MX378996B - Lamina de acero galvanizada endurecida al horno. - Google Patents

Lamina de acero galvanizada endurecida al horno.

Info

Publication number
MX378996B
MX378996B MX2016006878A MX2016006878A MX378996B MX 378996 B MX378996 B MX 378996B MX 2016006878 A MX2016006878 A MX 2016006878A MX 2016006878 A MX2016006878 A MX 2016006878A MX 378996 B MX378996 B MX 378996B
Authority
MX
Mexico
Prior art keywords
steel sheet
adjusted
base steel
bake
ferrite
Prior art date
Application number
MX2016006878A
Other languages
English (en)
Other versions
MX2016006878A (es
Inventor
Kohei Hasegawa
Koichiro Fujita
Kozo Harada
Yusuke Kimata
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2016006878A publication Critical patent/MX2016006878A/es
Publication of MX378996B publication Critical patent/MX378996B/es

Abstract

Se proporciona una lámina de acero galvanizada endurecida al horno que se puede utilizar preferiblemente para, por ejemplo, paneles exteriores de automóviles, que tiene una endurecibilidad al horno y una resistencia a la corrosión, que tiene buena capacidad de estampación, y con la cual un defecto de ampollas no se produce cuando se lleva a cabo un tratamiento de galvanización, a pesar de ser fabricada a bajo costo mediante el uso de acero de bajo contenido en carbono que se puede fabricar relativamente de forma fácil. La lámina de acero es una lámina de acero galvanizada endurecida al horno que tiene una lámina de acero base y una capa de recubrimiento formada sobre la lámina de acero base, la lámina de acero base tiene una composición química determinada y una estructura metalográfica que incluye una fase de ferrita y una fase de cementita, en la cual un diámetro de grano promedio de ferrita se controla para que sea de 10 µm o más y 30 µm o menos, y en la cual el área de superficie de la interfaz entre ferrita y cementita por unidad de volumen se controla para que sea de 1.0/mm o más y 10.0/mm o menos, una concentración de hidrógeno en acero de la lámina de acero base se controla para que sea de menos de 0.1 ppm, y un peso de recubrimiento de zinc por unidad de área de superficie de la lámina de acero se controla para que sea de 40 g/m2 o más y 100 g/m2 o menos.
MX2016006878A 2013-11-28 2014-11-27 Lamina de acero galvanizada endurecida al horno. MX378996B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013246237A JP6052145B2 (ja) 2013-11-28 2013-11-28 焼付け硬化型溶融亜鉛めっき鋼板
PCT/JP2014/005944 WO2015079699A1 (ja) 2013-11-28 2014-11-27 焼付け硬化型溶融亜鉛めっき鋼板

Publications (2)

Publication Number Publication Date
MX2016006878A MX2016006878A (es) 2016-08-17
MX378996B true MX378996B (es) 2025-03-10

Family

ID=53198661

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2016006878A MX378996B (es) 2013-11-28 2014-11-27 Lamina de acero galvanizada endurecida al horno.

Country Status (7)

Country Link
US (1) US9920394B2 (es)
EP (1) EP3075873B1 (es)
JP (1) JP6052145B2 (es)
KR (1) KR101825857B1 (es)
CN (1) CN105793457B (es)
MX (1) MX378996B (es)
WO (1) WO2015079699A1 (es)

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105970094B (zh) * 2016-06-14 2018-03-20 武汉钢铁有限公司 一种汽车外板用电镀锌烘烤硬化钢板的生产方法
JP6271067B1 (ja) * 2017-06-01 2018-01-31 日新製鋼株式会社 高強度Ｚｎ−Ａｌ−Ｍｇ系表面被覆鋼板およびその製造方法
JP6838665B2 (ja) * 2018-01-17 2021-03-03 Ｊｆｅスチール株式会社 高強度合金化電気亜鉛めっき鋼板およびその製造方法
KR102469709B1 (ko) 2018-03-30 2022-11-22 제이에프이 스틸 가부시키가이샤 고강도 아연 도금 강판, 고강도 부재 및 그들의 제조 방법
KR102179214B1 (ko) * 2018-11-30 2020-11-16 주식회사 포스코 법랑용 냉연 강판 및 그 제조방법
JP7315522B2 (ja) * 2020-11-11 2023-07-26 Ｊｆｅ鋼板株式会社 材質安定性に優れた溶融亜鉛系めっき鋼板の製造方法
KR102241684B1 (ko) * 2020-12-10 2021-04-16 하민호 단일 유니트 쿨러와 예비용 냉동장치가 구비된 냉동시스템
KR102279043B1 (ko) * 2020-12-11 2021-07-22 주식회사 다우일렉트론 냉각 시스템
CN114411057B (zh) * 2021-12-30 2022-12-16 钢铁研究总院 一种可烧结摩擦层的高强心板用钢

