MA40194A - Procédé de fabrication d'une tôle d'acier à haute résistance avec formabilité et ductilité ameliorées et la tôle obtenue - Google Patents

Procédé de fabrication d'une tôle d'acier à haute résistance avec formabilité et ductilité ameliorées et la tôle obtenue

Info

Publication number
MA40194A
MA40194A MA040194A MA40194A MA40194A MA 40194 A MA40194 A MA 40194A MA 040194 A MA040194 A MA 040194A MA 40194 A MA40194 A MA 40194A MA 40194 A MA40194 A MA 40194A
Authority
MA
Morocco
Prior art keywords
ductility
manufacturing
high strength
strength steel
sheet
Prior art date
Application number
MA040194A
Other languages
English (en)
Other versions
MA40194B1 (fr
Inventor
Gunhild Föjer
Jean-Christophe Hell
Michel Soler
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MA40194A publication Critical patent/MA40194A/fr
Publication of MA40194B1 publication Critical patent/MA40194B1/fr

Abstract

Procédé de fabrication d'une tôle à haute résistance mécanique présentant une aptitude au formage et à la ductilité améliorée, qui correspond à la composition chimique de l'acier, en pourcentage pondéral: 0,25%
MA40194A 2014-07-03 2015-07-03 Procédé de fabrication d'une tôle d'acier à haute résistance avec formabilité et ductilité ameliorées et la tôle obtenue MA40194B1 (fr)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
PCT/IB2014/002293 WO2016001705A1 (fr) 2014-07-03 2014-07-03 Procédé de fabrication d'une tôle d'acier à haute résistance présentant une aptitude au formage et une ductilité améliorées, et tôle ainsi obtenue
PCT/IB2015/055036 WO2016001892A2 (fr) 2014-07-03 2015-07-03 Procédé de fabrication d'une tôle d'acier à haute résistance présentant une aptitude au façonnage et une ductilité améliorées et tôle obtenue
EP15750809.4A EP3164514B1 (fr) 2014-07-03 2015-07-03 Procédé de fabrication d'une tôle d'acier à haute résistance avec formabilité et ductilité ameliorées et la tôle obtenue

Publications (2)

Publication Number Publication Date
MA40194A true MA40194A (fr) 2017-05-10
MA40194B1 MA40194B1 (fr) 2019-08-30

Family

ID=52000885

Family Applications (1)

Application Number Title Priority Date Filing Date
MA40194A MA40194B1 (fr) 2014-07-03 2015-07-03 Procédé de fabrication d'une tôle d'acier à haute résistance avec formabilité et ductilité ameliorées et la tôle obtenue

Country Status (16)

Country Link
US (1) US10472692B2 (fr)
EP (1) EP3164514B1 (fr)
JP (1) JP6586432B2 (fr)
KR (1) KR102453718B1 (fr)
CN (1) CN106661650B (fr)
BR (1) BR112017000026B1 (fr)
CA (1) CA2954142C (fr)
ES (1) ES2737884T3 (fr)
HU (1) HUE044390T2 (fr)
MA (1) MA40194B1 (fr)
MX (1) MX2017000185A (fr)
PL (1) PL3164514T3 (fr)
RU (1) RU2680043C2 (fr)
TR (1) TR201909724T4 (fr)
UA (1) UA118878C2 (fr)
WO (2) WO2016001705A1 (fr)

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9924224B2 (en) 2015-04-03 2018-03-20 The Nielsen Company (Us), Llc Methods and apparatus to determine a state of a media presentation device
DE102015004399A1 (de) 2015-04-10 2016-10-13 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Wasch- und Reinigungsmittel mit polymerem Wirkstoff
CN106244923B (zh) 2016-08-30 2018-07-06 宝山钢铁股份有限公司 一种磷化性能和成形性能优良的冷轧高强度钢板及其制造方法
KR101830538B1 (ko) * 2016-11-07 2018-02-21 주식회사 포스코 항복비가 우수한 초고강도 강판 및 그 제조방법
WO2019122965A1 (fr) * 2017-12-19 2019-06-27 Arcelormittal Tôle d'acier laminée à froid et revêtue et son procédé de fabrication
WO2019122964A1 (fr) 2017-12-19 2019-06-27 Arcelormittal Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication
RU2768717C1 (ru) * 2018-11-30 2022-03-24 Арселормиттал Холоднокатаный отожжённый стальной лист с высокой степенью раздачи отверстия и способ его изготовления
WO2020128574A1 (fr) * 2018-12-18 2020-06-25 Arcelormittal Tôle d'acier laminée à froid et traitée thermiquement et son procédé de fabrication

