TW202328462A - 無方向性電磁鋼板及其製造方法 - Google Patents

無方向性電磁鋼板及其製造方法 Download PDF

Info

Publication number
TW202328462A
TW202328462A TW111148046A TW111148046A TW202328462A TW 202328462 A TW202328462 A TW 202328462A TW 111148046 A TW111148046 A TW 111148046A TW 111148046 A TW111148046 A TW 111148046A TW 202328462 A TW202328462 A TW 202328462A
Authority
TW
Taiwan
Prior art keywords
rolling
less
steel sheet
hot
invention example
Prior art date
Application number
TW111148046A
Other languages
English (en)
Inventor
田中孝明
大久保智幸
Original Assignee
日商杰富意鋼鐵股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日商杰富意鋼鐵股份有限公司 filed Critical 日商杰富意鋼鐵股份有限公司
Publication of TW202328462A publication Critical patent/TW202328462A/zh

Abstract

本發明的無方向性電磁鋼板以質量%計包含C：0.010%以下、Si：1.0%以上且5.0%以下、Mn：0.05%以上且5.0%以下、P：0.1%以下、S：0.01%以下、Al：3.0%以下、N：0.005%以下，且剩餘部分為Fe及不可避免的雜質，平均結晶粒徑為60 μm以上且200 μm以下，＜100＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S A與＜111＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S B滿足S A-S B≧0。

Description

無方向性電磁鋼板及其製造方法
本發明是有關於一種無方向性電磁鋼板及其製造方法。
近年來，就對全球變暖等環境問題的考慮而言，要求削減CO 2排放量及節能化，於汽車領域中，正推進併用發動機與馬達的混合動力電動汽車（hybrid electric vehicle，HEV）、僅由電動馬達驅動的電動汽車（electric vehicle，EV）及燃料電池電動汽車（fuel cell electric vehicle，FCEV）等的開發。用於所述HEV、EV及FCEV等的馬達為了馬達效率的高效率化，一般而言是於有利於高速旋轉的高頻區域被驅動。所述馬達的鐵芯材料中大多使用無方向性電磁鋼板，為了達成馬達效率的高效率化，對所述鋼板強烈要求高頻區域下的低鐵損化。
先前，無方向性電磁鋼板主要藉由添加Si或Al等合金元素來提高電阻率，或使板厚變薄來減少渦流損耗，從而實現了低鐵損化。然而，合金元素的大量添加即便可達成低鐵損化，亦會導致飽和磁通密度的降低。飽和磁通密度的降低會導致馬達的銅損增加，因此導致馬達效率的降低。另外，板厚的減少需要使熱軋鋼板的板厚變薄或提高冷軋壓下率，因此會導致生產性的降低。因此認為，若可開發一種不會導致飽和磁通密度降低或生產性降低的高磁通密度-高頻低鐵損的無方向性電磁鋼板，則對馬達的高效率化有很大貢獻。
作為於高頻區域下獲得低鐵損的無方向性電磁鋼板的技術，例如專利文獻1中揭示有一種藉由添加Cr來提高鋼的電阻率，實現高頻區域下的低鐵損化的方法。 [現有技術文獻] [專利文獻]
專利文獻1：日本專利特開平11-343544號公報
[發明所欲解決之課題] 然而，Cr是使飽和磁通密度降低的元素。因此，於專利文獻1所揭示的技術中，無法兼顧高磁通密度與高頻低鐵損，無法充分地滿足近來對無方向性電磁鋼板的要求。
本發明是為解決所述課題而成，其目的在於提供一種不會導致飽和磁通密度降低或生產性降低的、高磁通密度-高頻低鐵損的無方向性電磁鋼板及其製造方法。 [解決課題之手段]
本發明者等人對所述課題的解決進行了努力研究，結果了解到，藉由對鋼板組織進行控制，以使＜100＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S A與＜111＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S B滿足S A-S B≧0，從而可獲得磁通密度高、且於高頻區域下為低鐵損的無方向性電磁鋼板。進而，亦發現，藉由將退火步驟中的加熱時的急熱停止溫度或中間保持時間等設為適當的範圍，可對朝向特定方位的結晶粒的面積率進行控制。
本發明是基於該見解而成者，具有以下的結構。
本發明的無方向性電磁鋼板以質量%計包含C：0.010%以下、Si：1.0%以上且5.0%以下、Mn：0.05%以上且5.0%以下、P：0.1%以下、S：0.01%以下、Al：3.0%以下、N：0.005%以下，且剩餘部分為Fe及不可避免的雜質，平均結晶粒徑為60 μm以上且200 μm以下，＜100＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S A與＜111＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S B滿足S A-S B≧0。
可為：＜100＞朝向軋製45°方向及軋製-45°方向的結晶粒的面積率之和S C與＜111＞朝向軋製45°方向及軋製-45°方向的結晶粒的面積率之和S D滿足5×S C-S D≧0。
可為：以質量%計更包含0.0005%以上且0.0050%以下的Co。
可為：以質量%計更包含0.0005%以上且0.0050%以下的Zn。
可為：以質量%計更含有下述A群組～D群組中的至少一個群組的成分、以及選自Cu：0%以上且0.5%以下、Ni：0%以上且0.5%以下、W：0%以上且0.05%以下、Ti：0%以上且0.005%以下、Nb：0%以上且0.005%以下、V：0%以上且0.010%以下、Ta：0%以上且0.002%以下、B：0%以上且0.002%以下、Ga：0%以上且0.005%以下、Pb：0%以上且0.002%以下、As：0%以上且0.05%以下及Ge：0%以上且0.05%以下中的一種或兩種以上。
·A群組；Mo：0.01%以上且0.20%以下 ·B群組；Cr：0.1%以上且5.0%以下 ·C群組；Ca：0.001%以上且0.10%以下、Mg：0.001%以上且0.10%以下及稀土金屬（rare earth metal，REM）：0.001%以上且0.10%以下中的任意一種或兩種以上 ·D群組；Sn：0.001%以上且0.20%以下及Sb：0.001%以上且0.20%以下中的任意一種或兩種
本發明的無方向性電磁鋼板的製造方法是製造本發明的無方向性電磁鋼板的方法，包括：熱軋步驟，藉由對具有所述無方向性電磁鋼板的組成的鋼原材料實施熱軋而獲得熱軋板；熱軋板退火步驟，視需要對所述熱軋板實施熱軋板退火；酸洗步驟，對所述熱軋板及實施了所述熱軋板退火的所述熱軋板實施酸洗；冷軋步驟，藉由對實施了所述酸洗的所述熱軋板實施冷軋而獲得冷軋板；以及退火步驟，以自200℃至400℃以上且600℃以下的保持溫度T 1的平均升溫速度V 1為50℃/s以上、保持溫度T 1下的保持時間t為1秒以上且10秒以下、自保持溫度T 1至750℃的平均升溫速度V 2為15℃/s以上的條件，將所述冷軋板加熱至875℃以上且1050℃以下的退火溫度T 2，並進行冷卻，藉此獲得冷軋退火板。
可為：以最終道次的工作輥徑為150 mmϕ以上、最終道次的壓下率為15%以上、最終道次的應變速度為100 s -1以上且1300 s -1以下的條件進行所述冷軋步驟。 [發明的效果]
藉由本發明，可提供一種不會導致飽和磁通密度降低或生產性降低的、高磁通密度-高頻低鐵損的無方向性電磁鋼板及其製造方法。因此，藉由使用本發明的無方向性電磁鋼板及其製造方法，可達成馬達的高效率化。目的在於減少衝壓時的應變引起的鐵損的上升，即便對本發明的無方向性電磁鋼板實施應變消除退火，所述效果亦不受任何影響。
以下，一併對本發明的詳細情況及其限定理由進行說明。
＜鋼板的成分組成＞ 首先，對本發明的無方向性電磁鋼板（以下，簡記為「鋼板」）及馬達鐵芯所具有的較佳的成分組成進行說明。成分組成中的元素的含量的單位均為「質量%」，以下，只要並無特別說明則僅由「%」表示。
C：0.010%以下 C是於馬達的使用中形成碳化物而引起磁時效並使馬達的鐵損特性劣化的有害元素。為了避免磁時效，鋼板中所含的C設為0.010%以下。較佳為0.004%以下。C添加量的下限並無特別規定，但過度地減少了C的鋼板非常昂貴，因此較佳為設為0.0001%左右。
Si：1.0%以上且5.0%以下 Si具有提高鋼的電阻率、減少鐵損的效果，另外，具有藉由固溶強化而提高鋼的強度的效果。為了獲得此種效果，只要將Si添加量設為1.0%以上即可。另一方面，若Si添加量超過5.0%，則伴隨飽和磁通密度的降低，磁通密度顯著降低，因此將上限設為5.0%以下。因此，Si添加量設為1.0%以上且5.0%以下的範圍。較佳為1.5%以上且未滿4.5%的範圍，更佳為2.0%以上且未滿4.0%的範圍。
