量份的話,環氧樹脂硬化劑及含有該環氧樹脂硬化劑的環氧樹脂組成物變成高黏度,故尤其使用在利用高週期樹脂轉移造模法成形之CFRP時,成形性及生產性降低。進一步,獲得之CFRP的機械強度、耐熱性亦降低。考量上述的觀點,環氧樹脂硬化劑中之苯酚化合物(B)之含量,相對於前述(A)成分100質量份較佳為10質量份以上,更佳為15質量份以上,較佳為30質量份以下,更佳為25質量份以下。
本發明之環氧樹脂硬化劑,亦可含有前述(A)成分以外之公知的硬化劑、前述(B)成分以外之公知的硬化促進劑、公知的添加劑、及溶劑等。前述(A)成分以外之硬化劑,可列舉前述(A)成分以外的於分子內具有2個以上之胺基的多胺化合物或其改性體等。就該多胺化合物而言,例如,可列舉乙二胺、二伸乙三胺、三伸乙四胺、四伸乙五胺、五伸乙六胺、己二胺、2-甲基戊二胺、三甲基己二胺等鏈狀脂肪族多胺化合物;孟烯二胺(menthene diamine)、異佛酮二胺、降莰烷二胺、三環癸烷二胺、金剛烷二胺、二胺基環己烷、1,4-二胺基-2-甲基環己烷、1,4-二胺基-3,6-二乙基環己烷、二胺基二乙基甲基環己烷、3,3’-二甲基-4,4’-二胺基二環己基甲烷、4,4’-二胺基二環己基甲烷等具有脂環族結構之多胺化合物;苯二胺、二胺基二苯基甲烷、二胺基二苯碸等芳香族多胺化合物;N-胺基甲基哌、N-胺基乙基哌等具有雜環結構之多胺化合物;聚醚多胺化合物、及該等之曼尼希(Mannich)改性物、環氧改性物、麥克爾加成物、麥克爾加成・縮聚物、苯乙烯改性物、聚醯胺改性物等。該等可單獨使用1種,亦可將2種以上組合使用。例如使用N-胺基乙基哌作為前述(A)成分以外之多胺化合物的話,考量硬化速度、及可賦予獲得之環氧樹脂組成物韌性的觀點為較佳。 但,考量有效率地顯現本發明之效果的觀點,前述胺化合物(A)與前述苯酚化合物(B)之合計含量,相對於本發明之環氧樹脂硬化劑總量較佳為50質量%以上,更佳為70質量%以上,尤佳為80質量%以上,又更佳為85質量%以上,又尤佳為95質量%以上,特佳為99質量%以上(上限為100質量%)。
本發明之環氧樹脂硬化劑,於溫度25℃之黏度較佳為150mPa‧s以下,更佳為100mPa‧s以下,尤佳為60mPa‧s以下。於溫度25℃之黏度為150mPa‧s以下的話,與環氧樹脂的混合變得容易,使用在CFRP用途時生產性提高。環氧樹脂硬化劑之於溫度25℃之黏度的下限值並無特別限制,考量與環氧樹脂之混合性的觀點,較佳為10mPa‧s以上。
[環氧樹脂組成物] 本發明之環氧樹脂組成物係含有前述本發明之環氧樹脂硬化劑與環氧樹脂者。就該環氧樹脂而言,只要是具有與本發明之環氧樹脂硬化劑中之活性胺氫反應之環氧丙基的環氧樹脂,皆可使用,考量硬化物之機械強度優異的觀點,宜為在分子內含有芳香環或脂環族結構的環氧樹脂較佳,選自於由雙酚A型環氧樹脂及雙酚F型環氧樹脂構成之群組中之1種以上更佳,雙酚A型環氧樹脂尤佳。其中,考量為低黏度且能確保硬化物之機械強度的觀點,下列通式(3)表示之環氧樹脂特佳。
(式(3)中,R21
~R24
各自獨立地為碳數1~6之烷基,p、q、r、及s各自獨立地為0~4之整數。多數個R21
、多數個R22
、多數個R23
、及多數個R24
可皆為相同也可彼此不同。Y1
及Y2
各自獨立地為單鍵、-CH2
-、-CH(CH3
)-、或-C(CH3
)2
-。R25
為-CH2
CH(OH)-、或-CH(OH)CH2
