TW586964B - Catalyst filter, method for producing the same and method for treating exhaust gas with the same - Google Patents
Catalyst filter, method for producing the same and method for treating exhaust gas with the same Download PDFInfo
- Publication number
- TW586964B TW586964B TW90124476A TW90124476A TW586964B TW 586964 B TW586964 B TW 586964B TW 90124476 A TW90124476 A TW 90124476A TW 90124476 A TW90124476 A TW 90124476A TW 586964 B TW586964 B TW 586964B
- Authority
- TW
- Taiwan
- Prior art keywords
- catalyst
- fiber
- fibers
- titanium dioxide
- filter
- Prior art date
Description
586964
五、發明說明(i ) 經濟部智慧財產局員工消費合作社印製 [發明領域] 本發明係有關一種觸媒過濾器、其製造方法、及使用 該觸媒過濾器之廢氣處理方法。 [背景技藝] 已知具有脫氮功能的過濾器,該種過濾器可藉由單一 裝置去除由都市廢棄物、污泥或工廠廢棄物用之焚化爐、 鍋爐、柴油機等產生的廢氣中之粉塵及氮氧化物(Ν0χ)。至 於此種過濾器,已提及包括含有氧化鈦及氧化釩之觸媒纖 維的過濾器[參見JP-A-5-184923、JP-A_!-2587846(相當於 USP 5,051,391)等 一般而言’該種過濾器經振動去除該過濾器所收集的 物質,詳言之,搖落氫氧化鈣(熟石灰)及粉塵。然而,在 JP-A-5-184923揭示的過濾器之例中,觸媒纖維本身在振動 時掉落,特定言之,對該過濾器施以規律的振動,易使過 濾、器的觸媒活性減少。此外,在其他公報揭示的過濾器之 例中’由於觸媒纖維包括承載於二氧化鈦纖維上之氧化釩 顆粒,該氧化釩顆粒由該二氧化鈦纖維脫落,使得過濾器 的觸媒活性傾向減少,即便是觸媒纖維本身未自過濾器脫 落亦然。[發明大綱] 本發明之一目的是提供一種觸媒過濾器,其可藉由單 一裝置去除去除廢氣中的粉塵及氮氧化物,該種過濾器具 有高度觸媒活性,且即使在經由振動該過濾器而搖落氫氧 化鈣及粉塵時亦維持該高度觸媒活性。 本紙張尺度適用中國國豕標準(CNS)A4規格(210 X 297公爱) 1 313080 (請先閱讀背面之注意事項再填寫本頁)
-------訂---------.
明 .£ _j 一目的係提供一種製造此種觸媒過濾器的 方法。 本發日月> Υ 〇 一目的係提供一種使用此種觸媒過濾器之 廢氣處理方法。 因此’本發明提供一種觸媒過濾器,該觸媒過濾器包 括一氧化鈦觸媒纖維及至少一層聚合物纖維之非織造織 物。 此外’木發明提供一種製造本發明觸媒過濾器的方 /会’包括將二氧化鈦觸媒纖維及聚合物纖維分散於溶劑(如 水等)以獲得纖維分散液,及由該纖維分散液製成片,而獲 得觸媒過濾器的步驟。 本發明亦提供一種製造本發明觸媒過濾器的方法,包 括將二氧化鈥觸媒纖維層置於聚合物纖維之非織造織物上 的步驟。 於一較佳具體例中,該觸媒過濾器中的非織造織物及 二氧化鈦觸媒纖維係藉由黏著、與紗線一起針織或纖維之 纏繞而固定在一起。 此外,本發明提供一種處理廢氣的方法,包括使該廢 氣通過本發明觸媒過漉器。 [圖式之簡單說明] 第1圖係本發明過滤器之第一具體例的橫切面圖。 第2圖係本發明過遽器之第二具體例的橫切面圖。 第3圖係本發明過滤器之第三具體例的橫切面圖。 第4圖係本發明具有斯克林布(scrim)之過濾器的第四 (請先閱讀背面之注意事項再填寫本頁)
