TW202345698A - 抗菌及抗病毒樹脂組成物 - Google Patents
抗菌及抗病毒樹脂組成物 Download PDFInfo
- Publication number
- TW202345698A TW202345698A TW112112549A TW112112549A TW202345698A TW 202345698 A TW202345698 A TW 202345698A TW 112112549 A TW112112549 A TW 112112549A TW 112112549 A TW112112549 A TW 112112549A TW 202345698 A TW202345698 A TW 202345698A
- Authority
- TW
- Taiwan
- Prior art keywords
- antibacterial
- antiviral
- resin composition
- fiber
- compound particles
- Prior art date
Abstract
本發明提供一種新穎的抗菌及抗病毒樹脂組成物。該抗菌及抗病毒樹脂組成物包含一價銅化合物粒子作為有效成分而具有抗菌及抗病毒性，該樹脂組成物在日本工業規格JIS Z 8781-4的L*a*b*的表色系中的L*值為0以上且小於40。
Description
本發明關於一種抗菌及抗病毒樹脂組成物，其能夠使已附著的細菌和病毒失去活性。
由於新型冠狀病毒感染(COVID-19)造成的疫情，人類的生活型態產生劇烈的變化。在日常生活中，口罩和消毒劑已成為必須，並且針對截至目前為止僅受到來自醫療人員高度關注的抗病毒相關製品，一般消費者的關注也日漸提高。其中，對於用以整頓室內環境的空氣清淨機和空調機器的需求日漸提升，並且不僅是抗菌功能，謀求抗病毒功能的需求也日漸提升。
為了解決該等問題，已開發有具有抗菌及抗病毒性的濾網和抗病毒薄膜等的成型品(例如，專利文獻1、專利文獻2、專利文獻3)。
[先前技術文獻]
(專利文獻)
專利文獻1：國際公開第2011/040048號。
專利文獻2：日本特開2005-007346號公報。
專利文獻3：日本特開2021-066874號公報。
[發明所欲解決的問題]
從商品設計的自由度的觀點等來看，較佳是具有抗菌及抗病毒性的材料存在有更多樣的選項。
本發明的目的在於提供一種新穎的抗菌及抗病毒樹脂組成物。
發明人致力於研究，結果發現，若使日本工業規格JIS Z 8781-4的L*a*b*的表色系中的L*值為0以上且小於40的樹脂組成物中含有一價銅化合物粒子來作為抗菌及抗病毒劑，比起包含一價銅化合物粒子卻不滿足上述L*值範圍的樹脂組成物，可表現出更高的抗菌及抗病毒性，進而完成本發明。
[解決問題的技術手段]
本發明的主旨如下。
[1] 一種抗菌及抗病毒樹脂組成物，其包含一價銅化合物粒子作為有效成分而具有抗菌及抗病毒性，該抗菌及抗病毒樹脂組成物在日本工業規格JIS Z 8781-4的L*a*b*的表色系中的L*值為0以上且小於40。
[2] 如上述[1]所述之抗菌及抗病毒樹脂組成物，其中，包含黑色顏料。
[3] 如上述[1]所述之抗菌及抗病毒樹脂組成物，其中，該抗菌及抗病毒樹脂組成物是利用黑色染料進行染色。
[4] 如上述[1]～[3]中任一項所述之抗菌及抗病毒樹脂組成物，其中，前述抗菌及抗病毒樹脂組成物為纖維、薄膜或薄片。