-。m表示平均重複單元數,為0~0.2之數。) R21
~R24
宜為碳數1~4之烷基較佳,選自於由甲基、乙基、異丙基、及第三丁基構成之群組中之至少1種更佳。 p、q、r、及s宜皆為0~2之整數較佳,為0或1更佳,皆為0尤佳。 Y1
及Y2
宜為-CH2
-、或-C(CH3
)2
-較佳,為-C(CH3
)2
-更佳。 又,考量為低黏度且能確保硬化物之機械強度的觀點,m宜為0~0.15較佳,為0.01~0.1更佳。
又,考量兼顧環氧樹脂組成物之低黏度性及快速硬化性的觀點,環氧樹脂之環氧當量較佳為300g/當量以下,更佳為220g/當量以下,尤佳為200g/當量以下,又更佳為180g/當量以下。 環氧樹脂可單獨使用1種,亦可將2種以上倂用。
本發明之環氧樹脂組成物,進一步亦可因應用途含有填充材、塑化劑等改質成分、觸變劑等流動調整成分、顏料、調平劑、黏接賦予劑、彈性體微粒等其他成分。
就本發明之環氧樹脂組成物中之前述環氧樹脂硬化劑之含量而言,環氧樹脂硬化劑中之活性胺氫數相對於環氧樹脂中之環氧基數的比(環氧樹脂硬化劑中之活性胺氫數/環氧樹脂中之環氧基數)較佳為1/0.8~1/1.2,更佳為1/0.9~1/1.1,尤佳為1/1的量。 本發明之環氧樹脂組成物之於溫度40℃之黏度較佳為400mPa‧s以下,更佳為350mPa‧s以下,尤佳為300mPa‧s以下。於溫度40℃之黏度為400mPa‧s以下的話,使用在CFRP用途時生產性提高。環氧樹脂組成物之於溫度40℃之黏度的下限值並無特別限制,考量抑制CFRP之成形中由於雷諾數(Reynolds number)上升導致模具內產生亂流而於碳纖維產生混亂之情形的觀點,較佳為150mPa‧s以上。
本發明之環氧樹脂組成物,考量快速硬化性的觀點,於溫度80℃之凝膠化時間較佳為10分鐘以下,更佳為8.0分鐘以下,尤佳為7.0分鐘以下,又更佳為6.0分鐘以下。又,考量作業性的觀點,該凝膠化時間較佳為0.5分鐘以上,更佳為1.0分鐘以上。 上述凝膠化時間可使用流變計(rheometer),依實施例記載之方法進行測定。具體而言,使用流變計於溫度80℃、頻率1Hz、板間距離0.5mm測定環氧樹脂組成物之儲存彈性模量G’、損失彈性模量G’’,並將G’與G’’交叉的點作為凝膠化時間。
本發明之環氧樹脂組成物的製造方法並無特別限制,可將環氧樹脂硬化劑、環氧樹脂、及視需要之其他成分利用公知的方法及裝置進行混合而製造。環氧樹脂組成物所含之各成分的混合順序並無特別限制,可將胺化合物(A)與苯酚化合物(B)予以混合而製備環氧樹脂硬化劑後,使其和環氧樹脂混合,亦可將環氧樹脂硬化劑所含之胺化合物(A)及苯酚化合物(B)和環氧樹脂同時予以混合。
本發明之環氧樹脂組成物,考量改善使用在後述碳纖維強化複合材等時之成形品的生產性的觀點,宜為硬化物之熱變形溫度高者較佳。環氧樹脂組成物之硬化物的熱變形溫度高的話,使用在碳纖維強化複合材等時即使不將模具冷卻至低溫,亦可脫模,故能縮短成形週期。 針對例如使本發明之環氧樹脂組成物於120℃硬化120分鐘而獲得之10mm×80mm×厚度2mm之硬化物,利用熱變形溫度試驗裝置以支點間距離64mm、荷重1.8MPa、升溫速度120℃/hr之條件測得的熱變形溫度較佳為100℃以上,更佳為110℃以上,尤佳為120℃以上,又更佳為123℃以上。上述熱變形溫度可利用實施例記載之方法進行測定。
