SU743966A1 - Raw mix for producing portlandcement clinker - Google Patents
Raw mix for producing portlandcement clinker Download PDFInfo
- Publication number
- SU743966A1 SU743966A1 SU782609315A SU2609315A SU743966A1 SU 743966 A1 SU743966 A1 SU 743966A1 SU 782609315 A SU782609315 A SU 782609315A SU 2609315 A SU2609315 A SU 2609315A SU 743966 A1 SU743966 A1 SU 743966A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- producing
- raw mix
- clinker
- portlandcement
- portlandcement clinker
- Prior art date
Description
Пример 2. Готов т сырьевую смесь состава, вес. %: глина 17,0, известн к 72,5, пиритные огарки 2,0, фтористый кальций 1,0, хлористый кальций 2,5, окись магни 2,0, фосфогипс 3,0.Example 2. Preparing the raw mix of the composition, wt. %: clay 17.0, limestone to 72.5, pyrite cinders 2.0, calcium fluoride 1.0, calcium chloride 2.5, magnesium oxide 2.0, phosphogypsum 3.0.
Пример 3. Готов т сырьевую смесьExample 3. Preparing the raw mix
состава, вес. %: глина 15,0, известн к 72,0, пиритные огарки 0,5, фтористый кальций 1,5, хлористый кальций 4,0, фосфогипс 7,0 и обжигают.composition, weight. %: clay 15.0, limestone to 72.0, pyrite cinder 0.5, calcium fluoride 1.5, calcium chloride 4.0, phosphogypsum 7.0 and burned.
В табл. 1 приведены данные содержани СаОсв. в клинкере.In tab. 1 shows the content of CaOsv. in clinker.
Таблица ITable I
Приведенные в табл. 1 данные позвол ют видеть, что использование предлагаемой минерализующей добавки позвол ет добитьс завершени процессом клинкерообразовани при обжиге вплоть до 1225°С.Given in Table. 1, it can be seen that the use of the proposed mineralizing additive makes it possible to achieve the completion of the clinker formation process during roasting up to 1225 ° C.
Прочность при изгибе рассматриваемого цемента во все сроки выше, чем у цементапрототипа на 30-40%.Flexural strength of the considered cement at all times is higher than that of cementprototype by 30-40%.
Коэффициент стойкости КС вычисл ют как отношение величины среднего предела прочности при изгибе после выдерживани в агрессивном растворе к величине среднего предела прочности при изгибе образцов из того же цемента цри выдерживании их в течение того же срока в питьевой воде.The coefficient of CS resistance is calculated as the ratio of the average flexural strength after keeping in an aggressive solution to the average flexural strength of samples from the same cement, and maintaining them for the same period in drinking water.
Продолжительность изотермической выдержки остаетс прежней - 15 мин.The isothermal holding time remains the same - 15 minutes.
Прочностные характеристики получаемых клинкеров приведены в табл. 2.The strength characteristics of the resulting clinkers are given in table. 2
Таблица 2table 2
Стойкость цемента по отношению к сульфитиой коррозии в растворе сернокислого магни приведены в табл. 3.The resistance of cement to sulfite corrosion in a solution of magnesium sulphate is given in table. 3
Таблица 3Table 3
Claims (2)