KR960023164A - 연성이 우수한 인장강도 100kg/㎟급 열연강판 및 그 제조방법 - Google Patents

연성이 우수한 인장강도 100kg/㎟급 열연강판 및 그 제조방법 Download PDF

Info

Publication number
KR960023164A
KR960023164A KR1019940033445A KR19940033445A KR960023164A KR 960023164 A KR960023164 A KR 960023164A KR 1019940033445 A KR1019940033445 A KR 1019940033445A KR 19940033445 A KR19940033445 A KR 19940033445A KR 960023164 A KR960023164 A KR 960023164A
Authority
KR
South Korea
Prior art keywords
hot rolled
tensile strength
steel sheet
rolled steel
ductility
Prior art date
Application number
KR1019940033445A
Other languages
English (en)
Other versions
KR970009505B1 (ko
Inventor
노광섭
Original Assignee
김만제
포항종합제철 주식회사
신창식
재단법인 산업과학기술연구소
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김만제, 포항종합제철 주식회사, 신창식, 재단법인 산업과학기술연구소 filed Critical 김만제
Priority to KR1019940033445A priority Critical patent/KR970009505B1/ko
Publication of KR960023164A publication Critical patent/KR960023164A/ko
Application granted granted Critical
Publication of KR970009505B1 publication Critical patent/KR970009505B1/ko

Abstract

본 발명은 강조성을 적절히 제어하고, 강의 미세조직을 페라이트-베이나이트-잔류 오스테나이트의 3상 조직으로 하고 상기 조직중 잔류오스테나이트를 5% 이상 함유하도록 하므로서, 극히 우수한 가공성을 발휘할 수 있는 고연성을 갖는 동시에 인장강도가 100kg/mm2급인 열연강판을 제공하고자 하는데 그 목적이 있다.
상기 목적을 달성하기 위한 본 발명은 중량%로, C : 0.15-3.30%, Si : 1.0∼2.5%, Mn : 1.0∼2.5%, Ni : 1.0∼2.0%, S : 0.01%이하, Al : 0.01∼0.08% 및 기타 불가피한 불순원소로 조성되고, 강의 조직이 페라이트, 베이나이트 및 5% 이상의 잔류 오스테나이트로 구성되는 연성이 우수한 인장도 100kg/mm2급 열연강판 및 그 제조방법에 관한 것을 그 요지로 한다.

Description

연성이 우수한 인장강도 100kg/mm2급 열연강판 및 그 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (3)

  1. 중량%로, C : 0.15-3.30%, Si : 1.0∼2.5%, Mn : 1.0∼2.5%, Ni : 1.0∼2.0%, S : 0.01%이하, Al : 0.01∼0.08% 및 기타 불가피한 불순원소로 조성되고, 강의 조직이 페라이트, 베이나이트 및 5% 이상의 잔류 오스테나이트로 구성됨을 특징으로 하는 연성이 우수한 인장강도 100kg/mm2급 열연강판.
  2. 제1항에 있어서, 상기 강의 인장강도가 100kg/mm2이상이고, (인장강도×연신율)값이 2500 이상임을 특징으로 하는 열연강판.
  3. 중량%로, C : 0.15-0.30%, Si : 1.0∼2.5%, Mn : 1.0∼2.5%, Ni : 1.0∼2.0%, S : 0.01%이하, Al : 0.01∼0.08% 및 기타 불가피한 불순원소로 조성되는 강을 800∼850℃의 온도범위로 마무리 압연한 다음, 700∼750℃ Ar1온도직상의 온도범위까지 수냉각하고, 이후 630∼680℃ Ar1온도직하의 온도범위까지 공랭한 후, 재차 수냉각하고 370∼430℃의 온도범위에서 권취함을 특징으로 하는 연성이 우수한 인장강도 100kg/mm2급 열연강판의 제조방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019940033445A 1994-12-09 1994-12-09 연성이 우수한 인장강도 100kg/mm^2급 열연강판의 제조방법 KR970009505B1 (ko)