ME01472B - Hidroizolacione membrane bazirane na bitumenu modifikovanom sa polimerima koji sadrže šuplje staklene mikrosfere - Google Patents

Hidroizolacione membrane bazirane na bitumenu modifikovanom sa polimerima koji sadrže šuplje staklene mikrosfere

Info

Publication number
ME01472B
ME01472B MEP-2013-10A MEP1013A ME01472B ME 01472 B ME01472 B ME 01472B ME P1013 A MEP1013 A ME P1013A ME 01472 B ME01472 B ME 01472B
Authority
ME
Montenegro
Prior art keywords
waterproofing membranes
mineral filler
hollow glass
glass microspheres
bitumen
Prior art date
Application number
MEP-2013-10A
Other languages
English (en)
Inventor
Daniele Pascon
Michele Drigo
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed filed Critical
Publication of ME01472B publication Critical patent/ME01472B/me

Description

Hidroizolacione membrane bazirane na bitumenu modifikovanom sa polimerima koji sadrže šuplje staklene mikrosfere.
 
 
Opis
[0001] Ovaj pronalazak se odnosi na hidroizolacione membrane na bazi bitumena i mineralnog punila koje se sastoji od šupljih staklenih mikrosfera.
 
Stanje tehnike
 
[0002] Formule koje se sastoje od industrijskog bitumena, mineralnog punila, termoplastičnog polimera ili mešavine termoplastičnih polimera su odavno predložene za pripremu hidroizolacionih membrana dizajniranih za primenu u građevinskoj industriji. Mineralno punilo koje je tipično za konvencionalne formule se sastoji od kalcijum-karbonata.
[0003] Na primer, US 2006/0110996 objavljuje hidroizolacione membrane koje su dobijene primenom formule koja se sastoji od bitumena, termoplastičnog polimera, kalcijum-karbonata i titanijum-dioksida na jednoj strani vlaknastog materijala kao što su fiberglas ili netkani poliestar.
[0004] US 4.420.524 opisuje slične hidroizolacione membrane dobijene impregnacijom mnogih ojačanih slojeva, izgrađenih od fiberglasa i poliestarskih struktura, sa bitumenom i termoplastičnim polimerom, a moguće i mineralnim punilom koji se sastoji od različitih supstanci kao što su gašeni kreč, talk, glina, dijatomejska zemlja, cement.
[0005] U ovom konkretnom prijavnom sektoru, osetila se posebno potreba za bituminoznim formulama koje omogućavaju izradu što lakših hidroizolacionih membrana a što neće loše uticati na jačinu i performanse membrane.
[0006] US 2009/061236 otkriva bituminoznu formulu koja se sastoji od etilen/alfa-olefinskog interpolimera koji se brzo rastvara u bitumenu i ima bolju stabilnost na toploti i UV zračenju. Nije se bavilo problemom smanjenja mase hidroizolacionih membrana.
[0007] DE 102006010446 opisuje bituminozna veziva za membrane koja se sastoje od mineralnog punila u procentu od 10 do 45% koje se sastoji od proširenih staklenih sfera sa velicinom sfere između 0,1 i 2,0 mm. Međutim, visok procenat staklenih sfera i njihova pojedinačna veličina izgleda nisu kompatibilne sa zadovoljavajućim performansama membrane po pitanju gustine, mase i hidroizolacionog kapaciteta.
[0008] US 6092557 opisuje cevovod izolovanog bituminoznom formulom koja se sastoji od punila kao što su staklene sfere ili kenosfere, piljevina ili druga vlakna. Hidroizolacione membrane za građevinsku industriju nisu opisane u tome.
[0009] US 4,168,178 otkriva bezazbestne bituminozne formule sa dodatkom ugljenika, uključujući i 10-45% čestičnog punila koje se sastoji od staklenih sfera, perlita, peska ili aluminijum-oksida. Tehnički problem koji je opisan se odnosi na zamenu azbestnih vlakana.
[0010] US 20070187647 otkriva materijale za premazivanje koji se sastoje od bitumena, vode i tiksotropnih aditiva izabranih od šupljih staklenih sfera, tkanina i organskih ili neorganskih derivata silicijuma. Navedeni materijali se koriste za zaštitu affaltnog puta ili građevinskih površina od vlage, korozije i/ili toplote. Hidroizolacione membrane nisu opisane u tome.
[0011] EP 782977 otkriva tečnu hidroizolacionu formulu koja se sastoji od dve komponente: veštačke komponente od lateksa ili gume i uljane komponente koja može da sadrži i do 30% bitumena zajedno sa reološkim agensima kao što su šuplje staklene sfere.
[0012] Nijedan od navedenih dokumenata se ne bavi tehničkim problemom smanjenja mase i poboljšavanja performansi hidroizolacionih membrana za građevinsku industriju.
 
