TW202214913A - 多孔性電解器氣體擴散層及其製備方法 - Google Patents
多孔性電解器氣體擴散層及其製備方法 Download PDFInfo
- Publication number
- TW202214913A TW202214913A TW110127202A TW110127202A TW202214913A TW 202214913 A TW202214913 A TW 202214913A TW 110127202 A TW110127202 A TW 110127202A TW 110127202 A TW110127202 A TW 110127202A TW 202214913 A TW202214913 A TW 202214913A
- Authority
- TW
- Taiwan
- Prior art keywords
- titanium
- porous titanium
- sheet
- porous
- anode
- Prior art date
Abstract
本發明描述一種經組態以充當質子交換膜(PEM)電解器之陽極側氣體擴散層的多孔性鈦薄片，該多孔性鈦薄片係藉由諸如薄帶成形或粉末冶金之粉末技術形成。
Description
本發明大體上係針對電解器，尤其針對用於電解器之氣體擴散層及其製備方法。
質子交換膜(PEM)電解器可用於將水轉化成分離之氫氣流及氧氣流。此類PEM電解器包括位於陽極電極與陰極電極之間的聚合物電解質。陽極側及陰極側多孔性氣體擴散層鄰近各別的陽極及陰極電極而定位。
在一個實施例中，經組態以充當質子交換膜(PEM)電解器之陽極側氣體擴散層的多孔性鈦薄片藉由粉末技術形成。
在一個實施例中，方法包含藉由粉末技術製備經組態以充當質子交換膜(PEM)電解器之陽極側氣體擴散層的多孔性鈦薄片。
圖1示出在Greig Chisholm等人之文章「3D printed flow plates for the electrolysis of water: An economic and adaptable approach to device manufacture」 Energy Environ. Sci., 2014, 7, 3026-3032中描述的PEM電解器之透視剖視圖。PEM電解器1包括：具有流體流道6及各別孔8、9、10之陽極側流板2及陰極側流板4、位於流板2與流板4之間的PEM聚合物電解質12、位於電解質12與陽極側流板2之間的陽極側氣體擴散層14、位於陽極側氣體擴散層14與電解質12之間的陽極電極16、位於電解質12與陰極側流板4之間的陰極側氣體擴散層18，及位於陰極側氣體擴散層18與電解質12之間的陰極電極20。
陽極側流板2可包括：水進口孔8、氧氣出口孔9及在面向陽極側氣體擴散層14之流板2一側連接水進口孔8與氧氣出口孔9的水流道(例如盤旋路徑凹槽) 6。陽極側氣體擴散層14可包含多孔性鈦層。陰極側氣體擴散層18可包含多孔性碳層。陽極電極16可包含任何適合之陽極催化劑，諸如銥層。陰極電極20可包含任何適合之陰極催化劑，諸如鉑層。其他貴金屬催化劑層亦可用於陽極及/或陰極電極。電解質12可包含任何適合之質子交換(例如，氫離子輸送)聚合物膜，諸如Nafion®膜，其由具有式C
7HF
13O
5S
.C
2F
4之基於磺化四氟乙烯之含氟聚合物-共聚物構成。
在操作中，通過水進口孔8將水提供至水流道6中。水流動通過水流道6且通過陽極側氣體擴散層14流動至陽極電極16。在陽極電極16與陰極電極20之間施加外部電流或電壓時，水在陽極電極16處電化學分離成氧氣及氫氣。氧氣通過陽極側氣體擴散層14擴散回至陽極側流板2且通過氧氣出口孔9離開電解器1。氫離子通過電解質12擴散至陰極電極20，且隨後通過陰極側氣體擴散層18及位於陰極側流板4中之氫氣出口孔10離開電解器1。
