PL3084014T3 - Stal o wysokiej wytrzymałości i sposób wytwarzania - Google Patents

Stal o wysokiej wytrzymałości i sposób wytwarzania

Info

Publication number
PL3084014T3
PL3084014T3 PL14821855T PL14821855T PL3084014T3 PL 3084014 T3 PL3084014 T3 PL 3084014T3 PL 14821855 T PL14821855 T PL 14821855T PL 14821855 T PL14821855 T PL 14821855T PL 3084014 T3 PL3084014 T3 PL 3084014T3
Authority
PL
Poland
Prior art keywords
manufacture
strength steel
steel
strength
Prior art date
Application number
PL14821855T
Other languages
English (en)
Inventor
Josée Drillet
Véronique Hebert
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of PL3084014T3 publication Critical patent/PL3084014T3/pl

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment 
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0421—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the working steps
    • C21D8/0436—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0447—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0447—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the heat treatment
    • C21D8/0473—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
    • C23C14/06—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material characterised by the coating material
    • C23C14/14—Metallic material, boron or silicon
    • C23C14/16—Metallic material, boron or silicon on metallic substrates or on substrates of boron or silicon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Steel (AREA)
  • Coating With Molten Metal (AREA)
PL14821855T 2013-12-11 2014-12-05 Stal o wysokiej wytrzymałości i sposób wytwarzania PL3084014T3 (pl)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
PCT/US2013/074482 WO2015088523A1 (en) 2013-12-11 2013-12-11 Cold rolled and annealed steel sheet
PCT/IB2014/066647 WO2015087224A1 (fr) 2013-12-11 2014-12-05 Acier à haute résistance et procédé de fabrication
EP14821855.5A EP3084014B1 (fr) 2013-12-11 2014-12-05 Acier à haute résistance et procédé de fabrication

Publications (1)

Publication Number Publication Date
PL3084014T3 true PL3084014T3 (pl) 2019-10-31

Family

ID=52278684

Family Applications (1)

Application Number Title Priority Date Filing Date
PL14821855T PL3084014T3 (pl) 2013-12-11 2014-12-05 Stal o wysokiej wytrzymałości i sposób wytwarzania

Country Status (16)

Country Link
US (1) US10597745B2 (pl)
EP (1) EP3084014B1 (pl)
JP (1) JP6599868B2 (pl)
KR (1) KR102264641B1 (pl)
CN (1) CN105874086B (pl)
BR (1) BR112016013130B1 (pl)
CA (1) CA2933542C (pl)
ES (1) ES2741304T3 (pl)
HU (1) HUE044562T2 (pl)
MA (1) MA39075B1 (pl)
MX (1) MX388381B (pl)
PL (1) PL3084014T3 (pl)
RU (1) RU2669487C2 (pl)
UA (1) UA118036C2 (pl)
WO (2) WO2015088523A1 (pl)
ZA (1) ZA201603640B (pl)

