RU2484047C1 - Ceramic mixture for making facade tiles - Google Patents

Ceramic mixture for making facade tiles Download PDF

Info

Publication number
RU2484047C1
RU2484047C1 RU2012104604/03A RU2012104604A RU2484047C1 RU 2484047 C1 RU2484047 C1 RU 2484047C1 RU 2012104604/03 A RU2012104604/03 A RU 2012104604/03A RU 2012104604 A RU2012104604 A RU 2012104604A RU 2484047 C1 RU2484047 C1 RU 2484047C1
Authority
RU
Russia
Prior art keywords
tiles
clay
facade tiles
ceramic mixture
making
Prior art date
Application number
RU2012104604/03A
Other languages
Russian (ru)
Inventor
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2012104604/03A priority Critical patent/RU2484047C1/en
Application granted granted Critical
Publication of RU2484047C1 publication Critical patent/RU2484047C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: invention relates to compositions of ceramic mixtures which can be used in making facade tiles. The ceramic mixture for making facade tiles contains the following components, wt %: clay - 69.0-77.0; scrap glass - 8.0-12.0; quartz sand - 3.0-4.0; granite screenings - 3.0-4.0; talc - 8.0-12.0.
EFFECT: high strength of tiles.
1 tbl

Description

Изобретение относится к области технологии силикатов и касается составов керамических масс, которые могут быть использованы для изготовления фасадной плитки.The invention relates to the field of technology of silicates and relates to compositions of ceramic masses that can be used for the manufacture of facade tiles.

Известна керамическая масса, содержащая, мас. %: глина 40,0-48,0; стеклобой 8,0-12,0; кварцевый песок 5,0-10,0; гранитные отсевы 28,0-35,0 [1].Known ceramic mass containing, by weight. %: clay 40.0-48.0; cullet 8.0-12.0; silica sand 5.0-10.0; granite screenings 28.0-35.0 [1].

Задача изобретения состоит в повышении прочности плитки, полученной из керамической массы.The objective of the invention is to increase the strength of tiles obtained from ceramic mass.

Технический результат достигается тем, что керамическая масса для изготовления фасадной плитки, включающая глину, стеклобой, кварцевый песок, гранитные отсевы, дополнительно содержит тальк при следующем соотношении компонентов, мас.%: глина 69,0-77,0; стеклобой 8,0-12,0; кварцевый песок 3,0-4,0; гранитные отсевы 3,0-4,0; тальк 8,0-12,0.The technical result is achieved in that the ceramic mass for the manufacture of facade tiles, including clay, cullet, quartz sand, granite screenings, additionally contains talc in the following ratio of components, wt.%: Clay 69.0-77.0; cullet 8.0-12.0; silica sand 3.0-4.0; granite screenings 3.0-4.0; talcum powder 8.0-12.0.

Для приготовления керамической массы могут быть использованы любые качественные беложгущиеся глины. Возможно использование боя любых силикатных стекол (тарного, листового, медицинского и др.). В таблице приведены составы керамической массы.For the preparation of ceramic mass, any high-quality white-burning clay can be used. It is possible to use the battle of any silicate glass (container, sheet, medical, etc.). The table shows the composition of the ceramic mass.

Таблица.Table. КомпонентыComponents Состав, мас.%:Composition, wt.%: 1one 22 33 ГлинаClay 77,077.0 73,073.0 69,069.0 СтеклобойCullet 8,08.0 10,010.0 12,012.0 Кварцевый песокQuartz sand 4,04.0 3,53,5 3,03.0 Гранитные отсевыGranite Screenings 3,03.0 3,53,5 4,04.0 ТалькTalc 8,08.0 10,010.0 12,012.0 Прочность на изгиб, МПаBending Strength, MPa ~50~ 50 ~50~ 50 ~50~ 50

Компоненты дозируют в требуемых количествах. В шаровую мельницу загружают стеклобой, кварцевый песок и гранитные отсевы, заливают воду и проводят измельчение компонентов в течение 6-8 часов до остатка 3-4% на сите 008. Затем размолотые компоненты смешивают с глиной и тальком. Влажность готовой керамической массы выбирают в пределах 10-14%. Из керамической массы прессуют плитки, которые обжигают при температуре 1250-1280°С. Возможно нанесение на поверхность обожженных плиток слоя легкоплавкой цветной эмали с последующим вторичным обжигом при температуре 800-850°СThe components are dosed in the required amounts. Glass ball, quartz sand and granite screenings are loaded into a ball mill, water is poured and components are ground for 6-8 hours to a residue of 3-4% on sieve 008. Then, the ground components are mixed with clay and talc. The moisture content of the finished ceramic mass is selected in the range of 10-14%. Tiles are pressed from the ceramic mass, which are fired at a temperature of 1250-1280 ° C. It is possible to apply a layer of low-melting colored enamel to the surface of the fired tiles, followed by secondary firing at a temperature of 800-850 ° C

Источники информацииInformation sources

1. SU 1544749, С04В 33/00, 1990.1. SU 1544749, C04B 33/00, 1990.

Claims (1)

Керамическая масса для изготовления фасадной плитки, включающая глину, стеклобой, кварцевый песок, гранитные отсевы, отличающаяся тем, что дополнительно содержит тальк при следующем соотношении компонентов, мас.%: глина 69,0-77,0; стеклобой 8,0-12,0; кварцевый песок 3,0-4,0; гранитные отсевы 3,0-4,0; тальк 8,0-12,0. Ceramic mass for the manufacture of facade tiles, including clay, cullet, quartz sand, granite screenings, characterized in that it further contains talc in the following ratio of components, wt.%: Clay 69.0-77.0; cullet 8.0-12.0; silica sand 3.0-4.0; granite screenings 3.0-4.0; talcum powder 8.0-12.0.
RU2012104604/03A 2012-02-09 2012-02-09 Ceramic mixture for making facade tiles RU2484047C1 (en)