SU398701A1 - METHOD OF ELECTROLYTIC DEPOSITION OF THE ALLOY - Google Patents
METHOD OF ELECTROLYTIC DEPOSITION OF THE ALLOYInfo
- Publication number
- SU398701A1 SU398701A1 SU1655458A SU1655458A SU398701A1 SU 398701 A1 SU398701 A1 SU 398701A1 SU 1655458 A SU1655458 A SU 1655458A SU 1655458 A SU1655458 A SU 1655458A SU 398701 A1 SU398701 A1 SU 398701A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- alloy
- electrolytic deposition
- zinc
- nickel
- electrolyte
- Prior art date
Description
1one
Изобретение относитс к способам электроосаждени сплавов, в частности сплава цинк - никель.The invention relates to methods for electrodeposition of alloys, in particular, zinc-nickel alloy.
Известен способ электролитического осаждени сплава цинк - никель из электролита, содержащего сернокислые соли цинка, пикел , аммони и натри .A known method for the electrolytic deposition of a zinc-nickel alloy from an electrolyte containing sulphate of zinc, pickel, ammonium and sodium.
Однако такой электролит не позвол ет использовать при электролитическом осаждении повышенные плотности тока и получать покрыти с содержанием никел менее 15%.However, such an electrolyte does not allow the use of increased current densities during electrolytic deposition and to obtain coatings with a nickel content of less than 15%.
С целью получени покрыти с содержанием никел 0,5-3,5% и интенсификации процесса по предложенному способу в электролит ввод т алюминий сернокислый при следующем соотношении компонентов, г/л:In order to obtain a coating with a nickel content of 0.5-3.5% and intensify the process according to the proposed method, aluminum sulphate is introduced into the electrolyte in the following ratio of components, g / l:
Цинк сернокислый200-250Zinc sulfate200-250
Никель-аммоний сернокислый 30-40Nickel-ammonium sulfate 30-40
Алюминий сернокислый20-30Aluminum sulphate20-30
и процесс ведут при плотности тока 6-and the process is conducted at a current density of 6-
7,5 а/дм, температуре 40-45°С и рН 2,6-7.5 A / dm, temperature 40-45 ° С and pH 2.6-
3,5.3.5.
Покрыти обладают хорощим сцеплением с основой.Coatings have a good grip on the base.
Сплав цинк - никель, получаемый по предложенному способу,имеет микротвердость 120 -160 кг/мм и внутренние напр жени 100- 250 КГ/СМ2.The zinc-nickel alloy obtained by the proposed method has a microhardness of 120-160 kg / mm and an internal stress of 100-250 KG / CM2.
Предмет изобретени Subject invention
Способ электролитического осаждени сплава цинк - никель из электролита, содержащего цинк сернокислый, никель-аммоний сернокислый , отличающийс тем, что, с целью получени покрыти с содержанием никел 0,5- 3,5% и интенсификации процесса, в электролит ввод т алюминий сернокислый при следующем соотношении компонентов, г/л:The method of electrolytic deposition of the zinc-nickel alloy from an electrolyte containing zinc sulfate, nickel-ammonium sulfate, characterized in that, in order to obtain a coating with a nickel content of 0.5-3.5% and to intensify the process, aluminum sulfate is introduced into the electrolyte the following ratio of components, g / l:
Цинк сернокислый200-250Zinc sulfate200-250
Никель-аммоний сернокислый 30-40 Алюминий сернокислый20-30Nickel-ammonium sulphate 30-40 Aluminum sulphate20-30
и процесс ведут при плотности тока 6- 7,5 а/дм, температуре 40-45°С и ,б- 3,5.and the process is conducted at a current density of 6-7.5 a / dm, a temperature of 40-45 ° C, and b-3.5.