Family Cites Families (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5920733B2 (ja) 1980-02-28 1984-05-15 日本鋼管株式会社 高強度冷延鋼板の製造方法
JPS5819442A (ja) 1981-07-27 1983-02-04 Nippon Kokan Kk <Nkk> 連続焼鈍による加工用高強度冷延鋼板の製造方法
JPS5831035A (ja) 1981-08-20 1983-02-23 Nippon Kokan Kk <Nkk> 加工性が優れかつ焼付硬化性を有する溶融亜鉛メツキ鋼板の製造方法
JPH02125817A (ja) 1988-12-28 1990-05-14 Nkk Corp ＴＳレベルが３５〜４５ｋｇ／ｍｍ↑２の高強度冷延鋼板の連続焼鈍による製造方法
JP2510367B2 (ja) 1991-09-02 1996-06-26 株式会社神戸製鋼所 焼付硬化性および加工性に優れた非時効性冷間圧延鋼板の製造方法
JPH0673498A (ja) 1992-08-27 1994-03-15 Kobe Steel Ltd 低温での塗装焼付硬化性に優れた冷延鋼板及びその製造方法
JP3374694B2 (ja) * 1997-02-05 2003-02-10 日本鋼管株式会社 耐めっきふくれ性に優れた直送圧延熱延鋼板の製造方法
JP3374693B2 (ja) * 1997-02-05 2003-02-10 日本鋼管株式会社 耐めっきふくれ性に優れた直送圧延熱延鋼板の製造方法
JP4003392B2 (ja) 2000-11-27 2007-11-07 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板およびその製造方法
JP5478804B2 (ja) * 2006-12-28 2014-04-23 新日鐵住金株式会社 表面外観及びめっき密着性に優れた合金化溶融亜鉛めっき鋼板
JP5151227B2 (ja) * 2007-04-17 2013-02-27 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5552864B2 (ja) 2009-03-31 2014-07-16 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
KR101250101B1 (ko) 2010-03-10 2013-04-03 제이에프이 스틸 가부시키가이샤 강의 연속 주조 방법 및 강판의 제조 방법
JP5549414B2 (ja) 2010-06-23 2014-07-16 Ｊｆｅスチール株式会社 形状凍結性に優れた冷延薄鋼板およびその製造方法
JP5527051B2 (ja) * 2010-06-30 2014-06-18 新日鐵住金株式会社 バーリング性に優れた焼付け硬化型熱延鋼板及びその製造方法
BR112013026849B1 (pt) 2011-04-21 2019-03-19 Nippon Steel & Sumitomo Metal Corporation Chapa de aço laminada a frio de alta resistência tendo excelentes alongamento uniforme e capacidade de expansão de furo e método para produção da mesma
JP5338873B2 (ja) 2011-08-05 2013-11-13 Ｊｆｅスチール株式会社 引張強度４４０ＭＰａ以上の加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法

Also Published As

Publication number Publication date
CN105793457A (zh) 2016-07-20
JP6052145B2 (ja) 2016-12-27
WO2015079699A1 (ja) 2015-06-04
KR101825857B1 (ko) 2018-02-05
US9920394B2 (en) 2018-03-20
MX2016006878A (es) 2016-08-17
CN105793457B (zh) 2018-04-03
EP3075873A1 (en) 2016-10-05
US20160298207A1 (en) 2016-10-13
EP3075873B1 (en) 2018-05-02
KR20160075716A (ko) 2016-06-29
JP2015105385A (ja) 2015-06-08
EP3075873A4 (en) 2017-01-18

Similar Documents

Publication Publication Date Title
MX378996B (es) Lamina de acero galvanizada endurecida al horno.
MY172243A (en) Hot-dip zinc alloy coated steel sheet excellent in coating adhesion, and method for producing the same
MX377777B (es) Lamina de acero galvanizada por inmersion en caliente para estampado en caliente y metodo para fabricar piezas de acero.
MX385547B (es) Componente de vehículo y método de fabricación de componente de vehículo.
IN2014DN07662A (es)
WO2015099455A8 (ko) 액체금속취화에 의한 크랙 저항성이 우수한 용융아연도금강판
MX362505B (es) Lamina de acero galvanizada por inmersion en caliente aleada y metodo para manufacturar la misma.
MX381190B (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MY167799A (en) Coated sheet materials having high solar reflective index and corrosion resistance, and methods of making same
MY155139A (en) Hot-dip zn-al-mg-si-cr alloy-coated steel material with excellent corrosion resistance
MX2012005996A (es) Acero elaborado por inmersion en caliente y metodo para producirlo.
MY160065A (en) High-strength galvanized steel sheet nad method of manufacturing the same
WO2009084848A3 (en) Zinc alloy coated steel sheet having good sealer adhesion and corrosion resistance and process of manufacturing the same
MX2015001224A (es) Lamina de acero galvanizada por inmersion en caliente y metodo de fabricacion de la misma.
MY182935A (en) Steel sheet for containers, and method for producing steel sheet for containers
IN2015MN02571A (es)
IN2015DN02531A (es)
MY174906A (en) Al-based alloy plated steel material having excellent post-coating corrosion resistance
MX387715B (es) Lámina de acero galvano-recocida y método para la producción de la misma.
MX2017004853A (es) Lamina de acero galvanizada de alta resistencia.
MY152832A (en) Tin-plated steel sheet and method for manufacturing the same
MX341700B (es) Lamina de acero galvanizada por inmersion en caliente aleado que tiene capacidades de conformacion excelentes y resistencia al desprendimiento de la post adhesion y metodo de fabricacion de la misma.
MY160923A (en) Steel sheet for container excellent in corrosion resistance
MX2017011743A (es) Lamina de acero galvanizada por inmersion en caliente.
MX2016001657A (es) Lamina de acero recubierta con ai que tiene excelentes caracteristicas de reflexion total y resistencia a la corrosion, y metodo para fabricar la misma.