Opis pronalaska
 
[0013] Sada je utvrđeno da se posebno povoljne bituminozne formule mogu dobiti zamenom kalcijum-karbonata ili ekvivalentnih mineralnih punila poznate formule sa materijalom koji se sastoji od staklenih šupljih mikrosfera sa gustinom mnogo manjom od 1g/cm3.
[0014] Sadašnji pronalazak zato obezbeđuje hidroizolacione membrane koje se sastoje od ojačanog materijala impregniranim formulom koju karakteriše specifična težina mnogo manja nego ona od konvencinalnih formula; to omogućava proizvodnju membrana koje su, ako su im debljine jednake, lakše nego one proizvedene po konvencionalnim formulama, bez smanjenja snage ili performansi membrane.
[0015] Smanjenje mase predstavlja veliku prednost u primeni hidroizolacionih membrana na gradilištima, jer se njihova primena još uvek obavlja ručno.
[0016] Formula prema pronalasku takođe omogućava da se dobiju posebno niske specifične težine, omogućavajući na taj način proizvodnju rolni hidroizolacionih membana sa kojom može na licu rukovati jedna osoba i pridržavanje važeće regulative koja se odnosi na “rukovanje teretom”.
[0017] Transport rolni membrana na visini je olakšano, i manje napora je potrebno za postavljanje membrane na površinu koja će biti hidroizolovana.
[0018] Veća fleksibilnost membrana prema pronalasku takođe znači da se bolje adaptira na površinu koja će biti hidroizolovana, koja je retko kad savršeno ravna.
 
DETALJAN OPIS PRONALASKA
 
[0019] Prvi aspekt pronalaska se odnosi na hidroizolacione membrane koje se sastoje od ojačanog materijala impregniranog bituminoznom formulom koja se sastoji od industrijskog bitumena, mineralnog punila, termoplastičnog polimera ili smeše termoplastičnih polimera, koje karakteriše mineralno punilo izgrađeno od staklenih šupljih mikrosfera sa gustinom između 0.1 i 0.14 g/cm3 i sa veličinom manjom od 120 µm.
[0020] Bituminozne hidroizolacione membrane se prema pronalasku odlikuju specifičnom težinom koja je ispod 1g/cm3.
[0021] Sledeći aspekt pronalaska se odnosi na proces izrade hidroizolacionih membrana koji obuhvata impregnaciju ojačanog materijala sa formulom opisanom iznad. Konačno, pronalazak se odnosi i na membrane koje se mogu dobiti po pomenutom postupku, a koje pripadaju različitim klasama definisanim izmerenim vrednostima hladnog savijanja prema standardu EN 1109, u opsegu 0-25°C.
[0022] Termoplastični polimer se po moguđstvu bira između polietilena male gustine, polietilena velike gustine, izotaktičnog polipropilena, etilen/propilen kopolimera, etilen/propilen/buten terpolimera, ataktičnog polipropilena i stiren-butadien-stiren blok kopolimera.
[0023] Industrijski bitumen, posebno bitumen 180/200, je uglavnom prisutan u formulama prema pronalasku u količinama između 70% i 80% po masi, dok termoplastični polimer ili polimeri su prisutni u količinama između 15% i 25%.
[0024] Staklene šuplje mikrosfere sa gustinom između 0,1 i 0,14 g/cm3 i sa veličinom manjom od 120 µm su prisutne u količinama između 2% i 7% po masi, a radije u količinama između 3% i 5%.
[0025] Ojačavajući materijal, impregniran formulama prema pronalasku za pripremanje hidroizolacionih membrana, je radije netkani poliester.
[0026] Staklene šuplje mikrosfere sa gustinom između 0,1 i 0,14 g/cm3 i sa veličinom manjom od 120 µm su dostupne na tržištu u okviru 3M Scotchlite brenda.
[0027] Bituminozne membrane su tradicionalno klasifikovane na bazi parametra o hladnom savijanju, merenom prema standardu EN 1109, koji određuje minimum temperature na kojoj se test uzorak bituminozne membrane može saviti oko posebne osovine bez pucanja.
[0028] Tri najzastupljenije klase na tržištu su Klasa -5°C, Klasa -10°C i Klasa -15°C. Ova klasifikacija nije uključena u određenom standardu, ali je istorijski bila prepoznata od strane tržišta. Tipične konvencionalne formule za svaku klasu su navedeni u nastavku:
 