多孔性鈦層(例如，薄片)可用作陽極側氣體擴散層(亦即，輸送層) 14。在一個實施例中，用作陽極側氣體擴散層14之多孔性鈦層(例如，薄片)藉由粉末方法形成。
在一個實施例中，粉末方法包含薄帶成形。在多孔性鈦薄片經燒結之後，其可於兩側上(例如，陽極電極側及流板側上)塗佈諸如鉑及/或金塗層之導電性增強及/或抗蝕塗層以提供良好的導電性及耐腐蝕性。可藉由諸如蒸發之物理氣相沈積形成塗層。
在另一實施例中，用作陽極側氣體擴散層14之多孔性鈦層(例如，薄片)藉由粉末冶金技術形成，其中使用壓實方法將鈦粉末壓製成多孔性鈦薄片。隨後燒結壓實薄片以產生具有已建立之冶金結合之氣體擴散層(例如，薄片)。多孔性鈦薄片可具有介於40%與60%之間的孔隙度。
圖2A至圖2F展示可用以形成多孔性陽極側鈦氣體擴散層之粉末冶金技術(例如，azom.com (https://www.azom.com/article.aspx?ArticleID=155)中所示之技術)中的例示性步驟。粉末冶金壓製設備100包括腔室101，該腔室101含有相對於定位在模具108中之模穴106軸向移動的上衝頭102及下衝頭104。
粉末冶金壓實循環中之步驟包括自較高位置降低下衝頭104以暴露模穴106，如圖2A及圖2B中所展示。鈦粉末112與潤滑劑混合且隨後提供至粉末填料靴110中。含有與潤滑劑混合之鈦粉末112的粉末填料靴110在模穴上方移動以用鈦粉末112與潤滑劑之混合物填充模穴。在抽取填料靴110後，上衝頭102及/或下衝頭104相對於模具108移動以壓縮鈦粉末112，如圖2C及圖2D中所展示。在壓實後，使上衝頭102向上回縮且下衝頭104相對於模具108移動以將經壓實之生坯鈦薄片114自模穴106中推出，如圖2E中所展示。填料靴110隨後再次跨越模具108之上表面移動，其中該填料靴用額外的鈦粉末112與潤滑劑之混合物再填充模穴且將生坯鈦薄片114推出模具108，如圖2F中所展示。
可將生坯鈦薄片114提供至移動帶上，該移動帶使生坯鈦薄片移動穿過一或多個帶式爐。薄片可首先在較低溫度下在脫脂過程中退火以燒去有機潤滑劑(亦即，黏合劑)，隨後在高溫下退火以燒結去潤滑之鈦薄片。經燒結之多孔性鈦薄片14隨後提供至陽極側流板2與膜電極組(亦即，具有陽極電極16及位於其相對側上之陰極電極20的電解質12)之間的電解器(例如，圖1之電解器1)中以充當陽極側氣體擴散層14。
在圖3中所展示之一個實施例中，多孔性鈦薄片14之第一主側面14A的孔隙度高於多孔性鈦薄片14之相對第二主側面14B。多孔性鈦薄片14之第一主側面14A面向陽極側流板2，且多孔性鈦薄片14之相對第二主側面14B面向陽極電極16。舉例而言，多孔性鈦薄片14之第一主側面14A的孔隙度可比多孔性鈦薄片14之相對第二主側面14B高至少10%。多孔性鈦薄片之第一主側面14A可具有40%至50%之孔隙度，而多孔性鈦薄片之相對第二主側面14B可具有50%至60%之孔隙度。在一個實施例中，多孔性鈦薄片14之流板2側面14A的較高孔隙度准許更多水進入孔隙，而鈦薄片14之陽極電極16側面14B的較低孔隙度提供與陽極電極16之改良的電接觸。
孔隙度差異可為連續孔隙度梯度，其中孔隙度自第一主側面14A至第二主側面14B(亦即在相對主要表面之間)連續增加。或者，孔隙度可以逐步方式改變，使得多孔性鈦薄片14至少具有各別孔隙度彼此不同之第一部分及第二部分(14A，14B)。為了形成不同的孔隙度區域，向模穴106中之鈦粉末112之頂部區段及底部區段以連續梯度或以逐步方式添加不同量之潤滑劑。多孔性鈦薄片14在由含有較高潤滑劑濃度之粉末區段製備之部分14A中的孔隙度高於由含有較低潤滑劑濃度之粉末區段製備之部分14B。模穴106中之不同潤滑劑濃度可由填料靴110之兩個或更多個不同遍次形成，其中鈦粉末112與潤滑劑之比率在不同遍次中係不同的(例如，更高或更低)。在第一填料靴110遍次期間用鈦粉末112與潤滑劑之混合物的具有第一鈦粉末與潤滑劑比率的第一部分對模穴106部分填充，且在第二填料靴110遍次期間用鈦粉末112與潤滑劑之混合物的具有不同於第一比率之第二鈦粉末與潤滑劑比率的第二部分另外填充模穴106。較低的鈦粉末112與潤滑劑之比率在脫脂退火步驟期間產生較高孔隙度。
