RU2019138727A - Композиция носителя катализатора накопления оксидов азота - Google Patents

Композиция носителя катализатора накопления оксидов азота Download PDF

Info

Publication number
RU2019138727A
RU2019138727A RU2019138727A RU2019138727A RU2019138727A RU 2019138727 A RU2019138727 A RU 2019138727A RU 2019138727 A RU2019138727 A RU 2019138727A RU 2019138727 A RU2019138727 A RU 2019138727A RU 2019138727 A RU2019138727 A RU 2019138727A
Authority
RU
Russia
Prior art keywords
cerium
oxide
phase
rare earth
composition
Prior art date
Application number
RU2019138727A
Other languages
English (en)
Other versions
RU2019138727A3 (ru
RU2769079C2 (ru
Inventor
Маркос ШЁНЕБОРН
Дирк НИМЕЙЕР
Томас ХАРМЕНИНГ
Сандра ФИБИКАР
Original Assignee
Сасол Джёмани Гмбх
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Сасол Джёмани Гмбх filed Critical Сасол Джёмани Гмбх
Publication of RU2019138727A publication Critical patent/RU2019138727A/ru
Publication of RU2019138727A3 publication Critical patent/RU2019138727A3/ru
Application granted granted Critical
Publication of RU2769079C2 publication Critical patent/RU2769079C2/ru

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
    • B01J37/0027—Powdering
    • B01J37/0045—Drying a slurry, e.g. spray drying
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/34—Chemical or biological purification of waste gases
    • B01D53/92—Chemical or biological purification of waste gases of engine exhaust gases
    • B01D53/94—Chemical or biological purification of waste gases of engine exhaust gases by catalytic processes
    • B01D53/9404—Removing only nitrogen compounds
    • B01D53/9409—Nitrogen oxides
    • B01D53/9413—Processes characterised by a specific catalyst
    • B01D53/9422—Processes characterised by a specific catalyst for removing nitrogen oxides by NOx storage or reduction by cyclic switching between lean and rich exhaust gases (LNT, NSC, NSR)
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
    • B01J21/02—Boron or aluminium; Oxides or hydroxides thereof
    • B01J21/04—Alumina
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
    • B01J21/10—Magnesium; Oxides or hydroxides thereof
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/002—Mixed oxides other than spinels, e.g. perovskite
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/005—Spinels
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/10—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of rare earths
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/20—Catalysts, in general, characterised by their form or physical properties characterised by their non-solid state
    • B01J35/23—Catalysts, in general, characterised by their form or physical properties characterised by their non-solid state in a colloidal state
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
    • B01J35/391—Physical properties of the active metal ingredient
    • B01J35/393—Metal or metal oxide crystallite size
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J35/61—Surface area
    • B01J35/613—10-100 m2/g
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J35/63—Pore volume
    • B01J35/633—Pore volume less than 0.5 ml/g
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J35/63—Pore volume
    • B01J35/635—0.5-1.0 ml/g
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J35/63—Pore volume
    • B01J35/638—Pore volume more than 1.0 ml/g
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/04—Mixing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/08—Heat treatment
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
    • C01F17/00—Compounds of rare earth metals
    • C01F17/30—Compounds containing rare earth metals and at least one element other than a rare earth metal, oxygen or hydrogen, e.g. La4S3Br6
    • C01F17/32—Compounds containing rare earth metals and at least one element other than a rare earth metal, oxygen or hydrogen, e.g. La4S3Br6 oxide or hydroxide being the only anion, e.g. NaCeO2 or MgxCayEuO
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
    • C01F7/00—Compounds of aluminium
    • C01F7/02—Aluminium oxide; Aluminium hydroxide; Aluminates
    • C01F7/16—Preparation of alkaline-earth metal aluminates or magnesium aluminates; Aluminium oxide or hydroxide therefrom
    • C01F7/162—Magnesium aluminates
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
    • F01N3/00—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust
    • F01N3/08—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous
    • F01N3/10—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust
    • F01N3/24—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by constructional aspects of converting apparatus
    • F01N3/28—Construction of catalytic reactors
    • F01N3/2803—Construction of catalytic reactors characterised by structure, by material or by manufacturing of catalyst support
    • F01N3/2832—Construction of catalytic reactors characterised by structure, by material or by manufacturing of catalyst support granular, e.g. pellets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/10—Noble metals or compounds thereof
    • B01D2255/102—Platinum group metals
    • B01D2255/1021—Platinum
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/90—Physical characteristics of catalysts
    • B01D2255/91—NOx-storage component incorporated in the catalyst
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/90—Physical characteristics of catalysts
    • B01D2255/92—Dimensions
    • B01D2255/9207—Specific surface
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2523/00—Constitutive chemical elements of heterogeneous catalysts
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/12—Surface area
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/14—Pore volume
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/80—Compositional purity
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
    • F01N2370/00—Selection of materials for exhaust purification
    • F01N2370/02—Selection of materials for exhaust purification used in catalytic reactors
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02T—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
    • Y02T10/00—Road transport of goods or passengers
    • Y02T10/10—Internal combustion engine [ICE] based vehicles
    • Y02T10/12—Improving ICE efficiencies

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Combustion & Propulsion (AREA)
  • Health & Medical Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • General Chemical & Material Sciences (AREA)
  • Analytical Chemistry (AREA)
  • Environmental & Geological Engineering (AREA)
  • Biomedical Technology (AREA)
  • Thermal Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Geology (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Toxicology (AREA)
  • Mechanical Engineering (AREA)
  • General Engineering & Computer Science (AREA)
  • Catalysts (AREA)
  • Exhaust Gas Treatment By Means Of Catalyst (AREA)
  • Compounds Of Alkaline-Earth Elements, Aluminum Or Rare-Earth Metals (AREA)
  • Dispersion Chemistry (AREA)
  • Crystallography & Structural Chemistry (AREA)

