RU2015118437A - Реакционная система для изготовления твердых пур- и пир-пеноматериалов, содержащих слоистые силикаты - Google Patents

Реакционная система для изготовления твердых пур- и пир-пеноматериалов, содержащих слоистые силикаты Download PDF

Info

Publication number
RU2015118437A
RU2015118437A RU2015118437A RU2015118437A RU2015118437A RU 2015118437 A RU2015118437 A RU 2015118437A RU 2015118437 A RU2015118437 A RU 2015118437A RU 2015118437 A RU2015118437 A RU 2015118437A RU 2015118437 A RU2015118437 A RU 2015118437A
Authority
RU
Russia
Prior art keywords
reaction system
isocyanates
paragraphs
reacting
mass
Prior art date
Application number
RU2015118437A
Other languages
English (en)
Inventor
Штефан ЛИНДНЕР
Вольфганг ФРИДЕРИХС
Райнхард ШТРАЙ
Томас СОТТМАНН
Диана ЭНГЕЛЕН
Original Assignee
Байер Матириальсайенс Аг
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Байер Матириальсайенс Аг filed Critical Байер Матириальсайенс Аг
Publication of RU2015118437A publication Critical patent/RU2015118437A/ru

Abstract

1. Реакционная система для изготовления твердых ПУР- и ПИР-пеноматериалов, включающая в себя следующие компоненты:А) соединение, способное реагировать с изоцианатами;B1) вспенивающее средство;C) вспенивающее средство в сверхкритическом или околокритическом состоянии;D) полиизоцианат; иE) слоистый силикат.2. Реакционная система для изготовления твердых ПУР- и ПИР-пеноматериалов, включающая в себя следующие компоненты:B2) поверхностно-активный компонент с функциональными группами, способными реагировать с изоцианатами;C) вспенивающее средство в сверхкритическом или околокритическом состоянии;D) полиизоцианат; иΕ) слоистый силикат.3. Реакционная система по п. 1, отличающаяся тем, что реакционная система дополнительно включает в себя:В2) поверхностно-активный компонент с функциональными группами, способными реагировать с изоцианатами.4. Реакционная система по п. 2, отличающаяся тем, что реакционная система дополнительно включает в себя:А) соединение, способное реагировать с изоцианатами.5. Реакционная система по одному из пп. 1-4, отличающаяся тем, что реакционная система содержит от 1 до 65% масс. поверхностно-активного компонента В1) и/или В2), в особенности от 2 до 45% масс., предпочтительно от 5 до 30% масс., в пересчете на реакционную систему.6. Реакционная система по одному из пп. 1-4, отличающаяся тем, что поверхностно-активный компонент В1) и/или В2) выбран из неионных ПАВ, причем значение HLB составляет от 4 до 18 в соответствии с уравнением HLB=20·(1-M/M), где M- это молярная масса гидрофобной части, a M - общая масса неионного ПАВ, еще более предпочтительно от 8 до 16.7. Реакционная система по одному из пп. 1-4, отличающаяся тем, что функциональность по отношению к изоцианатам соединения А) и/или соединения В2)

Claims (15)

