TWI616494B - 頂塗層組成物、以其塗佈基材之方法及基材 - Google Patents
頂塗層組成物、以其塗佈基材之方法及基材 Download PDFInfo
- Publication number
- TWI616494B TWI616494B TW105132941A TW105132941A TWI616494B TW I616494 B TWI616494 B TW I616494B TW 105132941 A TW105132941 A TW 105132941A TW 105132941 A TW105132941 A TW 105132941A TW I616494 B TWI616494 B TW I616494B
- Authority
- TW
- Taiwan
- Prior art keywords
- coating composition
- top coating
- radiation
- resin
- curable
- Prior art date
Abstract
本發明係關於阻燃且耐碘染色之頂塗層組成物，其包含：熱塑性組份，其包括乙烯乙酸乙烯酯樹脂與氯乙酸乙烯酯樹脂中之一者或兩者；及可輻射固化之組份，其包括一或多種丙烯酸系寡聚物及一或多種丙烯酸系單體。本發明進一步係關於利用該頂塗層組成物塗佈基材之至少一部分之方法及至少部分地經該頂塗層組成物塗佈之基材。本發明進一步揭示阻燃性頂塗層組成物，其包含氧化鋁顏料；及可輻射固化之組份，該可輻射固化之組份包括一或多種丙烯酸系寡聚物及一或多種丙烯酸系單體。
Description
本發明係關於頂塗層組成物，尤其係關於具有良好耐碘染色性及阻燃性之高固體可輻射固化之頂塗層組成物。本發明進一步係關於利用該頂塗層組成物塗佈基材之方法，及至少部分地經該頂塗層組成物塗佈之基材。
目前，各種天然或合成基材廣泛用作公共場所(例如，機場、火車站、酒店、辦公室或工廠建築物及醫院)或私人住宅之建築或裝飾材料(例如，樓面覆蓋物、面板或諸如此類)。為了改良表面性能或美學外觀，基材常常具有在其表面上施加之功能性及/或裝飾性塗層，例如底漆、頂塗層等。 習用頂塗層可主要包括基於溶劑(SB)之頂塗層、水性(WB)頂塗層、高固體含量(或甚至100%固體)之UV頂塗層、粉末頂塗層等。在該等中，高固體含量之頂塗層視為環境友好型產品，此乃因其含有極少或甚至不含揮發性有機化合物(VOC)。此外，高固體含量之頂塗層通常具有良好撓性及延展性。隨著公眾環境保護意識不斷提高，高固體含量之頂塗層在市場上變得愈來愈受歡迎。 此外，自安全性觀點來看，期望頂塗層(尤其在易燃基材(例如塑膠、木材或複合基材)之表面上使用之彼等)具阻燃性，以改變基材之燃燒性質或增加其耐火性以防止火災發生或阻止火蔓延。而且，對於在如醫院、診所等場所使用之基材，進一步期望頂塗層具有良好耐碘染色性，此乃因該等場所中廣泛使用高度可滲透之碘酊，且因此其將不可避免地滴落至(例如)地板、桌面、牆壁或諸如此類上，由此導致基材上之碘染色。 因此，業內持續需要具有良好阻燃性及良好耐碘染色性之新穎高固體含量之頂塗層。
為解決上述及其他問題，本發明提供包含熱塑性組份與可輻射固化之組份之組合之新穎高固體含量之可輻射固化之塗層組成物，其具有良好阻燃性及耐碘染色性。 本發明提供高固體含量之阻燃且耐碘染色之可輻射固化之頂塗層組成物，其包含： (a) 熱塑性組份，其包括乙烯乙酸乙烯酯(EVA)樹脂與氯乙酸乙烯酯樹脂中之一者或兩者；及 (b) 可輻射固化之組份，其包括一或多種丙烯酸系寡聚物及一或多種丙烯酸系單體。 在一個態樣中，EVA樹脂可具有在500至50,000範圍內之重量平均分子量(Mw
)，如藉由GPC (凝膠滲透層析)所量測。 在另一態樣中，EVA樹脂在其主鏈中可包含5重量%至45重量%之乙酸乙烯酯單元。 在另一態樣中，EVA樹脂可未經修飾或經修飾。舉例而言，EVA樹脂可經熱塑性塑膠或可輻射固化之樹脂(例如聚氯乙烯(PVC))修飾。 在另一態樣中，氯乙酸乙烯酯樹脂可具有在500至50,000範圍內之Mw
，如藉由GPC所量測。 在另一態樣中，氯乙酸乙烯酯樹脂在其主鏈中可包含3重量%至38重量%之乙酸乙烯酯單元。 在另一態樣中，氯乙酸乙烯酯樹脂可未經修飾或經修飾。舉例而言，氯乙酸乙烯酯樹脂可經苯乙烯及/或馬來酸酐修飾。 在另一態樣中，可輻射固化之組份亦可包含一或多種光起始劑。 在另一態樣中，可輻射固化之頂塗層組成物可包含選自氧化鋁(Al2