在另一實施例中，面向陽極側氣體擴散層14之陽極側流板的第一主表面含有水流道凹槽6，如圖1中所展示。面向陽極側流板2之多孔性鈦薄片14的第一主側面14A包括凹槽26，其為水流道凹槽6之實質上鏡像，如圖3中所展示。如本文中所使用，水流道凹槽26之實質上鏡像表示形狀為水流道凹槽6之大體鏡像，但可具有相差小於20%之尺寸。相比之下，面向陽極電極16之多孔性鈦薄片14的相對第二主側面14B具有缺少凹槽26之實質上平坦的表面。此類設計便於水在氣體擴散層14之流板2側面14A上的流動，同時維持氣體擴散層14與陽極電極16之間的良好電接觸。可藉由使用圖2A之設備中的上衝頭102或下衝頭104形成多孔性鈦薄片14中的凹槽26，該上衝頭102或下衝頭104含有作為凹槽26之鏡像的突起。
在圖4中所展示之另一實施例中，多孔性鈦薄片14具有作為孔隙網狀結構之部分的孔徑之雙峰式分佈。孔徑之兩種模式廣泛地分類為微孔15B及大於微孔15B之大孔15A。微孔15B充當毛細管且有助於將水自凹槽6輸送至陽極電極(例如陽極催化劑層) 16，而大孔15A為所產生之氣體提供低流動阻力路徑，使氣體藉由流動水輸送而離開電催化劑到達凹槽6。孔徑可使用楊-拉普拉斯方程式(Young Laplace equation)計算。在一個實施例中，微孔15B平均孔徑在1微米至5微米範圍內，且大孔15A平均孔徑在30微米至40微米範圍內。
在另一實施例中，圖2A至圖2F之粉末壓製設備100中之多孔性鈦薄片14在腔室101中之惰性、低氧氣分壓氛圍中形成，使得鈦不會氧化為二氧化鈦，以減少電阻損耗且避免因鈦氧化所致的著火。惰性氛圍可包含任何適合之惰性氣體，諸如稀有氣體，諸如氬氣。該氛圍可包含小於0.1 atm，諸如0.0001 atm至0.01 atm之氧氣分壓。可將惰性氣體提供至含有模具108及衝頭102、104之腔室101中。或者，在用鈦粉末填充模穴後，可將惰性氣體自惰性氣體導管提供至模穴中以作為氣體圍包。
在另一實施例中，多孔性鈦薄片14在圖2A至圖2F之粉末壓製設備100中用鈦合金粉末形成。鈦可與鉬、釩、鈮、鉭及/或鋯中之任何一或多者合金化。因此，含有超過50原子%之鈦(例如，60原子%至99原子%之Ti及低於50原子%，諸如1原子%至40原子%之鉬、釩、鈮、鉭及/或鋯)的鈦合金粉末可用於粉末壓製設備中。粉末顆粒包含鈦合金顆粒。或者，兩種粉末之組合(例如，混合物)可用於粉末壓製設備中：含鈦粉末，諸如純鈦粉末；及含有鉬、釩、鈮、鉭及/或鋯之合金元素粉末。粉末之組合含有超過50原子%之鈦粉末顆粒(例如，60原子%至99原子%之Ti)及低於50原子%(諸如，1原子%至40原子%)之合金元素粉末顆粒。在粉末壓製設備中之壓實過程中形成多孔性鈦合金薄片。可結合化學穩定性要求與可加工性要求來選擇鈦合金等級。合金等級可為等級1、2、3、6、7、9、11、16、17、18、21、24、26、27、29、32、36及/或37。