Mn：0.05%以上且5.0%以下 Mn與Si同樣地是對提高鋼的電阻率與強度而言有用的元素。為了獲得此種效果，需要含有0.05%以上的Mn。另一方面，超過5.0%的添加有時會促進MnC的析出而使馬達的磁特性劣化，因此上限設為5.0%。因此，Mn添加量設為0.05%以上且5.0%以下。較佳為0.1%以上且3.0%以下的範圍。
P：0.1%以下 P是用於鋼的強度（硬度）調整的有用的元素。然而，若P添加量超過0.1%，則韌性降低，加工時容易產生裂紋，因此上限設為0.1%。下限並無特別規定，但由於過度地減少了P的鋼板非常昂貴，因此設為0.001%。P添加量較佳為0.003%以上且0.08%以下的範圍。
S：0.01%以下 S是形成微細析出物而對馬達的鐵損特性帶來不良影響的元素。特別是，若S添加量超過0.01%，則其不良影響變得顯著，因此上限設為0.01%。下限並無特別規定，但由於過度地減少了S的鋼板非常昂貴，因此設為0.0001%。S添加量較佳為0.0003%以上且0.0080%以下的範圍。
Al：3.0%以下 Al與Si同樣地是具有提高鋼的電阻率、減少鐵損的效果的有用的元素。為了獲得此種效果，較佳為添加0.005%以上。更佳為0.010%以上，進而佳為0.015%以上。另一方面，超過3.0%的添加有時會助長鋼板表面的氮化，使磁特性劣化，因此將上限設為3.0%。更佳為2.0%以下。
N：0.0050%以下 N是形成微細析出物而對鐵損特性帶來不良影響的元素。特別是，若添加量超過0.0050%，則其不良影響變得顯著，因此上限設為0.0050%。下限並無特別規定，但由於過度地減少了N的鋼板非常昂貴，因此設為0.0005%。N添加量較佳為0.0008%以上且0.0030%以下的範圍。
於本發明的無方向性電磁鋼板中，所述成分以外的剩餘部分為Fe及不可避免的雜質。進而，根據要求特性，除了含有所述成分組成以外，亦可於下述範圍內含有選自Co、Zn、Mo、Cr、Ca、Mg、REM、Sn、Sb、Cu、Ni、W、Ti、Nb、V、Ta、B、Ga、Pb、As及Ge中的一種或兩種以上。
Co：0.0005%以上且0.0050%以下 Co具有如下效果：於將退火步驟中的加熱時的急熱停止溫度或中間保持時間等設為適當的範圍時，使＜100＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S A增加，使＜111＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S B降低。即，藉由微量地添加Co可穩定地實現S A-S B≧0。為了獲得此種效果，只要將Co添加量設為0.0005%以上即可。另一方面，若Co超過0.0050%，則效果飽和，徒然導致成本的上升，因此將上限設為0.0050%。因此，Co較佳為於0.0005%以上且0.0050%以下的範圍內添加。
Zn：0.0005%以上且0.0050%以下 Zn具有如下效果：於將退火步驟中的加熱時的急熱停止溫度或中間保持時間等設為適當的範圍時，使＜100＞朝向軋製45°方向及軋製-45°方向的結晶粒的面積率之和S C增加，使＜111＞朝向軋製45°方向及軋製-45°方向的結晶粒的面積率之和S D降低。即，藉由微量地添加Zn可穩定地實現5×S C-S D≧0。為了獲得此種效果，只要將Zn添加量設為0.0005%以上即可。另一方面，若Zn超過0.0050%則效果飽和，徒然導致成本的上升，因此將上限設為0.0050%。因此，Zn較佳為於0.0005%以上且0.0050%以下的範圍內添加。
Mo：0.01%以上且0.20%以下 Mo具有於鋼中形成微細的碳化物、提高鋼板的強度的效果。為了獲得此種效果，只要將Mo添加量設為0.01%以上即可。另一方面，若Mo添加量超過0.20%，則過度地形成碳化物，鐵損劣化，因此將上限設為0.20%。因此，Mo較佳為於0.01%以上且0.20%以下的範圍內添加。
Cr：0.1%以上且5.0%以下 Cr具有提高鋼的電阻率、減少鐵損的效果。為了獲得此種效果，只要將Cr添加量設為0.1%以上即可。另一方面，若Cr添加量超過0.1%，則伴隨飽和磁通密度的降低，磁通密度顯著降低，因此將上限設為5.0%。因此，Cr較佳為於0.1%以上且5.0%以下的範圍內添加。
Ca：0.001%以上且0.10%以下 Ca是將S以硫化物的形式固定，有助於鐵損的減少的元素。為了獲得此種效果，Ca添加量只要設為0.001%以上即可。另一方面，若Ca添加量超過0.10%，則效果飽和，徒然導致成本的上升，因此將上限設為0.10%。因此，Ca較佳為於0.001%以上且0.10%以下的範圍內添加。
Mg：0.001%以上且0.10%以下 Mg是將S以硫化物的形式固定，有助於鐵損的減少的元素。為了獲得此種效果，Mg添加量只要設為0.001%以上即可。另一方面，若Mg添加量超過0.10%，則效果飽和，徒然導致成本的上升，因此將上限設為0.10%。因此，Mg較佳為於0.001%以上且0.10%以下的範圍內添加。
REM：0.001%以上且0.10%以下 REM是將S以硫化物的形式固定，有助於鐵損的減少的元素群組。為了獲得此種效果，REM添加量只要設為0.001%以上即可。另一方面，若REM添加量超過0.10%，則效果飽和，徒然導致成本的上升，因此將上限設為0.10%。因此，REM較佳為於0.001%以上且0.10%以下的範圍內添加。
Sn：0.001%以上且0.20%以下 Sn是藉由織構改善而對磁通密度提高及鐵損減少有效果的元素。為了獲得此種效果，Sn添加量只要設為0.001%以上即可。另一方面，若Sn添加量超過0.20%，則效果飽和，徒然導致成本的上升，因此將上限設為0.20%。因此，Sn較佳為於0.001%以上且0.20%以下的範圍內添加。
Sb：0.001%以上且0.20%以下 Sb是藉由織構改善而對磁通密度提高及鐵損減少有效果的元素。為了獲得此種效果，Sb添加量只要設為0.001%以上即可。另一方面，若Sb添加量超過0.20%，則效果飽和，徒然導致成本的上升，因此將上限設為0.20%。因此，Sb較佳為於0.001%以上且0.20%以下的範圍內添加。
Cu：0%以上且0.5%以下、Ni：0%以上且0.5%以下 Cu、Ni是提高鋼的韌性的元素，可適宜添加。然而，即便添加超過0.5%，所述效果亦飽和，因此添加量的上限較佳為分別設為0.5%。更佳為添加量分別為0.01%以上且0.1%以下的範圍。
W：0%以上且0.05%以下 W經由形成微細碳化物並藉由析出強化而提高鋼板強度來提高衝壓疲勞強度，因此可適宜添加。另一方面，若添加量超過所述範圍，則過度地形成碳化物，鐵損劣化。因此，W的添加量設為0%以上且0.05%以下的範圍。較佳的添加量的上限為0.02%。
Ti：0%以上且0.005%以下、Nb：0%以上且0.005%以下、V：0%以上且0.010%以下、Ta：0%以上且0.002%以下 Ti、Nb、V、Ta經由形成微細的碳氮化物並藉由析出強化而提高鋼板強度來提高衝壓疲勞強度，因此可適宜添加。另一方面，若添加量超過所述範圍，則過度地形成碳氮化物，鐵損劣化。因此，Ti、Nb、V、Ta的添加量分別設為Ti：0%以上且0.005%以下、Nb：0%以上且0.005%以下、V：0%以上且0.010%以下、Ta：0%以上且0.002%以下的範圍。較佳的添加量的上限為Ti：0.002%、Nb：0.002%、V：0.005%、Ta：0.001%。
B：0%以上且0.002%以下、Ga：0%以上且0.005%以下 B、Ga經由形成微細的氮化物並藉由析出強化而提高鋼板強度來提高衝壓疲勞強度，因此可適宜添加。另一方面，若添加量超過所述範圍，則過度地形成氮化物，鐵損劣化。因此，B、Ga的添加量分別設為B：0%以上且0.002%以下、Ga：0%以上且0.005%以下的範圍。較佳的添加量的上限為B：0.001%、Ga：0.002%。
Pb：0%以上且0.002%以下 Pb經由形成微細的Pb粒子並藉由析出強化而提高鋼板強度來提高衝壓疲勞強度，因此可適宜添加。另一方面，若添加量超過所述範圍，則過度地形成Pb粒子，鐵損劣化。因此，Pb的添加量設為0%以上且0.002%以下的範圍。較佳的添加量的上限為0.001%。
As：0%以上且0.05%以下、Ge：0%以上且0.05%以下 As、Ge是藉由織構改善而對磁通密度提高及鐵損減少有效果的元素，可適宜添加。然而，即便添加超過0.05%，所述效果亦飽和。因此，添加量的上限較佳為分別設為0.05%。更佳為添加量分別為0.002%以上且0.01%以下的範圍。
＜鋼板的微觀組織＞ 接著，對本發明的無方向性電磁鋼板的微觀組織進行說明。
《平均結晶粒徑d為60 μm以上且200 μm以下》 根據本發明者等人的研究，若平均結晶粒徑d粗大，則鐵損降低。即，藉由將平均結晶粒徑d設為60 μm以上，可達成目標鐵損特性。另一方面，若平均結晶粒徑d過度粗大，則由於渦流損耗的增加，鐵損反而上升。即，藉由將平均結晶粒徑d設為200 μm以下，可達成目標鐵損特性。
《＜100＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S A與＜111＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S B滿足S A-S B≧0》 根據本發明者等人的研究判明，對於具有規定的成分組成的鋼，藉由設為＜100＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S A與＜111＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S B滿足S A-S B≧0的鋼板組織，鋼板的磁通密度提高，並且鐵損減少。結晶方位的容許誤差設為15°。即，若為S A-S B≧0，則磁通密度及鐵損滿足適用於HEV、EV及FCEV的馬達所需的值，因此設為S A-S B≧0。較佳為S A-S B≧2%，更佳為S A-S B≧5%。