[5] 如上述[1]所述之抗菌及抗病毒樹脂組成物，其中，前述一價銅化合物粒子為氯化物、乙酸鹽、硫化物、碘化物、溴化物、過氧化物、氧化物、硫氰化物或該等的混合物。
[6] 如上述[1]所述之抗菌及抗病毒樹脂組成物，其中，作為前述一價銅化合物粒子，含有選自由CuCl、CuOOCCH
3、CuI、CuBr、Cu
2O、Cu
2S及CuSCN所組成之群組中的1種或2種以上的化合物粒子。
[7] 如上述[1]所述之抗菌及抗病毒樹脂組成物，其中，作為前述一價銅化合物粒子，含有CuI粒子。
[8] 如上述[1]所述之抗菌及抗病毒樹脂組成物，其中，含有選自由碳黑、鈦黑及酞菁所組成之群組中的1種或2種以上。
[發明的效果]
根據本發明，能夠提供一種新穎的抗菌及抗病毒樹脂組成物。
以下，詳細敘述本實施形態的抗菌及抗病毒樹脂組成物。
首先，本實施形態的抗菌及抗病毒樹脂組成物包含樹脂與一價銅化合物粒子，並且在日本工業規格JIS Z 8781-4的L*a*b*的表色系中的L*值為0以上且小於40。
日本工業規格JIS Z 8781-4的L*a*b*的表色系中的L*值表示色彩的明亮度(明度)，a*值、b*值表示顯示出色相與彩度的色度。
日本工業規格JIS Z 8781-4的L*值為0以上且小於40的本實施形態的抗菌及抗病毒樹脂組成物，例如具有黑色的外觀。
有關本實施形態的樹脂組成物，要作成日本工業規格JIS Z 8781-4的L*a*b*的表色系中的L*值為0以上且小於40，例如能夠使用染色顏料來將樹脂組成物進行著色。其中，從耐久性這點來看，較佳是使用顏料(有機顏料、無機顏料)。此外，也可以混合複數種顏色的染色顏料來作成日本工業規格JIS Z 8781-4的L*a*b*的表色系中的L*值為0以上且小於40。
再者，日本工業規格JIS Z 8781-4所規定的L*a*b*的表色系中的L*值，例如能夠使用色差計來測定。此外，當使用染色顏料來將樹脂組成物進行著色時，染色顏料的含量並無特別限定，例如只要依據色差計的測定值以L*值成為0以上且小於40的方式來調整等即可。例如，在抗菌及抗病毒樹脂組成物100質量%中，染色顏料能夠設為0.05質量%以上且2.0質量%以下，較佳能夠設為0.1質量%以上且1.5質量%以下。
作為有機顏料能夠列舉：偶氮顏料、酞菁顏料、多環顏料(喹吖酮系、苝系、環萘酮(perinone)系、異吲哚啉酮系、異吲哚啉系、二噁嗪系、硫靛系、蒽醌系、喹啉黃系、金屬錯合物系、二酮吡咯并吡咯系等)、染料色澱系顏料等。
作為無機顏料能夠列舉：硫酸鋇、鋅白、硫酸鉛、鉛黃、鋅黃、氧化鐵紅(III)、鎘紅、群青藍、普魯士藍、氧化鉻綠、鈷綠、琥珀色、碳黑、骨黑、石墨、鈦黑、鐵黑、合成鐵黑、氧化鈦、四氧化鐵等的金屬氧化物粉末、金屬硫化物粉末、金屬粉末等。
作為染料，能夠列舉：偶氮系染料、蒽醌系染料、酞菁系染料、醌亞胺系染料、喹啉系染料、硝基系染料、羰基系染料、次甲基系染料等。
該等之中，從使抗病毒性及抗菌性提升的觀點來看，較佳是含有選自由碳黑、鈦黑及酞菁所組成之群組中的1種或2種以上。
構成本實施形態的樹脂組成物的樹脂，並無特別限定，能夠適當選擇。可列舉例如：聚乙烯樹脂、聚丙烯樹脂、聚苯乙烯樹脂、ABS樹脂、AS樹脂、AES樹脂、EVA樹脂、聚甲基戊烯樹脂、聚氯乙烯樹脂、聚偏二氯乙烯樹脂、聚丙烯酸甲酯樹脂、聚乙酸乙烯樹脂、聚醯胺樹脂、聚醯亞胺樹脂、聚碳酸酯樹脂、聚乙烯對苯二甲酸酯樹脂、聚對苯二甲酸丁二醇酯樹脂、聚縮醛樹脂、聚芳酯樹脂、聚碸樹脂等的熱塑性樹脂；矽氧樹脂；聚苯乙烯彈性體等的苯乙烯系彈性體、聚乙烯彈性體和聚丙烯彈性體等的烯烴系彈性體、聚胺酯彈性體等的聚胺酯系彈性體、氯化乙烯系彈性體、聚酯系彈性體、尼龍系彈性體等的熱塑性彈性體。