O3
)、二氧化矽(SiO2
)或其任何混合物之顏料。 在另一態樣中，基於頂塗層組成物之總重量，可輻射固化之頂塗層組成物可包含： (a) 1重量%至95重量%之熱塑性組份； (b) 5重量%至99重量%之可輻射固化之組份；及 (c) 0重量%至60重量%之顏料。 在另一態樣中，基於熱塑性組份之總重量，熱塑性組份可包含： (a-1) 0重量%至100重量%之EVA樹脂；及 (a-2) 0重量%至100重量%之氯乙酸乙烯酯樹脂。 在另一態樣中，基於可輻射固化之組份之總重量，可輻射固化之組份可包含： (b-1) 5重量%至98重量%之丙烯酸酯寡聚物；及/或 (b-2) 2重量%至95重量%之單體，及 (b-3) 0重量%至10重量%之光起始劑。 本發明進一步提供塗佈基材之至少一部分之方法，其包含：利用根據本發明之可輻射固化之頂塗層組成物塗佈基材；及利用輻射固化頂塗層組成物。 本發明進一步提供至少部分地經根據本發明之可輻射固化之頂塗層組成物塗佈之基材。 本發明進一步提供高固體含量之阻燃性可輻射固化之頂塗層組成物，其包含(a) 顏料，其選自由氧化鋁(Al2
O3
)、二氧化矽(SiO2
)及其任何混合物組成之群；及(b) 可輻射固化之組份，其包括丙烯酸系寡聚物與丙烯酸系單體中之一者或兩者。
除非另有指示，否則本文中所使用之所有術語具有以下定義。除非另有指示，否則本文中所使用之所有份數及百分比係基於重量。 本發明提供高固體含量之阻燃且耐碘染色之可輻射固化之頂塗層組成物，其包含： (a) 熱塑性組份，其包括乙烯乙酸乙烯酯(EVA)樹脂及氯乙酸乙烯酯樹脂中之一者或兩者；及 (b) 可輻射固化之組份，其包括一或多種丙烯酸系寡聚物及一或多種丙烯酸系單體。 如本文中所用，術語「固體含量」係指乾燥組份關於乳液或塗層之總組份之質量百分比，且術語「高固體含量」意指樹脂或組成物包含50%至100%之固體組份。換言之，根據塗料之可流動性及黏度要求，若需要，則樹脂或組成物可經調整以不含溶劑(例如，水性或非水性溶劑，例如水、揮發性有機溶劑等)，或含有一定量(例如0%至50%)溶劑。因此，在態樣中，根據本發明之頂塗層組成物可係100%固體，且在另一態樣中，根據本發明之頂塗層組成物可含有(例如) 50 wt%、60 wt%、70 wt%、80 wt%或甚至90 wt%之固體。因此，根據本發明之頂塗層組成物傾向於展現相對較低之毒性及火災風險，且可滿足嚴格的頂塗層工業揮發性有機化合物(VOC)之VOC排放標準(Emission Standard of Volatile Organic Compounds (VOC) for Topcoat Industry
VOC)，且因此其係環境友好型或「綠色」產品。 如本文中所用，術語「可輻射固化」意指液體樹脂或組成物中之低分子量材料(例如預聚物、寡聚物及/或單體)可藉助輻射固化技術(亦稱為「能量固化技術」，例如藉由UV或高能量電子束(EB)輻射固化)經歷聚合、共聚或交聯以便產生高分子量材料。輻射固化技術具有包括快速固化、低能量消耗、低溶劑殘留等之優點。 如本文中所用，術語「頂塗層」係指主要由一或多層底漆及一或多層頂塗層組成之多層塗層系統中之最外塗層。因此，與底漆相比，頂塗層應展現優異性能。舉例而言，頂塗層應具有良好之耐濕氣性、耐氣候性及耐化學試劑性(例如，碘酊)及良好阻燃性，且對下伏層提供保護。一般而言，頂塗層之表面性質主要取決於塗層中所用之樹脂(即，可聚合材料)。通常，根據本發明之頂塗層組成物可與任何習用底漆組合使用，只要其彼此相容即可。或者，根據本發明之頂塗層組成物可直接施加至任何基材之表面上，而無需預先施加任何底漆。 如前文所述，根據本發明之頂塗層組成物可包含熱塑性組份作為必需膜形成材料中之一者。此處，術語「熱塑性組份」係指可藉由空氣乾燥(例如，在高溫(例如，50℃)下)固化之樹脂或樹脂組成物。適用於本發明中之熱塑性組份可包含EVA樹脂與氯乙酸乙烯酯樹脂中之一者或兩者。熱塑性組份對於塗層之性能甚為關鍵，該等性能包括(但不限於)耐碘染色性、阻燃性、硬度及光澤。 此處，術語「乙烯乙酸乙烯酯(EVA)樹脂」係指藉由乙烯單體與乙酸乙烯酯單體共聚所形成之寡聚物；且「氯乙酸乙烯酯樹脂」 (亦稱為氯醋樹脂(vinisol))係指藉由氯乙烯單體與乙酸乙烯酯單體共聚所形成之寡聚物。EVA樹脂及氯乙酸乙烯酯樹脂可單獨使用，或其可以任何比率組合使用。EVA樹脂及/或氯醋樹脂可賦予頂塗層組成物耐碘染色及阻燃性質，但不會實質上影響可輻射固化組份之傳統優點，例如，環境友好及快速固化性質。 在一個態樣中，適用於本發明中之EVA樹脂可具有500或更大之重量平均分子量(Mw