《＜100＞朝向軋製45°方向及軋製-45°方向的結晶粒的面積率之和S C與＜111＞朝向軋製45°方向及軋製-45°方向的結晶粒的面積率之和S D滿足5×S C-S D≧0》 根據本發明者等人的研究判明，於所述鋼板組織的基礎上，還製成如下鋼板組織，即＜100＞朝向軋製45°方向及軋製-45°方向的結晶粒的面積率之和S C與＜111＞朝向軋製45°方向及軋製-45°方向的結晶粒的面積率之和S D滿足5×S C-S D≧0的鋼板組織，藉此磁特性的各向異性減少。各向異性的減少有助於提高馬達效率，因此作為適用於HEV、EV及FCEV的馬達用材料更佳。因此，較佳為滿足5×S C＞S D。更佳為5×S C＞S D≧1%。
接著，對本發明的無方向性電磁鋼板的製造方法進行說明。
概略而言，本發明的無方向性電磁鋼板的製造方法是如下方法：藉由對具有所述成分組成的鋼原材料依次實施熱軋、視需要的熱軋板退火、酸洗、冷軋、退火，獲得所述本發明的無方向性電磁鋼板。於本發明的無方向性電磁鋼板的製造方法中，只要本發明中規定的成分、冷軋、退火條件為本發明的範圍內，則除此以外通常可為公知的方法。
＜鋼原材料＞ 鋼原材料只要是具有所述組成的鋼原材料，則並無特別限定。鋼原材料的熔煉方法並無特別限定，可採用使用轉爐或電爐等的公知的熔煉方法。就生產性等問題而言，較佳為於熔煉後藉由連續鑄造法製成板坯（鋼原材料），但亦可藉由造塊-分塊軋製法或薄板坯連鑄法等公知的鑄造方法製成板坯。
＜熱軋步驟＞ 熱軋步驟是藉由對具有所述組成的鋼原材料實施熱軋而獲得熱軋板的步驟。熱軋步驟只要是對具有所述組成的鋼原材料進行加熱、實施熱軋而獲得規定尺寸的熱軋板的步驟，則並無特別限定，可適用常用的熱軋步驟。
作為常用的熱軋步驟，例如，可例示如下熱軋步驟，即，將鋼原材料加熱至1000℃以上且1200℃以下的溫度，以800℃以上且950℃以下的精軋製出側溫度對加熱後的鋼原材料實施熱軋，熱軋結束後，實施恰當的軋製後冷卻（例如，以20℃/s以上且100℃/s以下的平均冷卻速度於450℃以上且950℃以下的溫度區域進行冷卻），以400℃以上且700℃以下的捲取溫度進行捲取，從而製成規定尺寸形狀的熱軋板。
＜熱軋板退火步驟＞ 熱軋板退火步驟是藉由對所述熱軋板進行加熱並保持高溫來對熱軋板進行退火的步驟。熱軋板退火步驟並無特別限定，可適用常用的熱軋板退火步驟。該步驟並非必需，亦可省略。
＜酸洗步驟＞ 酸洗步驟是對所述熱軋板退火步驟後的鋼板或者於省略熱軋板退火步驟的情況下對所述熱軋板實施酸洗的步驟。酸洗步驟只要是可酸洗至可對酸洗後的鋼板實施冷軋的程度的步驟，則並無特別限定，例如可適用使用鹽酸或硫酸等的常用的酸洗步驟。該酸洗步驟可與所述熱軋板退火步驟於同一生產線內連續實施，亦可於另一生產線上實施。
＜冷軋步驟＞ 冷軋步驟是對經過了酸洗步驟的酸洗板實施冷軋的步驟。冷軋步驟只要是可將酸洗後的鋼板壓下至所期望的板厚的步驟，則並無特別限定，可適用常用的冷軋步驟。另外，亦可視需要藉由隔著中間退火的兩次以上的冷軋製成規定尺寸的冷軋板，此情況下的中間退火條件並無特別限定，可適用常用的中間退火步驟。較佳為如下冷軋步驟：藉由以最終道次的工作輥徑D為150 mmϕ以上、最終道次的壓下率r為15%以上及最終道次的應變速度（ε' m）為100 s -1以上且1300 s -1以下的條件實施冷軋而獲得冷軋板。
（最終道次的工作輥徑D） 於本發明的無方向性電磁鋼板的製造中，最終道次的工作輥徑D設為150 mmϕ以上。將最終道次的工作輥徑D設為150 mmϕ以上的理由在於，設為5×S C-S D≧0，獲得所期望的鋼板組織。於最終道次的工作輥徑D小於150 mmϕ的情況下，與平面壓縮的狀態相隔較遠，因此與工作輥徑大的情況相比，結晶粒單位下的剪切應變的不均勻性增強。後續的退火步驟中的成核及晶粒生長容易集中於特定方位的區域，因此＜100＞於軋製45°方向及軋製-45°方向上配向的結晶粒的面積率之和S C減小，＜111＞於所述軋製45°方向及軋製-45°方向上配向的結晶粒的面積率之和S D增加。結果，無法滿足5×S C-S D≧0。另一方面，於最終道次的工作輥徑D為150 mmϕ以上的情況下，滿足5×S C-S D≧0，獲得所期望的鋼板組織。最終道次的工作輥徑D較佳為170 mmϕ以上，進而佳為200 mmϕ以上。上限不需要特別設置，但於輥徑過大的情況下軋製載荷增大，因此較佳為設為700 mmϕ。
（最終道次的壓下率r） 於本發明的無方向性電磁鋼板的製造中，最終道次的壓下率r較佳為15%以上。將最終道次的壓下率r設為15%以上的理由在於，獲得一系列的冷軋控制的效果，以容易獲得所期望的鋼板組織。於最終道次的壓下率r未滿15%的情況下，壓下率過低，因此難以對退火後的組織進行控制。另一方面，於最終道次的壓下率r為15%以上的情況下，發揮出一系列的冷軋控制的效果。其結果，容易獲得所期望的鋼板組織。最終道次的壓下率r較佳為20%以上。於本發明中，不需要規定最終道次的壓下率r的上限，但過高的壓下率要求極大的裝置能力，另外，冷軋板的形狀控制亦變得困難，因此通常為50%以下。
（最終道次的應變速度（ε' m）） 於本發明的無方向性電磁鋼板的製造中，最終道次的應變速度（ε' m）較佳為100 s -1以上且1300 s -1以下。將最終道次的應變速度（ε' m）設為100 s -1以上且1300 s -1以下的理由在於，於抑制軋製中的斷裂的同時設為5×S C-S D≧0，獲得所期望的鋼板組織。於最終道次的應變速度（ε' m）未滿100 s -1的情況下，冷軋板的結晶粒單位下的剪切應變的不均勻性增強，後續的退火步驟中的成核及晶粒生長容易集中於特定方位的區域，因此＜100＞於軋製45°方向及軋製-45°方向上配向的結晶粒的面積率之和S C減小，＜111＞於所述軋製45°方向及軋製-45°方向上配向的結晶粒的面積率之和S D增加。結果，無法滿足5×S C-S D≧0。理由未必明確，但本發明者等人推定其原因在於，應變速度低而導致流動應力降低，應變容易集中於容易變形的結晶方位的結晶粒上，應變分佈不均勻化。另一方面，於最終道次的應變速度超過1300 s -1的情況下，流動應力過度增大，容易發生軋製中的脆性斷裂。於最終道次的應變速度（ε' m）為100 s -1以上且1300 s -1以下的情況下，於抑制軋製中的斷裂的同時滿足5×S C-S D≧0。最終道次的應變速度（ε' m）較佳為150 s -1以上，較佳為1300 s -1以下。本發明的冷軋時的各道次中的應變速度（ε' m）是使用以下的數式（1）所示的愛克倫德（Ekelund）的近似式導出。
[數1] ···（1）
此處，v R為輥圓周速度（mm/s），R'為輥半徑（mm），h 1為輥入側板厚（mm），r為壓下率（%）。
＜退火步驟＞ 退火步驟是對經過了冷軋步驟的冷軋板實施退火的步驟。更詳細而言，為如下退火步驟：以自200℃至400℃以上且600℃以下的保持溫度T 1的平均升溫速度V 1為50℃/s以上、保持溫度T 1下的保持時間t為1秒以上且10秒以下、保持溫度T 1至750℃的平均升溫速度V 2為15℃/s以上的條件，將經過了冷軋步驟的冷軋板加熱至875℃以上且1050℃以下的退火溫度T 2，並進行冷卻，藉此獲得冷軋退火板。退火步驟之後，對冷軋退火板的表面實施絕緣塗佈，所述方法及塗佈種類並無特別限定，可適用常用的絕緣塗佈步驟。
（保持溫度T 1） 於本發明的無方向性電磁鋼板的製造中，加熱升溫中的保持溫度T 1設為400℃以上且600℃以下。將保持溫度T 1設為400℃以上且600℃以下的理由在於，設為＜100＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S A與＜111＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S B滿足S A-S B≧0的範圍，獲得所期望的鋼板組織。於保持溫度T 1未滿400℃的情況下，溫度過低，因此無法獲得保持的效果，導致S B變高，結果，無法滿足S A-S B≧0。另一方面，於保持溫度T 1為600℃以上的情況下，不僅面積率的和S B而且面積率的和S A亦降低，因此結果無法滿足S A-S B≧0。
（自200℃至保持溫度T 1的平均升溫速度V 1） 於本發明的無方向性電磁鋼板的製造中，自200℃至保持溫度T 1的平均升溫速度V 1設為50℃/s以上。將平均升溫速度V 1設為50℃/s以上的理由在於，設為＜100＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S A與＜111＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S B滿足S A-S B≧0的範圍，獲得所期望的鋼板組織。於平均升溫速度V 1未滿所述速度的情況下，保持溫度T 1下的保持以前發生恢復，因此無法充分地控制恢復行為，S B及S A均降低，結果無法滿足S A-S B≧0。自200℃至保持溫度T 1的平均升溫速度V 1較佳為70℃/s以上，更佳為100℃/s以上。上限不需要特別設置，但若升溫速度過度高，則容易產生溫度不均，因此較佳為設為500℃/s。