本發明之環氧樹脂硬化劑及含有該環氧樹脂硬化劑之環氧樹脂組成物,具有快速硬化性且為低黏度之特徵,故宜為纖維強化複合材用較佳,尤其為碳纖維強化複合材用較佳。 纖維強化複合材(FRP)係包含前述環氧樹脂組成物之硬化物、及強化纖維,可藉由使前述環氧樹脂組成物含浸於強化纖維,然後使該組成物硬化而獲得。就FRP而言,除包含前述環氧樹脂組成物之硬化物與強化纖維外,可進一步包含發泡材。 作為強化纖維,例如,可列舉玻璃纖維、碳纖維、硼纖維及金屬纖維等。強化纖維可單獨使用1種,亦可將2種以上倂用。該等中,考量獲得之複合材的強度及輕量性的觀點,宜為碳纖維較佳。 發泡材並無特別限制,例如可列舉由聚氯乙烯樹脂、聚胺酯樹脂、聚苯乙烯樹脂、聚烯烴樹脂、丙烯酸樹脂、苯酚樹脂、聚甲基丙烯醯亞胺樹脂、環氧樹脂等樹脂材料構成的發泡材。 以下,針對包含前述環氧樹脂組成物之硬化物、及碳纖維之碳纖維強化複合材進行說明。
[碳纖維強化複合材(CFRP)] 本發明之碳纖維強化複合材(CFRP)係包含前述環氧樹脂組成物之硬化物、及碳纖維,可藉由使前述環氧樹脂組成物含浸於碳纖維,然後使該組成物硬化而獲得。 就CFRP而言,除包含環氧樹脂組成物之硬化物與碳纖維外,可進一步包含碳纖維以外之強化纖維、前述發泡材。
(碳纖維) 使用在本發明之CFRP的碳纖維,可為以嫘縈、聚丙烯腈(PAN)等作為原料而製得者,亦可為以石油、煤炭等瀝青作為原料進行紡紗而製得者。又,也可使用將碳纖維之端材進行再利用的再生品、從CFRP去除樹脂而得之再生品的碳纖維。碳纖維的形態,例如可列舉單純將單纖絲或多纖絲以單方向或交互交錯的方式排列而成者、編織物等布帛、不織布或氈等各種形態。該等中,宜為單纖絲、布帛、不織布或氈的形態較佳,為布帛的形態更佳。
碳纖維之平均纖維徑宜為1~100μm較佳,為3~50μm更佳,為4~20μm尤佳。平均纖維徑為該範圍的話,加工變得容易,獲得之CFRP的彈性模量及強度優異。此外,平均纖維徑可利用掃描式電子顯微鏡(SEM)等進行觀察而測定。可隨機選取50根以上之纖維測定長度,並計算個數平均之平均纖維徑。
碳纖維之纖度宜為20~4,500tex較佳,為50~4,000tex更佳。纖度為該範圍的話,環氧樹脂組成物的含浸變得容易,獲得之複合材的彈性模量及強度優異。此外,纖度能以求取任意長度之長纖維之重量並換算成每1,000m之重量的方式求得。通常可理想地使用纖絲數500~60,000左右之碳纖維。
[碳纖維強化複合材之製造方法] 本發明之碳纖維強化複合材的製造方法並無特別限制,本發明之環氧樹脂硬化劑及環氧樹脂組成物為快速硬化性,故宜於即將成形前將環氧樹脂硬化劑、環氧樹脂予以混合,然後在較佳為10分鐘以內,更佳為5分鐘以內進行朝碳纖維的含浸及硬化較佳。 考量該觀點,本發明之碳纖維強化複合材的製造方法,較佳為具有依照低壓樹脂轉移造模法、中壓樹脂轉移造模法、高壓樹脂轉移造模法、壓縮樹脂轉移造模法、液狀壓縮造模法、液狀淋澆法、飛沫淋澆法、表面樹脂轉移造模法、預浸體壓縮造模法或液狀鑄塑法進行成形的步驟。該等成形法中,考量適用於高週期樹脂轉移造模法的觀點,低壓樹脂轉移造模法、中壓樹脂轉移造模法、或高壓樹脂轉移造模法為較佳,中壓樹脂轉移造模法或高壓樹脂轉移造模法更佳,考量成形速度的觀點,高壓樹脂轉移造模法尤佳。 此外,本說明書中,低壓樹脂轉移造模法中之「低壓」係指將環氧樹脂組成物之主劑的環氧樹脂、及環氧樹脂硬化劑進行壓送並混合時的壓送時之壓力為未達0.5MPa。