)，如藉由GPC所量測。舉例而言，EVA樹脂可具有2,000或更大之Mw
。此外，EVA樹脂可具有50,000或更小之Mw
，或可具有10,000之Mw
。一般而言，Mw
大於50,000之EVA樹脂將賦予液體塗層極高之黏度，且具有較小Mw
(例如，小於500之Mw
)之EVA樹脂將為固化膜帶來差的硬度及撓性。 在另一態樣中，適用於本發明之EVA樹脂在其主鏈中可包含5%或更多之乙酸乙烯酯單元，例如，在其主鏈中20%或更多之乙酸乙烯酯單元；且此外，EVA樹脂在其主鏈中可包含45 wt%或更少之乙酸乙烯酯單元，例如，在其主鏈中32%或更少之乙酸乙烯酯單元。通常，併入EVA樹脂主鏈內之乙酸乙烯酯單元有助於改良溶解性、增塑效應、撓性、透明度及任何填料之併入能力，然而其對於拉伸強度、硬度、耐化學品性或諸如此類通常不利。因此，慮及EVA樹脂之各種性質間之平衡，建議在EVA樹脂之主鏈中包含5%至24% (例如，20%至32%)之乙酸乙烯酯單元。 在另一態樣中，適用於本發明之EVA樹脂可未經修飾或經修飾。術語「經修飾」意指藉由利用活性化學試劑處理樹脂來改變樹脂之物理及/或化學性質。舉例而言，EVA樹脂可經熱塑性塑膠或可輻射固化之樹脂(例如，聚氯乙烯(PVC))修飾。 在另一態樣中，適用於本發明之氯醋樹脂可具有500或更大之Mw
，如藉由GPC所量測，例如，2,000或更大。此外，氯醋樹脂可具有50,000或更小、例如10,000之Mw
。Mw
大於50,000之氯醋樹脂將賦予液體塗層更高之黏度及差的可溶性；而Mw
小於500之氯醋樹脂將對固化膜造成差的硬度及撓性。 在另一態樣中，適用於本發明之氯醋樹脂在其主鏈中可包含3%或更多之乙酸乙烯酯單元，例如5%或更多，例如14%或更多。此外，氯醋樹脂在其主鏈中可包含45%或更少之乙酸乙烯酯單元，例如38%或更少，例如25%或更少。通常，併入氯醋樹脂主鏈內之乙酸乙烯酯單元有助於改良可溶性、增塑效應、撓性、透明度及填料之併入能力；而其對於拉伸強度、硬度及耐化學品性通常不利。因此，慮及氯醋樹脂之各種性質間之平衡，建議在氯醋樹脂之主鏈中包含3%至45% (例如，5%至38%、或14%至25%)之乙酸乙烯酯單元。 在另一態樣中，適用於本發明之氯醋樹脂可未經修飾或經修飾。舉例而言，氯醋樹脂可經(例如)苯乙烯馬來酸酐修飾，或氯醋樹脂可經0.5%至2%之苯乙烯馬來酸酐修飾，此可改良固化膜之黏著性。 基於根據本發明之頂塗層組成物之總重量，熱塑性組份通常可以5 wt%或更多(例如，10 wt%或更多，例如20 wt%)之量存在於根據本發明之頂塗層組成物中。此外，基於本發明之頂塗層組成物之總重量，熱塑性組份通常可以95 wt%或更少(例如，80 wt%或更少、60 wt%或更少、50 wt%或更少或40 wt%或更少)之量存在於根據本發明之頂塗層組成物中。由於具有相對較高Mw
之熱塑性組份(即，EVA樹脂及/或氯醋樹脂)不參與化學輻射固化反應，因此適當百分比(例如，滿足上述上限及下限之彼等)之熱塑性組份有助於降低輻射交聯密度，藉此改良黏著性及抗翹曲性能。此外，(例如)超過上述上限之熱塑性組份可導致不足之輻射交聯密度，並因此將對固化膜之機械阻力具有不利影響。特別地，以適宜量(例如，在上述範圍內之量)使用之熱塑性組份可有助於改良耐碘染色及阻燃性質。與此相比，若熱塑性組份之量不足(例如，少於上述下限之量)，則將不利地影響耐碘染色性及阻燃性。 適用於本發明之EVA樹脂及氯乙酸乙烯酯樹脂可商業購得，或可根據此項技術中之習用技術合成。可商業購得之EVA樹脂之典型實例可包含(但不限於) DuPont ELVAX 150W及諸如此類。可商業購得之氯乙酸乙烯酯樹脂之典型實例可包含(但不限於) Guangzhou lu’ou T32氯醋樹脂、Wacker vinnol E22/48A或諸如此類。 