SU1031933A1 - Raw mix for preparing portland cement clinker - Google Patents
Raw mix for preparing portland cement clinker Download PDFInfo
- Publication number
- SU1031933A1 SU1031933A1 SU823382295A SU3382295A SU1031933A1 SU 1031933 A1 SU1031933 A1 SU 1031933A1 SU 823382295 A SU823382295 A SU 823382295A SU 3382295 A SU3382295 A SU 3382295A SU 1031933 A1 SU1031933 A1 SU 1031933A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- clinker
- component
- pickling
- iron
- portland cement
- Prior art date
Abstract
СЫРЬЕВАЯ СМЕСЬ дл ПОЛУЧЕрЯ ПОРТЛАНДЦЕМЕНТНОГО КЛИНКЕРА,включающа известн ковый , глинистый, железосодержащий компоненты, о т л и ю щ а с тем, что с целью снижени температуры- клинке- . рообразовани и повышени гидратационной активности клинкера, она. содержит в: качестве железосодержащее го компонента отход нейтрализации травильных вод прокатного inpoHaaoflCTйа стального листа при следующем со .отношении крмпонентов, мас.1: Глинистый компонент .Э Отход нейтрализации травильных , вод прокатного производства стального 2-.;6 листа Иэйестн крвый .коьшонент| ОстальноеRAW MIXTURE FOR RECEIVING A PORTLAND-CEMENT CLINKER, which includes limestone, clay, iron-containing components, so that with the aim of reducing the temperature- the blade-. formation and increase in the hydration activity of clinker, it. contains in: as an iron-containing component, waste of neutralization of pickling waters of rolling steel inpoHaaoflCTya steel sheet at the following ratio of components, wt.1: Clay component .E Waste of neutralization of pickling, waters of steel production of steel 2 -; 6 sheets Ieestn krvy. Rest
Description
соwith
00 00 Изобретение относитс к техноло гии получени в жущих материалов и может быть использовано при обжиге портландцементного клинкера. Известна сырьева смесь дл производства портландцементного клинкера, включающа КЭ рбонатный, алюмосиликатный компоненты и желез сод ержащук}- добавку, в качестве ко торой примен ют колчеданные огарки или колошниковую пыль при следующем соотношении компонентов Ц, мас.% Карбонатный компонент 75-85 Алюмосиликат ,ный компонент. 14-22 Колчеданные огарки или колошникова пыль 1-3 Однако такие смеси требуют дл обжи клинкера высоких температур и повы шенного расхода топлива. Наиболее близкой к предлагаемой по технической сущности вл етс сырьева смесь дл получени портландцементного клинкера, включающа известн ковый, глинистый и железосодержащий компоненты, в качестве железосодержащего компонента использ .уют пыль, уловленную из дымовых газЪв мартеновских и конвертор ных печей сталеплавильного Произво ства при следующем соотношении-кр.мл нентов 2, мас.%: Известн ковый компонент75-97 Глинистый крмпон.ент 2,5-21 Пыль мартеновскюс и Конверто рных печей сталеплавильного Производства .0,5-4,0 Недостатком сырьевой смеси дл получени портландцементного клин кера вл етс высока температура . клинкерообразовани и низка гидра ционна активность клинкера. Цель изобретени - снижение тем пературн клинкерообразовани и повышение гидратационной активности клинкера. Пос авленна цель достигаетс тем; что сырьева смесь дл полуг чени портландцементного клинкера включающа звеотн ковый, глинистый и железосодержащий компоненты содержит в качестве железо со держащего компонента отходы нейтрализа 1ции травильных вод прокатного производства стального листа при следующем соотношении компонентов Масс.и: Глинистый компонент9-19 отход нейтрализации травильных вод прокатного ( Производства стального листа 2-6 Известн ковый компонент Остальное По химическому составу отходы нейтрализации травильных вод прокатного производства стального листа состо т1.,из окисного железа (30-40%) и двуводного сульфата кальци . Кройе этого в состав отходов нейтрализации травильных вод вход т гидроокиси кальци и магни , а также кремнезем. По зерновому составу продукт представл ет тонкодисперсное веществЬ (более 98%, проходит сито с отверсти ми 0,08 мм) и не требует дополнительного измельчени перед применением. Втабл. 1 приведен химический ссэстав отходов нейтрализации травильных вод прокатного прой зводства стального листа и пыли мартеновских и конверторных печей. Пример . Готов т сырьевые смеси дл получени портландцементного клинкера-с использованием известн ка и глины Невь нского цементного завода и железистого комЪонента предлагаемого из отходов нейтрализации травильных вод прокатного цеха стального листа ВИЗа и дл сравнени -по прототипу-с использованием пыли мартеновских печей НТМК и базового объекта - колчеданные огарки. Шихты составл ют из предварительно высушенных и размолотых до. оди-. наковой тонкости цомола компонентов и гранулируют на тарельчатом гранул торе. Гранулированные . шихты обжигают газовым топливом при 1360°С. . В. табл. 2 приведены составы шихт, .