Klasa -5°C
 
[0029] Sastav formule, prikazan kao maseni procenat:
 
§       Smeša polietilena visoke i niske gustine: 6%;
§       Kalcijum-karbonat: 49%;
§       Industrijski bitumen 180/200:45%.
 
Masa membrane debljine 4mm: 5,7kg/m2.
Masa rolne membrane od 10m2: 57kg.
Mehaničke karakteristike smeše:
 
§       Hladno savijanje(EN1109): -5°C;
§       Prodiranje na 25°C (EN 1426): 18 dmm;
§       Prodiranje na 60 °C (EN 1426): 80 dmm;
§       Tačka omekšavanja (EN1427): 120°C;
§       Viskoznost na 180°C sa Brukfildovim DV-E viskozimetrom, RV07 osovina, 100 obrtaja u minuti (rpm), 13000 ciklusa u sekundi (cps).
 
[0030] Karakteristična svojstva membrane:
 
§       Otpornost na visokim temperaturama (EN 1110): 110°C.
§       Vodonepropustljivost (EN 1928-B): 100 kPa.
 
Klasa -10°C.
 
[0031] Sastav formule, prikazan kao maseni procenat:
 
§       Smeša polietilena visoke i niske gustine: 8%;
§       Kalcijum-karbonat: 38%;
§       Industrijski bitumen 180/200: 54%;
 
Masa membrane debljine 4mm: 5.2 kg/m2;
Masa rolne membrane od 10m2: 52 kg.
Mehaničke karakteristike smeše:
 
§       Hladno savijanje (EN1109): -10°C;
§       Prodiranje na 25°C (EN 1426): 18 dmm;
§       Prodiranje na 60°C (EN 1426): 85 dmm;
§       Tačka omekšavanja (EN1427): 120°C;
§       Viskoznost na 180°C sa Brukfildovim DV-E viskozimetrom, RV07 osovina, 100 obrtaja u minuti, 9300 ciklusa u sekundi (cps).
 
[0032] Karakteristična svojstva membrane:
 
§       Otpornost na visokim temperaturama (EN 1110): 110°C;
§       Vodonepropustljivost (EN 1928-B): 100 kPa.
 
Class -20°C.
 
[0033] Sastav formule, prikazan kao maseni procenat:
§       Smeša polietilena male gustine i stiren-butadien-stiren blok kopolimera: 6%;
§       Kalcijum-karbonat: 35%;
§       Industrijski bitumen 180/200: 59%.
 
Masa membrane debljine 4mm: 5.1 kg/m2;
Masa rolne membrane od 10m2: 51 kg.
Mehaničke karakteristike smeše:
§       Hladno savijanje (EN1109): -20°C;
§       Prodiranje na 25°C (EN 1426): 26 dmm;
§       Prodiranje na 60°C (EN 1426): 103 dmm;
§       Tačka omekšavanja (EN1427): 118°C;
§       Viskoznost na 180°C sa Brukfildovim DV-E viskozimetrom, RV07 osovina, 100 obrtaja u minuti, 9200 ciklusa u sekundi (cps).
 
[0034] Karakteristična svojstva membrane:
 
§       Otpornost na visokim temperaturama (EN 1110): 100°C.
§       Vodonepropustljivost (EN 1928-B): 100 kPa.
 