（保持溫度T 1下的保持時間t） 於本發明的無方向性電磁鋼板的製造中，保持溫度T 1下的保持時間t設為1秒以上且10秒以下。將保持時間t設為1秒以上且10秒以下的理由在於，設為＜100＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S A與＜111＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S B滿足S A-S B≧0的範圍，獲得所期望的鋼板組織。於保持時間t未滿1秒的情況下，組織的恢復不充分，因此S B變高，結果無法滿足S A-S B≧0。另一方面，於保持時間t超過10秒的情況下，過度地產生組織的恢復，不僅S B而且S A亦降低，因此結果無法滿足S A-S B≧0。
（自保持溫度T 1至750℃的平均升溫速度V 2） 於本發明的無方向性電磁鋼板的製造中，自保持溫度T 1至750℃的平均升溫速度V 2設為15℃/s以上。將平均升溫速度V 2設為15℃/s以上的理由在於，設為＜100＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S A與＜111＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S B滿足S A-S B≧0的範圍，獲得所期望的鋼板組織。於平均升溫速率V 2未滿15℃/s的情況下，再結晶核的生成位置的選擇性增強，＜111＞朝向軋製方向或軋製直角方向的結晶粒的生成頻率提高，因此S B增加。結果，無法滿足S A-S B≧0。平均升溫速度V 2較佳為20℃/s以上，更佳為30℃/s以上。上限不需要特別設置，但若升溫速度過度高，則容易產生溫度不均，因此較佳為設為200℃/s。
（退火溫度T 2） 於本發明的無方向性電磁鋼板的製造中，退火溫度T 2設為875℃以上且1050℃以下。將退火溫度T 2設為875℃以上且1050℃以下的理由在於，將平均結晶粒徑設為60 μm以上，獲得所期望的鋼板組織。於退火溫度T 2未滿875℃的情況下，再結晶粒無法充分地晶粒生長，無法將平均結晶粒徑設為60 μm以上。於退火溫度T 2為875℃以上的情況下，產生充分的晶粒生長，可將平均結晶粒徑設為60 μm以上。退火溫度T 2較佳為900℃以上。另一方面，於退火溫度T 2超過1050℃的情況下，再結晶粒過度生長，而無法將平均結晶粒徑設為200 μm以下。因此，退火溫度T 2設為1050℃以下。較佳為1025℃以下。加熱至所述退火溫度後進行冷卻，但就防止冷卻不均的觀點而言，所述冷卻較佳為以50℃/s以下的速度進行。 [實施例]
以下列舉實施例對本發明進行具體說明。但是，本發明並不限定於該些。
＜冷軋退火板的製造＞ 藉由通常公知的方法對具有表1-1、表1-2所示的成分組成的鋼水進行熔煉，並進行連續鑄造而製成厚度230 mm的板坯（鋼原材料）。藉由對所獲得的板坯實施熱軋，而獲得板厚2.0 mm的熱軋板。藉由公知的方法對所獲得的熱軋板實施熱軋板退火及酸洗，繼而，實施冷軋直至表2-1、表2-2所示的板厚為止，從而獲得冷軋板。以表2-1、表2-2所示的條件對所獲得的冷軋板實施退火，繼而藉由公知的方法實施塗佈，從而獲得冷軋退火板（無方向性電磁鋼板）。
[表1-1] （表1-1）
鋼 種 成分組成[質量%] 備註
C Si Mn P S Al N Co Zn Mo Cr Ca Mg REM Sn Sb
A 0.0016 3.5 0.3 0.004 0.0029 0.6 0.0022 - - - - - - - - - 適合例
B 0.0038 2.4 1.2 0.011 0.0033 1.2 0.0021 - - - - - - - - - 適合例
C 0.0035 3.5 0.2 0.019 0.0017 1.1 0.0015 - - - - - - - - - 適合例
D 0.0034 2.1 1.3 0.015 0.0027 0.9 0.0024 - - - - - - - - - 適合例
E 0.0033 2.2 0.6 0.005 0.0033 1.8 0.0026 - - - - - - - - - 適合例
F 0.0038 2.7 2.7 0.008 0.0021 0.5 0.0020 - - - - - - - - - 適合例
G 0.0027 2.9 1.2 0.006 0.0031 1.9 0.0024 - - - - - - - - - 適合例
H 0.0009 2.3 1.2 0.011 0.0024 1.4 0.0025 - - - - - - - - - 適合例
I 0.0029 2.9 1.0 0.012 0.0037 1.2 0.0027 - - - - - - - - - 適合例
J 0.0015 3.9 0.7 0.013 0.0008 1.5 0.0023 - - - - - - - - - 適合例
K 0.0047 2.2 1.3 0.009 0.0021 1.3 0.0024 - - - - - - - - - 適合例
L 0.0017 0.8 0.8 0.013 0.0007 1.5 0.0021 - - - - - - - - - 比較例
M 0.0016 1.2 0.8 0.012 0.0009 1.5 0.0022 - - - - - - - - - 適合例
N 0.0013 1.5 0.7 0.011 0.0009 1.6 0.0022 - - - - - - - - - 適合例
O 0.0015 4.8 0.7 0.015 0.0005 1.5 0.0022 - - - - - - - - - 適合例
P 0.0017 5.2 0.7 0.014 0.0005 1.4 0.0024 - - - - - - - - - 比較例
Q 0.0035 2.1 0.02 0.017 0.0028 0.9 0.0023 - - - - - - - - - 比較例
R 0.0036 2.1 0.08 0.013 0.0023 0.8 0.0026 - - - - - - - - - 適合例
S 0.0035 2.0 3.4 0.013 0.0030 0.8 0.0026 - - - - - - - - - 適合例
T 0.0034 2.1 5.1 0.015 0.0023 1.0 0.0022 - - - - - - - - - 比較例
U 0.0031 3.0 1.0 0.011 0.0033 0.003 0.0028 - - - - - - - - - 比較例
V 0.0029 3.0 1.0 0.010 0.0038 0.012 0.0028 - - - - - - - - - 適合例
W 0.0028 2.8 1.0 0.014 0.0038 2.2 0.0027 - - - - - - - - - 適合例
X 0.0030 2.9 1.1 0.012 0.0039 3.4 0.0028 - - - - - - - - - 比較例
Y 0.0035 3.4 0.3 0.020 0.0018 1.1 0.0013 0.0007 - - - - - - - - 適合例
Z 0.0037 3.5 0.2 0.017 0.0014 1.1 0.0016 0.0038 - - - - - - - - 適合例
AA 0.0037 3.4 0.2 0.018 0.0020 1.0 0.0014 - 0.0008 - - - - - - - 適合例
AB 0.0033 3.6 0.2 0.019 0.0016 1.1 0.0013 - 0.0029 - - - - - - - 適合例
AC 0.0016 3.5 0.3 0.003 0.0031 0.6 0.0023 - - 0.035 - - - - - - 適合例
AD 0.0015 3.5 0.3 0.005 0.0028 0.6 0.0023 - - - 0.14 - - - - - 適合例
AE 0.0017 3.6 0.4 0.005 0.0024 0.5 0.0023 - - - - 0.004 - - - - 適合例
AF 0.0014 3.5 0.2 0.003 0.0030 0.6 0.0020 - - - - - 0.003 - - - 適合例
AG 0.0018 3.5 0.3 0.002 0.0029 0.6 0.0023 - - - - - - 0.005 - - 適合例
AH 0.0017 3.5 0.4 0.006 0.0031 0.7 0.0022 - - - - - - - 0.032 - 適合例
AI 0.0016 3.5 0.3 0.003 0.0033 0.6 0.0024 - - - - - - - - 0.054 適合例
[表1-2] （表1-2）
鋼 種 成分組成[質量%] 備註
C Si Mn P S Al N Co Zn Mo Cr Ca Mg REM Sn Sb Cu Ni W Ti Nb V Ta B Ga Pb As Ge
AJ 0.0034 3.4 0.3 0.021 0.0013 1.0 0.0013 0.0021 - - - - - - - - - - - - - - - - - - - - 適合例
AK 0.0037 3.4 0.2 0.017 0.0021 1.0 0.0017 - 0.0046 - - - - - - - - - - - - - - - - - - - 適合例
AL 0.0014 3.4 0.4 0.003 0.0031 0.6 0.0023 - - 0.013 - - - - - - - - - - - - - - - - - - 適合例
