RU2018110576A - Молекулярное сито ssz-91, способы получения ssz-91, и применение ssz-91 - Google Patents
Молекулярное сито ssz-91, способы получения ssz-91, и применение ssz-91 Download PDFInfo
- Publication number
- RU2018110576A RU2018110576A RU2018110576A RU2018110576A RU2018110576A RU 2018110576 A RU2018110576 A RU 2018110576A RU 2018110576 A RU2018110576 A RU 2018110576A RU 2018110576 A RU2018110576 A RU 2018110576A RU 2018110576 A RU2018110576 A RU 2018110576A
- Authority
- RU
- Russia
- Prior art keywords
- molecular sieve
- sio
- paragraphs
- sieve according
- ssz
- Prior art date
Links
- 239000002808 molecular sieve Substances 0.000 title claims 20
- URGAHOPLAPQHLN-UHFFFAOYSA-N sodium aluminosilicate Chemical compound [Na+].[Al+3].[O-][Si]([O-])=O.[O-][Si]([O-])=O URGAHOPLAPQHLN-UHFFFAOYSA-N 0.000 title claims 20
- 238000000034 method Methods 0.000 title claims 5
- 229910004298 SiO 2 Inorganic materials 0.000 claims 10
- 229930195733 hydrocarbon Natural products 0.000 claims 5
- 150000002430 hydrocarbons Chemical class 0.000 claims 5
- 239000000463 material Substances 0.000 claims 5
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims 4
- 239000011541 reaction mixture Substances 0.000 claims 4
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 claims 3
- 238000006243 chemical reaction Methods 0.000 claims 3
- 230000000737 periodic effect Effects 0.000 claims 3
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims 2
- 239000004215 Carbon black (E152) Substances 0.000 claims 2
- VZJFGSRCJCXDSG-UHFFFAOYSA-N Hexamethonium Chemical group C[N+](C)(C)CCCCCC[N+](C)(C)C VZJFGSRCJCXDSG-UHFFFAOYSA-N 0.000 claims 2
- -1 hydroxide ions Chemical class 0.000 claims 2
- 229910052814 silicon oxide Inorganic materials 0.000 claims 2
- 238000002441 X-ray diffraction Methods 0.000 claims 1
- 229910021536 Zeolite Inorganic materials 0.000 claims 1
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims 1
- 229910052782 aluminium Inorganic materials 0.000 claims 1
- 239000003054 catalyst Substances 0.000 claims 1
- 239000013078 crystal Substances 0.000 claims 1
- 238000002425 crystallisation Methods 0.000 claims 1
- 230000008025 crystallization Effects 0.000 claims 1
- HNPSIPDUKPIQMN-UHFFFAOYSA-N dioxosilane;oxo(oxoalumanyloxy)alumane Chemical compound O=[Si]=O.O=[Al]O[Al]=O HNPSIPDUKPIQMN-UHFFFAOYSA-N 0.000 claims 1
- 229950002932 hexamethonium Drugs 0.000 claims 1
- 229910052710 silicon Inorganic materials 0.000 claims 1
- 239000010703 silicon Substances 0.000 claims 1
- 239000000377 silicon dioxide Substances 0.000 claims 1
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims 1
- 239000010457 zeolite Substances 0.000 claims 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B39/00—Compounds having molecular sieve and base-exchange properties, e.g. crystalline zeolites; Their preparation; After-treatment, e.g. ion-exchange or dealumination
- C01B39/02—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof; Direct preparation thereof; Preparation thereof starting from a reaction mixture containing a crystalline zeolite of another type, or from preformed reactants; After-treatment thereof
- C01B39/46—Other types characterised by their X-ray diffraction pattern and their defined composition
- C01B39/48—Other types characterised by their X-ray diffraction pattern and their defined composition using at least one organic template directing agent
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/70—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65
- B01J29/7023—EUO-type, e.g. EU-1, TPZ-3 or ZSM-50
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/70—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65
- B01J29/703—MRE-type, e.g. ZSM-48
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/70—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65
- B01J29/72—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65 containing iron group metals, noble metals or copper
- B01J29/74—Noble metals
- B01J29/7446—EUO-type, e.g. EU-1, TPZ-3 or ZSM-50
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/70—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65
- B01J29/72—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65 containing iron group metals, noble metals or copper
- B01J29/74—Noble metals
- B01J29/7461—MRE-type, e.g. ZSM-48
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/80—Mixtures of different zeolites
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/40—Catalysts, in general, characterised by their form or physical properties characterised by dimensions, e.g. grain size
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B39/00—Compounds having molecular sieve and base-exchange properties, e.g. crystalline zeolites; Their preparation; After-treatment, e.g. ion-exchange or dealumination