此外，本實施形態的抗菌及抗病毒樹脂組成物包含一價銅化合物粒子作為抗菌及抗病毒劑。已知一價銅化合物粒子原本就具有非常高的抗菌及抗病毒性，其機制並不清楚，但是認為若與空氣中或飛沫中的水分接觸，一價銅離子會溶解出來，而經溶出的一價銅離子藉由與細菌或病毒接觸會釋放出電子，此時，所產生的活性物種會對細菌或病毒賦予某種破壞。作為一價銅化合物粒子，具體而言較佳是：氯化物、乙酸鹽(乙酸化合物)、硫化物、碘化物、溴化物、過氧化物、氧化物、硫氰化物或該等的混合物。該等之中，從使抗病毒性及抗菌性提升的觀點來看，一價銅化合物粒子更佳是選自由CuCl、CuOOCCH
3、CuI、CuBr、Cu
2O、Cu
2S及CuSCN所組成之群組中的至少1種，進一步較佳是包含CuI(碘化銅(I))粒子。
本實施形態的抗菌及抗病毒樹脂組成物中的一價銅化合物粒子的含量，能夠依據所期望的抗菌功能及抗病毒功能適當地設定，例如相對於抗菌及抗病毒樹脂組成物100質量%，能夠設為0.5質量%以上且小於40質量%，較佳能夠設為1質量%以上且小於8質量%。
一價銅化合物粒子的粒徑並無特別限定，發明所屬技術領域中具有通常知識者能夠適當設定，較佳是平均粒徑為1 nm以上且小於500 nm。這是因為當平均粒徑小於1 nm時物性會不穩定，當平均粒徑為500 nm以上時，比起小於500 nm的情況，抗菌及抗病毒效果會變低的緣故。再者，本說明書中，所謂平均粒徑意指體積平均粒徑。體積平均粒徑例如能夠基於雷射都卜勒法(動態電氣泳動光散射法)來測定。測定裝置並無特別限定，例如能夠使用Zeta電位粒徑測定系統(大塚電子股份有限公司製造)。
本實施形態的抗菌及抗病毒樹脂組成物，不論基因體的種類和是否具病毒套膜，皆能夠降低各式各樣的病毒的感染力或使各式各樣的病毒失去活性。作為該病毒，能夠列舉例如：鼻病毒、小兒麻痺病毒、口蹄疫病毒、輪狀病毒、諾羅病毒、腸病毒、肝病毒、星狀病毒、札幌病毒、E型肝炎病毒、A型流感病毒、B型流感病毒、C型流感病毒、副流感病毒、腮腺炎病毒、麻疹病毒、人類間質肺炎病毒、呼吸道融合細胞病毒、立百病毒、亨德拉病毒、黃熱病病毒、登革熱病毒、日本腦炎病毒、西尼羅河病毒、B型肝炎病毒、C型肝炎病毒、東方馬腦炎病毒及西方馬腦炎病毒、奧絨絨病毒(O’Nyong-Nyong virus)、德國麻疹病毒、拉薩病毒、胡寧病毒(Junin virus)、馬丘波病毒(Machupo virus)、瓜納里托病毒(Guanarito virus)、薩比亞病毒(Sabia virus)、克里米亞-剛果出血熱病毒、白蛉熱病毒、漢他病毒、無名病毒(Sin Nombre virus)、狂犬病病毒、伊波拉病毒、馬堡病毒、蝙蝠狂犬病病毒、人類嗜T淋巴球病毒、人類免疫缺乏病毒、人類冠狀病毒、SARS(嚴重急性呼吸道症候群)冠狀病毒、人類微小病毒、多瘤病毒、人類乳突病毒、腺病毒、皰疹病毒、水痘帶狀皰疹病毒、EB病毒、人類巨細胞病毒、天花病毒、猴痘病毒、牛痘病毒、傳染性軟疣病毒、副痘病毒、茲卡病毒、新型冠狀病毒(covid-19)等。