在另一實施例中，貴金屬塗層(例如金或鉑族金屬塗層)可在粉末冶金方法期間形成於多孔性鈦薄片14上，這提高塗佈方法速度且降低塗佈方法成本。在此實施例中，將貴金屬粉末提供至模穴106中之鈦粉末112下方及上方，隨後使用衝頭102、104一起壓縮所有粉末，如圖2A至圖2F中所展示。可藉由填料靴110的三個或更多個不同遍次形成不同粉末層，其中粉末組成在不同遍次中變化。在第一填料靴遍次期間用貴金屬粉末與潤滑劑之混合物部分地填充模穴106，隨後在第二填料靴遍次期間用鈦粉末112與潤滑劑之混合物額外填充模穴，最後在第三填料靴遍次期間用貴金屬粉末與潤滑劑之混合物填充模穴。在一個實施例中，可使用填充有不同粉末之兩個不同的填料靴110。在第一填料靴遍次與第三填料靴遍次期間，使用填充有貴金屬粉末與潤滑劑之混合物的第一填料靴。在第二填料靴遍次期間，使用填充有鈦粉末與潤滑劑之混合物的不同的第二填料靴。此在模穴中形成貴金屬/鈦/貴金屬粉末三層。隨後壓縮三層以形成在兩個主表面上塗佈有貴金屬之多孔性鈦板。
在圖5中所展示之另一實施例中，多孔性鈦薄片具有固有通孔，其用一或多種貴金屬粉末填充以產生高導電性通孔22。換言之，多孔性鈦或鈦合金薄片14包括延伸通過薄片14之厚度方向的貴金屬通孔22。貴金屬通孔22可包括任何適合之貴金屬，諸如釕、銠、鈀、銀、鋨、銥、鉑及/或金。通孔提供良好的電導率，因此將電導率之功能與由化學穩定多孔性薄片14提供之水/氣體輸送功能相分離。
在另一實施例中，選擇脫脂及燒結方案以在多孔性鈦層14之相對主表面上獲得連續貴金屬塗層，同時增加多孔性鈦薄片之孔隙度。此可藉由使用較高的脫脂升溫速率及/或較低的燒結溫度來實現。在一個實施例中，相對較高的脫脂升溫速率可為1℃/min至5℃/min，例如2℃/min至4℃/min。在一個實施例中，相對較低的燒結溫度可為1100℃至1300℃，諸如1150℃至1250℃。
在另一實施例中，形成陽極側氣體擴散層14之方法包括控制矽化物形成。舉例而言，部分金屬合金在燒結期間形成矽化物相(參見J. D. Bolton, M. Youseffi & B. S. Becker (1998) Silicide Phase Formation and Its Influence on Liquid Phase Sintering in 316L Stainless Steel with Elemental Silicon Additions, Powder Metallurgy 41:2, (1998) 93-101，可在https://www.tandfonline.com/doi/abs/10.1179/pom.1998.41.2.93獲得，以全文引用之方式併入本文中)。特定言之，矽添加至316L不鏽鋼導致在燒結期間形成液體矽化物相，其在燒結完成後在不鏽鋼部件中留下較大孔隙。
在本發明實施例的一個態樣中，矽化物形成控制包括在用以形成陽極側氣體擴散層的粉末冶金方法中使用具有小於0.1重量%之矽(例如，0至0.01重量%之矽)的鈦粉末112。鈦粉末中完全或實質上不存在矽可避免或減少在陽極側氣體擴散層之表面上形成一或多個矽化鈦相，其可能會對陽極側氣體擴散層提供非所需的表面性質。
在另一態樣中，矽化物形成控制包括在用以形成陽極側氣體擴散層14的粉末冶金方法中使用遍及整個模穴分散的具有至少1重量%之矽(例如，1重量%至10重量%之矽)的鈦粉末112。在此實施例中，矽化鈦相在燒結(例如，液相燒結)期間遍及陽極側氣體擴散層之整個厚度形成，且充當成孔劑。因此，藉由在燒結期間有意地產生矽化物相成孔劑來增加陽極側氣體擴散層14之孔隙度，這在陽極側氣體擴散層中留下孔隙。此外，由於矽化物相遍及陽極側氣體擴散層14分佈，因此矽化物相不集中於陽極側氣體擴散層之表面上，且避免或減少非所需的表面效應。
因此，製備經組態以充當質子交換膜(PEM)電解器之陽極側氣體擴散層的多孔性鈦薄片的粉末冶金方法包括：提供鈦粉末與潤滑劑之混合物至模穴中，壓縮模穴中的鈦粉末與潤滑劑之混合物以形成生坯薄片，脫脂生坯薄片，及燒結生坯薄片以形成多孔性鈦薄片。