AM 0.0015 3.5 0.4 0.004 0.0030 0.6 0.0021 - - - 4.3 - - - - - - - - - - - - - - - - - 適合例
AN 0.0017 3.5 0.2 0.005 0.0030 0.6 0.0023 - - - - 0.001 - - - - - - - - - - - - - - - - 適合例
AO 0.0016 3.5 0.3 0.003 0.0032 0.5 0.0022 - - - - - 0.096 - - - - - - - - - - - - - - - 適合例
AP 0.0015 3.5 0.3 0.003 0.0032 0.6 0.0023 - - - - - - 0.093 - - - - - - - - - - - - - - 適合例
AQ 0.0015 3.5 0.3 0.003 0.0026 0.7 0.0020 - - - - - - - 0.17 - - - - - - - - - - - - - 適合例
AR 0.0018 3.6 0.3 0.005 0.0033 0.7 0.0024 - - - - - - - - 0.18 - - - - - - - - - - - - 適合例
AS 0.0040 2.3 1.2 0.011 0.0031 1.2 0.0019 - - - - - - - - - 0.03 - - - - - - - - - - - 適合例
AT 0.0038 2.5 1.2 0.011 0.0036 1.3 0.0021 - - - - - - - - - 0.49 - - - - - - - - - - - 適合例
AU 0.0037 2.5 1.2 0.012 0.0037 1.2 0.0023 - - - - - - - - - - 0.02 - - - - - - - - - - 適合例
AV 0.0037 2.5 1.1 0.013 0.0030 1.2 0.0022 - - - - - - - - - - 0.46 - - - - - - - - - - 適合例
AW 0.0032 2.3 0.5 0.003 0.0030 1.8 0.0026 - - - - - - - - - - - 0.006 - - - - - - - - - 適合例
AX 0.0034 2.2 0.7 0.006 0.0029 1.8 0.0024 - - - - - - - - - - - 0.043 - - - - - - - - - 適合例
AY 0.0035 2.1 0.5 0.005 0.0036 1.8 0.0028 - - - - - - - - - - - - 0.0016 - - - - - - - - 適合例
AZ 0.0032 2.1 0.5 0.005 0.0033 1.9 0.0025 - - - - - - - - - - - - 0.0047 - - - - - - - - 適合例
BA 0.0031 2.2 0.5 0.003 0.0029 1.8 0.0026 - - - - - - - - - - - - - 0.0007 - - - - - - - 適合例
BB 0.0032 2.2 0.5 0.005 0.0029 1.7 0.0025 - - - - - - - - - - - - - 0.0045 - - - - - - - 適合例
BC 0.0032 2.3 0.5 0.003 0.0032 1.7 0.0028 - - - - - - - - - - - - - - 0.0011 - - - - - - 適合例
BD 0.0032 2.2 0.5 0.007 0.0038 1.9 0.0024 - - - - - - - - - - - - - - 0.0095 - - - - - - 適合例
BE 0.0034 2.2 0.6 0.003 0.0031 1.8 0.0025 - - - - - - - - - - - - - - - 0.0004 - - - - - 適合例
BF 0.0032 2.1 0.7 0.005 0.0030 1.8 0.0025 - - - - - - - - - - - - - - - 0.0017 - - - - - 適合例
BG 0.0039 2.7 2.7 0.007 0.0024 0.5 0.0020 - - - - - - - - - - - - - - - - 0.0002 - - - - 適合例
BH 0.0038 2.7 2.6 0.006 0.0016 0.5 0.0020 - - - - - - - - - - - - - - - - 0.0018 - - - - 適合例
BI 0.0039 2.7 2.7 0.010 0.0020 0.5 0.0022 - - - - - - - - - - - - - - - - - 0.0002 - - - 適合例
BJ 0.0039 2.6 2.6 0.008 0.0022 0.5 0.0022 - - - - - - - - - - - - - - - - - 0.0047 - - - 適合例
BK 0.0040 2.7 2.6 0.010 0.0022 0.4 0.0022 - - - - - - - - - - - - - - - - - - 0.0002 - - 適合例
BL 0.0040 2.6 2.6 0.007 0.0020 0.5 0.0020 - - - - - - - - - - - - - - - - - - 0.0019 - - 適合例
BM 0.0028 2.9 1.1 0.004 0.0026 2.0 0.0023 - - - - - - - - - - - - - - - - - - - 0.004 - 適合例
RN 0.0028 2.9 1.1 0.004 0.0031 1.9 0.0024 - - - - - - - - - - - - - - - - - - - 0.043 - 適合例
BO 0.0029 2.9 1.1 0.004 0.0036 1.9 0.0025 - - - - - - - - - - - - - - - - - - - - 0.002 適合例
BP 0.0030 3.0 1.3 0.009 0.0036 2.0 0.0027 - - - - - - - - - - - - - - - - - - - - 0.046 適合例
[表2-1] （表2-1）
No. 鋼種    板厚 [mm] 冷軋步驟 退火步驟 備註
   最終道次的 工作輥徑D [mmϕ] 最終道次的 壓下率r[%] 最終道次的 應變速度 [s -1] 軋製中的 斷裂 保持溫度 T 1[℃] 升溫速度 V 1[℃/s] 保持時間 t[s] 升溫速度 V 2[℃/s] 退火溫度T 2[℃]
1 A    0.25 290 28 780 - 490 270 2 34 1000 發明例
2 B    0.25 330 23 860 - 480 460 3 53 990 發明例
3 C    0.25 360 31 300 - 590 120 9 33 920 發明例
4 D    0.25 390 27 260 - 470 120 7 31 1010 發明例
5 E    0.25 360 23 200 - 420 480 2 55 940 發明例
6 F    0.25 340 25 190 - 590 320 9 49 1000 發明例
7 G    0.25 290 29 700 - 440 310 5 37 1010 發明例
8 H    0.25 360 24 510 - 420 350 3 33 960 發明例
9 I    0.25 200 33 690 - 500 380 3 54 990 發明例
10 J    0.25 210 34 710 - 510 190 3 47 910 發明例
11 K    0.25 360 24 510 - 420 340 3 34 960 發明例
12 L    0.25 210 34 710 - 510 190 3 47 910 比較例
13 M    0.25 210 34 710 - 510 200 3 47 910 發明例
14 N    0.25 210 34 710 - 510 190 3 49 910 發明例
15 O    0.25 210 34 710 - 510 180 3 49 910 發明例
16 P    0.25 210 34 710 - 510 190 3 46 910 比較例
17 Q    0.25 390 27 260 - 470 120 7 30 1010 比較例
18 R    0.25 390 27 260 - 470 120 7 32 1010 發明例
19 S    0.25 390 27 260 - 470 120 7 31 1010 發明例
20 T    0.25 390 27 260 - 470 130 7 33 1010 比較例
21 U    0.25 200 33 690 - 500 370 3 52 990 比較例
22 V    0.25 200 33 690 - 500 400 3 56 990 發明例
23 W    0.25 200 33 690 - 500 380 3 54 990 發明例
24 X    0.25 200 33 690 - 500 360 3 55 990 比較例
