RU2440948C1 - Mixture for making glased tiles - Google Patents
Mixture for making glased tiles Download PDFInfo
- Publication number
- RU2440948C1 RU2440948C1 RU2010140283/03A RU2010140283A RU2440948C1 RU 2440948 C1 RU2440948 C1 RU 2440948C1 RU 2010140283/03 A RU2010140283/03 A RU 2010140283/03A RU 2010140283 A RU2010140283 A RU 2010140283A RU 2440948 C1 RU2440948 C1 RU 2440948C1
- Authority
- RU
- Russia
- Prior art keywords
- tiles
- mixture
- making
- kaolin
- alumina
- Prior art date
Abstract
Description
Изобретение относится к области технологии силикатов и касается составов шихты для изготовления печных изразцов, термостойкой керамической плитки.The invention relates to the field of technology of silicates and relates to compositions of the mixture for the manufacture of stove tiles, heat-resistant ceramic tiles.
Известен огнеупорный материал, содержащий, мас.%: муллит 10,0-25,0; корунд 20,0-48,9; глинозем 20,0-30,0; глина или каолин 15,0-25,0; оксид циркония стабилизированный 3,0-10,0 [1].Known refractory material containing, wt.%: Mullite 10.0-25.0; corundum 20.0-48.9; alumina 20.0-30.0; clay or kaolin 15.0-25.0; stabilized zirconium oxide 3.0-10.0 [1].
Задачей изобретения является снижение температуры обжига изделий, полученных из шихты.The objective of the invention is to reduce the firing temperature of products obtained from a mixture.
Технический результат достигается тем, что в шихте для изготовления изразцов, содержащей муллит, глинозем, каолин, оксид циркония, компоненты находятся при следующем соотношении, мас.%: муллит 7-9; глинозем 3-5; каолин 64-68; оксид циркония 20-24.The technical result is achieved in that in a mixture for the manufacture of tiles containing mullite, alumina, kaolin, zirconium oxide, the components are in the following ratio, wt.%: Mullite 7-9; alumina 3-5; kaolin 64-68; zirconium oxide 20-24.
В составе шихты могут быть использованы каолины следующего состава, мас.%: Si2O 46,02-46,5; Al2O3 38,69-40,17; TiO2 0,47-0,52; Fe2O3 0,55-0,92; CaO 0,05-0,19; п.п.п. 13,34-13,97.The composition of the mixture can be used kaolins of the following composition, wt.%: Si 2 O 46,02-46,5; Al 2 O 3 38.69-40.17; TiO 2 0.47-0.52; Fe 2 O 3 0.55-0.92; CaO 0.05-0.19; p.p.p. 13.34-13.97.
В таблице приведены составы шихты для изготовления изразцов.The table shows the composition of the mixture for the manufacture of tiles.
Размолотые до порошкообразного состояния (удельная поверхность 2500-3000 см2/г) компоненты шихты дозируют в требуемых количествах и смешивают. Полученную смесь увлажняют до 19-23% и формуют из нее изделия (изразцы, плитку) требуемой конфигурации, которые сушат до влажности не более 6% и обжигают при температуре 1180-1220°С. На поверхность обожженных изделий наносят слой глазури и при температуре 920-1020°C проводят второй обжиг.Milled to a powder state (specific surface 2500-3000 cm 2 / g) the components of the charge are dosed in the required quantities and mixed. The resulting mixture is moistened to 19-23% and molded from it products (tiles, tiles) of the desired configuration, which are dried to a moisture content of not more than 6% and fired at a temperature of 1180-1220 ° C. A layer of glaze is applied to the surface of the calcined products, and a second firing is carried out at a temperature of 920-1020 ° C.
Источники информацииInformation sources
1. RU 2132312, C04B 35/101, 1999.1. RU 2132312, C04B 35/101, 1999.
Claims (1)