在一個實施例中，該方法亦包括在將鈦粉末與潤滑劑之混合物提供至模穴中之前，將貴金屬粉末與潤滑劑之第一混合物提供至模穴中，及在將鈦粉末與潤滑劑之混合物提供至模穴中之後，將貴金屬粉末與潤滑劑之第二混合物提供至模穴中。在模穴中壓縮鈦粉末與潤滑劑之混合物連同壓縮貴金屬與潤滑劑之第一及第二混合物一起進行，以形成生坯薄片，且燒結生坯薄片之步驟形成多孔性鈦薄片之兩個主表面上具有貴金屬塗層之多孔性鈦薄片。
在另一實施例中，用作陽極側氣體擴散層14之多孔性鈦層(例如，薄片)藉由薄帶成形方法形成。圖6示出可用以形成陽極側氣體擴散層14之例示性薄帶成形設備200。低成本及可擴展的薄帶成形方法可不斷地生產用於形成陽極側氣體擴散層14之大幅面含鈦帶。
在圖6中所展示之薄帶成形方法之一實施例中，將諸如鈦粉末、溶劑、黏合劑及視情況選用之一或多種額外成分(諸如塑化劑及/或界面活性劑)之混合物(例如漿液)的漿料202自諸如流體儲存槽之儲存容器提供至分配室204中。鈦粉末可包含元素(亦即，金屬)鈦粉末及/或氫化鈦(例如，TiH
2)粉末。氫化鈦粉末可用於降低生產成本，因為原料成本較低，並且由於其在600℃至800℃左右進行Ti轉化時發生放熱反應，燒結期間的能量使用也較少。因此，在一個實施例中，含鈦粉末包含元素鈦與氫化鈦粉末之混合物，且氫化鈦隨後在放熱反應中，諸如在燒結期間及/或在單獨退火步驟期間熱轉化為元素鈦。
在一個實施例中，將具有所需粒徑及分佈之鈦及氫化鈦粉末摻合在一起，且與聚合黏合劑、有機溶劑及有機塑化劑混合，它們可在低氧或無氧燒結過程期間移除以在薄帶成形陽極側氣體擴散層14中形成孔隙。黏合劑、溶劑及塑化劑可分別包含聚碳酸丙二酯(「PPC」)、甲基乙基酮(「MEK」)及聚碳酸酯(「PC」)。亦可使用其他適合之材料。
漿料202自分配室204分配至移動帶載體網206上。帶載體網206可包含移動經過刮刀208之金屬(例如鋼)、玻璃、聚合物帶等。在刮刀208下方在帶載體網206上移動之漿料202經刮刀208壓成生坯含鈦帶210。粉末大小、特定含量及固體比率之不同摻合物之生坯含鈦帶210可由漿料(亦即，漿液) 202調配物之輕微變化產生。
帶載體網206可隨後移動生坯含鈦帶210通過乾燥室212。乾燥室212可包括加熱空氣入口214及飽和空氣出口216。加熱空氣(或另一熱源)乾燥生坯含鈦帶210，且自帶210蒸發之溶劑與空氣一起通過飽和空氣出口216移除。經乾燥之生坯含鈦帶210隨後可在切割台218中經切割成具有陽極側氣體擴散層之形狀的鈦生坯薄片210S。
已切割成鈦生坯薄片210S之經乾燥之生坯含鈦帶210隨後在所需溫度下在燒結室220中燒結以形成陽極側氣體擴散層14。較佳地，鈦生坯薄片210S在1000℃至1100℃下在無氧或低氧氛圍下燒結。該氛圍可包含任何適合之惰性氣體的惰性氛圍，諸如稀有氣體，諸如氬氣。該氛圍可包含小於0.1 atm，諸如0.0001 atm至0.01 atm之氧氣分壓。
在一個實施例中，可將經乾燥之生坯含鈦帶210自乾燥室212提供至切割台218中，且隨後使用同一帶載體網206將切割帶(亦即，鈦生坯薄片210S)自切割台218提供至燒結室220中以進行燒結。視情況，若需要在乾燥溫度與燒結溫度之間的溫度下進行脫脂步驟，則諸如脫脂室之附加腔室可位於乾燥室212與燒結室220之間。
在一個實施例中，燒結室220可包含電阻或氣體加熱式連續爐(例如，帶式爐)。在此實施例中，經乾燥之生坯含鈦帶210 (亦即，鈦生坯薄片210S)在同一帶載體網206上移動通過乾燥室212、切割台218及連續爐。在另一實施例中，燒結室220可包含快速熱退火(「RTA」)設備(亦被稱作快速熱處理(「RTP」)設備)，其中切割過的經乾燥之生坯含鈦帶210 (亦即，鈦生坯薄片210S)由閃光燈或雷射光束加熱。在此實施例中，生坯含鈦帶210在同一帶載體網206上移動通過乾燥室212、切割台218及RTA設備。因此，抹平漿料202、對帶進行乾燥、對帶進行切割及燒結切割帶之步驟可在同一移動帶載體網206上連續進行。