25 Y    0.25 360 31 300 - 590 130 9 32 920 發明例
26 Z    0.25 360 31 300 - 590 120 9 32 920 發明例
27 AA    0.25 360 31 300 - 590 120 9 33 920 發明例
28 AB    0.25 360 31 300 - 590 120 9 31 920 發明例
29 AC    0.25 290 28 780 - 490 260 2 33 1000 發明倒
30 AD    0.25 290 28 780 - 490 280 2 35 1000 發明例
31 AE    0.25 290 28 780 - 490 270 2 34 1000 發明例
32 AF    0.25 290 28 780 - 490 270 2 33 1000 發明例
33 AG    0.25 290 28 780 - 490 270 2 35 1000 發明例
34 AH    0.25 290 28 780 - 490 260 2 33 1000 發明例
35 AI    0.25 290 28 780 - 490 270 2 34 1000 發明例
36 J    0.25 210 34 710 - 630 190 3 46 910 比較例
37 J    0.25 210 34 710 - 380 190 3 47 910 比較例
38 D    0.25 390 27 260 - 470 30 7 31 1010 比較例
39 D    0.25 390 27 260 - 470 60 7 31 1010 發明例
40 D    0.25 390 27 260 - 470 90 7 32 1010 發明例
41 G    0.25 290 29 700 - 440 300 0 37 1010 比較例
42 G    0.25 290 29 700 - 440 300 15 38 1010 比較例
43 I    0.25 200 33 690 - 500 380 3 8 990 比較例
44 I    0.25 200 33 690 - 500 400 3 17 990 發明例
45 I    0.25 200 33 690 - 500 380 3 24 990 發明例
46 C    0.25 360 31 300 - 500 120 3 33 860 比較例
47 C    0.25 360 31 300 - 590 120 9 33 880 發明例
48 C    0.25 360 31 300 - 590 120 9 34 1040 發明例
49 C    0.25 360 31 300 - 590 130 9 33 1070 比較例
50 A    0.25 110 28 780 - 490 270 2 32 1000 發明例
51 A    0.25 160 28 780 - 490 280 2 35 1000 發明例
52 A    0.25 180 28 780 - 490 270 2 33 1000 發明例
53 A    0.25 290 9 780 - 490 270 2 35 1000 發明例
54 A    0.25 290 17 780 - 490 280 2 34 1000 發明例
55 A    0.25 290 28 60 - 490 260 2 34 1000 發明例
56 A    0.25 290 28 120 - 490 260 2 33 1000 發明例
57 A    0.25 290 28 1400 一部分斷裂 490 260 2 34 1000 發明例
註）下劃線部分表示發明範圍外
[表2-2] （表2-2）
No. 鋼種 板厚 [mm] 冷軋步驟 退火步驟 備註  
最終道次的 工作輥徑D [mmϕ] 最終道次的 壓下率r [%] 最終道次的 應變速度 [s -1] 軋製中的 斷裂 保持溫度 T 1[℃] 升溫速度 V 1[℃/s] 保持時間 t [s] 升溫速度 V 2[℃/s] 退火溫度 T 2[℃]  
58 AJ 0.25 360 31 300 - 590 120 9 31 920 發明例
59 AK 0.25 360 31 300 - 590 120 9 32 920 發明例
60 AL 0.25 290 28 780 - 490 270 2 33 1000 發明例
61 AM 0.25 290 28 780 - 490 260 2 35 1000 發明例
62 AN 0.25 290 28 780 - 490 260 2 34 1000 發明例
63 AO 0.25 290 28 780 - 490 260 2 33 1000 發明例
64 AP 0.25 290 28 780 - 490 280 2 35 1000 發明例
65 AQ 0.25 290 28 780 - 490 280 2 33 1000 發明例
66 AR 0.25 290 28 780 - 490 260 2 34 1000 發明例
67 AS 0.25 330 23 860 - 480 470 3 53 990 發明例
68 AT 0.25 330 23 860 - 480 460 3 52 990 發明例
69 AU 0.25 330 23 860 - 480 480 3 53 990 發明例
70 AV 0.25 330 23 860 - 480 450 3 54 990 發明例
71 AW 0.25 360 23 200 - 420 480 2 57 940 發明例
72 AX 0.25 360 23 200 - 420 480 2 57 940 發明例
73 AY 0.25 360 23 200 - 420 470 2 57 940 發明例
74 AZ 0.25 360 23 200 - 420 470 2 54 940 發明例
75 BA 0.25 360 23 200 - 420 490 2 54 940 發明例
76 BB 0.25 360 23 200 - 420 460 2 55 940 發明例
77 BC 0.25 360 23 200 - 420 490 2 53 940 發明例
78 BD 0.25 360 23 200 - 420 490 2 55 940 發明例
79 BE 0.25 360 23 200 - 420 460 2 55 940 發明例
80 BF 0.25 360 23 200 - 420 500 2 52 940 發明例
81 BG 0.25 340 25 190 - 590 320 9 50 1000 發明例
82 BH 0.25 340 25 190 - 590 330 9 50 1000 發明例
83 BI 0.25 340 25 190 - 590 320 9 48 1000 發明例
84 BJ 0.25 340 25 190 - 590 330 9 51 1000 發明例
85 BK 0.25 340 25 190 - 590 330 9 48 1000 發明例
86 BL 0.25 340 25 190 - 590 320 9 51 1000 發明例
87 BM 0.25 290 29 700 - 440 320 5 36 1010 發明例
88 BN 0.25 290 29 700 - 440 290 5 38 1010 發明例
89 BO 0.25 290 29 700 - 440 300 5 37 1010 發明例
90 BP 0.25 290 29 700 - 440 320 5 39 1010 發明例
＜評價＞ 《組織觀察》 自所獲得的冷軋退火板中採集組織觀察用的試驗片。繼而，對於所採集的試驗片，將與軋製方向垂直的面（RD面）作為觀察面進行填充樹脂，並藉由膠質氧化矽研磨進行鏡面化。對經鏡面化的觀察面實施電子射線背散射繞射（electron back scattered diffraction，EBSD）測定，獲得局部方位資料。此時，設為步長：5 μm、測定區域：50 mm 2以上。測定區域的寬度於後續的解析中以結晶粒的數量成為5000個以上的方式進行適宜調整。測定可以一次掃描於整個區域中進行，亦可利用康寶掃描（Combo Scan）功能將多次的掃描結果加以結合。解析軟體：使用OIM分析8（OIM Analysis 8），對所獲得的局部方位資料進行了解析。於進行資料解析之前，以成為試樣座標系的A1軸//軋製方向、A2軸//軋製直角方向、A3軸//板面方向的方式進行座標旋轉處理。另外，藉由解析軟體的分區屬性（Partition Properties）並以公式（Formula）：GCI[&;5.000,2,0.000,0,0,8.0,1,1,1.0,0;]＞0.1的條件進行晶粒平均資料點的篩選，將不適於解析的資料點排除。此時，有效的資料點為98%以上。