同樣,中壓樹脂轉移造模法中之「中壓」係指上述壓力為0.5MPa以上、未達7MPa,高壓樹脂轉移造模法中之「高壓」係指上述壓力為7MPa以上、20MPa以下。 上述成形法中,可於即將成形前將本發明之環氧樹脂硬化劑、及環氧樹脂予以混合並使用,故該環氧樹脂組成物的適用期沒那麼必要。又,該環氧樹脂組成物為快速硬化性且為低黏度,故於模具內的填充及朝碳纖維的含浸快,可快速硬化,因而能大幅縮短成形時間。故,本發明之環氧樹脂硬化劑及環氧樹脂組成物尤其適合於上述成形法。又,藉由利用上述成形法,可適用本發明之環氧樹脂硬化劑及環氧樹脂組成物並以良好的生產性製造汽車用結構材、建材用等中~大型的CFRP。
高壓樹脂轉移造模法中,將環氧樹脂組成物之主劑的環氧樹脂、及環氧樹脂硬化劑予以混合的裝置,宜使用碰撞混合混合器較佳。例如,於上下一對之模具內配置碳纖維並密閉,將模具內進行減壓。然後,將環氧樹脂組成物之主劑的環氧樹脂、及環氧樹脂硬化劑填充到各自的儲槽,並分別從非常小的孔穴(孔口)高速吐出,在碰撞混合混合器之混合腔室內使其碰撞混合。將以此種方式製備之環氧樹脂組成物高壓注入模具內並使其含浸於碳纖維,然後,使環氧樹脂硬化。
低壓樹脂轉移造模法中,將環氧樹脂組成物之主劑的環氧樹脂、及環氧樹脂硬化劑予以混合的裝置,宜使用動態混合器較佳。動態混合器具備於表面有凹凸之筒狀的高速旋轉體。例如,將環氧樹脂組成物之主劑的環氧樹脂、及環氧樹脂硬化劑填充到各自的儲槽,分別送液至動態混合器,並藉由前述旋轉體將主劑與硬化劑之2液進行混合。將以此種方式製備之環氧樹脂組成物注入模具內並使其含浸於碳纖維,然後,使環氧樹脂硬化。考量環氧樹脂與環氧樹脂硬化劑之摻合比顯著不同的情況、裝置成本、裝置的節省空間化的觀點,低壓樹脂轉移造模法係為有利。 中壓樹脂轉移造模法中,將環氧樹脂組成物之主劑的環氧樹脂、及環氧樹脂硬化劑予以混合的裝置,宜使用靜態混合器較佳。靜態混合器係組裝有1個以上之由多數個混合元件構成之靜止型混合器的管型反應器。例如,將環氧樹脂組成物之主劑的環氧樹脂、及環氧樹脂硬化劑填充到各自的儲槽,分別送液至靜態混合器。使主劑與硬化劑之2液通過靜態混合器之扭轉元件(twisted element),並藉由分割、轉換、反轉等作用將2液混合。將以此種方式製備之環氧樹脂組成物注入模具內並使其含浸於碳纖維,然後,使環氧樹脂硬化。考量可將環氧樹脂組成物壓送至模具內,及裝置成本的觀點,中壓樹脂轉移造模法係為有利。
CFRP除包含前述環氧樹脂組成物之硬化物與碳纖維之外,還包含發泡材時,可於前述模具內配置碳纖維及發泡材,和前述同樣進行CFRP的製造。
液狀壓縮造模(LCM)法、液狀淋澆法亦可適當使用本發明之環氧樹脂硬化劑及環氧樹脂組成物。LCM法及液狀淋澆法中,係使環氧樹脂組成物流延至碳纖維上(CFRP進一步包含發泡材時,為碳纖維及發泡材上)並使其含浸,然後進行加熱壓縮使環氧樹脂硬化。
CFRP之成形中,將環氧樹脂組成物注入模具內,或使其含浸於碳纖維時的溫度,較佳為30~120℃,更佳為50~100℃。將環氧樹脂硬化劑與環氧樹脂從各自的儲槽進行供給並在即將成形前予以混合時,環氧樹脂硬化劑與環氧樹脂在混合時間點的溫度可個別設定。環氧樹脂硬化劑在混合時間點的溫度,考量抑制黏度上升的觀點,較佳為5~30℃,更佳為10~25℃。又,環氧樹脂在混合時間點的溫度可因應環氧樹脂的黏度適當調整,較佳為30~120℃,更佳為50~100℃。 環氧樹脂組成物朝碳纖維的含浸時間,考量成形性及生產性的觀點,較佳為0.1~15分鐘,更佳為0.2~10分鐘,尤佳為0.5~5分鐘。