Families Citing this family (45)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102464733B1 (ko) 2014-07-03 2022-11-08 아르셀러미탈 초고강도의 코팅된 또는 비코팅된 강 시트를 제조하기 위한 방법 및 얻어진 시트
WO2016198906A1 (fr) 2015-06-10 2016-12-15 Arcelormittal Acier a haute résistance et procédé de fabrication
KR101736619B1 (ko) 2015-12-15 2017-05-17 주식회사 포스코 화성처리성 및 굽힘가공성이 우수한 초고강도 강판 및 이의 제조방법
WO2017109541A1 (en) 2015-12-21 2017-06-29 Arcelormittal Method for producing a high strength coated steel sheet having improved ductility and formability, and obtained coated steel sheet
WO2017109542A1 (en) * 2015-12-21 2017-06-29 Arcelormittal Method for producing a high strength steel sheet having improved ductility and formability, and obtained steel sheet
US11035020B2 (en) * 2015-12-29 2021-06-15 Arcelormittal Galvannealed steel sheet
JP6264507B2 (ja) * 2016-02-10 2018-01-24 Ｊｆｅスチール株式会社 高強度亜鉛めっき鋼板及びその製造方法
KR101822292B1 (ko) 2016-08-17 2018-01-26 현대자동차주식회사 고강도 특수강
KR101822295B1 (ko) 2016-09-09 2018-01-26 현대자동차주식회사 고강도 특수강
WO2018055425A1 (en) * 2016-09-22 2018-03-29 Arcelormittal High strength and high formability steel sheet and manufacturing method
KR101858852B1 (ko) * 2016-12-16 2018-06-28 주식회사 포스코 항복강도, 연성 및 구멍확장성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법
KR101889181B1 (ko) * 2016-12-19 2018-08-16 주식회사 포스코 굽힘성 및 신장플랜지성이 우수한 고장력강 및 이의 제조방법
KR102209592B1 (ko) * 2016-12-23 2021-01-29 주식회사 포스코 굽힘가공성이 우수한 초고강도 열연강판 및 그 제조방법
US11027522B2 (en) * 2017-01-17 2021-06-08 Nippon Steel Corporation Steel sheet for hot stamping
JP6428968B1 (ja) * 2017-02-20 2018-11-28 新日鐵住金株式会社 鋼板
DE102017112164A1 (de) * 2017-06-01 2018-12-06 Benteler Automobiltechnik Gmbh Blechumformbauteil sowie Verfahren zur Herstellung des Blechumformbauteils
WO2018220430A1 (en) 2017-06-02 2018-12-06 Arcelormittal Steel sheet for manufacturing press hardened parts, press hardened part having a combination of high strength and crash ductility, and manufacturing methods thereof
BR112020006128A2 (pt) * 2017-10-24 2020-09-24 Arcelormittal método para a fabricação de uma chapa de aço revestida, chapa de aço, junta soldada e uso de uma chapa de aço revestida
KR102206929B1 (ko) * 2017-10-24 2021-01-25 아르셀러미탈 코팅된 강 시트의 제조 방법
WO2019111028A1 (en) 2017-12-05 2019-06-13 Arcelormittal Cold rolled and annealed steal sheet and method of manufacturing the same
KR102095509B1 (ko) * 2017-12-22 2020-03-31 주식회사 포스코 고강도 열연 도금강판 및 그의 제조방법
US20210189517A1 (en) * 2018-05-22 2021-06-24 Thyssenkrupp Steel Europe Ag Sheet Metal Part Formed from a Steel Having a High Tensile Strength and Method for Manufacturing Said Sheet Metal Part
CN112313349B (zh) * 2018-06-12 2023-04-14 蒂森克虏伯钢铁欧洲股份公司 扁钢产品及其生产方法
CN109576579A (zh) 2018-11-29 2019-04-05 宝山钢铁股份有限公司 一种具有高扩孔率和较高延伸率的980MPa级冷轧钢板及其制造方法
WO2020128571A1 (en) 2018-12-18 2020-06-25 Arcelormittal A press hardened part with high resistance to delayed fracture and a manufacturing process thereof
KR102153197B1 (ko) 2018-12-18 2020-09-08 주식회사 포스코 가공성이 우수한 냉연강판, 용융아연도금강판 및 이들의 제조방법
WO2020229877A1 (en) * 2019-05-15 2020-11-19 Arcelormittal A cold rolled martensitic steel and a method for it's manufacture
WO2020250009A1 (en) * 2019-06-12 2020-12-17 Arcelormittal A cold rolled martensitic steel and a method of martensitic steel thereof
KR102290782B1 (ko) * 2019-09-26 2021-08-18 주식회사 포스코 내구성이 우수한 고강도 코팅강판의 제조방법
WO2021116741A1 (en) 2019-12-13 2021-06-17 Arcelormittal Heat treated cold rolled steel sheet and a method of manufacturing thereof
MX2022007458A (es) * 2019-12-18 2022-06-24 Arcelormittal Hoja de acero laminada en frio y recocida y metodo de fabricacion.
CN113025877A (zh) * 2019-12-24 2021-06-25 通用汽车环球科技运作有限责任公司 高性能压制硬化钢
KR102858952B1 (ko) 2020-06-30 2025-09-12 제이에프이 스틸 가부시키가이샤 강판, 부재 및 그들의 제조 방법
WO2022018481A1 (en) * 2020-07-20 2022-01-27 Arcelormittal Heat treated cold rolled steel sheet and a method of manufacturing thereof
KR102485004B1 (ko) * 2020-12-17 2023-01-04 주식회사 포스코 가공성이 우수한 고강도 강판 및 그 제조방법
CN113528947B (zh) * 2021-06-21 2022-03-25 武汉钢铁有限公司 一种用CSP生产抗拉强度为1500MPa级高塑韧性汽车结构件用钢及生产方法
CN113699337B (zh) * 2021-08-06 2023-05-05 山西太钢不锈钢股份有限公司 一种9Cr系耐热钢连铸大圆坯热处理工艺
KR20230045648A (ko) * 2021-09-27 2023-04-05 주식회사 포스코 구멍확장성 및 연성이 우수한 고강도 후물 강판 및 이의 제조방법
KR20230069426A (ko) * 2021-11-12 2023-05-19 주식회사 포스코 굽힘성 및 신장 플랜지성이 우수한 초고강도 강판 및 이의 제조 방법
KR20230077777A (ko) * 2021-11-25 2023-06-02 주식회사 포스코 성형성이 우수한 초고강도 열연 강판 및 이의 제조 방법
WO2023218731A1 (ja) * 2022-05-11 2023-11-16 Ｊｆｅスチール株式会社 鋼板、部材およびそれらの製造方法
WO2023218576A1 (ja) * 2022-05-11 2023-11-16 Ｊｆｅスチール株式会社 亜鉛めっき鋼板、部材およびそれらの製造方法
JP7635896B1 (ja) * 2023-03-31 2025-02-26 Ｊｆｅスチール株式会社 鋼板、部材およびそれらの製造方法
WO2024203410A1 (ja) * 2023-03-31 2024-10-03 Ｊｆｅスチール株式会社 鋼板、部材およびそれらの製造方法
CN116949366B (zh) 2023-08-01 2024-03-19 北京理工大学 无碳化物的回火马氏体钢及其制备方法