在一個實施例中，相對於帶載體網206之移動方向，燒結室220可包含上游部分220A及位於上游部分220A之下游的下游部分220B。視情況選用之隔板220P可設置於燒結室220之上游部分與下游部分之間。上游部分220A可維持於無氧或低氧氛圍中，諸如稀有氣體(例如氬氣)氛圍。下游部分220B可維持於含氮氣氛圍中，諸如氮氣氛圍或含氨氣氛圍(例如，具有含氮氣體分壓之低壓或真空氛圍)。鈦生坯薄片210S可在下游部分220B中反應性燒結以在其表面上形成氮化鈦層。因此，鈦氣體擴散層14可在一個或兩個主表面14A、14B上具有氮化鈦塗層。氮化鈦在鈦氣體擴散層14上形成硬的、抗腐蝕且導電的塗層。此塗層改良鈦氣體擴散層14之效能。此外，若形成氮化鈦抗蝕塗層，則可省略貴金屬(例如，Au或Pt)抗蝕塗層。應注意，藉由除薄帶成形之外的方法(諸如粉末冶金)形成之鈦氣體擴散層14亦可反應性燒結以在其上形成氮化鈦塗層。
在替代實施例中，可將漿料202自側面及/或自下部而不是像圖6中所展示地那樣自上部提供至帶載體網206上。若自側面提供漿料202，則設備200可被稱作狹縫型塗佈機設備。若自下部提供漿料202，則設備200可被稱作邊緣塗佈機(lip coater)或微凹版塗佈機(micro-gravure coater)。
概言之，薄帶成形方法可包含將含鈦粉末與黏合劑、溶劑及塑化劑混合以形成漿料202，將漿料202分配至帶載體網206上，用刮刀208將在帶載體網206上移動之漿料202抹平成生坯含鈦帶210，在乾燥室212中乾燥生坯含鈦帶210，在切割台218中將生坯含鈦帶210切割成具有第一孔隙度之第一鈦生坯薄片210S，及燒結第一生坯薄片210S以形成多孔性鈦薄片14。
在一個實施例中，犧牲性成孔劑材料粉末可添加至漿料(亦即，漿液) 202中，以允許較高燒結溫度，由此產生具有較高撓曲強度及韌性之陽極側氣體擴散層14。此種成孔劑材料可包含工程化碳粉或球形微米及/或亞微米大小之聚(甲基丙烯酸甲酯) (「PMMA」)粉末。成孔劑材料在燒結步驟期間移除以在氣體擴散層14中形成孔隙。
在一個實施例中，可藉由薄帶成形形成圖3之多孔性鈦薄片氣體擴散層14，其在一個部分14A中之孔隙度高於另一部分14B中之孔隙度。可藉由形成具有不同孔隙度之兩個單獨的生坯鈦薄片210S來形成此種多孔性鈦薄片。可藉由在漿料202中使用不同的鈦粉末大小、不同的固體比率、不同的帶材料含量及/或具有不同體積、組成及/或大小的成孔劑材料來獲得不同孔隙度。具有不同孔隙度之兩個生坯鈦薄片210S隨後彼此接觸地置放且隨後經燒結。燒結形成圖3之多孔性鈦薄片氣體擴散層14，其具有孔徑及微結構之功能分級。因此，在此實施例中，薄帶成形方法亦包括在燒結之前將具有不同於第一孔隙度之第二孔隙度的第二鈦生坯薄片210S置放在第一鈦生坯薄片210S上。第一及第二鈦生坯薄片210S彼此接觸地燒結，以使得所得經燒結多孔性鈦薄片14之第一主側面14A相較於多孔性鈦薄片14B之相對第二主側面14B具有較高孔隙度。
在另一實施例中，圖5中所展示之導電通孔22可在薄帶成形氣體擴散層14中形成。可藉由將貴金屬或導電鈦化合物通孔成形至生坯及/或經燒結含鈦帶210中來形成導電通孔22。替代地或另外，可將較大的鈦或氫化鈦顆粒及/或線添加至漿料202。較大顆粒可具有在多孔性鈦薄片14之厚度之20%以內，諸如10%以內的平均直徑。金屬線(例如，纖維)可具有在多孔性鈦薄片14之厚度之20%以內，諸如10%以內的平均長度。將較大顆粒及/或線與具有平均直徑小於多孔性鈦薄片14之厚度之50%的鈦或氫化鈦粉末顆粒混合。較大顆粒及/或線延伸穿過多孔性鈦薄片14之整個厚度且充當導電通孔22。如本文中所使用，多孔性鈦薄片14之厚度為多孔性鈦薄片14之第一主側面14A與第二主側面14A之間的尺寸。