環氧樹脂組成物之硬化溫度較佳為50~200℃,更佳為80~150℃,尤佳為100~150℃。硬化溫度為50℃以上的話,環氧樹脂的硬化充分進行,獲得之CFRP的機械特性優異。又,為200℃以下的話,模具溫度調整所花費的成本可較低。環氧樹脂組成物的硬化時間,考量成形性及生產性的觀點,較佳為0.1~15分鐘,更佳為0.2~10分鐘,尤佳為0.5~5分鐘。
使用本發明之環氧樹脂硬化劑或環氧樹脂組成物,並依上述成形法能以良好的生產性製造CFRP。本發明之碳纖維強化複合材宜為汽車用結構材、建材,尤其為汽車用結構材較佳。汽車用結構材可列舉保險桿、擾流板、整流罩、前格柵(front grille)、飾板、罩蓋、行李箱蓋、擋泥板(fender panel)、門板、車頂板、儀表盤(instrument panel)、門飾板(door trim)、艉飾板(quarter trim)、車頂襯裏(roof lining)、柱飾板(pillar garnish)、底板裝飾板(deck trim)、後車廂板(tonneau board)、雜物盤(package tray)、儀表板、中控台什物箱(console box)、車門下框(kicking plate)、開關板(switch base)、座椅靠背板、座椅骨架(seat frame)、扶手、遮陽板、進氣歧管、引擎頂蓋(engine head cover)、引擎底蓋(engine under cover)、濾油器殼體(oil filter housing)等。 [實施例]
以下舉實施例及比較例對本發明進行詳細地說明,但本發明並不限定於下列實施例。此外,環氧樹脂硬化劑的各種評價及測定係依照以下方法進行。
(黏度) 使用E型黏度計「TVE-22H型黏度計 錐板型」(東機產業(股)製)測定環氧樹脂硬化劑及環氧樹脂組成物的黏度。環氧樹脂硬化劑於25℃實施測定,環氧樹脂組成物於40℃實施測定。黏度越低,成形時之填充性越高,表示成形性越良好。
(凝膠化時間) 使用流變計「ARES-G2」(TA Instruments製)進行評價。在加溫至80℃之鋁板間填充環氧樹脂組成物,並於溫度80℃、頻率1Hz、板間距離0.5mm測定儲存彈性模量G’、損失彈性模量G’’,並將G’與G’’交叉的點作為凝膠化時間。凝膠化時間越短,表示越為快速硬化性。
(熱變形溫度(HDT)) 在塗布有脫模劑「Frekote700NC」(Henkel公司製)之2片鋁板之間,夾入Φ2mm之聚矽氧橡膠圓繩,利用C型夾(C-clamp)進行固定而製成鑄模。於加溫至80℃之鑄模,利用無針的塑膠注射器澆注經脫泡之環氧樹脂組成物約1分鐘,並於120℃之熱風乾燥機中使其硬化120分鐘,獲得由環氧樹脂組成物之硬化物構成的厚度2mm之澆注板。 將獲得之澆注板進行切削加工以製作10mm×80mm×厚度2mm之試驗片,利用HDT試驗裝置「Auto-HDT3D-2」(東洋精機製作所(股)製)於支點間距離64mm、荷重1.8MPa、升溫速度120℃/hr之條件測定熱變形溫度。