Family Cites Families (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06128631A (ja) 1992-10-20 1994-05-10 Nippon Steel Corp 低温靱性の優れた高マンガン超高張力鋼の製造方法
JP3857939B2 (ja) 2001-08-20 2006-12-13 株式会社神戸製鋼所 局部延性に優れた高強度高延性鋼および鋼板並びにその鋼板の製造方法
AU2003270334A1 (en) * 2002-09-04 2004-03-29 Colorado School Of Mines Method for producing steel with retained austenite
AR042494A1 (es) 2002-12-20 2005-06-22 Sumitomo Chemical Co Acero inoxidable martensitico de alta resistencia con excelentes propiedades de resistencia a la corrosion por dioxido de carbono y resistencia a la corrosion por fisuras por tensiones de sulfuro
CN101376945B (zh) 2007-08-28 2011-06-15 宝山钢铁股份有限公司 2000MPa级超高强度高韧性钢板及其制造方法
JP5365216B2 (ja) 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
EP2123787A1 (fr) 2008-05-06 2009-11-25 Industeel Creusot Acier à hautes caractéristiques pour pièces massives
KR101027250B1 (ko) 2008-05-20 2011-04-06 주식회사 포스코 고연성 및 내지연파괴 특성이 우수한 고강도 냉연강판,용융아연 도금강판 및 그 제조방법
JP5418047B2 (ja) 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5365112B2 (ja) * 2008-09-10 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5315956B2 (ja) * 2008-11-28 2013-10-16 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
CN101638749B (zh) 2009-08-12 2011-01-26 钢铁研究总院 一种低成本高强塑积汽车用钢及其制备方法
JP5883211B2 (ja) * 2010-01-29 2016-03-09 株式会社神戸製鋼所 加工性に優れた高強度冷延鋼板およびその製造方法
JP5327106B2 (ja) * 2010-03-09 2013-10-30 Ｊｆｅスチール株式会社 プレス部材およびその製造方法
JP5287770B2 (ja) 2010-03-09 2013-09-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5136609B2 (ja) * 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
KR101243002B1 (ko) 2010-12-22 2013-03-12 주식회사 포스코 연신율이 우수한 고강도 강판 및 그 제조방법
KR20120071583A (ko) 2010-12-23 2012-07-03 주식회사 포스코 저온인성이 우수한 고강도 고망간강
KR101253885B1 (ko) 2010-12-27 2013-04-16 주식회사 포스코 연성이 우수한 성형 부재용 강판, 성형 부재 및 그 제조방법
JP5821260B2 (ja) * 2011-04-26 2015-11-24 Ｊｆｅスチール株式会社 成形性及び形状凍結性に優れた高強度溶融亜鉛めっき鋼板、並びにその製造方法
JP5440672B2 (ja) 2011-09-16 2014-03-12 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板およびその製造方法
US9617614B2 (en) * 2011-10-24 2017-04-11 Jfe Steel Corporation Method for manufacturing high strength steel sheet having excellent formability
RU2474623C1 (ru) * 2011-10-31 2013-02-10 Валентин Николаевич Никитин Способ производства высокопрочной листовой стали мартенситного класса и деформационно-термический комплекс для его осуществления
JP2013237923A (ja) 2012-04-20 2013-11-28 Jfe Steel Corp 高強度鋼板およびその製造方法
RU2491357C1 (ru) * 2012-05-10 2013-08-27 Федеральное государственное автономное образовательное учреждение высшего профессионального образования "Национальный исследовательский технологический университет "МИСиС" Способ производства листовой стали
JP5857905B2 (ja) 2012-07-25 2016-02-10 新日鐵住金株式会社 鋼材およびその製造方法
US20150203947A1 (en) 2012-07-31 2015-07-23 Jfe Steel Corporation High-strength galvanized steel sheet with excellent formability and shape fixability and method for manufacturing the same
CN102912219A (zh) 2012-10-23 2013-02-06 鞍钢股份有限公司 一种高强塑积trip钢板及其制备方法

