SU593884A1 - Electrolyte for electrochemical polishing of titanium and its alloy articles - Google Patents
Electrolyte for electrochemical polishing of titanium and its alloy articles Download PDFInfo
- Publication number
- SU593884A1 SU593884A1 SU762338502A SU2338502A SU593884A1 SU 593884 A1 SU593884 A1 SU 593884A1 SU 762338502 A SU762338502 A SU 762338502A SU 2338502 A SU2338502 A SU 2338502A SU 593884 A1 SU593884 A1 SU 593884A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- acid
- electrolyte
- sodium salt
- titanium
- fraction
- Prior art date
Description
(54) ЭЛЕКТРОЛИТ ДЛ ЭЛЕКТРОХИМИЧЕСКОГО ПОЛИРОВАНИЯ -ИЗДЕЛИЙ ИЗ ТИТАНА И ЕГО СПЛАВОВ, ПРЕИМУЩЕСТВЕННО ИСКУССТВЕННЫХ КЛАПАНОВ СЕРДЦА(54) ELECTROLYTE DL ELECTROCHEMICAL POLISHING - PRODUCTS FROM TITANIUM AND ITS ALLOYS, PREVIOUSLY ARTIFICIAL HEART VALVES
пЩп+1 COONaPschp + 1 COONa
причем компененты, вход щие в состав электрапита, вз ты в следующем соотноше НИИ, вес.%:moreover, the compensators included in the composition of electrorapit are taken in the following ratio of scientific research institutes, wt.%
Азотна кислота7-16Nitric acid 7-16
Плавикова кислота27-ЗОHydrofluoric acid 27-ZO
Натриева соль сульфокислоты0 ,4-0,9 .Sodium salt of sulfonic acid, 4-0,9.
Натриева соль жирной кислоты0,1-0,6 Серна кислота Остальное Предлагаемый электролит при оптимальном технологическом режиме (анодна плотность тока 80-1ОО А/дм , напр жение 8-15 В, температура электролита 20-40°С, врем полировки 30-60 с) обеспечивал равномерное сглаживание микрорельефаповерхности по всем элементам издели (икс),Sodium salt of fatty acid 0.1-0.6 Sulfuric acid Else The proposed electrolyte at optimum process conditions (anode current density 80-1OO A / dm, voltage 8-15 V, electrolyte temperature 20-40 ° С, polishing time 30-60 c) ensured uniform smoothing of the microrelief of the surface over all elements of the product (X),
В процессе полировани электролитом с сол ми сульфокис;1бт и жирных кислотIn the process of electrolyte polishing with sulfoxide salts; 1bt and fatty acids
повышаетс рассеивающа способность раствора на 10-20%; наблюдаетс про вление эффекта синергизма: емкость двойного .электрического сло (46 мкФ/см ) уменьшаетс при введении 0-,6% мононатрий сульфопальмитата до 16 мкФ/см , при введении О,3% стеарата натри - до 25 МКФ/см, а Т1ри совместном добавлении - до 8 МКФ/см. На поверхности полируемого металла образуетс совершенна по строению в зка пленка, котора , обеспечивает равномерный съем металла и предотвращает точечный раствор поверх ности. , . . - V the dissipative capacity of the solution increases by 10-20%; a synergistic effect is observed: the capacity of the double electric layer (46 µF / cm) decreases with the introduction of 0-, 6% monosodium sulfopalmitate to 16 µF / cm, with the introduction of O, 3% sodium stearate - to 25 MKF / cm, and T1 joint addition - up to 8 IFF / cm. A perfectly viscous film is formed on the surface of the polished metal, which ensures a uniform removal of the metal and prevents the point solution of the surface. , . - V
в результате электрохимического полировани корпуса ИКС обладают высокой чистотой поверхности и электрохимически гомогенной поверхностью, что исключает .тромбообразование и ускор ет врем вживлени при имплантации.As a result of electrochemical polishing of the housing, the IRS have a high surface finish and an electrochemically homogeneous surface, which eliminates thrombosis and accelerates the implantation time of implantation.
Электролит прост в приготовлении и эксплуатации, обладает высокой работоспособностью .The electrolyte is easy to prepare and operate, has a high efficiency.
Формула и 3 о б р е тFormula 3 o b riet
е н и e ni
i Электролит дл электрохимического полировани изделий из титана и его сплавов , преимущественно искусственных клапанов сердца на основе серной, азотной и плавиковой кислот, о т ли чаю щи йс тем, что, с целью однородности и чистоты поверхности на всех участках издели сложной конфигурации, его состав дополнительно содержит натриевую соль сульфокислоты (фракци 0.0 ° четании с натриевой солью жирной кислоты (фракци -Cjjo ) при следующем соотнсилении .компонентов, вес. %: Азотна кислота7-16i Electrolyte for electrochemical polishing of products made of titanium and its alloys, mainly artificial heart valves based on sulfuric, nitric and hydrofluoric acids, due to the fact that, for the purpose of uniformity and cleanliness of the surface, on all parts of the product of complex configuration, its composition additionally contains the sodium salt of sulfonic acid (fraction of 0.0 ° when combined with the sodium salt of fatty acid (fraction —Cjjo) at the following ratio of components, wt.%: Nitric acid7-16
Плавикова кислота27-30Hydrofluoric acid 27-30
Натриева соль сульфокислоты0 ,4.0,9 Натриева соль жирной кислоты0,1-0,6 Серна кислотаОстальноеSodium salt of sulfonic acid 0, 4.0,9 Sodium salt of fatty acid 0,1-0,6 Sulfuric acid Other
Источники информации, прин тые во внимание при экспертизеSources of information taken into account in the examination
1. Патент Франции № 1589844, кл. С 23 OS 1/00, 1969.1. The patent of France No. 1589844, cl. From 23 OS 1/00, 1969.
Claims (1)