如前文所述，根據本發明之頂塗層組成物進一步包含可輻射固化組份。此處，術語「可輻射固化組份」係指包含一或多種寡聚物及/或一或多種單體之組成物，其在輻射(例如，UV或EB輻射)下可經交聯形成網狀結構。就實際需要(例如，黏度及諸如此類)而言，可輻射固化組份可僅包含一或多種寡聚物或一或多種單體或其組合。根據本發明之頂塗層組成物之可輻射固化組份在固化製程期間提供化學交聯網絡。 如前所述，根據本發明之可輻射固化之組份包含一或多種丙烯酸系寡聚物。術語「寡聚物」係指在其主鏈中包含相對較小量之重複單元之聚合物，例如，包含5至50個重複單元之彼等，且術語「丙烯酸系寡聚物」係指包含一或多個丙烯酸系重複單元(例如，丙烯酸、丙烯醯胺、丙烯酸酯、甲基丙烯酸酯及諸如此類)之寡聚物。若需要，適用於本發明之丙烯酸系寡聚物可進一步包含一或多個衍生自其他可聚合單體(例如，烯系單體及諸如此類)之重複單元。在固化製程期間，丙烯酸系寡聚物可在輻射(例如，UV或EB)下交聯以形成網狀結構。 在態樣中，適用於本發明之丙烯酸系寡聚物可具有500或更大(例如，1,000或更大)之Mw
。此外，適用於本發明之丙烯酸系寡聚物可具有20,000或更小(例如，10,000或更小)之Mw
。 在另一態樣中，適用於本發明之丙烯酸系寡聚物可包含(但不限於)乙酸乙烯酯丙烯酸酯、聚胺基甲酸酯丙烯酸酯、聚酯丙烯酸酯、環氧丙烯酸酯及諸如此類。通常，具有高官能度及輻射交聯密度之丙烯酸酯寡聚物可用作丙烯酸系寡聚物，此乃因其可有助於耐碘染色性及阻燃性。 適用於本發明之丙烯酸系寡聚物可商業購得，或可根據此項技術中之習用技術合成。可商業購得之丙烯酸酯樹脂之典型實例可包含(但不限於) PPG胺基甲酸酯丙烯酸酯，2官能之聚胺基甲酸酯丙烯酸酯；Jiangsu Sanmu SM6205，2官能之聚胺基甲酸酯丙烯酸酯；Guangdong JESIDA DSP‐552F，6官能之經氟修飾之聚胺基甲酸酯；ETERNAL 6196‐100，15官能之聚胺基甲酸酯丙烯酸酯；ETERNAL ETERCURE DR‐E532，2官能之聚酯丙烯酸酯；Guangdong Wuxing EA8204，2官能之聚酯丙烯酸酯；Jiangsu Sanmu SM6105‐75Y，雙酚A環氧丙烯酸酯；及諸如此類。 如前所述，根據本發明之可輻射固化之組份進一步包含一或多種丙烯酸系單體。術語「單體」係指小分子之集合，其可藉由聚合或共聚或縮聚與其自身或其他分子反應以形成(共)聚合物。適用於本發明之丙烯酸系單體可包含(但不限於)丙烯酸異莰基酯(IBOA)、丙烯酸異癸基酯(IDA)、三羥甲基丙烷三丙烯酸酯(TMPTA)、新戊四醇三丙烯酸酯(PETA)、新戊四醇四丙烯酸酯(PETTA)及諸如此類。丙烯酸系單體(例如，IBOA、IDA或諸如此類)可有助於頂塗層組成物之耐碘染色性質。 通常，基於根據本發明之頂塗層組成物之總重量，可輻射固化之組份可以5 wt%或更多(例如，20 wt%或更多、40 wt%或更多、50 wt%或更多或60 wt%或更多)之量存在於根據本發明之頂塗層組成物中。此外，可輻射固化之組份可以頂塗層組成物之95 wt%或更少(例如，90 wt%或更少，例如80重量%或更少)之量存在於根據本發明之頂塗層組成物中。單體(例如，IBOA、IDA或諸如此類)可有助於耐碘染色性；且此外，其可用來調整黏度，同時不像溶劑那樣不會降低樹脂之固體含量。此外，若單體之用量不足，則碘染色性能將受影響；且若單體之用量過量，則固化膜之撓性可較差，且UV固化反應可受影響，由此賦予不適當之黏度。 在一態樣中，基於可輻射固化之組份之總重量，丙烯酸系寡聚物可以0 wt%或更多(例如，5 wt%或更多、15 wt%或更多或25 wt%或更多)之量存在於根據本發明之可輻射固化之組份中。此外，基於可輻射固化之組份之總重量，丙烯酸系寡聚物可以100 wt%或更少、85 wt%或更少、65 wt%或更少、45 wt%或更少或35%或更少之量存在於根據本發明之可輻射固化之組份中。舉例而言，基於可輻射固化之組份之總重量，丙烯酸系寡聚物可以5 wt%至95 wt%、10 wt%至70 wt%、15 wt%至50 wt%或25 wt%至35 wt%之量存在於根據本發明之可輻射固化之組份中。