KR960023165A - 연성이 우수한 인장강도 120kgf/㎟급 열연강판 및 그 제조방법 - Google Patents

연성이 우수한 인장강도 120kgf/㎟급 열연강판 및 그 제조방법 Download PDF

Info

Publication number
KR960023165A
KR960023165A KR1019940040270A KR19940040270A KR960023165A KR 960023165 A KR960023165 A KR 960023165A KR 1019940040270 A KR1019940040270 A KR 1019940040270A KR 19940040270 A KR19940040270 A KR 19940040270A KR 960023165 A KR960023165 A KR 960023165A
Authority
KR
South Korea
Prior art keywords
120kgf
temperature range
tensile strength
steel sheet
rolled steel
Prior art date
Application number
KR1019940040270A
Other languages
English (en)
Other versions
KR970009516B1 (en
Inventor
박성호
Original Assignee
김만제
포항종합제철 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김만제, 포항종합제철 주식회사 filed Critical 김만제
Priority to KR94040270A priority Critical patent/KR970009516B1/ko
Publication of KR960023165A publication Critical patent/KR960023165A/ko
Application granted granted Critical
Publication of KR970009516B1 publication Critical patent/KR970009516B1/ko

Abstract

본 발명은 오스테나이트 형성을 촉진시키는 원소인 Mo, Cr 및 B을 첨가하여 기지조직을 페라이트 보다는 베이나이트로 변화시키므로서 동일한 제조공정을 사용하더라도 잔류 오스테나이트 및 베이나이트의 형성이 보다 원할하게 되어 연성 및 강도가 향상되는 연성이 우수한 인장강도 120kgf/mm2급 열연 강판 및 그 제조방법을 제공함에 그 목적이 있다.
상기 목적을 달성하기 위하여 본 발명은 중량%로, C : 0.15∼0.30%, Si : 1.0∼2.5%, Mn : 1.0∼2.5%, Cr : 0.1∼0.5%, Mo : 0.1∼0.5%, S : 0.01% 이하, Al : 0.01∼0.08%, B : 0.0005∼0.01%, 나머지 Fe 및 기타 불가피한 불순원소로 조성되는 강 슬라브를 800∼850℃ 온도 범위로 마무리 열간압연하고, 700∼750℃ 온도 범위까지 수냉한 다음, Ar1온도 직하인 630∼680℃ 온도 범위까지 공냉하고 재차 수냉하여 370∼530℃ 온도 범위로 권취한 후, 서냉하므로서 그 최종조직이 5% 이상의 잔류오스테나이트-50% 이상의 베이나이트-페라이트인 인성이 우수한 인장강도 120kgf/mm2급 열연강판 및 그 제조방법을 제공함을 그 요지로 한다.

Description

연성이 우수한 인장강도 120kgf/mm2급 열연강판 및 그 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 보론(B)첨가 유무에 따른 기지조직의 변화를 나타낸 미세조직 사진으로서 (가)는 브론을 첨가하지 않는 경우의 미세조직 사진, (나)는 보론을 첨가한 경우의 미세조직 사진.

Claims (2)

  1. 중량%로, C : 0.15∼0.30%, Si : 1.0∼2.5%, Mn : 1.0∼2.5%, Cr : 0.1∼0.5%, Mo : 0.1∼0.5%, S : 0.01% 이하, Al : 0.01∼0.08%, B : 0.0005∼0.01%, 나머지 Fe 및 기타 불가피한 불순원소로 조성되는 그 조직이 5% 이상의 잔류 오스테나이트-50% 이상의 베이나이트-나머지 페라이트조직임을 특징으로 하는 연성이 우수한 인장강도 120kgf/mm2급 열연강판.
  2. 중량%로, C : 0.15∼0.30%, Si : 1.0∼2.5%, Mn : 1.0∼2.5%, Cr : 0.1∼0.5%, Mo : 0.1∼0.5%, S : 0.01% 이하, Al : 0.01∼0.08%, B : 0.0005∼0.01%, 나머지 Fe 및 기타 불가피한 불순원소로 조성되는 강 슬라브를 800∼850℃ 온도 범위로 마무리 열간압연하고, 700∼750℃ 온도 범위까지 수냉한 다음, Ar1온도 직하인 630∼680℃ 온도 범위까지 공냉하고 재차 수냉하여 370∼530℃ 온도 범위로 권취한 후, 서냉하여 이루어짐을 특징으로 하는 인성이 우수한 인장강도 120kgf/mm2급 열연강판 제조방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR94040270A 1994-12-31 1994-12-31 MAKING METHOD OF TENSILE STRENGTH 120º©/º HOT ROLLED STEEL PLATE AND SAME PRODUCT KR970009516B1 (en)