-------訂---------線· 經濟部智慧財產局員工消費合作社印製 本紙張尺度綱+ _家標準(CNS)A4規格(210 X 297ϋ ) 2 313080 586964
五、發明說明(3 ) 具體例之橫切面圖。 第5圖係本發明具有斯克林布之過濾器的第五具體例 之檢切面圖。 第6圖係本發明具有斯克林布之過濾器的第六具體例 之橫切面圖。 第7圖係本發明具有斯克林布之過濾器的第七具體例 之橫切面圖。 [發明之詳細說明] 本發明觸媒過濾器包括二氧化鈦觸媒纖維及至少一層 聚合物纖維之非織造織物。 本發明所使用之二氧化鈦觸媒纖維可為習知者。例 如,可以使用含有至少一種由釩、鎢、鋁、砷、鎳、錯、 翻、釕、鎂、鈣及鉑所成組群選出之元素的金屬、金屬氧 化物及複合化合物的二氧化鈦觸媒纖維,例如Jp_A-11- 5036 及 JP-2000-22003 8-A 所述者。 使用如本發明之二氧化鈦觸媒纖維可以預防觸媒由過 濾器掉落,而可以長期維持觸媒活性。 即使是本發明過濾器中的二氡化鈦觸媒纖維重量(每 單位面後)增加時,過波器亦可違對農過濾速率而不堆加過 濾之壓力損失。 依本發明,用以固定觸:媒敗雉的黏著劑等之量可減少 氣避_免」以在觸媒過波器中貧用二I化鈦觸媒纖雉。倒此, 可以抑鲅因黏著劑等弓L起之觸媒活性降低,而有效地利用 觸媒的天然活性。二I化鈦觸媒氱維可依造紙法等加工成 本紙張尺度過用中國國家標準(CNS)A4規格(210 x 297公釐) (請先閱讀背面之注意事項再填寫本頁)
訂---------線· 經濟部智慧財產局員工消費合作社印製 586964 A7 B7 經 濟 部 智 慧 財 產 局 員 工 消 費 合 作 社 印 製 五、發明說明(4 ) 片狀。 較佳之二氧化鈦觸媒繳雉含有至少5〇重量%之氧化 欽及至少5重量%之氧化釩,其氬雉t度至少50微米1纖 維直—徑為:2微米至1 〇〇微米,此外依氮吸收法測得之多孔 性為—至少0.05立方公分/1。該二氧^化鈦觸媒纖雉之比表 面稜可為至少10平方公尺/克‘,較佳為20至300平方公尺 /1。詨二氧化鈦觸媒底維·中,iUi」L少l〇A(l nmX之:孔洞 的多孔性可為至少〇 〇2立方公分,孔徑之峰值範圍為 10 I 300A(1 至 30 nm},^_隹11〇 1 10〇Α(ι 至 1〇 nm)。 二I化鈦镯媒缓維的製法可怠何如:將鈦薄鹽(如乙醇 鈦、正丙醇鈦、異丙醇鈦、正丁避鈦、異丁醇鈦、第二丁 醇鈦、第三丁醇鈦等)溶於醇類(如乙醇、正丙醇、異丙醇、 正丁醇、異丁醇、第二丁醇、第三丁醇等),將妓等醇薄水 解成含有二氧化鈦的漿液,將釩化合物(如三乙氧化叙、三 異丙氧化釩、三正丙氧化釩、三正丁氧化釩等)溶於該漿液 中,獲得紡絲漿液,接著對該紡絲漿液進行紡絲,獲得母 體纖維,並锻燒該母體纖維。 本發明使用之非織造織物包括聚合物纖維。由於二氧 化鈦觸媒纖維係保存於非織造織物層,故本發明觸媒過渡 器可達到高粉塵收集效率,同時維持高度可渗透性或低壓 力損失’更進-步,由於該非織造織物防止二氧化欽觸媒 纖維脫落,故即使係振動該過遽器以搖落氮氧化約及粉塵 時,亦可維持觸媒活性。 聚合物纖維之實例包含聚醯胺纖維、聚丙烯纖維、聚 1本紙張尺度適用中國國家標準(CNS)A4規格⑵Gx 297公复)""""""'----- 4 313080 (請先閱讀背面之注意事項再填寫本頁)