Also Published As

Publication number Publication date
RU2016151786A (ru) 2018-06-28
US20170159143A1 (en) 2017-06-08
MA40194B1 (fr) 2019-08-30
MX2017000185A (es) 2017-05-01
UA118878C2 (uk) 2019-03-25
US10472692B2 (en) 2019-11-12
WO2016001892A3 (fr) 2016-03-17
CN106661650B (zh) 2018-12-25
WO2016001892A2 (fr) 2016-01-07
PL3164514T3 (pl) 2019-10-31
KR20170026402A (ko) 2017-03-08
CA2954142C (fr) 2022-08-30
BR112017000026B1 (pt) 2021-05-04
WO2016001705A1 (fr) 2016-01-07
KR102453718B1 (ko) 2022-10-11
JP6586432B2 (ja) 2019-10-02
RU2680043C2 (ru) 2019-02-14
CA2954142A1 (fr) 2016-01-07
CN106661650A (zh) 2017-05-10
EP3164514A2 (fr) 2017-05-10
TR201909724T4 (tr) 2019-07-22
ES2737884T3 (es) 2020-01-16
EP3164514B1 (fr) 2019-04-24
JP2017524817A (ja) 2017-08-31
HUE044390T2 (hu) 2019-10-28
BR112017000026A2 (pt) 2017-10-31
RU2016151786A3 (fr) 2018-12-10

Similar Documents

Publication Publication Date Title
MA40194A (fr) Procédé de fabrication d'une tôle d'acier à haute résistance avec formabilité et ductilité ameliorées et la tôle obtenue
MA54718A (fr) Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité et une aptitude au formage améliorées et tôle d'acier ainsi obtenue
MA49586A (fr) Procédé de production d'une feuille d'acier revêtue à haute résistance présentant une ductilité et une aptitude au formage améliorées et feuille d'acier revêtue ainsi obtenue
MA49778A (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance, une ductilité et une aptitude au formage améliorées
MA49159A (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle d'acier à haute résistance ainsi obtenue
MA49587A (fr) Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité et une aptitude au formage améliorées et tôle d'acier ainsi obtenue
MA49777A (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle ainsi obtenue
MX2017001688A (es) Lamina de acero de alta resistencia, metodo de produccion para la misma y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MA53357A (fr) Procédé de production d'une tôle d'acier revêtue haute résistance présentant une résistance, une ductilité et une aptitude au formage améliorées
MX2017001529A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MA50091A (fr) Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication
MA51296A (fr) Tôle d'acier à haute résistance et formabilité élevée et procédé de fabrication
MX2017001720A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MA45115B1 (fr) Procédé de fabrication d'une tôle d'acier twip à microstructure austénitique
MX2017001689A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX357839B (es) Hoja de acero platinada con zinc de alta resistencia y lámina de acero de alta resistencia que tiene maleabilidad superior y método para producir cada una de ellas.
MX2016007953A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2017005567A (es) Lamina de acero de alta resistencia, lamina de acero galvanizada por inmersion en caliente de alta resistencia, lamina de acero recubierta de aluminio por inmersion en caliente de alta resistencia, y lamina de acero electrogalvanizada de alta resistencia, y metodos para fabricacion de las mismas.
MA49660A (fr) Procédé de fabrication d'une feuille d'acier haute résistance et feuille obtenue selon le procédé
MA49585A (fr) Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées
BR112018071993A2 (pt) tubo de aço com alto teor de manganês com resistência à erosão-corrosão na zona com solda escalonada e método de fabricar o mesmo
MX2017003993A (es) Lamina de acero laminado en frio de alta resistencia y alta formabilidad o banda de acero y metodo para fabricar la misma.
MA49613A (fr) Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité, une aptitude au formage et une soudabilité élevées et tôle d'acier ainsi obtenue
UA113529C2 (xx) Мартенситні сталі з міцністю при розтягуванні 1700-2200 мпа
MX2015013538A (es) Placa de acero chapada de alta resistencia para elemento estructural soldado, metodo para producir la misma.