RU2019132423A - Промежуточная пленка для многослойных стекол и многослойное стекло - Google Patents

Промежуточная пленка для многослойных стекол и многослойное стекло Download PDF

Info

Publication number
RU2019132423A
RU2019132423A RU2019132423A RU2019132423A RU2019132423A RU 2019132423 A RU2019132423 A RU 2019132423A RU 2019132423 A RU2019132423 A RU 2019132423A RU 2019132423 A RU2019132423 A RU 2019132423A RU 2019132423 A RU2019132423 A RU 2019132423A
Authority
RU
Russia
Prior art keywords
interlayer film
laminated glass
layer
glass plate
polyvinyl acetal
Prior art date
Application number
RU2019132423A
Other languages
English (en)
Inventor
Хиромицу НИСИНО
Кодзи КИДО
Юусуке ООТА
Original Assignee
Секисуй Кемикал Ко., Лтд.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Секисуй Кемикал Ко., Лтд. filed Critical Секисуй Кемикал Ко., Лтд.
Publication of RU2019132423A publication Critical patent/RU2019132423A/ru

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10559—Shape of the cross-section
    • B32B17/10568—Shape of the cross-section varying in thickness
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10009—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets
    • B32B17/10036—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets comprising two outer glass sheets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10605—Type of plasticiser
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10678—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer comprising UV absorbers or stabilizers, e.g. antioxidants
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10761—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing vinyl acetal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10807—Making laminated safety glass or glazing; Apparatus therefor
    • B32B17/10816—Making laminated safety glass or glazing; Apparatus therefor by pressing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10807—Making laminated safety glass or glazing; Apparatus therefor
    • B32B17/10816—Making laminated safety glass or glazing; Apparatus therefor by pressing
    • B32B17/10871—Making laminated safety glass or glazing; Apparatus therefor by pressing in combination with particular heat treatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/06—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B27/08—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/18—Layered products comprising a layer of synthetic resin characterised by the use of special additives
    • B32B27/22—Layered products comprising a layer of synthetic resin characterised by the use of special additives using plasticisers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/30—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B60—VEHICLES IN GENERAL
    • B60J—WINDOWS, WINDSCREENS, NON-FIXED ROOFS, DOORS, OR SIMILAR DEVICES FOR VEHICLES; REMOVABLE EXTERNAL PROTECTIVE COVERINGS SPECIALLY ADAPTED FOR VEHICLES
    • B60J1/00—Windows; Windscreens; Accessories therefor
    • B60J1/02—Windows; Windscreens; Accessories therefor arranged at the vehicle front, e.g. structure of the glazing, mounting of the glazing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2250/00—Layers arrangement
    • B32B2250/03—3 layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/10—Properties of the layers or laminate having particular acoustical properties
    • B32B2307/102—Insulating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/50—Properties of the layers or laminate having particular mechanical properties
    • B32B2307/51—Elastic
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2331/00—Polyvinylesters
    • B32B2331/04—Polymers of vinyl acetate, e.g. PVA
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2605/00—Vehicles
    • B32B2605/006—Transparent parts other than made from inorganic glass, e.g. polycarbonate glazings

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Chemical & Material Sciences (AREA)
  • Biochemistry (AREA)
  • Joining Of Glass To Other Materials (AREA)
  • Instrument Panels (AREA)
  • Laminated Bodies (AREA)

Claims (37)