訂---------線- 586964 A7 B7 五、發明說明(5 經 濟 部 智 慧 財 產 局 消 費 合 作 社 印 製 酯纖維、丙烯酸纖維、芳族聚醯胺纖維、氟樹脂纖維 又 _醯亞胺纖維、聚醯亞胺纖維、聚苯硫醚纖維、 I _纖維 等。本發明使用之非織造織物可包括此等纖維中之 或兩種或更多種此等纖維。 聚合物纖維對二氧化鈦觸媒纖維之重瞀 里較佳為 2〇· 1至1· 1,以便使該觸媒過濾器具有良奸可操作座及 長期之形狀安定性。 包括聚合物纖維之非織造織物可藉由習知方法製得, 例如包括以樹脂黏著聚合物纖維之樹脂黏結法、包括以針 纏繞聚合物纖維之針刺法、包括以熱黏結聚合物纖維之熱 黏結法、包括以高壓流體喷射纏繞聚合物纖維之水刺法 等。 本發觸媒過濾器中,較佳該二氧化鈦觸媒纖維係保存 於非織造織物層,或間置於至少兩層非織造織物之間。在 此等情形下,即使該觸媒過濾器係放置於施加振動該觸媒 過遽器以去除該過濾器所收集之粉塵的裝置上時,亦可防 止觸媒(觸媒纖維及/或觸媒成份)脫落。 本發明觸媒過濾器的某些典型實例示於第1、2及3 圖。第1圖的觸媒過濾器包括聚合物纖維2之非織造織物 4’以及非織造織物4表面上攜載的二氧化鈦觸媒纖維1。 第2圖的觸媒過濾器包括二氧化鈦觸媒纖維1之非織造織 物5及聚合物纖維2,其中該二氧化鈦觸媒纖維丨係存於 聚合物纖維之非織造織物層内。第3圖的觸媒過濾器包括 聚合物f ^ 2之非織造織物4、二氧化鈦觸媒纖維1之層 本紙張尺度適用標準(CNS)A4規格(210 X 297公釐) 者 (請先閱讀背面之注意事項再填寫本頁)
-------訂---------· 5 313080 586964 A7 B7 經濟部智慧財產局員工消費合作杜印製 五、發明說明(6 ) 及另一塊聚合物纖維2之非織造織物4,依此順序放置。 本發明觸媒過濾器可包括斯克林布,其為一種聚合物 纖維之織造織物。某些具有斯克林布之觸媒過濾器的典型 實例示於第4至7圖。第4圖的觸媒過濾、器包括聚合物纖 維2之非織造織物4、斯克林布3、二氧化鈦觸媒纖維i 之層及另一塊聚合物纖維之非織造織物4,依此順序玫 置。第5圖的觸媒過濾器包括聚合物纖維2之非織造織物 4、 斯克林布3、及其中含有二氧化鈦觸媒纖維1之聚合物 纖維2的非織造織物5。第6圖的觸媒過濾器包括第一塊 聚合物纖維2之非織造織物4、第一塊斯克林布3、第二壤 聚合物纖維2之非織造織物4、其中含有二氧化鈦觸媒纖 維1之聚合物纖維2的非織造織物5、第三塊聚合物纖維2 之非織造織物4、第二塊斯克林布3及第四塊聚合物纖維2 之非織造織物4,依此順序放置。第7圖的觸媒過濾器包 括第一塊聚合物纖維2之非織造織物4、斯克林布3、其中 含有二氧化鈦觸媒纖維1之聚合物纖維2的非織造織物 5、 及第二塊聚合物纖維2之非織造織物4,依此順序放置。 本發明觸媒過濾器可藉由下述方法製造: 例如,第4圖的觸媒過濾器可以使用聚合物纖維藉由 針刺法製造兩片非織造織物,於其中一片非織造織物的一 表面上依序玫置斯克林布3、二氧化鈦觸媒纖維層及另一 片非織造織物,並將彼等材料針刺在一起。 製造本發明觸媒過濾器之其他方法的實例包含:包括 藉由樹脂黏揍二氧化鈦觸媒纖維及非織造織物的方法;包 本紙張尺度適用中國國家標準(CNS)A4規格(210 x 297公爱) 6 313080 rtt先閱讀背面之、凌意事項再填寫本頁)