(拉伸試驗) 利用和前述同樣的方法澆注環氧樹脂組成物,獲得由環氧樹脂組成物之硬化物構成的厚度2mm之澆注板。將獲得之澆注板進行切削加工以製作JIS K7162-1A型啞鈴形狀的試驗片,使用該試驗片進行拉伸試驗。利用拉伸試驗機(東洋精機製作所(股)製「Strograph AP-III」、荷重元(load cell)容量20kN),於測定溫度23℃、夾具間距離115mm、標線間距離50mm、以彈性模量測定區域之衝程速度為1mm/分鐘、強度測定區域之衝程速度為5mm/分鐘之條件實施拉伸試驗,測定拉伸彈性模量、最大點強度、最大點應變、及斷裂點應變。
(夏比衝擊試驗(Charpy impact test)) 利用和前述同樣的方法針對環氧樹脂組成物之硬化物製作10mm×80mm×厚度2mm之無缺口的試驗片。利用數位式夏比衝擊試驗機「DC-UB」(東洋精機製作所(股)製),於溫度23℃、相對濕度50%RH進行夏比衝擊試驗,求出夏比衝擊強度。
實施例1(環氧樹脂硬化劑及環氧樹脂組成物之製備) 相對於係胺化合物(A)之1,3-雙(胺基甲基)環己烷(1,3-BAC,三菱瓦斯化學(股)製,順式/反式比=77/23)100g,摻合作為苯酚化合物(B)之雙酚A(4,4’-(丙烷-2,2-二基)二苯酚,關東化學(股)製)10g並混合,獲得環氧樹脂硬化劑。 進一步,以使環氧樹脂硬化劑中之活性胺氫數與係主劑之環氧樹脂中之環氧基數成為等莫耳的方式,將該環氧樹脂硬化劑、及係主劑之雙酚A型液狀環氧樹脂(「jER825」,三菱化學(股)製)進行摻合並混合,以製備環氧樹脂組成物。 針對獲得之環氧樹脂硬化劑及環氧樹脂組成物,利用前述方法進行評價。結果顯示於表1。此外,環氧樹脂jER825係以下列結構式表示,環氧當量為175g/當量,m=0.035。
上述式中,R25
為-CH2
CH(OH)-、或-CH(OH)CH2
-。
實施例2~4 將環氧樹脂硬化劑中之雙酚A之含量變更為表1所示的量,除此以外,以和實施例1同樣的方法製備環氧樹脂硬化劑及環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
實施例5 使用以下列結構式表示之化合物為主成分之苯乙烯化苯酚(kumho Petrochemical製「Kumanox-3110」)替代雙酚A作為苯酚化合物(B),除此以外,以和實施例3同樣的方法製備環氧樹脂硬化劑及環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
實施例6 使用間亞二甲苯二胺(MXDA,三菱瓦斯化學(股)製)替代1,3-BAC作為胺化合物(A),除此以外,以和實施例1同樣的方法製備環氧樹脂硬化劑及環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
實施例7 使用間亞二甲苯二胺(MXDA,三菱瓦斯化學(股)製)替代1,3-BAC作為胺化合物(A),除此以外,以和實施例3同樣的方法製備環氧樹脂硬化劑及環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
實施例8 使用間亞二甲苯二胺(MXDA、三菱瓦斯化學(股)製)替代1,3-BAC作為胺化合物(A),除此以外,以和實施例4同樣的方法製備環氧樹脂硬化劑及環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