進一步，本實施形態的抗菌及抗病毒樹脂組成物能夠去除活性的細菌並無特別限定，不論是格蘭氏陽性、格蘭氏陰性、好氣性、厭氣性等的性質，能夠將各式各樣的細菌進行殺菌。作為具體性的細菌，可列舉例如：大腸桿菌、金黃色葡萄球菌、表皮葡萄球菌、鏈球菌、肺炎鏈球菌、流感嗜血桿菌、百日咳菌、腸炎桿菌、克雷伯氏肺炎桿菌、綠膿桿菌、弧菌、沙門氏菌、霍亂弧菌、赤痢桿菌、炭疽桿菌、結核桿菌、肉毒桿菌、破傷風桿菌、鏈球菌等。
本實施形態的樹脂組成物可含有一價銅化合物粒子以外的其他成分。作為其他成分，能夠列舉：塑化劑、乾燥劑、硬化劑、抗結皮劑、消光劑、抗流掛劑、抗黴劑、紫外線吸收劑、熱射線吸收劑、潤滑劑、界面活性劑、增黏劑、黏度調節劑、穩定劑、乾燥調節劑、顏料、分散劑、
抗黴組成物、抗過敏原組成物、催化劑、抗反射材料、具有隔熱特性之材料。其他成分可包含2種以上。其他成分所含有的態樣並無特別限定，可以作成分散於樹脂組成物的內部，也可以作成分散於樹脂組成物內部的部分的其他成分自樹脂組成物的表面露出，也可以作成固定於樹脂組成物的表面。
再者，本實施形態的抗菌及抗病毒樹脂組成物，例如作成薄膜、薄片、成形體，除此之外還能夠作成纖維或纖維結構體。作為纖維，可以是短纖維，也可以是長纖維，可以是單絲纖維，也可以是複絲纖維。作為纖維結構體，可列舉：織物、針織物、不織布、混抄紙等。
繼而，詳細地敘述本實施形態的抗菌及抗病毒樹脂組成物的製造方法的一例。再者，以下，列舉本實施形態的抗菌及抗病毒樹脂組成物作成纖維的情況為例進行說明。
首先，製作母料顆粒(master batch pellet)，其是抗菌及抗病毒劑也就是一價銅化合物粒子混合(分散)而成。母料顆粒例如如以下的操作來製造。
將已粉碎的一價銅化合物粒子與習知的分散劑混合，以分散劑包覆一價銅化合物粒子的表面後，將該一價銅化合物粒子與樹脂顆粒混合，然後使用揉合擠壓機，藉此使一價銅化合物粒子分散於樹脂顆粒的內部。或者，將已粉碎的一價銅化合物粒子和分散劑與樹脂顆粒混合，然後使用揉合擠壓機，藉此在揉合過程中分散劑會被吸引至一價銅化合物微粒的周圍，其結果，能夠以分散劑包覆一價銅化合物微粒，並且會使該一價銅化合物微粒分散於樹脂顆粒的內部。將揉合物冷卻後，使用製粒機將已含有一價銅化合物粒子之樹脂切割為小塊，獲得混合(分散)有一價銅化合物粒子而成之母料顆粒。再者，在製造母料顆粒時的一價銅化合物粒子的比例(濃度)，發明所屬技術領域中具有通常知識者能夠適當設定。
所獲得的母料顆粒，使用成型機與上述染色顏料和樹脂以及依據需要的其他成分熔融揉合，來製造紡絲原料。然後將所獲得的紡絲原料供以熔融紡絲步驟，藉此即能夠獲得本實施形態的纖維。針對熔融紡絲步驟，並未限定於特定的方法，能夠使用習知的方法。針對紡絲溫度，只要能夠在樹脂黏度適度地低的狀態下自紡絲口吐出，還不會引發樹脂的劣化和熱解，紡絲步驟不會顯著地不穩定從而藉由之後的延伸處理能夠獲得高強度的纖維這樣的範圍，即可適當選擇配合纖維材料的溫度區域。
在熔融紡絲步驟中，將紡絲原料自紡絲口吐出，將經吐出的纖維狀的紡絲原料冷卻來進行硬化，而作成纖維。具體而言，例如在空氣、水、甘油等的溶媒中，將經吐出的紡絲原料冷卻至硬化溫度以下來硬化。當為利用水冷式的冷卻的情況，加熱至60℃左右然後進行緩慢冷卻，藉此能夠在對水槽導入纖維時以不搖動的方式通過水槽，因此冷卻時的穩定性優異。當為空氣冷卻時，空氣的溫度、風速能夠任意地設定，為了要抑制分子配向，期望是風速低並且溫度不要過低。若在冷卻的時間點時分子配向的程度高，當在之後步驟要實行加熱延伸步驟時，纖維會變得不易延伸，有時會變得難以獲得抗菌及抗病毒效果。