ϋ ϋ >ϋ ϋ «ϋ ·ϋ-、· ί ϋ ϋ ϋ H ϋ n I i-φ 为
586964 經濟部智慧財產局員工消費合作社印製 7 A7 五、發明說明(7 ) 括以針使二氧化鈦觸媒纖維與非織造織物之聚合物纖維彼 此纏繞的方法;包括使二氧化鈦觸媒纖維及非織造織物與 紗線-起針織的方法;包括以熱黏結二氧化欽觸媒纖維與 非織造織物的方法;及包括以喷射高麗水纏繞二氧化欽觸 媒纖維與非織造織物之聚合物纖維的方法。此外,觸媒過 濾器可藉由在製造聚合物纖維之非織造織物的步驟時,使 二氧化鈦觸媒纖維與聚合物纖雉一起製造,至使該二氧化 鈦觸媒纖維保存於所製得之非織造織物層。再者,該觸媒 過濾器可藉由先以梳理法對該聚合物纖維塑形,將二氧化 鈦觸媒纖維及視需要之斯克林布放置於該經塑形之聚合物 纖維上’接著藉由針刺法將聚合物纖維與二氧化鈦觸媒纖 維纏繞在一起。 本發明中使用之聚合物纖維的非織造織物可包括一種 聚合物纖維,或兩種或更多種聚合物纖維。當觸媒過濾器 中存有二或更多層非織造織物時,在彼等非織造織物層中 的聚合物纖維的種類可為彼此相同或不同。 當觸媒逷濾器具有斯克林布時,在斯克林布回收粉塵 之側上的非織造織物的厚度較好是比在該斯克林布的另一 側上的非織造織物的厚度厚。當該將另一侧上的非織造織 物的厚度製成較小時,可減少壓力損失,且不損壞粉塵收 集效率及觸媒過濾器的催化效率。 根據本發明之觸媒過濾器的非織造織物可進一步包括 無機纖維如氧^化鋁纖維、二氧化矽纖維、氧化鍅纖維、玻 璃纖維等。無機纖維之使用可以增加所得觸媒過濾器之機 私紙張尺度適用中國國家標準(CNS)A4規格(210 x 297公釐 313080 (請先閱讀背面之注意事項再填寫本頁) --------訂---------線 586964
五、發明說明(8 械強度及耐熱性。無機纖維可用如同於非織造 二氧化鈦纖維的相同方式於非織造織物中提供。 /、 (請先閱讀背面之注意事項再填寫本頁) 無機纖雄、二氧化鈦纖維及聚合物纖維分散於水中,接著 以造紙法加工成片&。如是獲得包括無機纖 媒過濾器。 不發明觸 若本發明觸媒過遽器在去除粉塵及氮氧化物的同時進 行乾燥法(以乾燥法同時收集粉塵及脫氮),可達到優異效 果。此外,可使用本發明觸媒過濾器去除由都市廢棄物、 污泥或工廠廢棄物用之焚化爐、鍋爐、柴油機等產生的有 害物質如氣化氳、硫氧化物、有機氯化物(如戴奥辛)等。 如上述,本發明觸媒過濾器可用單一裝置去除粉塵及 氮氧化物,其具有尚度觸媒活性,且由於可防止觸媒脫落, 故即使在經由振動該過濾器而搖落氫氧化鈣及粉塵後亦維 持高度觸媒活性。 即使是每單位面積的二氧化鈦觸媒纖維重量增加時, 本發明觸媒過遽器亦可進行高速過濾,而不增加過濾器之 壓力損失。 經濟部智慧財產局員工消費合作社印製 此外’當本發明觸媒過濾器具有該二氧化鈦觸媒纖維 係保存於非織造織物層的結構,或二氧化鈦觸媒纖維間置 於非織造織物層之間的結構時,由於二氧化鈦觸媒纖維不 會由過渡器脫落,故即使是在對過濾器施加強力振動時, 該過遽器亦可維持過度觸媒活性。 根據本發明製造觸媒過濾器的方法可容易地提供具有 高度觸媒活性、且維持高度觸媒活性的觸媒過濾器,其中 本紙張尺度適用中關家標準(CNS)A4規格(210x297公爱) 8 313080 586964 a7 --—_____B7______ 五、發明說明(9 ) 該南度觸媒活性係藉由防止二氧化鈦觸媒纖維在即使是對 (請先閱讀背面之注意事項再填寫本頁) 過濾、器施加強力振動而搖落氫氧化鈣及粉塵時亦不由過濾 器脫落而達成。 