實施例9 使用80g的1,3-BAC作為胺化合物(A),使用20g的N-胺基乙基哌(AEP,東曹(股)製)作為(A)以外之胺化合物。相對於該等胺化合物100g,摻合20g的作為苯酚化合物(B)之雙酚A(4,4’-(丙烷-2,2-二基)二苯酚,關東化學(股)製)並進行混合,獲得環氧樹脂硬化劑。使用該環氧樹脂硬化劑以和實施例1同樣的方法製備環氧樹脂組成物,針對環氧樹脂硬化劑及環氧樹脂組成物利用前述方法進行評價。結果顯示於表1。
實施例10 使用雙酚E(1,1-雙(4-羥基苯基)乙烷,東京化成工業(股)製)替代雙酚A作為苯酚化合物(B),除此以外,以和實施例3同樣的方法製備環氧樹脂硬化劑及環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
實施例11 使用雙酚F(雙(4-羥基苯基)甲烷,東京化成工業(股)製)替代雙酚A作為苯酚化合物(B),除此以外,以和實施例3同樣的方法製備環氧樹脂硬化劑及環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
比較例1 未摻合苯酚化合物(B),除此以外,以和實施例1同樣的方法製備環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
比較例2~3 將環氧樹脂硬化劑中之雙酚A之含量變更為表1所示的量,除此以外,以和實施例1同樣的方法製備環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
比較例4 未摻合苯酚化合物(B),除此以外,以和實施例6同樣的方法製備環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
比較例5 使用異佛酮二胺(IPDA)替代1,3-BAC作為胺化合物,除此以外,以和比較例1同樣的方法製備環氧樹脂硬化劑及環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
比較例6 使用異佛酮二胺(IPDA)替代1,3-BAC作為胺化合物,除此以外,以和實施例1同樣的方法製備環氧樹脂硬化劑及環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
比較例7 使用異佛酮二胺(IPDA)替代1,3-BAC作為胺化合物,除此以外,以和實施例3同樣的方法製備環氧樹脂硬化劑及環氧樹脂組成物,並利用前述方法進行評價。結果顯示於表1。
比較例8 未摻合苯酚化合物(B),除此以外,以和實施例9同樣的方法製備環氧樹脂組成物,利用前述方法進行評價。結果顯示於表1。
由表1可知:本發明之環氧樹脂硬化劑及環氧樹脂組成物黏度低,且為快速硬化性。因此,適合於利用高週期樹脂轉移造模法等成形法製造各種成形體。又,可知如實施例1~4所示般,本發明之環氧樹脂組成物之硬化物,相較於使用不含苯酚化合物(B)之環氧樹脂硬化劑的比較例1,雖維持同等的機械特性,但關於拉伸彈性模量及夏比衝擊強度,有比起比較例1更為改善的傾向。
(CFRP之製造及脫模性評價) 利用於室溫之手工積層成形使實施例1~4、實施例9~11、比較例1及5之環氧樹脂組成物含浸於碳纖維織物(東麗(股)製「CO6343」,T300平織布,3K,198g/m2
,0.25mm厚,4ply),以製作CFRP基材。然後,將CFRP基材載置於在烘箱內預先加熱至120℃之鋁上下模具,迅速關閉模具,評價經過預定時間後的硬化行為及脫模性。 直到CFRP基材完全硬化並可脫模為止的時間顯示於表2。該時間越短則可在越短時間內硬化及脫模,表示CFRP的生產性優異。