Family Cites Families (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1087357C (zh) 1997-07-28 2002-07-10 埃克森美孚上游研究公司 具有良好韧性的超高强度、可焊接、基本无硼的钢
TW454040B (en) * 1997-12-19 2001-09-11 Exxon Production Research Co Ultra-high strength ausaged steels with excellent cryogenic temperature toughness
JP2002180182A (ja) * 2000-12-08 2002-06-26 Kawasaki Steel Corp 耐孔あき性に優れる鋼材
JP4109619B2 (ja) * 2003-12-16 2008-07-02 株式会社神戸製鋼所 伸び、及び伸びフランジ性に優れた高強度鋼板
DE102005008410B3 (de) * 2005-02-24 2006-02-16 Thyssenkrupp Stahl Ag Verfahren zum Beschichten von Stahlbändern und beschichtetes Stahlband
JP4772496B2 (ja) * 2005-12-27 2011-09-14 新日本製鐵株式会社 穴拡げ性に優れた高強度冷延薄鋼板及びその製造方法
EP1832667A1 (fr) * 2006-03-07 2007-09-12 ARCELOR France Procédé de fabrication de tôles d'acier à très hautes caractéristiques de résistance, de ductilité et de tenacité, et tôles ainsi produites
JP4959471B2 (ja) * 2007-08-28 2012-06-20 新日本製鐵株式会社 靭性に優れた機械構造用高強度シームレス鋼管及びその製造方法
JP5365217B2 (ja) 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5365216B2 (ja) * 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
US20110168000A1 (en) 2008-03-03 2011-07-14 Langner F Richard Ballistic wall panel device and system and method therefor
JP5251208B2 (ja) 2008-03-28 2013-07-31 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
EP2123786A1 (fr) * 2008-05-21 2009-11-25 ArcelorMittal France Procédé de fabrication de tôles d'aciers dual phase laminées à froid à trés haute résistance et tôles ainsi produites
JP5418168B2 (ja) * 2008-11-28 2014-02-19 Ｊｆｅスチール株式会社 成形性に優れた高強度冷延鋼板、高強度溶融亜鉛めっき鋼板およびそれらの製造方法
EP2199425A1 (fr) 2008-12-18 2010-06-23 ArcelorMittal France Générateur de vapeur industriel pour le dépôt d'un revêtement d'alliage sur une bande métallique (II)
US20130000798A1 (en) 2008-12-26 2013-01-03 Jfe Steel Corporation Steel material excellent in resistance of ductile crack initiation from welded heat affected zone and base material and method for manufacturing the same
JP4924730B2 (ja) * 2009-04-28 2012-04-25 Ｊｆｅスチール株式会社 加工性、溶接性および疲労特性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
JP5412182B2 (ja) 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
JP5703608B2 (ja) * 2009-07-30 2015-04-22 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5466552B2 (ja) * 2010-03-24 2014-04-09 株式会社神戸製鋼所 伸び、伸びフランジ性および溶接性を兼備した高強度冷延鋼板
JP5136609B2 (ja) 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
WO2012052626A1 (fr) * 2010-10-21 2012-04-26 Arcelormittal Investigacion Y Desarrollo, S.L. Tole d'acier laminee a chaud ou a froid, don procede de fabrication et son utilisation dans l'industrie automobile
KR101220619B1 (ko) * 2010-11-09 2013-01-10 주식회사 포스코 초고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법
US9745639B2 (en) 2011-06-13 2017-08-29 Kobe Steel, Ltd. High-strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof
WO2013047821A1 (ja) 2011-09-30 2013-04-04 新日鐵住金株式会社 焼付硬化性に優れた高強度溶融亜鉛めっき鋼板、高強度合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
BR112014017020B1 (pt) * 2012-01-13 2020-04-14 Nippon Steel & Sumitomo Metal Corp chapa de aço laminada a frio e método para produzir chapa de aço laminada a frio
JP6047037B2 (ja) * 2012-03-29 2016-12-21 株式会社神戸製鋼所 鋼板形状に優れた高強度冷延鋼板の製造方法
EP2831296B2 (en) 2012-03-30 2020-04-15 Voestalpine Stahl GmbH High strength cold rolled steel sheet and method of producing such steel sheet