依據本發明處理廢氣的方法,可同時有效地去除粉塵 及氮氧化物。 [實施例] 兹以下述實施例進一步說明本發明,但彼等實例不以 任何方法限制本發明範疇。 依下文進行掉落試驗及脫氮試驗: 掉落試驗: 自觸媒過濾'器切取直徑1〇公分的圓盤,該圓盤的周圍 經熱固性樹脂硬化處理,獲得一試樣。接著,在3公斤/ 平方公分(〇.3MPa)的壓力下,以脈衝式氣動喷射器(air pulse jet)振動該試樣1,〇〇〇次。由試驗前後之試樣重量差 計算物質掉落量。 脫氮試驗: 經濟部智慧財產局員工消費合作社印製 將過濾面積為22平方公分的觸媒過濾器放置於一玻 璃管末端,該玻璃管之内徑於垂直於該玻璃管處為53毫 米。然後,在200°C下加熱含有100ppmNO、I00 ρρη^ΝΗ3、 10% 〇2、20% 及餘量之Ν2的試驗氣體,使之以2.2升 /分鐘的流速,自玻璃管的開口端通過到達具有該過渡器的 末端。由通過該玻璃管前後的NO濃度差計算脫氮速率。
於彼等實施例中,單位’’旦(denier)”為纖維直徑的指 標,且係以每9,000公尺纖維的重量表示。一英忖為2 M 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 9 313080 586964 A7 _______ B7 五、發明說明(10 ) 公分。 實施例1 (請先閱讀背面之注意事項再填寫本頁) 二氧化鈦觸媒纖維之製備 使異丙醇鈦[購自和光純化工業(Wako Pure Chemical Industries)股份有限公司之超純試劑](3〇〇 〇克)及乙醢乙 酸乙醋(購自和光純化工業股份有限公司之保證極試 劑)(5 5.0克)溶於異丙醇(購自和光純化工業股份有限公司 之保證極試劑)(73·6克),所得溶液於氮氣圍下回流一小 時,製得原料Α。 另使純水(36.0克)與異丙醇(324·8克)混合,獲得含有 10重量%水之醇A。 接著在攪拌下,將醇A添加至原料a中,所得混合物 於氮氣圍下加熱,蒸發異丙醇,使異丙醇鈦水解。混合物 回流1小時後,進一步加熱該混合物,並藉蒸發異丙醇而 濃縮,直到鈦濃度達到3·46χ 1〇·3莫耳/克,獲得聚合物漿 液調整水解速率,使得異丙醇之蒸發速率與異丙醇之添 加速率實質相等,添加時間為13〇分鐘。 經濟部智慧財產局員工消費合作社印製 在所得之聚合物漿液中添加四氫呋喃(購自和光純化 工業股份有限公司之保證極試劑)(362克),使所得混合物 回流1小時,使於四氫呋喃中之漿液所含的聚合物溶解。 隨後,將三乙氧基釩[購自高純度化學(mgh pudty Chemicals)股份有限公司](51 2克)添加至該四氫呋喃溶 液,使所得混合物再回流丨小時,獲得聚合物溶液。三乙 氧基釩的量為藉由聚合物之紡紗及煅燒所得之二氧化鈦觸 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公爱) -----_ 10 313080 A7 11 586964 五、發明說明( 媒纖維中所含之釩量,其量為氧化釩之21重量%。 (請先閱讀背面之注意事項再填寫本頁) 使上文所得之聚合物溶液通過孔徑為3微米的氟樹脂 膜過濾器而過滤。接著,加熱該濾液,並藉由蒸發異丙醇 及四氫呋喃使之濃縮,獲得紡絲漿液(2〇〇克)。使所得之纺 絲漿液維持於4(TC,並由直徑為5〇微米之喷嘴擠出至4〇 ^:、60% RH之含有壓力為2〇公斤坪方公分(2 〇氮 氣的空氣中,所得紡絲材料以7〇公尺/分鐘的速度予以捲 取,獲得母體纖維。所得之母體纖維以含於85t、95%rh 之恆溫恆濕容器中的蒸汽(蒸汽之分壓為0·053 MPa)處理 15小時’接著於500〇c的空氣中煅燒1小時,獲得二氧化 鈦觸媒纖維。 