Claims (34)

1. Способ получения композиции материала носителя, содержащей две фазы:
- первую фазу, содержащую смешанный оксид Mg/Al; и
- вторую фазу, содержащую оксид на основе церия и оксид на основе редкоземельного элемента (или элементов), отличающийся от оксида церия, причем вторая фаза является твердым раствором;
который включает следующие стадии:
i) приготовление водной суспензии прекурсора смешанного оксида Mg/Al;
ii) приготовление водного раствора соли церия;
iii) приготовление водного раствора соли или солей одного или более редкоземельных элементов, отличающихся от солей церия;
iv) объединение в любом порядке по меньшей мере водной суспензии из стадии i) с водным раствором из стадии ii) и водным раствором из стадии iii) с получением водной смеси;
v) сушка водной смеси с получением высушенного зернистого материала; и
vi) кальцинирование высушенного зернистого материала,
причем содержание солей одного или более редкоземельных элементов, отличающихся от церия, лежит в диапазоне от 5 масс. % до 50 масс. %, предпочтительно - в диапазоне от 10 масс. % до 35 масс. %, в пересчете на сумму масс
- солей церия из водного раствора из стадии ii) и
- солей редкоземельных элементов, отличающихся от солей церия, из водного раствора из стадии iii),
причем массу всех солей пересчитывают на массу их оксидов.
2. Способ по п. 1, отличающийся тем, что прекурсор смешанного оксида Mg/Al получают посредством гидролиза смеси соответствующих алкоксидов алюминия и магния, который дает смесь гидротальцита, бемита и воды.
3. Способ по п. 1, отличающийся тем, что соль церия содержит одну или более солей, выбранных из нитрата церия, нитрата аммония-церия, сульфата церия, карбоната церия и ацетата церия, предпочтительно ацетат церия.
4. Способ по п. 1, отличающийся тем, что соль или соли редкоземельных элементов, отличающиеся от солей церия, включают соли La, Pr, Nd, Y, Sm или их смеси.
5. Способ по п. 4, отличающийся тем, что соль редкоземельного элемента является ацетатом La, Pr, Nd, Y или их смесью.
6. Способ по любому из предыдущих пунктов, отличающийся тем, что растворы из стадии ii) и стадии iii) вначале объединяют друг с другом и затем объединяют с суспензией из стадии i).
7. Способ по любому из предыдущих пунктов, отличающийся тем, что смесь суспензии и растворов сушат распылением с получением зернистого материала, предпочтительно - порошка.
8. Способ по любому из предыдущих пунктов, отличающийся тем, что зернистый материал кальцинируют при температуре в диапазоне от 500°С до 1100°С, предпочтительно - от 800°С до 1000°С, в течение периода времени в диапазоне от 30 минут до 5 часов, с получением композиции материала носителя.
9. Композиция материала носителя, полученная способом по любому из пп. 1-8, содержащая две фазы:
- первую фазу, содержащую смешанный оксид Mg/Al; и
- вторую фазу, содержащую оксид на основе церия и оксид на основе редкоземельного элемента (или элементов), отличающийся от оксида церия; причем вторая фаза является твердым раствором.
10. Композиция материала носителя, содержащая две фазы:
- первую фазу, содержащую смешанный оксид Mg/Al; и
- вторую фазу, содержащую оксид на основе церия и оксид на основе редкоземельного элемента (или элементов), отличающийся от оксида церия, причем вторая фаза является твердым раствором,
в которой содержание первой фазы составляет по меньшей мере 50 масс. % от общей массы композиции материала носителя,
причем количество Mg в первой фазе лежит в диапазоне от 1 масс. % до 40 масс. % в пересчете на MgO от массы первой фазы в пересчете на MgO и Al2O3; причем содержание оксида редкоземельного элемента (или элементов), отличающегося от оксида церия, во второй фазе лежит в диапазоне от 5 масс. % до 50 масс. % в пересчете на оксид редкоземельного элемента (или элементов), отличающегося от церия, от общей массы второй фазы.
11. Композиция материала носителя по п. 9 или 10, отличающаяся тем, что она имеет площадь поверхности, определенную способом Брунауэра-Эммета-Теллера (BET), которая превышает 50 м2/г и более предпочтительно превышает 80 м2/г.
12. Композиция материала носителя по любому из пп. 9-11, отличающаяся тем, что она имеет объем пор, лежащий в диапазоне от 0,1 мл/г до 1,5 мл/г, более предпочтительно - от 0,4 мл/г до 1,0 мл/г.
13. Композиция материала носителя по любому из пп. 9-12, отличающаяся тем, что она содержит менее 500 частей/млн Na2O, более предпочтительно - менее 100 частей/млн Na2O.
14. Композиция материала носителя по любому из пп. 10-13, отличающаяся тем, что содержание оксида редкоземельного элемента (или элементов), отличающегося от оксида церия, во второй фазе лежит в диапазоне от 10 масс. % до 35 масс. % в пересчете на оксид редкоземельного элемента (или элементов), отличающийся от оксида церия, от общей массы второй фазы.
15. Применение композиции материала носителя по любому из пп. 9-14 в качестве компонента для накопления оксидов азота в катализаторе для обработки выхлопных газов с целью снижения содержания в них NOx.
RU2019138727A 2017-05-05 2018-05-03 Композиция носителя катализатора накопления оксидов азота RU2769079C2 (ru)