MX2022016358A - Chapa de acero, miembro y metodo para producirlos. - Google Patents

Chapa de acero, miembro y metodo para producirlos.

Info

Publication number
MX2022016358A
MX2022016358A MX2022016358A MX2022016358A MX2022016358A MX 2022016358 A MX2022016358 A MX 2022016358A MX 2022016358 A MX2022016358 A MX 2022016358A MX 2022016358 A MX2022016358 A MX 2022016358A MX 2022016358 A MX2022016358 A MX 2022016358A
Authority
MX
Mexico
Prior art keywords
steel sheet
producing
tempered martensite
bainite
ferrite
Prior art date
Application number
MX2022016358A
Other languages
English (en)
Inventor
Tatsuya Nakagaito
Kentaro Sato
Shinsuke Komine
Tomohiro SAKAIDANI
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2022016358A publication Critical patent/MX2022016358A/es

Abstract

Se proporciona una chapa o miembro de acero con una tensión de rotura (TS) de 590 MPa o más y con buenas características de colisión y un método para producir la chapa o miembro de acero. Una chapa de acero de acuerdo a la presente invención tiene una composición química que satisface un contenido equivalente de carbono Ceq de 0.35% o más y menos de 0.60% y una microestructura de acero con una fracción de área de ferrita: de 40% a 85%, martensita templada y bainita: de 10% a 55% en total, austenita retenida: de 3% a 15%, y ferrita, martensita templada, bainita, y austenita retenida: 93% o más en total, donde la flexión de 90-grados es a una relación del radio de curvatura/espesor de 4.2 en la dirección de laminación (L) con respecto a un eje que se extiende en una dirección a lo ancho (C) produce un cambio de 0.50 o más en (un tamaño de grano en una dirección del espesor)/(un tamaño de grano en una dirección perpendicular al espesor) de la martensita templada en una sección transversal L en una región de 0- a 50-µm de una superficie de la chapa de acero sobre un lado de compresión, y la chapa de acero tiene una tensión de rotura de 590 MPa o más.
MX2022016358A 2020-06-30 2021-06-30 Chapa de acero, miembro y metodo para producirlos. MX2022016358A (es)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2020113060 2020-06-30
JP2021076975 2021-04-30
PCT/JP2021/024843 WO2022004817A1 (ja) 2020-06-30 2021-06-30 鋼板、部材及びそれらの製造方法

Publications (1)

Publication Number Publication Date
MX2022016358A true MX2022016358A (es) 2023-01-30

Family

ID=79316309

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2022016358A MX2022016358A (es) 2020-06-30 2021-06-30 Chapa de acero, miembro y metodo para producirlos.

Country Status (7)

Country Link
US (1) US20240229201A1 (es)
EP (1) EP4137593A4 (es)
JP (2) JP7031800B1 (es)
KR (1) KR20230012026A (es)
CN (1) CN115698362B (es)
MX (1) MX2022016358A (es)
WO (1) WO2022004817A1 (es)