上文製得之二氧化鈦觸媒纖維係一種長纖維 (continuous fiber),其纖維直徑為丨5微米,bet比表面積 為65平方公尺/克,以氮吸收法測得之多孔性為〇 18立方 公分/克(孔徑至少1 〇Α的孔洞)。 依X射線繞射分析’該二氧化鈦觸媒纖維係由銳欽確 氧化鈦所組成,且未發現銳鈦礦以外之任何氧化鈦。 經 濟 部 智 慧 財 產 局 員 工 消 費 合 作 社 印 製 當以掃晦式電子顯微鏡觀冑二氧化鈦觸媒纖維時,於 外表面上未發現有易於掉落的氧化釩顆粒。 、 非織造織物A之製法: 以針擊法處理聚醯亞胺纖維(商品名·· p84 ; 2旦;⑽ 毫米之短纖維;購自T0Y0 B〇SEKI SALES公司),製得每 單位面積重量為200克/平方公尺之非織造織物A 斯克林布A之製法: 本紙張尺度適用中國國家標準(CNS)A4 &格(210 X 297公$ ) 11 313080 586964
五、發明說明(u ) 聚釀亞胺纖維(商品名:P84 ; 96〇旦;48〇長絲;麟自 TOYO BOSEKI SALES公司)以12/1〇紗線/英时(經/緯)的編 (請先閱讀背面之注意事項再填寫本頁) 織密度平紋編織,製得每單位面積重量1〇〇克/平方公尺之 斯克林布A。 觸媒過濾器之製法及其評估: 將斯克林布A置於非織造織物a上。然後於斯克林布 A之上堆積已被裁切成長度約3公分之上文製得的二氧化 鈦觸媒纖維,製得其量係纖維密度為15〇克/平方公尺之纖 維層。再將另一塊非織造織物A置於該二氧化鈦觸媒纖維 層上’並針刺所得之層。 其後以平熱壓光調整彼等層之厚度,以3〇(rc對彼等 層熱處理30秒,接著以氣體燒毛機燒毛,製得觸媒過濾 器。 μ 使上文製得之觸媒過濾器進行掉落試驗。掉落量少於 3%。使依上述之相同方法製得之觸媒過濾器進行脫氮試 驗。脫氮率為70%或更多。 經濟部智慧財產局員工消費合作社印製 使業已進行掉落試驗之觸媒過濾器進一步進行脫氮試 驗。脫氮率為70%或更多。雖然觸媒過濾器在掉落試驗時 業經脈衝式氣動噴射器振動,但觸媒過濾器之脫氮率在進 行掉洛试驗後並未下降。 實施例2 非織造織物Β之製造 將經裁切成長度約3公分之依實施例1相同方法製得 的二氧化鈦觸媒纖維(150重量份)、聚醯亞胺纖維(商品 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 313080 12 586964
五、發明說明( 13 名.P84 ’單絲直徑:20微米;纖維長度:約5毫米;購 (請先閱讀背面之注意事項再填寫本頁) 自T〇Y〇B〇SEKISALES公司)(100重量份)、來自針葉樹 之牛皮紙漿(67重量份)分散於水中,以造紙法加工,製得 每單位面積重量為317克/平方公尺之非織造織物B。非織 造織物B中之二氧化鈦觸媒纖維的每單位面積重量為15〇 克/平方公尺。 觸媒過濾器之製法及其評估: 於依實施例1之方法製得之非織造織物A上依序放置 依實施ί列1之方法製得之斯克林_ 非織造織物B,並 針刺所得之層。 其後以平熱壓光調整彼等層之厚度,彼等層經氣體燒 毛機予以燒毛’製得觸媒過渡器。 使上文製得之觸媒過濾器進行掉落試驗。掉落量少於 3%。使依上述之相同方法製得之觸媒過濾器進行脫氮試 驗。脫氮率為70%或更多。 使業已進行掉落試驗之觸媒過遽器進一步進行脫氣試 驗。脫氮率為70%或更多。 經濟部智慧財產局員工消費合作社印製 實施例3 非織造織物C之製造: 於依實施例1之方法製得之非織造織物Α上依序放置 依實施例1之方法製得之斯克林布Α及另一塊非織造織物 A,並針刺所得之層。