1. Межслойная пленка для многослойного стекла, применяемая в многослойном стекле, причем межслойная пленка включает:
один конец и другой конец, находящийся на противоположной стороне относительно упомянутого одного конца, причем
упомянутый другой конец имеет бóльшую толщину, чем толщина упомянутого одного конца,
толщина межслойной пленки не увеличивается равномерно от упомянутого одного конца к упомянутому другому концу,
средняя степень изменения частичной клиновидности, определяемая нижеследующей формулой (Х), составляет 10% или менее, когда подвергнутая окончательному соединению под давлением межслойная пленка получается на нижеследующих первой, второй, третьей, четвертой и пятой стадиях, в этом порядке, посредством использования межслойной пленки для многослойного стекла в качестве межслойной пленки перед соединением под давлением, и в каждой из межслойной пленки перед соединением под давлением и межслойной пленки после окончательного соединения под давлением каждая частичная клиновидность измеряется в каждой точке каждых 10-миллиметровых интервалов в первой области от положения в 40 мм от одного конца в сторону упомянутого другого конца межслойной пленки до срединного положения между упомянутым одним концом и упомянутым другим концом;
cтепень изменения частичной клиновидности (%) = |(частичная клиновидность межслойной пленки после окончательного соединения под давлением - частичная клиновидность межслойной пленки перед соединением под давлением)/(частичная клиновидность межслойной пленки перед соединением под давлением)| × 100 ...Формула (Х);
первая стадия: размещение межслойной пленки перед соединением под давлением на первой стеклянной пластине одной поверхностной стороной; первая стеклянная пластина имеет такой же размер, как межслойная пленка перед соединением под давлением, и имеет толщину 2 мм; первая стеклянная пластина представляет собой пластину флоат-стекла в соответствии со стандартом JIS 3202-2011;
вторая стадия: размещение второй стеклянной пластины на другой поверхности межслойной пленки таким образом, что один конец второй стеклянной пластины совпадает с одним концом межслойной пленки, и направление плоскости второй стеклянной пластины является перпендикулярным направлению плоскости первой стеклянной пластины; вторая стеклянная пластина имеет такой же размер, как межслойная пленка перед соединением под давлением, и имеет толщину 2 мм; вторая стеклянная пластина представляет собой пластину флоат-стекла в соответствии со стандартом JIS 3202-2011;
третья стадия: выполнение наклона второй стеклянной пластины, при этом фиксируя упомянутый один конец второй стеклянной пластины, для приведения поверхности второй стеклянной пластины в контакт с другой поверхностью межслойной пленки, и приведение второй стеклянной пластины в такое состояние, что вес второго стекла распределяется на другую поверхность межслойной пленки;
четвертая стадия: предварительное соединение под давлением с помощью вальцового пресса при температуре 240°С и линейном давлении 98 Н/см;
пятая стадия: окончательное соединение под давлением при температуре 140°С и давлении 1,3 МПа с образованием межслойной пленки, подвергнутой окончательному соединению под давлением; полученная подвергнутая окончательному соединению под давлением межслойная пленка находится в таком наслоенном состоянии, в котором подвергнутая окончательному соединению под давлением межслойная пленка размещается между первой стеклянной пластиной и второй стеклянной пластиной.
2. Межслойная пленка для многослойного стекла по п. 1, в которой, когда каждая частичная клиновидность измеряется в каждой точке каждого 10-миллиметрового интервала во второй области от положения в 40 мм от упомянутого одного конца в сторону упомянутого другого конца межслойной пленки, до положения в 40 мм от упомянутого другого конца в сторону упомянутого одного конца межслойной пленки, максимальное значение степени изменения частичной клиновидности, определяемой формулой (Х), составляет 15% или менее.
3. Межслойная пленка для многослойного стекла по п. 1 или 2, причем межслойная пленка представляет собой межслойную пленку для многослойного стекла, в котором межслойная пленка и вторая стеклянная пластина находятся в контакте между собой в отдельных двух или более точках в области от положения упомянутого одного конца межслойной пленки до срединного положения между упомянутым одним концом и упомянутым другим концом, после третьей стадии и перед четвертой стадией при получении межслойной пленки, подвергнутой окончательному соединению под давлением в ходе первой, второй, третьей, четвертой и пятой стадий, в этом порядке.
4. Межслойная пленка для многослойного стекла по любому из пп. 1-3, причем межслойная пленка представляет собой межслойную пленку для многослойного стекла, в котором межслойная пленка и вторая стеклянная пластина находятся в контакте друг с другом в отдельных трех или более точках в области от положения упомянутого одного конца до положения упомянутого другого конца межслойной пленки, после третьей стадии и перед четвертой стадией при получении межслойной пленки, подвергнутой окончательному соединению под давлением в ходе первой, второй, третьей, четвертой и пятой стадий, в этом порядке.
5. Межслойная пленка для многослойного стекла по любому из пп. 1-4, включающая слой, имеющий модуль упругости G' при температуре 23°С, составляющий 4 МПа или более.
6. Межслойная пленка для многослойного стекла по любому из пп. 1-4, включающая слой, имеющий модуль упругости G' при температуре 23°С, составляющий 4 МПа или более, в качестве поверхностного слоя.
7. Межслойная пленка для многослойного стекла по любому из пп. 1-6, дополнительно содержащая термопластичную смолу.
8. Межслойная пленка для многослойного стекла по любому из пп. 1-7, дополнительно содержащая пластификатор.
9. Межслойная пленка для многослойного стекла по любому из пп. 1-8, причем межслойная пленка включает слой, содержащий термопластичную смолу, и пластификатор с содержанием 25 частей по весу или более и 45 частей по весу или менее, относительно 100 частей по весу термопластичной смолы.
10. Межслойная пленка для многослойного стекла по любому из пп. 1-9, дополнительно включающая:
первый слой, и
второй слой, размещенный на стороне первой поверхности первого слоя.
11. Межслойная пленка для многослойного стекла по п. 10, в которой
первый слой содержит поливинилацетальную смолу,
второй слой содержит поливинилацетальную смолу, и
содержание гидроксильных групп в поливинилацетальной смоле в первом слое является более низким, чем содержание гидроксильных групп в поливинилацетальной смоле во втором слое.
12. Межслойная пленка для многослойного стекла по п. 10 или 11, в которой
первый слой содержит поливинилацетальную смолу,
второй слой содержит поливинилацетальную смолу,
первый слой содержит пластификатор,
второй слой содержит пластификатор, и
содержание пластификатора в первом слое относительно 100 частей по весу поливинилацетальной смолы в первом слое является более высоким, чем содержание пластификатора во втором слое относительно 100 частей по весу поливинилацетальной смолы во втором слое.
13. Многослойное стекло, включающее:
первый элемент многослойного стекла;
второй элемент многослойного стекла; и
компонент в виде межслойной пленки, размещенный между первым элементом многослойного стекла и вторым элементом многослойного стекла,
причем компонент в виде межслойной пленки сформирован из межслойной пленки для многослойного стекла по любому из пп. 1-12.
RU2019132423A 2017-03-15 2018-03-14 Промежуточная пленка для многослойных стекол и многослойное стекло RU2019132423A (ru)