MA50091A - Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication - Google Patents

Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication

Info

Publication number
MA50091A
MA50091A MA050091A MA50091A MA50091A MA 50091 A MA50091 A MA 50091A MA 050091 A MA050091 A MA 050091A MA 50091 A MA50091 A MA 50091A MA 50091 A MA50091 A MA 50091A
Authority
MA
Morocco
Prior art keywords
ductility
strength
manufacturing process
sheet steel
showing excellent
Prior art date
Application number
MA050091A
Other languages
English (en)
Inventor
Coralie Jung
Frédéric Kegel
Astrid Perlade
Kangying Zhu
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MA50091A publication Critical patent/MA50091A/fr

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/26—Methods of annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/005—Modifying the physical properties by deformation combined with, or followed by, heat treatment of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/003—Cementite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
MA050091A 2017-12-19 2018-12-18 Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication MA50091A (fr)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IB2017/058129 WO2019122964A1 (fr) 2017-12-19 2017-12-19 Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication

Publications (1)

Publication Number Publication Date
MA50091A true MA50091A (fr) 2021-03-31

Family

ID=60972277

Family Applications (1)

Application Number Title Priority Date Filing Date
MA050091A MA50091A (fr) 2017-12-19 2018-12-18 Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication

Country Status (13)

Country Link
US (2) US11591665B2 (fr)
EP (1) EP3728655A2 (fr)
JP (2) JP7275137B2 (fr)
KR (2) KR102401886B1 (fr)
CN (2) CN114891961A (fr)
BR (1) BR112020011672B1 (fr)
CA (2) CA3085539C (fr)
MA (1) MA50091A (fr)
MX (1) MX2020006507A (fr)
RU (1) RU2747730C1 (fr)
UA (1) UA125358C2 (fr)
WO (2) WO2019122964A1 (fr)
ZA (1) ZA202003349B (fr)

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019122964A1 (fr) * 2017-12-19 2019-06-27 Arcelormittal Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication
WO2021009543A1 (fr) * 2019-07-16 2021-01-21 Arcelormittal Procédé de production de pièce en acier et pièce en acier
WO2021089851A1 (fr) * 2019-11-08 2021-05-14 Ssab Technology Ab Produit en acier au manganèse à haute résistance et son procédé de fabrication
WO2021123887A1 (fr) * 2019-12-19 2021-06-24 Arcelormittal Tôle d'acier laminée à chaud de ténacité élevée et son procédé de fabrication
WO2021123889A1 (fr) * 2019-12-19 2021-06-24 Arcelormittal Feuille d'acier laminée à chaud et traitée thermiquement et son procédé de fabrication
WO2021123886A1 (fr) * 2019-12-19 2021-06-24 Arcelormittal Tôle d'acier recuit laminée à chaud de haute ténacité et son procédé de fabrication
CN116034173A (zh) * 2020-09-23 2023-04-28 安赛乐米塔尔公司 经冷轧和涂覆的钢板及其制造方法
CN112375990B (zh) * 2020-10-30 2021-10-19 东北大学 一种屈服强度大于2000MPa的超高强度钢及其制备方法
CN112779465A (zh) * 2020-11-30 2021-05-11 江苏联峰能源装备有限公司 一种微合金车轴钢的制备方法
CN115181887B (zh) * 2021-04-02 2023-08-11 宝山钢铁股份有限公司 一种1180MPa级别低碳低合金Q＆P钢及其快速热处理制造方法
BR112023022131A2 (pt) * 2021-07-16 2024-01-23 Arcelormittal Processo de fabricação de partes de aço
TWI795076B (zh) * 2021-11-15 2023-03-01 中國鋼鐵股份有限公司 鋼材之熱處理方法
CN116144887B (zh) * 2022-09-09 2024-01-16 北京理工大学 一种实现无硅、无铝中锰钢的淬火-配分热处理方法
CN116752048A (zh) * 2023-06-12 2023-09-15 北京科技大学 一种强塑积大于90GPa%的超高强韧中锰钢及制备方法

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19936151A1 (de) * 1999-07-31 2001-02-08 Thyssenkrupp Stahl Ag Höherfestes Stahlband oder -blech und Verfahren zu seiner Herstellung
EP2115178B1 (fr) * 2007-02-23 2018-06-20 Tata Steel IJmuiden BV Feuillard d'acier à résistance élevée, laminé à froid et trempé en continu, et procédé de fabrication dudit feuillard
JP5440672B2 (ja) * 2011-09-16 2014-03-12 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板およびその製造方法
US9976203B2 (en) 2012-01-19 2018-05-22 Arcelormittal Ultra fine-grained advanced high strength steel sheet having superior formability
WO2015001367A1 (fr) * 2013-07-04 2015-01-08 Arcelormittal Investigación Y Desarrollo Sl Feuille d'acier laminée à froid, procédé de fabrication et véhicule
WO2015011510A1 (fr) 2013-07-25 2015-01-29 Arcelormittal Investigación Y Desarrollo Sl Joint soudé par points utilisant une résistance élevée et un formage élevé et son procédé de production
JPWO2015102050A1 (ja) 2014-01-06 2017-03-23 新日鐵住金株式会社 鋼材およびその製造方法
WO2016001703A1 (fr) * 2014-07-03 2016-01-07 Arcelormittal Procédé de fabrication d'une tôle d'acier à haute résistance et tôle obtenue par le procédé
WO2016001705A1 (fr) * 2014-07-03 2016-01-07 Arcelormittal Procédé de fabrication d'une tôle d'acier à haute résistance présentant une aptitude au formage et une ductilité améliorées, et tôle ainsi obtenue
US10550446B2 (en) 2014-10-30 2020-02-04 Jfe Steel Corporation High-strength steel sheet, high-strength hot-dip galvanized steel sheet, high-strength hot-dip aluminum-coated steel sheet, and high-strength electrogalvanized steel sheet, and methods for manufacturing same
JP6052471B2 (ja) 2015-01-15 2016-12-27 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
KR102246531B1 (ko) * 2015-05-20 2021-04-30 에이케이 스틸 프로퍼티즈 인코포레이티드 저합금 제3세대 초고강도 강
CN104988391A (zh) 2015-07-07 2015-10-21 河北钢铁股份有限公司 一种1200MPa级冷轧Q&P钢及其制造方法
KR101677396B1 (ko) * 2015-11-02 2016-11-18 주식회사 포스코 성형성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법
WO2017109538A1 (fr) 2015-12-21 2017-06-29 Arcelormittal Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées
WO2017109541A1 (fr) * 2015-12-21 2017-06-29 Arcelormittal Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue
US11414720B2 (en) 2016-01-29 2022-08-16 Jfe Steel Corporation High-strength steel sheet for warm working and method for manufacturing the same
WO2019122964A1 (fr) 2017-12-19 2019-06-27 Arcelormittal Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication

Also Published As

Publication number Publication date
EP3728655A2 (fr) 2020-10-28
UA125358C2 (uk) 2022-02-23
US20200362432A1 (en) 2020-11-19
MX2020006507A (es) 2020-09-17
CN114891961A (zh) 2022-08-12
JP2021508769A (ja) 2021-03-11
CA3135015A1 (fr) 2019-06-27
KR102470965B1 (ko) 2022-11-28
ZA202003349B (en) 2021-06-30
CN111511933A (zh) 2020-08-07
KR20220030308A (ko) 2022-03-10
CA3135015C (fr) 2023-06-13
US20230151452A1 (en) 2023-05-18
CA3085539A1 (fr) 2019-06-27
JP7275137B2 (ja) 2023-05-17
US11965225B2 (en) 2024-04-23
BR112020011672A2 (pt) 2020-11-17
KR20200083600A (ko) 2020-07-08
KR102401886B1 (ko) 2022-05-24
BR112020011672B1 (pt) 2023-05-09
CA3085539C (fr) 2022-08-30
RU2747730C1 (ru) 2021-05-13
WO2019122964A1 (fr) 2019-06-27
JP2023065520A (ja) 2023-05-12
WO2019123240A3 (fr) 2019-08-01
WO2019123240A2 (fr) 2019-06-27
US11591665B2 (en) 2023-02-28

Similar Documents

Publication Publication Date Title
MA50091A (fr) Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication
MA47078A (fr) Tôle d'acier trempé revêtue douée d'une excellente aptitude au formage et son procédé de fabrication
MA51296A (fr) Tôle d'acier à haute résistance et formabilité élevée et procédé de fabrication
MA43659A (fr) Tôle d'acier à haute résistance présentant une excellente aptitude au formage et procédé de fabrication de celle-ci
MA49778A (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance, une ductilité et une aptitude au formage améliorées
MA47018A (fr) Tôle d'acier à haute résistance et à haute formabilité traitée thermiquement et laminée à froid ainsi que son procédé de fabrication
MA48959A (fr) Tôle d'acier pour la production de pièces trempées sous presse, pièce trempée sous presse présentant une combinaison de résistance élevée et de ductilité élevée après collision, et procédés de production associés
MA49159A (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle d'acier à haute résistance ainsi obtenue
MA42495A (fr) Acier à haute résistance et procédé de fabrication
MA45115B1 (fr) Procédé de fabrication d'une tôle d'acier twip à microstructure austénitique
EP3533894A4 (fr) Tôle d'acier à haute résistance laminé à froid ayant une résistance à la traction supérieure ou égale à 1500 mpa et une excellente formabilité, et son procédé de fabrication
MA54718A (fr) Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité et une aptitude au formage améliorées et tôle d'acier ainsi obtenue
MA53357A (fr) Procédé de production d'une tôle d'acier revêtue haute résistance présentant une résistance, une ductilité et une aptitude au formage améliorées
MA49659A (fr) Tôle d'acier laminée à chaud et revêtue pour estampage à chaud, pièce en acier revêtue estampée à chaud et procédés de fabrication correspondants
MA49587A (fr) Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité et une aptitude au formage améliorées et tôle d'acier ainsi obtenue
MA49585A (fr) Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées
MA49777A (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle ainsi obtenue
PL2907886T3 (pl) Blacha stalowa cienka walcowana na gorąco o dużej wytrzymałości mająca maksymalną wytrzymałość na rozciąganie wynoszącą 980 MPa lub więcej oraz mająca doskonałą utwardzalność przy wypalaniu i wiązkość w niskiej temperaturze
EP3561119A4 (fr) Acier martensitique trempé ayant une faible limite d'élasticité et un excellent allongement uniforme et son procédé de fabrication
MA45140A (fr) Tôle d'acier twip ayant une matrice austénitique
MA40194B1 (fr) Procédé de fabrication d'une tôle d'acier à haute résistance avec formabilité et ductilité ameliorées et la tôle obtenue
MA45121A (fr) Feuille d'acier lamineè à froid et revenu, son procédeé de fabrication et son utilisation pour produire des pièces de véhicule
MA49660A (fr) Procédé de fabrication d'une feuille d'acier haute résistance et feuille obtenue selon le procédé
MA50999A (fr) Tôle d'acier laminée à froid et recuite et son procédé de fabrication
EP3719162A4 (fr) Matériau en acier à haute résistance ayant une excellente résistance à la fissuration induite par l'hydrogène et une ténacité à l'impact à basse température et son procédé de fabrication