然後，捲取已硬化的纖維。捲取速度能夠設定任意的速度。但是，當捲取速度比熔融未延伸絲的自由落體速度更為低速時，會變得無法獲得均勻的未延伸絲，有時會導致延伸性的降低。再者，當在之後步驟要實行加熱延伸步驟時，也可以直接供以加熱延伸步驟而不捲取已硬化的絲。
繼而，說明加熱延伸步驟。加熱延伸步驟，是將在紡絲步驟中所捲取的纖維(未延伸絲)進行加熱而延展的步驟。加熱延伸步驟可以具有複數個延伸步驟。當加熱延伸步驟具有複數個延伸步驟時，各延伸步驟中的延伸倍率的合計為總延伸倍率。再者，當加熱延伸步驟由單次的進行延伸的步驟所構成時，該單次的進行延伸的步驟中的延伸倍率為總延伸倍率。
本實施形態的抗菌及抗病毒樹脂組成物的一例之纖維，藉由進行加熱延伸可表現更優異的抗菌及抗病毒性，並且能夠效率良好地使附著於纖維表面等的細菌和病毒失去活性。特別是，當纖維為單絲纖維時，藉由加熱延伸能夠進一步提高抗菌及抗病毒效果。藉由加熱延伸使得抗菌及抗病毒效果能大幅度地提升的機制現在仍不清楚，但是認為是以下理由。在紡絲步驟中，熔融狀態的纖維若開始冷卻，纖維的表層部會直接冷卻硬化，存在於比表層部更靠纖維的內側的部分(內層部)的抗菌及抗病毒劑會呈不易與纖維的外部的水分接觸的結構。另一方面，內層部會隔著表層部進行冷卻硬化，因此內層部的冷卻速度會變得低於表層部的冷卻速度。因此認為，表層部的纖維結構會與內層部的纖維結構不同。若在這樣的狀態下實行加熱延伸，會在玻璃轉移溫度以上的加熱條件下實行延伸，表層部的纖維結構會成為抗菌及抗病毒劑容易與纖維的外部的水分接觸的纖維結構。並且認為，藉由加熱延伸，表層部的纖維結構會靠近內層部的纖維結構，因此能夠對細菌和病毒表面的電荷和DNA等造成某種影響而使其失去活性。
針對延伸方法並無特別限定，能夠採用熱輥延伸法、熱板延伸法、管狀延伸法、延伸吹塑法、雷射延伸法等的習知的延伸方法。當利用熱輥延伸法進行加熱延伸時，藉由改變以多段組合而成的熱輥的轉速，能夠將未延伸絲延伸為高倍率。
延伸倍率可依據被延伸物的纖度適當選擇，通常是以總延伸倍率為3.0以上且7.0倍以下的方式設定，較佳是4.0以上且6.0倍以下。藉由將延伸倍率設為3.0以上且7.0倍以下，能夠使分子進一步配向而獲得更高強度的纖維。當延伸倍率小於3.0倍時，與延伸倍率為3.0倍以上的情況相比，抗菌及抗病毒效果較低，並且所獲得的纖維的強度會降低。此外，當延伸倍率超過7.0倍時，延伸張力會變得極高，因此會經常發生斷絲而有製絲性降低的情況。
再者，本實施形態的抗菌及抗病毒樹脂組成物的一例之纖維，可具有芯鞘結構。此時，例如藉由芯部以通常的樹脂(不含一價銅化合物粒子之樹脂)形成，並且鞘部以含有一價銅化合物粒子且日本工業規格JIS Z 8781-4的L*a*b*的表色系中的L*值為0以上且小於40的樹脂形成，藉此會有下述優點：不僅能夠使纖維的強度提升，還能夠降低一價銅化合物粒子的含量。芯部的樹脂與鞘部的樹脂可以相同，也可以是不同的樹脂。
與芯鞘結構的纖維的長度方向正交的剖面形狀並無特別限定，較佳是將剖面形狀作成圓形，並且較佳是芯部及鞘部皆形成為同心圓狀。在與纖維的長度方向正交的剖面中，芯部的面積與鞘部的面積的比率並無特別限定，使用者能夠適當設定。