然後以平熱壓光調整彼等層之厚度, 以300〇C對彼等層熱處理3〇#,接著以氣體燒毛機燒:, 製得每單位面500克/平方公尺之非織造織物〇 本紙張尺度_ +國@家標4〇JNS)A4規格⑽X 297公 17 313080 13 A7 586964 " -------— B7__— —___ 五、發明說明(14 ) 觸媒過濾器之製法及其評估·· (請先閱讀背面之注意事項再填寫本頁) 使非織造織物C、依實施例2之方法製得之及非織造 織物B及另一塊非織造織物c依序放置。接著使用氟樹= 纖維(商品名·· PROFILEN; 400旦;購自Lenzing),以^ 攏法縫合所得層,製得觸媒過濾器。 使上文製得之觸媒過濾器進行掉落試驗。掉落量少於 3%。使依上述相同方法製得之觸媒過濾器進行脫氮試驗。 脫I率為70%或更多。 使業已進行掉落試驗之觸媒過漶器進一步進行脫氮試 驗。脫氮率為70%或更多。 资施例4 非織造織物D之製造: 使聚醯亞胺纖維(商品名:P84; 2旦;60毫米之短纖 維;購自TOYO B0SEKI SALES公司)(4〇重量份)與氟樹脂 纖維(商品名:PROFILEN;平均2.4旦;纖維長度:6〇毫 米;購自Lenzing)(60重量份)混合,以針刺法處理,製得 每單位面積重量為200克/平方公尺之非織造織物D。 經濟部智慧財產局員工消費合作社印製 斯克林布B之製法: 使氟樹脂纖維(商品名:PROFILEN ; 400旦;40長絲 紗;捻度S 100T/M ;購自Lenzing)以2 5/25紗線/英吋(經/ 緯)的編織密度平紋編織,製得每單位面積重量1〇〇克/平 方公尺之斯克林布B。 觸媒過濾器之製法及其評估: 於非織造織物D上依序放置斯克林布B、依實施例2 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公爱) 14 313080
Claims (1)
- 586964 m(92年4月3曰) •一種觸媒㈣器,包括含有至少5G重量%之氧化欽及至 少5重量%之氧化釩之二氧化鈦觸媒纖維及至少一層選自 聚醯胺纖維、芳族聚醯胺纖維、氟樹脂纖維、聚醚醯亞胺 纖維及聚醯亞胺纖維之聚合物纖維之非織造織物, 其中,該二氧化鈦觸媒纖維係保存於該非織造織物 層’或間置於至少兩層該非織造織物之間。 2·如申請專利範圍第1項之觸媒過濾器,其中該二氧化鈦觸 媒纖維係存留於至少一層該聚合物纖維之非織造織物 中。 3·如申請專利範圍第1項之觸媒過濾器,包括至少兩層聚合 物纖維之非織造織物及至少一層該二氧化鈦觸媒纖維,且 至少一層二氧化鈦觸媒纖維係間置於至少兩層非織造織 物之間。 4· 一種製造觸媒過濾器的方法,包括下列步驟: 經濟部中央標準局員工福利委員會印製 將一氧化鈦觸媒纖維與聚合物纖維分散於溶劑,獲得 纖維分散液;及 將該纖維分散液依造紙法塑形成片狀,獲得觸媒過滤 器。 5. —種製造觸媒過濾器的方法,包括將二氧化鈦觸媒纖維層 放置於聚合物纖維之非織造織物層上的步驟, 其中,該非織造織物與該二氧化鈦觸媒纖維係藉由黏 本紙張尺度適用中國國家標準(CNS) A4規格(210 X 297公釐) 1 313080 586964 H3 著、與紗線一起針織或纖維之.纏繞而固定在一起。 6.如申請專利範圍第1項之觸媒過濾器,其中,該觸媒過濾 器係藉由使廢氣通.過該觸媒過濾器而處理該廢氣。 經濟部中央標準局員工福利委員會印製 本紙張尺度適用中國國家標準(CNS) A4規格(210 X 297公釐) 2 313080