若丙烯酸系寡聚物之量太低(例如，少於5 wt%)，則塗層之輻射固化反應及固化膜之機械阻力可受影響；且若丙烯酸系寡聚物之量太高(例如，大於98 wt%)，則將不利地影響頂塗層組成物之整體性能。若丙烯酸酯樹脂佔少於5%，則可不利地影響塗層之輻射固化反應及固化膜之機械阻力性能。由於EVA樹脂、無機填料、光起始劑及一些添加劑對於塗層甚為關鍵，故不建議丙烯酸酯之百分比超過98%。 在另一態樣中，基於可輻射固化之組份之總重量，單體可以0 wt%或更多(例如，15 wt%或更多)之量存在於根據本發明之可輻射固化之組份中。此外，基於可輻射固化之組份之總重量，單體可以100 wt%或更少(例如，95 wt%或更少)之量存在於根據本發明之可輻射固化之組份中。舉例而言，基於可輻射固化之組份之總重量，單體可以10 wt%至95 wt% (例如，20 wt%至60 wt%或30 wt%至40 wt%)之量存在於根據本發明之可輻射固化之組份中。若單體之量太高(例如，大於95 wt%)，則可不利地影響塗層之輻射固化反應及/或固化膜之撓性。 在態樣中，基於可輻射固化之組份之總重量，根據本發明之可輻射固化之組份可包含： (b-1) 5重量%至98重量%之丙烯酸酯寡聚物； (b-2) 2重量%至95重量%之單體，及 (b-3) 0重量%至10重量%之光起始劑。 根據本發明之頂塗層組成物包含經特別選擇之熱塑性組份與可輻射固化之組份之組合，藉此達成良好阻燃性及良好耐碘性，同時保持UV塗層之傳統優點，包括環境友好及不含VOC性質、快速固化、易於施加、優良機械阻力及諸如此類。 除上述組份之外，根據本發明之頂塗層組成物可進一步包含顏料及/或額外添加劑以改良其性能。 如前所述，根據本發明之頂塗層組成物可包含顏料，該顏料係指能夠賦予目標對象色彩、填充及/或耐磨性之材料。通常，此等顏料包含有機顏料及無機顏料，且無機顏料亦稱為礦物顏料。在態樣中，適用於頂塗層組成物之顏料可包含無機顏料。無機顏料之典型實例可包括(但不限於)氧化鋁(Al2
O3
)、二氧化鈦(TiO2
)、碳酸鈣(CaCO3
)、碳酸鋇(BaCO3
)、鋁粉(Al)、氧化鐵(Fe2
O3
)、二氧化矽(SiO2
)或諸如此類。在另一態樣中，適用於本發明之頂塗層組成物之顏料可包含氧化鋁、非晶形二氧化矽或研磨二氧化矽，此乃因其可賦予或進一步改良頂塗層組成物之阻燃性及耐磨性。在態樣中，顏料可包含1 wt%或更多之頂塗層組成物，例如，5 wt%或更多或7 wt%或更多。在另一態樣中，顏料可包含60 wt%或更少之頂塗層組成物，例如，40 wt%或更少或20 wt%或更少。除提供色彩之外，顏料可進一步用來調整根據本發明之頂塗層組成物之光澤度(即，作為消光劑)或改良機械阻力(即，作為著色填料)。 根據本發明之頂塗層組成物可進一步包含一或多種光起始劑以促進光固化。此處，術語「光起始劑」係指一類可在輻射下分解並起始可聚合寡聚物及/或單體之聚合以形成三維網狀結構之材料。適用於本發明之頂塗層組成物之光起始劑可包含聚合物領域中常用之任何習用光起始劑。可用光起始劑之典型實例可包括(但不限於)選自由以下各項組成之群之一或多者：IRGACURE 1173 ‐ BASF、IRGACURE 184 ‐ BASF、IHT‐PI‐BP及IHT‐PI TPO。在態樣中，基於頂塗層組成物之總重量，光起始劑可以0 wt%或更多(例如，1 wt%或更多或2 wt%或更多)之量存在於根據本發明之頂塗層組成物中。在另一態樣中，基於頂塗層組成物之總重量，光起始劑可以10 wt%或更少(例如，4 wt%或更少)之量存在於根據本發明之頂塗層組成物中。 此外，根據本發明之頂塗層組成物可進一步包含其他添加劑。舉例而言，消泡劑可抑制氣泡形成並容許所產生之氣泡在生產期間逸出或破裂。消光劑可降低自頂塗層組成物形成之塗層膜之光澤度或使所形成之塗層膜具有消光外觀。溶劑可調整頂塗層組成物之黏度。流平劑可改良塗層之操作性質以產生平坦及光滑之塗層。香料可改良塗層之令人愉悅之氣味。流變調節劑可改良良好可流動性及流平性並減少乳化期間之缺陷。防腐劑可保護塗層免於發黴。填料在頂塗層中用於增加固體含量並降低生產成本。pH調整劑用於控制pH值並穩定塗層。蠟用來增加抗劃傷性並改良觸感。增稠劑可增加塗層之黏度並改良潤濕膜之厚度並保護頂塗層免於沈澱及層分離。