由表2可知:本案實施例之環氧樹脂硬化劑及利用該環氧樹脂硬化劑之環氧樹脂組成物,即使適用於CFRP用途時亦為快速硬化性,直到可脫模為止的時間快,故CFRP的生產性亦優異。 [產業上利用性]
根據本發明,可提供能利用高週期樹脂轉移造模法等以良好的生產性製造汽車用結構材、建材等之CFRP的為快速硬化性且低黏度的環氧樹脂硬化劑及環氧樹脂組成物。將該環氧樹脂組成物作為CFRP的基質樹脂使用的話,朝碳纖維之含浸性優異,且為快速硬化性,故直到可從模具脫模的時間亦短,能改善CFRP的生產性。
Claims (13)
- 一種環氧樹脂硬化劑,含有下列通式(1)表示之胺化合物(A)與苯酚化合物(B),該(B)成分為分子量未達1,000的苯酚化合物;相對於該(A)成分100質量份,該(B)成分之含量為8~35質量份;該胺化合物(A)與該苯酚化合物(B)之合計含量相對於環氧樹脂硬化劑總量為80質量%以上且100質量%以下;R1HN-H2C-A-CH2-NHR2 (1)式(1)中,R1及R2各自獨立地為氫原子、或碳數1~6之胺烷基;A為伸苯基。
- 一種環氧樹脂硬化劑,含有下列通式(1)表示之胺化合物(A)與苯酚化合物(B),該(B)成分為分子量未達1,000的苯酚化合物;相對於該(A)成分100質量份,該(B)成分之含量為8~35質量份;R1HN-H2C-A-CH2-NHR2 (1)式(1)中,R1及R2各自獨立地為氫原子、或碳數1~6之胺烷基;A為伸環己基。
- 如申請專利範圍第1或2項之環氧樹脂硬化劑,其中,該通式(1)中,R1及R2皆為氫原子。
- 如申請專利範圍第4項之環氧樹脂硬化劑,其中,該苯酚化合物(B)係選自於由4,4’-(丙烷-2,2-二基)二苯酚、雙(4-羥基苯基)甲烷、1,1-雙(4-羥基苯基)乙烷、及苯乙烯化苯酚構成之群組中之至少1種。
- 一種環氧樹脂組成物,含有如申請專利範圍第1至5項中任一項之環氧樹脂硬化劑,及環氧樹脂。
- 如申請專利範圍第6項之環氧樹脂組成物,其中,該環氧樹脂係在分子內含有芳香環或脂環族結構之環氧樹脂。
- 如申請專利範圍第6至8項中任一項之環氧樹脂組成物,其於溫度40℃之黏度為400mPa‧s以下。
- 如申請專利範圍第6至8項中任一項之環氧樹脂組成物,係碳纖維強化複合材用。
- 一種碳纖維強化複合材,含有如申請專利範圍第6至10項中任一項之環氧樹脂組成物之硬化物,及碳纖維。
- 如申請專利範圍第11項之碳纖維強化複合材,係汽車用結構材。
- 一種碳纖維強化複合材之製造方法,係製造如申請專利範圍第11或12項之碳纖維強化複合材之方法,具有依照低壓樹脂轉移造模法(low pressure resin transfer molding)、中壓樹脂轉移造模法(middle pressure resin transfer molding)、高壓樹脂轉移造模法(high pressure resin transfer molding)、壓縮樹脂轉移造模法(compression resin transfer molding)、液狀壓縮造模法、液狀淋澆法(liquid lay down method)、飛沫淋澆法(spray lay down method)、表面樹脂轉移造模法、預浸體壓縮造模法或液狀鑄塑法進行成形之步驟。