Family Cites Families (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3406094B2 (ja) * 1994-11-10 2003-05-12 株式会社神戸製鋼所 耐水素脆化特性にすぐれる超高強度薄鋼板の製造方法
JP3619357B2 (ja) * 1997-12-26 2005-02-09 新日本製鐵株式会社 高い動的変形抵抗を有する高強度鋼板とその製造方法
JP2006089804A (ja) * 2004-09-24 2006-04-06 Nisshin Steel Co Ltd 縮管性に優れたインパネリインフォースメント用高強度電縫鋼管の製造方法
JP5190824B2 (ja) * 2007-12-05 2013-04-24 国立大学法人大阪大学 車両用強度部材
JP5323563B2 (ja) * 2009-03-31 2013-10-23 株式会社神戸製鋼所 加工性および形状凍結性に優れた高強度冷延鋼板
JP5493986B2 (ja) * 2009-04-27 2014-05-14 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板および高強度溶融亜鉛めっき鋼板並びにそれらの製造方法
KR101115739B1 (ko) * 2009-09-09 2012-03-06 주식회사 포스코 점용접성, 강도 및 연신율이 우수한 자동차용 강판 및 그 제조방법
JP5136609B2 (ja) 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP6402460B2 (ja) 2014-03-18 2018-10-10 新日鐵住金株式会社 引張最大強度７８０ＭＰａ以上を有する衝突特性に優れた高強度鋼板、高強度溶融亜鉛めっき鋼板、及び高強度合金化溶融亜鉛めっき鋼板
JP6749818B2 (ja) * 2016-02-29 2020-09-02 株式会社神戸製鋼所 高強度鋼板およびその製造方法
JP2019052341A (ja) * 2017-09-14 2019-04-04 Ｊｆｅスチール株式会社 曲げ加工性に優れた非調質低降伏比高張力厚鋼板およびその製造方法
MX2020008623A (es) * 2018-02-19 2020-09-21 Jfe Steel Corp Lamina de acero de alta resistencia y metodo de produccion para la misma.
EP3786310A4 (en) * 2018-04-23 2022-01-19 Nippon Steel Corporation STEEL ELEMENT AND ITS PRODUCTION METHOD
JP7218533B2 (ja) * 2018-10-09 2023-02-07 日本製鉄株式会社 鋼材およびその製造方法
US11643701B2 (en) * 2019-01-29 2023-05-09 Jfe Steel Corporation High-strength hot-dip galvanized steel sheet and manufacturing method therefor

Also Published As

Publication number Publication date
CN115698362A (zh) 2023-02-03
EP4137593A1 (en) 2023-02-22
JPWO2022004817A1 (es) 2022-01-06
CN115698362B (zh) 2024-05-14
JP2022034013A (ja) 2022-03-02
WO2022004817A1 (ja) 2022-01-06
KR20230012026A (ko) 2023-01-25
US20240229201A1 (en) 2024-07-11
JP7031800B1 (ja) 2022-03-08
EP4137593A4 (en) 2023-09-06

Similar Documents

Publication Publication Date Title
MX2018009643A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2018010467A (es) Hoja de acero de alta resistencia y metodo para fabricar la misma.
EP2728029A1 (en) High strength hot-rolled steel sheet for welded steel line pipe having excellent souring resistance, and method for producing same
MX2019004457A (es) Lamina de acero.
JPWO2011142285A1 (ja) 高強度鋼板とその製造方法
MX2021009947A (es) Lamina de acero galvanizado por inmersion en caliente de alta resistencia y metodo para producir la misma.
MX2022003433A (es) Lamina de acero laminada en caliente.
MX2021008505A (es) Lamina de acero de alta resistencia.
MX2021009063A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
JP2007332438A (ja) 低サイクル疲労特性に優れた浸炭焼入れ鋼材及び浸炭焼入れ部品
MX2021004419A (es) Lamina de acero electrogalvanizada de alta resistencia y alto limite de alargamiento y metodo para la fabricacion de la misma.
JP5505263B2 (ja) 低サイクル疲労特性に優れた浸炭焼入れ鋼材及び浸炭焼入れ部品
US20180371591A1 (en) Austenitic stainless steel pipe exhibiting excellent wrinkle resistance
MX2020006703A (es) Placa de acero laminada en caliente y metodo para fabricar la misma.
MX2022004100A (es) Lamina de acero laminada en frio y metodo para producir la misma.
MX2021013765A (es) Hoja de acero.
MX2021001141A (es) Lamina de acero delgada y metodo para la fabricacion de la misma.
JP5368820B2 (ja) 耐震性に優れた建築構造用７８０ＭＰａ級低降伏比円形鋼管およびその製造方法
MX2022016016A (es) Lamina de acero galvanizado, miembro y metodo para producirlas.
MX2021001962A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX2021010031A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2024003168A (es) Pieza de acero estampada en caliente de alta resistencia y metodo de fabricacion de la misma.
MX2022013660A (es) Hoja de acero, miembro, y metodos para fabricar los mismos.
MX2022016359A (es) Chapa de acero, miembro y metodo para producirlos.
MX2022004669A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.