其他添加劑(例如，銹蝕抑制劑、硬化劑、滑動劑、UV吸收劑等)亦可用於本發明之頂塗層組成物中，只要其與本發明之頂塗層組成物之主要組份物理及化學上相容並可賦予頂塗層組成物一或多種益處即可。在實踐中，每一額外添加劑可含有0.1重量%至8重量%之根據本發明之頂塗層組成物。 本發明進一步提供塗佈基材之至少一部分之方法，其包含以下步驟：利用根據本發明之可輻射固化之頂塗層組成物塗佈基材；及在UV輻射下固化頂塗層組成物。如所述，術語「基材」係指具有粗糙或光滑表面且其上具有或不具有底漆之材料。基材之典型實例包括(但不限於)自以下製得之彼等：塑膠(例如，PE、PVC等)；木材(例如，橡木或松木材料)；基於人造木材之材料(例如，膠合板、刨花板、顆粒板等)；金屬(不銹鋼、鋁、鋁合金等)；玻璃；陶瓷；或其任何組合。適用於接收根據本發明之頂塗層組成物之基材可包括(但不限於)木材、塑膠(例如，PVC及PU基材)等。 本發明進一步提供至少部分地經根據本發明之頂塗層組成物塗佈之基材。 此外，本發明進一步提供高固體含量之阻燃性可輻射固化之頂塗層組成物，其包含氧化鋁顏料；及可輻射固化之組份，其包括丙烯酸系寡聚物；及丙烯酸系單體。在此一頂塗層組成物中，氧化鋁顏料與可輻射固化之組份組合以提供良好阻燃性。在該等中，丙烯酸系寡聚物可係如上文所述之彼等，而單體可係此項技術中所用之任何習用可輻射固化之單體。基於頂塗層組成物之總重量，UV組份可以40 wt%至100 wt%之量存在於本發明之頂塗層組成物中；且顏料Al2
O3
可以0 wt%至60 wt%之量存在於頂塗層組成物中。 出於本說明書之目的，應理解，除非明確說明相反情況，否則本發明可具有製程步驟之各種替代方案及順序。此外，除了在任何操作實例中以外或另有指示，否則說明書及申請專利範圍中所用表示值、範圍、量或百分比(例如，成份之數量)之所有數值在所有情形下可理解為如同以術語「約」開始並修飾一樣，即使該術語並未明確出現。亦應瞭解，本文所列舉之任何數值範圍均意欲包括彼等範圍之端點及其中所包含之所有子範圍。因此，除非指示與此相反，否則以下說明書及隨附申請專利範圍中所闡述之數值參數為可端視本發明欲獲得之期望性質而有所變化的近似值。最低限度地且並非試圖限制均等論應用於申請專利範圍，每一數值參數均應至少根據所報告有效數字之數值並藉由應用普通舍入技術來解釋。 儘管闡述本發明廣泛範圍之數值範圍及參數係近似值，但儘可能精確地報告特定實例中所闡述之數值。然而，任何數值固有地含有必然由其各別測試量測中發現之標凖偏差引起之某些誤差。 如本說明書及隨附申請專利範圍中所用，除非另有明確說明，否則單數涵蓋複數且反之亦然。舉例而言，儘管本文中提及冠詞「一(a、an)」及「該(the)」，但除非明確且清楚地限於一個指代物，否則其包括複數指代物。舉例而言，儘管本文中提及「一種」PMU粒子、「一種」光起始劑及諸如此類，但可使用每一該等組份及任何其他組份中之一或多者。另外，除非另有明確說明，否則在本申請案中使用「或」意指「及/或」，即使在某些情形下可能明確使用「及/或」。「包括」、「舉例而言」、「例如」及類似術語意指包括但不限於、舉例而言但不限於、例如但不限於。 就本發明之範圍而言，如本文中所呈現之本發明之各種實施例及實例中之每一者應理解為非限制性的。 參照以下實例來進一步闡述本發明。以下實例僅說明本發明且不欲限制本發明。實例
呈現以下實例以展示本發明之一般原則。實例闡述本發明之具有良好耐碘染色性及阻燃性之高固體含量頂塗層組成物之製備及測試。除非另有明確指示，否則所列示之所有量係以總重量之份數描述，且所列示之所有百分比係基於重量。本發明不應解釋為限於所呈現之特定實例。製備實例
通常藉由取800 g用於製備每一頂塗層組成物之樣品來製備包含下文所述組份之頂塗層組成物1‐6。換言之，在彼等頂塗層組成物之每一者之製備中，將丙烯酸系寡聚物及丙烯酸系單體(即，可輻射固化之組份)以及溶劑添加至1 L不銹鋼容器中。利用IKA高速分散設備(1500 rpm)將混合物在600 rpm至800 rpm下攪拌10 min。然後，添加EVA及/或氯乙酸乙烯酯樹脂(即，熱塑性塑膠)，並將混合物在1000‐1200 rpm下攪拌直至熱塑性塑膠完全溶解於可輻射固化之組份中以達成8000‐15000 cps (Brookfield RVT 3號轉子20 RPM，在25℃下)之黏度為止。然後，將一或多種顏料添加至混合物中，並利用高速混合器在低於70℃之溫度下攪拌不到60 min。最後，若使用，則添加頂塗層組成物之其餘組份(包括但不限於一或多種光起始劑及其他單體以及一或多種其他添加劑)，並攪拌混合物直至形成均質混合物為止，藉此產生所期望之頂塗層組成物。 此處為如上文所述製備之頂塗層組成物。頂塗層組成物實例 ‐ 1 ：