對於以如上方式調整後的資料，作為晶界的定義，將晶粒公差角度（Grain Tolerance Angle）設為5°，將最小晶粒尺寸（Minimum Grain Size）設為2，將最小反晶粒尺寸（Minimum Anti Grain Size）設為2，多數列需求（Multiple Rows Requirement）及反晶粒多數列需求（Anti-Grain Multiple Rows Requirement）均設為關（OFF），進行了以下的解析。對於實施了前處理的資料，將使用晶粒尺寸（Grain Size）（直徑（diameter））功能求出的面積平均（Area Average）的值作為平均結晶粒徑。另外，使用結晶配向（Crystal Direction）功能求出＜100＞及＜111＞相對於試樣座標系的[A1，A2，A3]=[100]、[010]、[110]、[1-10]此四個方向配向的結晶粒的面積率。計算面積率時的容許角度（Tolerance Angle）設為15°。若將＜uvw＞於試樣座標系的[u'v'w']方向上配向的結晶粒的面積率表述為S ＜ uvw ＞ //[u'v'w']，則＜100＞於軋製方向或軋製直角方向上配向的結晶粒的面積率之和S A可作為S A=S ＜ 100 ＞ //[100]+S ＜ 100 ＞ //[010]而求出。同時滿足＜100＞//[100]與＜100＞//[010]的方位的面積率設為雙重計數。以後亦同樣。同樣地，＜111＞於軋製方向或軋製直角方向上配向的結晶粒的面積率之和S B作為S B=S ＜ 111 ＞ //[100]+S ＜ 111 ＞ //[010]而求出，＜100＞於軋製45°方向及軋製-45°方向上配向的結晶粒的面積率之和S C作為S C=S ＜ 100 ＞ //[110]+S ＜ 100 ＞ //[1-10]而求出，＜111＞於軋製45°方向及軋製-45°方向上配向的結晶粒的面積率之和S D作為S D=S ＜ 111 ＞ //[110]+S ＜ 111 ＞ //[1-10]而求出。
《磁特性評價》 自所獲得的退火板中採集以長度方向為軋製方向或軋製直角方向的寬度30 mm、長度280 mm的磁測定用試驗片，依照日本工業標準（Japanese Industrial Standards，JIS）C2550-1：2011，並藉由愛普斯坦（Epstein）法對冷軋退火板的磁特性進行評價。評價項目設為飽和磁通密度：Bs、磁場的強度5000 A/m時的磁通密度：B50、及鐵損W10/800。另外，為了調查磁特性的各向異性，採集以長度方向為軋製45°方向及軋製-45°方向的寬度30 mm、長度280 mm的磁測定用試驗片，依照JIS C2550-1：2011，並藉由愛普斯坦（Epstein）對冷軋退火板的磁特性進行評價。評價項目設為磁場的強度5000 A/m時的磁通密度：B50_45°。於B50≧1.60（T）且B50/Bs≧0.82的情況下評價為磁通密度良好，於W10/800≦40（W/kg）的情況下評價為高頻鐵損特性良好。於ΔB50=B50-B50_45°≦0.120（T）的情況下評價為磁特性的各向異性小。
[表3-1] （表3-1）
No. 鋼板組織 特性 備註
平均 結晶粒徑 d（μm） SA [%] SB [%] SC [%] SD [%] SA-SB [%] 5SC-SD [%] 磁通密度 Bs（T） 磁通密度 B50（T） B50/Bs 鐵損 W 10/800（W/kg） 磁通密度 B50_45° （T） 各向異性 ΔB50（T）
1 103 19 6 6 25 13 5 1.97 1.72 0.87 30.2 1.67 0.048 發明例
2 124 13 6 6 25 7 5 1.98 1.71 0.86 29.7 1.66 0.047 發明例
3 69 17 4 7 27 13 8 1.95 1.73 0.89 28.0 1.69 0.042 發明例
4 104 19 6 3 11 13 4 2.00 1.76 0.88 31.5 1.71 0.053 發明例
5 106 20 6 4 11 14 9 1.97 1.74 0.88 29.1 1.71 0.034 發明例
6 126 17 8 7 27 9 8 1.96 1.71 0.87 27.5 1.67 0.042 發明例
7 124 16 5 4 13 11 7 1.92 1.69 0.88 25.1 1.65 0.038 發明例
8 86 16 5 6 26 11 4 1.97 1.71 0.87 29.0 1.66 0.047 發明例
9 90 19 6 7 28 13 7 1.96 1.70 0.87 28.3 1.66 0.044 發明例
10 100 13 6 5 16 7 9 1.91 1.65 0.86 25.0 1.62 0.032 發明例
11 84 15 5 5 21 10 4 1.98 1.70 0.86 29.6 1.65 0.053 發明例
12 66 12 5 6 21 7 9 2.04 1.76 0.86 47.7 1.73 0.030 比較例
13 90 13 6 4 12 7 8 2.03 1.78 0.88 38.0 1.74 0.038 發明例
14 99 12 5 5 17 7 8 2.01 1.75 0.87 36.3 1.71 0.041 發明例
15 96 13 6 5 16 7 9 1.87 1.62 0.87 22.7 1.59 0.032 發明例
16 91 13 6 4 12 7 8 1.86 1.59 0.86 22.3 1.55 0.038 比較例
17 112 19 6 3 11 13 4 2.03 1.75 0.86 46.9 1.71 0.042 比較例
18 132 19 6 3 11 13 4 2.03 1.79 0.88 36.0 1.74 0.048 發明例
19 120 21 7 3 11 14 4 1.96 1.68 0.86 35.4 1.64 0.043 發明例
20 95 19 6 3 11 13 4 1.91 1.67 0.87 42.1 1.63 0.041 比較例
21 96 19 7 6 23 12 7 2.01 1.74 0.87 43.3 1.70 0.038 比較例
22 104 17 5 7 28 12 7 2.01 1.77 0.88 36.1 1.73 0.039 發明例
23 136 19 6 7 28 13 7 1.92 1.67 0.87 37.6 1.63 0.042 發明例
24 93 20 6 7 27 14 8 1.86 1.65 0.89 40.7 1.61 0.038 比較例
25 97 19 4 3 11 15 4 1.96 1.76 0.90 27.5 1.72 0.044 發明例
26 106 21 4 3 11 17 4 1.96 1.78 0.91 27.0 1.74 0.043 發明例
27 108 18 4 5 13 14 12 1.96 1.68 0.86 29.4 1.65 0.026 發明例
28 67 17 4 6 16 13 14 1.95 1.73 0.89 28.1 1.71 0.025 發明例
29 94 19 7 5 20 12 5 1.98 1.70 0.86 30.7 1.66 0.045 發明例
30 110 18 6 6 25 12 5 1.98 1.71 0.87 30.1 1.67 0.045 發明例
31 91 20 7 5 20 13 5 1.97 1.69 0.86 30.2 1.65 0.044 發明例
32 123 19 6 7 30 13 5 1.98 1.75 0.89 29.6 1.71 0.040 發明例
33 97 20 7 6 25 13 5 1.97 1.70 0.86 30.2 1.65 0.047 發明例
34 137 17 5 6 25 12 5 1.97 1.77 0.90 28.7 1.72 0.049 發明例
35 109 17 5 6 25 12 5 1.98 1.78 0.90 29.3 1.73 0.050 發明例
36 100 13 15 5 15 -2 10 1.91 1.54 0.81 42.3 1.50 0.037 比較例
37 93 5 6 5 16 -1 9 1.91 1.50 0.79 40.5 1.46 0.038 比較例
38 117 3 5 3 11 -2 4 2.00 1.55 0.77 45.4 1.50 0.047 比較例
39 115 9 7 3 11 2 4 2.00 1.69 0.84 35.9 1.64 0.050 發明例
40 117 9 5 3 11 4 4 2.00 1.69 0.84 35.9 1.64 0.051 發明例
41 106 17 18 4 13 -1 7 1.92 1.50 0.78 41.5 1.46 0.038 比較例
42 127 3 5 4 12 -2 8 1.92 1.53 0.80 40.9 1.49 0.042 比較例
43 95 16 17 8 32 -1 8 2.01 1.61 0.80 46.1 1.57 0.037 比較例
44 96 15 14 7 28 1 7 2.01 1.66 0.83 38.1 1.62 0.036 發明例
45 129 15 11 8 33 4 7 2.01 1.71 0.85 37.2 1.67 0.042 發明例
46 53 17 4 3 11 13 4 1.96 1.70 0.87 42.9 1.65 0.048 比較例
47 62 17 4 3 11 13 4 1.96 1.69 0.86 37.4 1.65 0.041 發明例
48 193 18 4 3 11 14 4 1.96 1.72 0.88 36.8 1.68 0.043 發明例
49 232 18 4 3 11 14 4 1.96 1.68 0.86 43.3 1.64 0.045 比較例
50 88 25 6 5 26 19 -1 1.97 1.74 0.88 29.6 1.60 0.139 發明例
51 106 25 6 5 24 19 1 1.97 1.76 0.89 29.3 1.69 0.070 發明例