本實施形態的抗菌及抗病毒樹脂組成物的一例之纖維，能夠作成織物、針織物、不織布、混抄紙等的紙類來使用。並且，該纖維能夠用於各式各樣的如下製品：薄片狀的製品，其是衣類、寢具、寢飾材料、口罩、手帕、毛巾、地毯、窗簾、外壁材料、建築材料、內飾材料等；濾網，其用於空氣清淨機和空調、換氣扇、吸塵器、風扇、空調用及車輛用等；魚籠和定置網等的漁網；污水處理的濾網；飲用水用濾網；壓艙水處理用濾網；防護衣類；防護網；防蟲網；雞舍用網等。從而，本實施形態的抗菌及抗病毒樹脂組成物的一例之纖維是在各式各樣的技術領域中能夠提供優異的各種製品而有用的材料。
[實施例]
繼而，列舉實施例更具體地說明本發明。但是本發明並未僅限於該等實施例。
(實施例1)
使用碘化銅(I)作為一價銅化合物粒子。作為有效成分，熔融並混合成為下述量的如下成分：5 wt%的含有碘化銅(I)(粒徑：350 nm)之聚乙烯母料顆粒(NBC Meshtec Inc.製造的Cufitec(註冊商標)MB-PE)；5 wt%的含碳黑系黑色顏料之聚丙烯母料顆粒；及，90 wt%的聚丙烯樹脂。
使用被設置於熔融紡絲裝置中的熔融擠壓機，將所獲得的混合物熔融，然後自設置於熔融紡絲裝置中的紡絲口吐出，一邊在水槽中進行冷卻一邊以規定的速度捲取，藉此獲得樹脂組成物也就是抗菌及抗病毒性纖維。所獲得的抗菌及抗病毒性纖維的纖維徑為150 μm。
所獲得的抗菌及抗病毒性纖維100質量%中，黑色顏料為1.0質量%。
所獲得的抗菌及抗病毒性纖維100質量%中，碘化銅(I)為2.0質量%。
針對所獲得的抗菌及抗病毒性纖維，使用色差計(柯尼卡美能達公司製造，色差儀器CR-10(色差計)，以下相同)，測定日本工業規格JIS Z 8781-4所規定的L*a*b*的表色系中的L*值時，L*=16.5。
(實施例2)
將含碳黑系黑色顏料之聚丙烯母料顆粒變更為1.5 wt%的含鈦黑系黑色顏料之聚丙烯母料顆粒，並變更為93.5 wt%的聚丙烯樹脂，除此之外，利用與實施例1相同的方法作成抗菌及抗病毒性纖維。所獲得的抗菌及抗病毒性纖維的纖維徑為150 μm，並且當測定此時的日本工業規格JIS Z 8781-4所規定的L*a*b*的表色系中的L*值時，L*=1.8。
所獲得的抗菌及抗病毒性纖維100質量%中，黑色顏料為0.3質量%。
此外，所獲得的抗菌及抗病毒性纖維100質量%中，碘化銅(I)為2.0質量%。
(實施例3)
將含碳黑系黑色顏料之聚丙烯母料顆粒變更為1.0 wt%的含酞菁系黑色顏料之聚丙烯母料顆粒並變更為94 wt%的聚丙烯樹脂，除此之外，利用與實施例1相同的方法作成抗菌及抗病毒性纖維。所獲得的抗菌及抗病毒性纖維的纖維徑為150 μm，並且當測定此時的日本工業規格JIS Z 8781-4所規定的L*a*b*的表色系中的L*值時，L*=35。
所獲得的抗菌及抗病毒性纖維100質量%中，黑色顏料為0.2質量%。
此外，所獲得的抗菌及抗病毒性纖維100質量%中，碘化銅(I)為2.0質量%。
(實施例4)
使用碘化銅(I)作為一價銅化合物粒子。作為有效成分，熔融並混合成為下述量的如下成分：5 wt%的含有碘化銅(I)(粒徑：350 nm)之聚乙烯母料顆粒(NBC Meshtec Inc.製造的Cufitec(註冊商標)MB-PE)；5 wt%的含碳黑系黑色顏料之聚丙烯母料顆粒；及，90 wt%的聚乙烯樹脂。使用雙軸擠壓機(東洋精機股份有限公司製造，Labo Plastomill(註冊商標))，將所獲得的混合物進行薄膜化，而獲得實施例4的樹脂組成物也就是抗菌及抗病毒性薄膜。所獲得的薄膜的厚度為120 μm，並且在抗菌及抗病毒性薄膜100質量%中，碘化銅(I)為2.0質量%。當測定此時的日本工業規格JIS Z 8781-4所規定的L*a*b*的表色系中的L*值時，L*=35.6。