 
[0035] Specifične karakteristike nove formule, u poredjenju sa konvencionalnom formulom koja se koristi za proizvodnju membrane u istoj klasi, mogu biti rezimirane kao sledeće:
 
§       Potpuno odsustvo kalcijum-karbonata;
§       Mineralno punilo izgrađeno od šupljih staklenih mikrosfera sa gustinom između 0.1 i 0.14 g/cm3 i sa veličinom manjom od 120 µm.
§       Viša tačka omekšavanja.
§       Veći otpor protoka.
 
[0036] Pronalazak je detaljno ilustrovan u sledećim primerima.
 
PRIMER 1: Membrana klase -5
 
[0037] Sledeće supstance su uvedene u mešalicu zapremine 10m3:
§       Etilen/propilen kopolimer: 1100kg;
§       Izotaktički polipropilen: 400 kg;
§       Mineralno punilo izgrađeno od šupljih staklenih mikrosfera sa gustinom između 0.1 i 0.14 g/cm3 i sa veličinom manjom od 120 µm: 300kg;
§       Industrijski bitumen 180/200: 5900 kg.
 
 
[0038] Sastav formule, prikazan kao maseni procenat:
 
§       Smeša etilen/propilen kopolimera i izotaktičkog polipropilena: 19.5%;
§       Mineralno punilo: 3,9%;
§       Industrijski bitumen 180/200: 76,6%.
 
Mehaničke karakteristike smeše:
 
§       Hladno savijanje (EN1109): -5°C;
§       Prodiranje na 25°C (EN 1426): 21 dmm;
§       Prodiranje na 60°C (EN 1426): 78 dmm;
§       Tačka omekšavanja (EN1427): 157°C;
§       Viskoznost na 180°C sa Brukfildovim DV-E viskozimetrom, RV07 osovina, 100 obrtaja u minuti, 14000 ciklusa u sekundi (cps).
 
[0039] Kada se tako dobijena smeša koristi na proizvodnim linijama za potpuno konvencionalne membrane, dobije se membrana sa sledećim karakteristikama:
§       Masa membrane debljine 4mm: 3.0 kg/m2;
§       Masa rolne membrane od 10m2: 30 kg.
 
[0040] Karakteristična svojstva membrane:
 
§       Otpornost na visokim temperaturama (EN 1110): 130°C;
§       Vodonepropustljivost (EN 1928-B): 100 kPa.
 
PRIMER 2: Membrana klase -10
 
[0041] Sledeće supstance su uvedene u mešalicu zapremine 10m3:
 
§       Etilen/propilen kopolimer: 1400 kg;
§       Izotaktički polipropilen: 200 kg;
§       Mineralno punilo izgrađeno od šupljih staklenih mikrosfera sa gustinom između 0.1 i 0.14 g/cm3 i sa veličinom manjom od 120 µm: 300kg
§       Industrijski bitumen 180/200: 5822 kg.
 
[0042] Sastav formule, prikazan kao maseni procenat:
 
§       Smeša izotaktički polipropilena, etilen/propilen kopolimera: 20,7%;
§       Mineralno punilo: 3,9%;
§       Industrijski bitumen 180/200: 75,4%.
 
Mehaničke karakteristike smeše:
 
§       Hladno savijanje (EN1109): -10°C;
§       Prodiranje na 25°C (EN 1426): 27 dmm;
§       Prodiranje na 60°C (EN 1426): 107 dmm;
§       Tačka omekšavanja (EN1427): 154°C;
§       Viskoznost na 180°C sa Brukfildovim DV-E viskozimetrom, RV07 osovina, 100 obrtaja u minuti, 12900 ciklusa u sekundi (cps).
 
[0043] Kada se tako dobijena smeša koristi na proizvodnim linijama za potpuno konvencionalne membrane, dobije se membrana sa sledećim karakteristikama:
 
§       Masa membrane debljine 4mm:3,0kg/m2
§       Masa rolne membrane od 10m2: 30 kg.
 
[0044] Karakteristična svojstva membrane:
 
§       Otpornost na visokim temperaturama (EN 1110): 140°C.
§       Vodonepropustljivost (EN 1928-B): 100 kPa.
 
