RU2005132999A - Готовая к употреблению композиция отверждающегося типа и относящийся к ней комплект - Google Patents
Готовая к употреблению композиция отверждающегося типа и относящийся к ней комплект Download PDFInfo
- Publication number
- RU2005132999A RU2005132999A RU2005132999/03A RU2005132999A RU2005132999A RU 2005132999 A RU2005132999 A RU 2005132999A RU 2005132999/03 A RU2005132999/03 A RU 2005132999/03A RU 2005132999 A RU2005132999 A RU 2005132999A RU 2005132999 A RU2005132999 A RU 2005132999A
- Authority
- RU
- Russia
- Prior art keywords
- composition
- composition according
- acid
- combinations
- salt
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
- C04B28/14—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing calcium sulfate cements
- C04B28/145—Calcium sulfate hemi-hydrate with a specific crystal form
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B40/00—Processes, in general, for influencing or modifying the properties of mortars, concrete or artificial stone compositions, e.g. their setting or hardening ability
- C04B40/06—Inhibiting the setting, e.g. mortars of the deferred action type containing water in breakable containers ; Inhibiting the action of active ingredients
- C04B40/0641—Mechanical separation of ingredients, e.g. accelerator in breakable microcapsules
- C04B40/065—Two or more component mortars
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/10—Compositions or ingredients thereof characterised by the absence or the very low content of a specific material
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2201/00—Mortars, concrete or artificial stone characterised by specific physical values
- C04B2201/10—Mortars, concrete or artificial stone characterised by specific physical values for the viscosity
Landscapes
- Chemical & Material Sciences (AREA)
- Ceramic Engineering (AREA)
- Engineering & Computer Science (AREA)
- Organic Chemistry (AREA)
- Materials Engineering (AREA)
- Structural Engineering (AREA)
- Analytical Chemistry (AREA)
- Crystallography & Structural Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Inorganic Chemistry (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Curing Cements, Concrete, And Artificial Stone (AREA)
- Physical Or Chemical Processes And Apparatus (AREA)
- Preparation Of Clay, And Manufacture Of Mixtures Containing Clay Or Cement (AREA)
Claims (42)
1. Композиция, включающая:
a) воду;
b) обожженный гипс и
с) ингибитор схватывания, выбранный из группы, состоящей из полиакриловой кислоты, соли полиакриловой кислоты и их комбинаций,
где массовое отношение воды к обожженному гипсу в композиции составляет от примерно 0,15 до примерно 0,5 и где композиция имеет вязкость от примерно 5000 сП до примерно 48000 сП, и указанная композиция образует связную матрицу отвержденного гипса при смешивании с активатором взаимодействия полугидрата сульфата кальция с водой с получением отвержденного гипса.
2. Композиция по п.1, где композиция по существу не содержит одного или нескольких следующих компонентов:
i) полиакриламид;
ii) карбонат кальция;
iii) четырехзамещенный пирофосфат натрия и
iv) лимонную кислоту
3. Композиция по п.1, где композиция имеет срок годности при хранении, по меньшей мере, примерно 90 дней.
4. Композиция по п.1, где при добавлении активатора и образовании связной матрицы отвержденного гипса композиция имеет предел прочности при сжатии, по меньшей мере, примерно 1500 фунт/кв.дюйм.
5. Композиция по п.1, где композиция имеет рН от примерно 5,5 до примерно 10.
6. Композиция по п.1, где композиция имеет рН от примерно 8 до примерно 9.
7. Композиция по п.1, где вода присутствует в количестве от примерно 15% до примерно 30% от массы композиции.
8. Композиция по п.1, где обожженный гипс представляет собой альфа-полугидрат сульфата кальция.
9. Композиция по п.1, дополнительно включающая армирующий полимер.
10. Композиция по п.1, где армирующий полимер выбран из группы, состоящей из полиуретана, сополимера стирола и бутадиена, акрилового латекса или его соли, поливинилацетата и их комбинаций.
11. Композиция по п.1, где обожженный гипс присутствует в количестве от примерно 50% до примерно 85% от массы композиции.
12. Композиция по п.1, где ингибитор схватывания имеет молекулярную массу от примерно 1800 Дальтон до примерно 2200 Дальтон.
13. Композиция по п.1, где ингибитор схватывания выбран из группы, состоящей из полиакрилата натрия, полиакрилата калия, полиакриловой кислоты и их комбинаций.
14. Композиция по п.1, где ингибитор схватывания присутствует в количестве от примерно 0,45% до примерно 1,2% от массы композиции.
15. Композиция по п.1, где композиция дополнительно включает хелатообразующее вещество.
16. Композиция по п.15, где хелатообразующее вещество выбрано из группы, состоящей из 2-амино-2-метил-1-пропанола, гидроксида аммония, триэтаноламина и их комбинаций.
17. Композиция по п.15, где хелатообразующее вещество присутствует в количестве от примерно 0,1% до примерно 0,5% от массы готовой к употреблению композиции.
18. Композиция по п.15, где массовое отношение ингибитора схватывания к хелатообразующему веществу составляет от примерно 1,2:1 до примерно 6:1.