所獲得的抗菌及抗病毒性薄膜100質量%中，黑色顏料為1.0質量%。
此外，所獲得的抗菌及抗病毒性薄膜100質量%中，碘化銅(I)為2.0質量%。
(比較例1)
除了不添加碳黑系黑色顏料以外，利用與實施例1相同的方法進行紡絲，獲得比較例1的抗菌及抗病毒性纖維。所獲得的抗菌及抗病毒性纖維的纖維徑為150 μm。
針對抗菌及抗病毒性纖維，使用色差計測定日本工業規格JIS Z 8781-4所規定的L*a*b*的表色系中的L*值時，L*=85.2。
此外，所獲得的抗菌及抗病毒性纖維100質量%中，碘化銅(I)為2.0質量%。
(比較例2)
除了不添加鈦黑系黑色顏料以外，利用與實施例2相同的方法進行紡絲，獲得比較例2的抗菌及抗病毒性纖維。所獲得的抗菌及抗病毒性纖維的纖維徑為150 μm。
針對抗菌及抗病毒性纖維，使用色差計測定日本工業規格JIS Z 8781-4所規定的L*a*b*的表色系中的L*值時，L*=57.3。
此外，所獲得的抗菌及抗病毒性纖維100質量%中，碘化銅(I)為2.0質量%。
(比較例3)
除了不添加酞菁系黑色顏料以外，利用與實施例3相同的方法進行紡絲，獲得比較例3的抗菌及抗病毒性纖維。所獲得的抗菌及抗病毒性纖維的纖維徑為150 μm。
針對抗菌及抗病毒性纖維，使用色差計測定日本工業規格JIS Z 8781-4所規定的L*a*b*的表色系中的L*值時，L*=63.1。
此外，所獲得的抗菌及抗病毒性纖維100質量%中，碘化銅(I)為2.0質量%。
(比較例4)
除了不添加碳黑系黑色顏料以外，利用與實施例4相同的方法進行薄膜化，獲得比較例4的抗菌及抗病毒性薄膜。所獲得的抗菌及抗病毒性薄膜的厚度為120 μm，使用色差計測定日本工業規格JIS Z 8781-4所規定的L*a*b*的表色系中的L*值時，L*=61.7。
此外，所獲得的抗菌及抗病毒性薄膜100質量%中，碘化銅(I)為2.0質量%。
(比較例5)
不添加含有碘化銅(I)(粒徑：350 nm)作為有效成分之母料顆粒，並且將聚乙烯樹脂量設為95 wt%，除此以外，利用與實施例1相同的方法進行紡絲，獲得比較例4的纖維。所獲得的纖維的纖維徑為150 μm。
針對所獲得的抗菌及抗病毒性纖維，使用色差計測定日本工業規格JIS Z 8781-4所規定的L*a*b*的表色系中的L*值時，L*=7.6。
所獲得的纖維100質量%中，黑色顏料為1.0質量%。
＜抗病毒性的測定＞
針對實施例1～4、比較例1～5的抗病毒性的測定，使用流感病毒並依據日本工業規格JIS L1922「溶斑測定法」來測定。將結果顯示於表1。再者，作為對照組使用的標準布，設為依據日本工業規格JIS L 0803的試驗用白布 棉(細白布(canequim)3號)。
[表1]
| L* | 感染價數(Log PFU) | |
| 2小時 | ||
| 標準布 | - | 6.77 |
| 實施例1 | 16.5 | ＜2.30 |
| 實施例2 | 1.8 | 3.75 |
| 實施例3 | 35 | 3.25 |
| 實施例4 | 35.6 | ＜2.30 |
| 比較例1 | 85.2 | 5.26 |
