SU1186594A1

SU1186594A1 - Glass

Info

Publication number: SU1186594A1
Application number: SU843730590A
Authority: SU
Inventors: Виктор Борисович Демидович; Лилия Николаевна Новикова; Иван Владимирович Пищ
Original assignee: Минский научно-исследовательский институт строительных материалов
Priority date: 1984-04-20
Filing date: 1984-04-20
Publication date: 1985-10-23

Abstract

СТЕКЛО, включающее SiOj., AIj 0, NajO и кальцийсодержащий компонент, отличающеес тем, что, с целью снижени температуры варки и начала разм гчени , оно содержит в качестве кальцийсодержащего компонента СаО и дополнительно ион F при следующем соотношении кo 0Ioнeнтoв, мас.%: SiOz60-69 AliOj6,5-7,7 Na O23-30 СаО0,4-1,2 .F0,8-1,4GLASS, including SiOj., AIj 0, NajO and calcium-containing component, characterized in that, in order to reduce the cooking temperature and start softening, it contains as calcium-containing component CaO and additionally F ion in the following ratio to 0I elements, wt.%: SiOz60-69 AliOj6.5-7.7 Na O23-30 CaO0.4-1.2 .F0.8-1.4

Description

(X) 9d СД(X) 9d rec

;o 4 1 Изобретение, относитс к составам стекол, примен емым в промьппленности строительных материалов дл полу шни стеклоплитки, в качестве глазури дл керамической плитки при температурах 550-700°С и легкоплавкого компонента при получении керамических композиций, а также в стекольной промьшшенности как легкоплавкий компонент при получении спе циальных видов стекла. Цель изобретени - снижение температуры варки стекла и начала его разм гчени . Конкретные составы стекол приведены в табл. 1, Стекло изготавливают на основе отхода производства фтористого алюмини и отхода производства алюмини . Указанные отходы представл ют 4.2 собой мелкодисперсное белое вещество . Состав отхода производства фтористого алюмини следующий, мас.%: SiOj 30,8-38,2; AlFj 1,8-4,2; вода остальное. Отход производства алюмини содержит , мас.%: NajSOj, 70; NajCOj 22; присадки солей алюмини , кали , кальци , магни 2; вода 6. . Содержание.шихты дл составов предлагаемого стекла приведено в табл. 2, Шихту приготавливают путем смешивани отдозированных количеств отходов в двухзальном смесителе. Варку осуществл ют в шамотных тигл х . Выработку стекла производ т гранул цией. Свойства предлагаемого и известного стекол приведены в табл. 3. аблица 1; o 4 1 The invention relates to glass compositions used in the production of building materials for glass tile flooring, as a glaze for ceramic tiles at temperatures of 550-700 ° C and a low-melting component in the preparation of ceramic compositions, as well as in a glass industry as low-melting component when obtaining special types of glass. The purpose of the invention is to reduce the temperature of glass melting and the beginning of its softening. Specific compositions of the glasses are given in table. 1, Glass is made on the basis of waste production of aluminum fluoride and waste production of aluminum. These wastes are 4.2 fine white matter. The composition of the waste production of aluminum fluoride the following, wt.%: SiOj 30,8-38,2; AlFj 1.8-4.2; water the rest. Waste aluminum production contains, wt%: NajSOj, 70; NajCOj 22; additives of aluminum, potassium, calcium, magnesium salts 2; water 6.. The contents of the mixture for the compositions of the proposed glass are given in table. 2, The mixture is prepared by mixing the dosed quantities of waste in a two-zone mixer. Cooking is carried out in fireclay crucibles. Glass production is produced by granulation. The properties of the proposed and known glasses are given in table. 3. table 1

SiOiSiOi

А1гОзA1gOz

NajONajO

СаОCao

Отход производстваProduction waste

фтористого алюмини aluminum fluoride

алюмини aluminum

66 7,7 66 7.7

60 7,4 25 0,5 30 1,260 7.4 25 0.5 30 1.2

Таблица 2table 2

45 5545 55

50 5050 50

40 6040 60

Температура варки.Cooking temperature.

Температура начала разм гчени , с КЛТРTemperature start softening, with CTE

в интервале температур 20 - .in the temperature range of 20 -.

-7-7

10ten

градhail

Кристаллизационна способность стекла в интервале температур 20 - The crystallization ability of glass in the temperature range of 20 -

Плотность, кг/мDensity, kg / m

Таблица 3Table 3

П90P90

11801180

12001200

480480

476476

478478

103,9111,8115,6103,9111,8115,6

Не кристаллизуетс 2357 2413 2427Does not crystallize 2357 2413 2427

Claims

GLASS, including SxO ^, Al ₂ 0 $, Na ₂ 0 and a calcium-containing component, characterized in that, in order to reduce the cooking temperature and start softening, it contains CaO as a calcium-containing component and additionally F ion in the following ratio of components, wt. %: SiO ₂ '60-69

A1 _g 0e 6.5-7.7

Na ₂ 0 23-30

CaO 0.4-1.2

F 0.8-1.4