Also Published As

Publication number Publication date
RU2669487C2 (ru) 2018-10-11
UA118036C2 (uk) 2018-11-12
WO2015088523A1 (en) 2015-06-18
BR112016013130A2 (pt) 2017-08-08
RU2016123172A3 (pl) 2018-08-21
MA39075B1 (fr) 2017-11-30
WO2015087224A1 (fr) 2015-06-18
KR102264641B1 (ko) 2021-06-14
ES2741304T3 (es) 2020-02-10
EP3084014B1 (fr) 2019-05-08
MX2016007664A (es) 2016-09-13
US10597745B2 (en) 2020-03-24
HUE044562T2 (hu) 2019-11-28
CA2933542C (fr) 2023-02-14
MX388381B (es) 2025-03-19
JP6599868B2 (ja) 2019-10-30
JP2017507241A (ja) 2017-03-16
RU2016123172A (ru) 2017-12-14
MA39075A1 (fr) 2017-01-31
EP3084014A1 (fr) 2016-10-26
CA2933542A1 (fr) 2015-06-18
US20160312326A1 (en) 2016-10-27
CN105874086A (zh) 2016-08-17
BR112016013130B1 (pt) 2021-03-09
KR20160096611A (ko) 2016-08-16
CN105874086B (zh) 2018-07-03
ZA201603640B (en) 2017-11-29

Similar Documents

Publication Publication Date Title
PL3084014T3 (pl) Stal o wysokiej wytrzymałości i sposób wytwarzania
IL295860B1 (en) Methods and processes for non-invasive assessment of genetic variations
IL283586A (en) Methods and processes for non-invasive assessment of genetic variations
HUE046359T2 (hu) Martenzites acél töréssel szembeni késleltetett ellenállással, valamint gyártási eljárás
DK3087095T3 (da) FcRn-antagonist og fremgangsmåder til anvendelse
PL3427584T3 (pl) Sposób zwalczania rdzy
DK3009021T3 (da) Handske og fremgangsmåde til fremstilling deraf
DK3049056T3 (da) Topisk antisvampesammensætning og fremgangsmåder til behandling
HRP20170840T1 (hr) Supstituirani ksantini i metode njihove uporabe
PL2970123T3 (pl) Sól omekamtywu mekarbilu i sposób otrzymywania soli
DK3082902T3 (da) Kropsbåret injektor og anvendelsesmetode
PL3140430T3 (pl) Sposób wytwarzania taśmy stalowej elektrotechnicznej o ziarnie niezorientowanym z wysokim stopniem redukcji na zimno
LT3007726T (lt) Tautopatijos gydymo būdai
DK3074544T3 (da) Martensitholdigt rustfrit stål, stykke udført i dette stål og fremgangsmåde til fremstilling heraf
IL243728A0 (en) Heterobicycloaryl rorc2 inhibitors and methods of use thereof
GB201307434D0 (en) Gate Assembly and Method of Use Thereof
DK3022361T4 (da) Rambuk og fremgangsmåde til anvendelse deraf
PL3006586T3 (pl) Materiał stalowy poddany obróbce cieplnej i sposób jego wytwarzania
LT3369724T (lt) Iopamidolio gamybos būdas
IL240695A0 (en) Nme inhibitors and methods of using nme inhibitors
PL3043874T3 (pl) Sposób strącania odpadów metalowych
EP2859965A4 (en) Deep draw moulding method and moulding metal die therefor
ZA201600927B (en) Structural assembly and method of assembly thereof
ITUB20156002A1 (it) Composizione e metodo per trattare i nematodi
HUE051592T2 (hu) Kezelési módszer