результаты обжига и испытани цементов. Минералогический состав клинкеров приведен в табл. 3. Ускорение процессов клинкерообразовани в составах, содержащих отходы нейтрализации травильных вод прокатного производства стального листа обеспечиваетс ускорением процесса декарбонизации, более ранним по влением жидкой фазы, что обеспечивает более быстрое при паниженнах температурах образование силикатов кальци . Клинкер из предлагаемой сырьевой смеси отличаетс высоким содержанием и наличием в составе клинкеров Минерала 3(Са)СаЗО4 , что все вмес;тф обеспечивает быстрое нарастание :прочности цементов во времени и более высокую конечную прочность цементов из этих клинкеров по сравнению с прототипом.00 00 The invention relates to a technology for the preparation of cementing materials and can be used in the firing of portland cement clinker. The known raw material mixture for the production of portland cement clinker, which includes CE, carbonate, aluminosilicate components and glands containing starch} is an additive, which uses pyrite cinders or flue dust in the following ratio of components C, wt.% Carbonate component 75-85 Aluminosilicate component. 14-22 Pyrite cinder or flue dust 1-3 1-3 However, such mixtures require high temperatures and increased fuel consumption to burn clinker. Closest to the proposed technical essence is the raw mix for the production of portland cement clinker, which includes limestone, clay and iron-containing components, as the iron-containing component, the dust collected from the flue gas from the open-hearth and converter furnaces of the steelmaking Production is used as the iron-containing component 2 ml.% by weight: Limestone component 75-97 Claystone 2.5–2-21 Dust of open-hearth and converter furnaces of steelmaking Production .0.5–4.0 Disadvantage of raw materials howl mixture for obtaining Portland cement wedge ker is a high temperature. clinker formation and low hydration activity of clinker. The purpose of the invention is to reduce the temperature of clinker formation and increase the hydration activity of clinker. The intended goal is achieved by that; that the raw material mixture for the half-portland cement clinker comprising the animal, clay and iron-containing components contains as iron containing the component neutralization waste of pickling waters of rolling steel sheet steel in the following ratio of components Mass: Clay component 9-19 neutralization waste of rolling mill pickling waters ( Steel sheet production 2-6 Limestone component Else By chemical composition, neutralization waste of pickling waters of rolling production is steel sheet consists of iron oxide (30–40%) and calcium sulfate dihydrate. Croye this includes calcium hydroxide and magnesium hydroxide as a neutralizing waste product, as well as silica, which is finely dispersed in grain composition (more than 98 % passes a sieve with openings of 0.08 mm) and does not require additional grinding before use.Table 1 shows the chemical part of the neutralization waste of pickling waters of the rolling steel sheet and dust of open-hearth and converter furnaces. An example. Raw materials are prepared to produce Portland cement clinker — using limestone and clay from the Nevinsky cement plant and the ferrous component of the VIZ steel sheet from the neutralizing pickling waste from the rolling mill, and for comparison — using the prototype — using the NTMK open-hearth furnace dust and the base facility - pyrite stubs. The mixtures are from pre-dried and ground to. odin The granularity of the components is ground and granulated on a plate granulator. Granular The mixture is burned with gas fuel at 1360 ° C. . V. tab. Table 2 lists blend compositions, calcining results and cement testing. The mineralogical composition of clinkers is given in table. 3. Acceleration of clinker-forming processes in compositions containing neutralizing waste from pickling waters of steel sheet rolling production is provided by accelerating the decarbonization process, the earlier appearance of the liquid phase, which ensures the formation of calcium silicates more quickly at well-balanced temperatures. The clinker from the proposed raw mix is distinguished by a high content and presence of Mineral 3 (Ca) CazO4 in the clinker composition, which takes place all together; TF ensures a rapid increase: the strength of cements over time and a higher final strength of cements from these clinkers compared to the prototype.
Использование в составе сырьевой . смеси дл получени портландцементноге клинкера в качестве железосодержащего компонента отхода нейтрализации травильных вод прокатного производства стального листа обеспечивает снижение температуры клинкерообразовани и повышение гидратационной активности клинкера, экономию топлива, увеличение производительноети печи и повышение стойкости футеровки в печах вследствие снижени температуры обжига, а также получение быстротвердеющих и высокопрочных цементов и утилизацию отходов.Use in the composition of raw materials. mixtures for obtaining portland cement clinker as an iron-containing component of the neutralization waste of pickling waters of steel sheet steel production reduces the temperature of clinker formation and increases the hydration activity of clinker, fuel economy, increased furnace productivity and increased durability of the lining in furnaces due to lower calcination temperature cements and waste management.
Т а б л и ц а 1Table 1
2,252.25
8,868.86
9,989.98
14,8414.84
,36,29 22,0 0,85 .29,75, 36.29 22.0 0.85 .29.75
4,92 57,78 6,52 2,330,994.92 57.78 6.52 2.330.99
ТаблицаTable
2.2
2222
40 3840 38
2020
Таблица 3Table 3
Claims (1)