在另一實施例中，生坯含鈦帶210之表面可經壓印(例如，粗糙化或圖案化)以產生凸起及凹下之表面部分。圖案可包含凹陷至帶表面中之凹坑及/或自帶表面凸起或凹陷至帶表面中之「華夫(waffle)」形網格。帶之壓紋可增大其表面積且改良水流動。可藉由在燒結之前(諸如在乾燥帶之前或之後)將紋理化或圖案化滾筒按壓至生坯含鈦帶210之表面中來執行壓紋(例如，表面粗糙化或圖案化)。
在另一實施例中，在薄帶成形期間，貴金屬塗層(例如金或鉑族金屬塗層)或另一抗腐蝕劑材料塗層可形成於多孔性鈦薄片14上。在此實施例中，抗腐蝕劑材料之粉末可在燒結之前形成於經乾燥之生坯含鈦帶210之表面上，以將抗腐蝕劑塗層燒結至多孔性鈦薄片14之至少一個表面上。
在另一實施例中，可將除鈦之外的材料的離子植入至多孔性鈦薄片14中或經乾燥之生坯含鈦帶210中。舉例而言，矽原子可經離子植入至中以形成上文所描述之矽化鈦成孔劑區域。
儘管前述內容涉及特定較佳實施例，但應理解，本發明不限於此。一般熟習此項技術者將想到可對所揭示之實施例進行各種修改且該等修改意欲在本發明之範疇內。本文所引用之所有公開案、專利申請案及專利的全部內容以引用的方式併入本文中。
1:PEM電解器
2:陽極側流板
4:陰極側流板
6:流體流道
8:水進口孔
9:氧氣出口孔
10:氫氣出口孔
12:電解質
14:陽極側氣體擴散層/多孔性鈦薄片
14A:第一主側面
14B:第二主側面
15A:大孔
15B:微孔
16:陽極電極
18:陰極側氣體擴散層
20:陰極電極
22:貴金屬通孔
26:凹槽
101:腔室
102:上衝頭
104:下衝頭
106:模穴
108:模具
110:填料靴
112:鈦粉末
114:生坯鈦薄片
200:薄帶成形設備
202:漿料
204:分配室
206:帶載體網
208:刮刀
210:生坯含鈦帶
210S:鈦生坯薄片
212:乾燥室
214:加熱空氣入口
216:飽和空氣出口
218:切割台
220:燒結室
220A:上游部分
220B:下游部分
220P:隔板
圖1為PEM電解器之透視剖視圖。
圖2A至圖2F為製備用於PEM電解器之氣體擴散層之粉末冶金方法中的步驟的側面橫截面圖。
圖3為根據本發明之一實施例的氣體擴散層的透視圖。
圖4及圖5為根據本發明之實施例的氣體擴散層的另一透視圖。
圖6為根據本發明之實施例的可用於形成氣體擴散層之薄帶成形設備的側面橫截面圖。
14:陽極側氣體擴散層
200:薄帶成形設備
202:漿料
204:分配室
206:帶載體網
208:刮刀
210:生坯含鈦帶
210S:鈦生坯薄片
212:乾燥室
214:加熱空氣入口
216:飽和空氣出口
218:切割台
220:燒結室
220A:上游部分
220B:下游部分
220P:隔板
Claims (22)
- 一種經組態以充當質子交換膜(PEM)電解器之陽極側氣體擴散層的多孔性鈦薄片，其中該多孔性鈦薄片藉由粉末技術形成。
- 如請求項1之多孔性鈦薄片，其中該多孔性鈦薄片之第一主側面的孔隙度高於該多孔性鈦薄片之相對第二主側面。
- 如請求項2之多孔性鈦薄片，其中該多孔性鈦薄片之該第一主側面經組態以面向陽極側流板，且該多孔性鈦薄片之該第二主側面經組態以面向陽極電極。
- 如請求項2之多孔性鈦薄片，其中該多孔性鈦薄片之該第一主側面的孔隙度比該多孔性鈦薄片之該相對第二主側面高至少10%。
- 如請求項1之多孔性鈦薄片，其中該多孔性鈦薄片的第一主側面包括凹槽，且該多孔性鈦薄片的相對第二主側面具有缺少凹槽之實質上平坦之表面。
- 如請求項1之多孔性鈦薄片，其中： 該多孔性鈦薄片在其至少一個表面上含有氮化鈦塗層；及 該多孔性鈦薄片包含純鈦或含有超過50原子%之鈦及小於50原子%之鉬、釩、鈮、鉭或鋯中之至少一者的鈦合金。