- C01B39/02—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof; Direct preparation thereof; Preparation thereof starting from a reaction mixture containing a crystalline zeolite of another type, or from preformed reactants; After-treatment thereof
- C01B39/023—Preparation of physical mixtures or intergrowth products of zeolites chosen from group C01B39/04 or two or more of groups C01B39/14 - C01B39/48
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2229/00—Aspects of molecular sieve catalysts not covered by B01J29/00
- B01J2229/10—After treatment, characterised by the effect to be obtained
- B01J2229/18—After treatment, characterised by the effect to be obtained to introduce other elements into or onto the molecular sieve itself
- B01J2229/186—After treatment, characterised by the effect to be obtained to introduce other elements into or onto the molecular sieve itself not in framework positions
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G2300/00—Aspects relating to hydrocarbon processing covered by groups C10G1/00 - C10G99/00
- C10G2300/70—Catalyst aspects
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Crystallography & Structural Chemistry (AREA)
- Life Sciences & Earth Sciences (AREA)
- General Life Sciences & Earth Sciences (AREA)
- Geology (AREA)
- Inorganic Chemistry (AREA)
- Silicates, Zeolites, And Molecular Sieves (AREA)
- Catalysts (AREA)
- Production Of Liquid Hydrocarbon Mixture For Refining Petroleum (AREA)
- Solid-Sorbent Or Filter-Aiding Compositions (AREA)
- Compounds Of Unknown Constitution (AREA)
Claims (31)
1. Молекулярное сито, принадлежащее к семейству цеолитов ZSM-48, причем молекулярное сито имеет
молярное соотношение оксида кремния к оксиду алюминия от 40 до 200,
по меньшей мере 70% политипа 6 от общего количества материала типа ZSM-48, присутствующего в продукте, и
дополнительную фазу молекулярного сита EUO-типа в количестве от 0 до 3,5% мас. от общего количества продукта; и
при том, что молекулярное сито имеет морфологию, характеризующуюся как поликристаллические агрегаты, содержащие кристаллиты, имеющие в совокупности средний коэффициент формы от 1 до 8.
2. Молекулярное сито по п. 1, отличающееся тем, что молекулярное сито имеет, в своей свежесинтезированнрй форме, рентгеновскую дифрактограмму, по существу описанную в следующей Таблице:
2-тета Межплоскостное расстояние (нм) Относительная интенсивность(b)
7,55±0,20 1,170 W
8,71±0,20 1,015 W
12,49±0,20 0,708 W
15,12±0,20 0,586 W
21,18±0,20 0,419 VS
22,82±0,20 0,390 VS
24,62±0,20 0,361 W
(b) W=слабая (от >0 до≤20); M=средняя (от >20 до≤40); S=сильная (от >40 до≤60); VS=очень сильная (от >60 до≤100).
3. Молекулярное сито по п. 1 или 2, отличающееся тем, что имеет молярное соотношение оксида кремния к оксиду алюминия от 70 до 160.
4. Молекулярное сито по любому из пп. 1-3, отличающееся тем, что имеет молярное соотношение оксида кремния к оксиду алюминия от 80 до 140.
5. Молекулярное сито по любому из пп. 1-4, отличающееся тем, что содержит по меньшей мере 80% политипа 6 от общего количества материала типа ZSM-48, присутствующего в продукте.
6. Молекулярное сито по любому из пп. 1-5, отличающееся тем, что содержит от 0,1 до 2% мас. EU-1.
7. Молекулярное сито по любому из пп. 1-6, отличающееся тем, что кристаллиты имеют в совокупности средний коэффициент формы от 1 до 5.
8. Молекулярное сито по любому из пп. 1-7, отличающееся тем, что содержит по меньшей мере 90% политипа 6 от общего количества материала типа ZSM-48, присутствующего в продукте.
9. Молекулярное сито по любому из пп. 1-8, отличающееся тем, что кристаллиты имеют в совокупности средний коэффициент формы от 1 до 3.
10. Способ получения молекулярного сита по любому из пп. 1-9, включающий приготовление реакционной смеси, содержащей по меньшей мере один источник кремния, по меньшей мере один источник алюминия, по меньшей мере один источник элемента, выбранного из Групп I и II Периодической таблицы элементов, гидроксид-ионы, катионы гексаметония и воду; и воздействие на реакционную смесь условий кристаллизации, достаточных для образования кристаллов молекулярного сита.
11. Способ по п. 10, отличающийся тем, что молекулярное сито получают из реакционной смеси, содержащей, в переводе на молярные соотношения, следующие материалы:
где M выбирают из группы, состоящей из элементов Групп I и II Периодической таблицы элементов; и Q обозначает катион гексаметония.
12. Способ по п. 10, отличающийся тем, что молекулярное сито получают из реакционной смеси, содержащей, в переводе на молярные соотношения, следующие материалы:
где M выбирают из группы, состоящей из элементов Групп I и II Периодической таблицы элементов; и Q обозначает катион гексаметония.
13. Способ конверсии углеводородов, включающий приведение углеводородного сырья в контакт с катализатором, содержащим молекулярное сито по любому из пп. 1-9, в условиях, пригодных для конверсии углеводорода.
14. Применение молекулярного сита по любому из пп. 1-9, для конверсии углеводородов в условиях, пригодных для конверсии углеводородов.