SU872487A1 - Binder - Google Patents

Binder Download PDF

Info

Publication number
SU872487A1
SU872487A1 SU792853909A SU2853909A SU872487A1 SU 872487 A1 SU872487 A1 SU 872487A1 SU 792853909 A SU792853909 A SU 792853909A SU 2853909 A SU2853909 A SU 2853909A SU 872487 A1 SU872487 A1 SU 872487A1
Authority
SU
USSR - Soviet Union
Prior art keywords
magnesium
monoaluminate
cao
calcium
binder
Prior art date
Application number
SU792853909A
Other languages
Russian (ru)
Inventor
Николай Григорьевич Илюха
Михаил Тихонович Мельник
Валентина Ивановна Репина
Фолькер Хессе
Александр Григорьевич Моссур
Original Assignee
Харьковский Ордена Ленина Политехнический Институт Им.В.И.Ленина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Харьковский Ордена Ленина Политехнический Институт Им.В.И.Ленина filed Critical Харьковский Ордена Ленина Политехнический Институт Им.В.И.Ленина
Priority to SU792853909A priority Critical patent/SU872487A1/en
Application granted granted Critical
Publication of SU872487A1 publication Critical patent/SU872487A1/en

Description

(54) ВЯЖУЩЕЕ(54) BINDING

Изобретение относитс  к магнезиальным огнеупорным цементам. Известно в жушее, включающее WgD ll Наиболее близким по технической сущности и достигаемому эффекту к изобретению  вл етс  в жущее, включающее,%: СаО 36, 41.9; СаО-2Ае20 6,9 2J. Нецостатками известных в жущих  вл ютс  низкие огнеупорность и прочность Цель изобретени  - повышение прочности и огнеупорности в жущего. Поставленна  цель достигаетс  тем, что в жущее, включающее моноалюминаты кальци  и магни , содержит указанные компоненты при следующем соотношении, вес.%: Моноалюминат кальци 1О-ЗО Моноалюминат магни 7О-90, В жущее может быть получено двум  способами: синтезом минералов CaO-AtgO и MgOAtji Oj с последующим их смешением в заданном процентном соотношении , синтезом из компонентов, содержащих окислы Са, Mg, At, вз тых в определейном 9отн6шении. Из сырьевых материалов, окиси магни  MgO, технического глинозема МуОл, углекислого кальци  CaCOg составл ют сырьевую смесь в расчете получени  соответствующих соединений. В лабораторных услови х roTOBsrr три состава в жущего. Помол сырьевых смесей производ т по мокрому способу Размолотую смесь высушивают, брикетируют и обжигают при шш получени  СаО-АЙ О и при 16 дл  псвтученн  ftrtgD-AC Oj.Полученный клинкер в за.аанном мин& ралогическом соотношении размалывают в фарфоровой мельнице до удельной поверхности 35О6-4ООО . В таблице приведен химический и минералогический состав в жущего. Как видно лз таблицы, повьппение со- . держани  щпинели; MgrQ . составе в жущего Приводит к повышению его огнеупорности. Оптимальным составом в жущего  вл етс  состав: 2О% CaOA O MQ D-Ae2p3. Этосг состав в жущего имеет высокий предел прочности при сжатии Р 5 90кг/см в огнеупорность ,This invention relates to magnesia refractory cements. It is known in the living, including WgD II. The closest in technical essence and effect to be achieved to the invention is in the living, including,%: CaO 36, 41.9; CaO-2Ae20 6.9 2J. The non-residues of the known people are low refractoriness and strength. The purpose of the invention is to increase the strength and refractoriness of the agent. The goal is achieved by the fact that a ratant, including calcium and magnesium monoaluminates, contains these components in the following ratio, wt.%: Calcium monoaluminate 1O-3O Magnesium aluminate 7O-90, O2 can be obtained in two ways: synthesis of minerals CaO-AtgO and MgOAtji Oj followed by their mixing in a predetermined percentage ratio, by synthesis from components containing oxides of Ca, Mg, At, taken in a definite 9-6 expansion. From raw materials, magnesium oxide MgO, technical alumina MuOl, calcium carbonate CaCOg are the raw material mixture in the calculation of the corresponding compounds. In the laboratory, roTOBsrr has three ingredients per slash. Grinding of raw mixes is carried out by the wet method. The ground mixture is dried, briquetted and burned at the time of production of CaO-AO O and at 16 for juicer ftrtgD-AC Oj. The obtained clinker is in a good min & The logistic ratio is ground in a porcelain mill to a specific surface of 35О6-4ООО. The table shows the chemical and mineralogical composition of the suspect. As you can see on the table, see. holding chinello; MgrQ. composition in a tugger leads to an increase in its refractoriness. The optimal composition for the binder is: 2O% CaOA O MQ D-Ae2p3. Ethosg composition in the binder has a high compressive strength P 5 90kg / cm in refractoriness,

Химический состав,%Chemical composition,%

СаОCao

Per;. Per ;.

БЮдByd

Минералогический состав,%Mineralogical composition,%

моноапюминат кальци calcium monoapyuminate

СаО-Ае2 ОдCaO-Ae2 Aude

моноалюминат магни magnesium monoaluminate

СаО Cao

4СаОАваС - 4СаОАВАС -

СаО-М 6i02.CaO-M 6i02.

Claims (2)

Формула изобретени Invention Formula В жущее, включающее моноалюминаты кальци  И магни , отличающеес  тем, что, с цепью повышени  огнеупсфности и прочнрсти, оно содержит указанныекомпоненти при следующем соотнс  ении вес.%: 67М 5 Including calcium and magnesium monoaluminates, characterized in that, with a chain of increased refractory strength and durability, it contains the indicated components in the following ratio, wt.%: 67M 5 7,0 7.0 3,6 22,5 25,4 70,4 71,03.6 22.5 25.4 70.4 71.0 30thirty 10ten 2020 7070 9090 8080 Моноалюминат кальци 1О-ЗОCalcium monoaluminate 1O-ZO Моноалюминат магни 70-9ОMagnesium monoaluminate 70-9O Источники информации, прин тые во внимание при экспертизеSources of information taken into account in the examination 1,Авторское свидетельство СССР1, USSR author's certificate № 568616, кл. С 04 В 35/О4, 1975.No. 568616, cl. C 04 B 35 / O4, 1975. 2.Патент США № 3718492, кл. С О4 В 35/О4, 1973. 674 В жущее может быть использовано дл  изготовлени  огнеупорных бетонов и бе тонных изделий, примен емых при 2000 С и выше, разработки высокотемпературных покрытий по металлам, производства тиглей дл  плавки кислых и основных материалов.2. US patent number 3718492, cl. C O4 B 35 / O4, 1973. 674 The substrate can be used to make refractory concrete and concrete products used at 2000 C and above, to develop high-temperature coatings for metals, to produce crucibles for melting acidic and basic materials.
SU792853909A 1979-12-14 1979-12-14 Binder SU872487A1 (en)