EVA：DuPont ELVAX 150W 5% 氯醋樹脂：lu’ou T32 EVA氯醋樹脂 10% 丙烯酸系寡聚物：PPG胺基甲酸酯丙烯酸酯 20% 丙烯酸系寡聚物：Guangdong Wuxing EA8204 20% 丙烯酸系單體：丙烯酸異莰基酯(IBOA) 5% 丙烯酸系單體：丙烯酸異癸基酯(IDA) 15% 溶劑：丙二醇甲醚乙酸酯(pma) 20% 光起始劑：IRGACURE 184 - BASF 3% 光起始劑：IHT‐PI‐BP 2%頂塗層組成物實例 ‐ 2 ：
氯醋樹脂：Wacker vinnol E22/48 8% EVA：DuPont ELVAX 150W 8% 丙烯酸系寡聚物：ETERNAL 6196‐100 10% 丙烯酸系寡聚物：Jiangsu Sanmu SM6105‐75Y 20% 丙烯酸系寡聚物：Guangdong JESIDA DSP‐552F 15% 丙烯酸系單體：三羥甲基丙烷三丙烯酸酯(TMPTA) 35% 光起始劑：IRGACURE 1173 – BASF 2% 光起始劑：IHT‐PI TPO 2%頂塗層組成物實例 ‐ 3 ：
EVA：DuPont ELVAX 150W 5% 丙烯酸系寡聚物：PPG胺基甲酸酯丙烯酸酯 34% 丙烯酸系寡聚物：Guangdong JESIDA DSP‐552F 10% 丙烯酸系單體：丙烯酸異莰基酯(IBOA) 10% 丙烯酸系單體：丙烯酸異癸基酯(IDA) 10% Al2O3：MICROGRIT WCA 3S ‐ MICRO ABRASIVES CORPORATION 10% 研磨二氧化矽：TREMIX958‐600EST – SIBELCO 10% 二氧化矽消光劑：SYLOID ED 80 ‐ GRACE DAVISON 5% 光起始劑：IRGACURE 1173 – BASF 6%頂塗層組成物實例 ‐ 4 ：
未經修飾之氯醋樹脂：wacker vinnol E22/48 A 5% 經修飾之氯醋樹脂：lu’ou T32 EVA 氯醋樹脂樹脂 5% 未經修飾之eva：DuPont ELVAX 150W 5% 溶劑：N‐BUTYL ACETATE 10% 丙烯酸系寡聚物：PPG胺基甲酸酯丙烯酸酯 10% 丙烯酸系寡聚物：Jiangsu Sanmu SM6105‐75Y 9.8% 丙烯酸系單體：三羥甲基丙烷三丙烯酸酯(TMPTA) 30% 丙烯酸系單體：丙烯酸異莰基酯(IBOA) 5% 二氧化矽消光劑：SYLOID ED 80 ‐ GRACE DAVISON 3% Al2O3：MICROGRIT WCA 3S ‐ MICRO ABRASIVES CORPORATION 10% 研磨二氧化矽：TEGO AIREX 920 ‐ EVONIK INDUSTRIES 0.2% 光起始劑：IHT‐PI‐BP 2% 光起始劑：IHT‐PI TPO 2% 光起始劑：IRGACURE 184 – BASF 3% 無光起始劑之頂塗層組成物實例 ‐ 5 ：
EVA：DuPont ELVAX 150W 5% 丙烯酸系寡聚物：PPG胺基甲酸酯丙烯酸酯 34% 丙烯酸系寡聚物：Guangdong JESIDA DSP‐552F 13% 丙烯酸系單體：丙烯酸異莰基酯(IBOA) 10% 丙烯酸系單體：丙烯酸異癸基酯(IDA) 13% Al2O3：MICROGRIT WCA 3S ‐ MICRO ABRASIVES CORPORATION 10% 研磨二氧化矽：TREMIX958‐600EST - SIBELCO 10% 二氧化矽消光劑：SYLOID ED 80 ‐ GRACE DAVISON 5% 此處為兩個比較實例比較實例 ‐ 1 ( 無 EVA 或氯醋樹脂 )