| 比較例2 | 57.3 | 4.38 |
| 比較例3 | 63.1 | 4.61 |
| 比較例4 | 61.7 | 4.76 |
| 比較例5 | 7.6 | 7.08 |
| 接種病毒數 | - | 7.28 |
如同由表1所能夠理解，在含有抗病毒劑也就是一價銅化合物粒子且L*值為0以上且小於40這樣的全部的實施例中，表現出優異的抗病毒功能。相對於此，即便含有抗病毒劑也就是一價銅化合物粒子但是L*值高於40的比較例1～4則呈現了抗病毒性低於實施例1～4的結果。此外，在L*值為0以上且小於40但是不含抗病毒劑也就是一價銅化合物粒子之比較例5中，並未觀察到抗病毒效果。
＜抗菌性的測定＞
針對實施例1～4、比較例1～5的抗菌性的測定，使用金黃色葡萄球菌並依據日本工業規格JIS L1902來測定。將結果顯示於表2。
[表2]
| L* | 生菌數(Log CFU) | |
| 18小時 | ||
| 標準布 | - | 5.72 |
| 實施例1 | 16.5 | ＜1.30 |
| 實施例2 | 1.8 | 1.52 |
| 實施例3 | 35 | ＜1.30 |
| 實施例4 | 35.6 | ＜1.30 |
| 比較例1 | 85.2 | 3.47 |
| 比較例2 | 57.3 | 3.58 |
| 比較例3 | 63.1 | 3.47 |
| 比較例4 | 61.3 | 4.38 |
| 比較例5 | 7.6 | 6.77 |
| 接種菌數 | - | 4.68 |
如同由表2所能夠理解，在含有抗病毒劑也就是一價銅化合物粒子且L*值為0以上且小於40之實施例1～4中，表現出在18小時為偵測極限值以下或3Log CFU以下這樣的優異抗菌性。相對於此，即便含有抗菌劑也就是一價銅化合物粒子但是L*值高於40的比較例1～4呈現了抗菌性低於全部的實施例的結果。此外，在L*值為0以上且小於40但是不含抗病毒劑也就是一價銅化合物粒子之比較例5中，菌仍有增殖。
無
無
國內寄存資訊(請依寄存機構、日期、號碼順序註記)
無
國外寄存資訊(請依寄存國家、機構、日期、號碼順序註記)
無
Claims (8)
- 一種抗菌及抗病毒樹脂組成物，其包含一價銅化合物粒子作為有效成分而具有抗菌及抗病毒性， 該抗菌及抗病毒樹脂組成物在日本工業規格JIS Z 8781-4的L*a*b*的表色系中的L*值為0以上且小於40。
- 如請求項1所述之抗菌及抗病毒樹脂組成物，其中，包含黑色顏料。
- 如請求項1所述之抗菌及抗病毒樹脂組成物，其中，該抗菌及抗病毒樹脂組成物是利用黑色染料進行染色。
- 如請求項1～3中任一項所述之抗菌及抗病毒樹脂組成物，其中，前述抗菌及抗病毒樹脂組成物為纖維、薄膜或薄片。
- 如請求項1所述之抗菌及抗病毒樹脂組成物，其中，前述一價銅化合物粒子為氯化物、乙酸鹽、硫化物、碘化物、溴化物、過氧化物、氧化物、硫氰化物或該等的混合物。
- 如請求項1所述之抗菌及抗病毒樹脂組成物，其中，作為前述一價銅化合物粒子，含有選自由CuCl、CuOOCCH 3、CuI、CuBr、Cu 2O、Cu 2S及CuSCN所組成之群組中的1種或2種以上的化合物粒子。
- 如請求項1所述之抗菌及抗病毒樹脂組成物，其中，作為前述一價銅化合物粒子，含有CuI粒子。
- 如請求項1所述之抗菌及抗病毒樹脂組成物，其中，含有選自由碳黑、鈦黑及酞菁所組成之群組中的1種或2種以上。