SU281779A1 - GLASS - Google Patents

GLASS

Info

Publication number
SU281779A1
SU281779A1 SU1118441A SU1118441A SU281779A1 SU 281779 A1 SU281779 A1 SU 281779A1 SU 1118441 A SU1118441 A SU 1118441A SU 1118441 A SU1118441 A SU 1118441A SU 281779 A1 SU281779 A1 SU 281779A1
Authority
SU
USSR - Soviet Union
Prior art keywords
glass
cao
aegog
chemical resistance
ratios
Prior art date
Application number
SU1118441A
Other languages
Russian (ru)
Inventor
А.Ф. Трепетов
Л.И. Дружинина
Рс. Салихзянова
Р.А. Максутов
Original Assignee
Татарский Нефт ной научно исследовательски институт
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Татарский Нефт ной научно исследовательски институт filed Critical Татарский Нефт ной научно исследовательски институт
Priority to SU1118441A priority Critical patent/SU281779A1/en
Application granted granted Critical
Publication of SU281779A1 publication Critical patent/SU281779A1/en

Description

Изобретшие относитс  к стекольной промышленности и предназначено дл  остеклени  металлических поверхностей.Invented in the glass industry and intended for the glazing of metal surfaces.

Иввестно стекло, включасщее % AEgOg. Ре20з, СаО ,Well-known glass, including% AEgOg. Re203, CaO,

8203, NagO.8203, NagO.

Лредлагаеыое стекло по сравнению с иавесташ обладает повышенной сцепл еиостью с иетадлом при температуре ниже и повышенной химической устойчивостью против агрессивных сред.Lredlagayeyy glass compared with iaveshtash has a high adhesion with the formula at a temperature below and increased chemical resistance against aggressive media.

Это достигаетс  тем, что стекло содержит указанные компонента в следующих соотношени х, весД:This is achieved by the fact that the glass contains the indicated components in the following ratios, wD:

StOgStog

/Г20з-.е20з СаО t llqO/Г20з-.э20з СаО t llqO

СцО1-3SCO1-3

более 3 more than 3

Сцепл емость данного стекла с малоуглеродистой стальо 0,55 кги,Linkage of this glass with low-carbon steel of 0.55 kg,

химическа  устойчивость на 100 см поверхности образца, мгchemical resistance per 100 cm of sample surface, mg

-0,015-0,015

NHgS.04 NHgS.04

к 1 to 1

-0,055 НаОН к 2-0,055 NaOH to 2

Предлагаемое стекло может быть использовано в качестве материала покрыти  дл  борьбы против коррозии нефтепромыслового оборудовани  и предотвращени  отложений парафина.The proposed glass can be used as a coating material to combat the corrosion of oilfield equipment and to prevent paraffin deposits.

ПРЕдаВТ ИЗОБРЕТЕНИЯPRIORITY OF THE INVENTION

Стекло дл  покрыти  металлической поверхности, включающее cOg, , fegOg, СаО, , с     его темп 3/i тем 49Q с целью улучшени  « химической устойчивости, оно ГС HTWj ъ цолощ лугчшсилдрлпрпжит йга нинА wnunnuisHipM « сцеплени  е метадлом присодержит указанные компонентн в ературе ниже и повыше-следующих соотношени х, весД: SL Og56 - 61 AegOg+SPegOg 3-4 CaO + MuO 8- 8,5 BgOg 6,6 - 7 Ma2018,5- 21 и,кроме того, CLiO1-3 более 3 28Т779.Glass for metal surface coating comprising cOg,, fegOg, CaO, with its rate 3 / i so 49Q in order to improve "chemical stability, it is heavy HTWj b tsolosch lugchshsildrlprpzhit yga Nina wnunnuisHipM« bonding e metadlom prisoderzhit said component in erature below and higher ratios, weight: SL Og56 - 61 AegOg + SPegOg 3-4 CaO + MuO 8- 8.5 BgOg 6.6 - 7 Ma2018.5-21 and, moreover, CLiO1-3 more than 3 28Т779.

SU1118441A 1966-12-10 1966-12-10 GLASS SU281779A1 (en)