丙烯酸系寡聚物：ALLNEX EB 809 50% 丙烯酸系單體：Eternal ETERMER 2211 18% 丙烯酸系單體：MIWON Miramer M130 15% 二氧化矽消光劑：SYLOID ED 80 ‐ GRACE DAVISON 8% Al2O3：MICROGRIT WCA 3S ‐ MICRO ABRASIVES CORPORATION 5% 顏料：IRGACURE 1173 - BASF 2.5% 顏料：IHT‐PI‐BP 1.5%比較實例 ‐ 2 ( 使用不同熱塑性組份 )
丙烯酸系寡聚物：ALLNEX EB 809 15% 丙烯酸系單體：Eternal ETERMER 2211 35% 丙烯酸系單體：MIWON MIRAMER M3190 20% 熱塑性組份：TEGO ADDBOND LTH 10% 二氧化矽消光劑：SYLOID ED 30 ‐ GRACE DAVISON 5% 顏料：Sibelco silverBond 602 5% 顏料：IHT‐PI TPO 3% 顏料：IRGACURE 184 - BASF 2%測試：
根據EN 13501‐1:2007+A1:2009之方法，對於如上述實例及上述比較實例中所製備之頂塗層組成物1‐6測試其各別阻燃性，且根據EN 438‐2:2005之方法測試其各別耐碘染色性。結果分別列示於下表-1及表-2中。 表-1： 表 -2 ：
注釋1：根據EN13501‐1:2007+A1:2009之阻燃性級別： A級為最高，然後B級、C級、D級等等。 注釋2：根據EN 438‐2:2005之染色等級係如下： 等級5：無可見變化； 等級4：光澤及/或色彩輕微變化，僅在某些視角下可見； 等級3：光澤及/或色彩中度變化； 等級2：光澤及/或色彩顯著變化；及 等級1：表面失真及/或起泡。 自以上實例及測試可見，本發明之頂塗層組成物展現良好阻燃性及極佳耐碘染色性，而比較組成物未展現。 儘管上文已出於說明目的闡述本發明之具體態樣，但顯然熟習此項技術者將可對本發明之某些細節作出多種改變，而不背離如隨附申請專利範圍中所界定之本發明。因此，應理解，本發明並不限於上文中所揭示及所說明之具體態樣，而是意欲涵蓋在如由隨附申請專利範圍所界定之本發明之精神及範圍內之修改。
無
Claims (16)
- 一種高固體含量之阻燃及耐碘染色之可輻射固化之頂塗層組成物，其包含：(a)熱塑性組份，其包括乙烯乙酸乙烯酯樹脂與氯乙酸乙烯酯樹脂中之一者或兩者；及(b)可輻射固化之組份，其包括：(b-1)一或多種丙烯酸系寡聚物；及(b-2)一或多種丙烯酸系單體。
- 如請求項1之頂塗層組成物，其中該乙烯乙酸乙烯酯樹脂或該氯乙酸乙烯酯具有在5,000至50,000範圍內之重量平均分子量。
- 如請求項1之頂塗層組成物，其中該乙烯乙酸乙烯酯樹脂或該氯乙酸乙烯酯在其主鏈中包含5%至45%之乙酸乙烯酯單元。
- 如請求項1之頂塗層組成物，其中該乙烯乙酸乙烯酯樹脂或該氯乙酸乙烯酯未經修飾或經修飾。
- 如請求項4之頂塗層組成物，其中該乙烯乙酸乙烯酯樹脂經聚氯乙烯修飾。
- 如請求項4之頂塗層組成物，其中該氯乙酸乙烯酯樹脂經苯乙烯馬來 酸酐修飾。
- 如請求項1之頂塗層組成物，其中該可輻射固化之組份進一步包含一或多種光起始劑。
- 如請求項1之頂塗層組成物，其進一步包含：至少一種顏料。
- 如請求項8之頂塗層組成物，其中該顏料係氧化鋁或二氧化矽。
- 如請求項1之頂塗層組成物，其中該一或多種丙烯酸系單體包含丙烯酸異莰基酯及丙烯酸異癸基酯。
- 如請求項8之頂塗層組成物，其基於該頂塗層組成物之總重量包含：(a)1重量%至95重量%之該熱塑性組份；(b)5重量%至99重量%之該可輻射固化之組份；及(c)1重量%至60重量%之該顏料。
- 一種塗佈基材之至少一部分之方法，其包含以下步驟：利用如請求項1至10中任一項之可輻射固化之頂塗層組成物塗佈該基材；及在UV輻射下固化該頂塗層組成物。
- 一種基材，其至少部分地經如請求項1至11中任一項之頂塗層組成物塗佈。
- 如請求項13之基材，其中該基材包含木材。
- 如請求項13之基材，其中該基材包含塑膠。
- 一種阻燃性可輻射固化之頂塗層組成物，其包含：(a)氧化鋁顏料；(b)可輻射固化之組份，其包含：(b-1)一或多種丙烯酸系寡聚物；及(b-2)一或多種丙烯酸系單體；及(c)熱塑性組份，其包括乙烯乙酸乙烯酯樹脂與氯乙酸乙烯酯樹脂中之一者或兩者。