19. Композиция по п.1, дополнительно включающая органическое полифосфоновое соединение или смесь органических полифосфоновых соединений.
20. Композиция по п.19, где обожженный гипс представляет собой бета-полугидрат сульфата кальция.
21. Композиция по п.19, где органическое полифосфоновое соединение выбрано из группы, состоящей из аминотри(метиленфосфоновой кислоты), пентанатриевой соли аминотри(метиленфосфоновой кислоты), 1-гидроксиэтилиден-1,1-дифосфоновой кислоты, тетранатриевой соли 1-гидроксиэтилиден-1,1-дифосфоновой кислоты, пентанатриевой соли диэтилентриамин-пента(метиленфосфоновой кислоты), тринатриевой соли диэтилентриамин-пента(метиленфосфоновой кислоты), гексаметилендиамин-тетра(метиленфосфоновой кислоты), калиевой соли гексаметилендиамин-тетра(метиленфосфоновой кислоты) и их комбинаций.
22. Композиция по п.19, где органическое полифосфоновое соединение или смесь органических полифосфоновых соединений присутствует в количестве от примерно 0,1% до примерно 0,5% от массы композиции.
23. Композиция по п.1, где композиция является текучей в течение, по меньшей мере, 0,25 ч после смешивания с активатором.
24. Композиция по п.1, где ингибитор схватывания выбран из группы, состоящей из полиэтакриловой кислоты, полиметакриловой кислоты, полиэтакрилата, полиметакрилата и их комбинаций.
25. Композиция по п.1, дополнительно включающая пластификатор.
26. Композиция по п.25, где указанный пластификатор представляет собой полиэфирполикарбоновое соединение, соль полиэфирполикарбонового соединения или их комбинации.
27. Композиция по п.26, где пластификатор представляет собой натриевую соль полиэфирполикарбоксилата.
28. Композиция по п.25, где пластификатор присутствует в количестве от примерно 0,2% до примерно 0,8% от массы готовой к употреблению композиции.
29. Комплект, состоящий из отдельно упакованных компонентов, включающих:
a) композицию по п.1 и
b) компонент активатора.
30. Комплект по п.29, где компонент активатора включает одно или несколько соединений из нижеследующего: сульфата цинка, сульфата алюминия, гидросульфата натрия, серной кислоты, хлористоводородной кислоты, гидросульфата калия, алюмокалиевых квасцов, или их комбинаций.
31. Комплект по п.29, где любой из компонентов (a) и (b) или оба компонента включают хелатообразующее вещество.
32. Комплект по п.31, где компонент активатора включает сульфат цинка и/или дигидрат сульфата кальция.
33. Комплект по п.29, дополнительно включающий (c) загуститель.
34. Комплект, состоящий из отдельно упакованных компонентов, включающих:
a) композицию, включающую (i) полугидрат сульфата кальция и (ii) ингибитор схватывания, выбранный из группы, состоящей из полиакриловой кислоты, соли полиакриловой кислоты и их комбинаций; и
b) компонент активатора;
где любой из компонентов (a) и (b) или оба компонента дополнительно включают хелатообразующее вещество.
35. Комплект по п.34, где хелатообразующее вещество выбрано из группы, состоящей из 2-амино-2-метил-1-пропанола, гидроксида аммония, триэтаноламина и их комбинаций.
36. Комплект по п.34, дополнительно включающий (c) загуститель.
37. Композиция, включающая:
a) воду,
b) обожженный гипс,
c) ингибитор схватывания, выбранный из группы, состоящей из полиакриловой кислоты, соли полиакриловой кислоты и их комбинаций; и, необязательно, один или несколько из нижеследующих ингредиентов:
d) пластификатор,
e) хелатообразующее вещество,
f) модификатор рН,
g) противопенную добавку,
h) армирующий полимер,
i) пенообразующее вещество,
j) вещество, предохраняющее от замерзания,
k) суспендирующую добавку,
l) бактерицид,
m) фунгицид или
n) загуститель;
где массовое отношение воды к обожженному гипсу в композиции составляет от примерно 0,15 до примерно 0,5 и где композиция имеет вязкость от примерно 5000 сП до примерно 48000 сП, и указанная композиция образует связную матрицу отвержденного гипса при смешивании с активатором для взаимодействия полугидрата сульфата кальция с водой с получением отвержденного гипса.
38. Комплект, состоящий из отдельно упакованных компонентов, включающих:
a) композицию по п.37 и
b) компонент активатора, который при смешивании с композицией позволяет композиции схватываться.
39. Композиция, включающая
a) обожженный гипс;
b) полиакриловую кислоту и/или ее соль; и
с) хелатообразующее вещество, причем указанная композиция образует связную матрицу отвержденного гипса при смешивании с водой и активатором взаимодействия полугидрата сульфата кальция с водой с получением отвержденного гипса.
40. Композиция по п.39, дополнительно включающая воду.
41. Композиция по п.39, где хелатообразующее вещество выбрано из группы, состоящей из 2-амино-2-метил-1-пропанола, гидроксида аммония, триэтаноламина и их комбинаций.
42. Композиция по п.39, дополнительно включающая органическое полифосфоновое соединение или смесь органических полифосфоновых соединений.