1. Реакционная система для изготовления твердых ПУР- и ПИР-пеноматериалов, включающая в себя следующие компоненты:
А) соединение, способное реагировать с изоцианатами;
B1) вспенивающее средство;
C) вспенивающее средство в сверхкритическом или околокритическом состоянии;
D) полиизоцианат; и
E) слоистый силикат.
2. Реакционная система для изготовления твердых ПУР- и ПИР-пеноматериалов, включающая в себя следующие компоненты:
B2) поверхностно-активный компонент с функциональными группами, способными реагировать с изоцианатами;
C) вспенивающее средство в сверхкритическом или околокритическом состоянии;
D) полиизоцианат; и
Ε) слоистый силикат.
3. Реакционная система по п. 1, отличающаяся тем, что реакционная система дополнительно включает в себя:
В2) поверхностно-активный компонент с функциональными группами, способными реагировать с изоцианатами.
4. Реакционная система по п. 2, отличающаяся тем, что реакционная система дополнительно включает в себя:
А) соединение, способное реагировать с изоцианатами.
5. Реакционная система по одному из пп. 1-4, отличающаяся тем, что реакционная система содержит от 1 до 65% масс. поверхностно-активного компонента В1) и/или В2), в особенности от 2 до 45% масс., предпочтительно от 5 до 30% масс., в пересчете на реакционную систему.
6. Реакционная система по одному из пп. 1-4, отличающаяся тем, что поверхностно-активный компонент В1) и/или В2) выбран из неионных ПАВ, причем значение HLB составляет от 4 до 18 в соответствии с уравнением HLB=20·(1-Mh/M), где Mh - это молярная масса гидрофобной части, a M - общая масса неионного ПАВ, еще более предпочтительно от 8 до 16.
7. Реакционная система по одному из пп. 1-4, отличающаяся тем, что функциональность по отношению к изоцианатам соединения А) и/или соединения В2) составляет 1,8-6,0, в частности ≥2,0.
8. Реакционная система по одному из пп. 1-4, отличающаяся тем, что вспенивающее средство С) выбрано из группы, включающей в себя линейные, разветвленные или циклические углеводороды с 1-6 атомами углерода, линейные, разветвленные или циклические фтороуглеводороды с 1-6 атомами углерода, N2, О2, аргон и/или СО2, а предпочтительно состоит из смеси СО2 и по меньшей мере еще одного другого из указанных вспенивающих средств, причем целесообразно, чтобы доля CO2 в смеси вспенивающих средств составляла по меньшей мере 30% масс., более предпочтительно по меньшей мере 50% масс., особо предпочтительно по меньшей мере 70% масс.
9. Реакционная система по одному из пп. 1-4, отличающаяся тем, что вспенивающее средство С) в реакционной системе находится в форме капель, причем размер капель составляет от 1 нм до 100 нм.
10. Реакционная система по одному из пп. 1-4, отличающаяся тем, что вспенивающее средство С) дополнительно включает в себя гидрофобный сокомпонент, который предпочтительно выбран из группы, включающей в себя длинноцепочечные алканы по меньшей мере с 8 атомами углерода, ароматические соединения по меньшей мере с 8 атомами углерода, полисилоксаны ("силиконовые масла") по меньшей мере с 3 атомами кремния и длинноцепочечные органические простые эфиры, сложные эфиры и кетоны по меньшей мере с 8 атомами углерода.
11. Реакционная система по одному из пп. 2-4, отличающаяся тем, что у соединения В2) среднее число ОН-групп на молекулу составляет от 1,0 до 5, предпочтительно от 2,0 до 3,5, причем в частности по меньшей мере одна из ОН-групп этерифицирована жирной кислотой, и причем предпочтительно доля этерифицированной жирной кислоты составляет от ≥0,5% масс. до ≤25% масс. в пересчете на реакционную смесь, включающую в себя компоненты А), В1 и/или В2), С), D) и Е), предпочтительно от ≥2% масс. до ≤15% масс., особо предпочтительно от ≥4% масс. до ≤10% масс.
12. Способ изготовления твердых ПУР- и ПИР-пеноматериалов, при осуществлении которого компоненты реакционной системы по одному из пп. 1-11 смешивают друг с другом и подвергают взаимодействию, причем, в частности, сначала создают смесь из всех компонентов, за исключением полиизоцианата D), в смесительной головке под давлением, в условиях, сверхкритических или околокритических для вспенивающего средства С), а затем к этой смеси добавляют полиизоцианат D) и выполняют вывод из смесительной головки под давлением, снижая давление до атмосферного или ниже, осуществляют взаимодействие компонентов реакционной системы, в частности под давлением от 40 до 300 бар и/или при температуре от 10 до 80°С, причем предпочтительно в случае вспенивающего средства, которое содержит СО2 или состоит из него, устанавливают давление по меньшей мере в 73,75 бар и температуру по меньшей мере в 31°С.
13. Твердый пеноматериал для применения в качестве теплоизоляции, в частности для изготовления теплоизоляционных плит, металлических композитных панелей или для изоляции холодильников, который получают путем смешивания и взаимодействия компонентов реакционной системы по одному из пп. 1-11, причем твердый пеноматериал, в частности, представляет собой полиуретановую пену и/или полиизоциануратную пену, которая предпочтительно обладает объемной плотностью согласно DIN EN 1602 от 20 кг/м3 до 160 кг/м3.
14. Применение реакционной системы, включающей в себя следующие компоненты, для изготовления твердых ПУР- и ПИР-пеноматериалов:
А) соединение, способное реагировать с изоцианатами;
В1) поверхностно-активный компонент;
C) вспенивающее средство в сверхкритическом или околокритическом состоянии;
D) полиизоцианат; и
Е) слоистый силикат.
15. Применение реакционной системы, включающей в себя следующие компоненты, для изготовления твердых ПУР- и ПИР-пеноматериалов:
В2) поверхностно-активный компонент с функциональными группами, способными реагировать с изоцианатами;
C) вспенивающее средство в сверхкритическом или околокритическом состоянии;
D) полиизоцианат; и
Е) слоистый силикат.
RU2015118437A 2012-10-19 2013-10-17 Реакционная система для изготовления твердых пур- и пир-пеноматериалов, содержащих слоистые силикаты RU2015118437A (ru)