- 如請求項1之多孔性鈦薄片，其中該多孔性鈦薄片包括雙峰孔隙大小分佈，該雙峰孔隙大小分佈包含平均孔隙大小在1微米至5微米範圍內之微孔及平均孔隙大小在30微米至40微米範圍內之大孔。
- 如請求項1之多孔性鈦薄片，其進一步包含在該多孔性鈦薄片厚度方向上延伸通過該多孔性鈦薄片之導電通孔。
- 一種PEM電解器，其包含： 陽極側流板； 陰極側流板； PEM聚合物電解質，其位於該陽極側流板與該陰極側流板之間； 陽極側氣體擴散層，其包含位於該電解質與該陽極側流板之間的如請求項1之多孔性鈦薄片； 陽極電極，其位於該陽極側氣體擴散層與該電解質之間； 陰極側氣體擴散層，其位於該電解質與該陰極側流板之間；及 陰極電極，其位於該陰極側氣體擴散層與該電解質之間。
- 如請求項9之PEM電解器，其中： 該多孔性鈦薄片之第一主側面的孔隙度高於該多孔性鈦薄片之相對第二主側面；或 該多孔性鈦薄片之該第一主側面面向該陽極側流板，且該多孔性鈦薄片之該第二主側面面向該陽極電極；或 該多孔性鈦薄片之該第一主側面的孔隙度比該多孔性鈦薄片之該相對第二主側面高至少10%；或 面向該陽極側氣體擴散層之該陽極側流板的第一主表面含有水流道凹槽，面向該陽極側流板之該第一主表面的該多孔性鈦薄片之第一主側面包括凹槽，該凹槽為該水流道凹槽的實質上鏡像，且該多孔性鈦薄片之相對第二主側面具有缺少凹槽之實質上平坦的表面。
- 一種方法，其包含藉由粉末技術製備經組態以充當質子交換膜(PEM)電解器之陽極側氣體擴散層的多孔性鈦薄片。
- 如請求項11之方法，其中該粉末技術包含粉末冶金技術，該粉末冶金技術包括將鈦粉末與潤滑劑之混合物提供至模穴中，壓縮該模穴中之鈦粉末與潤滑劑之該混合物以形成生坯薄片，將該生坯薄片脫脂，及燒結該生坯薄片以形成該多孔性鈦薄片。
- 如請求項11之方法，其中該粉末技術包含薄帶成形。
- 如請求項13之方法，其中該薄帶成形包含： 將含鈦粉末與黏合劑、溶劑及塑化劑混合以形成漿料； 將該漿料分配至帶載體網上； 使用刮刀將在該帶載體網上移動之該漿料抹平成生坯含鈦帶； 乾燥該生坯含鈦帶； 將該生坯含鈦帶切割成具有第一孔隙度之第一鈦生坯薄片；及 燒結該第一生坯薄片以形成該多孔性鈦薄片。
- 如請求項14之方法，其中： 該含鈦粉末包含元素鈦與氫化鈦粉末之混合物；及 該氫化鈦在放熱反應中熱轉化為元素鈦。
- 如請求項14之方法，其進一步包含將成孔劑材料添加至該漿料及在該燒結期間移除該成孔劑材料以在該多孔性鈦薄片中形成孔隙。
- 如請求項14之方法，其中抹平、乾燥、切割及燒結步驟連續在同一移動帶載體網上進行。
- 如請求項14之方法，其進一步包含在該燒結之前將具有不同於該第一孔隙度之第二孔隙度的第二鈦生坯薄片置於該第一鈦生坯薄片上。
- 如請求項18之方法，其中： 該第一鈦生坯薄片與該第二鈦生坯薄片彼此接觸地燒結，以使得該多孔性鈦薄片之第一主側面的孔隙度高於該多孔性鈦薄片之相對第二主側面；及 該多孔性鈦薄片之該第一主側面經組態以面向該陽極側流板，且該多孔性鈦薄片之該第二主側面經組態以面向該陽極電極。
- 如請求項14之方法，其中： 該含鈦粉末具有小於該多孔性鈦薄片之厚度之50%的平均直徑； 該含鈦粉末進一步與平均直徑在該多孔性鈦薄片之該厚度的20%以內的額外含鈦顆粒或平均長度在該多孔性鈦薄片之該厚度的20%以內的含鈦金屬線中之至少一者混合；及 該等額外含鈦顆粒或該等含鈦金屬線中之至少一者延伸通過該多孔性鈦薄片的整個厚度且充當導電通孔。
- 如請求項11之方法，其進一步包含在含氮氣氛圍中反應性燒結該多孔性鈦薄片以在該多孔性鈦薄片之至少一個表面上形成氮化鈦塗層。
- 如請求項11之方法，其進一步包含將該多孔性鈦薄片置放至該PEM電解器中。