52 122 25 7 4 17 18 3 1.97 1.75 0.89 29.5 1.70 0.055 發明例
53 116 24 6 5 27 18 -2 1.97 1.73 0.88 29.8 1.60 0.127 發明例
54 138 24 6 4 20 18 0 1.97 1.73 0.88 29.8 1.63 0.096 發明例
55 139 23 6 4 21 17 -1 1.97 1.75 0.89 29.5 1.62 0.131 發明例
56 99 25 6 5 24 19 1 1.97 1.75 0.89 29.5 1.68 0.067 發明例
57 94 19 6 6 25 13 5 1.97 1.73 0.88 30.0 1.69 0.045 發明例
註）下劃線部分表示發明範圍外
[表3-2] （表3-2）
No. 鋼板組織 特性 備註
平均 結晶粒徑 d（μm） SA [%] SB [%] SC [%] SD [%] SA-SB [%] 5SC-SD [%] 磁通密度 Bs （T） 磁通密度 B50 （T） B50/Bs 鐵損 W 10/800（W/kg） 磁通密度 B50_45° （T） 各向異性 ΔB50 （T）
58 98 19 4 3 11 15 4 1.95 1.78 0.91 27.1 1.73 0.051 發明例
59 103 18 4 5 12 14 13 1.95 1.67 0.85 28.8 1.64 0.028 發明例
60 107 19 7 7 29 12 6 1.97 1.68 0.85 30.8 1.64 0.038 發明例
61 99 19 6 6 25 13 5 1.97 1.68 0.85 30.5 1.64 0.040 發明例
62 109 21 7 6 25 14 5 1.97 1.74 0.88 29.6 1.69 0.047 發明例
63 139 17 5 5 20 12 5 1.97 1.70 0.86 30.2 1.66 0.044 發明例
64 120 19 6 6 25 13 5 1.97 1.72 0.87 29.9 1.67 0.046 發明例
65 116 21 7 6 25 14 5 1.97 1.77 0.90 29.2 1.72 0.046 發明例
66 120 20 7 6 25 13 5 1.97 1.76 0.89 29.3 1.72 0.040 發明例
67 113 11 5 7 30 6 5 1.98 1.68 0.85 30.2 1.64 0.038 發明例
68 102 14 7 5 20 7 5 1.98 1.74 0.88 29.3 1.70 0.039 發明例
69 96 13 6 6 25 7 5 1.98 1.70 0.86 29.9 1.66 0.040 發明例
70 112 13 5 5 20 8 5 1.98 1.68 0.85 30.2 1.64 0.045 發明例
71 91 20 7 4 11 13 9 1.97 1.70 0.86 29.7 1.67 0.032 發明例
72 117 19 5 4 11 14 9 1.97 1.68 0.85 29.9 1.64 0.040 發明例
73 88 18 5 4 12 13 8 1.97 1.71 0.87 29.5 1.68 0.033 發明例
74 71 19 6 4 11 13 9 1.97 1.69 0.86 29.8 1.66 0.035 發明例
75 85 19 6 4 11 13 9 1.97 1.69 0.86 29.8 1.66 0.035 發明例
76 77 19 6 4 12 13 8 1.97 1.75 0.89 29.0 1.72 0.031 發明例
77 85 18 5 4 11 13 9 1.97 1.73 0.88 29.2 1.70 0.032 發明例
78 116 21 7 4 10 14 10 1.97 1.70 0.86 29.7 1.67 0.035 發明例
79 75 21 6 4 10 15 10 1.97 1.73 0.88 29.2 1.70 0.030 發明例
80 91 19 6 4 11 13 9 1.97 1.70 0.86 29.7 1.66 0.038 發明例
81 133 18 9 7 27 9 8 1.96 1.71 0.87 27.5 1.68 0.032 發明例
82 90 18 9 7 27 9 8 1.96 1.72 0.88 27.4 1.68 0.042 發明例
83 100 17 9 8 32 9 8 1.96 1.68 0.86 27.9 1.65 0.034 發明例
84 140 16 7 6 22 8 8 1.96 1.68 0.86 27.9 1.64 0.041 發明例
85 113 18 9 6 23 9 7 1.96 1.71 0.87 27.5 1.67 0.042 發明例
86 97 16 7 7 27 9 8 1.96 1.70 0.87 27.7 1.66 0.038 發明例
87 101 16 6 4 13 10 7 1.92 1.75 0.91 24.4 1.71 0.040 發明例
88 124 15 4 4 12 11 8 1.92 1.77 0.92 24.2 1.73 0.039 發明例
89 96 17 5 4 12 12 8 1.92 1.73 0.90 24.7 1.69 0.042 發明例
90 100 17 6 4 13 11 7 1.92 1.75 0.91 24.4 1.72 0.035 發明例
根據表3-1、表3-2的結果可知，按照本發明的無方向性電磁鋼板均兼顧優異的磁通密度與優異的高頻鐵損特性。進而，目的在於恢復衝壓時的應變引起的鐵損減少，對鋼板實施了應變消除退火，結果對本發明的效果無任何影響，可兼顧優異的磁通密度與優異的鐵損特性。 [產業上的可利用性]
藉由本發明，可提供一種不會導致飽和磁通密度降低或生產性降低的、高磁通密度-高頻低鐵損的無方向性電磁鋼板及其製造方法。
無

Claims (7)

  1. 一種無方向性電磁鋼板，以質量%計包含 C：0.010%以下、 Si：1.0%以上且5.0%以下、 Mn：0.05%以上且5.0%以下、 P：0.1%以下、 S：0.01%以下、 Al：3.0%以下、及 N：0.005%以下，且 剩餘部分為Fe及不可避免的雜質， 平均結晶粒徑為60 μm以上且200 μm以下， ＜100＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S A與＜111＞朝向軋製方向或軋製直角方向的結晶粒的面積率之和S B滿足S A-S B≧0。
  2. 如請求項1所述的無方向性電磁鋼板，其中，＜100＞朝向軋製45°方向及軋製-45°方向的結晶粒的面積率之和S C與＜111＞朝向軋製45°方向及軋製-45°方向的結晶粒的面積率之和S D滿足5×S C-S D≧0。
  3. 如請求項1或2所述的無方向性電磁鋼板，其中，以質量%計更包含0.0005%以上且0.0050%以下的Co。
  4. 如請求項1至3中任一項所述的無方向性電磁鋼板，其中，以質量%計更包含0.0005%以上且0.0050%以下的Zn。
  5. 如請求項1至4中任一項所述的無方向性電磁鋼板，其中，以質量%計更含有下述A群組～D群組中的至少一個群組的成分；以及選自Cu：0%以上且0.5%以下、Ni：0%以上且0.5%以下、W：0%以上且0.05%以下、Ti：0%以上且0.005%以下、Nb：0%以上且0.005%以下、V：0%以上且0.010%以下、Ta：0%以上且0.002%以下、B：0%以上且0.002%以下、Ga：0%以上且0.005%以下、Pb：0%以上且0.002%以下、As：0%以上且0.05%以下及Ge：0%以上且0.05%以下中的一種或兩種以上， ·A群組；Mo：0.01%以上且0.20%以下 ·B群組；Cr：0.1%以上且5.0%以下 ·C群組；Ca：0.001%以上且0.10%以下、Mg：0.001%以上且0.10%以下及稀土金屬：0.001%以上且0.10%以下中的任意一種或兩種以上 ·D群組；Sn：0.001%以上且0.20%以下及Sb：0.001%以上且0.20%以下中的任意一種或兩種。
  6. 一種無方向性電磁鋼板的製造方法，是製造如請求項1至5中任一項所述的無方向性電磁鋼板的方法，包括：熱軋步驟，藉由對具有所述無方向性電磁鋼板的組成的鋼原材料實施熱軋而獲得熱軋板；熱軋板退火步驟，視需要對所述熱軋板實施熱軋板退火；酸洗步驟，對所述熱軋板及實施了所述熱軋板退火的所述熱軋板實施酸洗；冷軋步驟，藉由對實施了所述酸洗的所述熱軋板實施冷軋而獲得冷軋板；以及退火步驟，以自200℃至400℃以上且600℃以下的保持溫度T 1的平均升溫速度V 1為50℃/s以上、保持溫度T 1下的保持時間t為1秒以上且10秒以下、並且自保持溫度T 1至750℃的平均升溫速度V 2為15℃/s以上的條件，將所述冷軋板加熱至875℃以上且1050℃以下的退火溫度T 2，並進行冷卻，藉此獲得冷軋退火板。
  7. 如請求項6所述的無方向性電磁鋼板的製造方法，其中，以最終道次的工作輥徑為150 mmϕ以上、最終道次的壓下率為15%以上、且最終道次的應變速度為100 s -1以上且1300 s -1以下的條件進行所述冷軋步驟。
TW111148046A 2021-12-16 2022-12-14 無方向性電磁鋼板及其製造方法 TW202328462A (zh)