 
PRIMER 3: Membrana klase -20
 
[0045] Sledeće supstance su uvedene u mešalicu zapremine 10m3:
 
§       Smeša polietilena male gustine i stiren-butadien-stiren blok kopolimera: 1000kg.
§       Mineralno punilo izgrađeno od šupljih staklenih mikrosfera sa gustinom između 0.1 i 0.14 g/cm3 i sa veličinom manjom od 120 µm: 300kg
§       Industrijski bitumen 180/200: 6489 kg.
 
[0046] Sastav formule, prikazan kao maseni procenat:
 
§       Smeša polietilena male gustine i stiren-butadien-stiren blok kopolimera: 12,8%;
§       Mineralno punilo: 3,9%;
§       Industrijski bitumen 180/200: 83.3%.
 
[0047] Mehaničke karakteristike smeše:
§       Hladno savijanje (EN1109): -25°C;
§       Prodiranje na 25°C (EN 1426): 32 dmm;
§       Prodiranje na 60°C (EN 1426): 88 dmm;
§       Tačka omekšavanja (EN1427): 135°C;
§       Viskoznost na 180°C sa Brukfildovim DV-E viskozimetrom, RV07 osovina, 100 obrtaja u minuti, 16620 ciklusa u sekundi (cps).
 
[0048] Kada se tako dobijena smeša koristi na proizvodnim linijama za potpuno konvencionalne membrane, dobije se membrana sa sledećim karakteristikama:
 
§       Masa membrane debljine 4mm: 3.0 kg/m;
§       Masa rolne membrane od 10m2: 30 kg.
 
[0049] Karakteristična svojstva membrane:
 
§       Otpornost na visokim temperaturama (EN 1110): 120°C;
§       Vodonepropustljivost (EN 1928-B): 100 kPa.
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
6

Claims (9)

1.Hidroizolacione membrane koje se sastoje od ojačanog materijala impregniranog bituminoznom formulom koja se sastoji od industrijskog bitumena, mineralnog punila, termoplastičnog polimera ili smeše termoplastičnih polimera, koje karakteriše mineralno punilo izgrađeno od šupljih staklenih mikrosfera sa gustinom između 0.1 i 0.14 g/cm3 i sa veličinom manjom od 120 µm.
2.Hidroizolacione membrane prema zahtevu 1 naznačene time da se termoplastični polimer bira između polietilena male gustine, polietilena velike gustine, izotaktičnog polipropilena, etilen/propilen kopolimera, etilen/propilen/buten terpolimera, ataktičnog polipropilena i stiren-butadien-stiren blok kopolimera.
3.Hidroizolacione membrane prema bilo kom od zahteva 1-2, u kojima je industrijski bitumen prisutan u količinama između 70% i 80% po masi.
4.Hidroizolacione membrane prema bilo kom od zahteva od 1-3, u kojima je termoplasticni polimer ili polimeri prisutni u količinama između 15% i 25%.
5.Hidroizolacione membrane prema bilo kom od zaheva 1-4, u kojima je mineralno punjenje prisutno u količinama između 2% i 7% po masi, a radije u količinama između 3% i 5% po masi.
6.Hidroizolacione membrane prema bilo kom od patentnih zahteva 1-5, karakterisane specifičnom težinom koja je ispod 1g/cm3.
7.Postupak za izradu hidroizolacionih membrana koje pripadaju različitim klasama je definisan vrednostima hladnog savijanja, merenim prema standardu EN 1109, u opsegu od 0-25°C, uključuje impregnaciju ojačanog materijala industrijskim bitumenom, mineralnim punilom koe je izgrađeno od šupljih staklenih mikrosfera sa gustinom između 0.1 i 0.14 g/cm3 i sa veličinom manjom od 120 µm i termoplastičnim polimerom ili smešom termoplastičnih polimera.
8.Postupak prema zahtevu 7 pri čemu je ojačani materijal netkani poliester.
9.Hidroizolacione membrane naznačene time da se mogu dobiti postupkom iz zahteva 8.
MEP-2013-10A 2009-06-16 2010-06-11 Hidroizolacione membrane bazirane na bitumenu modifikovanom sa polimerima koji sadrže šuplje staklene mikrosfere ME01472B (me)