RU2487098C1 - Ceramic mass - Google Patents

Ceramic mass Download PDF

Info

Publication number
RU2487098C1
RU2487098C1 RU2012121137/03A RU2012121137A RU2487098C1 RU 2487098 C1 RU2487098 C1 RU 2487098C1 RU 2012121137/03 A RU2012121137/03 A RU 2012121137/03A RU 2012121137 A RU2012121137 A RU 2012121137A RU 2487098 C1 RU2487098 C1 RU 2487098C1
Authority
RU
Russia
Prior art keywords
ceramic mass
talc
zircon
clay
sodium oleate
Prior art date
Application number
RU2012121137/03A
Other languages
Russian (ru)
Inventor
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2012121137/03A priority Critical patent/RU2487098C1/en
Application granted granted Critical
Publication of RU2487098C1 publication Critical patent/RU2487098C1/en

Abstract

FIELD: construction.
SUBSTANCE: ceramic mass contains clay, granite siftings, zircon, S talc and sodium oleate, at the following ratio of components, wt %: clay - 51.5-57.5; granite siftings - 16.0-22.0; zircon - 16.0-22.0; talc - 4.0-6.0; sodium oleate - 0.5-1.0.
EFFECT: products freeze resistance improvement.
1 tbl

Description

Изобретение касается составов керамических масс, которые могут быть использованы для изготовления фасадной плитки, кирпича, черепицы.The invention relates to compositions of ceramic masses that can be used for the manufacture of facade tiles, bricks, tiles.

Известна керамическая масса состава, мас.%: глина 40,0-48,0; стеклобой 8,0-12,0; кварцевый песок 5,0-10,0; гранитные отсевы 28,0-35,0; марганцевый шлам 3,0-11,0 [1].Known ceramic mass of the composition, wt.%: Clay 40,0-48,0; cullet 8.0-12.0; silica sand 5.0-10.0; granite screenings 28.0-35.0; Manganese sludge 3.0-11.0 [1].

Задача изобретения состоит в повышении морозостойкости изделий, полученных из керамической массы.The objective of the invention is to increase the frost resistance of products obtained from ceramic mass.

Технический результат достигается тем, что керамическая масса, содержащая глину и гранитные отсевы, дополнительно содержит циркон, тальк и олеат натрия при следующем соотношении компонентов, мас.%: глина 51,5-57,5; гранитные отсевы 16,0-22,0; циркон 16,0-22,0; тальк 4,0-6,0; олеат натрия 0,5-1,0.The technical result is achieved in that the ceramic mass containing clay and granite screenings additionally contains zircon, talc and sodium oleate in the following ratio of components, wt.%: Clay 51.5-57.5; granite screenings 16.0-22.0; zircon 16.0-22.0; talc 4.0-6.0; sodium oleate 0.5-1.0.

В таблице приведены составы керамической массы.The table shows the composition of the ceramic mass.

ТаблицаTable КомпонентыComponents Состав, мас.%Composition, wt.% 1one 22 33 4four ГлинаClay 51,551.5 54,054.0 57,557.5 57,557.5 Гранитные отсевыGranite Screenings 22,022.0 19,019.0 16,016,0 20,020,0 ЦирконZircon 22,022.0 21,021.0 20,020,0 16,016,0 ТалькTalc 4,04.0 5,05,0 6,06.0 6,06.0 Олеат натрияSodium oleate 0,50.5 1,01,0 0,50.5 0,50.5 Морозостойкость, циклыFrost resistance cycles 120-130120-130 120-130120-130 120-130120-130 120-130120-130

В составе керамической массы могут быть использованы качественные беложгущиеся глины любых месторождений.As part of the ceramic mass, high-quality white-burning clays of any deposits can be used.

Гранитные отсевы, циркон по отдельности размалывают до прохождения через сетку 008, смешивают с измельченной глиной, тальком, олеатом натрия и готовят керамическую массу с влажностью 18-23%. Из керамической массы формуют пластическим способом изделия, которые сушат до влажности не более 6% и обжигают при температуре 1170-1220°С. Возможно нанесение на поверхность высушенных изделий до обжига слоя глазурной суспензии.Granite screenings, zircon are individually milled to pass through a grid 008, mixed with crushed clay, talc, sodium oleate and a ceramic mass with a moisture content of 18-23% is prepared. From a ceramic mass, plastic products are molded that are dried to a moisture content of not more than 6% and fired at a temperature of 1170-1220 ° C. It is possible to apply on the surface of the dried products before firing a layer of glaze suspension.

Источники информацииInformation sources

1. SU 1544749, С04В 33/00, 1990.1. SU 1544749, C04B 33/00, 1990.

Claims (1)

Керамическая масса, содержащая глину и гранитные отсевы, отличающаяся тем, что дополнительно содержит циркон, тальк и олеат натрия при следующем соотношении компонентов, мас.%: глина - 51,5-57,5; гранитные отсевы - 16,0-22,0; циркон - 16,0-22,0; тальк - 4,0-6,0; олеат натрия - 0,5-1,0. Ceramic mass containing clay and granite screenings, characterized in that it additionally contains zircon, talc and sodium oleate in the following ratio of components, wt.%: Clay - 51.5-57.5; granite screenings - 16.0-22.0; zircon - 16.0-22.0; talc - 4.0-6.0; sodium oleate - 0.5-1.0.
RU2012121137/03A 2012-05-22 2012-05-22 Ceramic mass RU2487098C1 (en)